“The merging of silica-surfactant microspheres under hydrothermal conditions”. Liu S, Lebedev OI, Mertens M, Meynen V, Cool P, Van Tendeloo G, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 116, 141 (2008). http://doi.org/10.1016/j.micromeso.2008.03.034
Abstract: Post-synthesis hydrothermal treatments have been used to improve the quality of MCM-41 materials. In our latest work, merging of surfactant-containing silica microspheres during the hydrothermal treatments was observed. Mechanistic insights and the different stages that are involved in the merging process can be summarized as follows. First, the surfaces of the starting microspheres open up due to the dissolution of silica. Then the dissolved silica species provide mass source for the formation of particle necks connecting two neighboring microspheres. Gradually, surfaces of the starting microspheres are flattened to meet the needs of further growth of the necks. Finally, some chain-like highly-ordered mesoporous structures up to several micrometers are formed. The observed merging of the surfactant-containing microspheres is a re-assembling process, which is under the control of electrostatic force between the dissolved silica species and the surfactant cations. The occluded surfactant cations in the precursor spheres play important roles in the merging process.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 5
DOI: 10.1016/j.micromeso.2008.03.034
|
|
|
“The influence of surface oxides on the distribution and release of nickel from Nitinol wires”. Shabalovskaya SA, Tian H, Anderegg JW, Schryvers DU, Carroll WU, van Humbeeck J, Biomaterials 30, 468 (2009). http://doi.org/10.1016/j.biomaterials.2008.10.014
Abstract: The patterns of Ni release from Nitinol vary depending on the type of material (NiTi alloys with low or no processing versus commercial wires or sheets). A thick TiO2 layer generated on the wire surface during processing is often considered as a reliable barrier against Ni release. The present study of Nitinol wires with surface oxides resulting from production was conducted to identify the sources of Ni release and its distribution in the surface sublayers. The chemistry and topography of the surfaces of Nitinol wires drawn using different techniques were studied with XPS and SEM. The distribution of Ni into surface depth and the surface oxide thickness were evaluated using Auger spectroscopy, TEM with FIB and ELNES. Ni release was estimated using either ICPA or AAS. Potentiodynamic potential polarization of selected wires was performed in as-received state with no strain and in treated strained samples. Wire samples in the as-received state showed low breakdown potentials (200 mV); the improved corrosion resistance of these wires after treatment was not affected by strain. It is shown how processing techniques affect surface topography, chemistry and also Ni release. Nitinol wires with the thickest surface oxide TiO2 (up to 720 nm) showed the highest Ni release, attributed to the presence of particles of essentially pure Ni whose number and size increased while approaching the interface between the surface and the bulk. The biological implications of high and lasting Ni release are also discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.402
Times cited: 102
DOI: 10.1016/j.biomaterials.2008.10.014
|
|
|
“Size effects and strain state of Ga1-xInxAs/GaAs multiple quantum wells: Monte Carlo study”. Titantah JT, Lamoen D, Schowalter M, Rosenauer A, Physical review : B : condensed matter and materials physics 78, 165326 (2008). http://doi.org/10.1103/PhysRevB.78.165326
Abstract: The effect of the size of the GaAs barrier and the Ga1−xInxAs well on the structural properties of a Ga1−xInxAs/GaAs multiple quantum well structure is investigated using the Metropolis Monte Carlo approach based on a well-parametrized Tersoff potential. It is found that within the well the Ga-As and In-As bond lengths undergo contractions whose magnitude increases with increasing In content in sharp contrast with bond-length variations in the bulk Ga1−xInxAs systems. For fixed barrier size and In content, the contraction of the bonds is also found to increase with increasing size of the well. Using the local atomic structure of the heterostructures, a more local analysis of the strain state of the systems is given and comparison with the prediction of macroscopic continuum elasticity theory shows deviations from the latter.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 5
DOI: 10.1103/PhysRevB.78.165326
|
|
|
“Tetrahedral chain order in the Sr2Fe2O5 brownmillerite”. d' Hondt H, Abakumov AM, Hadermann J, Kalyuzhnaya AS, Rozova MG, Antipov EV, Van Tendeloo G, Chemistry of materials 20, 7188 (2008). http://doi.org/10.1021/cm801723b
Abstract: The crystal structure of the Sr2Fe2O5 brownmillerite has been investigated using electron diffraction and high resolution electron microscopy. The Sr2Fe2O5 structure demonstrates two-dimensional order: the tetrahedral chains with two mirror-related configurations (L and R) are arranged within the tetrahedral layers according to the −L−R−L−R− sequence, and the layers themselves are displaced with respect to each other over 1/2[111] or 1/2[11] vectors of the brownmillerite unit cell, resulting in different ordered stacking variants. A unified superspace model is constructed for ordered stacking sequences in brownmillerites based on the average brownmillerite structure with a = 5.5298(4)Å, b = 15.5875(12)Å, c = 5.6687(4)Å, and (3 + 1)-dimensional superspace group I2/m(0βγ)0s, q = βb* + γc*, 0 ≤ β ≤ 1/2, 0 ≤ γ ≤ 1.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 64
DOI: 10.1021/cm801723b
|
|
|
“Oxygen vacancy ordering in the double-layered Ruddlesden-Popper cobaltite Sm2BaCo2O7-\delta”. Gillie LJ, Hadermann J, Hervieu M, Maignan A, Martin C, Chemistry of materials 20, 6231 (2008). http://doi.org/10.1021/cm8010138
Abstract: A new oxygen-deficient Ruddlesden−Popper (RP) cobaltite Sm2BaCo2O7−δ (δ ≈ 1.0) has been synthesized and the crystal structure elucidated by Rietveld analysis of X-ray powder diffraction (XRD) data and transmission electron microscopy (TEM). The phase crystallizes in a primitive orthorhombic unit cell, with lattice parameters a = 5.4371(4) Å; b = 5.4405(4) Å and c = 19.8629(6) Å, and space group Pnnm. Contrary to other oxygen-deficient cobalt RP phases, the oxygen vacancies are located in the equatorial positions of the [CoO] layers to give an intralayer structure similar to Sr2Mn2O5, which is not usually observed for cobalt-containing materials. The Sm3+ and Ba2+ cations show a strong preference for distinct sites, with the majority of the larger Ba2+ cations situated in the perovskite block layers and Sm3+ cations predominantly in the rock salt layers. Magnetic susceptibility data demonstrate the strong antiferromagnetic (AFM) character of Sm2BaCo2O7−δ.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 7
DOI: 10.1021/cm8010138
|
|
|
“μ-XRF/μ-RS vs. SR μ-XRD for pigment identification in illuminated manuscripts”. van der Snickt G, de Nolf W, Vekemans B, Janssens K, Applied physics A : materials science &, processing 92, 59 (2008). http://doi.org/10.1007/S00339-008-4447-9
Abstract: For the non-destructive identification of pigments and colorants in works of art, in archaeological and in forensic materials, a wide range of analytical techniques can be used. Bearing in mind that every method holds particular limitations, two complementary spectroscopic techniques, namely confocal ì-Raman spectroscopy (ì-RS) and ì-X-ray fluorescence spectroscopy (ì-XRF), were joined in one instrument. The combined ì-XRF and ì-RS device, called PRAXIS unites both complementary techniques in one mobile setup, which allows ì- and in situ analysis. ì-XRF allows one to collect elemental and spatially-resolved information in a non-destructive way on major and minor constituents of a variety of materials. However, the main disadvantages of ì-XRF are the penetration depth of the X-rays and the fact that only elements and not specific molecular combinations of elements can be detected. As a result ì-XRF is often not specific enough to identify the pigments within complex mixtures. Confocal Raman microscopy (ì-RS) can offer a surplus as molecular information can be obtained from single pigment grains. However, in some cases the presence of a strong fluorescence background limits the applicability. In this paper, the concrete analytical possibilities of the combined PRAXIS device are evaluated by comparing the results on an illuminated sheet of parchment with the analytical information supplied by synchrotron radiation ì-X-ray diffraction (SR ì-XRD), a highly specific technique.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.455
Times cited: 56
DOI: 10.1007/S00339-008-4447-9
|
|
|
“Nanodiamond photoemitters based on strong narrow-band luminescence from silicon-vacancy defects”. Vlasov II, Barnard AS, Ralchenko VG, Lebedev OI, Kanzyuba MV, Saveliev AV, Konov VI, Goovaerts E, Advanced materials 21, 808 (2009). http://doi.org/10.1002/adma.200802160
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Nanostructured and organic optical and electronic materials (NANOrOPT)
Impact Factor: 19.791
Times cited: 98
DOI: 10.1002/adma.200802160
|
|
|
“Formation of a combined micro- and mesoporous material using zeolite Beta nanoparticles”. van Oers CJ, Stevens WJJ, Bruijn E, Mertens M, Lebedev OI, Van Tendeloo G, Meynen V, Cool P, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 120, 29 (2009). http://doi.org/10.1016/j.micromeso.2008.08.056
Abstract: Composite micro- and mesoporous materials are synthesized using zeolite Beta nanoparticles without the need for a structure directing agent to form the mesopores. This leads to important ecological and economical advantages. The influence of the way of cooling the aged nanoparticles solution on the formation of the composite materials has been studied. The materials have been characterized towards porosity by N2-sorption, towards zeolitic properties by TGA, DRIFT, XRD and TEM, towards aluminium content by EPMA. All prepared structures possess zeolitic properties. However, the method of cooling down of the aged seeds leads to differences in the porosity and intensity of the zeolitic characteristics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 42
DOI: 10.1016/j.micromeso.2008.08.056
|
|
|
“Gas-phase loading of [Zn4O(btb)2] (MOF-177) with organometallic CVD-precursors: inclusion compounds of the type [LnM]a@MOF-177 and the formation of Cu and Pd nanoparticles inside MOF-177”. Müller M, Lebedev OI, Fischer RA, Journal of materials chemistry 18, 5274 (2008). http://doi.org/10.1039/b810989c
Abstract: The highly porous and desolvated (activated) coordination polymer [Zn4O(btb)2] (btb = benzene-1,3,5-tribenzoate; MOF-177) was loaded with the organometallic compounds [Cp2Fe], [Cp*2Zn], [Cu(OCHMeCH2NMe2)2], [CpCuL] (L = PMe3, CNtBu) and [CpPd(3-C3H5)] via solvent-free adsorption from the gas-phase. The inclusion compounds of the type [LnM]a@MOF-177, where [LnM] indicates the respective compound and the parameter a denotes the number of molecules per formula unit of the MOF-177, were characterised by elemental analysis, FT-IR, solid-state NMR spectroscopy and by powder X-ray diffraction (PXRD). Remarkably high effective loadings of up to 11 molecules [Cp2Fe] and 10 molecules [CpPd(3-C3H5)] per cavity were determined. The analytical data prove that the host lattice and the guest molecules interact only by weak van-der-Waals forces without any significant change of the framework or the chemical nature of the included molecules. Cu nanoparticles showing the typical surface plasmon resonance at 580 nm and Pd nanoparticles of about 2.6 nm in size were formed inside the cavities of MOF-177 by the thermally activated hydrogenolysis of the inclusion compounds [CpCuCNtBu]2@MOF-177 and by photolysis of [CpPd(3-C3H5)]10@MOF-177 in an inert atmosphere (Ar). PXRD, FT-IR and NMR studies revealed that the MOF-177 matrix remained unchanged during the decomposition process of the precursors. N2 adsorption studies of the obtained materials Cu@MOF-177 (e.g. 10.6 wt.% Cu, 2309 m2 g-1) and Pd@MOF-177 (e.g. 32.5 wt.%, 1063 m2 g-1) reveal high remaining specific surface areas (Langmuir model).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 65
DOI: 10.1039/b810989c
|
|
|
“End-to-end assembly of shape-controlled nanocrystals via a nanowelding approach mediated by gold domains”. Figuerola A, Franchini IR, Fiore A, Mastria R, Falqui A, Bertoni G, Bals S, Van Tendeloo G, Kudera S, Cingolani R, Manna L, Advanced materials 21, 550 (2009). http://doi.org/10.1002/adma.200801928
Abstract: Welding nanocrystals for assembly: The welding of Au domains grown on the tips of shape-controlled cadmium chalcogenide colloidal nanocrystals is used as a strategy for their assembly. Iodine-induced coagulation of selectively grown Au domains leads to assemblies such as flowerlike structures based on bullet-shaped nanocrystals, linear and cross-linked chains of nanorods, and globular networks with tetrapods as building blocks.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 110
DOI: 10.1002/adma.200801928
|
|
|
“Morphology and the chemical make-up of the inorganic components of black corals”. Nowak D, Florek M, Nowak J, Kwiatek W, Lekki J, Chevallier P, Hacura A, Wrzalik R, Ben-Nissan B, Van Grieken R, Kuczumow A, Materials science and engineering: part C: biomimetic materials 29, 1029 (2009). http://doi.org/10.1016/J.MSEC.2008.08.028
Abstract: Black corals (Cnidaria, Antipatharia) from three different sources were investigated with the aim of detecting inorganic components and their morphology. In general, the skeleton of black corals was composed of the chitin fibrils admixed with peptides and the chitin presence was confirmed by the X-ray diffraction (XRD), Fourier Transformed Infrared Spectrometry (FTIR) and microRaman Microscopy, the latter giving the opportunity of tracing single fibrils and their location. The composition and concentrations of the inorganic components of the black corals were measured, using a scanning electron microprobe and micro-Particle Induced X-ray Emission (µ-PIXE). The application of such instruments enabled the estimation of the constituent distributions in a microscale. The mapping option was the most useful technique of making analyses in these studies, just to reveal the composition of chamber-like cells. Analysis of the morphology and microstructure showed that there were three distinct regions within the coral: a core and the cells encircled with adjacent interface gluing strips. The majority of the elements analyzed were selectively distributed and segregated in a striking way in mentioned distinctive zones of the skeleton and it was detected for the first time. The core area was characterized by the relatively elevated concentrations of Ca. The measurements gave extremely clear images of the distribution of particular elements in the skeletal tissue, with I, Ca, K and Fe much more concentrated in the gluing zones, while C, N, Na and Mg present in the interiors of particular skeletal cells. The distribution of some elements (Mg, Fe) and some compounds (chitin) and functional groups (SS, CI) allows differentiating the biological and mechanical functions of particular fragments of the rods. The kinds of elements and their concentrations measured were essentially in compliance with rare data available in the literature. The Raman technique gave the additional qualitative information about the structure of gluing zone and the chitin fibrils and surrounding matrix inside the cell interior.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.MSEC.2008.08.028
|
|
|
“Ordered end-member of ZSM-48 zeolite family”. Kirschhock CEA, Liang D, Van Tendeloo G, Fécant A, Hastoye G, Vanbutsele G, Bats N, Guillon E, Martens JA, Chemistry of materials 21, 371 (2009). http://doi.org/10.1021/cm802614x
Abstract: ZSM-48 and related zeolites are considered to be highly disordered structures. Different polytypes can be clearly distinguished by simulation of high-resolution electron microscopy images. Synthesis of phase-pure polytypes was attempted. One of the investigated samples crystallized via seeding designated as COK-8 consisted of nanoscopic, needlelike crystals with a very large length/width ratio, growing along the pore direction. These specimens are phase-pure polytype 6 (PT6, numbering according to Lobo and van Koningsveld). Aggregates of these nanoneedles occasionally contained a second polytype: PT1. The latter polytype occurred more abundantly in larger crystal rods in an IZM-1 sample crystallized in ethylene glycol. Here too, the isolated crystallites mainly consist of large, defect-free regions of PT6. A simulation of polytype lattice energies offers a rational explanation for the observed polytypical intergrowth formation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 30
DOI: 10.1021/cm802614x
|
|
|
“Pd@MOF-5: limitations of gas-phase infiltration and solution impregnation of [Zn4O(bdc)3] (MOF-5) with metalorganic palladium precursors for loading with Pd nanoparticles”. Esken D, Zhang X, Lebedev OI, Schröder F, Fischer RA, Journal of materials chemistry 19, 1314 (2009). http://doi.org/10.1039/b815977g
Abstract: The limitations of the loading of the porous metalorganic framework [Zn4O(bdc)3] (bdc = benzene-1,4-dicarboxylate; MOF-5 or IRMOF-1) with Pd nanoparticles was investigated. First, the volatile organometallic precursor [Pd(5-C5H5)(3-C3H5)] was employed to get the inclusion compound [Pd(5-C5H5)(3-C3H5)]x@MOF-5 via gas-phase infiltration at 10-3 mbar. A loading of four molecules of [Pd(5-C5H5)(3-C3H5)] per formula unit of MOF-5 (x = 4) can be reached (35 wt.% Pd). Second, the metalorganic precursor [Pd(acac)2] (acac = 2,4-pentanedionate) was used and the inclusion materials [Pd(acac)2]x@MOF-5 of different Pd loadings were obtained by incipient wetness infiltration. However, the maximum loading was lower as compared with the former case with about two precursor molecules per formula unit of MOF-5. Both loading routes are suitable for the synthesis of Pd nanoparticles inside the porous host matrix. Homogeneously distributed nanoparticles with diameter of 2.4(±0.2) nm can be achieved by photolysis of the inclusion compounds [Pd(5-C5H5)(3-C3H5)]x@MOF-5 (x 4), while the hydrogenolysis of [Pd(acac)2]x@MOF-5 (x 2) leads to a mixture of small particles inside the network (< 3 nm) and large Pd agglomerates (40 nm) on the outer surface of the MOF-5 specimens. The pure Pdx@MOF-5 materials proved to be stable under hydrogen pressure (2 bar) at 150 °C over many hours. Neither hydrogenation of the bdc linkers nor particle growth was observed. The new composite materials were characterized by 1H/13C-MAS-NMR, powder XRD, ICP-AES, FT-IR, N2 sorption measurements and high resolution TEM. Raising the Pd loading of a representative sample Pd4@MOF-5 (35 wt.% Pd) by using [Pd(5-C5H5)(3-C3H5)] as precursor in a second cycle of gas-phase infiltration and photolysis was accompanied by the collapse of the long-range crystalline order of the MOF.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 100
DOI: 10.1039/b815977g
|
|
|
“Diamond nucleation by carbon transport from buried nanodiamond TiO2 sol-gel composites”. Doenen M, Zhang L, Erni R, Williams OA, Hardy A, van Bael MK, Wagner P, Haenen K, Nesladek M, Van Tendeloo G, Advanced materials 21, 670 (2009). http://doi.org/10.1002/adma.200802305
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 20
DOI: 10.1002/adma.200802305
|
|
|
“A new mixed-valence ferrite with a cubic structure, YBaFe4O7: spin-glass-like behavior”. Caignaert V, Abakumov AM, Pelloquin D, Pralong V, Maignan A, Van Tendeloo G, Raveau B, Chemistry of materials 21, 1116 (2009). http://doi.org/10.1021/cm803312f
Abstract: A new mixed-valence ferrite, YBaFe4O7, has been synthesized. Its unique cubic structure, with a = 8.9595(2) Å, is closely related to that of the hexagonal 114 oxides YBaCo4O7 and CaBaFe4O7. It consists of corner-sharing FeO4 tetrahedra, forming triangular and kagome layers parallel to (111)C. In fact, the YBaFe4O7 and CaBaFe4O7 structures can be described as two different ccc and chch close packings of [BaO3]∞ and [O4]∞ layers, respectively, whose tetrahedral cavities are occupied by Fe2+/Fe3+ cations. The local structure of YBaFe4O7 is characterized by a large amount of stacking faults originating from the presence of hexagonal layers in the ccc cubic close-packed YBaFe4O7 structure. In this way, they belong to the large family of spinels and hexagonal ferrites studied for their magnetic properties. Differently from all the ferrites and especially from CaBaFe4O7, which are ferrimagnetic, YBaFe4O7 is an insulating spin glass with Tg = 50 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 39
DOI: 10.1021/cm803312f
|
|
|
“Enhancing total conductivity of La2NiO4+\delta epitaxial thin films by reducing thickness”. Burriel M, Santiso J, Rossell MD, Van Tendeloo G, Figueras A, Garcia G, The journal of physical chemistry: C : nanomaterials and interfaces 112, 10982 (2008). http://doi.org/10.1021/jp7101622
Abstract: High quality epitaxial c axis oriented La2NiO4+ä thin films have been prepared by the pulsed injection metal organic chemical vapor deposition technique on different substrates. High-resolution electron microscopy/transmission electron microscopy has been used to confirm the high crystalline quality of the deposited films. The c-parameter evolution has been studied by XRD as a function of time and gas atmosphere. The high temperature transport properties along the basal a−b plane of epitaxial La2NiO4+ä films have been measured, and the total conductivity of the layers has been found to increase as the thickness is reduced. Layers of 50 nm and thinner have shown a maximum conductivity larger than that measured for single-crystals, in particular, the 33 nm thick films with a conductivity of 475 S/cm in oxygen correspond to the highest value measured to date for this material.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 35
DOI: 10.1021/jp7101622
|
|
|
“Direct imaging of loaded metal-organic framework materials (metal@MOF-5)”. Turner S, Lebedev OI, Schroeder F, Fischer RA, Van Tendeloo G, Chemistry of materials 20, 5622 (2008). http://doi.org/10.1021/cm801165s
Abstract: We illustrate the potential of advanced transmission electron microscopy for the characterization of a new class of soft porous materials: metal@Zn4O(bdc)3 (metal@MOF-5; bdc = 1,4-benzenedicarboxylate). By combining several electron microscopy techniques (transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), electron diffraction (ED), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), and electron tomography) and by carefully reducing the electron dose to avoid beam damage, it is possible to simultaneously characterize the MOF-5 framework material and the loaded metal nanoparticles. We also demonstrate that electron tomography can be used to accurately determine the position and distribution of the particles within the MOF-5 framework. To demonstrate the implementation of these microscopy techniques and what kind of results can be expected, measurements on gas-phase-loaded metal−organic framework materials Ru@MOF-5 and Pd@MOF-5 are presented.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 112
DOI: 10.1021/cm801165s
|
|
|
“A layered iron-rich 2234-type with a mixed valence of iron: the ferrimagnetic Tl-doped Fe2(Sr2-\varepsilonTl\varepsilon)Sr3Fe4O14.65”. Lepoittevin C, Malo S, Nguyen N, Hebert S, Van Tendeloo G, Hervieu M, Chemistry of materials 20, 6468 (2008). http://doi.org/10.1021/cm8014385
Abstract: A new Tl-doped strontium ferrite Fe2(Sr2-Tl)Sr3Fe4O14.65, with an original structure, has been synthesized and structurally characterized by powder X-ray diffraction and transmission electron microscopy. The TGA and Mssbauer studies evidence a mixed valence of iron. The structure exhibits a commensurate modulation, with a F-type subcell a ≈ b ≈ 5.4 Å (≈ ap√2), c ≈ 42 Å with a modulation vector q = αa* with α = 0.4. The supercell parameters have been refined as a= 27.1101(8) Å, b= 5.5187(2) Å and c= 42.0513(9) Å, in the space group Fmmm. The electron diffraction and electron microscopy data of this novel ferrite show that it can be described as a FeTl-2234-type structure corresponding to the intergrowth of a quadruple perovskite slice [(SrFeO2.8)4], with a complex rock salt related slice [Fe2(Sr2-Tl)O3.4]∞, built up of one double iron layer [Fe2O2.4] sandwiched between two [SrO] layers. The HRTEM images show that the oxygen atoms and vacancies are randomly distributed in the perovskite layers while the HAADF STEM images evidence the absence of Tl segregation in the matrix. Fe2(Sr2-Tl)Sr3Fe4O14.65 exhibits a very large value of χ (11emu/mol) at 5 K, which remains large at 400 K; the M(H) loop presents a shape characteristic of ferrimagnetism, with a large coercive field of 0.3 T. The value of magnetization saturates at 400 K at 0.68 μB/Fe. At 10 K, the value of magnetization reaches a maximum of 2 μB/Fe. The resistivity presents a semiconducting-like behavior, with ρ 800 Ω·cm at 300 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 8
DOI: 10.1021/cm8014385
|
|
|
“Rapid microwave-assisted synthesis of benzene bridged periodic mesoporous organosilicas”. Smeulders G, Meynen V, van Baelen G, Mertens M, Lebedev OI, Van Tendeloo G, Maes BUW, Cool P, Journal of materials chemistry 19, 3042 (2009). http://doi.org/10.1039/b820792e
Abstract: Following extended use in organic chemistry, microwave-assisted synthesis is gaining more importance in the field of inorganic chemistry, especially for the synthesis of nanoporous materials. It offers some major advantages such as a significant shortening of the synthesis time and an improved promotion of nucleation. In the research here reported, microwave technology is applied for the synthesis of benzene bridged PMOs (periodic mesoporous organosilicas). PMOs are one of the latest innovations in the field of hybrid ordered mesoporous materials and have attracted much attention because of their feasibility in electronics, catalysis, separation and sorption applications. The different synthesis steps (stirring, aging and extraction) of the classical PMO synthesis are replaced by microwave-assisted synthesis steps. The characteristics of the as-synthesized materials are evaluated by X-ray diffraction, N2-sorption, thermogravimetric analysis, scanning- and transmission electron microscopy. The microwave-assisted synthesis drastically reduces the synthesis time by more than 40 hours without any loss in structural properties, such as mesoscale and molecular ordering. The porosity of the PMO materials has even been improved by more than 25%. Moreover, the number of handling/transfer steps and amounts of chemicals and waste are drastically reduced. The study also shows that there is a clear time (1 to 3 hours) and temperature frame (373 K to 403 K) wherein synthesis of benzene bridged PMO is optimal. In conclusion, the microwave-assisted synthesis pathway allows an improved material to be obtained in a more economical way i.e. a much shorter time with fewer chemicals and less waste.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY)
Times cited: 20
DOI: 10.1039/b820792e
|
|
|
“Combined SEM/EDX and micro-Raman spectroscopy analysis of uranium minerals from a former uranium mine”. Stefaniak EA, Alsecz A, Frost R, Máthé, Z, Sajó, IE, Török S, Worobiec A, Van Grieken R, Journal of hazardous materials 168, 416 (2009). http://doi.org/10.1016/J.JHAZMAT.2009.02.057
Abstract: Samples of the secondary uranium minerals collected in the abandoned uranium mine at Pecs (Hungary) were investigated by two micro-techniques: scanning electron microscopy (SEM/EDX) and micro-Raman spectroscopy (MRS). They were applied to locate U-rich particles and identify the chemical form and oxidation state of the uranium compounds. The most abundant mineral was a K and/or Na uranyl sulphate (zippeite group). U(VI) was also present in the form showing intensive Raman scattering at 860 cm−1 which can be attributed to uranium trioxide. This research has shown the successful application of micro-Raman spectroscopy for the identification of uranyl mineral species on the level of individual particles.
Keywords: A1 Journal article; Laboratory Experimental Medicine and Pediatrics (LEMP); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.JHAZMAT.2009.02.057
|
|
|
“Comment on ALaMn2O6-y (A = K, Rb): novel ferromagnetic manganites exhibiting negative giant magnetoresistance”. Hadermann J, Abakumov AM, Van Rompaey S, Mankevich AS, Korsakov IE, Chemistry of materials 21, 2000 (2009). http://doi.org/10.1021/cm900298a
Keywords: Editorial; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 4
DOI: 10.1021/cm900298a
|
|
|
“Advanced electron microscopy and its possibilities to solve complex structures: application to transition metal oxides”. Van Tendeloo G, Hadermann J, Abakumov AM, Antipov EV, Journal of materials chemistry 19, 2660 (2009). http://doi.org/10.1039/b817914j
Abstract: Design and optimization of materials properties can only be performed through a thorough knowledge of the structure of the compound. In this feature article we illustrate the possibilities of advanced electron microscopy in materials science and solid state chemistry. The different techniques are briefly discussed and several examples are given where the structures of complex oxides, often with a modulated structure, have been solved using electron microscopy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 9
DOI: 10.1039/b817914j
|
|
|
“Characterization of gas concrete materials used in buildings of Turkey”. Damla N, Čevik U, Kobya AI, Celik A, Van Grieken R, Kobya Y, Journal of hazardous materials 168, 681 (2009). http://doi.org/10.1016/J.JHAZMAT.2009.02.092
Abstract: The activity concentration of 226Ra, 232Th and 40K in gas concrete samples collected from different suppliers and some provinces in Turkey were measured using gamma-ray spectrometry. Knowledge of radioactivity in gas concrete used in building materials enables one to assess any possible radiological risks to human health. The mean activity concentrations observed in the gas concrete samples were 82.0, 28.2 and 383.9 Bq kg−1 for 226Ra, 232Th and 40K, respectively. The radium equivalent activity, external and internal hazard indices as well as terrestrial absorbed dose and annual effective dose rate was calculated. The results indicate that the radium equivalent activity values of gas concrete samples are lower than the limit of 370 Bq kg−1, equivalent to a gamma-dose of 1.5 mSv y−1. Moreover, mass attenuation coefficients were measured in some gas concrete samples. It was found that the mass attenuation coefficients decreased with increasing photon energies. Also, chemical compositions and structural analysis (XRD and SEM) of the gas concrete samples were investigated.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.JHAZMAT.2009.02.092
|
|
|
“One-pot synthesis of catalytically stable and active nanoreactors: encapsulation of size-controlled nanoparticles within a hierarchically macroporous core@ordered mesoporous shell system”. Yang X-Y, Li Y, Van Tendeloo G, Xiao F-S, Su B-L, Advanced materials 21, 1368 (2009). http://doi.org/10.1002/adma.200802914
Abstract: Size-controlled, catalytically active nanoparticles are successfully encapsulated in a one-pot synthesis to form novel hierarchical macroporous core@mesoporous shell structures, where macroporous cores are connected by uniform and ordered mesoporous channels. Most importantly, the encapsulated nanoparticles can be used as nanoreactors, with high activities and excellent long-term recycling stability.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 61
DOI: 10.1002/adma.200802914
|
|
|
“La2MnVO6 double perovskite: a structural, magnetic and X-ray absorption investigation”. Mandal TK, Croft M, Hadermann J, Van Tendeloo G, Stephens PW, Greenblatt M, Journal of materials chemistry 19, 4382 (2009). http://doi.org/10.1039/b823513a
Abstract: The synthesis, electron diffraction (ED), synchrotron X-ray and neutron structure, X-ray absorption spectroscopy (XAS) and magnetic property studies of La2MnVO6 double perovskite are described. Analysis of the synchrotron powder X-ray diffraction data for La2MnVO6 indicates a disordered arrangement of Mn and V at the B-site of the perovskite structure. Absence of super-lattice reflections in the ED patterns for La2MnVO6 supports the disordered cation arrangement. Room temperature time-of-flight (TOF) neutron powder diffraction (NPD) data show no evidence of cation ordering, in corroboration with the ED and synchrotron studies (orthorhombic Pnma, a = 5.6097(3), b = 7.8837(5) and c = 5.5668(3) ; 295 K, NPD). A comparison of XAS analyses of La2TVO6 with T = Ni and Co shows T2+ formal oxidation state while the T = Mn material evidences a Mn3+ admixture into a dominantly Mn2+ ground state. V-K edge measurements manifest a mirror image behavior with a V4+ state for T = Ni and Co with a V3+ admixture arising in the T = Mn material. The magnetic susceptibility data for La2MnVO6 show ferromagnetic correlations; the observed effective moment, µeff (5.72 µB) is much smaller than the calculated moment (6.16 µB) based on the spin-only formula for Mn2+ (d5, HS) /V4+ (d1), supportive of the partly oxidized Mn and reduced V scenario (Mn3+/V3+).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 10
DOI: 10.1039/b823513a
|
|
|
“3D reconstruction of Ni4Ti3 precipitates in a Ni51Ti49 alloy in a FIB/SEM dual-beam system”. Cao S, Tirry W, van den Broek W, Schryvers D, Materials science forum 583, 277 (2008). http://doi.org/10.4028/www.scientific.net/MSF.583.277
Abstract: Ni4Ti3 precipitates play an important role in the shape memory and superelastic behaviour of thermo-mechanically treated Ni-Ti material. The 3D morphology and distribution of such precipitates with lenticular shape and rhombohedral atomic structure in the austenitic B2 matrix of a binary Ni-rich Ni-Ti alloy has been elucidated via a slice view procedure in a Dual-Beam FIB/SEM system. With the sequence of cross-section SE images obtained from the SEM, a 3D reconstruction has been achieved after proper alignment and image processing, from which both qualitative and quantitative analysis can be performed. Careful imaging is needed to ensure that all variants of the precipitates are observed with equal probability, regardless sample orientation. Moreover, due to the weak contrast of the precipitates, proper imaging conditions need to be selected to allow for semi-automated image treatment. Finally, a volume ratio of 10.2% for the Ni4Ti3 precipitates could be calculated, summed over all variants, which yields a net composition of Ni50.36Ti49.64 for the matrix, leading to an increase of 113 degrees for the martensitic start temperature Ms. Also, the expected relative orientation of the different variants of the precipitates could be confirmed. In the near future, other quantitative measures on the distribution of the precipitates can be expected.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
DOI: 10.4028/www.scientific.net/MSF.583.277
|
|
|
“Fabrication and characterization of functionally graded Ni-Ti multilayer thin films”. Tian H, Schryvers D, Mohanchandra KP, Carman GP, van Humbeeck J, Functional materials letters 2, 61 (2009). http://doi.org/10.1142/S1793604709000570
Abstract: A functionally graded multilayer NiTi thin film was deposited on a SiO2/Si substrate by d.c. sputtering using a ramped heated NiTi alloy target. The stand-alone films were crystallized at 500°C in vacuum better than 10-7 Torr. Transmission electron microscopy micrographs taken along the film cross section show two distinct regions, thin and thick, with weak R and B2 phases, respectively. The film compositions along the thickness were measured and quantified using the standard-less EELSMODEL method. The film deposited during the initial thermal ramp (thin regions) displays an average of 54 at.% Ni while the film deposited at a more elevated target temperature (thick regions) shows about 51 at.% Ni.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.234
Times cited: 9
DOI: 10.1142/S1793604709000570
|
|
|
“Microstructure and functional property changes in thin Ni-Ti wires heat teated by electric current: high energy X-ray and TEM investigations”. Malard B, Pilch J, Sittner P, Gartnerova V, Delville R, Schryvers D, Curfs C, Functional materials letters 2, 45 (2009). http://doi.org/10.1142/S1793604709000557
Abstract: High energy synchrotron X-ray diffraction, transmission electron microscopy and mechanical testing were employed to investigate the evolution of microstructure, texture and functional superelastic properties of 0.1 mm thin as drawn NiTi wires subjected to a nonconventional heat treatment by controlled electric current (FTMT-EC method). As drawn NiTi wires were prestrained in tension and exposed to a sequence of short DC power pulses in the millisecond range. The annealing time in the FTMT-EC processing can be very short but the temperature and force could be very high compared to the conventional heat treatment of SMAs. It is shown that the heavily strained, partially amorphous microstructure of the as drawn NiTi wire transforms under the effect of the DC pulse and tensile stress into a wide range of annealed nanosized microstructures depending on the pulse time. The functional superelastic properties and microstructures of the FTMT-EC treated NiTi wire are comparable to those observed in straight annealed wires.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.234
Times cited: 21
DOI: 10.1142/S1793604709000557
|
|
|
“Linking a completely three-dimensional nanostrain to a structural transformation eigenstrain”. Tirry W, Schryvers D, Nature materials 8, 752 (2009). http://doi.org/10.1038/NMAT2488
Abstract: NiTi is one of the most popular shape-memory alloys, a phenomenon resulting from a martensitic transformation. Commercial NiTi-based alloys are often thermally treated to contain Ni4Ti3 precipitates. The presence of these precipitates can introduce an extra transformation step related to the so-called R-phase. It is believed that the strain field surrounding the precipitates, caused by the matrixprecipitate lattice mismatch, lies at the origin of this intermediate transformation step. Atomic-resolution transmission electron microscopy in combination with geometrical phase analysis is used to measure the elastic strain field surrounding these precipitates. By combining measurements from two different crystallographic directions, the three-dimensional strain matrix is determined from two-dimensional measurements. Comparison of the measured strain matrix to the eigenstrain of the R-phase shows that both are very similar and that the introduction of the R-phase might indeed compensate the elastic strain introduced by the precipitate.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 39.737
Times cited: 53
DOI: 10.1038/NMAT2488
|
|
|
“Multiwalled carbon nanotubes functionalized with 7-octenyltrichlorosilane and n-octyltrichlorosilane: dispersion in Sylgard®184 silicone and Youngs modulus”. Vast L, Carpentier L, Lallemand F, Colomer J-F, Van Tendeloo G, Fonseca A, Nagy JB, Mekhalif Z, Delhalle J, Journal of materials science 44, 3476 (2009). http://doi.org/10.1007/s10853-009-3464-1
Abstract: Sylgard®184/multiwalled carbon nanotube (MWNT) composites have been prepared by in situ polymerization using purified and functionalized multiwalled carbon nanotubes (f-MWNTs) as fillers. Surface modification of the MWNTs has been carried out by silanization with 7-octenyltrichlorosilane (7OTCS) and n-octyltrichlorosilane (nOTCS). The modification and dispersion of the carbon nanotubes in composites were characterized by X-ray photoelectron spectroscopy (XPS), transmission electron spectroscopy (TEM), and high-resolution transmission electron spectroscopy (HRTEM). Youngs modulus results were derived from indentation testing. It is shown that the terminal-vinyl group of 7OTCS molecules plays an essential role for both the dispersion of the f-MWNTs in the composite and its mechanical properties. At loading as low as 0.2 wt%, the Youngs modulus is shown to increase up to 50%. This is interpreted as resulting from a combination of the good compatibility in the forming silicone matrix of the MWNTs coated with a siloxane network, on the one hand, and the covalent links created between the terminal-vinyl groups and the host matrix in formation, on the other hand.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.599
Times cited: 16
DOI: 10.1007/s10853-009-3464-1
|
|