“Influence of artificial pinning centers on structural and superconducting properties of thick YBCO films on ABAD-YSZ templates”. Pahlke P, Sieger M, Ottolinger R, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Haenisch J, Holzapfel B, Schultz L, Nielsch K, Huehne R, Superconductor science and technology 31, 044007 (2018). http://doi.org/10.1088/1361-6668/AAAFBE
Abstract: Recent efforts in the development of YBa2Cu3O7-x (YBCO) coated conductors are devoted to the increase of the critical current I-c in magnetic fields. This is typically realized by growing thicker YBCO layers as well as by the incorporation of artificial pinning centers. We studied the growth of doped YBCO layers with a thickness of up to 7 mu m using pulsed laser deposition with a growth rate of about 1.2 nm s(-1). Industrially fabricated ion-beam textured YSZ templates based on metal tapes were used as substrates for this study. The incorporation of BaHfO3 (BHO) or Ba2Y(Nb0.5Ta0.5)O-6 (BYNTO) secondary phase additions leads to a denser microstructure compared to undoped films. A purely c-axis-oriented YBCO growth is preserved up to a thickness of about 4 mu m, whereas misoriented texture components were observed in thicker films. The critical temperature is slightly reduced compared to undoped films and independent of film thickness. The critical current density J(c) of the BHO- and BYNTO-doped YBCO layers is lower at 77 K and self-field compared to pure YBCO layers; however, I-c increases up to a thickness of 5 mu m. A comparison between films with a thickness of 1.3 mu m revealed that the anisotropy of the critical current density J(c)(theta) strongly depends on the incorporated pinning centers. Whereas BHO nanorods lead to a strong B vertical bar vertical bar c-axis peak, the overall anisotropy is significantly reduced by the incorporation of BYNTO forming a mixture of short c-axis-oriented nanorods and small (a-b)-oriented platelets. As a result, the J(c) values of the doped films outperform the undoped samples at higher fields and lower temperatures for most magnetic field directions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 9
DOI: 10.1088/1361-6668/AAAFBE
|
“Fe-containing magnesium aluminate support for stability and carbon control during methane reforming”. Theofanidis SA, Galvita VV, Poelman H, Dharanipragada NVRA, Longo A, Meledina M, Van Tendeloo G, Detavernier C, Marin GB, ACS catalysis 8, 5983 (2018). http://doi.org/10.1021/ACSCATAL.8B01039
Abstract: We report a MgFexAl2-xO4 synthetic spinel, where x varies from 0 to 0.26, as support for Ni-based catalysts, offering stability and carbon control under various conditions of methane reforming. By incorporation of Fe into a magnesium aluminate spine!, a support is created with redox functionality and high thermal stability, as concluded from temporal analysis of products (TAP) experiments and redox cycling, respectively. A diffusion coefficient of 3 x 10(-17) m(2) s(-1) was estimated for lattice oxygen at 993 K from TAP experiments. X-ray diffraction (XRD) and extended X-ray absorption fine structure (EXAFS) modeling identified that the incorporation of iron occurs as Fe3+ in the octahedral sites of the spinel lattice, replacing aluminum. Simulation of the X-ray absorption near edge structure (XANES) spectrum of the reduced support showed that 60 +/- 10% of iron was reduced from 3+ to 2+ at 1073 K, while there was no formation of metallic iron. A series of Ni/MgFexAl2-xO4 catalysts, where x varies from 0 to 0.26, was synthesized and reduced, yielding a supported Ni-Fe alloy. The evolution of the catalyst structure during H-2 temperature-programmed reduction (TPR) and CO2 temperature-programmed oxidation (TPO) was examined using time-resolved in situ XRD and XANES. During reforming, iron in both the support and alloy keeps control of carbon accumulation, as confirmed by O-2-TPO on the spent catalysts. By fine tuning the amount of Fe in MgFexAl2-xO4, a supported alloy was obtained with a Ni/Fe molar ratio of similar to 10, which was active for reforming and stable. By comparison of the performance of Ni-based catalysts with Fe either incorporated into or deposited onto the support, the location of Fe within the support proved crucial for the stability and carbon mitigation under reforming conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 10.614
Times cited: 18
DOI: 10.1021/ACSCATAL.8B01039
|
“Exciton Fine Structure and Lattice Dynamics in InP/ZnSe Core/Shell Quantum Dots”. Brodu A, Ballottin MV, Buhot J, van Harten EJ, Dupont D, La Porta A, Prins PT, Tessier MD, Versteegh MAM, Zwiller V, Bals S, Hens Z, Rabouw FT, Christianen PCM, de Donega CM, Vanmaekelbergh D, ACS Photonics 5, 3353 (2018). http://doi.org/10.1021/ACSPHOTONICS.8B00615
Abstract: Nanocrystalline InP quantum dots (QDs) hold promise for heavy-metal-free optoelectronic applications due to their bright and size tunable emission in the visible range. Photochemical stability and high photoluminescence (PL) quantum yield are obtained by a diversity of epitaxial shells around the InP core. To understand and optimize the emission line shapes, the exciton fine structure of InP core/shell QD systems needs be investigated. Here, we study the exciton fine structure of InP/ZnSe core/shell QDs with core diameters ranging from 2.9 to 3.6 nm (PL peak from 2.3 to 1.95 eV at 4 K). PL decay measurements as a function of temperature in the 10 mK to 300 K range show that the lowest exciton fine structure state is a dark state, from which radiative recombination is assisted by coupling to confined acoustic phonons with energies ranging from 4 to 7 meV, depending on the core diameter. Circularly polarized fluorescence line-narrowing (FLN) spectroscopy at 4 K under high magnetic fields (up to 30 T) demonstrates that radiative recombination from the dark F = +/- 2 state involves acoustic and optical phonons, from both the InP core and the ZnSe shell. Our data indicate that the highest intensity FLN peak is an acoustic phonon replica rather than a zero-phonon line, implying that the energy separation observed between the F = +/- 1 state and the highest intensity peak in the FLN spectra (6 to 16 meV, depending on the InP core size) is larger than the splitting between the dark and bright fine structure exciton states.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.756
Times cited: 40
DOI: 10.1021/ACSPHOTONICS.8B00615
|
“Dopant-induced electron localization drives CO2 reduction to C2 hydrocarbons”. Zhou Y, Che F, Liu M, Zou C, Liang Z, De Luna P, Yuan H, Li J, Wang Z, Xie H, Li H, Chen P, Bladt E, Quintero-Bermudez R, Sham T-K, Bals S, Hofkens J, Sinton D, Chen G, Sargent EH, Nature chemistry 10, 974 (2018). http://doi.org/10.1038/S41557-018-0092-X
Abstract: The electrochemical reduction of CO2 to multi-carbon products has attracted much attention because it provides an avenue to the synthesis of value-added carbon-based fuels and feedstocks using renewable electricity. Unfortunately, the efficiency of CO2 conversion to C-2 products remains below that necessary for its implementation at scale. Modifying the local electronic structure of copper with positive valence sites has been predicted to boost conversion to C-2 products. Here, we use boron to tune the ratio of Cu delta+ to Cu-0 active sites and improve both stability and C-2-product generation. Simulations show that the ability to tune the average oxidation state of copper enables control over CO adsorption and dimerization, and makes it possible to implement a preference for the electrosynthesis of C-2 products. We report experimentally a C-2 Faradaic efficiency of 79 +/- 2% on boron-doped copper catalysts and further show that boron doping leads to catalysts that are stable for in excess of similar to 40 hours while electrochemically reducing CO2 to multi-carbon hydrocarbons.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 25.87
Times cited: 700
DOI: 10.1038/S41557-018-0092-X
|
“Deactivation of Sn-Beta during carbohydrate conversion”. van der Graaf WNP, Tempelman CHL, Hendriks FC, Ruiz-Martinez J, Bals S, Weckhuysen BM, Pidko EA, Hensen EJM, Applied catalysis : A : general 564, 113 (2018). http://doi.org/10.1016/J.APCATA.2018.07.023
Abstract: The deactivation of Sn-Beta zeolite catalyst during retro-aldolization and isomerization of glucose is investigated. Confocal fluorescence microscopy reveals that retro-aldolization of glucose in CH3OH at 160 degrees C is accompanied with the build-up of insoluble oligomeric deposits in the micropores, resulting in a rapid catalyst deactivation. These deposits accumulate predominantly in the outer regions of the zeolite crystals, which points to mass transport limitations. Glucose isomerization in water is not only accompanied by the formation of insoluble deposits in the micropores, but also by the structural degradation of the zeolite due to desilication and destannation. Enhanced and sustained catalytic performance can be achieved by using ethanol/water mixtures as the reaction solvent instead of water.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 25
DOI: 10.1016/J.APCATA.2018.07.023
|
“Cuboidal supraparticles self-assembled from cubic CsPbBr3 perovskite nanocrystals”. van der Burgt JS, Geuchies JJ, van der Meer B, Vanrompay H, Zanaga D, Zhang Y, Albrecht W, Petukhov AV, Filion L, Bals S, Swart I, Vanmaekelbergh D, The journal of physical chemistry: C : nanomaterials and interfaces 122, 15706 (2018). http://doi.org/10.1021/ACS.JPCC.8B02699
Abstract: Colloidal CsPbBr3 nanocrystals (NCs) have emerged as promising candidates for various opto-electronic applications, such as light-emitting diodes, photodetectors, and solar cells. Here, we report on the self-assembly of cubic NCs from an organic suspension into ordered cuboidal supraparticles (SPs) and their structural and optical properties. Upon increasing the NC concentration or by addition of a nonsolvent, the formation of the SPs occurs homogeneously in the suspension, as monitored by in situ X-ray scattering measurements. The three-dimensional structure of the SPs was resolved through high-angle annular dark-field scanning transmission electron microscopy and electron tomography. The NCs are atomically aligned but not connected. We characterize NC vacancies on superlattice positions both in the bulk and on the surface of the SPs. The occurrence of localized atomic-type NC vacancies-instead of delocalized ones-indicates that NC-NC attractions are important in the assembly, as we verify with Monte Carlo simulations. Even when assembled in SPs, the NCs show bright emission, with a red shift of about 30 meV compared to NCs in suspension.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 60
DOI: 10.1021/ACS.JPCC.8B02699
|
“Complex Magnetic Ordering in the Oxide Selenide Sr2Fe3Se2O3”. Cassidy SJ, Orlandi F, Manuel P, Hadermann J, Scrimshire A, Bingham PA, Clarke SJ, Inorganic chemistry 57, 10312 (2018). http://doi.org/10.1021/ACS.INORGCHEM.8B01542
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 2
DOI: 10.1021/ACS.INORGCHEM.8B01542
|
“A comparison of floating-electrode DBD and kINPen jet : plasma parameters to achieve similar growth reduction in colon cancer cells under standardized conditions”. Bekeschus S, Lin A, Fridman A, Wende K, Weltmann K-D, Miller V, Plasma chemistry and plasma processing 38, 1 (2018). http://doi.org/10.1007/S11090-017-9845-3
Abstract: A comparative study of two plasma sources (floating-electrode dielectric barrier discharge, DBD, Drexel University; atmospheric pressure argon plasma jet, kINPen, INP Greifswald) on cancer cell toxicity was performed. Cell culture protocols, cytotoxicity assays, and procedures for assessment of hydrogen peroxide (H2O2) were standardized between both labs. The inhibitory concentration 50 (IC50) and its corresponding H2O2 deposition was determined for both devices. For the DBD, IC50 and H2O2 generation were largely dependent on the total energy input but not pulsing frequency, treatment time, or total number of cells. DBD cytotoxicity could not be replicated by addition of H2O2 alone and was inhibited by larger amounts of liquid present during the treatment. Jet plasma toxicity depended on peroxide generation as well as total cell number and amount of liquid. Thus, the amount of liquid present during plasma treatment in vitro is key in attenuating short-lived species or other physical effects from plasmas. These in vitro results suggest a role of liquids in or on tissues during plasma treatment in a clinical setting. Additionally, we provide a platform for correlation between different plasma sources for a predefined cellular response.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.355
Times cited: 12
DOI: 10.1007/S11090-017-9845-3
|
“Clustering behavior during natural aging and artificial aging in Al-Mg-Si alloys with different Ag and Cu addition”. Weng Y, Jia Z, Ding L, Muraishi S, Liu Q, Microstructure And Processing 732, 273 (2018). http://doi.org/10.1016/J.MSEA.2018.07.018
Abstract: The effect of Ag and Cu addition on clustering behavior of Al-Mg-Si alloys during natural aging (NA) and artificial aging (AA) was investigated by hardness measurement, tensile test and atom probe tomography analysis. The results show that both Ag and Cu atoms could enter clusters and GP-zones, change the Mg/Si ratio and increase their volume fractions. Compared with the Al base alloy, the clusters in the Ag/Cu-added alloys more easily transform to beta" phases for size and compositional similarity, and the strengthening ability of these particles is enhanced by the increased volume fraction and shear modulus. In NA condition, Cu is greater in improving the volume fraction of clusters than Ag and thus produces higher T4 temper hardness. In AA condition, in contrary, Ag is more effective in facilitating the formation and growth of particles than Cu due to the stronger Ag-Mg interaction and the high diffusivity of Ag atoms in Al matrix, leading to highest hardening response. Compared to the Cu-added alloy, the Ag-added alloy shows higher precipitation kinetics during AA treatment and maintains a lower T4 temper hardness.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 11
DOI: 10.1016/J.MSEA.2018.07.018
|
“Atomic-scale quantification of charge densities in two-dimensional materials”. Müller-Caspary K, Duchamp M, Roesner M, Migunov V, Winkler F, Yang H, Huth M, Ritz R, Simson M, Ihle S, Soltau H, Wehling T, Dunin-Borkowski RE, Van Aert S, Rosenauer A, Physical review B 98, 121408 (2018). http://doi.org/10.1103/PHYSREVB.98.121408
Abstract: The charge density is among the most fundamental solid state properties determining bonding, electrical characteristics, and adsorption or catalysis at surfaces. While atomic-scale charge densities have as yet been retrieved by solid state theory, we demonstrate both charge density and electric field mapping across a mono-/bilayer boundary in 2D MoS2 by momentum-resolved scanning transmission electron microscopy. Based on consistency of the four-dimensional experimental data, statistical parameter estimation and dynamical electron scattering simulations using strain-relaxed supercells, we are able to identify an AA-type bilayer stacking and charge depletion at the Mo-terminated layer edge.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 10
DOI: 10.1103/PHYSREVB.98.121408
|
“The atomic lensing model: new opportunities for atom-by-atom metrology of heterogeneous nanomaterials”. van den Bos KHW, Janssens L, De Backer A, Nellist PD, Van Aert S, Ultramicroscopy 203, 155 (2019). http://doi.org/10.1016/j.ultramic.2018.12.004
Abstract: The atomic lensing model has been proposed as a promising method facilitating atom-counting in heterogeneous nanocrystals [1]. Here, image simulations will validate the model, which describes dynamical diffraction as a superposition of individual atoms focussing the incident electrons. It will be demonstrated that the model is reliable in the annular dark field regime for crystals having columns containing dozens of atoms. By using the principles of statistical detection theory, it will be shown that this model gives new opportunities for detecting compositional differences.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 4
DOI: 10.1016/j.ultramic.2018.12.004
|
“Chemistry of Shape-Controlled Iron Oxide Nanocrystal Formation”. Feld A, Weimer A, Kornowski A, Winckelmans N, Merkl J-P, Kloust H, Zierold R, Schmidtke C, Schotten T, Riedner M, Bals S, Weller PD Horst, ACS nano 13, 152 (2018). http://doi.org/10.1021/acsnano.8b05032
Abstract: Herein we demonstrate that meticulous and in-depth analysis of the reaction mechanisms of nanoparticle formation is rewarded by full control of size, shape and crystal structure of superparamagnetic iron oxide nanocrystals during synthesis. Starting from two iron sources – iron(II)- and iron(III) carbonate -a strict separation of oleate formation from the generation of reactive pyrolysis products and concomitant nucleation of iron oxide nanoparticles was achieved. This protocol enabled us to analyze each step of nanoparticle formation independently in depth. Progress of the entire reaction was monitored via matrix-assisted laser desorption ionization time-of-flight mass spectrometry (MALDI-TOF MS) and gas chromatography (GC) gaining insight into the formation of various iron oleate species prior to nucleation. Interestingly, due to the intrinsic strongly reductive pyrolysis conditions of the oleate intermediates and redox process in early stages of the synthesis, pristine iron oxide nuclei were composed exclusively from wustite, irrespective of the oxidation state of the iron source. Controlling the reaction conditions provided a very broad range of size- and shape defined monodisperse iron oxide nanoparticles. Curiously, after nucleation star shaped nanocrystals were obtained, which underwent metamorphism towards cubic shaped particles. EELS tomography revealed ex post oxidation of the primary wustite nanocrystal providing a full 3D image of Fe2+ and Fe3+ distribution within. Overall, we developed a highly flexible synthesis, yielding multigram amounts of well-defined iron oxide nanocrystals of different sizes and morphologies.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 54
DOI: 10.1021/acsnano.8b05032
|
“Fe2+Deficiencies, FeO Subdomains, and Structural Defects Favor Magnetic Hyperthermia Performance of Iron Oxide Nanocubes into Intracellular Environment”. Lak A, Cassani M, Mai BT, Winckelmans N, Cabrera D, Sadrollahi E, Marras S, Remmer H, Fiorito S, Cremades-Jimeno L, Litterst FJ, Ludwig F, Manna L, Teran FJ, Bals S, Pellegrino T, Nano letters 18, 6856 (2018). http://doi.org/10.1021/acs.nanolett.8b02722
Abstract: Herein, by studying a stepwise phase transformation of 23 nm FeO-Fe3O4 core-shell nanocubes into Fe3O4, we identify a composition at which the magnetic heating performance of the nanocubes is not affected by the medium viscosity and aggregation. Structural and magnetic characterizations reveal the transformation of the FeO-Fe3O4 nanocubes from having stoichiometric phase compositions into Fe2+ deficient Fe3O4 phases. The resultant nanocubes contain tiny compressed and randomly distributed FeO sub-domains as well as structural defects. This phase transformation causes a tenfold increase in the magnetic losses of the nanocubes, which remains exceptionally insensitive to the medium viscosity as well as aggregation unlike similarly sized single-phase magnetite nanocubes. We observe that the dominant relaxation mechanism switches from Néel in fresh core-shell nanocubes to Brownian in partially oxidized nanocubes and once again to Néel in completely treated nanocubes. The Fe2+ deficiencies and structural defects appear to reduce the magnetic energy barrier and anisotropy field, thereby driving the overall relaxation into Néel process. The magnetic losses of the particles remain unchanged through a progressive internalization/association to ovarian cancer cells. Moreover, the particles induce a significant cell death after being exposed to hyperthermia treatment. Here, we present the largest heating performance that has been reported to date for 23 nm iron oxide nanoparticles under cellular and intracellular conditions. Our findings clearly demonstrate the positive impacts of the Fe2+ deficiencies and structural defects in the Fe3O4 structure on the heating performance under cellular and intracellular conditions.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 51
DOI: 10.1021/acs.nanolett.8b02722
|
“3D characterization of heat-induced morphological changes of Au nanostars by fast in situ electron tomography”. Vanrompay H, Bladt E, Albrecht W, Béché, A, Zakhozheva M, Sánchez-Iglesias A, Liz-Marzán LM, Bals S, Nanoscale 10, 22792 (2018). http://doi.org/10.1039/C8NR08376B
Abstract: A thorough understanding of the thermal stability and potential reshaping of anisotropic gold nanostars is required for various potential applications. Combination of a tomographic heating holder with fast tilt series acquisition has been used to monitor temperature-induced morphological changes of Au nanostars. The outcome of our 3D investigations can be used as an input for boundary element method simulations, enabling us to investigate the influence of reshaping on the nanostars’ plasmonic properties. Our work leads to a better understanding of the mechanism behind thermal reshaping. In addition, the approach presented here is generic and can hence be applied to a wide variety of nanoparticles made of different materials and with arbitrary morphology.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 55
DOI: 10.1039/C8NR08376B
|
“Plasma-based multi-reforming for Gas-To-Liquid: tuning the plasma chemistry towards methanol”. Snoeckx R, Wang W, Zhang X, Cha MS, Bogaerts A, Scientific reports 8, 15929 (2018). http://doi.org/10.1038/s41598-018-34359-x
Abstract: Because of its unique properties, plasma technology has gained much prominence in the
microelectronics industry. Recently, environmental and energy applications of plasmas have gained a lot of attention. In this area, the focus is on converting CO 2 and reforming hydrocarbons, with the goal of developing an efficient single-step ‘gas-to-liquid’ (GTL) process. Here we show that applying tri-reforming principles to plasma—further called ‘plasma-based multi-reforming’—allows us to better control the plasma chemistry and thus the formed products. To demonstrate this, we used chemical kinetics calculations supported by experiments and reveal that better control of the plasma chemistry can be achieved by adding O 2 or H 2 O to a mixture containing CH 4 and CO 2 (diluted in N 2 ). Moreover, by adding O 2 and H 2 O simultaneously, we can tune the plasma chemistry even further, improving the conversions, thermal efficiency and methanol yield. Unlike thermocatalytic reforming, plasma-based reforming is capable of producing methanol in a single step; and compared with traditional plasma-based dry reforming, plasma-based multi-reforming increases the methanol yield by more than seven times and the thermal efficiency by 49%, as revealed by our model calculations. Thus, we believe that by using plasma-based multi-reforming, ‘gas-to-liquid’ conversion may be made efficient and scalable.
Keywords: A1 Journal article; Engineering sciences. Technology; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 4.259
DOI: 10.1038/s41598-018-34359-x
|
“Reduction of Human Glioblastoma Spheroids Using Cold Atmospheric Plasma: The Combined Effect of Short- and Long-Lived Reactive Species”. Privat-Maldonado A, Gorbanev Y, Dewilde S, Smits E, Bogaerts A, Cancers 10, 394 (2018). http://doi.org/10.3390/cancers10110394
Abstract: Cold atmospheric plasma (CAP) is a promising technology against multiple types of cancer. However, the current findings on the effect of CAP on two-dimensional glioblastoma cultures do not consider the role of the tumour microenvironment. The aim of this study was to determine the ability of CAP to reduce and control glioblastoma spheroid tumours in vitro . Three-dimensional glioblastoma spheroid tumours (U87-Red, U251-Red) were consecutively treated directly and indirectly with a CAP using dry He, He + 5% H 2 O or He + 20% H 2 O. The cytotoxicity and spheroid shrinkage were monitored using live imaging. The reactive oxygen and nitrogen species produced in phosphate buffered saline (PBS) were measured by electron paramagnetic resonance (EPR) and colourimetry. Cell migration was also assessed. Our results demonstrate that consecutive CAP treatments (He + 20% H 2 O) substantially shrank U87-Red spheroids and to a lesser degree, U251-Red spheroids. The cytotoxic effect was due to the short- and long-lived species delivered by CAP: they inhibited spheroid growth, reduced cell migration and decreased proliferation in CAP-treated spheroids. Direct treatments were more effective than indirect treatments, suggesting the importance of CAP-generated, short-lived species for the growth inhibition and cell cytotoxicity of solid glioblastoma tumours. We concluded that CAP treatment can effectively reduce glioblastoma tumour size and restrict cell migration, thus demonstrating the potential of CAP therapies for glioblastoma.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
DOI: 10.3390/cancers10110394
|
“Recent Advances in Transmission Electron Microscopy for Materials Science at the EMAT Lab of the University of Antwerp”. Guzzinati G, Altantzis T, Batuk M, De Backer A, Lumbeeck G, Samaee V, Batuk D, Idrissi H, Hadermann J, Van Aert S, Schryvers D, Verbeeck J, Bals S, Materials 11, 1304 (2018). http://doi.org/10.3390/ma11081304
Abstract: The rapid progress in materials science that enables the design of materials down to the nanoscale also demands characterization techniques able to analyze the materials down to the same scale, such as transmission electron microscopy. As Belgium’s foremost electron microscopy group, among the largest in the world, EMAT is continuously contributing to the development of TEM techniques, such as high-resolution imaging, diffraction, electron tomography, and spectroscopies, with an emphasis on quantification and reproducibility, as well as employing TEM methodology at the highest level to solve real-world materials science problems. The lab’s recent contributions are presented here together with specific case studies in order to highlight the usefulness of TEM to the advancement of materials science.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.654
Times cited: 15
DOI: 10.3390/ma11081304
|
“Enhanced electrochemical performance of Li-rich cathode materials through microstructural control”. Serrano-Sevillano J, Reynaud M, Saracibar A, Altantzis T, Bals S, van Tendeloo G, Casas-Cabanas M, Physical chemistry, chemical physics 20, 23112 (2018). http://doi.org/10.1039/C8CP04181D
Abstract: The microstructural complexity of Li-rich cathode materials has so far hampered understanding the critical link between size, morphology and structural defects with both capacity and voltage fadings that this family of materials exhibits. Li2MnO3 is used here as a model material to extract reliable structure–property
relationships that can be further exploited for the development of high-performing and long-lasting Li-rich oxides. A series of samples with microstructural variability have been prepared and thoroughly characterized using the FAULTS software, which allows quantification of planar defects and extraction of
average crystallite sizes. Together with transmission electron microscopy (TEM) and density functional theory (DFT) results, the successful application of FAULTS analysis to Li2MnO3 has allowed rationalizing the synthesis conditions and identifying the individual impact of concurrent microstructural features on
both voltage and capacity fadings, a necessary step for the development of high-capacity Li-ion cathode materials with enhanced cycle life.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.123
Times cited: 36
DOI: 10.1039/C8CP04181D
|
“Metal–insulator-transition engineering by modulation tilt-control in perovskite nickelates for room temperature optical switching”. Liao Z, Gauquelin N, Green RJ, Müller-Caspary K, Lobato I, Li L, Van Aert S, Verbeeck J, Huijben M, Grisolia MN, Rouco V, El Hage R, Villegas JE, Mercy A, Bibes M, Ghosez P, Sawatzky GA, Rijnders G, Koster G, America 115, 9515 (2018). http://doi.org/10.1073/pnas.1807457115
Abstract: In transition metal perovskites ABO3 the physical properties are largely driven by the rotations of the BO6 octahedra, which can be tuned in thin films through strain and dimensionality control. However, both approaches have fundamental and practical limitations due to discrete and indirect variations in bond angles, bond lengths and film symmetry by using commercially available substrates. Here, we introduce modulation tilt control as a new approach to tune the ground state of perovskite oxide thin films by acting explicitly on the oxygen octahedra rotation modes, i.e. directly on the bond angles. By intercalating the prototype SmNiO3 target material with a tilt-control layer, we cause the system to change the natural amplitude of a given rotation mode without affecting the interactions. In contrast to strain and dimensionality engineering, our method enables a continuous fine-tuning of the materials properties. This is achieved through two independent adjustable parameters: the nature of the tilt-control material (through its symmetry, elastic constants and oxygen rotation angles) and the relative thicknesses of the target and tilt-control materials. As a result, a magnetic and electronic phase diagram can be obtained, normally only accessible by A-site element substitution, within the single SmNiO3 compound. With this unique approach, we successfully adjusted the metal-insulator transition (MIT) to room temperature to fulfill the desired conditions for optical switching applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.661
Times cited: 50
DOI: 10.1073/pnas.1807457115
|
“Spectral field mapping in plasmonic nanostructures with nanometer resolution”. Krehl J, Guzzinati G, Schultz J, Potapov P, Pohl D, Martin J, Verbeeck J, Fery A, Büchner B, Lubk A, Nature communications 9, 4207 (2018). http://doi.org/10.1038/s41467-018-06572-9
Abstract: Plasmonic nanostructures and -devices are rapidly transforming light manipulation technology by allowing to modify and enhance optical fields on sub-wavelength scales. Advances in this field rely heavily on the development of new characterization methods for the fundamental nanoscale interactions. However, the direct and quantitative mapping of transient electric and magnetic fields characterizing the plasmonic coupling has been proven elusive to date. Here we demonstrate how to directly measure the inelastic momentum transfer of surface plasmon modes via the energy-loss filtered deflection of a focused electron beam in a transmission electron microscope. By scanning the beam over the sample we obtain a spatially and spectrally resolved deflection map and we further show how this deflection is related quantitatively to the spectral component of the induced electric and magnetic fields pertaining to the mode. In some regards this technique is an extension to the established differential phase contrast into the dynamic regime.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 15
DOI: 10.1038/s41467-018-06572-9
|
“Impact of the Particle Diameter on Ion Cloud Formation from Gold Nanoparticles in ICPMS”. Fuchs J, Aghaei M, Schachel TD, Sperling M, Bogaerts A, Karst U, Analytical chemistry 90, 10271 (2018). http://doi.org/10.1021/acs.analchem.8b02007
Abstract: The unique capabilities of microsecond dwell time (DT) single-particle inductively coupled plasma mass spectrometry (spICPMS) were utilized to characterize the cloud of ions generated from the introduction of suspensions of gold nanoparticles (AuNPs) into the plasma. A set of narrowly distributed particles with diameters ranging from 15.4 to 100.1 nm was synthesized and characterized according to established protocols. Statistically significant numbers of the short transient spICPMS events were evaluated by using 50 μs DT for their summed intensity, maximum intensity, and duration, of which all three were found to depend on the particle diameter. The summed intensity increases from 10 to 1661 counts and the maximum intensity from 6 to 309 counts for AuNPs with diameters from 15.4 to 83.2 nm. The event duration rises from 322 to 1007 μs upon increasing AuNP diameter. These numbers represent a comprehensive set of key data points of the ion clouds generated in ICPMS from AuNPs. The extension of event duration is of high interest to appoint the maximum possible particle number concentration at which separation of consecutive events in spICPMS can still be achieved. Moreover, the combined evaluation of all above-mentioned ion cloud characteristics can explain the regularly observed prolonged single-particle events. The transport and ionization behavior of AuNPs in the ICP was also computationally modeled to gain insight into the size-dependent signal generation. The simulated data reveals that the plasma temperature, and therefore the point of ionization of the particles, is the same for all diameters. However, the maximum number density of Au+, as well as the extent of the ion cloud, depends on the particle diameter, in agreement with the experimental data, and it provides an adequate explanation for the observed ion cloud characteristics.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 6.32
Times cited: 5
DOI: 10.1021/acs.analchem.8b02007
|
“Nanoscale insight into silk-like protein self-assembly: effect of design and number of repeat units”. Razzokov J, Naderi S, van der Schoot P, Physical biology 15, 066010 (2018). http://doi.org/10.1088/1478-3975/aadb5e
Abstract: By means of replica exchange molecular dynamics simulations we investigate how the length of a silk-like, alternating diblock oligopeptide influences its secondary and quaternary structure. We carry out simulations for two protein sizes consisting of three and five blocks, and study the stability of a single protein, a dimer, a trimer and a tetramer. Initial configurations of our simulations are β-roll and β-sheet structures. We find that for the triblock the secondary and quaternary structures upto and including the tetramer are unstable: the proteins melt into random coil structures and the aggregates disassemble either completely or partially. We attribute this to the competition between conformational entropy of the proteins and the formation of hydrogen bonds and hydrophobic interactions between proteins. This is confirmed by our simulations on the pentablock proteins, where we find that, as the number of monomers in the aggregate increases, individual monomers form more hydrogen bonds whereas their solvent accessible surface area decreases. For the pentablock β-sheet protein, the monomer and the dimer melt as well, although for the β-roll protein only the monomer melts. For both trimers and tetramers remain stable. Apparently, for these the entropy loss of forming β-rolls and β-sheets is compensated for in the free-energy gain due to the hydrogen-bonding and hydrophobic interactions. We also find that the middle monomers in the trimers and tetramers are conformationally much more stable than the ones on the top and the bottom. Interestingly, the latter are more stable on the tetramer than on the trimer, suggesting that as the number of monomers increases protein-protein interactions cooperatively stabilize the assembly.
According to our simulations, the β-roll and β-sheet aggregates must be approximately equally
stable.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Times cited: 1
DOI: 10.1088/1478-3975/aadb5e
|
“Novel power-to-syngas concept for plasma catalytic reforming coupled with water electrolysis”. Li K, Liu J-L, Li X-S, Lian H-Y, Zhu X, Bogaerts A, Zhu A-M, Chemical engineering journal 353, 297 (2018). http://doi.org/10.1016/j.cej.2018.07.111
Abstract: We propose a novel Power to Synthesis Gas (P2SG) approach, composed of two high-efficiency and renewable electricity-driven units, i.e., plasma catalytic reforming (PCR) and water electrolysis (WE), to produce high quality syngas from CH4, CO2 and H2O. As WE technology is already commercial, we mainly focus on the PCR unit, consisting of gliding arc plasma and Ni-based catalyst, for oxidative dry reforming of methane. An energy efficiency of 78.9% and energy cost of 1.0 kWh/Nm3 at a CH4 conversion of 99% and a CO2 conversion of 79% are obtained. Considering an energy efficiency of 80% for WE, the P2SG system yields an overall energy efficiency of 79.3% and energy cost of 1.8 kWh/Nm3. High-quality syngas is produced without the need for posttreatment units, featuring the ideal stoichiometric number of 2, with concentration of 94.6 vol%, and a desired CO2 fraction of 1.9 vol% for methanol synthesis. The PCR unit has the advantage of fast response to adapting to fluctuation of renewable electricity, avoiding local hot spots in the catalyst bed and coking, in contrast to conventional catalytic processes. Moreover, pure O2 from the WE unit is directly utilized by the PCR unit for oxidative dry reforming of methane, and thus, no air separation unit, like in conventional processes, is required. This work demonstrates the viability of the P2SG approach for large-scale energy storage of renewable electricity via electricity-to-fuel conversion.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 6.216
Times cited: 7
DOI: 10.1016/j.cej.2018.07.111
|
“The maximum a posteriori probability rule for atom column detection from HAADF STEM images”. Fatermans J, Van Aert S, den Dekker AJ, Ultramicroscopy 201, 81 (2019). http://doi.org/10.1016/j.ultramic.2019.02.003
Abstract: Recently, the maximum a posteriori (MAP) probability rule has been proposed as an objective and quantitative method to detect atom columns and even single atoms from high-resolution high-angle annular dark-field (HAADF) scanning transmission electron microscopy (STEM) images. The method combines statistical parameter estimation and model-order selection using a Bayesian framework and has been shown to be especially useful for the analysis of the structure of beam-sensitive nanomaterials. In order to avoid beam damage, images of such materials are usually acquired using a limited incoming electron dose resulting in a low contrast-to-noise ratio (CNR) which makes visual inspection unreliable. This creates a need for an objective and quantitative approach. The present paper describes the methodology of the MAP probability rule, gives its step-by-step derivation and discusses its algorithmic implementation for atom column detection. In addition, simulation results are presented showing that the performance of the MAP probability rule to detect the correct number of atomic columns from HAADF STEM images is superior to that of other model-order selection criteria, including the Akaike Information Criterion (AIC) and the Bayesian Information Criterion (BIC). Moreover, the MAP probability rule is used as a tool to evaluate the relation between STEM image quality measures and atom detectability resulting in the introduction of the so-called integrated CNR (ICNR) as a new image quality measure that better correlates with atom detectability than conventional measures such as signal-to-noise ratio (SNR) and CNR.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 1
DOI: 10.1016/j.ultramic.2019.02.003
|
“Quantitative modeling of secondary electron emission from slow-ion bombardment on semiconductors”. Bercx M, Partoens B, Lamoen D, Physical review B 99, 085413 (2019). http://doi.org/10.1103/PhysRevB.99.085413
Abstract: When slow ions incident on a surface are neutralized, the excess potential energy is passed on to an electron inside the surface, leading to emission of secondary electrons. The microscopic description of this process, as
well as the calculation of the secondary electron yield, is a challenging problem due to its complexity as well
as its sensitivity to surface properties. One of the first quantitative descriptions was articulated in the 1950s by
Hagstrum, who based his calculation on a parametrization of the density of states of the material. In this paper, we
present a model for calculating the secondary electron yield, derived from Hagstrum’s initial approach. We use
first-principles density functional theory calculations to acquire the necessary input and introduce the concept of
electron cascades to Hagstrum’s model in order to improve the calculated spectra, as well as remove its reliance
on fitting parameters. We apply our model to He+ and Ne+ ions incident on Ge(111) and Si(111) and obtain
yield spectra that match closely to the experimental results of Hagstrum.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 5
DOI: 10.1103/PhysRevB.99.085413
|
“Control of Knock-On Damage for 3D Atomic Scale Quantification of Nanostructures: Making Every Electron Count in Scanning Transmission Electron Microscopy”. Van Aert S, De Backer A, Jones L, Martinez GT, Béché, A, Nellist PD, Physical review letters 122, 066101 (2019). http://doi.org/10.1103/PhysRevLett.122.066101
Abstract: Understanding nanostructures down to the atomic level is the key to optimizing the design of advancedmaterials with revolutionary novel properties. This requires characterization methods capable of quantifying the three-dimensional (3D) atomic structure with the highest possible precision. A successful approach to reach this goal is to count the number of atoms in each atomic column from 2D annular dark field scanning transmission electron microscopy images. To count atoms with single atom sensitivity, a minimum electron dose has been shown to be necessary, while on the other hand beam damage, induced by the high energy electrons, puts a limit on the tolerable dose. An important challenge is therefore to develop experimental strategies to optimize the electron dose by balancing atom-counting fidelity vs the risk of knock-on damage. To achieve this goal, a statistical framework combined with physics-based modeling of the dose-dependent processes is here proposed and experimentally verified. This model enables an investigator to theoretically predict, in advance of an experimental measurement, the optimal electron dose resulting in an unambiguous quantification of nanostructures in their native state with the highest attainable precision.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.462
Times cited: 3
DOI: 10.1103/PhysRevLett.122.066101
|
“Electrical Polarization in AlN/GaN Nanodisks Measured by Momentum-Resolved 4D Scanning Transmission Electron Microscopy”. Müller-Caspary K, Grieb T, Müßener J, Gauquelin N, Hille P, Schörmann J, Verbeeck J, Van Aert S, Eickhoff M, Rosenauer A, Physical review letters 122, 106102 (2019). http://doi.org/10.1103/PhysRevLett.122.106102
Abstract: We report the mapping of polarization-induced internal electric fields in AlN/GaN nanowire heterostructures at unit cell resolution as a key for the correlation of optical and structural phenomena in semiconductor optoelectronics. Momentum-resolved aberration-corrected scanning transmission electron microscopy is employed as a new imaging mode that simultaneously provides four-dimensional data in real and reciprocal space. We demonstrate how internal mesoscale and atomic electric fields can be separated in an experiment, which is verified by comprehensive dynamical simulations of multiple electron scattering. A mean difference of 5.3 +- 1.5 MV/cm is found for the polarization-induced electric fields in AlN and GaN, being in accordance with dedicated simulations and photoluminescence measurements in previous publications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.462
Times cited: 26
DOI: 10.1103/PhysRevLett.122.106102
|
“Influence of M23C6 dissolution on the kinetics of ferrite to austenite transformation in Fe-11Cr-0.06C stainless steel”. Miotti Bettanini A, Ding L, Mithieux J-D, Parrens C, Idrissi H, Schryvers D, Delannay L, Pardoen T, Jacques PJ, Materials &, design 162, 362 (2019). http://doi.org/10.1016/j.matdes.2018.12.005
Abstract: The design of high-strength martensitic stainless steels requires an accurate control over the stability of undesired phases, like carbides and ferrite, which can hamper strength and ductility. Here, the ferrite to austenite transformation in Fe-11Cr-0.06C has been studied with a combined experimental-modelling approach. Experimental observations of the austenization process indicate that austenite growth proceeds in multiple steps, each one characterized by a different transformation rate. DICTRA based modelling reveals that the dissolution of the M23C6 Cr-rich carbides leads to Cr partitioning between austenite and parent phases, which controls the rate of transformation through (i) a soft-impingement effect and (ii) consequent stabilization of the ferrite, which remains untransformed inside chromium-enriched-zones even after prolonged austenization stage. Slow heating rate and smaller initial particle sizes allow the design of ferrite-free microstructure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.364
Times cited: 3
DOI: 10.1016/j.matdes.2018.12.005
|
“Hydrogenation of Carbon Dioxide to Value-Added Chemicals by Heterogeneous Catalysis and Plasma Catalysis”. Liu M, Yi Y, Wang L, Guo H, Bogaerts A, Catalysts 9, 275 (2019). http://doi.org/10.3390/catal9030275
Abstract: Due to the increasing emission of carbon dioxide (CO2), greenhouse effects are becoming more and more severe, causing global climate change. The conversion and utilization of CO2 is one of the possible solutions to reduce CO2 concentrations. This can be accomplished, among other methods, by direct hydrogenation of CO2, producing value-added products. In this review, the progress of mainly the last five years in direct hydrogenation of CO2 to value-added chemicals (e.g., CO, CH4, CH3OH, DME, olefins, and higher hydrocarbons) by heterogeneous catalysis and plasma catalysis is summarized, and research priorities for CO2 hydrogenation are proposed.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 3.082
DOI: 10.3390/catal9030275
|
“Transmission electron microscopy study of complex oxide scales on DIN 1.4970 steel exposed to liquid Pb-Bi eutectic”. Charalampopoulou E, Delville R, Verwerft M, Lambrinou K, Schryvers D, Corrosion science 147, 22 (2019). http://doi.org/10.1016/j.corsci.2018.10.018
Abstract: The deployment of Gen-IV lead-cooled fast reactors requires a good compatibility between the selected structural/cladding steels and the inherently corrosive heavy liquid metal coolant. An effective liquid metal corrosion mitigation strategy involves the in-situ steel passivation in contact with the oxygen-containing Pb-alloy coolant. Transmission electron microscopy was used in this work to study the multi-layered oxide scales forming on an austenitic stainless steel fuel cladding exposed to oxygen-containing (CO ≈ 10−6 mass%) static liquid leadbismuth eutectic (LBE) for 1000 h between 400 and 500 °C. The oxide scale constituents were analyzed, including the intertwined phases comprising the innermost biphasic layer.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Times cited: 5
DOI: 10.1016/j.corsci.2018.10.018
|