Abstract: (Sr1-xCax)(33)Bi-24,partial derivative Al48O141+3 partial derivative/2 fullerenoid solid solutions have been synthesized and the effect of partial substitution of Sr by Ca has been characterized by (scanning) transmission electron microscopy, applying different imaging methods. Most of the defects commonly observed in face centered cubic compounds, have also been observed in (Sr1-xCax)(33)Bi24-partial derivative Al48O141+3 partial derivative/2. Based on purely geometrical and topological models, structural presentations for the coherent twin boundaries and stacking faults have been constructed on the basis of complex spherical “Al84O210” units. The results are compared to defects observed in the crystallite fullerite C-60.

Abstract: Transmission electron microscopy and X-ray diffraction proved chain/ladder incommensurate single crystal structure of investigated samples. The incommensurate ratio was determined from the X-ray and electron diffraction being equal to 0.704. Diffuse scattering intensities localised on the planes perpendicular to the c*-axis and passing through the spots originating from the periodicity of chain sublattice were detected. High-angle grain boundary or twinning formed by rotation of 33.3 degrees around [100] direction was observed. High-resolution electron microscopy images revealed the stacking faults in ac planes.

Abstract: Control of the texture and the biaxial alignment of sputter deposited films has provoked a great deal of interest due to its technological importance. indeed, many physical properties of thin films are influenced by the biaxial alignment. In this context, extensive research has been established to understand the growth mechanism of biaxially aligned Yttria Stabilized Zirconia (YSZ) as a buffer layer for high temperature superconducting copper oxides. In this work, the growth mechanism in general and the mechanism responsible of the biaxial alignment in detail were investigated for thin films of YSZ and TiN deposited by unbalanced magnetron sputtering using non-aligned polycrystalline stainless steel substrates. The mechanism responsible for the preferential out-of-plane alignment has been investigated by performing depositions on a non-tilted substrate. However, to study the in-plane alignment a tilted substrate was used. The microstructure of the deposited layers was characterised by Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). The crystallographic alignment has been investigated by X-ray diffraction (XRD) (angular scans and pole figures) and by Selective Area Diffraction (SAD). It was observed that the deposited layers show a zone T or zone II structure and the layers with a zone T structure consist of faceted grains. There seems to be a correlation between the crystal habit of these faceted grains and the measured biaxial alignment. A model for the preferential out-of-plane orientation, the in-plane alignment and the correlation between the microstructure and the biaxial alignment is proposed.

Abstract: The highly porous and desolvated (activated) coordination polymer [Zn4O(btb)2] (btb = benzene-1,3,5-tribenzoate; MOF-177) was loaded with the organometallic compounds [Cp2Fe], [Cp*2Zn], [Cu(OCHMeCH2NMe2)2], [CpCuL] (L = PMe3, CNtBu) and [CpPd(3-C3H5)] via solvent-free adsorption from the gas-phase. The inclusion compounds of the type [LnM]a@MOF-177, where [LnM] indicates the respective compound and the parameter a denotes the number of molecules per formula unit of the MOF-177, were characterised by elemental analysis, FT-IR, solid-state NMR spectroscopy and by powder X-ray diffraction (PXRD). Remarkably high effective loadings of up to 11 molecules [Cp2Fe] and 10 molecules [CpPd(3-C3H5)] per cavity were determined. The analytical data prove that the host lattice and the guest molecules interact only by weak van-der-Waals forces without any significant change of the framework or the chemical nature of the included molecules. Cu nanoparticles showing the typical surface plasmon resonance at 580 nm and Pd nanoparticles of about 2.6 nm in size were formed inside the cavities of MOF-177 by the thermally activated hydrogenolysis of the inclusion compounds [CpCuCNtBu]2@MOF-177 and by photolysis of [CpPd(3-C3H5)]10@MOF-177 in an inert atmosphere (Ar). PXRD, FT-IR and NMR studies revealed that the MOF-177 matrix remained unchanged during the decomposition process of the precursors. N2 adsorption studies of the obtained materials Cu@MOF-177 (e.g. 10.6 wt.% Cu, 2309 m2 g-1) and Pd@MOF-177 (e.g. 32.5 wt.%, 1063 m2 g-1) reveal high remaining specific surface areas (Langmuir model).

Abstract: This work focuses on the use of tailored copper oxide nanoarchitectures as multi-functional materials for the sustainable production of hydrogen and its on-line detection. An innovative copper(II) precursor, Cu(hfa)2TMEDA, was adopted in the CVD of CuxO (x=1,2) nanosystems under both O2 and O2+H2O atmospheres on Si(100) and Al2O3 substrates. A multi-technique characterization indicates that both the phase composition (from Cu2O to CuO) and morphology (from continuous films to entangled quasi-1D nanosystems) can be tailored by varying the growth temperature and reaction atmosphere. The obtained CuxO nanodeposits are active in the photocatalytic H2 production from aqueous solutions under UV-Vis irradiation and display interesting gas sensing performances towards hydrogen detection even at moderate temperatures.

Abstract: Monolithic nickel/carbon (Ni/C) composites were prepared from coal tar pitch-impregnated compressed expanded graphite pre-decorated with NiO particles (EGNiO) by pyrolysis at 550 °C and subsequent steam activation at 800 °C. The microstructural arrangement of the Ni-comprising nanoparticles in the composites was investigated using transmission electron microscopy. The specific surface area and porosity of the composites were analyzed by nitrogen adsorption. The catalytic activity of the composites was compared with the material obtained by the conventional H2 treatment of EGNiO using hydrocracking of 2,2,3-trimethylpentane as a model reaction.

Abstract: The limitations of the loading of the porous metalorganic framework [Zn4O(bdc)3] (bdc = benzene-1,4-dicarboxylate; MOF-5 or IRMOF-1) with Pd nanoparticles was investigated. First, the volatile organometallic precursor [Pd(5-C5H5)(3-C3H5)] was employed to get the inclusion compound [Pd(5-C5H5)(3-C3H5)]x@MOF-5 via gas-phase infiltration at 10-3 mbar. A loading of four molecules of [Pd(5-C5H5)(3-C3H5)] per formula unit of MOF-5 (x = 4) can be reached (35 wt.% Pd). Second, the metalorganic precursor [Pd(acac)2] (acac = 2,4-pentanedionate) was used and the inclusion materials [Pd(acac)2]x@MOF-5 of different Pd loadings were obtained by incipient wetness infiltration. However, the maximum loading was lower as compared with the former case with about two precursor molecules per formula unit of MOF-5. Both loading routes are suitable for the synthesis of Pd nanoparticles inside the porous host matrix. Homogeneously distributed nanoparticles with diameter of 2.4(±0.2) nm can be achieved by photolysis of the inclusion compounds [Pd(5-C5H5)(3-C3H5)]x@MOF-5 (x 4), while the hydrogenolysis of [Pd(acac)2]x@MOF-5 (x 2) leads to a mixture of small particles inside the network (< 3 nm) and large Pd agglomerates (40 nm) on the outer surface of the MOF-5 specimens. The pure Pdx@MOF-5 materials proved to be stable under hydrogen pressure (2 bar) at 150 °C over many hours. Neither hydrogenation of the bdc linkers nor particle growth was observed. The new composite materials were characterized by 1H/13C-MAS-NMR, powder XRD, ICP-AES, FT-IR, N2 sorption measurements and high resolution TEM. Raising the Pd loading of a representative sample Pd4@MOF-5 (35 wt.% Pd) by using [Pd(5-C5H5)(3-C3H5)] as precursor in a second cycle of gas-phase infiltration and photolysis was accompanied by the collapse of the long-range crystalline order of the MOF.