Abstract: The rational synthesis, comprehensive characterization, and mechanical and micromechanical properties of a calcium phosphate cement are presented. Hydroxyapatite cement biomaterial was synthesized from reactive sub-micrometer-sized dicalcium phosphate dihydrate and tetracalcium phosphate via a dissolution-precipitation reaction using water as the liquid phase. As a result nanostructured, Ca-deficient and carbonated B-type hydroxyapatite is formed. The cement shows good processibility, sets in 22 ± 2 min and entirely transforms to the end product after 6 h of setting reaction, one of the highest conversion rates among previously reported for calcium phosphate cements based on dicalcium and tetracalcium phosphates. The combination of all elucidated physical-chemical traits leads to an essential bioactivity and biocompatibility of the cement, as revealed by in vitro acellular simulated body fluid and cell culture studies. The compressive strength of the produced cement biomaterial was established to be 25 ± 3 MPa. Furthermore, nanoindentation tests were performed directly on the cement to probe its local elasticity and plasticity at sub-micrometer/micrometer level. The measured elastic modulus and hardness were established to be Es = 23 ± 3.5 and H = 0.7 ± 0.2 GPa, respectively. These values are in close agreement with those reported in literature for trabecular and cortical bones, reflecting good elastic and plastic coherence between synthesized cement biomaterial and human bones.

Abstract: A plasma enhanced-chemical vapor deposition (PE-CVD) route to Fe2O3-based materials on Al2O3(0001) single crystals at moderate growth temperatures (200400 °C) is reported. The use of the fluorinated Fe(hfa)2TMEDA (hfa = 1,1,1,5,5,5-hexafluoro-2,4-pentanedionate; TMEDA = N,N,N′,N′-tetramethylethylenediamine) molecular precursor in Ar/O2 plasmas enabled an in situ F-doping of iron oxide matrices, with a fluorine content tunable as a function of the adopted preparative conditions. Variations of the thermal energy supply enabled control of the system phase composition, resulting in γ-Fe2O3 at 200 °C and α-Fe2O3 nanostructures at higher deposition temperatures. Notably, at 400 °C the formation of highly oriented α-Fe2O3 nanocolumns characterized by an epitaxial relation with the Al2O3(0001) substrate was observed. Beside fluorine content, phase composition and nano-organization, even the system optical properties and, in particular, energy gap values, could be tailored by proper modifications of processing parameters.

Abstract: Cu-Pd alloys containing 10, 20, 30, 40, and 50 at. % Pd and quenched from a temperature just above the ordering temperature T-c are investigated by electron diffraction and high-resolution electron microscopy (HREM). The results show diffuse electron diffraction intensities at {100} and {110} positions for the alloy with 10 at. % Pd, but with a characteristic twofold and fourfold splitting for the alloys with more than 10 at. % Pd. High-resolution images show the formation of microdomains best developed between 20 and 30 at. % Pd. A real-space characterization has been performed by applying videographic real-structure simulations revealing that the splitting of the diffuse maxima depends on the average distance between microdomains of Cu3Au type in antiphase with each other. By applying image processing routines on the HREM images, correlation vectors are identified which correspond to correlations between microdomains.

Abstract: The relationships between incommensurability, charge ordering and magnetotransport properties in Nd0.5Ca0.5Mn1-xCrxO3 manganites have been studied by electron diffraction and lattice imaging versus temperature with 0.02 less than or equal to x less than or equal to 0.07. All compositions show an incommensurate superstructure over the whole temperature domain, despite the fact that they are ferromagnetic and conductive below 140 K, The q-vector (1/2 – delta)a* decreases with increasing temperature for all compositions x. For a given temperature q also decreases with x. Lattice images obtained at low temperature give a clear view of the characteristics of the incommensurate structure. They also provide a better understanding of the charge ordering process. The low-temperature form of the Cr-doped manganites is not a perfectly doubled cell [[2a(p)root 2 x 2a(p) x a(p)root 2]], but defects inducing a tripled cell occur pseudo-periodically. (C) 2000 Elsevier Science B.V. All rights reserved.

Abstract: A data-acquisition and data-processing method is proposed that aims at minimizing the effect of retardation on the Kramers-Kronig analysis of valence electron energy-loss spectra. This method is applied to diamond, which, due to its high dielectric constant, is a material that shows strong retardation effects and thus is a challenging material to be studied by valence electron energy-loss spectroscopy. The results obtained show a significant improvement but still show small discrepancies with respect to optical data, which are most likely due to the residual retardation contributions and the fact that nonzero momentum transfers are measured.

Abstract: Lithium-rich oxides are a promising class of positive electrode materials for next generation lithium-ion batteries, and oxygen plays a prominent role during electrochemical cycling either by forming peroxo-like species and/or by irreversibly forming oxygen gas during first charge. Here, we present Li-Fe-Te-O materials which show a tremendous amount of oxygen gas release. This oxygen release accounts for nearly all the capacity during the first charge and results in vacancies as seen by transmission electron microscopy. There is no oxidation of either metal during charge but significant changes in their environments. These changes are particularly extreme for tellurium. XRD and neutron powder diffraction both show limited Changes during cycling and no appreciable change in lattice parameters. A density functional theory study of this material is performed and demonstrates that the holes created on some of the oxygen atoms upon oxidation are partially stabilized through the formation of shorter O-O bonds, i.e. (O-2)(n-) species which on further delithiation show a spontaneous O-2 de-coordination from the cationic network and migration to the now empty lithium layer. The rate limiting step during charge is undoubtedly the diffusion of oxygen either out along the lithium layer or via columns of oxygen atoms. (C) 2015 The Electrochemical Society. All rights reserved.

Abstract: This work compares the morphology of gold nanoparticles (NPs) produced at room temperature on single-crystalline (MgO nanocubes and plates) and amorphous (carbon/glass plates) substrates by pulsed laser deposition (PLD). The results show that similar deposition and nucleation rates (>5×1013 cm−2 s−1) are achieved irrespective of the nature of the substrate. Instead, the shape of NPs is substrate dependent, i.e., quasispheres and faceted NPs in amorphous and single-crystalline substrates, respectively. The shape of the latter is octahedral for small NPs and truncated octahedral for large ones, with the degree of truncation being well explained using the Wulff-Kaichew theorem. Furthermore, epitaxial growth at room temperature is demonstrated for single-crystalline substrate. The large fraction of ions having energies higher than 200 eV and the large flux of species arriving to the substrate (1016 at. cm−2 s−1) involved in the PLD process are, respectively, found to be responsible for the high nucleation rates and epitaxial growth at room temperature.