“Multistep loading of titania nanoparticles in the mesopores of SBA-15 for enhanced photocatalytic activity”. de Witte K, Cool P, de Witte I, Ruys L, Rao J, Van Tendeloo G, Vansant EF, Journal of nanoscience and nanotechnology 7, 2511 (2007). http://doi.org/10.1166/jnn.2007.445
Keywords: A1 Journal article; Laboratory of adsorption and catalysis (LADCA); Electron microscopy for materials research (EMAT)
Impact Factor: 1.483
Times cited: 13
DOI: 10.1166/jnn.2007.445
|
|
|
“Influence of the synthesis parameters of TiO2-SBA-15 materials on the adsorption and photodegradation of rhodamine-6G”. de Witte K, Busuioc AM, Meynen V, Mertens M, Bilba N, Van Tendeloo G, Cool P, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 110, 100 (2008). http://doi.org/10.1016/j.micromeso.2007.09.035
Keywords: A1 Journal article; Laboratory of adsorption and catalysis (LADCA); Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 54
DOI: 10.1016/j.micromeso.2007.09.035
|
|
|
“Zn-Al layered double hydroxides: synthesis, characterization and photocatalytic application”. Seftel EM, Popovici E, Mertens M, de Witte K, Van Tendeloo G, Cool P, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 113, 296 (2008). http://doi.org/10.1016/j.micromeso.2007.11.029
Keywords: A1 Journal article; Laboratory of adsorption and catalysis (LADCA); Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 154
DOI: 10.1016/j.micromeso.2007.11.029
|
|
|
“Combined TiO2/SiO2 mesoporous photocatalysts with location and phase controllable TiO2 nanoparticles”. Beyers E, Biermans E, Ribbens S, de Witte K, Mertens M, Meynen V, Bals S, Van Tendeloo G, Vansant EF, Cool P, Applied catalysis : B : environmental 88, 515 (2009). http://doi.org/10.1016/j.apcatb.2008.10.009
Abstract: Combined TiO2/SiO2 mesoporous materials were prepared by deposition of TiO2 nanoparticles synthesised via the acid-catalysed solgel method. In the first synthesis step a titania solution is prepared, by dissolving titaniumtetraisopropoxide in nitric acid. The influences of the initial titaniumtetraisopropoxide concentration and the temperature of dissolving on the final structural properties were investigated. In the second step of the synthesis, the titania nanoparticles were deposited on a silica support. Here, the influence of the temperature during deposition was studied. The depositions were carried out on two different mesoporous silica supports, SBA-15 and MCF, leading to substantial differences in the catalytic and structural properties. The samples were analysed with N2-sorption, X-ray diffraction (XRD), electron probe microanalysis (EPMA) and transmission electron microscopy (TEM) to obtain structural information, determining the amount of titania, the crystal phase and the location of the titania particles on the mesoporous material (inside or outside the mesoporous channels). The structural differences of the support strongly determine the location of the nanoparticles and the subsequent photocatalytic activity towards the degradation of rhodamine 6G in aqueous solution under UV irradiation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 9.446
Times cited: 69
DOI: 10.1016/j.apcatb.2008.10.009
|
|
|
“Multi-step loading of titania on mesoporous silica: influence of the morphology and the porosity on the catalytic degradation of aqueous pollutants and VOC's”. de Witte K, Meynen V, Mertens M, Lebedev OI, Van Tendeloo G, Sepúlveda-Escribano A, Rodríguez-Reinoso F, Vansant EF, Cool P, Applied catalysis : B : environmental 84, 125 (2008). http://doi.org/10.1016/j.apcatb.2008.03.015
Abstract: Titania nanoparticles have been deposited on inert porous silica supports with high specific surface area. These materials have potential applications in paint and textile industry as the titania particles selectively deposited on the inner surface of the silica supports act as a photocatalyst. The inert external surface is necessary to avoid photodegradation of the textile material or the paint components. The photocatalytic activity of the catalysts has been evaluated with two catalytic setups. One setup in aqueous phase, for the degradation of dyes such as rhodamine-6G, is commonly used. The second setup is a continuous flow gaseous phase setup which was used for the mineralization of ethanol as a representative volatile organic compound (VOC). The influence of the porosity and the morphology of the silica supports on the photocatalytic activity are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 9.446
Times cited: 24
DOI: 10.1016/j.apcatb.2008.03.015
|
|