Abstract: The post-growth modification of diamond-like amorphous hydrogenated carbon a-C:H films by laser treatment has been studied by transmission electron microscopy and Raman spectroscopy. a-C:H films grown on Si substrates by benzene decomposition in a rf glow discharge were irradiated with 15 ns pulses of a KrF-excimer laser with fluences in the ran e of E = 50-700 mJ/cm(2). At fluences below 100 mJ/cm(2) an increase in the number of graphitic clusters and in their ordering was evidenced from Raman spectra, while the film structure remained amorphous according to electron microscopy and electron diffraction observations. At higher fluences the appearance of diamond particles of 2-7 nm size, embedded into the lower crystallized graphitic matrix, was observed and simultaneously a progressive growth of graphite nanocrystals with dimensions from 2 nm to 4 nm was deduced from Raman measurements. The maximum thickness of the crystallized surface layer (approximate to 400 nm) and the degree of laser annealing are limited by the film ablation which starts at E > 250 mJ/cm(2). The laser-treated areas lose their chemical inertness. In particular, chemical etching in chromium acid becomes possible, which may be used for patterning the highly inert carbon films.

Abstract: The structure of Fe/GaN/Fe ferromagnetic electrodes is studied by high resolution transmission electron microscopy. The layers grow epitaxially on the GaAs substrate with the top Fe layer 90degrees rotated compared to the bottom one. The interfaces are quite rough. There is an indication of the possible occurrence of Fe3GaAs formation on the GaAs interface.

Abstract: The thermal stability of amorphous Al2O3 films (similar to8 and 80 nut thick) deposited by atomic layer deposition on HF-last and thin SiO2 covered (001) Si substrates is studied by transmission electron microscopy. The layers are in- and ex-situ annealed in the same temperature range.

Abstract: ZnO is a wide band-gap (ca. 3.4 eV) semiconductor, piezoelectric, pyroelectric, biocompatible, transparent in the visible spectrum and UV light emitting material. The fabrication in 2001 of the first nanobelts of semiconductor oxide materials lead to a rapid expansion of researches concerning one dimensional nanostructures (nanotubes, nanowires, nanobelts), given their possible application in optics, optoelectronics, piezoelectricity, catalysis. Researches carried on up to date evidenced the possibility to obtain an extraordinary variety of ZnO nanostructures, in function of the experimental parameters and the used growth methods. In this work we present morphostructural results on nanostructured ZnO layers obtained by electrochemical deposition. The films have been grown on gold covered glass plates and Si wafers, in various experimental conditions such as: nature of the wetting agents, electrical polarization of the substrate (continuous, pulsed). The influence of the growth conditions on the crystalline structure and morphology of the films is revealed by scanning and transmission electron microscopy studies. The films show a variety of growth morphologies, from entangled-wires-like to honeycomb-like layers. These large-specific-surface layers will be tested as nanostructured substrates for photovoltaic cells with improved efficiency.

Abstract: A Ti target was submitted to laser ablation in low ambient pressure N-2. Electron microscopy examination of the cross-section of the crater zone forming on the Ti target, and XPS analyses, indicate that there is a small effect on the nitridation processes taking place on and in the vicinity of the target. The studies show a zone influenced by the multipulse laser treatment extending beneath the crater down to a depth of the same order of magnitude as the crater depth (i.e. similar to 10 mu m). In this zone, TiN could be identified as being present only in traces, while the whole zone exhibited a layer structure with differences in morphology and mechanical wear.