Abstract: Samples of transparent glass-ceramics in the ternary system Li2O-Al2O3-SiO2 (LAS), with Er2O3 as a luminescent dopant, are investigated. The initial glass is obtained by the classical melting technique. In order to induce ceramization of the glass, TiO2 and ZrO2 are added in small amount as nucleating agents. The thermal treatments at 730 and 770 degrees C are carried out to promote formation of titanium zirconate solid solution precipitates. The spatial distribution of the precipitates in the material, their morphology, and their composition are investigated with TEM, HRTEM, HAADF-STEM, EELS and EFTEM. The results demonstrate that with the glass-melting preparation technique it is possible to achieve small nanoparticles with uniform distribution and higher number density than with the sol-gel glass preparation.

Abstract: La1-xCaxMnO3-delta (LCMO) thin films are grown by pulsed laser deposition on a (100) SrTiO3 substrate at temperatures between 530 degrees C and 890 degrees C. The magnetotransport properties show a high negative magnetoresistance and a shift of the maximum of the R(T) curve as function of temperature. The Curie temperature changes with deposition temperature and film quality in the range of 100-220K. The film quality is characterised by X-ray diffraction and transmission electron microscopy (TEM); film and target compositions were verified by atomic emission spectroscopy. The local structure of the film depends on the growth conditions and substrate temperature. TEM reveals a slight distortion of the film leading to a breakdown of the symmetry from orthorhombic to monoclinic. At the highest growth temperatures, a well defined interface is observed within the LCMO film, parallel to the substrate surface; this interface divides the film into two lamellae with a different microstructure. The lamella close to the substrate is perfectly coherent with the substrate, suggesting that it is strained as a result of the lattice parameter mismatch; the upper lamella shows a typical domain structure with unusual translation interfaces characterised by a displacement vector of the type 1/2[010](m) and 1/2[001](m) when referred ten the monoclinic lattice.

Abstract: The phase transformation sequences during thermal decomposition are investigated for Ni-rich melt-quenched body-centred cubic (bcc) and amorphous Ni-Zr alloys. Transmission electron microscopy (TEM) and X-ray diffraction (XRD) are used to determine the structure of crystallization products occurring after heating the melt-spun ribbon samples to various degrees of the phase transformation process monitored by differential scanning calorimetry (DSC). A single DSC peak is observed for both the bcc and amorphous Ni(91)Zr(9) alloys and a two-step process is indicated by DSC for the amorphous Ni(90)Zr(10) alloy. In the bcc-Ni(91)Zr(9) alloy which is actually a Ni(Zr) solid solution phase, the phase transformation starts with the precipitation of Ni(5)Zr crystallites followed, after a sufficient depletion of the matrix in Zr, by the subsequent transformation of the bcc-Ni(Zr) lattice to face-centred cubic (fcc) Ni. In the amorphous alloy of the same composition, the final products are fcc-Ni and Ni(5)Zr but at intermediate stages of the phase transformation, bcc-Ni(Zr) crystallites also appear. In the a-Ni(90)Zr(10) alloy the first DSC peak corresponds to the formation of the bcc-Ni(Zr) phase which then decomposes (second DSC peak) to the equilibrium phases fcc-Ni and Ni(5)Zr. Thus, in addition to the previous observation of the formation of the metastable bcc-Ni(Zr) phase by rapid quenching from the melt, here we present evidence that this phase can form also after partial crystallization of metallic glasses of appropriate chemical compositions.

Abstract: LaAMnSnO(6) (A = Sr, Ba) have been synthesized by high temperature solid-state reactions under dynamic 1% H(2)/Ar flow. Rietveld refinements on room temperature powder X-ray diffraction data indicate that LaSrMnSnO(6) crystallizes in the GdFeO(3)-structure, with space group Pnma and, combined with transmission electron microscopy, LaBaMnSnO(6) in Imma. Both space groups are common in disordered double-perovskites. The Mn(3+) and Sn(4+) ions whose valence states were confirmed by X-ray absorption spectroscopy, are completely disordered over the B-sites and the BO(6) octahedra are slightly distorted. LaAMnSnO(6) are ferromagnetic semiconductors with a T(C) = 83 K for the Sr- and 66 K for the Ba-compound. The title compounds, together with the previously reported LaCaMnSnO(6) provide an interesting example of progression from Pnma to Imma as the tolerance factor increases. An analysis of the relationship between space group and tolerance factor for the series LaAMnMO(6) (A = Ca, Sr, Ba; M = Sn, Ru) provides a better understanding of the symmetry determination for double perovskites.