“Characterization of IASCC crack tips extracted from neutron-irradiated flux thimble tube specimens in view of a probabilistic fracture model”. Penders AG, Konstantinović, MJ, Van Renterghem W, Bosch R-W, Schryvers D, Somville F, Journal of nuclear materials 571, 154015 (2022). http://doi.org/10.1016/J.JNUCMAT.2022.154015
Abstract: This study reports the properties of irradiation assisted stress corrosion crack tips extracted by means of focused-ion beam from 60 to 80 dpa neutron-irradiated O-ring specimens tested under straining conditions under a pressurized-water reactor environment. Various crack tip morphologies and surrounding deformation features were analyzed as a function of applied stress, surface oxidation state and loading form – constant versus cyclic. All investigated cracks exhibit grain boundary oxidation in front of the crack tip, with the extent of oxidation being proportional to applied stress. These findings clearly demonstrate that, under the subcritical crack propagation regime, the grain boundary oxide grows faster than the crack. On the other hand, crack tips appertaining to specimens with removed oxide layer at the outer surface show comparatively less oxidation at the crack tip, which could indicate towards crack initiation from regions that exemplify lower stress, such as the O-ring inner surface. Cyclic loading is found to have a more pronounced effect on the crack tip microstructure, demonstrating increased deformation twinning and -martensitic transformation, which signifies towards an increased susceptibility to intergranular failure. Still, the extent of crack tip grain boundary oxidation in this case agrees well with expected values for maximum stress applied during cyclic loading. All results are interpreted based on the probabilistic subcritical crack propagation mechanism and provide strong support to a stress-driven internal oxidation model.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.1
DOI: 10.1016/J.JNUCMAT.2022.154015
|
|
|
“K₅Eu(MoO₄)₄, red phosphor for solid state lighting applications, prepared by different techniques”. Posokhova SMM, Morozov VA, Deyneko DVV, Redkin BSS, Spassky DAA, Nagirnyi V, Belik AAA, Hadermann J, Pavlova ETT, Lazoryak BII, CrystEngComm 25, 835 (2023). http://doi.org/10.1039/D2CE01107G
Abstract: The influence of preparation techniques on the structure and luminescent properties of K5Eu(MoO4)(4) (KEMO) was investigated. KEMO phosphors were synthesized by three different techniques: solid state and sol-gel (sg) methods as well as the Czochralski (CZ) crystal growth technique. Laboratory powder X-ray diffraction (PXRD) studies revealed that all KEMO samples had a structure analogous to that of other high temperature alpha-K5R(MoO4)(4) palmierite-type phases (space group (SG) R3m). Contrary to laboratory PXRD data, electron diffraction revealed that the KEMO crystal grown by the CZ technique had a (3 + 1)D incommensurately modulated structure (super space group (SSG) C2/m(0 beta 0)00) with the modulation vector q = 0.689b*. A detailed analysis of electron diffraction patterns has shown formation of three twin domains rotated along the c axis of the R-subcell at 60 degrees with respect to each other. Synchrotron XRD patterns showed additional ultra-wide reflexes in addition to reflections of the R-subcell of the palmierite. However, the insufficient number of reflections, their low intensity and large width in the synchrotron X-ray diffraction patterns made it impossible to refine the structure as incommensurately modulated C2/m(0 beta 0)00. An average structure was refined in the C2/m space group with random distribution of K1 and Eu1 in [M1A(2)O(8)]-layers of the palmierite-type structure. The dependence of luminescent properties on utilized synthesis techniques was studied. The emission spectra of all samples exhibit intense red emission originating from the D-5(0) -> F-7(2) Eu3+ transition. The integrated intensity of the emission from the Eu3+ 5D0 term was found to be the highest in the crystal grown by the CZ technique. The quantum yield measured for KEMO crystals demonstrates a very high value of 66.5%. This fact confirms that KEMO crystals are exceptionally attractive for applications as a near-UV converting red phosphor for LEDs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.1
DOI: 10.1039/D2CE01107G
|
|
|
“Ab initio study of the adsorption of O, O2, H2O and H2O2 on UO2 surfaces using DFT+U and non-collinear magnetism”. Arts I, Saniz R, Baldinozzi G, Leinders G, Verwerft M, Lamoen D, Journal of Nuclear Materials 599, 155249 (2024). http://doi.org/10.1016/j.jnucmat.2024.155249
Abstract: In order to model correctly the corrosion of spent nuclear fuel under disposal conditions, it is important to understand its behavior in the presence of oxidants. To advance in this direction, we consider the oxidation of UO2. We investigate computationally the adsorption of various species on its three most stable surfaces: (111), (110), and (100), with emphasis on incorporating a full non-collinear PBE+U approach. Various species, namely O, O2, H2O and H2O2 are considered due to their relevance for the oxidation of UO2. The dissociation energy and an estimate for the dissociation barrier for O2 were obtained, using the preferred adsorption configurations of O and O2. The adsorption configurations for H2O in our study compare well with previous studies that used collinear approximations, both in terms of relative stability of configurations and bond lengths. Differences in adsorption energies were found, which may be important for reaction kinetics. Dissociative reactions in which the water molecule splits in hydrogen and hydroxyl occur only on one of the three surfaces. The hydrogen further reacts with a surface oxygen to also form a hydroxyl group. Not surprisingly, we find that H2O2 binds more strongly to the three surfaces than water (lower formation energy), and similar to H2O adsorption, dissociative reactions may occur. The dissociated hydrogen reacts with a surface oxygen to form a hydroxyl group and the hydroperoxyl molecule binds with a surface uranium. Our study, which includes a detailed study of electron transfer, magnetic structure and the preferred adsorption configurations, gives insight into the uranium oxidation states and the influence of surface geometry on adsorption. The findings contribute to a more comprehensive understanding of the early stages of UO2 oxidation.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 3.1
DOI: 10.1016/j.jnucmat.2024.155249
|
|
|
“Applications of advanced transmission electron microscopic techniques to Ni-Ti based shape memory materials”. Schryvers D, Potapov P, Santamarta R, Tirry W, Materials science and engineering: part A: structural materials: properties, microstructure and processing 378, 11 (2004). http://doi.org/10.1016/j.msea.2003.10.325
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 6
DOI: 10.1016/j.msea.2003.10.325
|
|
|
“Au particles supported on (110) anatase-TiO2”. Giorgio S, Henry CR, Pauwels B, Van Tendeloo G, Microstructure And Processing 297, 197 (2001). http://doi.org/10.1016/S0921-5093(00)01261-2
Abstract: Au particles were prepared by evaporation in ultra high vacuum at high temperature, on the surfaces of TiO2 micro-spheres with the anatase structure. The morphology and the structural deformation in Au deposits were studied by high resolution transmission electron microscopy and image simulations by the multislice technique. The particles were polyhedral, limited by (100) and (111) faces. Patches with a hexagonal lattice were found around the particles, which was interpreted as thin Au islands on the surface. In these islands the Au lattice was deformed and perfectly accommodated to the (110) surface of TiO2. (C) 2001 Elsevier Science B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 40
DOI: 10.1016/S0921-5093(00)01261-2
|
|
|
“Effect of annealing on cold-rolled Ni-Ti alloys”. Srivastava AK, Yang Z, Schryvers D, van Hurnbeeck J, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 594 (2008). http://doi.org/10.1016/j.msea.2006.12.216
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 8
DOI: 10.1016/j.msea.2006.12.216
|
|
|
“Electron energy-loss spectroscopy study of NiTi shape memory alloys”. Yang ZQ, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 214 (2008). http://doi.org/10.1016/j.msea.2006.12.227
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 7
DOI: 10.1016/j.msea.2006.12.227
|
|
|
“Hardening in relation with microstructure evolution of high purity \alpha-titanium deformed under monotonic and cyclic simple shear loadings at room temperature”. Bouvier S, Benmhenni N, Tirry W, Gregory F, Nixon ME, Cazacu O, Rabet L, Materials science and engineering: part A: structural materials: properties, microstructure and processing 535, 12 (2012). http://doi.org/10.1016/j.msea.2011.12.033
Abstract: The aim of this paper is to gain understanding of the quasi-static, large strain deformation behavior at room-temperature of high-purity alpha-Ti with an initial split-basal texture. Simple shear tests were conducted along different directions in order to quantify the material's anisotropy and hardening evolution for different strain paths such as monotonic, Bauschinger, and cyclic loadings. The stress-strain curves indicate that the material displays strong anisotropy in the flow behavior. In order to capture the link between microstructure evolution (occurrence of twinning, grain size evolution, etc.) and the macroscopic response, a thoroughly detailed multi-scale characterization using scanning electron microscope (SEM) observations and electron backscattered diffraction (EBSD) analysis was also conducted. Specifically, EBSD analyses indicate that the twin activity and grain fragmentation are responsible for the observed difference between the macroscopic hardening rates corresponding to different directions and loading paths. (C) 2011 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 22
DOI: 10.1016/j.msea.2011.12.033
|
|
|
“High resolution TEM study of Ni4Ti3 precipitates in austenitic Ni51Ti49”. Tirry W, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 378, 157 (2004). http://doi.org/10.1016/j.msea.2003.10.336
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 19
DOI: 10.1016/j.msea.2003.10.336
|
|
|
“Importance of twinning in static and dynamic compression of a Ti-6Al-4V titanium alloy with an equiaxed microstructure”. Coghe F, Tirry W, Rabet L, Schryvers D, Van Houtte P, Materials science and engineering: part A: structural materials: properties, microstructure and processing 537, 1 (2012). http://doi.org/10.1016/j.msea.2011.12.047
Abstract: Whereas deformation twinning is known to be an important deformation mechanism for hexagonal materials like magnesium and pure titanium, so far almost no literature exists on the twinning behaviour of the Ti-6Al-4V alloy. In this work it was shown that the activation of twinning as a deformation mechanism could have a pronounced effect on the mechanical behaviour of the Ti-6Al-4V alloy. This effect is even more pronounced under dynamic loading conditions. Transmission electron microscopy showed that only the {1 0 1 2}{1 0 1 1} tensile twin system was activated under certain loading conditions. Light-optical microscopy and electron backscatter diffraction data were afterwards used to experimentally determine the twin fractions. The importance of twinning for the texture evolution was also studied. It was shown that even small twin fractions can lead to distinct texture features, especially due to the discrete reorientation of the c-axes. The experimental results were compared to simulated results that were obtained with a viscoplastic self-consistent crystal plasticity code, after experimental validation that twinning can be reliably modelled as a unidirectional slip system. Although good agreement was obtained for the experimental and simulated stress-strain curves, the simulated results concerning twinning correlated well only on a qualitative basis as the simulated twin fractions were systematically higher than the experimental fractions. This seems to strengthen the hypothesis made by other research groups that complete grains might reorient by twinning. (C) 2011 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 35
DOI: 10.1016/j.msea.2011.12.047
|
|
|
“In situ transmission electron microscopy of stress-induced martensite with focus on martensite twinning”. Tirry W, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 420 (2008). http://doi.org/10.1016/j.msea.2006.12.214
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 22
DOI: 10.1016/j.msea.2006.12.214
|
|
|
“Martensitic transformations and microstructures in splat-cooled Ni-Al”. Schryvers D, Holland-Moritz D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 273/275, 697 (1999). http://doi.org/10.1016/S0921-5093(99)00399-8
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 6
DOI: 10.1016/S0921-5093(99)00399-8
|
|
|
“Measuring strain fields and concentration gradients around Ni4Ti3 precipitates”. Schryvers D, Tirry W, Yang ZQ;, Materials science and engineering A: structural materials properties microstructure and processing 438, 485 (2006). http://doi.org/10.1016/j.msea.2006.02.166
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 35
DOI: 10.1016/j.msea.2006.02.166
|
|
|
“A multi-scale characterization of deformation twins in Ti6Al4V sheet material deformed by simple shear”. Tirry W, Coghe F, Bouvier S, Gasperini M, Rabet L, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 527, 4136 (2010). http://doi.org/10.1016/j.msea.2010.03.039
Abstract: Ti6Al4V sheet material is subjected to simple shear deformation with strain ratio's of 10%, 30% and 50%. Optical microscopy, transmission electron microscopy and electron backscatter diffraction techniques are applied to study the presence and morphology of deformation twins. Only the View the MathML source type of twins seems to be present with a volume fraction below 1%. These View the MathML source twins show a high density of basal stacking faults of the ABABACAC type identified using atomic resolution transmission electron microscopy. A resolved shear stress analysis shows that twins most often occur on those planes with the highest resolved shear stresses, but that the starting texture is not beneficial for the occurrence of twins. It is further suggested that a transitory strain hardening regime observed around 530 MPa might be related with the onset of twinning.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 20
DOI: 10.1016/j.msea.2010.03.039
|
|
|
“New (3(3)under-bar) long-period microtwin variant in the martensitic phase of the PtTi alloy”. Rotaru G-M, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 437 (2008). http://doi.org/10.1016/j.msea.2006.12.201
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 3
DOI: 10.1016/j.msea.2006.12.201
|
|
|
“Quantitative determination of the crystal structure of Ni4Ti3 precipitates”. Tirry W, Schryvers D, Jorissen K, Lamoen D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 438, 517 (2006). http://doi.org/10.1016/j.msea.2006.02.063
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 7
DOI: 10.1016/j.msea.2006.02.063
|
|
|
“Structure of multi-grain spherical particles in an amorphous Ti50Ni25Cu25 melt-spun ribbon”. Santamarta R, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 378, 143 (2004). http://doi.org/10.1016/j.msea.2003.11.060
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 5
DOI: 10.1016/j.msea.2003.11.060
|
|
|
“Clustering behavior during natural aging and artificial aging in Al-Mg-Si alloys with different Ag and Cu addition”. Weng Y, Jia Z, Ding L, Muraishi S, Liu Q, Microstructure And Processing 732, 273 (2018). http://doi.org/10.1016/J.MSEA.2018.07.018
Abstract: The effect of Ag and Cu addition on clustering behavior of Al-Mg-Si alloys during natural aging (NA) and artificial aging (AA) was investigated by hardness measurement, tensile test and atom probe tomography analysis. The results show that both Ag and Cu atoms could enter clusters and GP-zones, change the Mg/Si ratio and increase their volume fractions. Compared with the Al base alloy, the clusters in the Ag/Cu-added alloys more easily transform to beta" phases for size and compositional similarity, and the strengthening ability of these particles is enhanced by the increased volume fraction and shear modulus. In NA condition, Cu is greater in improving the volume fraction of clusters than Ag and thus produces higher T4 temper hardness. In AA condition, in contrary, Ag is more effective in facilitating the formation and growth of particles than Cu due to the stronger Ag-Mg interaction and the high diffusivity of Ag atoms in Al matrix, leading to highest hardening response. Compared to the Cu-added alloy, the Ag-added alloy shows higher precipitation kinetics during AA treatment and maintains a lower T4 temper hardness.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 11
DOI: 10.1016/J.MSEA.2018.07.018
|
|
|
“Enhancement of toughness of Al-to-steel Friction Melt Bonded welds via metallic interlayers”. Jimenez-Mena N, Jacques PJ, Ding L, Gauquelin N, Schryvers D, Idrissi H, Delannay F, Simar A, Materials science and engineering: part A: structural materials: properties, microstructure and processing 740-741, 274 (2019). http://doi.org/10.1016/j.msea.2018.10.101
Abstract: The toughness of Al-to-steel welds decreases with increasing thickness of the intermetallic (IM) layer formed at the interface. Co plating has been added as interlayer in Al-to-steel Friction Melt Bonded (FMB) welds to control the nature and thickness of the IM layer. In comparison to a weld without interlayer, Co plating brings about a reduction of the thickness of the IM layer by 70%. The critical energy release rate of the crack propagating in the weld is used as an indicator of toughness. It is evaluated via an adapted crack propagation test using an energy conservation criterion. For a weld without interlayer, critical energy release rate is found to increase when the thickness of the intermetallic layer decreases. When the intermetallic layer is thick, the crack propagates in a brittle manner through the intermetallic whereas, at low layer thickness, the crack deviates and partially propagates through the Al plate, which causes an increase of toughness. The use of a Co interlayer brings about an increase of toughness by causing full deviation of the crack towards the Al plate.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 4
DOI: 10.1016/j.msea.2018.10.101
|
|
|
“Damage mechanisms in selective laser melted AlSi10Mg under as built and different post-treatment conditions”. Zhao L, Macias JGS, Ding L, Idrissi H, Simar A, Microstructure And Processing 764, 138210 (2019). http://doi.org/10.1016/J.MSEA.2019.138210
Abstract: Selective laser melting (SLM) manufactured AlSi10Mg alloys present a fine silicon-rich network and precipitates which grant high mechanical strength but low ductility. Post-treatments, aiming at eliminating inherent defects related to SLM such as residual stresses, porosity or inhomogeneity, result in significant changes in the microstructure and impact both the hardening and the damage mechanisms of the post-treated material. The present work is dedicated to the investigation of the fracture of SLM AlSi10Mg under as built and three post-treatment conditions, namely two stress relieve heat treatments and friction stir processing (FSP). It is found that the interconnected Si network fosters damage at low strain due to the brittleness of the Si phase. The onset of damage transfers load to the enclosed Al phase which then fractures quickly under high stress, thus leading to low material ductility. In contrast, when the Si network is globularized into Si particles, the ductility is highly increased even in the case where the porosity and inhomogeneity of the microstructure remain after the post-treatment. The ductility enhancement results from the delay in void nucleation on the Si particles as well as from the tolerance for void growth in the Al matrix.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 1
DOI: 10.1016/J.MSEA.2019.138210
|
|
|
“On the Origin of Damped Electrochemical Oscillations at Silicon Anodes (Revisited)”. Proost J, Blaffart F, Turner S, Idrissi H, ChemPhysChem : a European journal of chemical physics and physical chemistry 15, 3116 (2014). http://doi.org/10.1002/cphc.201402207
Abstract: Electrochemical oscillations accompanying the formation of anodic silica have been shown in the past to be correlated with rather abrupt changes in the mechanical stress state of the silica film, commonly associated with some kind of fracture or porosification of the oxide. To advance the understanding on the origin of such oscillations in fluoride-free electrolytes, we have revisited a seminal experiment reported by Lehmann almost two decades ago. We thereby demonstrate that the oscillations are not stress-induced, and do not originate from a morphological transformation of the oxide in the course of anodisation. Alternatively, the mechanical features accompanying the oscillations can be explained by a partial relaxation of the field-induced electrostrictive stress. Furthermore, our observations suggest that the oscillation mechanism more likely results from a periodic depolarisation of the anodic silica.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 5
DOI: 10.1002/cphc.201402207
|
|
|
“Rational design of Ag/TiO2 nanosystems by a combined RF-sputtering/sol-gel approach”. Armelao L, Barreca D, Bottaro G, Gasparotto A, Maccato C, Tondello E, Lebedev OI, Turner S, Van Tendeloo G, Štangar UL, ChemPhysChem : a European journal of chemical physics and physical chemistry 10, 3249 (2009). http://doi.org/10.1002/cphc.200900571
Abstract: The present work is devoted to the preparation of Ag/TiO2 nanosystems by an original synthetic strategy, based on the radio-frequency (RF) sputtering of silver particles on titania-based xerogels prepared by the sol-gel (SG) route. This approach takes advantage of the synergy between the microporous xerogel structure and the infiltration power characterizing RF-sputtering, whose combination enables the obtainment of a tailored dispersion of Ag-containing particles into the titania matrix. In addition, the systems chemico-physical features can be tuned further through proper ex situ thermal treatments in air at 400 and 600 °C. The synthesized composites are extensively characterized by the joint use of complementary techniques, that is, X-ray photoelectron and X-ray excited Auger electron spectroscopies (XPS, XE-AES), secondary ion mass spectrometry (SIMS), glancing incidence X-ray diffraction (GIXRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), electron diffraction (ED), high-angle annular dark field scanning TEM (HAADF-STEM), energy-filtered TEM (EF-TEM) and optical absorption spectroscopy. Finally, the photocatalytic performances of selected samples in the decomposition of the azo-dye Plasmocorinth B are preliminarily investigated. The obtained results highlight the possibility of tailoring the system characteristics over a broad range, directly influencing their eventual functional properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 56
DOI: 10.1002/cphc.200900571
|
|
|
“The role of oxygen at the interface between titanium and carbon nanotubes”. Felten A, Suarez-Martinez I, Ke X, Van Tendeloo G, Ghijsen J, Pireaux J-J, Drube W, Bittencourt C, Ewels CP, ChemPhysChem : a European journal of chemical physics and physical chemistry 10, 1799 (2009). http://doi.org/10.1002/cphc.200900193
Abstract: We study the interface between carbon nanotubes (CNTs) and surface-deposited titanium using electron microscopy and photoemission spectroscopy, supported by density functional calculations. Charge transfer from the Ti atoms to the nanotube and carbide formation is observed at the interface which indicates strong interaction. Nevertheless, the presence of oxygen between the Ti and the CNTs significantly weakens the Ti-CNT interaction. Ti atoms at the surface will preferentially bond to oxygenated sites. Potential sources of oxygen impurities are examined, namely oxygen from any residual atmosphere and pre-existing oxygen impurities on the nanotube surface, which we enhance through oxygen plasma surface pre-treatment. Variation in literature data concerning Ohmic contacts between Ti and carbon nanotubes is explained via sample pre-treatment and differing vacuum levels, and we suggest improved treatment routes for reliable Schottky barrier-free Ti-nanotube contact formation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 38
DOI: 10.1002/cphc.200900193
|
|
|
“Spectroscopy and defect identification for fluorinated carbon nanotubes”. Bittencourt C, van Lier G, Ke X, Suarez-Martinez I, Felten A, Ghijsen J, Van Tendeloo G, Ewels CO, ChemPhysChem : a European journal of chemical physics and physical chemistry 10, 920 (2009). http://doi.org/10.1002/cphc.200800851
Abstract: Multi-wall carbon nanotubes (MWCNTs) were exposed to a CF4 radio-frequency (rf) plasma. High-resolution photoelectron spectroscopy shows that the treatment effectively grafts fluorine atoms onto the MWCNTs, altering the valence electronic states. Fluorine surface concentration can be tuned by varying the exposure time. Evaporation of gold onto MWCNTs is used to mark active site formation. High-resolution transmission electron microscopy coupled with density functional theory (DFT) modelling is used to characterise the surface defects formed, indicating that the plasma treatment does not etch the tube surface. We suggest that this combination of theory and microscopy of thermally evaporated gold atoms onto the CNT surface may be a powerful approach to characterise both surface defect density as well as defect type.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 14
DOI: 10.1002/cphc.200800851
|
|
|
“ZnO nanorod arrays by plasma-enhanced CVD for light-activated functional applications”. Bekermann D, Gasparotto A, Barreca D, Devi A, Fischer RA, Kete M, Štangar UL, Lebedev OI, Maccato C, Tondello E, Van Tendeloo G, ChemPhysChem : a European journal of chemical physics and physical chemistry 11, 2337 (2010). http://doi.org/10.1002/cphc.201000333
Abstract: Switch of the surface properties: Supported ZnO nanorod arrays with tailored roughness and aspect ratios are successfully synthesized by plasma-enhanced chemical vapor deposition. Such nanostructures exhibit significant superhydrophilic and photocatalytic properties tunable as a function of their morphological organization (see picture). This renders them promising building blocks for the fabrication of stimuli-responsive materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 38
DOI: 10.1002/cphc.201000333
|
|
|
“Substitutional phosphorus incorporation in nanocrystalline CVD diamond thin films”. Janssen W, Turner S, Sakr G, Jomard F, Barjon J, Degutis G, Lu YG, D'Haen J, Hardy A, Bael MV, Verbeeck J, Van Tendeloo G, Haenen K, Physica status solidi: rapid research letters 8, 705 (2014). http://doi.org/10.1002/pssr.201409235
Abstract: Nanocrystalline diamond (NCD) thin films were produced by chemical vapor deposition (CVD) and doped by the addition of phosphine to the gas mixture. The characterization of the films focused on probing the incorporation and distribution of the phosphorus (P) dopants. Electron microscopy evaluated the overall film morphology and revealed the interior structure of the nanosized grains. The homogeneous films with distinct diamond grains featured a notably low sp(2):sp(3)-ratio as confirmed by Raman spectroscopy. High resolution spectroscopy methods demonstrated a homogeneous P-incorporation, both in-depth and in-plane. The P concentration in the films was determined to be in the order of 10(19) cm(-3) with a significant fraction integrated at substitutional donor sites. (C) 2014 WILEY-VCH Verlag GmbH Co. KGaA, Weinheim
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.032
Times cited: 20
DOI: 10.1002/pssr.201409235
|
|
|
“Stabilization of the Perovskite Phase in the Y-Bi-O System By Using a BaBiO3 Buffer Layer”. Bouwmeester RL, de Hond K, Gauquelin N, Verbeeck J, Koster G, Brinkman A, Physica Status Solidi-Rapid Research Letters 13, 1970028 (2019). http://doi.org/10.1002/pssr.201970028
Abstract: A topological insulating phase has theoretically been predicted for the thermodynamically unstable perovskite phase of YBiO3. Here, it is shown that the crystal structure of the Y-Bi-O system can be controlled by using a BaBiO3 buffer layer. The BaBiO3 film overcomes the large lattice mismatch with the SrTiO3 substrate by forming a rocksalt structure in between the two perovskite structures. Depositing an YBiO3 film directly on a SrTiO3 substrate gives a fluorite structure. However, when the Y–Bi–O system is deposited on top of the buffer layer with the correct crystal phase and comparable lattice constant, a single oriented perovskite structure with the expected lattice constants is observed.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 3.032
DOI: 10.1002/pssr.201970028
|
|
|
“Fabrication, microstructure, and enhanced thermionic electron emission properties of vertically aligned nitrogen-doped nanocrystalline diamond nanorods”. Sankaran KJ, Deshmukh S, Korneychuk S, Yeh C-J, Thomas JP, Drijkoningen S, Pobedinskas P, Van Bael MK, Verbeeck J, Leou K-C, Leung K-T, Roy SS, Lin I-N, Haenen K, MRS communications 8, 1311 (2018). http://doi.org/10.1557/MRC.2018.158
Abstract: Vertically aligned nitrogen-doped nanocrystalline diamond nanorods are fabricated from nitrogen-doped nanocrystalline diamond films using reactive ion etching in oxygen plasma. These nanorods show enhanced thermionic electron emission (TEE) characteristics, viz.. a high current density of 12.0 mA/cm(2) and a work function value of 4.5 eV with an applied voltage of 3 Vat 923 K. The enhanced TEE characteristics of these nanorods are ascribed to the induction of nanographitic phases at the grain boundaries and the field penetration effect through the local field enhancement from nanorods owing to a high aspect ratio and an excellent field enhancement factor.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.01
Times cited: 1
DOI: 10.1557/MRC.2018.158
|
|
|
“Identification of nano-width variants in a fully monoclinic martensitic Ni50Ti50 alloy by scanning electron microscope-based transmission Kikuchi diffraction and improved groupoid structure approach”. Zhao ZX, Ma X, Cao S, Li YY, Zeng CY, Wang DX, Yao X, Deng ZJ, Zhang XP, Materials Letters 281, 128624 (2020). http://doi.org/10.1016/J.MATLET.2020.128624
Abstract: Nano-width martensite plates in a fully martensitic Ni50Ti50 alloy are indexed successfully by using the off-axis transmission Kikuchi diffraction in scanning electron microscope (i.e., SEM-based TKD). The data obtained by SEM-TKD are effectively interpreted using an improved approach based on the framework of the theoretical groupoid structure method, where the equivalent variants transformed from the monoclinic variants are introduced to calculate all theoretical axis/angle pairs of rotation, and to formulate a complete list of source martensite to target martensite pairs. Consequently, B19' monoclinic martensite variants in NiTi alloys are identified unambiguously, by using numerical comparison between the experimental and theoretical rotation components, without the reference of retained parent phase. (C) 2020 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3
DOI: 10.1016/J.MATLET.2020.128624
|
|
|
“Genomic oropharyngeal Neisseria surveillance detects MALDI-TOF MS species misidentifications and reveals a novel Neisseria cinerea clade”. de Block T, De Baetselier I, Van den Bossche D, Abdellati S, Gestels Z, Laumen JGE, Van Dijck C, Vanbaelen T, Claes N, Vandelannoote K, Kenyon C, Harrison O, Santhini Manoharan-Basil S, Journal of Medical Microbiology 73 (2024). http://doi.org/10.1099/jmm.0.001871
Abstract: Introduction. Commensal Neisseria spp. are highly prevalent in the oropharynx as part of the healthy microbiome. N. meningitidis can colonise the oropharynx too from where it can cause invasive meningococcal disease. To identify N. meningitidis, clinical microbiology laboratories often rely on Matrix Assisted Laser Desorption/Ionisation Time of Flight Mass Spectrometry (MALDI-TOF MS).
Hypothesis/Gap statement. N. meningitidis may be misidentified by MALDI-TOF MS.
Aim. To conduct genomic surveillance of oropharyngeal Neisseria spp. in order to: (i) verify MALDI-TOF MS species identification, and (ii) characterize commensal Neisseria spp. genomes.
Methodology. We analysed whole genome sequence (WGS) data from 119 Neisseria spp. isolates from a surveillance programme for oropharyngeal Neisseria spp. in Belgium. Different species identification methods were compared: (i) MALDI-TOF MS, (ii) Ribosomal Multilocus Sequence Typing (rMLST) and (iii) rplF gene species identification. WGS data were used to further characterize Neisseria species found with supplementary analyses of Neisseria cinerea genomes.
Results. Based on genomic species identification, isolates from the oropharyngeal Neisseria surveilence study were composed of the following species: N. meningitidis (n=23), N. subflava (n=61), N. mucosa (n=15), N. oralis (n=8), N. cinerea (n=5), N. elongata (n=3), N. lactamica (n=2), N. bacilliformis (n=1) and N. polysaccharea (n=1). Of these 119 isolates, four isolates identified as N. meningitidis (n=3) and N. subflava (n=1) by MALDI-TOF MS, were determined to be N. polysaccharea (n=1), N. cinerea (n=2) and N. mucosa (n=1) by rMLST. Phylogenetic analyses revealed that N. cinerea isolates from the general population (n=3, cluster one) were distinct from those obtained from men who have sex with men (MSM, n=2, cluster two). The latter contained genomes misidentified as N. meningitidis using MALDI-TOF MS. These two N. cinerea clusters persisted after the inclusion of published N. cinerea WGS (n=42). Both N. cinerea clusters were further defined through pangenome and Average Nucleotide Identity (ANI) analyses.
Conclusion. This study provides insights into the importance of genomic genus-wide Neisseria surveillance studies to improve the characterization and identification of the Neisseria genus.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 3
DOI: 10.1099/jmm.0.001871
|
|