“The identification of chromophores in ancient glass by the use of UV-VIS-NIR spectroscopy”. Meulebroeck W, Baert K, Wouters H, Cosyns P, Ceglia A, Cagno S, Janssens K, Nys K, Terryn H, Thienpont H, Proceedings of the Society of Photo-optical Instrumentation Engineers 7726, 77260d (2010). http://doi.org/10.1117/12.853666
Abstract: In this publication optical spectroscopy is considered to be a supplementary technique to study ancient colored glass. It results from a systematic study of the UV-VIS-NIR transmission spectra of intentionally colored glass fragments from various archaeological and historical sites and dated from the Roman period to the 21th century AD. The main goal consists of defining optical sensing parameters for this type of material. The considered colorants are iron, cobalt, manganese, copper and chromium. It is proved that many cases exist where optical spectroscopy can be seen as a straightforward, non-destructive, low-cost and in-situ applicable technique in identifying authentic material or to obtain information about the origin of the material. Possible sensing parameters are defined as the absence/presence of absorption bands characteristic for a specific coloring metal oxide and the spectral position of these bands. These parameters could reveal information about the applied furnace conditions and/or to the composition of the glass matrix. It is shown that the cobalt absorption band situated around 535 nm for soda rich glasses (Roman and industrial times) is shifted towards 526 nm for potash rich glasses (medieval and post-medieval times).
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Times cited: 10
DOI: 10.1117/12.853666
|
|
|
“Corrosion protection of Cu by atomic layer deposition”. Cremers V, Rampelberg G, Baert K, Abrahami S, Claes N, de Oliveira TM, Terryn H, Bals S, Dendooven J, Detavernier C, Journal of vacuum science and technology: A: vacuum surfaces and films 37, 060902 (2019). http://doi.org/10.1116/1.5116136
Abstract: Atomic layer deposition (ALD) is a vapor phase technique that is able to deposit uniform, conformal thin films with an excellent thickness control at the atomic scale. 18 nm thick Al2O3 and TiO2 coatings were deposited conformaly and pinhole-free onto micrometer-sized Cu powder, using trimethylaluminum and tetrakis(dimethylamido)titanium(IV), respectively, as a precursor and de-ionized water as a reactant. The capability of the ALD coating to protect the Cu powder against corrosion was investigated. Therefore, the stability of the coatings was studied in solutions with different pH in the range of 0–14, and in situ raman spectroscopy was used to detect the emergence of corrosion products of Cu as an indication that the protective coating starts to fail. Both ALD coatings provide good protection at standard pH values in the range of 5–7. In general, the TiO2 coating shows a better barrier protection against corrosion than the Al2O3 coating. However, for the most extreme pH conditions, pH 0 and pH 14, the TiO2 coating starts also to degrade.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.374
Times cited: 7
DOI: 10.1116/1.5116136
|
|
|
“A XANES study of chromophores : the case of black glass”. Ceglia A, Nuyts G, Cagno S, Meulebroeck W, Baert K, Cosyns P, Nys K, Thienpont H, Janssens K, Terryn H, Analytical methods 6, 2662 (2014). http://doi.org/10.1039/C3AY42029A
Abstract: We studied the Fe K-edge X-ray absorption near edge (XANES) spectra of several Roman black glass fragments in order to determine the Fe3+/ΣFe ratio of these materials. The selected archaeological glass samples cover the period 1st5th century AD in nine different sites of the North Western provinces of the Roman Empire. The fragments belong to two different compositional groups demonstrating a diachronic evolution: early Roman HMG (High Magnesia Glass) and Roman Imperial LMG (Low Magnesia Glass). The first group contains natural Fe levels (below 2 wt% as Fe2O3), while the LMG has concentrations above 5 wt%. This difference is also reflected by Fe3+/ΣFe values. Low iron glass was produced under strongly reducing conditions in order to obtain the black colour, with average Fe3+/ΣFe values ≈ 0.17. LMG glass is somewhat more oxidised (Fe3+/ΣFe ≈ 0.40.5). While HMG glass required active control of the furnace environment, LMG was made under ambient atmosphere and its higher oxidation degree is mainly determined by the chemistry of the raw glass.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.9
Times cited: 14
DOI: 10.1039/C3AY42029A
|
|
|
“Optical spectroscopy as a rapid and low-cost tool for the first-line analysis of glass artefacts : a step-by-step plan for Roman green glass”. Meulebroeck W, Cosyns P, Baert K, Wouters H, Cagno S, Janssens K, Terryn H, Nys K, Thienpont H, Journal of archaeological science 38, 2387 (2011). http://doi.org/10.1016/J.JAS.2011.04.023
Abstract: Archaeometric research on glass artefacts is continuously evolving and is converging towards a multidisciplinary research domain where different types of techniques are applied depending on the questions asked and the circumstances involved. The technique described in this work is optical spectroscopy. The benefit of this technique being the possibility of building up a knowledge database for a large amount of material in a relatively short period of time and with a relatively limited budget. This is of particular interest for the investigation of extensive and/or unexplored glass collections where a first-line analysis of artefacts could facilitate the selection of material needing further and more detailed examination. This publication explores the extent to which optical spectroscopy can be used for a first-line analysis of green coloured glass artefacts from the Roman period. It is shown that the colour coordinates calculated from the measured transmission spectrum could reveal information about the fragment under study. In particular it is shown that 1) based on the position of the calculated colour values on the colour diagram (CIE1931) one could easily know whether the artefact was coloured using only iron or if copper oxides were also present. In the case of the artefact owing its colour solely to the presence of iron, the distance between the measured colour values and the colour diagrams white point can roughly indicate the iron concentration of the sample; 2) artefacts that were fabricated under similar furnace conditions can also be identified on the colour diagram; 3) samples with identical compositions and fabrication conditions but with different sample thickness, gave rise to a variation in the colour coordinates, thus allowing optical spectroscopy to help identify fragments which might belong to the same object.
Keywords: A1 Journal article; Engineering sciences. Technology; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.602
Times cited: 18
DOI: 10.1016/J.JAS.2011.04.023
|
|
|
“Deposition of aminosilane coatings on porous Al2O3microspheres by means of dielectric barrier discharges”. Garzia Trulli M, Claes N, Pype J, Bals S, Baert K, Terryn H, Sardella E, Favia P, Vanhulsel A, Plasma processes and polymers 14, 1600211 (2017). http://doi.org/10.1002/ppap.201600211
Abstract: Advances in the synthesis of porous microspheres and in their functionalization are increasing the interest in applications of alumina. This paper deals with coatings plasma deposited from 3-aminopropyltriethoxysilane by means of dielectric barrier discharges on alumina porous microspheres, shaped by a vibrational droplet coagulation technique. Aims of the work are the functionalization of the particles with active amino groups, as well as the evaluation of their surface coverage and of the penetration of the coatings into their pores. A multi-diagnostic approach was used for the chemical/morphological characterization of the particles. It was found that 5 min exposure to plasma discharges promotes the deposition of homogeneous coatings onto the microspheres and within their pores, down to 1 μm.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.846
Times cited: 8
DOI: 10.1002/ppap.201600211
|
|
|
“Use of nanoscale carbon layers on Ag-based gas diffusion electrodes to promote CO production”. Pacquets L, Van den Hoek J, Arenas Esteban D, Ciocarlan R-G, Cool P, Baert K, Hauffman T, Daems N, Bals S, Breugelmans T, ACS applied nano materials 5, 7723 (2022). http://doi.org/10.1021/ACSANM.2C00473
Abstract: A promising strategy for the inhibition of the hydrogen evolution reaction along with the stabilization of the electrocatalyst in electrochemical CO2 reduction cells involves the application of a nanoscale amorphous carbon layer on top of the active catalyst layer in a gas diffusion electrode. Without modifying the chemical nature of the electrocatalyst itself, these amorphous carbon layers lead to the stabilization of the electrocatalyst, and a significant improvement with respect to the inhibition of the hydrogen evolution reaction was also obtained. The faradaic efficiencies of hydrogen could be reduced from 31.4 to 2.1% after 1 h of electrolysis with a 5 nm thick carbon layer. Furthermore, the impact of the carbon layer thickness (5–30 nm) on this inhibiting effect was investigated. We determined an optimal thickness of 15 nm where the hydrogen evolution reaction was inhibited and a decent stability was obtained. Next, a thickness of 15 nm was selected for durability measurements. Interestingly, these durability measurements revealed the beneficial impact of the carbon layer already after 6 h by suppressing the hydrogen evolution such that an increase of only 37.9% exists compared to 56.9% without the use of an additional carbon layer, which is an improvement of 150%. Since carbon is only applied afterward, it reveals its great potential in terms of electrocatalysis in general.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 5.9
Times cited: 3
DOI: 10.1021/ACSANM.2C00473
|
|
|
“Synthesis &ndash, properties correlation and the unexpected role of the titania support on the Grignard surface modification”. Van Dijck JG, Mampuys P, Ching HYV, Krishnan D, Baert K, Hauffman T, Verbeeck J, Van Doorslaer S, Maes BUW, Dorbec M, Buekenhoudt A, Meynen V, Applied Surface Science 527, 146851 (2020). http://doi.org/10.1016/J.APSUSC.2020.146851
Abstract: While the impact of reaction conditions on surface modification with Grignard reactants has been studied for silica supports, such information is absent for metal oxides like titania. Differences between modified titania and silica are observed, making it paramount to explore the reaction mechanism. A detailed study on the impact of the reaction conditions is reported, with a focus on the chain length of the alkyl Grignard reactant, its concentration, the reaction time and temperature, and the type of titania support. While the increase in the chain length reduces the amount of organic groups on the surface, the concentration, time and temperature show little/no influence on the modification degree. However, the type of titania support used and the percentage of amorphous phase present has a significant impact on the amount of grafted groups. Even though the temperature and concentration show no clear impact on the modification degree, they can cause changes in the surface hydroxyl population, which are thus not linked to the modification degree. Furthermore, the titania support is reduced during functionalization. This reduction dependents on the reaction temperature, the titania support and the chain length of the Grignard reactant. Similarly, this reduction is not linked to the modification degree.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 6.7
Times cited: 5
DOI: 10.1016/J.APSUSC.2020.146851
|
|
|
“Mapping composition–selectivity relationships of supported sub-10 nm Cu–Ag nanocrystals for high-rate CO₂, electroreduction”. Choukroun D, Pacquets L, Li C, Hoekx S, Arnouts S, Baert K, Hauffman T, Bals S, Breugelmans T, Acs Nano 15, 14858 (2021). http://doi.org/10.1021/ACSNANO.1C04943
Abstract: Colloidal Cu–Ag nanocrystals measuring less than 10 nm across are promising candidates for integration in hybrid CO2 reduction reaction (CO2RR) interfaces, especially in the context of tandem catalysis and selective multicarbon (C2–C3) product formation. In this work, we vary the synthetic-ligand/copper molar ratio from 0.1 to 1.0 and the silver/copper atomic ratio from 0 to 0.7 and study the variations in the nanocrystals’ size distribution, morphology and reactivity at rates of ≥100 mA cm–2 in a gas-fed recycle electrolyzer operating under neutral to mildly basic conditions (0.1–1.0 M KHCO3). High-resolution electron microscopy and spectroscopy are used in order to characterize the morphology of sub-10 nm Cu–Ag nanodimers and core–shells and to elucidate trends in Ag coverage and surface composition. It is shown that Cu–Ag nanocrystals can be densely dispersed onto a carbon black support without the need for immediate ligand removal or binder addition, which considerably facilitates their application. Although CO2RR product distribution remains an intricate function of time, (kinetic) overpotential and processing conditions, we nevertheless conclude that the ratio of oxygenates to hydrocarbons (which depends primarily on the initial dispersion of the nanocrystals and their composition) rises 3-fold at moderate Ag atom % relative to Cu NCs-based electrodes. Finally, the merits of this particular Cu–Ag/C system and the recycling reactor employed are utilized to obtain maximum C2–C3 partial current densities of 92–140 mA cm–2 at −1.15 VRHE and liquid product concentrations in excess of 0.05 wt % in 1 M KHCO3 after short electrolysis periods.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 13.942
Times cited: 25
DOI: 10.1021/ACSNANO.1C04943
|
|