Abstract: La1-xCaxMnO3-delta (LCMO) thin films are grown by pulsed laser deposition on a (100) SrTiO3 substrate at temperatures between 530 degrees C and 890 degrees C. The magnetotransport properties show a high negative magnetoresistance and a shift of the maximum of the R(T) curve as function of temperature. The Curie temperature changes with deposition temperature and film quality in the range of 100-220K. The film quality is characterised by X-ray diffraction and transmission electron microscopy (TEM); film and target compositions were verified by atomic emission spectroscopy. The local structure of the film depends on the growth conditions and substrate temperature. TEM reveals a slight distortion of the film leading to a breakdown of the symmetry from orthorhombic to monoclinic. At the highest growth temperatures, a well defined interface is observed within the LCMO film, parallel to the substrate surface; this interface divides the film into two lamellae with a different microstructure. The lamella close to the substrate is perfectly coherent with the substrate, suggesting that it is strained as a result of the lattice parameter mismatch; the upper lamella shows a typical domain structure with unusual translation interfaces characterised by a displacement vector of the type 1/2[010](m) and 1/2[001](m) when referred ten the monoclinic lattice.

Abstract: The phase transformation sequences during thermal decomposition are investigated for Ni-rich melt-quenched body-centred cubic (bcc) and amorphous Ni-Zr alloys. Transmission electron microscopy (TEM) and X-ray diffraction (XRD) are used to determine the structure of crystallization products occurring after heating the melt-spun ribbon samples to various degrees of the phase transformation process monitored by differential scanning calorimetry (DSC). A single DSC peak is observed for both the bcc and amorphous Ni(91)Zr(9) alloys and a two-step process is indicated by DSC for the amorphous Ni(90)Zr(10) alloy. In the bcc-Ni(91)Zr(9) alloy which is actually a Ni(Zr) solid solution phase, the phase transformation starts with the precipitation of Ni(5)Zr crystallites followed, after a sufficient depletion of the matrix in Zr, by the subsequent transformation of the bcc-Ni(Zr) lattice to face-centred cubic (fcc) Ni. In the amorphous alloy of the same composition, the final products are fcc-Ni and Ni(5)Zr but at intermediate stages of the phase transformation, bcc-Ni(Zr) crystallites also appear. In the a-Ni(90)Zr(10) alloy the first DSC peak corresponds to the formation of the bcc-Ni(Zr) phase which then decomposes (second DSC peak) to the equilibrium phases fcc-Ni and Ni(5)Zr. Thus, in addition to the previous observation of the formation of the metastable bcc-Ni(Zr) phase by rapid quenching from the melt, here we present evidence that this phase can form also after partial crystallization of metallic glasses of appropriate chemical compositions.

Abstract: LaAMnSnO(6) (A = Sr, Ba) have been synthesized by high temperature solid-state reactions under dynamic 1% H(2)/Ar flow. Rietveld refinements on room temperature powder X-ray diffraction data indicate that LaSrMnSnO(6) crystallizes in the GdFeO(3)-structure, with space group Pnma and, combined with transmission electron microscopy, LaBaMnSnO(6) in Imma. Both space groups are common in disordered double-perovskites. The Mn(3+) and Sn(4+) ions whose valence states were confirmed by X-ray absorption spectroscopy, are completely disordered over the B-sites and the BO(6) octahedra are slightly distorted. LaAMnSnO(6) are ferromagnetic semiconductors with a T(C) = 83 K for the Sr- and 66 K for the Ba-compound. The title compounds, together with the previously reported LaCaMnSnO(6) provide an interesting example of progression from Pnma to Imma as the tolerance factor increases. An analysis of the relationship between space group and tolerance factor for the series LaAMnMO(6) (A = Ca, Sr, Ba; M = Sn, Ru) provides a better understanding of the symmetry determination for double perovskites.

Abstract: Recent developments in the field of TEM characterisation of Si device materials are discussed and illustrated by a few case studies of material in different stages of various kinds of processing. Important challenges are the ever decreasing defect densities and device feature sizes. Defect delineation techniques using large area inspection tools yielding accurate coordinates of the defects to be studied have therefore become an essential part of the TEM analysis procedure. The possibility to transfer these defect coordinates without loss of accuracy to tools for local TEM specimen preparation is also a conditio sine qua non for a successful analysis. Insitu TEM remains important as dynamic processes can be observed and analysed under well defined experimental conditions. As case studies illustrating new developments, results are presented on defects in as-grown Ct silicon, on in-situ studies in processed silicon, on problem sites in advanced integrated circuit structures and on assessment of localised strain fields in the nm size scale.

Abstract: The surface of commercial Nitinol wires with original oxides and a thickness in the 30-190 nm range was investigated by different state of art TEM techniques. The oxide surface layer was identified as a combination of TiO and TiO2 depending on the processing of the wire. Between the core of the wires and the oxidized surface, an interfacial Ni3Ti nanolayer was observed while Ni nanoparticles are found inside the original oxide. The particle sizes, their distribution in the surface and the Ti-O stoichiometry were deduced from the analysis of the obtained data. Molecular dynamics calculations performed for evaluation of the stability of Ni particles relative to the atomic state revealed that a pure Ni particle has a lower energy than free Ni atoms inside the TiO2 lattice. The obtained results are discussed with respect to surface stability and Ni release in the human body.

Abstract: The synthesis, electron diffraction (ED), synchrotron X-ray and neutron structure, X-ray absorption spectroscopy (XAS) and magnetic property studies of La2MnVO6 double perovskite are described. Analysis of the synchrotron powder X-ray diffraction data for La2MnVO6 indicates a disordered arrangement of Mn and V at the B-site of the perovskite structure. Absence of super-lattice reflections in the ED patterns for La2MnVO6 supports the disordered cation arrangement. Room temperature time-of-flight (TOF) neutron powder diffraction (NPD) data show no evidence of cation ordering, in corroboration with the ED and synchrotron studies (orthorhombic Pnma, a = 5.6097(3), b = 7.8837(5) and c = 5.5668(3) ; 295 K, NPD). A comparison of XAS analyses of La2TVO6 with T = Ni and Co shows T2+ formal oxidation state while the T = Mn material evidences a Mn3+ admixture into a dominantly Mn2+ ground state. V-K edge measurements manifest a mirror image behavior with a V4+ state for T = Ni and Co with a V3+ admixture arising in the T = Mn material. The magnetic susceptibility data for La2MnVO6 show ferromagnetic correlations; the observed effective moment, µeff (5.72 µB) is much smaller than the calculated moment (6.16 µB) based on the spin-only formula for Mn2+ (d5, HS) /V4+ (d1), supportive of the partly oxidized Mn and reduced V scenario (Mn3+/V3+).

Abstract: We present a theoretical study of macrotwins arising in cubic to tetragonal martensitic transformations. The results help to explain some features of such macrotwins observed in Ni65Al35.

Abstract: Multishell tabular grains have a higher speed than pure AgBr tabular grains. Usually the shells differ in size and iodide content, but also the precipitation method for the iodide containing shells has an influence on the iodide incorporation. A TEM investigation was performed to determine the defect structure of multishell AgBr (111) tabular crystals containing a shell with a low iodide concentration and one with a high iodide concentration. The twins that induce tabular growth and stacking fault contrast in the region of the iodide shells have been observed, similar to previously studied AgBr/Ag(Br,I) coreshell crystals. Moreover in some of the crystals dislocations have been observed, sometimes even an entire network. The number of dislocations formed varies for the different methods of iodide addition. Also variations in average thickness between the different iodide addition methods have been observed. A higher number of dislocations and thicker crystals point towards a higher local concentration of iodide. These observations allow deciding which iodide incorporation method is most useful for a preferred dislocation pattern.