Abstract: Nanocrystalline powders of undoped and lanthanide (Pr3+, Tm3+)- doped gadolinium gallium garnet, Gd3Ga5O12 (GGG), were prepared by propellant synthesis and studied by x-ray powder diffraction (XRD), electron diffraction (ED), high-resolution electron microscopy (HREM) and luminescence spectroscopy. The x-ray diffraction patterns of the GGG samples were analysed using the Rietveld method. The Rietveld refinement reveals the existence of two garnet-type phases: both are cubic (space group Ia $(3) over bar $d) with a slightly different lattice parameter and probably a slightly different composition. Electron diffraction and electron microscopy measurements confirm the x-ray diffraction results. EDX measurements for lanthanide-doped samples show that stable solid solutions with composition Gd(3-x)Ln(x)Ga(5)O(12), x approximate to 0.3 ( Ln = Pr; Tm) have been obtained. The luminescence properties of the Tm3+ -doped nanocrystalline GGG samples were measured and analysed.

Abstract: The magnetic proper-ties and their correlation with the microstructure and electrical transport are investigated in La0.88Sr0.1MnO3 films grown on (100)SrTiO3 Single crystal substrates with thickness ranging from 100 to 2500 Angstrom. The ultrathin film (t = 100 Angstrom) has a single ferromagnetic transition (FMT) at T-c of 250 K, whereas the thicker films exhibit two FMTs, with the main one at a lowered T-c of 200 K while the minor one around 300 K. Furthermore, a thickness dependent magnetic anisotropy has been found, strongly indicating the existence of strain effect, which is also revealed by the transmission electron microscopy study. The suppressed Jahn-Teller distortion (JTD) by the epitaxial strain, and the recovered JTD due to the strain relexation are suggested to explain the metallic behavior in thin films and the insulating behavior in the thick film (t = 2500 Angstrom), repectively.

Abstract: Infrared absorption spectra of oxygen precipitates in boron-doped silicon with a boron concentration between 10(17) and 10(19) cm(-3) are analyzed, applying the spectral function representation of composite materials. The aspect ratio of the platelet precipitates is determined by transmission electron microscopy measurements. The analysis shows that in samples with moderate doping levels (<10(18) B cm(-3)) SiOγ precipitates are formed with the same composition as in the lightly doped case. In the heavily boron-doped (>10(18) cm(-3)) samples, however, the measured spectra of the precipitates are consistent with a mixture of SiO2 and B2O3, with a volume fraction of B2O3 as high as 0.41 in the most heavily doped case. (C) 2004 The Electrochemical Society.

Abstract: We present a detailed analysis of the point-defect clustering in strained Si/Si(1-x)Ge(x)/(001)Si structures, including the interaction of the point defects with the strained interfaces and the sample surface during 400 kV electron irradiation at room temperature. Point-defect cluster formation is very sensitive to the type and magnitude of the strain in the Si and Si(1-x)Ge(x) layers. A small compressive strain (-0.3%) in the SiGe alloy causes an aggregation of vacancies in the form of metastable [110]-oriented chains. They are located on {113} planes and further recombine with interstitials. Tensile strain in the Si layer causes an aggregation of interstitial atoms in the forms of additional [110] rows which are inserted on {113} planes with [001]-split configurations. The chainlike configurations are characterized by a large outward lattice relaxation for interstitial rows (0.13 +/-0.01 nm) and a very small inward relaxation for vacancy chains (0.02+/-0.01 nm). A compressive strain higher than -0.5% strongly decreases point-defect generation inside the strained SiGe alloy due to the large positive value of the formation volume of a Frenkel pair. This leads to the suppression of point-defect clustering in a strained SiGe alloy so that SiGe relaxes via a diffusion of vacancies from the Si layer, giving rise to an intermixing at the Si/SiGe interface. In material with a 0.9% misfit a strongly increased flow of vacancies from the Si layer to the SiGe layer and an increased biaxial strain in SiGe bath promote the preferential aggregation of vacancies in the (001) plane, which relaxes to form intrinsic 60 degrees dislocation loops.

Abstract: Neodymium nickelate thin films have been prepared on NdGaO3 substrates by RF magnetron sputtering and post-annealing treatment under oxygen pressure. Transport properties are found to depend strongly on film thickness. Thick films show transport properties close to bulk ceramics, while very thin films exhibit a large transition from metal to insulator which occurs over a wide temperature range with high resistivity. Structure and surface morphology of the films have been investigated by Transmission Electron Microscopy (TEM) and Atomic Force Microscopy (AFM). Thin films (approximate to17 nm) grow heteroepitaxially, while thicker films (approximate to73 nm) show a granular structure. The thinnest sample suggests a symmetry change induced by the epitaxial strain of the substrate. This paper discusses the relationship between microstructure and transport properties.

Abstract: The present paper describes the synthesis, characterization of mixed-valence bismuthates with 3- or 2-dimensional perovskite-like structures and structural criteria that influence superconductivity in these compounds. Single-phase samples of Sr1-xKxBiO3 were prepared for the broad range of K-content: 0.25 less than or equal to x less than or equal to 0.65. For these bismuthates the symmetry of the structure changes from monoclinic to orthorhombic and finally to tetragonal upon increasing the K-content thus resulting in the decrease of the Bi-O distances and reduction of the network distortions. Superconductivity with maximum T-c = 12K exists in the narrow range (x approximate to 0.5 – 0.6) within the stability field of the tetragonal phase (0.33 less than or equal to x less than or equal to 0.65), when the 3-dimensional octahedral framework has close to the ideal perovskite structure arrangement. At the same time compositions with close to optimal Bi-valence (x = 0.33 and 0.43) do not show any sign of superconductivity, probably, due to structural distortions. The layered type (BaK)(3)Bi2O7 and (Ba,K)(2)BiO4 bismuthates belonging to the A(n+1)B(n)O(3n+1) homologous series were investigated Buckling of the (BiO2) layers in the structure of the n = 2 member was revealed The formation of the n=1 bismuthate was found by Electron Microscopy and X-ray powder diffraction studies. Both types of compounds are considered to be possible candidates for new superconducting materials among bismuthates.

Abstract: Silicon dominates the electronics industry, but its poor optical properties mean that III-V compound semiconductors are preferred for photonics applications. Photoluminescence at visible wavelengths was observed from porous Si at room temperature in 1990, but the origin of these photons (do they arise from highly localized defect states or quantum confinement effects?) has been the subject of intense debate ever since. Attention has subsequently shifted from porous Si to Si nanocrystals, but the same fundamental question about the origin of the photoluminescence has remained. Here we show, based on measurements in high magnetic fields, that defects are the dominant source of light from Si nanocrystals. Moreover, we show that it is possible to control the origin of the photoluminescence in a single sample: passivation with hydrogen removes the defects, resulting in photoluminescence from quantum-confined states, but subsequent ultraviolet illumination reintroduces the defects, making them the origin of the light again.

Abstract: Rational synthesis of nanowires via the vaporliquidsolid (VLS) mechanism with compositional and structural controls is vitally important for fabricating functional nanodevices from bottom up. Here, we show that branched indium tin oxide nanowires can be in situ seeded in vapor transport growth using tailored AuCu alloys as catalyst. Furthermore, we demonstrate that VLS synthesis gives unprecedented freedom to navigate the ternary InSnO phase diagram, and a rare and bulk-unstable cubic phase can be selectively stabilized in nanowires. The stabilized cubic fluorite phase possesses an unusual almost equimolar concentration of In and Sn, forming a defect-free epitaxial interface with the conventional bixbyite phase of tin-doped indium oxide that is the most employed transparent conducting oxide. This rational methodology of selecting phases and making abrupt axial heterojunctions in nanowires presents advantages over the conventional synthesis routes, promising novel composition-modulated nanomaterials.