“Effect of pretreatment and temperature on the properties of Pinnularia biosilica frustules”. Van Eynde E, Lenaerts B, Tytgat T, Verbruggen SW, Hauchecorne B, Blust R, Lenaerts S, RSC advances 4, 56200 (2014). http://doi.org/10.1039/C4RA09305D
Abstract: Diatoms are unicellular microalgae that self-assemble an intricate porous silica cell wall, called frustule. Diatom frustules possess a unique combination of physical and chemical properties (chemical inertness, high mechanical strength, large surface area, low density, good porosity and highly ordered features on the nano-to-micro scale) making diatom frustules suited for many nanotechnological applications. For most proposed applications the organic material covering the frustules needs to be removed. In this paper we investigate the effect of different frustule cleaning methods (drying, autoclavation, SDS/EDTA treatment, H2O2 treatment and HNO3 treatment) and subsequent heat treatment at different temperatures (105 °C, 350 °C, 550 °C and 750 °C) on the material characteristics of the diatom Pinnularia sp. Material characteristics under study are morphology, surface area, pore size, elemental composition and organic content. The cleaned Pinnularia frustules are subsequently investigated as adsorbents to remove methylene blue (MB) from aqueous solution.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 3.108
Times cited: 10
DOI: 10.1039/C4RA09305D
|
“Effect of van der Waals interactions on the adhesion strength at the interface of the hydroxyapatite-titanium biocomposite : a first-principles study”. Grubova IY, Surmeneva MA, Surmenev RA, Neyts EC, RSC advances 10, 37800 (2020). http://doi.org/10.1039/D0RA06006B
Abstract: Hydroxyapatite (HAP) is frequently used as biocompatible coating on Ti-based implants. In this context, the HAP-Ti adhesion is of crucial importance. Here, we report ab initio calculations to investigate the influence of Si incorporation into the amorphous calcium-phosphate (a-HAP) structure on the interfacial bonding mechanism between the a-HAP coating and an amorphous titanium dioxide (a-TiO2) substrate, contrasting two different density functionals: PBE-GGA, and DFT-D3, which are capable of describing the influence of the van der Waals (vdW) interactions. In particular, we discuss the effect of dispersion on the work of adhesion (W-ad), equilibrium geometries, and charge density difference (CDD). We find that replacement of P by Si in a-HAP (a-Si-HAP) with the creation of OH vacancies as charge compensation results in a significant increase in the bond strength between the coating and substrate in the case of using the PBE-GGA functional. However, including the vdW interactions shows that these forces considerably contribute to the W-ad. We show that the difference (W-ad – W-ad(vdW)) is on average more than 1.1 J m(-2) and 0.5 J m(-2) for a-HAP/a-TiO2 and a-Si-HAP/a-TiO2, respectively. These results reveal that including vdW interactions is essential for accurately describing the chemical bonding at the a-HAP/a-TiO2 interface.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
DOI: 10.1039/D0RA06006B
|
“Characterization and analysis of the adsorption immobilization mechanism of \beta-galactosidase on metal oxide powders”. Satyawali Y, Van Roy S, Roevens A, Meynen V, Mullens S, Jochems P, Doyen W, Cauwenberghs L, Dejonghe W, RSC advances 3, 24054 (2013). http://doi.org/10.1039/C3RA45107K
Abstract: Immobilization of the enzymes plays a vital role in enhancing their applicability in a wide range of applications, thus ensuring the use of sustainable enzymatic processes over the conventional chemical processes on an industrial scale. This study provides the background information for the selection and screening of inorganic metal oxide (MO) powders for their use as fillers in mixed matrix membranes for enzyme immobilization as the future aim. A total of 13 MOs, ranging in size from 0.01 μm to <5 μm, were tested for their performance as a support for enzyme (β-galactosidase) immobilization via adsorption. Alumina appeared to be the best performing MO with the amount and activity of the immobilized enzyme being 64 mg g−1 and up to 288 U g−1, respectively. The amount of immobilized enzyme on alumina (α-Al2O3 C and γ-Al2O3) was >3 times higher than ZrO2 (used as a reference MO in this study). Upon heat treatment at 900 °C, up to 15%, 52% and 42% decline was observed in the amount of immobilized enzyme in case of alumina metal oxides (MOs), ZrO2 and TiO2, respectively. The results suggested that both isoelectric point and surface area of the MO influence the immobilization. The most important observation in this study was that the bonding of the enzyme to the MO surface seems to be mediated by the bonding/interaction of the buffer to the enzyme.
Keywords: A1 Journal article; Laboratory of adsorption and catalysis (LADCA); Sustainable Energy, Air and Water Technology (DuEL)
DOI: 10.1039/C3RA45107K
|
“Optical-quality controllable wet-chemical doping of graphene through a uniform, transparent and low-roughness F4-TCNQ/MEK layer”. Misseeuw L, Krajewska A, Pasternak I, Ciuk T, Strupinski W, Reekmans G, Adriaensens P, Geldof D, Geldof D, Van Vlierberghe S, Thienpont H, Dubruelf P, Vermeulen N, RSC advances , 104491 (2016). http://doi.org/10.1039/C6RA24057G
Abstract: Controllable chemical doping of graphene has already proven very useful for electronic applications, but when turning to optical and photonic applications, the additional requirement of having both a high transparency and a low surface roughness has, to our knowledge, not yet been fulfilled by any chemical dopant system reported so far. In this work, a new method that meets for the first time this opticalquality requirement while also providing efficient, controllable doping is presented. The method relies on F4-TCNQ dissolved in methyl ethyl ketone (MEK) yielding a uniform deposition after spin coating because of an extraordinary charge transfer interaction between the F4-TCNQ and MEK molecules. The formed F4-TCNQ/MEK layer exhibits a very high surface quality and optical transparency over the visible-infrared wavelength range between 550 and 1900 nm. By varying the dopant concentration of F4-TCNQ from 2.5 to 40 mg ml1 MEK, the doping effect can be controlled between Dn ¼ +5.73 1012 cm2 and +1.09 1013 cm2 for initially strongly p-type hydrogen-intercalated graphene grown on 6Hsilicon- carbide substrates, and between Dn ¼ +5.56 1012 cm2 and +1.04 1013 cm2 for initially weakly p-type graphene transferred on silicon samples. This is the first time that truly optical-quality chemical doping of graphene is demonstrated, and the obtained doping values exceed those reported before for F4-TCNQ-based graphene doping by as much as 50%.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1039/C6RA24057G
|