Abstract: Control of the texture and the biaxial alignment of sputter deposited films has provoked a great deal of interest due to its technological importance. indeed, many physical properties of thin films are influenced by the biaxial alignment. In this context, extensive research has been established to understand the growth mechanism of biaxially aligned Yttria Stabilized Zirconia (YSZ) as a buffer layer for high temperature superconducting copper oxides. In this work, the growth mechanism in general and the mechanism responsible of the biaxial alignment in detail were investigated for thin films of YSZ and TiN deposited by unbalanced magnetron sputtering using non-aligned polycrystalline stainless steel substrates. The mechanism responsible for the preferential out-of-plane alignment has been investigated by performing depositions on a non-tilted substrate. However, to study the in-plane alignment a tilted substrate was used. The microstructure of the deposited layers was characterised by Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). The crystallographic alignment has been investigated by X-ray diffraction (XRD) (angular scans and pole figures) and by Selective Area Diffraction (SAD). It was observed that the deposited layers show a zone T or zone II structure and the layers with a zone T structure consist of faceted grains. There seems to be a correlation between the crystal habit of these faceted grains and the measured biaxial alignment. A model for the preferential out-of-plane orientation, the in-plane alignment and the correlation between the microstructure and the biaxial alignment is proposed.

Abstract: Nanocrystalline diamond films have generated much interested due to their diamond-like properties and low surface roughness. Several techniques have been used to obtain a high re-nucleation rate, such as hydrogen poor or high methane concentration plasmas. In this work, the properties of nano-diamond films grown on silicon substrates using a continuous DC bias voltage during the complete duration of growth are studied. Subsequently, the layers were characterised by several morphological, structural and optical techniques. Besides a thorough investigation of the surface structure, using SEM and AFM, special attention was paid to the bulk structure of the films. The application of FTIR, XRD, multi wavelength Raman spectroscopy, TEM and EELS yielded a detailed insight in important properties such as the amount of crystallinity, the hydrogen content and grain size. Although these films are smooth, they are under a considerable compressive stress. FTIR spectroscopy points to a high hydrogen content in the films, while Raman and EELS indicate a high concentration of sp2 carbon. TEM and EELS show that these films consist of diamond nano-grains mixed with an amorphous sp2 bonded carbon, these results are consistent with the XRD and UV Raman spectroscopy data.

Abstract: Infrared absorption spectra of oxygen precipitates in boron doped silicon with a boron concentration between 10(17) and 10(19) cm(-3) are analyzed, applying the spectral function theory of the composite precipitates. The aspect ratio of the platelet precipitates has been determined by transmission electron microscopy measurements. Our analysis shows that in samples with moderate doping levels (<10(18) B cm(-3)) SiOgamma precipitates are formed with stoichiometry as in the lightly doped case. In the heavily (>10(18) cm(-3)) boron doped samples, however, the measured spectra of the precipitates are consistent with a mixture of SiO2 and B2O3. with a volume fraction of B2O3 as high as 0.41 in the most heavily doped case.

Abstract: Rutherford backscattering and channeling spectrometry (RBS), photoluminescence (PL) spectroscopy and transmission electron microscopy (TEM) have been used to investigate macroscopic and microscopic segregation in MOCVD grown InGaN layers. The PL peak energy and In content (measured by RES) were mapped at a large number of distinct points on the samples. An indium concentration of 40%, the highest measured in this work, corresponds to a PL peak of 710 nn strongly suggesting that the light-emitting regions of the sample me very indium-rich compared to the average measured by RES. Cross-sectional TEM observations show distinctive layering of the InGaN films. The TEM study further reveals that these layers consist of amorphous pyramidal contrast features with sizes of order 10 nm The composition of these specific contrast features is shown to be In-rich compared to the nitride matrix.