“Sn2-2xSbxFexO4 solid solutions as possible inert anode materials in aluminum electrolysis”. Govorov VA, Abakumov AM, Rozova MG, Borzenko AG, Vassiliev SY, Mazin VM, Afanasov MI, Fabritchnyi PB, Tsirlina GA, Antipov EV, Morozova EN, Gippius AA, Ivanov VV, Van Tendeloo G, Chemistry of materials 17, 3004 (2005). http://doi.org/10.1021/cm048145i
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 11
DOI: 10.1021/cm048145i
|
“Synthesis and structural investigations on the new Sr1.32Mn0.83Cu0.17O3 compound”. Abakumov AM, Mironov AV, Govorov VA, Lobanov MV, Rozova MG, Antipov EV, Lebedev OI, Van Tendeloo G, Solid state sciences 5, 1117 (2003). http://doi.org/10.1016/S1293-2558(03)00141-9
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 8
DOI: 10.1016/S1293-2558(03)00141-9
|
“Microstructural aspects of the degradation behavior of SnO2-based anodes for aluminum electrolysis”. Vassiliev SY, Laurinavichute VK, Abakumov AM, Govorov VA, Bendovskii EB, Turner S, Filatov AY, Tarasovskii VP, Borzenko AG, Alekseeva AM, Antipov EV, Journal of the electrochemical society 157, C178 (2010). http://doi.org/10.1149/1.3327903
Abstract: The performance of SnO2 ceramic anodes doped with copper and antimony oxides was examined in cryolite alumina melts under anodic polarization at different cryolite ratios, temperatures, times, and current densities. The corroded part consists of a narrow strong corrosion zone at the anode surface with damage of the intergrain contacts and a large increase in porosity, a wider moderate corrosion zone with a smaller porosity increase, and a Cu depletion zone, where the ceramic retains its initial microstructure and a slight porosity increase occurs due to the removal of the Cu-rich inclusions. Mechanical destruction of the anode was never observed in the 10100 h tests. A microstructural model of the ceramic was suggested, consisting of grains with an Sb-doped SnO2 grain core surrounded by an ~200 to 500 nm grain shell where SnO2 was simultaneously doped with Sb and Mn+ (M=Cu2+,Fe3+,Al3+). The grains were separated by a few nanometers thick Cu-enriched grain boundaries. Different secondary charge carrier (holes) concentrations and electric conductivities in the grain core and grain shell result in a higher current density at the intergrain regions that leads to their profound degradation, especially in the low temperature acidic melt.