“High-temperature phase transition in the whitlockite-type phosphate Ca9In(PO4)7”. Morozov VA, Belik AA, Stefanovich SY, Grebenev VV, Lebedev OI, Van Tendeloo G, Lazoryak BI, Journal of solid state chemistry 165, 278 (2002). http://doi.org/10.1006/jssc.2001.9521
Abstract: The double phosphate Ca9In(PO4)(7) was obtained by solid-state reaction and was studied by room and high-temperature Xray powder diffraction, electron diffraction, high-resolution electron microscopy, second-harmonic generation (SHG) technique, differential scanning calorimetry, dielectric and conductivity measurements. The beta-Ca9In(PO4)(7) room-temperature phase is related to the mineral whitlockite and is similar to beta-Ca-3(PO4)(2). It has space group R (3) over barc, with unit cell parameters: a = 10.4008(1) Angstrom, c = 37.272(1) Angstrom, Z = 6. The structure was refined by the Rietveld method (R-wp = 4.69, R-I = 1.81). A reversible first-order beta <----> beta' phase transition of the ferroelectric type with T-c = 902 K is revealed by SHG, differential scanning calorimetry and dielectric measurements. The centrosymmetric beta'-Ca9In(PO4)(7) (973 K) has space group R (3) over barc, a = 10.4611(2) Angstrom, c = 37.874 (1) Angstrom (R-wp = 4.27, R-I = 4.11). Compared to the low-temperature beta-Ca9In(PO4)(7) structure, beta'-Ca9In(PO4)(7) can be described as an orientational disordering of the P1O(4) tetrahedra together with a calcium disordering on the M3 site. (C) 2002 Elsevier Science (USA).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 57
DOI: 10.1006/jssc.2001.9521
|
“New nano-architectures of mesoporous silica spheres analyzed by advanced electron microscopy”. Lebedev OI, Turner S, Liu S, Cool P, Van Tendeloo G, Nanoscale 4, 1722 (2012). http://doi.org/10.1039/c2nr11715k
Abstract: Using template-containing silica microspheres as a precursor, novel ordered mesoporous silica nanoparticles with a narrow pore size distribution and high crystallinity have been synthesized by various hydrothermal merging processes. Several architectures like chains, dumbbells, triangles, squares and flowers have been discovered. The linking mechanisms of these interacting silica spheres leading to the formation of ordered nano-structures are studied by HRTEM, HAADF-STEM and electron tomography and a plausible model is presented for several merging processes.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 7.367
Times cited: 5
DOI: 10.1039/c2nr11715k
|
“Au@ZIFs: stabilization and encapsulation of cavity-size matching gold clusters inside functionalized Zeolite Imidazolate Frameworks, ZIFs”. Esken D, Turner S, Lebedev OI, Van Tendeloo G, Fischer RA, Chemistry of materials 22, 6393 (2010). http://doi.org/10.1021/cm102529c
Abstract: The selective formation and stabilization of very small, naked metal particles inside the cavities of metal organic frameworks (MOFs) and the simultaneous realization of an even distribution of the particles throughout the crystalline MOF host matrix over a wide range of metal loading are challenging goals. MOFs reveal high specific surface areas, tunable pore sizes, and organic linkers, which are able to interact with guests. The chemically very robust zeolite imidazolate frameworks (ZIFs) are a subclass of MOFs. We chose the microporous sodalite-like ZIF-8 (Zn(MelM)(2); IM = imidazolate) and ZIF-90 (Zn(ICA)(2); ICA = imidazolate-2-carboxyaldehyde) as host matrices to influence the dispersion of imbedded gold nanoparticles (Au NPs). The metal loading was achieved via gas phase infiltration of [Au(CO)Cl] followed by a thermal hydrogenation step to form the Au NPs. Low-dose high-resolution transmission electron microscopy ((HR)TEM) and electron tomography reveal a homogeneous distribution of Au NPs throughout the ZIF matrix. The functional groups of ZIF-90 direct the anchoring of intermediate Au species and stabilize drastically smaller and quite monodisperse Au NPs in contrast to the parent not functionalized ZIF-8. The particles can be very small, match the cavity size and approach defined molecular clusters of magic numbers, i.e., Au(55), independently from the level of loading. Post-synthetic oxidation of the aldehyde groups to yield alkyl esters by the adjacent, catalytically active metal NPs is presented as a new concept of encapsulating nanoparticles inside MOFs and allows multiple steps of metal loadings without decomposition of the MOF.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 194
DOI: 10.1021/cm102529c
|
“The superstructure and superconductivity of Ru1222 based RuSr2Gd2-x-yYyCexCu2O10-\delta compounds”. Tan H, Lebedev OI, McLaughlin AC, Van Tendeloo G, Superconductor science and technology 23, 115013 (2010). http://doi.org/10.1088/0953-2048/23/11/115013
Abstract: For the first time, the local structure and physical properties of Ru1222 based compounds (RuSr(2)Gd(1.4)Ce(0.6)Cu(2)O(10-delta) and RuSr(2)Gd(1.8-x)Y(0.2)CexCu(2)O(10) (x = 0.90-0.55)) have been investigated and analyzed together on the very same compounds. The Ru1222 superstructure was confirmed by TEM at a local scale and was suggested to have an orthorhombic symmetry with space group Aba2 and lattice parameters a(s) similar or equal to root 2a, b(s) similar or equal to root 2a and c(s) = c. This new Ru1222 superstructure distortion from tetragonal symmetry is proposed to have a positive correlation with the superconductivity variation of these compounds. The more the distortion towards orthorhombic symmetry, the higher the critical superconducting temperature these compounds can achieve. The T(c)(0) of RuSr(2)Gd(1.8-x)Y(0.2)Ce(x)Cu(2)O(10-delta) (x = 0.85-0.55) increases monotonically from 4 to 16 K when x decreases from 0.85 to 0.70, then RuSr(2)Gd(2)Cu(2)O(8) defects emerge and the T(c) decreases with decreasing x. Ru1212 defects are observed to intergrow epitaxially with the Ru1222 structure as lamellas along the c-axis in RuSr(2)Gd(1.4)Ce(0.6)Cu(2)O(10-delta). Although Ru1212 is a superconductor, the intergrowth severely restrains its superconductivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 1
DOI: 10.1088/0953-2048/23/11/115013
|
“LiZnNb4O11.5 : a novel oxygen deficient compound in the Nb-rich part of the Li2O-ZnO-Nb2O5 system”. Morozov VA, Arakcheeva AV, Konovalova VV, Pattison P, Chapuis G, Lebedev OI, Fomichev VV, Van Tendeloo G, Journal of solid state chemistry 183, 408 (2010). http://doi.org/10.1016/j.jssc.2009.12.008
Abstract: A novel lithium zinc niobium oxide LiZnNb(4)O(11.5) (LZNO) has been found in the Nb-rich part of Li(2)O-ZnO-Nb(2)O(5) system. LZNO, with an original alpha-PbO(2) related structure, has been synthesized by the routine ceramic technique and characterized by X-ray diffraction and transmission electron microscopy (TEM). Reflections belonging to the LZNO phase, observed in X-ray powder diffraction (XRPD) and electron diffraction, have been indexed as monoclinic with unit cell parameters a=17.8358(9)angstrom, b=15.2924(7)angstrom, c=5.0363(3)angstrom and gamma=96.607(5)degrees or as alpha-PbO(2)-like with lattice constants a=4.72420(3)angstrom, b=5.72780(3)angstrom, c=5.03320(3)angstrom, gamma=90.048(16)degrees and modulation vector q=0.3a*+1.1b* indicating a commensurately modulated alpha-PbO(2) related structure. The monoclinic cell is a supercell related to the latter. Using synchrotron powder diffraction data, the structure has been solved and refined as a commensurate modulation (superspace group P112(1)/n(alpha beta 0)00) as well as a supercell (space group P2(1)/b). The superspace description allows us to consider the LZNO structure as a member of the proposed alpha-PbO(2)-Z (3 + 1)D structure type, which unifies both incommensurately and commensurately modulated structures. HRTEM reveals several types of defects in LZNO and structural models for these defects are proposed. Two new phases in Li(2)O-ZnO-Nb(2)O(5) system are predicted on the basis of this detailed HRTEM analysis. (C) 2009 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 9
DOI: 10.1016/j.jssc.2009.12.008
|
“Structure and magnetotransport properties of La2/3Ca1/3MnO3 thin films prepared by pulsed laser deposition”. Lebedev OI, Van Tendeloo G, Amelinckx S, Leibold B, Habermeier HU, Phillipp F, Materials Research Society symposium proceedings
T2 –, Symposium on Advances in Laser Ablation of Materials at the 1998 MRS, Spring Meeting, April 13-16, 1998, San Francisco, Calif. , 219 (1998). http://doi.org/10.1557/PROC-526-219
Abstract: La1-xCaxMnO3-delta (LCMO) thin films are grown by pulsed laser deposition on a (100) SrTiO3 substrate at temperatures between 530 degrees C and 890 degrees C. The magnetotransport properties show a high negative magnetoresistance and a shift of the maximum of the R(T) curve as function of temperature. The Curie temperature changes with deposition temperature and film quality in the range of 100-220K. The film quality is characterised by X-ray diffraction and transmission electron microscopy (TEM); film and target compositions were verified by atomic emission spectroscopy. The local structure of the film depends on the growth conditions and substrate temperature. TEM reveals a slight distortion of the film leading to a breakdown of the symmetry from orthorhombic to monoclinic. At the highest growth temperatures, a well defined interface is observed within the LCMO film, parallel to the substrate surface; this interface divides the film into two lamellae with a different microstructure. The lamella close to the substrate is perfectly coherent with the substrate, suggesting that it is strained as a result of the lattice parameter mismatch; the upper lamella shows a typical domain structure with unusual translation interfaces characterised by a displacement vector of the type 1/2[010](m) and 1/2[001](m) when referred ten the monoclinic lattice.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
DOI: 10.1557/PROC-526-219
|
“Vertically oriented CuO/ZnO nanorod arrays : from plasma-assisted synthesis to photocatalytic H2 production”. Simon Q, Barreca D, Gasparotto A, Maccato C, Montini T, Gombac V, Fornasiero P, Lebedev OI, Turner S, Van Tendeloo G, Journal of materials chemistry 22, 11739 (2012). http://doi.org/10.1039/c2jm31589k
Abstract: 1D CuO/ZnO nanocomposites were grown on Si(100) substrates by means of an original two-step synthetic strategy. ZnO nanorod (NR) arrays were initially deposited by plasma enhanced-chemical vapor deposition (PE-CVD) from an ArO2 atmosphere. Subsequently, tailored amounts of CuO were dispersed over zinc oxide matrices by radio frequency (RF)-sputtering of Cu from Ar plasmas, followed by thermal treatment in air. A thorough characterization of the obtained systems was carried out by X-ray photoelectron and X-ray excited-Auger electron spectroscopies (XPS and XE-AES), glancing incidence X-ray diffraction (GIXRD), field emission-scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDXS), atomic force microscopy (AFM), transmission electron microscopy (TEM), electron diffraction (ED) and energy filtered-TEM (EF-TEM). Pure and highly oriented CuO/ZnO NR arrays, free from ternary ZnCuO phases and characterized by a copper(II) oxide content controllable as a function of the adopted RF-power, were successfully obtained. Interestingly, the structural relationships between the two oxides at the CuO/ZnO interface were found to depend on the overall CuO loading. The obtained nanocomposites displayed promising photocatalytic performances in H2 production by reforming of ethanolwater solutions under simulated solar illumination, paving the way to the sustainable conversion of solar light into chemical energy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 74
DOI: 10.1039/c2jm31589k
|