Abstract: Catalytic methods for the production of carbon nanotubules have been developed based on the decomposition of acetylene on well-dispersed metal particles strongly adsorbed on a support. Cobalt on silica was found to be the best catalyst-support combination for the production of graphitic tubules. The method for the catalyst preparation and the reaction conditions were optimized. Straight and coiled carbon tubules were obtained with inner and outer diameter of 3-7 and 15-20 nm, respectively, and up to 30 mum in length. These nanotubules were not coated by amorphous carbon. Traces of amorphous carbon could be removed by hydrogen. High resolution electron microscopy images and electron diffraction patterns of the straight nanotubules were similar to those obtained by the arc-discharge method. Coiled nanotubules were revealed by TEM to be regular polygonized helices where the bends are caused by pairs of pentagon-heptagon carbon rings among the hexagonal network.

Abstract: The structure and defect structure of Bi2-xPbxSr3.5Cu2 (CO3)O8-delta compounds with 0 less-than-or-equal-to x less-than-or-equal-to 0.75 are carefully investigated by electron diffraction and high-resolution electron microscopy. All compounds have an orthorhombic structure with a almost-equal-to b almost-equal-to 5.4 angstrom and c almost-equal-to 39.5 angstrom. The length of the b-axis decreases monotonically with increasing x. The space group for the basic structure is Abm2. The structure can be considered as an intergrowth of Bi2Sr2CuO6 lamellae with Sr2CuO2 (CO3) lamellae along the c-axis. CO3 groups behave as bridges connecting the CuO6 octahedra. In the x = 0 compound the carbon atoms are shifted away from their symmetry positions; the orientational ordering of the CO3 groups (or the carbon shift) in successive CO planes alternates along +b and -b. Typical Bi-type and Pb-type modulations are found along the b-axis up to a Pb content x = 0.5. Electron beam irradiation destroys the ordering of the CO3 groups and alters the modulated structure. (C) 1994 Academic press, inc.

Abstract: La1-xCaxMnO3-delta (LCMO) thin films are grown by pulsed laser deposition on a (100) SrTiO3 substrate at temperatures between 530 degrees C and 890 degrees C. The magnetotransport properties show a high negative magnetoresistance and a shift of the maximum of the R(T) curve as function of temperature. The Curie temperature changes with deposition temperature and film quality in the range of 100-220K. The film quality is characterised by X-ray diffraction and transmission electron microscopy (TEM); film and target compositions were verified by atomic emission spectroscopy. The local structure of the film depends on the growth conditions and substrate temperature. TEM reveals a slight distortion of the film leading to a breakdown of the symmetry from orthorhombic to monoclinic. At the highest growth temperatures, a well defined interface is observed within the LCMO film, parallel to the substrate surface; this interface divides the film into two lamellae with a different microstructure. The lamella close to the substrate is perfectly coherent with the substrate, suggesting that it is strained as a result of the lattice parameter mismatch; the upper lamella shows a typical domain structure with unusual translation interfaces characterised by a displacement vector of the type 1/2[010](m) and 1/2[001](m) when referred ten the monoclinic lattice.

Abstract: The growth features of FeCr2S4 spinel single crystals prepared by chemical vapour transport were studied by means of scanning electron microscopy, transmission electron microscopy, high resolution electron microscopy, electron diffraction and X-ray analysis. Our results indicate that the epitaxial growth of the new phases FeCr7S12 and FeCr8S12, both based on the NiAs structure, can essentially inhibit the growth of large FeCr2S4 spinel single crystals in the octahedral habit. The new phases are fully characterised and the effects of defect ordering in these new phases are also reported.