“The fine structure of YCuO2+x delafossite determined by synchrotron powder diffraction and electron microscopy”. Van Tendeloo G, Garlea O, Darie C, Bougerol-Chaillout C, Bordet P, Journal of solid state chemistry 156, 428 (2001). http://doi.org/10.1006/jssc.2000.9018
Abstract: YCuO2 delafossite crystallizes into two stacking variants; hexagonal 2H or rhombohedral 3R, depending on the preparation conditions. The structure of the fully oxygenated material YCuO2.50 has been determined as orthorhombic (a(O) = 6.1961 Angstrom; b(O) = 11.2158 Angstrom; c(O) = 7.1505 Angstrom; space group Pnma). The structure is based on the hexagonal 2H structure (a(O) = a(H)root3; b(O) = c(H); c(O) = 2a(H)). Upon incomplete oxidation, a different YCuOZ phase with ideal composition YCuO2.33 and lattice parameters a(H root)3, a(H)root3, c(H) is also formed. Diffraction patterns are often very complex because of the presence of planar defects and intergrowth of both phases. Under electron beam irradiation, oxygen is released from the structure and one phase gradually transforms into the other. (C) 2001 Academic Press.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 33
DOI: 10.1006/jssc.2000.9018
|
“Direct evidence of spontaneous quantum dot formation in a thick InGaN epilayer”. Nistor L, Bender H, Vantomme A, Wu MF, van Landuyt J, O'Donnell KP, Martin R, Jacobs K, Moerman I, Applied physics letters 77, 507 (2000). http://doi.org/10.1063/1.127026
Abstract: We report a direct observation of quantum dots formed spontaneously in a thick InGaN epilayer by high resolution transmission electron microscopy. Investigation of a (280 nm thick) In0.22Ga0.78N single layer, emitting in the blue/green spectral region, reveals quantum dots with estimated sizes in the range of 1.5-3 nm. Such sizes are in very good agreement with calculations based on the luminescence spectra of this specimen. (C) 2000 American Institute of Physics. [S0003-6951(00)00930-X].
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 44
DOI: 10.1063/1.127026
|
“Structural and magnetotransport transitions in the electron-doped Pr1-xSrxMnO3(0.85\leq x\leq1) manganites”. Hervieu M, Martin C, Maignan A, Van Tendeloo G, Jirak Z, Hejtmanek J, Barnabe A, Thopart D, Raveau B, Chemistry and materials 12, 1456 (2000). http://doi.org/10.1021/cm000016o
Abstract: The exploration of the Mn4+-rich side of the Pr1-xSrxMnO3 system has allowed the extension of the domain of the cubic perovskite, by using a two-step process, combining synthesis under Ar flow at high temperature and O-2 pressure annealing at lower temperature. We show that these Pr-doped cubic perovskites exhibit a coupled structural (cubic-tetragonal) and magnetic (para-antiferro) transition connected with a resistivity jump at the same temperature. The strong interplay between lattice, charges, and spins for these oxides results from the appearance at low temperature of the distorted C-type antiferromagnetic structure. The Pr1-xSrxMnO3 magnetic phase diagram shows, for 0.9 less than or equal to x less than or equal to 1 (i.e., on the Mn4+-rich side), the existence at low temperature of C- and G-type antiferromagnetism. The absence of ferromagnetic-antiferromagnetic competition explains that magnetoresistante properties are not observed in this system, in contrast to Mn4+-rich Ln(1-x)Ca(x)MnO(3) systems.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 24
DOI: 10.1021/cm000016o
|
“In situ HREM irradiation study of point-defect clustering in MBE-grown strained Si1-xGex/(001)Si structures”. Fedina L, Lebedev OI, Van Tendeloo G, van Landuyt J, Mironov OA, Parker EHC, Physical review : B : condensed matter and materials physics 61, 10336 (2000). http://doi.org/10.1103/PhysRevB.61.10336
Abstract: We present a detailed analysis of the point-defect clustering in strained Si/Si(1-x)Ge(x)/(001)Si structures, including the interaction of the point defects with the strained interfaces and the sample surface during 400 kV electron irradiation at room temperature. Point-defect cluster formation is very sensitive to the type and magnitude of the strain in the Si and Si(1-x)Ge(x) layers. A small compressive strain (-0.3%) in the SiGe alloy causes an aggregation of vacancies in the form of metastable [110]-oriented chains. They are located on {113} planes and further recombine with interstitials. Tensile strain in the Si layer causes an aggregation of interstitial atoms in the forms of additional [110] rows which are inserted on {113} planes with [001]-split configurations. The chainlike configurations are characterized by a large outward lattice relaxation for interstitial rows (0.13 +/-0.01 nm) and a very small inward relaxation for vacancy chains (0.02+/-0.01 nm). A compressive strain higher than -0.5% strongly decreases point-defect generation inside the strained SiGe alloy due to the large positive value of the formation volume of a Frenkel pair. This leads to the suppression of point-defect clustering in a strained SiGe alloy so that SiGe relaxes via a diffusion of vacancies from the Si layer, giving rise to an intermixing at the Si/SiGe interface. In material with a 0.9% misfit a strongly increased flow of vacancies from the Si layer to the SiGe layer and an increased biaxial strain in SiGe bath promote the preferential aggregation of vacancies in the (001) plane, which relaxes to form intrinsic 60 degrees dislocation loops.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 27
DOI: 10.1103/PhysRevB.61.10336
|
“Ground state of excitons and charged excitons in a quantum well”. Riva C, Peeters FM, Varga K, Physica status solidi: A: applied research
T2 –, 6th International Conference on Optics of Excitons in Confined Systems, (OECS-6), AUG 30-SEP 02, 1999, ASCONA, SWITZERLAND 178, 513 (2000). http://doi.org/10.1002/1521-396X(200003)178:1<513::AID-PSSA513>3.0.CO;2-1
Abstract: A variational calculation of the ground state of a neutral exciton and of positively and negatively charged excitons (trions) in a single quantum well is presented. We study the dependence of the correlation energy and of the binding energy on the well width and on the hole mass. Our results are compared with previous theoretical results and with available experimental data.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Times cited: 16
DOI: 10.1002/1521-396X(200003)178:1<513::AID-PSSA513>3.0.CO;2-1
|
“Polarizability induced cooperative proton ordering, coexistence of order/disorder and displacive dynamics and isotope effects in hydrogen-bonded systems”. Bussmann-Holder A, Dalal N, Michel KH, The journal of physics and chemistry of solids
T2 –, Williamsburg Workshop on Ferroelectrics 99, JAN 31-FEB 03, 1999, WILLIAMSBURG, VIRGINIA 61, 271 (2000). http://doi.org/10.1016/S0022-3697(99)00292-9
Abstract: Despite the general belief that hydrogen-bonded ferro- and antiferroelectrics undergo a pure order/disorder transition at the structural instability, new NMR data and a new theoretical concept yield convincing evidence that a pronounced displacive component is present in these systems, which modifies substantially the temperature dependencies of the tunnel and lattice mode frequencies. The experiments and their interpretation are presented. (C) 1999 Elsevier Science Ltd. All rights reserved.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.059
Times cited: 8
DOI: 10.1016/S0022-3697(99)00292-9
|
“Preparation of nanocrystalline titania powder via aerosol pyrolysis of titanium tetrabutoxide”. Ahonen PP, Kauppinen EI, Joubert JC, Deschanvres JL, Van Tendeloo G, Journal of materials research 14, 3938 (1999). http://doi.org/10.1557/JMR.1999.0533
Abstract: Nanocrystalline titanium dioxide was prepared via aerosol pyrolysis of titanium alkoxide precursor at 200-580 degrees C in air and in nitrogen atmospheres. Powders were characterized by x-ray diffraction, thermogravimetric analysis, Brunauer-Emmett-Teller analysis, scanning electron microscopy, transmission electron microscopy, energy dispersive spectroscopy, x-ray fluorescence, Raman and infrared spectroscopy, and Berner-type low-pressure impactor. The anatase phase transition was initiated at 500 degrees C in nitrogen and at 580 degrees C in air. Under other conditions amorphous powders were observed and transformed to nanocrystalline TiO2 via thermal postannealing. In air, smooth and spherical particles with 2-4-mu m diameter were formed with an as-expected tendency to convert to rutile in the thermal postannealings. In nitrogen, a fraction of the titanium tetrabutoxide precursor evaporated and formed ultrafine particles via the gas-to-particle conversion. At 500 degrees C thermally stable anatase phase was formed in nitrogen. A specific surface area as high as 280 m(2) g(-1) was observed for an as-prepared powder.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.673
Times cited: 38
DOI: 10.1557/JMR.1999.0533
|
“Accurate infrared spectroscopy determination of interstitial and precipitated oxygen in highly doped Czochralski-grown silicon”. de Gryse O, Clauws P, Rossou L, van Landuyt J, Vanhellemont J, The review of scientific instruments 70, 3661 (1999). http://doi.org/10.1063/1.1149974
Abstract: A method has been developed to determine the interstitial and precipitated oxygen concentration in highly doped n- and p-type silicon. 10-30-mu m-thin silicon samples in a mechanical stress-free state and without alteration of the thermal history are prepared and measured with Fourier transform infrared spectroscopy at 5.5-6 K. The measured oxygen contents in the as-grown Si samples agree well with those obtained with gas fusion analysis. In the highly boron-doped samples, the interstitial oxygen can be determined down to 10(17) cm(-3). (C) 1999 American Institute of Physics. [S0034-6748(99)04909-6].
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.515
Times cited: 5
DOI: 10.1063/1.1149974
|
“Correlation of microstructure and magnetotransport properties of epitaxially grown La-Ca-Mn-O3 thin films”. Habermeier HU, Razavi F, Lebedev O, Gross GM, Praus R, Zhang PX, Physica status solidi: B: basic research
T2 –, International Conference on Solid State Spectroscopy –, (ICSSS), SEP 05-07, 1999, SCHWABISCH-GMUND, GERMANY 215, 679 (1999). http://doi.org/10.1002/(SICI)1521-3951(199909)215:1<679::AID-PSSB679>3.0.CO;2-H
Abstract: We have investigated epitaxially grown single-crystalline Ca-doped LaMnO3 thin films using the pulsed laser deposition technique in a case study aimed to explore the possibilities buried in epitaxial stress tailoring in order to control the transport properties of CMR materials beyond the limits set by equilibrium thermodynamics. Depending on the film thickness there is an abrupt transition from pseudomorphic to epitaxial granular growth observable which is related to the epitaxial strain of the films. This is associated with microscopic stress relaxation and leads to well controllable modifications of the atomic arrangements of the Mn-O sublattice in the films. Due to the interrelation of double exchange, spin-, charge- and orbital ordering and the Jahn-Teller effect mediated coupling of the electronic system to the crystal lattice, the magnetotransport properties of the firms can be modified in a controllable way.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.674
Times cited: 3
DOI: 10.1002/(SICI)1521-3951(199909)215:1<679::AID-PSSB679>3.0.CO;2-H
|
“Modeling of photon scattering at high X-ray energies : experiment versus simulation”. Vincze L, Vekemans B, Janssens K, Adams F, Journal of analytical atomic spectrometry
T2 –, 15th International Congress on X-Ray Optics and Microanalysis (ICXOM), AUG 24-27, 1998, ANTWERP, BELGIUM 14, 529 (1999). http://doi.org/10.1039/A808040B
Abstract: The use of a detailed Monte Carlo simulation code for X-ray fluorescence spectrometers is demonstrated for calculating the outcome of X-ray scattering experiments in the incident energy range 40-80 keV. The code was validated by comparisons of experimental and simulated spectral distributions in the case of thick, homogeneous samples in which multiple photon scattering occurs with high probability. The experimental spectral distributions were collected at beamline BW5 of HASYLAB, Germany, where a highly energetic, monochromatic synchrotron beam is available. With respect to heterogeneous samples, the code was employed to evaluate the use of Rayleigh and Compton scatter signals for obtaining three dimensional information on the sample dark matrix composition.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
DOI: 10.1039/A808040B
|
“The non-destructive determination of REE in fossilized bone using synchrotron radiation induced K-line X-ray microfluorescence analysis”. Janssens K, Vincze L, Vekemans B, Williams CT, Radtke M, Haller M, Knöchel A, Fresenius' journal of analytical chemistry 363, 413 (1999). http://doi.org/10.1007/S002160051212
Abstract: The sensitivity and applicability of the synchrotron radiation induced X-ray microfluorescence (mu-SRXRF) spectrometer at the Hamburg synchrotron laboratory Hasylab for the determination of the distribution of trace concentrations of rare-earth elements (REE) in fossilized bone are discussed and critically compared to those of other trace analytical methods such as instrumental neutron activation analysis (INAA) and LAMP-ICPMS (laser ablation microprobe inductively-coupled plasma mass spectrometry). Measurements were carried out on two bone samples from contrasting terrestrial depositional environments at Olduvai Gorge (Tanzania). Results indicate that the microdistribution of the REE in these biological materials is not homogeneous and that the relative abundance of these elements can provide information on the palaeoenvironment during the fossilization process. The heterogeneous distribution of the REE can be determined in a quantitative and completely non-destructive manner provided the concentrations of individual REE are above 10 mu g/g.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1007/S002160051212
|
“Electrostatic modes in multi-ion and pair-ion collisional plasmas”. Vranjes J, Petrovic D, Pandey BP, Poedts S, Physics of plasmas 15, 072104 (2008). http://doi.org/10.1063/1.2949696
Abstract: The physics of plasmas containing positive and negative ions is discussed with special attention to the recently produced pair-ion plasma containing ions of equal mass and opposite charge. The effects of the density gradient in the direction perpendicular to the ambient magnetic field vector are discussed. The possible presence of electrons is discussed in the context of plasma modes propagating at an angle with respect to the magnetic field vector. It is shown that the electron plasma mode may become a backward mode in the presence of a density gradient, and this behavior may be controlled either by the electron number density or the mode number in the perpendicular direction. In plasmas with hot electrons an instability may develop, driven by the combination of electron collisions and the density gradient, and in the regime of a sound ions' response. In the case of a pure pair-ion plasma, for lower frequencies and for parameters close to those used in the recent experiments, the perturbed ions may feel the effects of the magnetic field. In this case the plasma mode also becomes backward, resembling features of an experimentally observed but yet unexplained backward mode. (C) 2008 American Institute of Physics.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.115
Times cited: 54
DOI: 10.1063/1.2949696
|
“Inelastic electron holography as a variant of the Feynman thought experiment”. Potapov PL, Verbeeck J, Schattschneider P, Lichte H, van Dyck D, Ultramicroscopy 107, 559 (2007). http://doi.org/10.1016/j.ultramic.2006.11.003
Abstract: Using a combination of electron holography and energy filtering, interference fringes produced after inelastic interaction of electrons with hydrogen molecules are examined. Surprisingly, the coherence of inelastic scattering increases when moving from the surface of a hydrogen-containing bubble to the vacuum. This phenomenon can be understood in terms of the Feynman two-slit thought experiment with a variable ambiguity of the which-way registration. (C) 2006 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 13
DOI: 10.1016/j.ultramic.2006.11.003
|
“Observation of Co/CoO nanoparticles below the critical size for exchange bias”. Dobrynin AN, Temst K, Lievens P, Margueritat J, Gonzalo J, Afonso CN, Piscopiello E, Van Tendeloo G, Journal of applied physics 101, 113913 (2007). http://doi.org/10.1063/1.2736303
Abstract: We compare the magnetic properties of pure and oxidized Co nanoparticles embedded in an amorphous Al2O3 matrix. Nanoparticles with diameters of 2 or 3 nm were prepared by alternate pulsed laser deposition in high vacuum conditions, and some of them were exposed to O-2 after production and before being embedded. The nanoparticles are organized in layers, the effective edge-to-edge in-depth separation being 5 or 10 nm. The lower saturation magnetizations per Co atom for the samples containing oxidized nanoparticles provide evidence for the formation of antiferromagnetic CoO shells in the nanoparticles. None of the samples with Co/CoO nanoparticles show exchange bias, while vertical hysteresis loop shifts and enhanced coercivities (as compared to samples with pure Co nanoparticles) are observed. This constitutes evidence for the nanoparticles size being in all cases smaller than the critical size for exchange bias. The difference in coercivity versus temperature dependences for the samples with pure and oxidized Co nanoparticles shows that the exchange anisotropy in Co/CoO nanoparticles appears at temperatures lower than 50 K. (c) 2007 American Institute of Physics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 27
DOI: 10.1063/1.2736303
|
“Confocal mu-XRF, mu-XAFS, and mu-XRD studies of sediment from a nuclear waste disposal natural analogue site and fractured granite following a radiotracer migration experiment”. Denecke MA, Janssens K, Brendebach B, de Nolf W, Falkenberg G, Rothe J, Simon R, Somogyi A, Vekemans B, Noseck U, AIP conference proceedings 882, 187 (2007)
Abstract: Combined mu-XRF, mu-XAFS, and mu-XRD investigations of a uranium-rich tertiary sediment, from a nuclear repository natural analogue site, and a fractured granite bore core section after a column tracer experiment using a Np(V) containing cocktail have been performed. Most mu-XRF/mu-XAFS measurements are recorded in a confocal geometry to provide added depth information. The U-rich sediment results show uranium to be present as a tetravalent phosphate and that U(IV) is associated with As(V). Arsenic present is either As(V) or As(0). The As(0) form thin coatings on the surface of pyrite nodules. A hypothesis for the mechanism of uranium immobilization is proposed, where arsenopyrite acted as reductant of ground water dissolved U(VI) leading to precipitation of less soluble U(IV) and thereby forming As(V). Results for the granite sample show the immobilized Np to be tetravalent and associated with facture material.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Platinum particle size and support effects in NOx mediated carbon oxidation over platinum catalysts”. Villani K, Vermandel W, Smets K, Liang D, Van Tendeloo G, Martens JA, Environmental science &, technology 40, 2727 (2006). http://doi.org/10.1021/es051871h
Abstract: Platinum metal was dispersed on microporous, mesoporous, and nonporous support materials including the zeolites Na-Y, Ba-Y, Ferrierite, ZSM-22, ETS-10, and AlPO-11, alumina, and titania. The oxidation of carbon black loosely mixed with catalyst powder was monitored gravimetrically in a gas stream containing nitric oxide, oxygen, and water. The carbon oxidation activity of the catalysts was found to be uniquely related to the Pt dispersion and little influenced by support type. The optimum dispersion is around 3-4% corresponding to relatively large Pt particle sizes of 2040 nm. The carbon oxidation activity reflects the NO oxidation activity of the platinum catalyst, which reaches an optimum in the 20-40 nm Pt particle size range. The lowest carbon oxidation temperatures were achieved with platinum loaded ZSM-22 and AlPO-11 zeolite crystallites bearing platinum of optimum dispersion on their external surfaces.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.198
Times cited: 29
DOI: 10.1021/es051871h
|
“Copper stabilization by zeolite synthesis in polluted soils treated with coal fly ash”. Terzano R, Spagnuolo M, Medici L, Vekemans B, Vincze L, Janssens K, Ruggiero P, Environmental science and technology 39, 6280 (2005). http://doi.org/10.1021/ES050079D
Abstract: This study deals with the process of zeolite formation in an agricultural soil artificially polluted by high amounts of Cu (15 mg of Cu/g of soil dry weight) and treated with fused coal fly ash at 30 and 60 degrees C and how this process affects the mobility and availability of the metal. As a consequence of the treatment, the amount of dissolved Cu, and thus its mobility, was strongly reduced, and the percentage of the metal stabilized in the solid phase increased over time, reaching values of 30% at 30 degrees C and 40% at 60 degrees C. The physicochemical phenomena responsible for Cu stabilization in the solid phase have been evaluated by EDTA sequential extractions and synchrotron radiation based X-ray microanalytical techniques. These techniques were used for the visualization of the spatial distribution and the speciation of Cu in and/or on the neo-formed zeolite particles. In particular, micro XRF (X-ray fluorescence) tomography showed direct evidence that Cu can be entrapped as clusters inside the porous zeolitic structures while,mu-XANES (X-ray absorption near edge structure) spectroscopy determinations revealed Cu to be present mainly as Cu(II) hydroxide and Cu(II) oxide. The reported results could be useful as a basic knowledge for planning new technologies for the on site physicochemical stabilization of heavy metals in heavily polluted soils.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.198
Times cited: 39
DOI: 10.1021/ES050079D
|
“Coulomb-interaction driven anomaly in the Stark effect for an exciton in vertically coupled quantum dots”. Chwiej T, Bednarek S, Adamowski J, Szafran B, Peeters FM, Journal of luminescence
T2 –, 6th International Conference on Excitonic Processes in Condensed Matter, (EXCON 04), JUL 06-09, 2004, Cracow, POLAND 112, 122 (2005). http://doi.org/10.1016/j.jlumin.2004.09.009
Abstract: The effect of the electric field on an exciton confined in a pair of vertically coupled quantum dots is studied. We use a single-band approximation and a parabolic model potential. As a result of these idealizations, we obtain a numerically solvable model, which is used to describe the influence of the electron-hole interaction on the Stark effect for the lowest-energy photo luminescence lines. We show that for intermediate tunnel coupling between the dots this interaction leads to an anomalous Stark effect with an essential deviation of the recombination energy from the usual quadratic dependence on the electric field. (c) 2004 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.686
Times cited: 10
DOI: 10.1016/j.jlumin.2004.09.009
|
“Giant magnetoresistance in a two-dimensional electron gas modulated by magnetic barriers”. Papp G, Peeters FM, Journal of physics : condensed matter 16, 8275 (2004). http://doi.org/10.1088/0953-8984/16/46/014
Abstract: The temperature-dependent giant magnetoresistance effect is investigated in a magnetically modulated two-dimensional electron gas, which can be realized by depositing two parallel ferromagnets on the top and bottom of a heterostructure. The effective potential for electrons arising for parallel magnetization allows the electrons to resonantly tunnel through the magnetic barriers, while this is excluded in the anti-parallel situation. Such a discrepancy results in a giant magnetoresistance ratio (MRR), which can be up to 10(31)%. The MRR shows a strong dependence on temperature, but our study indicates that for realistic parameters for a GaAs heterostructure the effect can be as high as 10(4)% at 4 K.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.649
Times cited: 69
DOI: 10.1088/0953-8984/16/46/014
|
“Controlling the diameters in large-scale synthesis of single-walled carbon nanotubes by catalytic decomposition of CH4”. Li Y, Zhang X, Shen L, Luo J, Tao X, Liu F, Xu G, Wang Y, Geise HJ, Van Tendeloo G, Chemical physics letters 398, 276 (2004). http://doi.org/10.1016/j.cplett.2004.09.068
Abstract: High-quality single-walled carbon nanotubes (SWNTs) are synthesized in gram amount on Fe-Mo/MgO catalysts by catalytic decomposition of CH4 in H-2 or N-2. Raman data reveal that the as-prepared SATNTs have a diameter of about 0.74-1.29 nm. It is found that the diameter of the as-prepared SWNTs can be controlled mainly by adjusting the molar ratio of Fe-Mo versus the MgO support. Several other factors that potentially influence the growth of SWNTs have been studied in detail. The experimental results show that the nature of the catalyst determines the diameter of the as-prepared SWNTs. (C) 2004 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 45
DOI: 10.1016/j.cplett.2004.09.068
|
“One-step synthesis of shelled PbS nanoparticles in a layered double hydroxide matrix”. Lukashin AV, Eliseev AA, Zhuravleva NG, Vertegel AA, Tretyakov YD, Lebedev OI, Van Tendeloo G, Mendeleev communications , 174 (2004). http://doi.org/10.1070/MC2004v014n04ABEH001973
Abstract: The one-step preparation of capped PbS nanoparticles in an inorganic matrix via UV-induced decomposition of lead thiosulfate complexes intercalated into a hydrotalcite-type layered double hydroxide is reported.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.741
Times cited: 9
DOI: 10.1070/MC2004v014n04ABEH001973
|
“Stable and metastable states in a mesoscopic superconducting “eight&rdquo, loop in presence of an external magnetic field”. Vodolazov DY, Peeters FM, Physica: C : superconductivity 400, 165 (2004). http://doi.org/10.1016/j.physc.2003.08.003
Abstract: The stable and metastable states of different configurations of a mesoscopic loop in the form of an eight is studied in the presence of a magnetic field. We find that for certain configurations the current is equal to zero for any value of the magnetic field leading to a magnetic field independent superconducting state. The state with fixed phase circulation becomes unstable when the momentum of the superconducting electrons reaches a critical value. At this moment the kinetic energy of the superconducting condensate becomes of the same order as the potential energy of the Cooper pairs and it leads to an instability. Numerical analysis of the time-dependent Ginzburg-Landau equations shows that the absolute value of the order parameter changes gradually at the transition from a state with one phase circulation to another although the vorticity change occurs abruptly. (C) 2003 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 1.404
Times cited: 5
DOI: 10.1016/j.physc.2003.08.003
|
“Comparison of mono- and polyatomic primary ions for the characterization of organic dye overlayers with static secondary ion mass spectrometry”. Lenaerts J, van Vaeck L, Gijbels R, Van Luppen J, Rapid communications in mass spectrometry 18, 257 (2004). http://doi.org/10.1002/rcm.1320
Abstract: Organic carbocyanine dye coatings have been analyzed by time-of-flight static secondary ion mass spectrometry (TOF-S-SIMS) using three types of primary ions: Ga+ operating at 25 keV, and Xe+ and SF5+ both operating at 9 keV. Secondary ion yields obtained with these three primary ions have been compared for coatings with different layer thickness, varying from (sub)-monolayer to multilayers, on different substrates (Si, Ag and AgBr cubic microcrystals). For (sub)-monolayers deposited on Ag, Xe+ and SF5+ primary ions generate similar precursor ion intensities, but with Ga+ slightly lower precursor ion intensities were obtained. Thick coatings on Ag as well as mono- and multilayers on Si produce the highest precursor and fragment ion intensities with the polyatomic primary ion. The yield difference between SF5+ and Xe+ can reach a factor of 6. In comparison with Ga+, yield enhancements by up to a factor of 180 are observed with SF5+. For the mass spectrometric analysis of dye layers on AgBr microcrystals, SF5+ again proves to be the primary ion of choice. Copyright (C) 2004 John Wiley Sons, Ltd.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 1.998
Times cited: 5
DOI: 10.1002/rcm.1320
|
“Characterization of oxide precipitates in heavily B-doped silicon by infrared spectroscopy”. de Gryse O, Clauws P, Vanhellemont J, Lebedev OI, van Landuyt J, Simoen E, Claeys C, Journal of the electrochemical society 151, G598 (2004). http://doi.org/10.1149/1.1776592
Abstract: Infrared absorption spectra of oxygen precipitates in boron-doped silicon with a boron concentration between 10(17) and 10(19) cm(-3) are analyzed, applying the spectral function representation of composite materials. The aspect ratio of the platelet precipitates is determined by transmission electron microscopy measurements. The analysis shows that in samples with moderate doping levels (<10(18) B cm(-3)) SiOγ precipitates are formed with the same composition as in the lightly doped case. In the heavily boron-doped (>10(18) cm(-3)) samples, however, the measured spectra of the precipitates are consistent with a mixture of SiO2 and B2O3, with a volume fraction of B2O3 as high as 0.41 in the most heavily doped case. (C) 2004 The Electrochemical Society.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.259
Times cited: 13
DOI: 10.1149/1.1776592
|
“A novel approach to analyse FTIR spectra of precipitates in boron-doped silicon”. de Gryse O, Vanhellemont J, Clauws P, Lebedev O, van Landuyt J, Simoen E, Claeys C, Physica: B : condensed matter
T2 –, 22nd International Conference on Defects in Semiconductors (ICDS-22), JUL 28-AUG 01, 2003, UNIV AARHUS, AARHUS, DENMARK 340, 1013 (2003). http://doi.org/10.1016/j.physb.2003.09.194
Abstract: Infrared absorption spectra of composite precipitates are analysed with a modified Day-Thorpe algorithm, assuming a precipitated phase consisting of a mixture of two components with known optical properties. Additional constraints are introduced when solving the model equations by using a priori knowledge making the algorithm more reliable. It is shown that this novel approach allows determining both morphology and composition of precipitates. The method is applied to characterise oxide precipitates in boron-doped silicon. The results indicate that for the resistivity range above 60 mOmegacm, the precipitated phase is most probably SiO1.17+/-0.14, while for resistivities below 20 mOmega cm, precipitates consist of a SiO2/B2O3 composite with a large volume fraction of B(2)0(3) (up to 40% for 8 mOmegacm material). (C) 2003 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.386
Times cited: 4
DOI: 10.1016/j.physb.2003.09.194
|
“Dislocations in diamond : dissociation into partials and their glide motion”. Blumenau AT, Jones R, Frauenheim T, Willems B, Lebedev OI, Van Tendeloo G, Fisher D, Martineau PM, Physical review : B : condensed matter and materials physics 68, 014115 (2003). http://doi.org/10.1103/PhysRevB.68.014115
Abstract: The dissociation of 60degrees and screw dislocations in diamond is modeled in an approach combining isotropic elasticity theory with ab initio-based tight-binding total-energy calculations. Both dislocations are found to dissociate with a substantial lowering of their line energies. For the 60degrees dislocation, however, an energy barrier to dissociation is found. We investigate the core structure of a screw dislocation distinguishing “shuffle,” “mixed,” and “glide” cores. The latter is found to be the most stable undissociated screw dislocation. Further, the glide motion of 90degrees and 30degrees partials is discussed in terms of a process involving the thermal formation and subsequent migration of kinks along the dislocation line. The calculated activation barriers to dislocation motion show that the 30degrees partial is less mobile than the 90degrees partial. Finally, high-resolution electron microscopy is performed on high-temperature, high-pressure annealed natural brown diamond, allowing the core regions of 60degrees dislocations to be imaged. The majority of dislocations are found to be dissociated. However, in some cases, undissociated 60degrees dislocations were also observed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 39
DOI: 10.1103/PhysRevB.68.014115
|
“Multiply connected mesoscopic superconductors”. Baelus BJ, Peeters FM, Modern physics letters B
T2 –, 3rd International Conference on Modern Problems in Superconductivity, SEP 09-14, 2002, YALTA, UKRAINE 17, 527 (2003). http://doi.org/10.1142/S021798490300555X
Abstract: Multiply connected mesoscopic: superconductors are considered within the framework of the nonlinear Ginzburg-Landau theory. The two coupled nonlinear equations are solved numerically and we investigated the properties of a superconducting ring, two concentric rings, and an asymmetric ring. We find that (i) for a mesoscopic superconducting ring the flux through the hole is not quantized, (ii) two concentric mesoscopic superconducting rings are magnetically coupled and the interaction energy increases with increasing sample thickness, and (iii) in asymmetric rings, a stationary phase slip state is predicted.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 0.617
DOI: 10.1142/S021798490300555X
|
“On the ferromagnetic exchange in Mn-doped III-V semiconductors”. Ivanov VA, Krstajic PM, Peeters FM, Fleurov V, Kikoin K, Physica: B : condensed matter
T2 –, 23rd International Conference on Low Temperature Physics (LT23), AUG 20-27, 2002, HIROSHIMA, JAPAN 329, 1282 (2003). http://doi.org/10.1016/S0921-4526(02)02240-8
Abstract: We propose a microscopic model for double exchange in GaAs:Mn, GaP:Mn which is based on the interaction between the transition metal impurities and the heavy holes of host semiconductor. The kinematic exchange is derived and the Curie temperature is calculated which agrees with recent experiments. (C) 2003 Elsevier Science B.V. All rights reserved.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 1.386
Times cited: 5
DOI: 10.1016/S0921-4526(02)02240-8
|
“Single chain elasticity and thermoelasticity of polyethylene”. Titantah JT, Pierleoni C, Ryckaert J-P, The journal of chemical physics 117, 9028 (2002). http://doi.org/10.1063/1.1514974
Abstract: Single-chain elasticity of polyethylene at theta point up to 90% of stretching with respect to its contour length is computed by Monte Carlo simulation of an atomistic model in continuous space. The elasticity law together with the free-energy and the internal energy variations with stretching are found to be very well represented by the wormlike chain model up to 65% of the chain elongation, provided the persistence length is treated as a temperature-dependent parameter. Beyond this value of elongation simple ideal chain models are not able to describe the Monte Carlo data in a thermodynamic consistent way. This study reinforces the use of the wormlike chain model to interpret experimental data on the elasticity of synthetic polymers in the finite extensibility regime, provided the chain is not yet in its fully stretched regime. Specific solvent effects on the elasticity law and the partition between energetic and entropic contributions to single chain elasticity are investigated. (C) 2002 American Institute of Physics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.965
Times cited: 5
DOI: 10.1063/1.1514974
|
“Chemical microcharacterization of ultrathin iodide conversion layers and adsorbed thiocyanate surface layers on silver halide microcrystals with time-of-flight SIMS”. Verlinden G, Gijbels R, Geuens I, Microscopy and microanalysis 8, 216 (2002). http://doi.org/10.1017/S1431927602020159
Abstract: The technique of imaging time-of-flight secondary ion mass spectrometry (TOF-SIMS) and dual beam depth,profiling has been used to study the composition of the surface of tabular silver halide microcrystals. Analysis of individual microcrystals with a size well below 1 mum from a given emulsion is possible. The method is successfully applied for the characterization of silver halide microcrystals with subpercent global iodide concentrations confined in surface layers with a thickness below 5 nm. The developed TOF-SIMS analytical procedure is explicitly demonstrated for the molecular imaging of adsorbed thiocyanate layers (SCN) at crystal surfaces of individual crystals and for the differentiation of iodide conversion layers synthesized with KI and with AgI micrates (nanocrystals with a size between 10 and 50 nm). It can be concluded that TOF-SIMS as a microanalytical, surface-sensitive technique has some unique properties over other analytical techniques for the study of complex structured surface layers of silver halide microcrystals. This offers valuable information to support the synthesis of future photographic emulsions.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 1.891
Times cited: 1
DOI: 10.1017/S1431927602020159
|