“Metal to insulator transition in the n-type hollandite vanadate Pb1.6V8O16”. Maignan A, Lebedev OI, Van Tendeloo G, Martin C, Hebert S, Physical review : B : condensed matter and materials physics 82, 035122 (2010). http://doi.org/10.1103/PhysRevB.82.035122
Abstract: The transport and magnetic measurements of polycrystalline Pb1.6V8O16 hollandite reveal a concomitant metal to insulator and antiferromagnetic transition at TMI≈140 K. A clear localization is found below TMI, evidenced by a rapid increase in the absolute value of the negative Seebeck coefficient. The structural study by x-ray and transmission electron microscopy confirms the hollandite structure and shows that no structural transition occurs at TMI, ruling out a possible charge orbital ordering. The negative Seebeck coefficient observed from 50 K up to 900 K, with values reaching S=−38 μV K−1 at 900 K, is explained by the electron doping of ∼1.4e− in the V empty t2g orbitals responsible for the bad metal resistivity (ρ900 K∼2 mΩ cm). As this S value is close to that obtained by considering only the spin and orbital degeneracies, it is expected that |S| for such vanadates will not be sensitive at high temperature to the t2g band filling
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 10
DOI: 10.1103/PhysRevB.82.035122
|
|
|
“Metallic nanoparticles on plasma treated carbon nanotubes : $Nano2hybrids$”. Bittencourt C, Felten A, Douhard B, Colomer J-F, Van Tendeloo G, Drube W, Ghijsen J, Pireaux J-J, Surface science : a journal devoted to the physics and chemistry of interfaces
T2 –, International Conference on NANO-Structures Self Assembling, JUL 02-06, 2006, Aix en Provence, FRANCE 601, 2800 (2007). http://doi.org/10.1016/j.susc.2006.12.045
Abstract: Multi-wall carbon nanotubes (MWCNTs) were decorated with metal clusters by thermal evaporation. Transmission electron microscopy (TEM) shows that the nature and extent of metal coverage can be varied by plasma treating the MWCNT surface. The metal clusters on oxygen plasma treated arc-discharge MWCNTs have a more dense distribution than the clusters evaporated on as-synthesized are-discharge MWCNTs. In contrast, the plasma treatment did not affect the cluster distribution on CVD MWCNTs. Analyses of the valence band and the core levels by X-ray photoelectron spectroscopy suggest poor charge transfer between gold clusters and MWCNTs; on the contrary suggest good charge transfer between Ni clusters and MWCNTs. (c) 2007 Elsevier B. V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.062
Times cited: 44
DOI: 10.1016/j.susc.2006.12.045
|
|
|
“Metals and alloys”. de Hosson JTM, Van Tendeloo G Vch, Weinheim, page 1 (1997).
Keywords: H3 Book chapter; Electron microscopy for materials research (EMAT)
|
|
|
“Metals and alloys: 2: phase transformations”. Schryvers D, Van Tendeloo G Vch, Weinheim, page 80 (1997).
Keywords: H3 Book chapter; Electron microscopy for materials research (EMAT)
|
|
|
“Metals@MOFs –, loading MOFs with metal nanoparticles for hybrid functions”. Meilikhov M, Yusenko K, Esken D, Turner S, Van Tendeloo G, Fischer RA, European journal of inorganic chemistry 2010, 3701 (2010). http://doi.org/10.1002/ejic.201000473
Abstract: Metalorganic frameworks (MOFs) as well as porous coordination polymers (PCPs) are porous, organicinorganic hybrid solids with zeolite-like structures and properties. Due to their extraordinarily high surface area and well defined pore structure MOFs can be used for the stabilization of metal nanoparticles with adjustable size. The embedded metal nanoparticles are still accessible for other reagents due to the high porosity of the MOF systems. This fact makes metal@MOF systems especially interesting for heterogeneous catalysis, gas storage and chemical sensing. This review compiles the cases of metal nanoparticles supported by or embedded into MOFs reported so far and the main aspects and problems associated with these novel nanocomposite systems. The determination of the dispersion and the location of the particles at the MOF support, the control of the loading degree and its effect on the catalytic activity of the system are discussed as well as the partial degradation of the MOF structure upon particle formation. Examples of the introduction of stabilizing groups into the MOF network that direct the loading and can influence the size and shape of the embedded particles are still rare and point into the possible direction of future investigations. Finally, the formation of bimetallic nanoparticles, which are stabilized and supported by a MOF network, will also be reviewed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
Times cited: 366
DOI: 10.1002/ejic.201000473
|
|
|
“The metastable Ni7\pm xS6 and mixed Ni6\pm x(S1-ySey)5 phases”. Liu Y, Norén L, Withers RL, Hadermann J, Van Tendeloo G, Garcia-Garcia J, Journal of solid state chemistry 170, 351 (2003). http://doi.org/10.1016/S0022-4596(02)00123-8
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/S0022-4596(02)00123-8
|
|
|
“A method to determine the local surface profile from reconstructed exit waves”. Wang A, Chen FR, Van Aert S, van Dyck D, Ultramicroscopy 111, 1352 (2011). http://doi.org/10.1016/j.ultramic.2011.04.005
Abstract: Reconstructed exit waves are useful to quantify unknown structure parameters such as the position and composition of the atom columns at atomic scale. Existing techniques provide a complex wave in a flat plane which is close to the plane where the electrons leave the atom columns. However, due to local deviation in the flatness of the exit surface, there will be an offset between the plane of reconstruction and the actual exit of a specific atom column. Using the channelling theory, it has been shown that this defocus offset can in principle be determined atom column-by-atom column. As such, the surface roughness could be quantified at atomic scale. However, the outcome strongly depends on the initial plane of reconstruction especially in a crystalline structure. If this plane is further away from the true exit, the waves of the atom columns become delocalized and interfere mutually which strongly complicates the interpretation of the exit wave in terms of the local structure. In this paper, we will study the delocalization with defocus using the channelling theory in a more systematic way.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 3
DOI: 10.1016/j.ultramic.2011.04.005
|
|
|
“Methods of structural analysis of modulated structures and quasicrystals”. van Landuyt J, Kuypers S, van Heurck C, Van Tendeloo G, Amelinckx S s.l., page 205 (1993).
Keywords: H3 Book chapter; Electron microscopy for materials research (EMAT)
|
|
|
“Micro-structure of fullerites and high Tc superconductors”. Van Tendeloo G, Krekels T, Amelinckx S Granada, page 17 (1992).
Keywords: H3 Book chapter; Electron microscopy for materials research (EMAT)
|
|
|
“Microscopic origin of dimerization in the CuO2 chains in Sr14Cu24O41”. Hiroi Z, Amelinckx S, Van Tendeloo G, Kobayashi N, Physical review : B : condensed matter and materials physics 54, 849 (1996). http://doi.org/10.1103/PhysRevB.54.15849
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.736
Times cited: 33
DOI: 10.1103/PhysRevB.54.15849
|
|
|
“La microscopie électronique à, transmission (MET) et son utilisation dans l'étude d'inclusions nano-cristallines dans le verre”. Fredrickx P, Schryvers D, L'archéométrie au service des monuments et des oeuvres d'art 10, 131 (2002)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Microscopy of gemmological materials”. van Landuyt J, van Bockstael MHG, van Royen J Vch, Weinheim, page 293 (1997).
Keywords: H3 Book chapter; Electron microscopy for materials research (EMAT)
Times cited: 4
|
|
|
“Microstructural analysis of 9.7% efficient Cu2ZnSnSe4 thin film solar cells”. Buffière M, Brammertz G, Batuk M, Verbist C, Mangin D, Koble C, Hadermann J, Meuris M, Poortmans J, Applied physics letters 105, 183903 (2014). http://doi.org/10.1063/1.4901401
Abstract: This work presents a detailed analysis of the microstructure and the composition of our record Cu 2ZnSnSe4 (CZTSe)-CdS-ZnO solar cell with a total area efficiency of 9.7%. The average composition of the CZTSe crystallites is Cu 1.94 Zn 1.12Sn0.95Se3.99. Large crystals of ZnSe secondary phase (up to 400 nm diameter) are observed at the voids between the absorber and the back contact, while smaller ZnSe domains are segregated at the grain boundaries and close to the surface of the CZTSe grains. An underlying layer and some particles of Cu xSe are observed at the Mo-MoSe2-Cu2ZnSnSe4 interface. The free surface of the voids at the back interface is covered by an amorphous layer containing Cu, S, O, and C, while the presence of Cd, Na, and K is also observed in this region.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 17
DOI: 10.1063/1.4901401
|
|
|
“Microstructural and physical properties of layered manganite oxides related to the magnetoresistive perovskites”. Laffez P, Van Tendeloo G, Seshadri R, Hervieu M, Martin C, Maignan A, Raveau B, Journal of applied physics 80, 5850 (1996). http://doi.org/10.1063/1.363578
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.183
Times cited: 36
DOI: 10.1063/1.363578
|
|
|
“Microstructural aspects of the degradation behavior of SnO2-based anodes for aluminum electrolysis”. Vassiliev SY, Laurinavichute VK, Abakumov AM, Govorov VA, Bendovskii EB, Turner S, Filatov AY, Tarasovskii VP, Borzenko AG, Alekseeva AM, Antipov EV, Journal of the electrochemical society 157, C178 (2010). http://doi.org/10.1149/1.3327903
Abstract: The performance of SnO2 ceramic anodes doped with copper and antimony oxides was examined in cryolite alumina melts under anodic polarization at different cryolite ratios, temperatures, times, and current densities. The corroded part consists of a narrow strong corrosion zone at the anode surface with damage of the intergrain contacts and a large increase in porosity, a wider moderate corrosion zone with a smaller porosity increase, and a Cu depletion zone, where the ceramic retains its initial microstructure and a slight porosity increase occurs due to the removal of the Cu-rich inclusions. Mechanical destruction of the anode was never observed in the 10100 h tests. A microstructural model of the ceramic was suggested, consisting of grains with an Sb-doped SnO2 grain core surrounded by an ~200 to 500 nm grain shell where SnO2 was simultaneously doped with Sb and Mn+ (M=Cu2+,Fe3+,Al3+). The grains were separated by a few nanometers thick Cu-enriched grain boundaries. Different secondary charge carrier (holes) concentrations and electric conductivities in the grain core and grain shell result in a higher current density at the intergrain regions that leads to their profound degradation, especially in the low temperature acidic melt.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.259
Times cited: 3
DOI: 10.1149/1.3327903
|
|
|
“Microstructural characterization of diamond films deposited on c-BN crystals”. Nistor L, Buschmann V, Ralchenko V, Dinca G, Vlasov I, van Landuyt J, Fuess H, Diamond and related materials
T2 –, 10th European Conference on Diamond, Diamond-Like Materials, Nitrides, and Silicon Carbide (Diamond 1999), SEP 12-17, 1999, PRAGUE, CZECH REPUBLIC 9, 269 (2000). http://doi.org/10.1016/S0925-9635(99)00246-0
Abstract: The morphology and structure of diamond films, deposited on cubic boron nitride (c-BN) crystals by microwave-plasma-enhanced chemical vapor deposition, is studied by high-resolution scanning electron microscopy and micro-Raman spectroscopy. The c-BN crystals, with sizes of 200 to 350 mu m and grown by a high-temperature/high-pressure technique, were embedded in a copper holder, and used as substrates in deposition runs of 15 min to 5 h. The nucleation centers for diamond appear as well-shaped cuboctahedral crystallites, having diameters of approximately 100 nm. With increasing deposition time the diamond crystallites grew larger, forming islands on the c-BN faces. In some cases, epitaxial growth was observed on the (111) c-BN faces where coalesced particles gave rise to very smooth regions. A number of diamond crystals with peculiar shapes are observed, such as a pseudo five-fold symmetry due to multiple twinning. Moreover, both randomly distributed carbon tubes, about 100 nn in diameter and 1 mu m in length, and spherically shaped features are observed in samples prepared under the typical conditions of diamond deposition, this effect being ascribed to the influence of plasma-sputtered copper contamination. Quite unusual diamond crystals with a deep, pyramidal-shaped hole in the middle grew on the copper substrate between the c-BN crystals. (C) 2000 Elsevier Science S.A. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 9
DOI: 10.1016/S0925-9635(99)00246-0
|
|
|
“Microstructural dependence on middle eigenvalue in Ti-Ni-Au”. Shi H, Delville R, Srivastava V, James RD, Schryvers D, Journal of alloys and compounds 582, 703 (2013). http://doi.org/10.1016/j.jallcom.2013.08.132
Abstract: The microstructure of various compounds of the Ti-Ni-Au alloy system is investigated by transmission electron microscopy in relation with changing lattice parameters improving the compatibility conditions between austenite and martensite expressed by the lambda(2) = 1 equation based on the Geometrically NonLinear Theory of Martensite (GNLTM). Although local differences in microstructure are observed, when increasing the gold content compound twins are replaced by Type I twins, while twinned lamellar structures are replaced by untwinned plates and self-accommodating structures when lambda(2) = 1 is approached, all confirming the predictions of the GNLTM. (c) 2013 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 8
DOI: 10.1016/j.jallcom.2013.08.132
|
|
|
“Microstructural investigation of a La1.9Sr0.1CuO4 thin film grown by MBE under a large compressive strain”. Seo JW, Perret J, Fompeyrine J, Loquet J-P, Van Tendeloo G, Electron microscopy: vol. 2 , 287 (1998)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Microstructural investigation of BaTiO3 thin films deposited on (001) MgO”. Lei CH, Van Tendeloo G, Siegert M, Schubert J, Journal of materials research 17, 1923 (2002). http://doi.org/10.1557/JMR.2002.0285
Abstract: The microstructure of BaTiO3 thin films, epitaxially deposited on (001) MgO by pulsed laser ablation, has been investigated by transmission electron microscopy. The films are always c-axis-orientated, but dislocations, {111} stacking faults, and antiphase boundaries are frequently observed. Conventional TEM and high-resolution microscopy allow one to deduce the Burgers vectors of dislocations as b(1) = <100> or b(2) = <110>, both being perfect dislocations. Most extrinsic stacking faults are ending at 1/3<112> or 1/3<111> partial dislocations; the displacement vector of the antiphase boundaries is 1/2<101>. Studying the interfacial structure by means of zone images taken along [100] and [110] shows that the misfit is mainly released by dislocations with Burgers vectors of 1/2<110> and 1/2<101>.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.673
Times cited: 8
DOI: 10.1557/JMR.2002.0285
|
|
|
“Microstructural investigation of La1.9Sr0.1CuO4 thin film grown by MBE”. Seo JW, Perret J, Fompeyrine J, Van Tendeloo G, Loquet J-P s.l., page 300 (1998).
Keywords: H3 Book chapter; Electron microscopy for materials research (EMAT)
|
|
|
“Microstructural mechanism of development in photothermographic materials”. Potapov PL, Schryvers D, Strijckers H, van Roost C, The journal of imaging science and technology 47, 115 (2003)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.348
|
|
|
“Microstructural study of equiatomic PtTi martensite and the discovery of a new long-period structure”. Rotaru G-M, Tirry W, Sittner P, van Humbeeck J, Schryvers D, Acta materialia 55, 4447 (2007). http://doi.org/10.1016/j.actamat.2007.04.010
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 7
DOI: 10.1016/j.actamat.2007.04.010
|
|
|
“A microstructural study of the thermal stability of atomic layer deposited Al2O3 thin films”. Nistor LC, Richard O, Zhao O, Bender H, Stesmans A, Van Tendeloo G, Institute of physics conference series
T2 –, Microscopy of semiconducting materials , 397 (2003)
Abstract: The thermal stability of amorphous Al2O3 films (similar to8 and 80 nut thick) deposited by atomic layer deposition on HF-last and thin SiO2 covered (001) Si substrates is studied by transmission electron microscopy. The layers are in- and ex-situ annealed in the same temperature range.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Microstructure and defect characterization at interfaces in TiN/CrN multilayer coatings”. Major L, Tirry W, Van Tendeloo G, Surface and coatings technology 202, 6075 (2008). http://doi.org/10.1016/j.surfcoat.2008.07.005
Abstract: Microstructures of TiN/CrN multilayer coatings deposited on austenite steel (Cr Ni 18 8) by pulsed laser deposition (PLD) are characterized using transmission electron microscopy while their mechanical properties were assessed in a ball-on-disk test. All coatings have the same total thickness of about 1 ìm. The individual layers show a highly defective columnar structure, which is characterized by conventional electron microscopy (TEM) as well as by high resolution TEM. These techniques, combined with measurements of the local chemical composition through EDS prove that PLD allows to produce fully separated CrN and TiN layers. The friction, and consequently the wear, are lowered by increasing the total number of layers in the coating.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.589
Times cited: 23
DOI: 10.1016/j.surfcoat.2008.07.005
|
|
|
“Microstructure and flux pinning properties of melt textured grown doped YBa2Cu3O7-\delta”. Monot I, Verbist K, Hervieu M, Laffez P, Delamare MP, Wang J, Desgardin G, Van Tendeloo G, Physica: C : superconductivity 274, 253 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.404
Times cited: 33
|
|
|
“Microstructure and formation mechanisms of cylindrical and conical scrolls of the misfit layer compounds PbNbnS2n+1”. Bernaerts D, Amelinckx S, Van Tendeloo G, van Landuyt J, Journal of crystal growth 172, 433 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.751
Times cited: 23
|
|
|
“Microstructure and functional property changes in thin Ni-Ti wires heat teated by electric current: high energy X-ray and TEM investigations”. Malard B, Pilch J, Sittner P, Gartnerova V, Delville R, Schryvers D, Curfs C, Functional materials letters 2, 45 (2009). http://doi.org/10.1142/S1793604709000557
Abstract: High energy synchrotron X-ray diffraction, transmission electron microscopy and mechanical testing were employed to investigate the evolution of microstructure, texture and functional superelastic properties of 0.1 mm thin as drawn NiTi wires subjected to a nonconventional heat treatment by controlled electric current (FTMT-EC method). As drawn NiTi wires were prestrained in tension and exposed to a sequence of short DC power pulses in the millisecond range. The annealing time in the FTMT-EC processing can be very short but the temperature and force could be very high compared to the conventional heat treatment of SMAs. It is shown that the heavily strained, partially amorphous microstructure of the as drawn NiTi wire transforms under the effect of the DC pulse and tensile stress into a wide range of annealed nanosized microstructures depending on the pulse time. The functional superelastic properties and microstructures of the FTMT-EC treated NiTi wire are comparable to those observed in straight annealed wires.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.234
Times cited: 21
DOI: 10.1142/S1793604709000557
|
|
|
“Microstructure and high temperature transport properties of high quality epitaxial SrFeO3-\delta films”. Solís C, Rossell MD, Garcia G, Figueras A, Van Tendeloo G, Santiso J, Solid state ionics 179, 1996 (2008). http://doi.org/10.1016/j.ssi.2008.06.004
Abstract: We report the high temperature electronic transport properties of SrFeO3 − ä epitaxial thin films obtained by pulsed laser deposition on NdGaO3(110) substrates. The films show total conductivity higher than the bulk material and apparent activation energy of about 0.12 eV in O2, lower than reported values for SrFeO3 − ä films. The conductivity dependence with oxygen partial pressure shows a power dependence with an exponent close to + 1/4, in agreement with expected point defect equilibrium. For a given oxygen partial pressure, the temperature coefficient of resistance (TCR) shows a low positive value of about 1.52.5 10− 3 K− 1, which is still suitable for resistive oxygen sensing applications. The transport properties of the films are discussed in view of their particular microstructure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.354
Times cited: 10
DOI: 10.1016/j.ssi.2008.06.004
|
|
|
“Microstructure and interface studies of LaVO3/SrVO3 superlattices”. Boullay P, David A, Sheets WC, Lüders U, Prellier W, Tan H, Verbeeck J, Van Tendeloo G, Gatel C, Vincze G, Radi Z, Physical review : B : condensed matter and materials physics 83, 125403 (2011). http://doi.org/10.1103/PhysRevB.83.125403
Abstract: The structure and interface characteristics of (LaVO3)6m(SrVO3)m superlattices deposited on a (100)-SrTiO3 substrate were studied using transmission electron microscopy (TEM). Cross-section TEM studies revealed that both LaVO3 (LVO) and SrVO3 (SVO) layers are good single-crystal quality and epitaxially grown with respect to the substrate. It is evidenced that LVO layers are made of two orientational variants of a distorted perovskite compatible with bulk LaVO3, while SVO layers suffers from a tetragonal distortion due to the substrate-induced stain. Electron energy loss spectroscopy investigations indicate changes in the fine structure of the V L23 edge, related to a valence change between the LaVO3 and the SrVO3 layers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 26
DOI: 10.1103/PhysRevB.83.125403
|
|
|
“The microstructure and interfaces of intermediate layers in sapphire bicrystals”. Vasiliev AL, Stepantsov EA, Ivanov ZG, Verbist K, Van Tendeloo G, Olsson E, Applied surface science 119, 215 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.387
Times cited: 2
|
|