“Metal-decorated multi-wall carbon nanotubes for low temperature gas sensing”. Espinosa EH, Lonescu R, Bittencourt C, Felten A, Erni R, Van Tendeloo G, Pireaux J-J, Llobet E, Thin solid films : an international journal on the science and technology of thin and thick films 515, 8322 (2007). http://doi.org/10.1016/j.tsf.2007.03.017
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.879
Times cited: 86
DOI: 10.1016/j.tsf.2007.03.017
|
“Particulate ba-barite and acantharians in the Southern Ocean during the European iron fertilization experiment (EIFEX)”. Jacquet SHM, Henjes J, Dehairs F, Worobiec A, Savoye N, Cardinal D, Journal of geophysical research: G: biogeosciences 112, 04006 (2007). http://doi.org/10.1029/2006JG000394
Keywords: A1 Journal article; Laboratory Experimental Medicine and Pediatrics (LEMP); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1029/2006JG000394
|
“Variation in particulate PAHs levels and their relation with the transboundary movement of the air masses”. Ravindra K, Wauters E, Van Grieken R, The science of the total environment 396, 100 (2008). http://doi.org/10.1016/J.SCITOTENV.2008.02.018
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.SCITOTENV.2008.02.018
|
“Formation of Mn304/C core-shell nanowires and a new MN-O phase by electron beam irradiation”. Du GH, Van Tendeloo G, Applied physics A : materials science &, processing 91, 393 (2008). http://doi.org/10.1007/s00339-008-4430-5
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.455
Times cited: 1
DOI: 10.1007/s00339-008-4430-5
|
“Dynamics of nanoclustering in Te+ implanted Si after application of high frequency electromagnetic field and thermal annealing”. Kalitzova M, Lebedev OI, Zollo G, Gesheva K, Vlakhov E, Marinov Y, Ivanova T;, Applied physics A : materials science &, processing 91, 515 (2008). http://doi.org/10.1007/s00339-008-4441-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.455
DOI: 10.1007/s00339-008-4441-2
|
“In situ transmission electron microscopy of stress-induced martensite with focus on martensite twinning”. Tirry W, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 420 (2008). http://doi.org/10.1016/j.msea.2006.12.214
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 22
DOI: 10.1016/j.msea.2006.12.214
|
“New (3(3)under-bar) long-period microtwin variant in the martensitic phase of the PtTi alloy”. Rotaru G-M, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 437 (2008). http://doi.org/10.1016/j.msea.2006.12.201
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 3
DOI: 10.1016/j.msea.2006.12.201
|
“Effect of annealing on cold-rolled Ni-Ti alloys”. Srivastava AK, Yang Z, Schryvers D, van Hurnbeeck J, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 594 (2008). http://doi.org/10.1016/j.msea.2006.12.216
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 8
DOI: 10.1016/j.msea.2006.12.216
|
“Electron energy-loss spectroscopy study of NiTi shape memory alloys”. Yang ZQ, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 214 (2008). http://doi.org/10.1016/j.msea.2006.12.227
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 7
DOI: 10.1016/j.msea.2006.12.227
|
“Local structure of perovskite-based “Pb2Fe2O5””. Hadermann J, Abakumov AM, Nikolaev IV, Antipov EV, Van Tendeloo G, Solid state sciences 10, 382 (2008). http://doi.org/10.1016/j.solidstatesciences.2007.12.008
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 29
DOI: 10.1016/j.solidstatesciences.2007.12.008
|
“Carbonates from the lower part of transition zone or even the lower mantle”. Brenker FE, Vollmer C, Vincze L, Vekemans B, Szymanski A, Janssens K, Szaloki I, Nasdala L, Joswig W, Kaminsky F, Earth and planetary science letters 260, 1 (2007). http://doi.org/10.1016/J.EPSL.2007.02.038
Abstract: Effective CO2-storage in the shallow solid Earth mainly occurs by the formation of carbonates. Although the possibility of transport and storage of carbonates to great depth is demonstrated experimentally, ultra-deep mantle carbonates have not been found before. Applying several in situ analytical techniques on inclusions in diamonds from Juina (Brazil) originating from the lower part of the transition zone (> 580 km) or even the lower mantle (> 670 km), reveal the existence of deep Earth carbonates. These finding unquestionably show that at least locally carbonates exist within the deep Earth and may indicate that the Earth's global CO2-cycle has an ultra-deep extension.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 4.409
Times cited: 156
DOI: 10.1016/J.EPSL.2007.02.038
|
“μ-XRF/μ-RS vs. SR μ-XRD for pigment identification in illuminated manuscripts”. van der Snickt G, de Nolf W, Vekemans B, Janssens K, Applied physics A : materials science &, processing 92, 59 (2008). http://doi.org/10.1007/S00339-008-4447-9
Abstract: For the non-destructive identification of pigments and colorants in works of art, in archaeological and in forensic materials, a wide range of analytical techniques can be used. Bearing in mind that every method holds particular limitations, two complementary spectroscopic techniques, namely confocal ì-Raman spectroscopy (ì-RS) and ì-X-ray fluorescence spectroscopy (ì-XRF), were joined in one instrument. The combined ì-XRF and ì-RS device, called PRAXIS unites both complementary techniques in one mobile setup, which allows ì- and in situ analysis. ì-XRF allows one to collect elemental and spatially-resolved information in a non-destructive way on major and minor constituents of a variety of materials. However, the main disadvantages of ì-XRF are the penetration depth of the X-rays and the fact that only elements and not specific molecular combinations of elements can be detected. As a result ì-XRF is often not specific enough to identify the pigments within complex mixtures. Confocal Raman microscopy (ì-RS) can offer a surplus as molecular information can be obtained from single pigment grains. However, in some cases the presence of a strong fluorescence background limits the applicability. In this paper, the concrete analytical possibilities of the combined PRAXIS device are evaluated by comparing the results on an illuminated sheet of parchment with the analytical information supplied by synchrotron radiation ì-X-ray diffraction (SR ì-XRD), a highly specific technique.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.455
Times cited: 56
DOI: 10.1007/S00339-008-4447-9
|
“A scanning electron microscopy study on hollow silica microspheres: defects and influences of the synthesis composition”. Liu S, Wei M, Sui X, Cheng X, Cool P, Van Tendeloo G, Journal of sol-gel science and technology 49, 373 (2009). http://doi.org/10.1007/s10971-008-1875-0
Abstract: Defects on hollow silica spheres synthesized in a tetraethylorthosilicate-octylamine-HCl-H2O system were recorded by scanning microscope. Based on the results, influences of synthesis composition on the formation of these defects are discussed. It is evidenced that products prepared with different octylamine-to-tetraethylorthosilicate ratios may have surface depressions, cracks and non-hollow microspheres. However, by changing water and acid additions, these defects could be reduced or eliminated. Generally, samples synthesized with a large octylamine addition commonly exhibit surface depressions. A small octylamine or a large water addition benefits the formation of solid silica microspheres among the product. Acid, although is not indispensable for the formation of hollow spheres, helps to eliminate or reduce depressions on the hollow shells. It is explained that the added acid gives rise to a relative localized fast hydrolysis versus condensation, facilitating an easy mobility of hydrolyzed silica species, and consequently the shell surface is smoothened.
Keywords: A1 Journal article; Laboratory of adsorption and catalysis (LADCA); Electron microscopy for materials research (EMAT)
Impact Factor: 1.575
Times cited: 1
DOI: 10.1007/s10971-008-1875-0
|
“Control and readout of current-induced magnetic flux quantization in a superconducting transformer”. Kerner C, Hackens B, Golubović, DS, Poli S, Faniel S, Magnus W, Schoenmaker W, Bayot V, Maes H, Superconductor science and technology 22, 025001 (2009). http://doi.org/10.1088/0953-2048/22/2/025001
Abstract: We demonstrate a simple and robust method for inducing and detecting changes of magnetic flux quantization in the absence of an externally applied magnetic field. In our device, an isolated ring is interconnected with two access loops via permalloy cores, forming a superconducting transformer. By applying and tuning a direct current at the first access loop, the number of flux quanta trapped in the isolated ring is modified without the aid of an external field. The flux state of the isolated ring is simply detected by recording the evolution of the critical current of the second access loop.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.878
Times cited: 2
DOI: 10.1088/0953-2048/22/2/025001
|
“Particulate matter and gaseous pollutants in residences in Antwerp, Belgium”. Stranger M, Potgieter-Vermaak SS, Van Grieken R, The science of the total environment 407, 1182 (2009). http://doi.org/10.1016/J.SCITOTENV.2008.10.019
Abstract: This comprehensive study, a first in Flanders, Belgium, aimed at characterizing the residential indoor air quality of subgroups that took part in the European Community Respiratory Health Survey (ECRHS I1991 and ECHRS II1996) questionnaire-based asthma and related illnesses studies. This pilot study aimed at the evaluation of particulate matter and various inorganic gaseous compounds in residences in Antwerp. In addition personal exposure to the gaseous compounds of one individual per residence was assessed. The main objective was to obtain some base-line pollutant levels and compare these with studies performed in other cities, to estimate the indoor air quality in residences in Antwerp. Correlations between the various pollutant levels, indoor:outdoor ratios and the micro-environments of each residence were investigated. This paper presents results on indoor and ambient PM1, PM2.5 and PM10 mass concentrations, its elemental composition in terms of K, Ca, Ti, V, Cr, Mn, Fe, Ni, Cu, Zn, Br, Pb, Al, Si, S and Cl and the water-soluble ionic concentrations in terms of SO42−, NO32−, Cl−, NH4+ K+, Ca2+. In addition, indoor, ambient and personal exposure levels of the gases NO2, SO2, and O3 were determined. Elevated indoor:outdoor ratios were found for NO2 in residences containing gas stoves. In smoker's houses increased PM concentrations of 58 and 43% were found for the fine and coarse fractions respectively. Contrary to the fact that all I/O ratios of the registered elements in each individual house were significantly correlated to each other, no correlation could be established between the I/O ratios of the different houses, thus indicating a unique micro-environment for each residence. Linear relationships between the particulate matter elemental composition, SO2 and O3 levels indoors and outdoors could be established. No linear relationships between indoor and outdoor NO2 and particulate mass concentrations were found.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.SCITOTENV.2008.10.019
|
“Morphology and the chemical make-up of the inorganic components of black corals”. Nowak D, Florek M, Nowak J, Kwiatek W, Lekki J, Chevallier P, Hacura A, Wrzalik R, Ben-Nissan B, Van Grieken R, Kuczumow A, Materials science and engineering: part C: biomimetic materials 29, 1029 (2009). http://doi.org/10.1016/J.MSEC.2008.08.028
Abstract: Black corals (Cnidaria, Antipatharia) from three different sources were investigated with the aim of detecting inorganic components and their morphology. In general, the skeleton of black corals was composed of the chitin fibrils admixed with peptides and the chitin presence was confirmed by the X-ray diffraction (XRD), Fourier Transformed Infrared Spectrometry (FTIR) and microRaman Microscopy, the latter giving the opportunity of tracing single fibrils and their location. The composition and concentrations of the inorganic components of the black corals were measured, using a scanning electron microprobe and micro-Particle Induced X-ray Emission (µ-PIXE). The application of such instruments enabled the estimation of the constituent distributions in a microscale. The mapping option was the most useful technique of making analyses in these studies, just to reveal the composition of chamber-like cells. Analysis of the morphology and microstructure showed that there were three distinct regions within the coral: a core and the cells encircled with adjacent interface gluing strips. The majority of the elements analyzed were selectively distributed and segregated in a striking way in mentioned distinctive zones of the skeleton and it was detected for the first time. The core area was characterized by the relatively elevated concentrations of Ca. The measurements gave extremely clear images of the distribution of particular elements in the skeletal tissue, with I, Ca, K and Fe much more concentrated in the gluing zones, while C, N, Na and Mg present in the interiors of particular skeletal cells. The distribution of some elements (Mg, Fe) and some compounds (chitin) and functional groups (SS, CI) allows differentiating the biological and mechanical functions of particular fragments of the rods. The kinds of elements and their concentrations measured were essentially in compliance with rare data available in the literature. The Raman technique gave the additional qualitative information about the structure of gluing zone and the chitin fibrils and surrounding matrix inside the cell interior.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.MSEC.2008.08.028
|
“Formation of vortex shells in mesoscopic superconducting squares”. Misko VR, Zhao HJ, Peeters FM, Oboznov V, Dubonos SV, Grigorieva IV, Superconductor science and technology 22, 034001 (2009). http://doi.org/10.1088/0953-2048/22/3/034001
Abstract: We study vortex configurations in mesoscopic superconducting squares. Our theoretical approach is based on the analytical solution of the London equation using the Green's function method. The potential energy landscape found is then used in Langevin-type molecular-dynamics simulations to obtain stable vortex configurations. We show that the filling rules for vortices in squares with increasing applied magnetic field can be formulated, although in a different manner than in disks, in terms of the formation of vortex 'shells'. We discuss metastable states and the stability of the vortex configurations found with respect to variations of the material parameters and deformations of the shape of the sample.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.878
Times cited: 14
DOI: 10.1088/0953-2048/22/3/034001
|
“Synthesis and structural mechanisms of the 2201-type ferrites and polytypes: Fe2(Sr2-xAx)FeO6.5-\delta/2 (A = Ba, La, Tl, Pb and Bi)”. Lepoittevin C, Malo S, Van Tendeloo G, Hervieu M, Solid state sciences 11, 595 (2009). http://doi.org/10.1016/j.solidstatesciences.2008.12.005
Abstract: The Fe2(Sr2 − xAx)FeO6.5 − ä/2 systems have been investigated, by doping the iron rich 2201-type parent structure with Ba2+, La3+ and 5d10 post-transition cations. The syntheses have been carried out up to the limit of the 2201-type solid solutions, in order to test the role of the double iron layer Fe2O2.5 − ä/2. The localisation of the charge carriers in these compounds is consistent with their strong antiferro-magnetism. The investigation was then carried out in the transition part of the diagram up to the formation of stable phases. The study of structural mechanisms was carried using high resolution electron microscopy (transmission and scanning transmission), electron diffraction and energy dispersive spectroscopy. Different non-stoichiometry mechanisms are observed, depending on the electronic structure and chemical properties of the doping elements. The specific behavior of the modulated double iron layer is discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 3
DOI: 10.1016/j.solidstatesciences.2008.12.005
|
“Numerical study of the sputtering in a dc magnetron”. Kolev I, Bogaerts A, Journal of vacuum science and technology: A: vacuum surfaces and films 27, 20 (2009). http://doi.org/10.1021/jp8058992
Abstract: Molecular dynamics simulations were used to investigate the size-dependent melting mechanism of nickel nanoclusters of various sizes. The melting process was monitored by the caloric curve, the overall cluster Lindemann index, and the atomic Lindemann index. Size-dependent melting temperatures were determined, and the correct linear dependence on inverse diameter was recovered. We found that the melting mechanism gradually changes from dynamic coexistence melting to surface melting with increasing cluster size. These findings are of importance in better understanding carbon nanotube growth by catalytic chemical vapor deposition as the phase state of the catalyst nanoparticle codetermines the growth mechanism.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 4.536
Times cited: 66
DOI: 10.1021/jp8058992
|
“Addition of yttrium into HfO2 films: microstructure and electrical properties”. Dubourdieu C, Rauwel E, Roussel H, Ducroquet F, Hollaender B, Rossell M, Van Tendeloo G, Lhostis S, Rushworth S, Journal of vacuum science and technology: A: vacuum surfaces and films 27, 503 (2009). http://doi.org/10.1116/1.3106627
Abstract: The cubic phase of HfO2 was stabilized by addition of yttrium in thin films grown on Si/SiO2 by metal-organic chemical vapor deposition. The cubic phase was obtained for contents of 6.5 at. % Y or higher at a temperature as low as 470 °C. The complete compositional range (from 1.5 to 99.5 at. % Y) was investigated. The crystalline structure of HfO2 was determined from x-ray diffraction, electron diffraction, and attenuated total-reflection infrared spectroscopy. For cubic films, the continuous increase in the lattice parameter indicates the formation of a solid-solution HfO2Y2O3. As shown by x-ray photoelectron spectroscopy, yttrium silicate is formed at the interface with silicon; the interfacial layer thickness increases with increasing yttrium content and increasing film thickness. The dependence of the intrinsic relative permittivity r as a function of Y content was determined. It exhibits a maximum of ~30 for ~8.8 at. % Y. The cubic phase is stable upon postdeposition high-temperature annealing at 900 °C under NH3.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.374
Times cited: 29
DOI: 10.1116/1.3106627
|
“3D reconstruction of Ni4Ti3 precipitates in a Ni51Ti49 alloy in a FIB/SEM dual-beam system”. Cao S, Tirry W, van den Broek W, Schryvers D, Materials science forum 583, 277 (2008). http://doi.org/10.4028/www.scientific.net/MSF.583.277
Abstract: Ni4Ti3 precipitates play an important role in the shape memory and superelastic behaviour of thermo-mechanically treated Ni-Ti material. The 3D morphology and distribution of such precipitates with lenticular shape and rhombohedral atomic structure in the austenitic B2 matrix of a binary Ni-rich Ni-Ti alloy has been elucidated via a slice view procedure in a Dual-Beam FIB/SEM system. With the sequence of cross-section SE images obtained from the SEM, a 3D reconstruction has been achieved after proper alignment and image processing, from which both qualitative and quantitative analysis can be performed. Careful imaging is needed to ensure that all variants of the precipitates are observed with equal probability, regardless sample orientation. Moreover, due to the weak contrast of the precipitates, proper imaging conditions need to be selected to allow for semi-automated image treatment. Finally, a volume ratio of 10.2% for the Ni4Ti3 precipitates could be calculated, summed over all variants, which yields a net composition of Ni50.36Ti49.64 for the matrix, leading to an increase of 113 degrees for the martensitic start temperature Ms. Also, the expected relative orientation of the different variants of the precipitates could be confirmed. In the near future, other quantitative measures on the distribution of the precipitates can be expected.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
DOI: 10.4028/www.scientific.net/MSF.583.277
|
“Multiwalled carbon nanotubes functionalized with 7-octenyltrichlorosilane and n-octyltrichlorosilane: dispersion in Sylgard®184 silicone and Youngs modulus”. Vast L, Carpentier L, Lallemand F, Colomer J-F, Van Tendeloo G, Fonseca A, Nagy JB, Mekhalif Z, Delhalle J, Journal of materials science 44, 3476 (2009). http://doi.org/10.1007/s10853-009-3464-1
Abstract: Sylgard®184/multiwalled carbon nanotube (MWNT) composites have been prepared by in situ polymerization using purified and functionalized multiwalled carbon nanotubes (f-MWNTs) as fillers. Surface modification of the MWNTs has been carried out by silanization with 7-octenyltrichlorosilane (7OTCS) and n-octyltrichlorosilane (nOTCS). The modification and dispersion of the carbon nanotubes in composites were characterized by X-ray photoelectron spectroscopy (XPS), transmission electron spectroscopy (TEM), and high-resolution transmission electron spectroscopy (HRTEM). Youngs modulus results were derived from indentation testing. It is shown that the terminal-vinyl group of 7OTCS molecules plays an essential role for both the dispersion of the f-MWNTs in the composite and its mechanical properties. At loading as low as 0.2 wt%, the Youngs modulus is shown to increase up to 50%. This is interpreted as resulting from a combination of the good compatibility in the forming silicone matrix of the MWNTs coated with a siloxane network, on the one hand, and the covalent links created between the terminal-vinyl groups and the host matrix in formation, on the other hand.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.599
Times cited: 16
DOI: 10.1007/s10853-009-3464-1
|
“Composition of pigments on human bones found in excavations in Argentina studied with micro-Raman spectrometry and scanning electron microscopy”. Darchuk L, Stefaniak EA, Vázquez C, Palacios OM, Worobiec A, Van Grieken R, e-Preservation Science 6, 112 (2009)
Abstract: Results on analysis of prehistoric pigments from excavations and pigments on coloured child bones from North Patagonia, Argentina, are reported. To analyze their composition we used two micro-analytical techniques: micro- Raman spectrometry (MRS) and scanning electron microscopy coupled with X-ray micro-analysis (SEM/EDX). Most investigated excavated pigments show red or yellow ochres consistent with reddish or yellow minerals, such as á- and ã-goethite, haematite, erdite, haapalaite and jarosite. Raman spectra show also evidence of calcium oxalate monohydrate and calcite indicating lichen activity. Pigments covering human bones were identified as hematite and magnetite. This study allows us to infer that pigments found in excavation were employed for burial ceremonies, even though distances between excavated pigment archaeological site and buried remains are quite far, more than 50 km in a straight line.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Laboratory Experimental Medicine and Pediatrics (LEMP)
|
“Combining HPLC-GCXGC, GCXGC/ToF-MS, and selected ecotoxicity assays for detailed monitoring of petroleum hydrocarbon degradation in soil and leaching water”. Mao D, Lookman R, van de Weghe H, Weltens R, Vanermen G, de Brucker N, Diels L, Environmental science and technology 43, 7651 (2009). http://doi.org/10.1021/ES9015603
Abstract: HPLC-GCXGC/FID (high-performance liquid chromatography followed by comprehensive two-dimensional gas chromatography with flame-ionization detection) and GCXGC/ToF-MS (comprehensive two-dimensional gas chromatography with time-of-flight mass spectrometry) were used to study the biodegradation of petroleum hydrocarbons in soil microcosms during 20 weeks. Two soils were studied: one spiked with fresh diesel and one field sample containing weathered diesel-like oil. Nutrient amended and unamended samples were included. Total petroleum hydrocarbon (TPH) levels in spiked soil decreased from 15000 to 7500 mg/kg d.m. and from 12000 to 4000 mg/kg d.m. in the field soil. Linear alkanes and aromatic hydrocarbons were better biodegradable (>60% degraded) than iso-alkanes; cycloalkanes were least degradable (<40%). Aromatic hydrocarbons up to three rings showed better degradability than n-alkanes. GCXGC/ToF-MS analysis of leaching water showed that initially various oxygenated hydrocarbons were produced. Compound peaks seemed to move up and rightward in the GCXGC chromatograms, indicating that more polar and heavier compounds were formed as biodegradation proceeded. Nutrient amendment can increase TPH removal rates, but had adverse effects on ecotoxicity and leaching potential in our experiment. This was explained by observed shifts in the soil microbial community. Ecotoxicity assays showed that residual TPH still inhibited cress (Lepidium sativum) seed germination, but the leaching water was no longer toxic toward luminescent bacteria (Vibrio fischeri).
Keywords: A1 Journal article; Sustainable Energy, Air and Water Technology (DuEL)
DOI: 10.1021/ES9015603
|
“Rational synthesis of a nanocrystalline calcium phosphate cement exhibiting rapid conversion to hydroxyapatite”. Neira IS, Kolen'ko YV, Lebedev OI, Van Tendeloo G, Gupta HS, Matsushita N, Yoshimura M, Guitian F, Materials science and engineering: part C: biomimetic materials 29, 2124 (2009). http://doi.org/10.1016/j.msec.2009.04.011
Abstract: The rational synthesis, comprehensive characterization, and mechanical and micromechanical properties of a calcium phosphate cement are presented. Hydroxyapatite cement biomaterial was synthesized from reactive sub-micrometer-sized dicalcium phosphate dihydrate and tetracalcium phosphate via a dissolution-precipitation reaction using water as the liquid phase. As a result nanostructured, Ca-deficient and carbonated B-type hydroxyapatite is formed. The cement shows good processibility, sets in 22 ± 2 min and entirely transforms to the end product after 6 h of setting reaction, one of the highest conversion rates among previously reported for calcium phosphate cements based on dicalcium and tetracalcium phosphates. The combination of all elucidated physical-chemical traits leads to an essential bioactivity and biocompatibility of the cement, as revealed by in vitro acellular simulated body fluid and cell culture studies. The compressive strength of the produced cement biomaterial was established to be 25 ± 3 MPa. Furthermore, nanoindentation tests were performed directly on the cement to probe its local elasticity and plasticity at sub-micrometer/micrometer level. The measured elastic modulus and hardness were established to be Es = 23 ± 3.5 and H = 0.7 ± 0.2 GPa, respectively. These values are in close agreement with those reported in literature for trabecular and cortical bones, reflecting good elastic and plastic coherence between synthesized cement biomaterial and human bones.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.164
Times cited: 18
DOI: 10.1016/j.msec.2009.04.011
|
“Analysis of micro computed tomography images, a look inside historic enamelled metal objects”. van der Linden V, Van de Casteele E, Thomas MS, de Vos A, Janssen E, Janssens K, Applied physics A : materials science &, processing 98, 385 (2010). http://doi.org/10.1007/S00339-009-5394-9
Abstract: In this study the usefulness of micro-Computed Tomography (µ-CT) for the in-depth analysis of enamelled metal objects was tested. Usually investigations of enamelled metal artefacts are restricted to non-destructive surface analysis or analysis of cross sections after destructive sampling. Radiography, a commonly used technique in the field of cultural heritage studies, is limited to providing two-dimensional information about a three-dimensional object (Lang and Middleton, Radiography of Cultural Material, pp. 6061, Elsevier-Butterworth-Heinemann, Amsterdam-Stoneham-London, 2005). Obtaining virtual slices and information about the internal structure of these objects was made possible by CT analysis. With this technique the underlying metal work was studied without removing the decorative enamel layer. Moreover visible defects such as cracks were measured in both width and depth and as of yet invisible defects and weaker areas are visualised. All these features are of great interest to restorers and conservators as they allow a view inside these objects without so much as touching them.
Keywords: A1 Journal article; Vision lab; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.455
Times cited: 3
DOI: 10.1007/S00339-009-5394-9
|
“Klein tunneling in single and multiple barriers in graphene”. Pereira JM, Peeters FM, Chaves A, Farias GA, Semiconductor science and technology 25, 033002 (2010). http://doi.org/10.1088/0268-1242/25/3/033002
Abstract: We review the transmission properties of carriers interacting with potential barriers in graphene. The tunneling of electrons and holes in quantum structures in graphene is found to display features that are in marked contrast with those of other systems. In particular, the interaction between the carriers with electrostatic potential barriers can be related to the propagation of electromagnetic waves in media with negative refraction indices, also known as metamaterials. This behavior becomes evident as one calculates the time evolution of wavepackets propagating across the barrier interface. In addition, we discuss the effect of trigonal warping on the tunneling through potential barriers.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.305
Times cited: 83
DOI: 10.1088/0268-1242/25/3/033002
|
“Fabrication and oxygen permeability of gastight, macrovoid-free Ba0.5Sr0.5Co0.8Fe0.2O3-\delta capillaries for high temperature gas separation”. Buysse C, Kovalevsky A, Snijkers F, Buekenhoudt A, Mullens S, Luyten J, Kretzschmar J, Lenaerts S, Journal of membrane science 359, 86 (2010). http://doi.org/10.1016/J.MEMSCI.2009.10.030
Abstract: Oxygen-permeable perovskites with mixed ionic-electronic conducting properties can play an important role in the separation of oxygen from air which is needed in the oxy-fuel and pre-combustion technologies for the removal and capture of CO2. In this work, gastight, macrovoid-free Ba0.5Sr0.5Co0.8Fe0.2O3−δ (BSCF) capillaries were successfully shaped by a phase-inversion spinning technique, followed by calcination and sintering. It was found that both the rheology of the ceramic suspension and the composition of bore liquid and coagulation bath are key factors for making macrovoid-free green capillaries. Gastight BSCF capillaries were obtained by sintering for 5 h at 1100 °C. The sintered BSCF capillaries contained a significant amount of BaSO4 due to a reaction with the polysulfone binder during calcination. The oxygen permeation flux through the BSCF capillaries was measured and compared to literature data on BSCF disk and hollow fiber membranes measured in similar conditions.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 6.035
Times cited: 38
DOI: 10.1016/J.MEMSCI.2009.10.030
|
“A multi-scale characterization of deformation twins in Ti6Al4V sheet material deformed by simple shear”. Tirry W, Coghe F, Bouvier S, Gasperini M, Rabet L, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 527, 4136 (2010). http://doi.org/10.1016/j.msea.2010.03.039
Abstract: Ti6Al4V sheet material is subjected to simple shear deformation with strain ratio's of 10%, 30% and 50%. Optical microscopy, transmission electron microscopy and electron backscatter diffraction techniques are applied to study the presence and morphology of deformation twins. Only the View the MathML source type of twins seems to be present with a volume fraction below 1%. These View the MathML source twins show a high density of basal stacking faults of the ABABACAC type identified using atomic resolution transmission electron microscopy. A resolved shear stress analysis shows that twins most often occur on those planes with the highest resolved shear stresses, but that the starting texture is not beneficial for the occurrence of twins. It is further suggested that a transitory strain hardening regime observed around 530 MPa might be related with the onset of twinning.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 20
DOI: 10.1016/j.msea.2010.03.039
|
“Conversion of carbon dioxide to value-added chemicals in atmospheric pressure dielectric barrier discharges”. Paulussen S, Verheyde B, Tu X, De Bie C, Martens T, Petrovic D, Bogaerts A, Sels B, Plasma sources science and technology 19, 034015 (2010). http://doi.org/10.1088/0963-0252/19/3/034015
Abstract: The aim of this work consists of the evaluation of atmospheric pressure dielectric barrier discharges for the conversion of greenhouse gases into useful compounds. Therefore, pure CO2 feed flows are administered to the discharge zone at varying discharge frequency, power input, gas temperature and feed flow rates, aiming at the formation of CO and O2. The discharge obtained in CO2 is characterized as a filamentary mode with a microdischarge zone in each half cycle of the applied voltage. It is shown that the most important parameter affecting the CO2-conversion levels is the gas flow rate. At low flow rates, both the conversion and the CO-yield are significantly higher. In addition, also an increase in the gas temperature and the power input give rise to higher conversion levels, although the effect on the CO-yield is limited. The optimum discharge frequency depends on the power input level and it cannot be unambiguously stated that higher frequencies give rise to increased conversion levels. A maximum CO2 conversion of 30% is achieved at a flow rate of 0.05 L min−1, a power density of 14.75 W cm−3 and a frequency of 60 kHz. The most energy efficient conversions are achieved at a flow rate of 0.2 L min−1, a power density of 11 W cm−3 and a discharge frequency of 30 kHz.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 3.302
Times cited: 116
DOI: 10.1088/0963-0252/19/3/034015
|