Abstract: Results are presented on the photoluminescence (PL) characterization of heavily doped p(+) Czochralski silicon, which has been subjected to a two-step, oxygen precipitation heat treatment. It will be shown that the presence of oxygen precipitates gives rise to the D1, D2 and D5 lines, where the energy of the D1 line shifts to lower values for a stronger degree of precipitation. The occurrence of these PL features is also a function of the boron concentration in the p(+) material. The PL results are compared with Fourier transform infrared absorption data and with transmission electron microscope, results. From this, it is concluded that PL has a good potential for use in the assessment of oxygen precipitation in heavily doped silicon.

Abstract: The main results and conclusions are presented of a round robin study of silicon oxide on silicon reference samples for ellipsometry. The oxide films with nominal thicknesses of 10, 50 and 120 nm are grown by thermal oxidation. The oxide film thicknesses have been determined by single wavelength ellipsometry (SWE), by spectroscopic ellipsometry (SE) and by cross-sectional conventional and high-resolution transmission electron microscopy (TEM and HREM) in different laboratories. The main conclusions are that special precautions have to be taken in order to use TEM as a reliable thickness measurement technique; that single wavelength ellipsometry can be used with great accuracy and reproducibility for the 50 and 120 nm film thicknesses but that it shows some inherent problems for the 10 nm films; and that spectroscopic ellipsometry showed for all film thicknesses an accuracy and reproducibility which is clearly superior to that of SWE.

Abstract: An alternative pathway to assemble mesoporous molecular sieve silicas is developed using nonionic alkylamines and N,N-dimethylalkylamines (SO) as structure-directing agents in acidic conditions. The synthesized mesostructures possess wormhole-like frameworks with pore sizes and pore volumes in the range of 20-90 Angstrom and 0.5-1.3 cm(3)/g, respectively. The formation of the mesophase is controlled by a counterion-mediated mechanism of the type (S(0)H(+))(X(-)I(+)), where S(0)H(+) are protonated water molecules that are hydrogen bonded to the lone electron pairs on the amine surfactant headgroups (S(0)H(+)), X(-) is the counteranion originating from the acid, and I(+) are the positively charged (protonated) silicate species. We found that the stronger the ion X(-) is bonded to S(0)H(+), the more it catalyzes the silica condensation into (S(0)H(+))(X(-)I(+)). Br(-) is shown to be a strong binding anion and therefore a fast silica polymerization promoter compared to Cl(-) resulting in the formation of a higher quality mesophase for the Br(-) syntheses. We also showed that the polymerization rate of the silica, dictated by the counterion, controls the morphology of the mesostructures from nonuniform agglomerated blocks in the case of Br(-) syntheses to spherical particles for the Cl(-) syntheses. Next to many benefits such as low temperature, short synthesis time, and the use of inexpensive, nontoxic, and easily extractable amine templates, the developed materials have a remarkable higher thermal and hydrothermal stability compared to hexagonal mesoporous silica, which is also prepared with nonionic amines but formed through the S(0)I(0) mechanism.

Abstract: Infrared absorption spectra of oxygen precipitates in boron-doped silicon with a boron concentration between 10(17) and 10(19) cm(-3) are analyzed, applying the spectral function representation of composite materials. The aspect ratio of the platelet precipitates is determined by transmission electron microscopy measurements. The analysis shows that in samples with moderate doping levels (<10(18) B cm(-3)) SiOγ precipitates are formed with the same composition as in the lightly doped case. In the heavily boron-doped (>10(18) cm(-3)) samples, however, the measured spectra of the precipitates are consistent with a mixture of SiO2 and B2O3, with a volume fraction of B2O3 as high as 0.41 in the most heavily doped case. (C) 2004 The Electrochemical Society.

Abstract: We report a direct observation of quantum dots formed spontaneously in a thick InGaN epilayer by high resolution transmission electron microscopy. Investigation of a (280 nm thick) In0.22Ga0.78N single layer, emitting in the blue/green spectral region, reveals quantum dots with estimated sizes in the range of 1.5-3 nm. Such sizes are in very good agreement with calculations based on the luminescence spectra of this specimen. (C) 2000 American Institute of Physics. [S0003-6951(00)00930-X].

Abstract: CeO2-doped ZrO2, (8 mol%) starting powder was sintered by means of spark plasma sintering (SPS) at 1300 degrees C without holding time. The stability of the tetragonal ZrO2 phase in the Ce-ZrO2 ceramic sintered under strongly reducing conditions was investigated. The SPS sample consisted of monoclinic and tetragonal ZrO2 phase, with a volume ratio of two to one, as well as a trace amount of a Zr-Ce-O cubic solid solution phase. In contrast, the same powder sintered by hot-pressing in nitrogen at 1300 and 1500 degrees C for 1h showed no tetragonal ZrO2. Microstructural observation of the SPS ceramic by SEM and TEM revealed grains with and without twins. The reason for the appearance of the tetragonal phase in the SPS sample sintered under strongly reducing conditions is discussed. (c) 2004 Elsevier Ltd. All rights reserved.

Abstract: Pure and Nb-doped TiO2 thick-films were prepared by screen-printing, starting from nanosized powders. Grain growth and crystalline phase modification occurred as consequence of firing at high temperature. It has been shown that niobium addition inhibits grain coarsening and hinders anatase-to-rutile phase transition. These semiconducting films exhibited n-type behavior, while Nb acted as donor-dopant. Gas measurements demonstrated that the films are suitable for CO or NO2 sensing. Microstructural characterization by electron microscopy and differential thermal analysis (DTA) highlights the dependence of gas-sensing behavior on film's properties. (C) 2000 Elsevier Science S.A. All rights reserved.