“Direct observation of laser-induced crystallization of a-C : H films”. Nistor LC, van Landuyt J, Ralchenko VG, Kononenko TV, Obraztsova ED, Strelnitsky VE, Applied physics A : materials science &, processing 58, 137 (1994). http://doi.org/10.1007/BF00332170
Abstract: The post-growth modification of diamond-like amorphous hydrogenated carbon a-C:H films by laser treatment has been studied by transmission electron microscopy and Raman spectroscopy. a-C:H films grown on Si substrates by benzene decomposition in a rf glow discharge were irradiated with 15 ns pulses of a KrF-excimer laser with fluences in the ran e of E = 50-700 mJ/cm(2). At fluences below 100 mJ/cm(2) an increase in the number of graphitic clusters and in their ordering was evidenced from Raman spectra, while the film structure remained amorphous according to electron microscopy and electron diffraction observations. At higher fluences the appearance of diamond particles of 2-7 nm size, embedded into the lower crystallized graphitic matrix, was observed and simultaneously a progressive growth of graphite nanocrystals with dimensions from 2 nm to 4 nm was deduced from Raman measurements. The maximum thickness of the crystallized surface layer (approximate to 400 nm) and the degree of laser annealing are limited by the film ablation which starts at E > 250 mJ/cm(2). The laser-treated areas lose their chemical inertness. In particular, chemical etching in chromium acid becomes possible, which may be used for patterning the highly inert carbon films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 73
DOI: 10.1007/BF00332170
|
“Nanodiamond photoemitters based on strong narrow-band luminescence from silicon-vacancy defects”. Vlasov II, Barnard AS, Ralchenko VG, Lebedev OI, Kanzyuba MV, Saveliev AV, Konov VI, Goovaerts E, Advanced materials 21, 808 (2009). http://doi.org/10.1002/adma.200802160
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Nanostructured and organic optical and electronic materials (NANOrOPT)
Impact Factor: 19.791
Times cited: 98
DOI: 10.1002/adma.200802160
|
“Hybrid diamond-graphite nanowires produced by microwave plasma chemical vapor deposition”. Vlasov IL, Lebedev OI, Ralchenko VG, Goovaerts E, Bertoni G, Van Tendeloo G, Konov VI, Advanced materials 19, 4058 (2007). http://doi.org/10.1002/adma.200700442
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Nanostructured and organic optical and electronic materials (NANOrOPT)
Impact Factor: 19.791
Times cited: 75
DOI: 10.1002/adma.200700442
|
“Microstructural characterization of diamond films deposited on c-BN crystals”. Nistor L, Buschmann V, Ralchenko V, Dinca G, Vlasov I, van Landuyt J, Fuess H, Diamond and related materials
T2 –, 10th European Conference on Diamond, Diamond-Like Materials, Nitrides, and Silicon Carbide (Diamond 1999), SEP 12-17, 1999, PRAGUE, CZECH REPUBLIC 9, 269 (2000). http://doi.org/10.1016/S0925-9635(99)00246-0
Abstract: The morphology and structure of diamond films, deposited on cubic boron nitride (c-BN) crystals by microwave-plasma-enhanced chemical vapor deposition, is studied by high-resolution scanning electron microscopy and micro-Raman spectroscopy. The c-BN crystals, with sizes of 200 to 350 mu m and grown by a high-temperature/high-pressure technique, were embedded in a copper holder, and used as substrates in deposition runs of 15 min to 5 h. The nucleation centers for diamond appear as well-shaped cuboctahedral crystallites, having diameters of approximately 100 nm. With increasing deposition time the diamond crystallites grew larger, forming islands on the c-BN faces. In some cases, epitaxial growth was observed on the (111) c-BN faces where coalesced particles gave rise to very smooth regions. A number of diamond crystals with peculiar shapes are observed, such as a pseudo five-fold symmetry due to multiple twinning. Moreover, both randomly distributed carbon tubes, about 100 nn in diameter and 1 mu m in length, and spherically shaped features are observed in samples prepared under the typical conditions of diamond deposition, this effect being ascribed to the influence of plasma-sputtered copper contamination. Quite unusual diamond crystals with a deep, pyramidal-shaped hole in the middle grew on the copper substrate between the c-BN crystals. (C) 2000 Elsevier Science S.A. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 9
DOI: 10.1016/S0925-9635(99)00246-0
|
“Structural aspects of CVD idamond wafers grown at different hydrogen flow rates”. Nistor L, van Landuyt J, Ralchenko V, Physica status solidi: A: applied research 171, 5 (1999). http://doi.org/10.1002/(SICI)1521-396X(199907)174:1<5::AID-PSSA5>3.3.CO;2-3
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 15
DOI: 10.1002/(SICI)1521-396X(199907)174:1<5::AID-PSSA5>3.3.CO;2-3
|
“Nanocrystalline diamond films: transmission electron microscopy and Raman spectroscopy characterization”. Nistor LC, van Landuyt J, Ralchenko VG, Obratzova ED, Smolin AA, Diamond and related materials 6, 159 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 116
|
“Structural studies of nanocrystalline diamond thin films”. Nistor LC, van Landuyt J, Ralchenko VG, Obratzova ED, Korothushenko KG, Smolin AA, Materials science forum 239-241, 115 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
“Formation of diamond nanocrystals in laser-irradiated amorphous carbon films”. Nistor LC, van Landuyt J, Ralchenko VG, Kononenko TV, Obraztsova ED, Strelnitsky VE, International Conference on the New Diamond Science and Technology 4, 25 (1994)
Keywords: P3 Proceeding; Electron microscopy for materials research (EMAT)
|