“Synthesis and crystal structure of new titanyl phosphate Sr2TiO(PO4)2”. Shpanchenko RV, Tsirlin AA, Hadermann J, Antipov EV, Russian chemical bulletin 57, 552 (2008). http://doi.org/10.1007/s11172-008-0085-9
Abstract: New strontium titanyl phosphate Sr2TiO(PO4)2 (1) was synthesized and characterized by X-ray powder diffraction, electron diffraction, high-resolution electron microscopy, and band structure calculations. Titanyl phosphate 1 is isostructural with vanadyl phosphate Sr2VO(PO4)2 and has a layered structure. The titanium atoms are shifted from the centers of the TiO6 octahedra and form short (1.74 Å) titanyl bonds. The structure of 1 is an unusual example of the disordered orientation of the chains formed by TiO6 octahedra in complex titanium phosphates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.529
Times cited: 2
DOI: 10.1007/s11172-008-0085-9
|
|
|
“Synthesis and crystal structure of the new complex oxide Ca7Mn2.14Ga5.86O17.93”. Kalyuzhnaya AS, Abakumov AM, Rozova MG, d' Hondt H, Hadermann J, Antipov EV, Russian chemical bulletin 59, 706 (2010). http://doi.org/10.1007/s11172-010-0150-z
Abstract: The complex oxide Ca7Mn2.14Ga5.86O17.93 was synthesized by the solid-state reaction in a sealed evacuated quartz tube at 1000 °C. Its crystal structure was determined by electron diffraction and X-ray powder diffraction. The structure can be represented as a tetrahedral framework, viz., the polyanion [(Mn0.285Ga0.715)15O29.86]19- stabilized by the incorporated cation [Ca14GaO6]19+. The polycation consists of the GaO6 octahedra surrounded by the Ca atoms, which are arranged to form a cube capped at all places. The tetrahedral framework is partially disordered due to the presence of tetrahedra with two possible orientations in the positions (0, 0, 0) and (x, x, x) with x ≈ 0.15 and 0.17. The relationship between the Ca7Mn2.14Ga5.86O17.93 structures and related ordered phases with the symmetry F23, as well as the influence of the oxygen content on the ordering in the tetrahedral framework, are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.529
Times cited: 1
DOI: 10.1007/s11172-010-0150-z
|
|
|
“The synthesis and thermodynamic properties of strontium fluoromanganite Sr2.5Mn6O12.5-\deltaF2”. Kovba ML, Skolis YY, Abakumov AM, Hadermann J, Sukhushina IS, Russian journal of physical chemistry A 84, 2033 (2010). http://doi.org/10.1134/S0036024410120046
Abstract: The existence of the [SrF(0.8)O(0.1)](2.5)[Mn(6)O(12)] = Sr(2.5)Mn(6)O(12.5 – delta)F(2) compound was established in the SrO-Mn(2)O(3)-SrF(2) system at 900A degrees C and p(O(2)) = 1 atm. The crystal structure of strontium fluoromanganite was determined from the X-ray powder diffraction data, electron diffraction, and high-resolution electron microscopy. It can be described in the monoclynic system with four Miller hklm indices: hklm: H = h a* + k b* + l c (1) (*) + m q (1), q (1), q (1) = c (2) (*) = gamma c (1) (*) , gamma a parts per thousand 0.632, a a parts per thousand a a parts per thousand 9.72 , b a parts per thousand 9.55 , c (1) a parts per thousand 2.84 , c (2) a parts per thousand 4.49 , monoclinic angle gamma a parts per thousand 95.6A degrees. The electromotive force method with a solid fluorine ion electrolyte was used to refine the composition of fluoromanganite and determine the thermodynamic functions of its formation from phases neighboring in the phase diagram (SrMn(3)O(6), Mn(2)O(3), SrF(2), and oxygen), Delta GA degrees, kJ/mol = -(111.7 +/- 1.9) + (89.5 +/- 1.5) x 10(-3) T.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.581
Times cited: 1
DOI: 10.1134/S0036024410120046
|
|
|
“Synthesis and structure of fluorinated RBa2Cu2O6+. (R=Dy, Ho and Tm) phases”. Oleynikov PN, Shpanchenko RV, Rozova MG, Abakumov AM, Antipov EV, Hadermann J, Lebedev OI, Van Tendeloo G, Russian journal of inorganic chemistry 46, 153 (2001)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.787
|
|
|
“Effect of Bimetallic Pd/Pt Clusters on the Sensing Properties of Nanocrystalline SnO2 in the Detection of CO”. Malkov I V, Krivetskii VV, Potemkin D I, Zadesenets A V, Batuk MM, Hadermann J, Marikutsa A V, Rumyantseva MN, Gas'kov AM, Russian journal of inorganic chemistry 63, 1007 (2018). http://doi.org/10.1134/S0036023618080168
Abstract: Nanocrystalline tin dioxide modified by Pd and Pt clusters or by bimetallic PdPt nanoparticles was synthesized. Distribution of the modifers on the SnO2 surface was studied by high-resolution transmission electron microscopy and energy dispersive X-ray microanalysis with element distribution mapping. It was shown that the Pd/Pt ratio in bimetallic particles varies over a broad range and does not depend on the particle diameter. The effect of platinum metals on the reducibility of nanocrystalline SnO2 by hydrogen was determined. The sensing properties of the resulting materials towards 6.7 ppm CO in air were estimated in situ by electrical conductivity measurements. The sensor response of SnO2 modified with bimetallic PdPt particles was a superposition of the signals of samples with Pt and Pd clusters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.787
Times cited: 3
DOI: 10.1134/S0036023618080168
|
|
|
“Lanthanum-strontium cuprate as a promising cathodic matreila for solid oxide fuel cells”. Mazo GN, Savvin SN, Abakumov AM, Hadermann J, Dobrovol'skii YA, Leonova LS, Russian journal of electrochemistry 43, 436 (2007). http://doi.org/10.1134/S1023193507040106
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.828
Times cited: 8
DOI: 10.1134/S1023193507040106
|
|
|
“Crystal structure and magnetic properties of novel reduced V(IV)-based oxide Pb2V5O12”. Shpanchenko RV, Chyornaya VV, Abakumov AM, Antipov EV, Hadermann J, Van Tendeloo G, Kaul E, Geibel C, Sheptyakov D, Balagurov AM, Zeitschrift für anorganische und allgemeine Chemie 627, 2143 (2001). http://doi.org/10.1002/1521-3749(200109)627:9<2143::AID-ZAAC2143>3.0.CO;2-R
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.144
Times cited: 4
DOI: 10.1002/1521-3749(200109)627:9<2143::AID-ZAAC2143>3.0.CO;2-R
|
|
|
“Mg1-xRhB, a new boridometallide with 2D polyanion”. Alekseeva AM, Abakumov AM, Leithe-Jasper A, Schnelle W, Prots Y, Hadermann J, Van Tendeloo G, Antipov EV, Grin Y, Zeitschrift für anorganische und allgemeine Chemie 631, 1047 (2005). http://doi.org/10.1002/zaac.200400479
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.144
Times cited: 13
DOI: 10.1002/zaac.200400479
|
|
|
“Determination of spinel content in cycled Li1.2Ni0.13Mn0.54Co0.13O2 using three-dimensional electron diffraction and precession electron diffraction”. Quintelier M, Perkisas T, Poppe R, Batuk M, Hendrickx M, Hadermann J, Symmetry-Basel 13, 1989 (2021). http://doi.org/10.3390/SYM13111989
Abstract: Among lithium battery cathode materials, Li1.2Ni0.13Mn0.54Co0.13O2 (LR-NMC) has a high theoretical capacity, but suffers from voltage and capacity fade during cycling. This is partially ascribed to transition metal cation migration, which involves the local transformation of the honeycomb layered structure to spinel-like nano-domains. Determination of the honeycomb layered/spinel phase ratio from powder X-ray diffraction data is hindered by the nanoscale of the functional material and the domains, diverse types of twinning, stacking faults, and the possible presence of the rock salt phase. Determining the phase ratio from transmission electron microscopy imaging can only be done for thin regions near the surfaces of the crystals, and the intense beam that is needed for imaging induces the same transformation to spinel as cycling does. In this article, it is demonstrated that the low electron dose sufficient for electron diffraction allows the collection of data without inducing a phase transformation. Using calculated electron diffraction patterns, we demonstrate that it is possible to determine the volume ratio of the different phases in the particles using a pair-wise comparison of the intensities of the reflections. Using this method, the volume ratio of spinel structure to honeycomb layered structure is determined for a submicron sized crystal from experimental three-dimensional electron diffraction (3D ED) and precession electron diffraction (PED) data. Both twinning and the possible presence of the rock salt phase are taken into account. After 150 charge-discharge cycles, 4% of the volume in LR-NMC particles was transformed irreversibly from the honeycomb layered structure to the spinel structure. The proposed method would be applicable to other multi-phase materials as well.
Keywords: A1 Journal article; Engineering sciences. Technology; Engineering Management (ENM); Electron microscopy for materials research (EMAT)
Impact Factor: 1.457
DOI: 10.3390/SYM13111989
|
|
|
“Nanoscale Characterization of Growth of Secondary Phases in Off-Stoichiometric CZTS Thin Films”. Vishwakarma M, Karakulina OM, Abakumov AM, Hadermann J, Mehta BR, Journal of nanoscience and nanotechnology 18, 1688 (2018). http://doi.org/10.1166/jnn.2018.14261
Abstract: The presence of secondary phases is one of the main issues that hinder the growth of pure kesterite Cu2ZnSnS4 (CZTS) based thin films with suitable electronic and junction properties for efficient solar cell devices. In this work, CZTS thin films with varied Zn and Sn content have been prepared by RF-power controlled co-sputtering deposition using Cu, ZnS and SnS targets and a subsequent sulphurization step. Detailed TEM investigations show that the film shows a layered structure with the majority of the top layer being the kesterite phase. Depending on the initial thin film composition, either about ~1 μm Cu-rich and Zn-poor kesterite or stoichiometric CZTS is formed as top layer. X-ray diffraction, Raman spectroscopy and transmission electron microscopy reveal the presence of Cu2−x S, ZnS and SnO2 minor secondary phases in the form of nanoinclusions or nanoparticles or intermediate layers.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.483
DOI: 10.1166/jnn.2018.14261
|
|
|
“Surface passivation of CIGS solar cells using gallium oxide”. Garud S, Gampa N, Allen TG, Kotipalli R, Flandre D, Batuk M, Hadermann J, Meuris M, Poortmans J, Smets A, Vermang B, Physica status solidi : A : applications and materials science 215, 1700826 (2018). http://doi.org/10.1002/PSSA.201700826
Abstract: This work proposes gallium oxide grown by plasma-enhanced atomic layer deposition, as a surface passivation material at the CdS buffer interface of Cu(In,Ga)Se-2 (CIGS) solar cells. In preliminary experiments, a metal-insulator-semiconductor (MIS) structure is used to compare aluminium oxide, gallium oxide, and hafnium oxide as passivation layers at the CIGS-CdS interface. The findings suggest that gallium oxide on CIGS may show a density of positive charges and qualitatively, the least interface trap density. Subsequent solar cell results with an estimated 0.5nm passivation layer show an substantial absolute improvement of 56mV in open-circuit voltage (V-OC), 1mAcm(-2) in short-circuit current density (J(SC)), and 2.6% in overall efficiency as compared to a reference (with the reference showing 8.5% under AM 1.5G).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.775
Times cited: 8
DOI: 10.1002/PSSA.201700826
|
|
|
“Compositionally induced phase transition in the Ca2MnGa1-xAlxO5 solid solutions: ordering of tetrahedral chains in brownmillerite structure”. Abakumov AM, Kalyuzhnaya AS, Rozova MG, Antipov EV, Hadermann J, Van Tendeloo G, Solid state sciences 7, 801 (2005). http://doi.org/10.1016/j.solidstatesciences.2005.01.020
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 38
DOI: 10.1016/j.solidstatesciences.2005.01.020
|
|
|
“Local structure of perovskite-based “Pb2Fe2O5””. Hadermann J, Abakumov AM, Nikolaev IV, Antipov EV, Van Tendeloo G, Solid state sciences 10, 382 (2008). http://doi.org/10.1016/j.solidstatesciences.2007.12.008
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 29
DOI: 10.1016/j.solidstatesciences.2007.12.008
|
|
|
“Synthesis and investigation of novel Mn-based oxyfluoride Sr2Mn2O5-xF1+x”. Lobanov MV, Abakumov AM, Sidorova AV, Rozova MG, D'yachenko OG, Antipov EV, Hadermann J, Van Tendeloo G, Solid state sciences 4, 19 (2002). http://doi.org/10.1016/S1293-2558(01)01209-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 21
DOI: 10.1016/S1293-2558(01)01209-2
|
|
|
“Increasing the solubility limit for tetrahedral aluminium in ZnO:Al nanorods by variation in synthesis parameters”. Kelchtermans A, Adriaensens P, Slocombe D, Kuznetsov VL, Hadermann J, Riskin A, Elen K, Edwards PP, Hardy A, Van Bael MK, Journal of nanomaterials 2015, 1 (2015). http://doi.org/10.1155/2015/546041
Abstract: Nanocrystalline ZnO:Al nanoparticles are suitable building blocks for transparent conductive layers. As the concentration of substitutional tetrahedral Al is an important factor for improving conductivity, here we aim to increase the fraction of substitutional Al. To this end, synthesis parameters of a solvothermal reaction yielding ZnO:Al nanorods were varied. A unique set of complementary techniques was combined to reveal the exact position of the aluminium ions in the ZnO lattice and demonstrated its importance in order to evaluate the potential of ZnO:Al nanocrystals as optimal building blocks for solution deposited transparent conductive oxide layers. Both an extension of the solvothermal reaction time and stirring during solvothermal treatment result in a higher total tetrahedral aluminium content in the ZnO lattice. However, only the longer solvothermal treatment effectively results in an increase of the substitutional positions aimed for.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.871
Times cited: 2
DOI: 10.1155/2015/546041
|
|
|
“Effect of selenium content of CuInSex alloy nanopowder precursors on recrystallization of printed CuInSe2 absorber layers during selenization heat treatment”. E Zaghi A, Buffière M, Koo J, Brammertz G, Batuk M, Verbist C, Hadermann J, Kim WK, Meuris M, Poortmans J, Vleugels J;, Thin solid films : an international journal on the science and technology of thin and thick films , 1 (2014). http://doi.org/10.1016/j.tsf.2014.10.003
Abstract: Polycrystalline CuInSe2 semiconductors are efficient light absorber materials for thin film solar cell technology, whereas printing is one of the promising low cost and non-vacuum approaches for the fabrication of thin film solar cells. The printed precursors are transformed into a dense polycrystalline CuInSe2 semiconductor film via thermal treatment in ambient selenium atmosphere (selenization). In this study, the effect of the selenium content in high purity mechanically synthesized CuInSex (x = 2, 1.5, 1 or 0.5) alloy precursors on the recrystallization of the CuInSe2 phase during the selenization process was investigated. The nanostructure and phase variation of CuInSex nanopowders were investigated by different characterization techniques. The recrystallization process of the 12 μm thick CuInSex coatings into the CuInSe2 phase during selenization in selenium vapor was investigated via in-situ high temperature X-ray diffraction. The CuInSex precursors with lower selenium content showed a more pronounced phase conversion into CuInSe2 compared to the higher selenium content CuInSex precursors. Moreover, the CuInSex (x = 0.5 and 1) precursor resulted in a denser polycrystalline CuInSe2 semiconductor film with larger crystals. This could be attributed to a more intensive atomic interdiffusion within the CuInSex precursor system compared to a CuInSe2 phase precursor, and the formation of intermediate CuSe and CuSe2 fluxing phases during selenization.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.879
Times cited: 7
DOI: 10.1016/j.tsf.2014.10.003
|
|
|
“Effect of the burn-out step on the microstructure of the solution-processed Cu(In,Ga)Se2 solar cells”. Batuk M, Buffiere M, Zaghi AE, Lenaers N, Verbist C, Khelifi S, Vleugels J, Meuris M, Hadermann J, Thin solid films : an international journal on the science and technology of thin and thick films 583, 142 (2015). http://doi.org/10.1016/j.tsf.2015.03.063
Abstract: For the development of the photovoltaic industry cheap methods for the synthesis of Cu(In,Ga)Se-2 (CIGSe) based solar cells are required. In this work, CIGSe thin films were obtained by a solution-based method using oxygen-bearing derivatives. With the aimof improving the morphology of the printed CIGSe layers, we investigated two different annealing conditions of the precursor layer, consisting of (1) a direct selenization step (reference process), and (2) a pre-treatment thermal step prior to the selenization. We showed that the use of an Air/H2S burn-out step prior to the selenization step increases the CIGSe grain size and reduces the carbon content. However, it leads to the reduction of the solar cell efficiency from 4.5% in the reference sample down to 0.5% in the annealed sample. Detailed transmission electron microscopy analysis, including high angle annular dark field scanning transmission electron microscopy and energy dispersive X-ray mapping, was applied to characterize the microstructure of the film and to determine the relationship between microstructure and the solar cell performance. We demonstrated that the relatively low efficiency of the reference solar cells is related not only to the nanosize of the CIGSe grains and presence of the pores in the CIGSe layer, but also to the high amount of secondary phases, namely, In/Ga oxide (or hydroxide) amorphous matter, residuals of organicmatter (carbon), and copper sulfide that is formed at the CIGSe/MoSe2 interface. The annealing in H2S during the burn-out step leads to the formation of the copper sulfide at all grain boundaries and surfaces in the CIGSe layer, which results in the noticeably efficiency drop. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.879
Times cited: 5
DOI: 10.1016/j.tsf.2015.03.063
|
|
|
“Polytypism in mcalpineite : a study of natural and synthetic Cu₃TeO₆”. Missen OP, Mills SJ, Canossa S, Hadermann J, Nenert G, Weil M, Libowitzky E, Housley RM, Artner W, Kampf AR, Rumsey MS, Spratt J, Momma K, Dunstan MA, Acta Crystallographica. Section B: Structural Science, Crystal Engineering and Materials (Online) 78 (2022). http://doi.org/10.1107/S2052520621013032
Abstract: Synthetic and naturally occurring forms of tricopper orthotellurate, (Cu3TeO6)-Te-II-O-IV (the mineral mcalpineite) have been investigated by 3D electron diffraction (3D ED), X-ray powder diffraction (XRPD), Raman and infrared (IR) spectroscopic measurements. As a result of the diffraction analyses, (Cu3TeO6)-Te-II-O-IV is shown to occur in two polytypes. The higher-symmetric (Cu3TeO6)-Te-II-O-IV-1C polytype is cubic, space group 1a (3) over bar, with a = 9.537 (1) angstrom and V = 867.4 (3) angstrom(3) as reported in previous studies. The 1C polytype is a well characterized structure consisting of alternating layers of (CuO6)-O-II octahedra and both (CuO6)-O-II and (TeO6)-O-VI octahedra in a patchwork arrangement. The structure of the lower-symmetric orthorhombic (Cu3TeO6)-Te-II-O-IV-2O polytype was determined for the first time in this study by 3D ED and verified by Rietveld refinement. The 2O polytype crystallizes in space group Pcca, with a = 9.745 (3) angstrom, b = 9.749 (2) angstrom, c = 9.771 (2) angstrom and V = 928.3 (4) angstrom(3) . High-precision XRPD data were also collected on (Cu3TeO6)-Te-II-O-IV-2O to verify the lower-symmetric structure by performing a Rietveld refinement. The resultant structure is identical to that determined by 3D ED, with unit-cell parameters a = 9.56157 (19) angstrom, b = 9.55853 (11) angstrom, c = 9.62891 (15) angstrom and V = 880.03 (2) angstrom(3) . The lower symmetry of the 2O polytype is a consequence of a different cation ordering arrangement, which involves the movement of every second (CuO6)-O-II and (TeO6)-O-VI octahedral layer by (1/4, 1/4, 0), leading to an offset of (TeO6)-O-VI and (CuO6)-O-II octahedra in every second layer giving an ABAB* stacking arrangement. Syntheses of (Cu3TeO6)-Te-II-O-IV showed that low-temperature (473 K) hydrothermal conditions generally produce the 2O polytype. XRPD measurements in combination with Raman spectroscopic analysis showed that most natural mcalpineite is the orthorhombic 2O polytype. Both XRPD and Raman spectroscopy measurements may be used to differentiate between the two polytypes of (Cu3TeO6)-Te-II-O-IV. In Raman spectroscopy, (Cu3TeO6)-Te-II-O-IV-1C has a single strong band around 730 cm(-1), whereas (Cu3TeO6)-Te-II-O-IV-2O shows a broad double maximum with bands centred around 692 and 742 cm(-1).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.9
DOI: 10.1107/S2052520621013032
|
|
|
“Synergy between transmission electron microscopy and powder diffraction : application to modulated structures”. Batuk D, Batuk M, Abakumov AM, Hadermann J, Acta crystallographica: section B: structural science 71, 127 (2015). http://doi.org/10.1107/S2052520615005466
Abstract: The crystal structure solution of modulated compounds is often very challenging, even using the well established methodology of single-crystal X-ray crystallography. This task becomes even more difficult for materials that cannot be prepared in a single-crystal form, so that only polycrystalline powders are available. This paper illustrates that the combined application of transmission electron microscopy (TEM) and powder diffraction is a possible solution to the problem. Using examples of anion-deficient perovskites modulated by periodic crystallographic shear planes, it is demonstrated what kind of local structural information can be obtained using various TEM techniques and how this information can be implemented in the crystal structure refinement against the powder diffraction data. The following TEM methods are discussed: electron diffraction (selected area electron diffraction, precession electron diffraction), imaging (conventional high-resolution TEM imaging, high-angle annular dark-field and annular bright-field scanning transmission electron microscopy) and state-of-the-art spectroscopic techniques (atomic resolution mapping using energy-dispersive X-ray analysis and electron energy loss spectroscopy).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.032
Times cited: 11
DOI: 10.1107/S2052520615005466
|
|
|
“Interstitial defects in the van der Waals gap of Bi2Se3”. Callaert C, Bercx M, Lamoen D, Hadermann J, Acta Crystallographica. Section B: Structural Science, Crystal Engineering and Materials (Online) 75, 717 (2019). http://doi.org/10.1107/S2052520619008357
Abstract: Bi<sub>2</sub>Se<sub>3</sub>is a thermoelectric material and a topological insulator. It is slightly conducting in its bulk due to the presence of defects and by controlling the defects different physical properties can be fine tuned. However, studies of the defects in this material are often contradicting or inconclusive. Here, the defect structure of Bi<sub>2</sub>Se<sub>3</sub>is studied with a combination of techniques: high-resolution scanning transmission electron microscopy (HR-STEM), high-resolution energy-dispersive X-ray (HR-EDX) spectroscopy, precession electron diffraction tomography (PEDT), X-ray diffraction (XRD) and first-principles calculations using density functional theory (DFT). Based on these results, not only the observed defects are discussed, but also the discrepancies in results or possibilities across the techniques. STEM and EDX revealed interstitial defects with mainly Bi character in an octahedral coordination in the van der Waals gap, independent of the applied sample preparation method (focused ion beam milling or cryo-crushing). The inherent character of these defects is supported by their observation in the structure refinement of the EDT data. Moreover, the occupancy probability of the defects determined by EDT is inversely proportional to their corresponding DFT calculated formation energies. STEM also showed the migration of some atoms across and along the van der Waals gap. The kinetic barriers calculated using DFT suggest that some paths are possible at room temperature, while others are most probably beam induced.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.032
DOI: 10.1107/S2052520619008357
|
|
|
“Crystallographic and magnetic structures of Y0.8Sr2.2Mn2GaO8-\delta: a new vacancy-ordered perovskite structure”. Gillie LJ, Palmer HM, Wright AJ, Hadermann J, Van Tendeloo G, Greaves C, The journal of physics and chemistry of solids 65, 87 (2004). http://doi.org/10.1016/j.jpcs.2003.08.012
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.059
Times cited: 15
DOI: 10.1016/j.jpcs.2003.08.012
|
|
|
“First-principles study of CO and OH adsorption on in-doped ZnO surfaces”. Saniz R, Sarmadian N, Partoens B, Batuk M, Hadermann J, Marikutsa A, Rumyantseva M, Gaskov A, Lamoen D, The journal of physics and chemistry of solids 132, 172 (2019). http://doi.org/10.1016/j.jpcs.2019.04.023
Abstract: We present a first-principles computational study of CO and OH adsorption on non-polar ZnO (10¯10) surfaces doped with indium. The calculations were performed using a model ZnO slab. The position of the In dopants was varied from deep bulk-like layers to
the surface layers. It was established that the preferential location of the In atoms is at the surface by examining the dependence of
the defect formation energy as well as the surface energy on In location. The adsorption sites on the surface of ZnO and the energy
of adsorption of CO molecules and OH-species were determined in connection to In doping. It was found that OH has higher
bonding energy to the surface than CO. The presence of In atoms at the surface of ZnO is favorable for CO adsorption, resulting
in an elongation of the C-O bond and in charge transfer to the surface. The effect of CO and OH adsorption on the electronic
and conduction properties of surfaces was assessed. We conclude that In-doped ZnO surfaces should present a higher electronic
response upon adsorption of CO.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 2.059
Times cited: 7
DOI: 10.1016/j.jpcs.2019.04.023
|
|
|
“Anisotropic magnetism and spin-dependent transport in Co nanoparticle embedded ZnO thin films”. Li DY, Zeng YJ, Pereira LMC, Batuk D, Hadermann J, Zhang YZ, Ye ZZ, Temst K, Vantomme A, Van Bael MJ, Van Haesendonck C;, Journal of applied physics 114, 033909 (2013). http://doi.org/10.1063/1.4815877
Abstract: Oriented Co nanoparticles were obtained by Co ion implantation in crystalline ZnO thin films grown by pulsed laser deposition. Transmission electron microscopy revealed the presence of elliptically shaped Co precipitates with nanometer size, which are embedded in the ZnO thin films, resulting in anisotropic magnetic behavior. The low-temperature resistance of the Co-implanted ZnO thin films follows the Efros-Shklovskii type variable-range-hopping. Large negative magnetoresistance (MR) exceeding 10% is observed in a magnetic field of 1 T at 2.5K and the negative MR survives up to 250K (0.3%). The negative MR reveals hysteresis as well as anisotropy that correlate well with the magnetic properties, clearly demonstrating the presence of spin-dependent transport. (C) 2013 AIP Publishing LLC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 10
DOI: 10.1063/1.4815877
|
|
|
“(Ba0.85Ca0.15)(Ti0.9Zr0.1)O3 thin films prepared by PLD : relaxor properties and complex microstructure”. Piorra A, Hrkac V, Wolff N, Zamponi C, Duppel V, Hadermann J, Kienle L, Quandt E, Journal of applied physics 125, 244103 (2019). http://doi.org/10.1063/1.5063428
Abstract: Ferroelectric lead-free thin films of the composition (Ba0.85Ca0.15)(Ti0.9Zr0.1)O-3 (BCZT) were deposited by pulsed laser deposition on Pt/TiO2/SiO2/Si substrates using a ceramic BCZT target prepared by a conventional solid state reaction. The target material itself shows a piezoelectric coefficient of d(33)=640pm/V. The (111) textured thin films possess a thickness of up to 1.1 mu m and exhibit a clamped piezoelectric response f of up to 190pm/V, a dielectric coefficient of (r)=2000 at room temperature, and a pronounced relaxor behavior. As indicated by transmission electron microscopy, the thin films are composed of longitudinal micrometersized columns with similar to 100nm lateral dimension that are separated at twin- and antiphase boundaries. The superposition phenomena according to this columnar growth were simulated based on suitable supercells. The major structural component is described as a tetragonal distorted variant of the perovskite parent type; however, frequently coherently intergrown nanodomains were observed indicating a much more complex structure that is characterized by a 7-layer modulation along the growth direction of the films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
DOI: 10.1063/1.5063428
|
|
|
“Gaining new insight into low-temperature aqueous photochemical solution deposited ferroelectric PbTiO3 films”. De Dobbelaere C, Lourdes Calzada M, Bretos I, Jimenez R, Ricote J, Hadermann J, Hardy A, Van Bael MK, Materials chemistry and physics 174, 28 (2016). http://doi.org/10.1016/J.MATCHEMPHYS.2016.02.047
Abstract: The nature of the low-temperature photochemical assisted formation process of ferroelectric lead titanate (PbTiO3) films is studied in the present work. Films are obtained by the deposition of an aqueous solution containing citric acid based (citrato) metal ion complexes with intrinsic UV activity. This UV activity is crucial for the aqueous photochemical solution deposition (aqueous PCSD) route being used. UV irradiation enhances the early decomposition of organics and results in improved electrical properties for the crystalline oxide film, even if the film is crystallized at low temperature. GATR-FTIR shows that UV irradiation promotes the decomposition of organic precursor components, resulting in homogeneous films if applied in the right temperature window during film processing. The organic content, morphology and crystallinity of the irradiated films, achieved at different processing atmospheres and temperatures, is studied and eventually correlated to the functional behavior of the obtained films. This is an important issue, as crystalline films obtained at low temperatures often lack ferroelectric responses. In this work, the film prepared in pure oxygen at the very low temperature of 400 degrees C and after an optimized UV treatment presents a significant remanent polarization value of P-r = 8.8 mu C cm(-2). This value is attributed to the better crystallinity, the larger grain size and the reduced porosity obtained thanks to the early film crystallization effectively achieved through the UV treatment in oxygen. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.084
Times cited: 4
DOI: 10.1016/J.MATCHEMPHYS.2016.02.047
|
|
|
“Anion ordering in fluorinated La2CuO4”. Abakumov AM, Hadermann J, Van Tendeloo G, Shpanchenko RV, Oleinikov PN, Antipov EV, Journal of solid state chemistry 142, 311 (1999). http://doi.org/10.1006/jssc.1998.8064
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 20
DOI: 10.1006/jssc.1998.8064
|
|
|
“B-site ordered perovskite LaSrMnNbO6 : synthesis, structure and antiferromagnetism”. Yang T, Perkisas T, Hadermann J, Croft M, Ignatov A, Greenblatt M, Journal of solid state chemistry 183, 2689 (2010). http://doi.org/10.1016/j.jssc.2010.08.041
Abstract: LaSrMnNbO6 has been synthesized by high temperature solid state reaction under 1% H2/Ar dynamic flow. The structure is determined by Rietveld refinement of the powder X-ray diffraction data. It crystallizes in the monoclinic space group P21/n with the unit cell parameters: a=5.69187(12), b=5.74732(10), c=8.07018(15) Å and β=90.0504(29)°, which were also confirmed by electron diffraction. The Mn2+ and Nb5+ ions, whose valence states are confirmed by X-ray absorption near-edge spectroscopy, are almost completely ordered over the B-site (<1% inversion) of the perovskite structure due to the large differences of both cationic size (0.19 Å) and charge. The octahedral framework displays significant tilting distortion according to Glazers tilt system a−b−c+. Upon heating, LaSrMnNbO6 decomposes at 690 °C under O2 flow or at 775 °C in air. The magnetic susceptibility data indicate the presence of long-range antiferromagnetic ordering at TN=8 K; the experimentally observed effective paramagnetic moment, μeff=5.76 μB for high spin Mn2+ (3d5, S=5/2) is in good agreement with the calculated value (μcalcd=5.92 μB).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 13
DOI: 10.1016/j.jssc.2010.08.041
|
|
|
“Coupled anion and cation ordering in Sr3RFe4O10.5 (R=Y, Ho, Dy) anion-deficientperovskites”. Abakumov AM, d' Hondt H, Rossell MD, Tsirlin AA, Gutnikova O, Filimonov DS, Schnelle W, Rosner H, Hadermann J, Van Tendeloo G, Antipov EV, Journal of solid state chemistry 183, 2845 (2010). http://doi.org/10.1016/j.jssc.2010.09.039
Abstract: The Sr3RFe4O10.5 (R=Y, Ho, Dy) anion-deficient perovskites were prepared using a solid-state reaction in evacuated sealed silica tubes. Transmission electron microscopy and 57Fe Mössbauer spectroscopy evidenced a complete A-cations and oxygen vacancies ordering. The structure model was further refined by ab initio structure relaxation, based on density functional theory calculations. The compounds crystallize in a tetragonal a≈2√2ap≈11.3 Å, с≈4сp≈16 Å unit cell (ap: parameter of the perovskite subcell) with the P42/mnm space group. Oxygen vacancies reside in the (FeO5/4□3/4) layers, comprising corner-sharing FeO4 tetrahedra and FeO5 tetragonal pyramids, which are sandwiched between the layers of the FeO6 octahedra. Smaller R atoms occupy the 9-fold coordinated position, whereas the 10-fold coordinated positions are occupied by larger Sr atoms. The Fe sublattice is ordered aniferromagnetically up to at least 500 K, while the rare-earth sublattice remains disordered down to 2 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1016/j.jssc.2010.09.039
|
|
|
“Crystal structure and magnetic properties of complex oxides Mg4-xNixO9, 0\leq x\leq4”. Tarakina NV, Nikulina EA, Hadermann J, Kellerman DG, Tyutunnik AP, Berger IF, Zubkov VG, Van Tendeloo G, Journal of solid state chemistry 180, 3180 (2007). http://doi.org/10.1016/j.jssc.2007.09.007
Abstract: In the Mg4−xNixNb2O9 (0x4) system two ranges of solid solution have been found. One of the solid solutions has a corundum-related structure type (space group ); the second one adopts the II-Ni4Nb2O9 structure type (space group Pbcn). The unit cell constants and atomic positions have been determined and refined using neutron powder diffraction data. Electron diffraction and high-resolution transmission electron microscopy (HRTEM) from MgNi3Nb2O9 crystals identify the presence of planar defects and the intergrowth of several (structurally related) phases. The magnetic susceptibility of Mg3NiNb2O9, measured in the temperature range T=2300 K, shows no indications of magnetic ordering at low temperatures, while for MgNi3Nb2O9 there is a magnetic ordering at temperatures below 45.5 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 3
DOI: 10.1016/j.jssc.2007.09.007
|
|
|
“Crystal structure and properties of the new vanadyl(IV)phosphates Na2MVO(PO4)2 M=Ca and Sr”. Chernaya VV, Tsirlin AA, Shpanchenko RV, Antipov EV, Gippius AA, Morozova EN, Dyakov V, Hadermann J, Kaul EE, Geibel C, Journal of solid state chemistry 177, 2875 (2004). http://doi.org/10.1016/j.jssc.2004.04.035
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 6
DOI: 10.1016/j.jssc.2004.04.035
|
|