Abstract: The stress corrosion cracking (SCC) mechanism is investigated in high Si duplex stainless steel in a simulated PWR environment based on TEM analysis of FIB-extracted SCC crack tips. The microstructural investigation in the near vicinity of SCC crack tips illustrates a strain-rate dependence in SCC mechanisms. Detailed analysis of the crack tip morphology, that includes crack tip oxidation and surrounding deformation field, indicates the existence of an interplay between corrosion- and deformation-driven failure as a function of the strain rate. Slow strain-rate crack tips exhibit a narrow cleavage failure which can be linked to the film-induced failure mechanism, while rounded shaped crack tips for faster strain rates could be related to the strain-induced failure. As a result, two nominal strain-rate-dependent failure regimes dominated either by corrosion or deformation-driven cracking mechanisms can be distinguished.

Abstract: This study investigates farmers' preferences and willingness to pay for cropland attributes in Bahir Dar, north-west Ethiopia. A choice experiment is used to elicit farmers' preferences between different land use attributes, including a monetary attribute. The study was conducted in the croplands that are threatened by land expro-priation for urban expansion. A survey was undertaken with 144 farmers in four rural kebeles surrounding the city (Addis Alem, Weramit, Wereb and Zenzelima). In the survey, respondents were provided with hypothetical land purchasing decisions, with three alternatives (i.e., two hypothetical parcels and an opt-out option). A choice experiment was undertaken to measure farmers' interest in different types of croplands, which varies with respect to irrigability, number of trees per ha, soil erosion resistance and water holding capacity of the cropland. Estimation of two mixed logit models was carried out. The estimation results show that, although the farmers did not show strong preferences for each attribute of the cropland, many farmers in the area showed interest in the proposed alternative croplands. Farmers show more interest for the land that is irrigable, gentle slope and with medium water holding capacity. The results also indicate that farmers assign highest marginal willingness to pay (MWTP) (79.01 ETB per square meter) for irrigated land, followed by medium water holding capacity with MWTP of 52.13 ETB per square meter. We believe that the results of this study would help land use policy and decision makers in the study area to consider the various attributes of cropland in land use planning, including land expropriation programs, which assures the sustainability of ecosystem services.

Abstract: The interface-dependent electronic, vibrational, piezoelectric, and optical properties of van der Waals heterobilayers, formed by buckled GeO (b-GeO) and Janus MoSO structures, are investigated by means of first-principles calculations. The electronic band dispersions show that O/Ge and S/O interface formations result in a type-II band alignment with direct and indirect band gaps, respectively. In contrast, O/O and S/Ge interfaces give rise to the formation of a type-I band alignment with an indirect band gap. By considering the Bethe-Salpeter equation (BSE) on top of G(0)W(0) approximation, it is shown that different interfaces can be distinguished from each other by means of the optical absorption spectra as a consequence of the band alignments. Additionally, the low- and high-frequency regimes of the Raman spectra are also different for each interface type. The alignment of the individual dipoles, which is interface-dependent, either weakens or strengthens the net dipole of the heterobilayers and results in tunable piezoelectric coefficients. The results indicate that the possible heterobilayers of b-GeO/MoSO asymmetric structures possess various electronic, optical, and piezoelectric properties arising from the different interface formations and can be distinguished by means of various spectroscopic techniques.

Abstract: Sulfur hexafluoride (SF6), as a man-made gas, is widely used in power industry, semiconductor industry and metal-processing industry. However, SF6 is a greenhouse gas and its global warming potential is 23500 times that of CO2. Besides, SF6 is very stable, with a lifetime in the atmosphere for more than one thousand years. Under natural conditions, only the ultraviolet light can make it slowly decomposed. Thus, the emission of SF6 has a great threat to the environment. In recent years, with the development of our national economy, the use of SF6 increased dramatically. And 90% of the SF6 emissions come from the power industry. In the meantime, the emission of SF6 exists a ‘hysteresis effect’, as many of the SF6-gas insulation equipment will retire in next decades, the emission of SF6 may increase sharply, and this may put great pressure on the environment. Therefore, it’s necessary to make efforts in controlling and treating the SF6 emission. Among the SF6 abatement technologies, the non-thermal plasma(NTP) represented by the dielectric barrier discharge(DBD) can effectively degrade SF6 and is suitable for large-scale industry applications. However, its energy efficiency still gets room for improvement and this kind of method has a defect that it’s hard to regulate the degradation by-products. Therefore, this paper proposed the combination of the packed bed reactor and the DBD technology to form a packed DBD discharge system for SF6 degradation, so that to further improve the energy efficiency and regulate the selectivity of by-products. By experiment and simulation research, the following innovations have been achieved: (1) Based on the packed bed DBD platform, the power parameter and gas-phase parameters of SF6 degradation were studied. It was found that the discharge process was significantly enhanced with the addition of packing particles, and the discharge energy efficiency was improved. The increase of input voltage can obviously increase the degradation rate, but reduces the energy efficiency. The increase of SF6 initial concentration and gas flow rate can improve the energy efficiency, but reduce the degradation rate. Therefore, both degradation rate and energy efficiency should be considered in deciding basic experimental conditions. (2) Active gases, such as O2, H2O and NH3, could effectively promote the degradation rate of SF6, and changed the product selectivity. In our packed bed DBD system, O2 and H2O have the optimal concentration conditions, which are 2% and 1%, respectively. The addition of O2 can promote the generation of S-O-F products, and inhibit the selectivity of SO2, while the addition of H2O had the opposite effects. In addition, the synergistic degradation of NH3 and SF6 will produce solid products, such as NH3HF, NH4HF2 and elemental S. For gaseous products, the increase of NH3 will lead to the generation of SO2 in the final degradation products and inhibit the generation of S-O-F products. (3) Different kinds of packing materials have great impacts on the degradation system in the discharge parameters, degradation rate and energy efficiency, as well as the products distribution. In the experiment, we compared the degradation results in three systems: glass beads packing, γ-Al2O3 packing and no-packing system. The packing of glass beads effectively improved the discharge voltage amplitude and discharge power, while had a limited effect on the equivalent capacitance of the dielectric. Besides, γ-Al2O3 packing had little effect on voltage amplitude, but obviously increased the equivalent capacitance of the dielectric. Furthermore, the degradation rate and energy efficiency in γ-Al2O3 system was higher than that of glass bead system. For products selectivity, γ-Al2O3 system was more desirable, where S-O-F type of product selectivity was suppressed and the SO2 selectivity increased significantly. By contrast, the glass beads system hardly affected the product selectivity. This results are presumably due to the relatively high dielectric constant of γ-Al2O3 particles and γ-Al2O3 itself may act as a reactant or a catalyst participating in the degradation reactions. (4) The size and status of the packing particles also have significant effects on the degradation process. The systems packed with 1, 2 and 4mm γ-Al2O3 particles for SF6 degradation were compared, and the 2mm system had the best performance, which may because the 2mm system had a good balance between the active contact area and the gas residence time. In addition, the packing pellets suffered from a hydration process slightly reduced the discharge parameters in the γ-Al2O3 packing system and significantly reduced the degradation rate was, which may because the H2O molecules pre-occupied the active sites on the γ-Al2O3 surface and reduced the discharge process. (5) Based on density functional theory (DFT), the degradation process of SF6 in the packed bed DBD system was studied at atomic scale. It was found that the SF6 can occur a physical adsorption at AlⅢ active sites on γ-Al2O3 surface. The activation barrier for the first degradation step of SF6 on γ-Al2O3 surface is much lower than in gas phase, which proved that the SF6 molecule is activated on the γ-Al2O3 surface. In addition, the plasma may affect the γ-Al2O3 surface to generate excess electrons or external electric fields. This two effects can change the adsorbed SF6 molecules from physical adsorption to chemisorption, together with an obvious stretching of S-F bonds, indicating that the plasma surface effects prmote the activation and decomposition of SF6 molecules. Furthermore, the stepwise degradation process of SF6 on γ-Al2O3 surface were investigated. The influence of radicals produced by plasma on the degradation process was analyzed. It was found that via Eley–Rideal (ER) reactions, high-energy radicals could effectively reduce the activation barriers and promote the surface reactions. Finally, the degradation mechanism of SF6 molecules in the packed bed plasma system was summarized, which may provide a theoretical basis for the study of harmless degradation of SF6. Keywords: SF6; Packed Bed DBD; Discharge Parameters; Products Analysis; Degradation Mechanism

Abstract: This study presents novel sulfolane based non-aqueous CO2 capture solvents, as an alternative solution for capturing CO2 from industrial processes. In order to select the most promising amine system, five different amines were tested by monitoring CO2 absorption and desorption processes using the time-base Attenuated Total Reflectance-Fourier Transform Infrared (ATR-FTIR) spectroscopy. During absorption experiments, we observed the formation of Monomethyl Carbonate (MMC) in diisopropylamine (DIPA) and 2-amino-2-methyl-1-propanol (AMP) systems, while carbamate was observed as the main product for the other three amine systems tested. In regeneration experiments, the MMC could be desorbed relatively easily from the amine solution at a mild temperature.