“Tilted BaHfO3 nanorod artificial pinning centres in REBCO films on inclined substrate deposited-MgO coated conductor templates”. Stafford BH, Sieger M, Ottolinger R, Meledin A, Strickland NM, Wimbush SC, Van Tendeloo G, Huehne R, Schultz L, Superconductor science and technology 30, 055002 (2017). http://doi.org/10.1088/1361-6668/AA621D
Abstract: We grow BaHfO3 (BHO) nanorods in REBa2Cu3O7-x (REBCO, RE: Gd or Y) thin films on metal tapes coated with the inclined substrate deposited (ISD)-MgO template by both electron beam physical vapour deposition and pulsed laser deposition. In both cases the nanorods are inclined by an angle of 21 degrees-29 degrees with respect to the sample surface normal as a consequence of the tilted growth of the REBCO film resulting from the ISD-MgO layer. We present angular critical current density (J(c)) anisotropy as well as field- and temperature-dependant J(c) data of the BHO nanorod-containing GdBCO films demonstrating an increase in J(c) over a wide range of temperatures between 30 and 77 K and magnetic fields up to 8 T. In addition, we show that the angle of the peak in the J(c) anisotropy curve resulting from the nanorods is dependent both on temperature and magnetic field. The largest J(c) enhancement from the addition of the nanorods was found to occur at 30 K, 3 T, resulting in a J(c) of 3.0 MA cm(-2).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 6
DOI: 10.1088/1361-6668/AA621D
|
“Influence of artificial pinning centers on structural and superconducting properties of thick YBCO films on ABAD-YSZ templates”. Pahlke P, Sieger M, Ottolinger R, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Haenisch J, Holzapfel B, Schultz L, Nielsch K, Huehne R, Superconductor science and technology 31, 044007 (2018). http://doi.org/10.1088/1361-6668/AAAFBE
Abstract: Recent efforts in the development of YBa2Cu3O7-x (YBCO) coated conductors are devoted to the increase of the critical current I-c in magnetic fields. This is typically realized by growing thicker YBCO layers as well as by the incorporation of artificial pinning centers. We studied the growth of doped YBCO layers with a thickness of up to 7 mu m using pulsed laser deposition with a growth rate of about 1.2 nm s(-1). Industrially fabricated ion-beam textured YSZ templates based on metal tapes were used as substrates for this study. The incorporation of BaHfO3 (BHO) or Ba2Y(Nb0.5Ta0.5)O-6 (BYNTO) secondary phase additions leads to a denser microstructure compared to undoped films. A purely c-axis-oriented YBCO growth is preserved up to a thickness of about 4 mu m, whereas misoriented texture components were observed in thicker films. The critical temperature is slightly reduced compared to undoped films and independent of film thickness. The critical current density J(c) of the BHO- and BYNTO-doped YBCO layers is lower at 77 K and self-field compared to pure YBCO layers; however, I-c increases up to a thickness of 5 mu m. A comparison between films with a thickness of 1.3 mu m revealed that the anisotropy of the critical current density J(c)(theta) strongly depends on the incorporated pinning centers. Whereas BHO nanorods lead to a strong B vertical bar vertical bar c-axis peak, the overall anisotropy is significantly reduced by the incorporation of BYNTO forming a mixture of short c-axis-oriented nanorods and small (a-b)-oriented platelets. As a result, the J(c) values of the doped films outperform the undoped samples at higher fields and lower temperatures for most magnetic field directions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 9
DOI: 10.1088/1361-6668/AAAFBE
|
“Electronically tunable quantum phase slips in voltage-biased superconducting rings as a base for phase-slip flux qubits”. Kenawy A, Magnus W, Milošević, MV, Sorée B, Superconductor Science &, Technology 33, 125002 (2020). http://doi.org/10.1088/1361-6668/ABB8EB
Abstract: Quantum phase slips represent a coherent mechanism to couple flux states of a superconducting loop. Since their first direct observation, there have been substantial developments in building charge-insensitive quantum phase-slip circuits. At the heart of these devices is a weak link, often a nanowire, interrupting a superconducting loop. Owing to the very small cross-sectional area of such a nanowire, quantum phase slip rates in the gigahertz range can be achieved. Instead, here we present the use of a bias voltage across a superconducting loop to electrostatically induce a weak link, thereby amplifying the rate of quantum phase slips without physically interrupting the loop. Our simulations reveal that the bias voltage modulates the free energy barrier between subsequent flux states in a very controllable fashion, providing a route towards a phase-slip flux qubit with a broadly tunable transition frequency.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.6
Times cited: 4
DOI: 10.1088/1361-6668/ABB8EB
|