“Novel class of nanostructured metallic glass films with superior and tunable mechanical properties”. Ghidelli M, Orekhov A, Bassi AL, Terraneo G, Djemia P, Abadias G, Nord M, Béché, A, Gauquelin N, Verbeeck J, Raskin J-p, Schryvers D, Pardoen T, Idrissi H, Acta Materialia , 116955 (2021). http://doi.org/10.1016/j.actamat.2021.116955
Abstract: A novel class of nanostructured Zr50Cu50 (%at.) metallic glass films with superior and tunable mechanical
properties is produced by pulsed laser deposition. The process can be controlled to synthetize a wide
range of film microstructures including dense fully amorphous, amorphous embedded with nanocrystals
and amorphous nano-granular. A unique dense self-assembled nano-laminated atomic arrangement
characterized by alternating Cu-rich and Zr/O-rich nanolayers with different local chemical enrichment
and amorphous or amorphous-crystalline composite nanostructure has been discovered, while
significant in-plane clustering is reported for films synthetized at high deposition pressures. This unique
nanoarchitecture is at the basis of superior mechanical properties including large hardness and elastic
modulus up to 10 and 140 GPa, respectively and outstanding total elongation to failure (>9%), leading to
excellent strength/ductility balance, which can be tuned by playing with the film architecture. These
results pave the way to the synthesis of novel class of engineered nanostructured metallic glass films
with high structural performances attractive for a number of applications in microelectronics and
coating industry.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 27
DOI: 10.1016/j.actamat.2021.116955
|
|
|
“Synergistic effects altering reaction pathways : the case of glucose hydrogenation over Fe-Ni catalysts”. Fu Y, Ding L, Singleton ML, Idrissi H, Hermans S, Applied Catalysis B-Environmental 288, 119997 (2021). http://doi.org/10.1016/J.APCATB.2021.119997
Abstract: Carbon black (CB) supported Ni, Fe, or Fe-Ni alloy catalysts were synthesized by sol-gel to elucidate the reaction pathways over each catalyst, as well as synergistic effects in glucose to sorbitol hydrogenation. The bimetallic materials presented small and alloyed nanoparticles that were richer in reduced metallic sites at the surface than their monometallic counterparts. Glucose isomerization to fructose was favoured over Fe/CB, while glucose hydrogenation to sorbitol is the dominating pathway over Ni/CB catalyst. By contrast, sorbitol production was promoted and undesired isomerization was suppressed when Fe and Ni formed a nanoalloy. In addition, the alloy catalyst presented better stability than the corresponding monometallic catalyst. A comparison with a mechanical mixture of Fe/CB and Ni/CB monometallic catalysts demonstrated the synergy at the nanoscale in the alloy. By comparing different Fe:Ni ratios, the 1:1 formulation was identified as the best compromise to achieve a high activity while maintaining high sorbitol selectivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.446
DOI: 10.1016/J.APCATB.2021.119997
|
|
|
“On the nucleation mechanism of {112} <, 111 >, mechanical twins in as-quenched beta metastable Ti-12 wt.% Mo alloy”. Marteleur M, Idrissi H, Amin-Ahmadi B, Prima F, Schryvers D, Jacques PJ, Materialia 7, Unsp 100418 (2019). http://doi.org/10.1016/J.MTLA.2019.100418
Abstract: Recently developed beta-metastable Ti grades take advantage of the simultaneous activation of TRIP and TWIP effects for enhancing their work hardening rate. However, the role of each plasticity mechanism on the macroscopic mechanical response is still unclear. In this work, the nucleation mechanism of the first activated plasticity mechanism, namely {112} < 111 > twinning, was investigated. Firstly, post-mortem TEM analysis showed that twins nucleate on pre-existing microstructural defects such as thermal jogs with the zonal dislocation mechanism. The precipitation of the omega phase on twin boundaries has been observed, as well as the emission of numerous dislocations from super-jogs present in these twin boundaries. It is also shown that {112} < 111 > twins act as effective dislocation sources for the subsequent plasticity mechanisms such as beta -> alpha '' martensitic transformation and {332} < 111 > twinning. Secondly, in situ TEM tensile testing of the investigated Ti grade highlighted the primary role of the initial defect configuration present in the microstructure. It is shown that twins cannot nucleate without the presence of specific defects allowing the triggering of the dislocation decomposition needed for the twinning mechanism highlighted in investigated bulk samples.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.MTLA.2019.100418
|
|
|
Samaeeaghmiyoni V, Cordier P, Demouchy S, Bollinger C, Gasc J, Mussi A, Schryvers D, Idrissi H (2020) Research data supporting for Stress-induced amorphization triggers deformation in the lithospheric mantle
Keywords: Dataset; Electron microscopy for materials research (EMAT)
DOI: 10.5281/zenodo.3893661
|
|
|
“Rheology of amorphous olivine thin films characterized by nanoindentation”. Baral P, Orekhov A, Dohmen R, Coulombier M, Raskin JP, Cordier P, Idrissi H, Pardoen T, Acta Materialia 219, 117257 (2021). http://doi.org/10.1016/J.ACTAMAT.2021.117257
Abstract: The rheological properties of amorphous olivine thin films deposited by pulsed laser deposition have been studied based on ambient temperature nanoindentation under constant strain-rate as well as re-laxation conditions. The amorphous olivine films exhibit a viscoelastic-viscoplastic behavior with a significant rate dependency. The strain-rate sensitivity m is equal to similar to 0 . 05 which is very high for silicates, indicating a complex out-of-equilibrium structure. The minimum apparent activation volume determined from nanoindentation experiments corresponds to Mg and Fe atomic metallic sites in the (Mg,Fe)(2)SiO4 crystalline lattice. The ambient temperature creep behavior of the amorphous olivine films differs very much from the one of single crystal olivine. This behavior directly connects to the recent demonstration of the activation of grain boundary sliding in polycrystalline olivine following grain boundary amorphization under high-stress. (C) 2021 The Authors. Published by Elsevier Ltd on behalf of Acta Materialia Inc.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
DOI: 10.1016/J.ACTAMAT.2021.117257
|
|
|
Idrissi H, Samaee V, Lumbeeck G, van der Werf T, Pardoen T, Schryvers D, Cordier P (2019) Supporting data for “In situ Quantitative Tensile Tests on Antigorite in a Transmission Electron Microscope”
Abstract: The determination of the mechanical properties of serpentinites is essential towards the understanding of the mechanics of faulting and subduction. Here, we present the first in situ tensile tests on antigorite in a transmission electron microscope. A push-to-pull deformation device is used to perform quantitative tensile tests, during which force and displacement are measured, while the microstructure is imaged with the microscope. The experiments have been performed at room temperature on beams prepared by focused ion beam. The specimens are not single crystals despite their small sizes. Orientation mapping indicated that some grains were well-oriented for plastic slip. However, no dislocation activity has been observed even though engineering tensile stress went up to 700 MPa. We show also that antigorite does not exhibit an pure elastic-brittle behaviour since, despite the presence of defects, the specimens underwent plastic deformation and did not fail within the elastic regime. Instead, we observe that strain localizes at grain boundaries. All observations concur to show that under our experimental conditions, grain boundary sliding is the dominant deformation mechanism. This study sheds a new light on the mechanical properties of antigorite and calls for further studies on the structure and properties of grain boundaries in antigorite and more generally in phyllosilicates.
Keywords: Dataset; Electron microscopy for materials research (EMAT)
DOI: 10.5281/ZENODO.3583135
|
|
|
“Towards ductilization of high strength 7XXX aluminium alloys via microstructural modifications obtained by friction stir processing and heat treatments”. Lezaack MB, Hannard F, Zhao L, Orekhov A, Adrien J, Miettinen A, Idrissi H, Simar A, Materialia 20, 101248 (2021). http://doi.org/10.1016/J.MTLA.2021.101248
Abstract: High strength 7XXX aluminium series reach exceptional strength, higher than all other industrial aluminium alloys. However, they suffer from a lack of ductility compared to softer series. This work presents a procedure to improve the ductility of 7475 Al alloy in high strength condition, reaching a true fracture strain of 70% at full 500 MPa T6 yield strength. Using friction stir processing (FSP) and post-FSP heat treatments, 100% of industrial rolled material T6 yield stress is maintained but a 180% increase in fracture strain is measured for the processed material. This ductility improvement is studied by in-situ synchrotron X-ray tomography and is explained by the reduction of intermetallic particles size and the homogenization of their spatial distribution. Furthermore, the microstructure after FSP shows equiaxed refined grains which favour crack deviation as opposed to large cracks parallel to the elongated coarse grains in rolled plate. These results are paving the way to better formability and crashworthiness of 7XXX alloys.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.MTLA.2021.101248
|
|
|
““Branched&rdquo, structural transformation of the L12-Al3Zr phase manipulated by Cu substitution/segregation in the Al-Cu-Zr alloy system”. Ding L, Zhao M, Ehlers FJH, Jia Z, Zhang Z, Weng Y, Schryvers D, Liu Q, Idrissi H, Journal of materials science &, technology 185, 186 (2024). http://doi.org/10.1016/j.jmst.2023.11.015
Abstract: The effect of Cu on the evolution of the Al3Zr phase in an Al-Cu-Zr cast alloy during solution treatment at 500 °C has been thoroughly studied by combining atomic resolution high-angle annular dark-field scanning transmission electron microscopy, energy-dispersive X-ray spectroscopy and first-principles cal- culations. The heat treatment initially produces a pure L12-Al3Zr microstructure, allowing for about 13 % Cu to be incorporated in the dispersoid. Cu incorporation increases the energy barrier for anti-phase boundary (APB) activation, thus stabilizing the L12 structure. Additional heating leads to a Cu-induced “branched”path for the L12 structural transformation, with the latter process accelerated once the first APB has been created. Cu atoms may either (i) be repelled by the APBs, promoting the transformation to a Cu-poor D023 phase, or (ii) they may segregate at one Al-Zr layer adjacent to the APB, promoting a transformation to a new thermodynamically favored phase, Al4CuZr, formed when these segregation layers are periodically arranged. Theoretical studies suggest that the branching of the L12 transformation path is linked to the speed at which an APB is created, with Cu attraction triggered by a comparatively slow process. This unexpected transformation behavior of the L12-Al3Zr phase opens a new path to understanding, and potentially regulating the Al3Zr dispersoid evolution for high temperature applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 10.9
DOI: 10.1016/j.jmst.2023.11.015
|
|
|
“On amorphization as a deformation mechanism under high stresses”. Idrissi H, Carrez P, Cordier P, Current opinion in solid state and materials science 26, 100976 (2022). http://doi.org/10.1016/J.COSSMS.2021.100976
Abstract: In this paper we review the work related to amorphization under mechanical stress. Beyond pressure, we highlight the role of deviatoric or shear stresses. We show that the most recent works make amorphization appear as a deformation mechanism in its own right, in particular under extreme conditions (shocks, deformations under high stresses, high strain-rates).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11
DOI: 10.1016/J.COSSMS.2021.100976
|
|
|
“Electronic and chemical properties of nickel oxide thin films and the intrinsic defects compensation mechanism”. Poulain R, Lumbeeck G, Hunka J, Proost J, Savolainen H, Idrissi H, Schryvers D, Gauquelin N, Klein A, ACS applied electronic materials 4, 2718 (2022). http://doi.org/10.1021/ACSAELM.2C00230
Abstract: Although largely studied, contradictory results on nickel oxide (NiO) properties can be found in the literature. We herein propose a comprehensive study that aims at leveling contradictions related to NiO materials with a focus on its conductivity, surface properties, and the intrinsic charge defects compensation mechanism with regards to the conditions preparation. The experiments were performed by in situ photo-electron spectroscopy, electron energy loss spectroscopy, and optical as well as electrical measurements on polycrystalline NiO thin films prepared under various preparation conditions by reactive sputtering. The results show that surface and bulk properties were strongly related to the deposition temperature with in particular the observation of Fermi level pinning, high work function, and unstable oxygen-rich grain boundaries for the thin films produced at room temperature but not at high temperature (>200 degrees C). Finally, this study provides substantial information about surface and bulk NiO properties enabling to unveil the origin of the high electrical conductivity of room temperature NiO thin films and also for supporting a general electronic charge compensation mechanism of intrinsic defects according to the deposition temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1021/ACSAELM.2C00230
|
|
|
“On the formation of antiphase boundaries in Fe₄Al₁₃, intermetallics during a high temperature treatment”. Ding L, Sapanathan T, Schryvers D, Simar A, Idrissi H, Scripta materialia 215, 114726 (2022). http://doi.org/10.1016/J.SCRIPTAMAT.2022.114726
Abstract: In this paper, we report atomic scale observations and formation mechanisms of a high-density of antiphase boundaries (APBs) within an ultra-fine-grained Fe4Al13 intermetallic layer at an Al/steel interface after a heat treatment at 596 degrees C. The results reveal that the APBs are formed by nucleation and the glide of partial dislocations with Burgers vector of b/3[010] (b = 12.47 angstrom). The intensive activation of APBs locally transforms the Fe4Al13 structure from the quasicrystal approximant structure to a quasicrystal. Very few stacking faults and nanotwins are observed indicating that the formation of planar defects is mainly driven by this transformation. This new insight on the formation of high density of APBs could possibly lead to an improvement in toughness by increasing the strength/ductility balance of this intermetallic.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6
DOI: 10.1016/J.SCRIPTAMAT.2022.114726
|
|
|
“Tailoring Mechanical Properties of a-C:H:Cr Coatings”. Bagherpour A, Baral P, Colla M-S, Orekhov A, Idrissi H, Haye E, Pardoen T, Lucas S, Coatings 13, 2084 (2023). http://doi.org/10.3390/coatings13122084
Abstract: The development of coatings with tunable performances is critical to meet a wide range of technological applications each one with different requirements. Using the plasma-enhanced chemical vapor deposition (PECVD) process, scientists can create hydrogenated amorphous carbon coatings doped with metal (a-C:H:Me) with a broad range of mechanical properties, varying from those resembling polymers to ones resembling diamond. These diverse properties, without clear relations between the different families, make the material selection and optimization difficult but also very rich. An innovative approach is proposed here based on projected performance indices related to fracture energy, strength, and stiffness in order to classify and optimize a-C:H:Me coatings. Four different a-C:H:Cr coatings deposited by PECVD with Ar/C2H2 discharge under different bias voltage and pressures are investigated. A path is found to produce coatings with a selective critical energy release rate between 5–125 J/m2 without compromising yield strength (1.6–2.7 GPa) and elastic limit (≈0.05). Finally, fine-tuned coatings are categorized to meet desired applications under different testing conditions.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
DOI: 10.3390/coatings13122084
|
|
|
“Shear banding-activated dynamic recrystallization and phase transformation during quasi-static loading of β-metastable Ti &ndash, 12 wt % Mo alloy”. Choisez L, Ding L, Marteleur M, Kashiwar A, Idrissi H, Jacques PJ, Acta materialia 235, 118088 (2022). http://doi.org/10.1016/J.ACTAMAT.2022.118088
Abstract: Dynamic recrystallization (DRX) within adiabatic shear bands forming during the fracture of TRIP-TWIP β−metastable Ti-12Mo (wt %) alloy was recently reported. The formation of 1-3 µm thick-adiabatic shear bands, and of dynamic recrystallization, was quite surprising as their occurrence generally requires high temperature and/or high strain rate loading while these samples were loaded in quasi-static conditions at room temperature. To better understand the fracture mechanism and associated microstructural evolution, thin foils representative of different stages of the fracture process were machined from the fracture surface by Focused Ion Beam (FIB) and analyzed by Transmission Electron Microscopy (TEM) and Automated Crystal Orientation mapping (ACOM-TEM). Complex microstructure transformations involving severe plastic deformed nano-structuration, crystalline rotation and local precipitation of the omega phase were identified. The spatial and temporal evolution of the microstructure during the propagation of the crack was explained through dynamic recovery and continuous dynamic recrystallization, and linked to the modelled distribution of temperature and strain level where TEM samples were extracted.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.4
DOI: 10.1016/J.ACTAMAT.2022.118088
|
|
|
“A new healing strategy for metals : programmed damage and repair”. Arseenko M, Hannard F, Ding L, Zhao L, Maire E, Villanova J, Idrissi H, Simar A, Acta materialia 238, 118241 (2022). http://doi.org/10.1016/J.ACTAMAT.2022.118241
Abstract: Self-healing strategies aim at avoiding part repair or even replacement, which is time consuming, expen-sive and generates waste. However, strategies for metallic systems are still under-developed and solid-state solutions for room temperature service are limited to nano-scale damage repair. Here we propose a new healing strategy of micron-sized damage requiring only short and low temperature heating. This new strategy is based on damage localization particles, which can be healed by fast diffusing atoms of the matrix activated during heat treatment. The healing concept was successfully validated with a com-mercial aluminum alloy and manufactured by Friction Stir Processing (FSP). Damage was demonstrated to initiate on particles that were added to the matrix during material processing. In situ 2D and 3D nano -imaging confirmed healing of the damaged material and showed that heating this material for 10 min at 400 degrees C is sufficient to heal incipient damage with complete filling of 70% of all damage (and up to 90% when their initial size is below 0.2 mu m). Furthermore, strength is retained and the work of fracture of the alloy is improved by about 40% after healing. The proposed Programmed Damage and Repair healing strategy could be extended to other metal based systems presenting precipitation. (C) 2022 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.4
DOI: 10.1016/J.ACTAMAT.2022.118241
|
|
|
“On the formation mechanisms of intragranular shear bands in olivine by stress-induced amorphization”. Idrissi H, Béché, A, Gauquelin N, Ul-Haq I, Bollinger C, Demouchy S, Verbeeck J, Pardoen T, Schryvers D, Cordier P, Acta materialia 239, 118247 (2022). http://doi.org/10.1016/J.ACTAMAT.2022.118247
Abstract: Intragranular amorphization shear lamellae are found in deformed olivine aggregates. The detailed trans-mission electron microscopy analysis of intragranular lamella arrested in the core of a grain provides novel information on the amorphization mechanism. The deformation field is complex and heteroge-neous, corresponding to a shear crack type instability involving mode I, II and III loading components. The formation and propagation of the amorphous lamella is accompanied by the formation of crystal defects ahead of the tip. These defects are geometrically necessary [001] dislocations, characteristics of high-stress deformation in olivine, and rotational nanodomains which are tentatively interpreted as disclinations. We show that these defects play an important role in dictating the path followed by the amorphous lamella. Stress-induced amorphization in olivine would thus result from a direct crystal-to -amorphous transformation associated with a shear instability and not from a mechanical destabilization due to the accumulation of high number of defects from an intense preliminary deformation. The pref-erential alignment of some lamellae along (010) is a proof of the lower ultimate mechanical strength of these planes.(c) 2022 The Authors. Published by Elsevier Ltd on behalf of Acta Materialia Inc. This is an open access article under the CC BY license ( http://creativecommons.org/licenses/by/4.0/ )
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.4
Times cited: 5
DOI: 10.1016/J.ACTAMAT.2022.118247
|
|
|
“Controlled precipitation in a new Al-Mg-Sc alloy for enhanced corrosion behavior while maintaining the mechanical performance”. Krishnamurthy SC, Arseenko M, Kashiwar A, Dufour P, Marchal Y, Delahaye J, Idrissi H, Pardoen T, Mertens A, Simar A, Materials characterization 200, 112886 (2023). http://doi.org/10.1016/J.MATCHAR.2023.112886
Abstract: The hot working of 5xxx series alloys with Mg ≥3.5 wt% is a concern due to the precipitation of β (Al3Mg2) phase at grain boundaries favoring Inter Granular Corrosion (IGC). The mechanical and corrosion properties of a new 5028-H116 Al-Mg-Sc alloy under various β precipitates distribution is analyzed by imposing different cooling rates from the hot forming temperature (i.e. 325 °C). The mechanical properties are maintained regardless of the heat treatment. However, the different nucleation sites and volume fractions of β precipitates for different cooling rates critically affect IGC. Controlled furnace cooling after the 325 °C heat treatment is ideal in 5028-H116 alloy to reduce susceptibility to IGC after sensitization.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.7
DOI: 10.1016/J.MATCHAR.2023.112886
|
|
|
“Effect of annealing on mechanical properties and thermal stability of ZrCu/O nanocomposite amorphous films synthetized by pulsed laser deposition”. Bignoli F, Rashid S, Rossi E, Jaddi S, Djemia P, Terraneo G, Li Bassi A, Idrissi H, Pardoen T, Sebastiani M, Ghidelli M, Materials &, design 221, 110972 (2022). http://doi.org/10.1016/J.MATDES.2022.110972
Abstract: Binary ZrCu nanocomposite amorphous films are synthetized by pulsed laser deposition (PLD) under vac-uum (2 x 10-3 Pa) and 10 Pa He pressure, leading to fully amorphous compact and nanogranular mor-phologies, respectively. Then, post-thermal annealing treatments are carried out to explore thermal stability and crystallization phenomena together with the evolution of mechanical properties. Compact films exhibit larger thermal stability with partial crystallization phenomena starting at 420 degrees C, still to be completed at 550 degrees C, while nanogranular films exhibit early-stage crystallization at 300 degrees C and com-pleted at 485 degrees C. The microstructural differences are related to a distinct evolution of mechanical
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.4
DOI: 10.1016/J.MATDES.2022.110972
|
|
|
“Suppressing hydrogen blistering in a magnesium-rich healable laser powder bed fusion aluminum alloy analyzed by in-situ high resolution techniques”. Gheysen J, Kashiwar A, Idrissi H, Villanova J, Simar A, Materials &, design 231, 112024 (2023). http://doi.org/10.1016/J.MATDES.2023.112024
Abstract: Hydrogen blistering, i.e. precipitation of supersaturated hydrogen at elevated temperatures, increases porosity during heat treatments in 4xxx series Al alloys manufactured by laser powder bed fusion (LPBF), as demonstrated by 3D X-ray nano-imaging in AlSi12. This paper proposes the design of a healable Al alloy to suppress hydrogen blistering and improve the damage management. The strategy consists of solute atoms diffusing towards nano-voids and precipitating on their surface, thereby filling the damage sites. A new healable Al alloy was thus developed and successfully manufactured by LPBF. 3D X-ray nano-imaging evidenced that the addition of Mg in 4xxx series Al alloys suppresses the hydrogen blistering. This is expectedly due to Mg in solid solution which increases the hydrogen solubility in the Al matrix and due to the healing of these hydrogen pores. Moreover, a significant healing of voids smaller than 500 nm diameter is observed. In-situ heating inside transmission electron microscopy pointed out that Al matrix diffuses inside the fractured Mg2Si particles, thereby demonstrating the healing ability of the new alloy. This has opened the doors to development of new healable Al alloys manufactured by LPBF as well as to new post-treatments to tailor mechanical properties and microstructure without hydrogen blistering.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.4
DOI: 10.1016/J.MATDES.2023.112024
|
|
|
“On the role of microstructural defects on precipitation, damage, and healing behavior in a novel Al-0.5Mg2Si alloy”. Kashiwar A, Arseenko M, Simar A, Idrissi H, Materials &, design 239, 112765 (2024). http://doi.org/10.1016/J.MATDES.2024.112765
Abstract: A recently developed healable Al-Mg2Si designed by the programmed damage and repair (PDR) strategy is studied considering the role microstructural defects play on precipitation, damage, and healing. The alloy incorporates sacrificial Mg2Si particles that precipitate after friction stir processing (FSP). They act as damage localization sites and are healable based on the solid-state diffusion of Al-matrix. A combination of different transmission electron microscopy (TEM) imaging techniques enabled the visualization and quantification of various crystallographic defects and the spatial distribution of Mg2Si precipitates. Intragrain nucleation is found to be the dominant mechanism for precipitation during FSP whereas grain boundaries and subgrain boundaries mainly lead to coarsening of the precipitates. The statistical and spatial analyses of the damaged particles have shown particle fracture as the dominant damage mechanism which is strongly dependent on the size and aspect ratio of the particles whereas the damage was not found to depend on the location of the precipitates within the matrix. The damaged particles are associated with dislocations accumulated around them. The interplay of these dislocations is directly visualized during healing based on in situ TEM heating which revealed recovery in the matrix as an operative mechanism during the diffusion healing of the PDR alloy.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.4
DOI: 10.1016/J.MATDES.2024.112765
|
|
|
“On-chip very low strain rate rheology of amorphous olivine films”. Coulombier M, Baral P, Orekhov A, Dohmen R, Raskin JP, Pardoen T, Cordier P, Idrissi H, Acta materialia 266, 119693 (2024). http://doi.org/10.1016/J.ACTAMAT.2024.119693
Abstract: Recent observations made by the authors revealed the activation of stress induced amorphization and sliding at grain boundary in olivine [1], a mechanism which is expected to play a pivotal role in the viscosity drop at the lithosphere-asthenosphere boundary and the brittle -ductile transition in the lithospheric mantle. However, there is a lack of information in the literature regarding the intrinsic mechanical properties and the elementary deformation mechanisms of this material, especially at time scales relevant for geodynamics. In the present work, amorphous olivine films were obtained by pulsed laser deposition (PLD). The mechanical response including the rate dependent behavior are investigated using a tension -on -chip (TOC) method developed at UCLouvain allowing to perform creep/relaxation tests on thin films at extremely low strain rates. In the present work, strain rate down to 10-12 s- 1 was reached which is unique. High strain rate sensitivity of 0.054 is observed together with the activation of relaxation at the very early stage of deformation. Furthermore, digital image correlation (DIC), used for the first time on films deformed by TOC, reveals local strain heterogeneities. The relationship between such heterogeneities, the high strain rate sensitivity and the effect of the electron beam in the scanning electron microscope is discussed and compared to the literature.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.4
DOI: 10.1016/J.ACTAMAT.2024.119693
|
|
|
“Tailoring mechanical properties and shear band propagation in ZrCu metallic glass nanolaminates through chemical heterogeneities and interface density”. Brognara A, Kashiwar A, Jung C, Zhang X, Ahmadian A, Gauquelin N, Verbeeck J, Djemia P, Faurie D, Dehm G, Idrissi H, Best JP, Ghidelli M, Small Structures , 2400011 (2024). http://doi.org/10.1002/SSTR.202400011
Abstract: The design of high‐performance structural thin films consistently seeks to achieve a delicate equilibrium by balancing outstanding mechanical properties like yield strength, ductility, and substrate adhesion, which are often mutually exclusive. Metallic glasses (MGs) with their amorphous structure have superior strength, but usually poor ductility with catastrophic failure induced by shear bands (SBs) formation. Herein, we introduce an innovative approach by synthesizing MGs characterized by large and tunable mechanical properties, pioneering a nanoengineering design based on the control of nanoscale chemical/structural heterogeneities. This is realized through a simplified model Zr 24 Cu 76 /Zr 61 Cu 39 , fully amorphous nanocomposite with controlled nanoscale periodicity ( Λ , from 400 down to 5 nm), local chemistry, and glass–glass interfaces, while focusing in‐depth on the SB nucleation/propagation processes. The nanolaminates enable a fine control of the mechanical properties, and an onset of crack formation/percolation (>1.9 and 3.3%, respectively) far above the monolithic counterparts. Moreover, we show that SB propagation induces large chemical intermixing, enabling a brittle‐to‐ductile transition when Λ ≤ 50 nm, reaching remarkably large plastic deformation of 16% in compression and yield strength ≈2 GPa. Overall, the nanoengineered control of local heterogeneities leads to ultimate and tunable mechanical properties opening up a new approach for strong and ductile materials.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1002/SSTR.202400011
|
|
|
“Grain boundary-mediated plasticity in aluminum films unraveled by a statistical approach combining nano-DIC and ACOM-TEM”. Baral P, Kashiwar A, Coulombier M, Delannay L, Hoummada K, Raskin JP, Idrissi H, Pardoen T, Acta materialia 276, 120081 (2024). http://doi.org/10.1016/J.ACTAMAT.2024.120081
Abstract: Nanomechanical on-chip testing is combined with nanoscale in situ digital image correlation and automated crystal orientation mapping in TEM to deliver novel statistically representative quantitative data about the deformation mechanisms in nanocrystalline aluminum films. The films are very ductile, with a rare stable multiple necking process with local strains reaching up to 0.45 and macroscopic elongation up to 0.17. The strain fields with resolution below 100 nm are related to the underlying microstructure and crystallographic orientation maps. This reveals nanoscopic shear bands forming preferentially along GB with high misorientations, tilted at +/− 45° with respect to loading direction. The analysis of these data prove that the strong strain delocalization process is promoted by GB migration and grain rotation, leading to large strain rate sensitivity. The distribution of misorientation angles between grains evolve during deformation. The GBs with misorientation between 20° and 40°, which are the GBs with highest energy, involve the largest strains.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.4
DOI: 10.1016/J.ACTAMAT.2024.120081
|
|