“Enamels in stained glass windows: preparation, chemical composition, microstructure and causes of deterioration”. Schalm O, van der Linden V, Frederickx P, Luyten S, van der Snickt G, Caen J, Schryvers D, Janssens K, Cornelis E, van Dyck D, Schreiner M, Spectrochimica acta: part B : atomic spectroscopy 64, 812 (2009). http://doi.org/10.1016/j.sab.2009.06.005
Abstract: Stained glass windows incorporating dark blue and purple enamel paint layers are in some cases subject to severe degradation while others from the same period survived the ravages of time. A series of dark blue, greenblue and purple enamel glass paints from the same region (Northwestern Europe) and from the same period (16early 20th centuries) has been studied by means of a combination of microscopic X-ray fluorescence analysis, electron probe micro analysis and transmission electron microscopy with the aim of better understanding the causes of the degradation. The chemical composition of the enamels diverges from the average chemical composition of window glass. Some of the compositions appear to be unstable, for example those with a high concentration of K2O and a low content of CaO and PbO. In other cases, the deterioration of the paint layers was caused by the less than optimal vitrification of the enamel during the firing process. Recipes and chemical compositions indicate that glassmakers of the 1617th century had full control over the color of the enamel glass paints they made. They mainly used three types of coloring agents, based on Co (dark blue), Mn (purple) and Cu (light-blue or greenblue) as coloring elements. Bluepurple enamel paints were obtained by mixing two different coloring agents. The coloring agent for redpurple enamel, introduced during the 19th century, was colloidal gold embedded in grains of lead glass.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Vision lab
Impact Factor: 3.241
Times cited: 28
DOI: 10.1016/j.sab.2009.06.005
|
“Blue enamel on sixteenth- and seventeenth-century window glass : deterioration, microstructure, composition and preparation”. van der Snickt G, Schalm O, Caen J, Janssens K, Schreiner M, Studies in conservation 51, 212 (2006). http://doi.org/10.1179/SIC.2006.51.3.212
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 0.578
Times cited: 8
DOI: 10.1179/SIC.2006.51.3.212
|
“The colour of silver stained glass : analytical investigations carried out with XRF, SEM/EDX, TEM and IBA”. Jembrih-Simbürger D, Neelmeijer C, Schalm O, Fredrickx P, Schreiner M, De Vis K, Mäder M, Schryvers D, Caen J, Journal of analytical atomic spectrometry 17, 321 (2002). http://doi.org/10.1039/b111024c
Abstract: Glass treated on its surface with silver compounds and an aluminosilicate, such as ochre or clay, at higher temperatures (between 550 and 650 °C) accepts a wide variety of a yellow colour. It is the aim of this study to investigate the parameters of the manufacturing process affecting the final colour of silver stained glass and to correlate them with the final colour and colour intensity. Therefore, defined mixtures of ochre and a silver compound (AgCl, AgNO3, Ag2SO4, Ag3PO4, Ag2O) were prepared and applied on soda-lime glass. The firing process was modified within the range from 563 to 630 °C and glass samples were analysed after treatment with energy dispersive X-ray fluorescence analysis (EDXRF), scanning electron microscopy (SEM/EDX), transmission electron microscopy (TEM), as well as ion beam analysis (IBA) with an external beam. Within the scope of IBA simultaneous measurements using particle-induced X-ray emission (PIXE), particle-induced gamma-ray emission (PIGE), and Rutherford backscattering spectrometry (RBS) were carried out in order to obtain the thickness of the Ag-rich surface layer and the depth distribution of Ag. By means of TEM the microstructure of the silver particles was visualised. XRF results show that the lowest amount of Ag could be detected on glass samples treated with silver stain mixtures containing AgCl and Ag2O. A low kiln temperature (e.g. 563 °C) results in a higher silver concentration at the surface and lower penetration depths. Furthermore, the results obtained with SEM/EDX at cross-sections of the glass samples could be confirmed by PIXE, PIGE, RBS, and TEM.
Keywords: A1 Journal article; Art; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 42
DOI: 10.1039/b111024c
|
“Determination of localized Fe2+/Fe3+ ratios in inks of historic documents by means of \mu-XANES”. Proost K, Janssens K, Wagner B, Bulska E, Schreiner M, Nuclear instruments and methods in physics research: B: beam interactions with materials and atoms 213, 723 (2004). http://doi.org/10.1016/S0168-583X(03)01693-8
Abstract: An important part of the European cultural heritage is composed of hand-written documents. Many of these documents were drawn up with iron-gall ink. This type of ink present a serious conservation problem, as it slowly oxidizes ('burns') the paper it is written on, thereby gradually disintegrating the historic document. Acid hydrolysis of the cellulose and/or the oxidation of organic compounds promoted by radical intermediates that are formed due to the presence of Fe2+ ions are considered to be the cause of the disintegration. mu-XANES measurements were performed with a lateral resolution of 30-50 mum in order to determine the local Fe2+/Fe3+ ratio in 19th C. documents from the Austrian National Archives and fragments of 16th C documents from the Polish National Library. In the 19th C documents, no significant amount of Fe2+ was detected. On the other hand, in the 16th C fragments, significant amounts of Fe2+ and appreciable differences in distribution of Fe2+ and Fe3+ within individual letters/ink stains were observed. (C) 2003 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.109
DOI: 10.1016/S0168-583X(03)01693-8
|
“A compact μ-XRF spectrometer for (in-situ) analyses of cultural heritage and forensic materials”. Vittiglio G, Bichlmeier S, Klinger P, Heckel J, Fuzhong W, Vincze L, Janssens K, Engström P, Rindby A, Dietrich K, Jembrih-Simbürger D, Schreiner M, Denis D, Lakdar A, Lamotte A, Nuclear instruments and methods in physics research B 213, 693 (2004)
Keywords: A3 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“The use of focussed X-ray beams for non-destructive characterization of historical materials: from elemental trace analysis towards chemical state investigations”. Janssens K, Proost K, Deraedt I, Bulska E, Wagner B, Schreiner M, , 193 (2003)
Keywords: P1 Proceeding; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Characterization of a polycapillary lens for use in micro-XANES experiments”. Proost K, Vincze L, Janssens K, Gao N, Bulska E, Schreiner M, Falkenberg G, X-ray spectrometry 32, 215 (2003). http://doi.org/10.1002/XRS.635
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.298
Times cited: 50
DOI: 10.1002/XRS.635
|
“Multianalytical study of patina formed on archaeological metal objects from Bliesbruck-Reinheim”. Wadsak M, Constantinides I, Vittiglio G, Adriaens A, Janssens K, Schreiner M, Adams FC, Brunella P, Wuttmann M, Microchimica acta 133, 159 (2000). http://doi.org/10.1007/S006040070086
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 4.58
DOI: 10.1007/S006040070086
|
“Einfluss verschiedener Silbersalze auf die Farbintensität von Silbergelb : analytische Untersuchungen”. De Vis K, Jembrih-Simbürger D, Schalm O, Schreiner M, Caen J, Zeitschrift für Kunsttechnologie und Konservierung 16, 147 (2002)
Keywords: A2 Journal article; Art; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Enamels in stained-glass windows : preparation, chemical composition, microstructure and causes of deterioration”. Caen J, Schalm O, van der Snickt G, van der Linden V, Frederickx P, Schryvers D, Janssens K, Cornelis E, van Dyck D, Schreiner M, , 121 (2005)
Keywords: P3 Proceeding; Art; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Vision lab
|