“3D FIB/SEM study of Ni4Ti3 precipitates in Ni-Ti alloys with different thermal-mechanical histories”. Cao S, Nishida M, Somsen C, Eggeler G, Schryvers D, , 02004 (2009). http://doi.org/10.1051/esomat/200902004
Abstract: The three-dimensional size, morphology and distribution of Ni4Ti3 precipitates growing in binary Ni-rich Ni-Ti alloys have been investigated via a slice view procedure in a Dual-Beam FIB/SEM system, in order to better stress-free Ni50.8Ti49.2 alloy with all four variants of precipitates and a compressed Ni51Ti49 alloy with aligned precipitates in one family were studied. The Ni4Ti3 precipitates reach a volume fraction of 9.6% in the reconstructed region of the stress-free alloy and 4.3% in the compressed one. In both cases, the mean volume, specific surface area, sphericity and aspect ratio of the precipitates are calculated and the Pair Distribution Functions of the precipitates are obtained. It is shown that most precipitates in the stress-free sample grow larger and have a more lenticular shape, while those in the compressed sample are more cylindrical. Deviations from these ideal shapes reveal internal steps in the stress-free sample and lamellae formation in the compressed one.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1051/esomat/200902004
|
|
|
“FIB/SEM applied to quantitative 3D analysis of precipitates in Ni-Ti”. Cao S, Nishida M, Schryvers D, Diffusion and defect data : solid state data : part B : solid state phenomena 172/174, 1284 (2011). http://doi.org/10.4028/www.scientific.net/SSP.172-174.1284
Abstract: Ni4Ti3 precipitates with a heterogeneous distribution growing in a polycrystalline Ni50.8Ti49.2 alloy have been investigated in a Dual-Beam FIB/SEM system. The volume ratio, mean volume, central plane diameter, thickness, aspect ratio and sphericity of the precipitates in the grain interior as well as near to the grain boundary were measured or calculated. The morphology of the precipitates was classified according to the Zingg scheme. The multistage martensitic transformation occurring in these kinds of samples is interpreted in view of the data of this heterogeneous microstructure of matrix and precipitates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.4028/www.scientific.net/SSP.172-174.1284
|
|
|
“Quantitative three-dimensional analysis of Ni4Ti3 precipitate morphology and distribution in polycrystalline Ni-Ti”. Cao S, Nishida M, Schryvers D, Acta materialia 59, 1780 (2011). http://doi.org/10.1016/j.actamat.2010.11.044
Abstract: The three-dimensional size, morphology and distribution of Ni4Ti3 precipitates in a Ni50.8Ti49.2 polycrystalline shape memory alloy with a heterogeneous microstructure have been investigated using a focused ion beam/scanning electron microscopy slice-and-view procedure. The mean volume, central plane diameter, thickness, aspect ratio and sphericity of the precipitates in the grain interior as well as near to the grain boundary were measured and/or calculated. The morphology of the precipitates was quantified by determining the equivalent ellipsoids with the same moments of inertia and classified according to the Zingg scheme. Also, the pair distribution functions describing the three-dimensional distributions were obtained from the coordinates of the precipitate mass centres. Based on this new data it is suggested that the existence of the heterogeneous microstructure could be due to a very small concentration gradient in the grains of the homogenized material and that the resulting multistage martensitic transformation originates in strain effects related to the size of the precipitates and scale differences of the available B2 matrix in between the precipitates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 34
DOI: 10.1016/j.actamat.2010.11.044
|
|
|
“Precipitation behaviors in Ti-2.3 Wt Pct Cu alloy during isothermal and two-step aging”. Akamine H, Mitsuhara M, Nishida M, Samaee V, Schryvers D, Tsukamoto G, Kunieda T, Fujii H, Metallurgical And Materials Transactions A-Physical Metallurgy And Materials Science 52, 2760 (2021). http://doi.org/10.1007/S11661-021-06265-X
Abstract: Time evolution of precipitates related to age-hardening in Ti-2.3 wt pct Cu alloys was investigated by electron microscopy. In isothermal aging at 723 K, the hardness increases continuously owing to precipitation strengthening, whereas in two-step aging where the aging temperature is switched from 673 K to 873 K after 100 hours, the hardness is found to drastically drop after the aging temperature switches. In isothermal aging, metastable and stable precipitates are independently nucleated, whereas characteristic V-shaped clusters of precipitates are observed during the two-step aging. It is revealed by atomic-scale observations that the V-shaped clusters are composed of metastable and stable precipitates and each type of precipitate has a different orientation relationship with the alpha phase: (10 (3) over bar)//(0001)(alpha) and [0 (1) over bar0]//respectively. The drop in hardness during two-step aging can be explained by a synergistic effect of decreased precipitation strengthening and solid solution strengthening. (C) The Minerals, Metals & Materials Society and ASM International 2021
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.874
DOI: 10.1007/S11661-021-06265-X
|
|
|
“Determination of the atomic width of an APB in ordered CoPt using quantified HAADF-STEM”. Akamine H, Van den Bos KHW, Gauquelin N, Farjami S, Van Aert S, Schryvers D, Nishida M, Journal of alloys and compounds 644, 570 (2015). http://doi.org/10.1016/j.jallcom.2015.04.205
Abstract: Anti-phase boundaries (APBs) in an ordered CoPt alloy are planar defects which disturb the ordered structure in their vicinity and decrease the magnetic properties. However, it has not yet been clarified to what extend the APBs disturb the ordering. In this study, high-resolution HAADF-STEM images are statistically analysed based on the image intensities estimated by the statistical parameter estimation theory. In the procedure, averaging intensities, fitting the intensity profiles to specific functions, and assessment based on a statistical test are performed. As a result, the APBs in the stable CoPt are found to be characterised by two atomic planes, and a contrast transition range as well as the centre of an inclined APB is determined. These results show that the APBs are quite sharp and therefore may have no notable effect on the net magnetic properties due to their small volume fraction. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 12
DOI: 10.1016/j.jallcom.2015.04.205
|
|
|
“Quantification by aberration corrected (S)TEM of boundaries formed by symmetry breaking phase transformations”. Schryvers D, Salje EKH, Nishida M, De Backer A, Idrissi H, Van Aert S, Ultramicroscopy 176, 194 (2017). http://doi.org/10.1016/j.ultramic.2016.12.022
Abstract: The present contribution gives a review of recent quantification work of atom displacements, atom site occupations and level of crystallinity in various systems and based on aberration corrected HR(S)TEM images. Depending on the case studied, picometer range precisions for individual distances can be obtained, boundary widths at the unit cell level determined or statistical evolutions of fractions of the ordered areas calculated. In all of these cases, these quantitative measures imply new routes for the applications of the respective materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 1
DOI: 10.1016/j.ultramic.2016.12.022
|
|