“Atomic and electronic structures of BaHfO3-doped TFA-MOD-derived YBa2Cu3O7−δthin films”. Molina-Luna L, Duerrschnabel M, Turner S, Erbe M, Martinez GT, Van Aert S, Holzapfel B, Van Tendeloo G, Superconductor science and technology 28, 115009 (2015). http://doi.org/10.1088/0953-2048/28/11/115009
Abstract: Tailoring the properties of oxide-based nanocomposites is of great importance for a wide range of materials relevant for energy technology. YBa2Cu3O7−δ (YBCO) superconducting thin films containing nanosized BaHfO3 (BHO) particles yield a significant improvement of the magnetic flux pinning properties and a reduced anisotropy of the critical current density. These films were prepared by chemical solution deposition (CSD) on (100) SrTiO3 (STO) substrates yielding critical current densities up to 3.6 MA cm−2 at 77 K and self-field. Transport in-field J c measurements demonstrated a high pinning force maximum of around 6 GN/m3 for a sample annealed at T = 760 °C that has a doping of 12 mol% of BHO. This sample was investigated by scanning transmission electron microscopy (STEM) in combination with electron energy-loss spectroscopy (EELS) yielding strain and spectral maps. Spherical BHO nanoparticles of 15 nm in size were found in the matrix, whereas the particles at the interface were flat. A 2 nm diffusion layer containing Ti was found at the YBCO (BHO)/STO interface. Local lattice deformation mapping at the atomic scale revealed crystal defects induced by the presence of both sorts of BHO nanoparticles, which can act as pinning centers for magnetic flux lines. Two types of local lattice defects were identified and imaged: (i) misfit edge dislocations and (ii) Ba-Cu-Cu-Ba stacking faults (Y-248 intergrowths). The local electronic structure and charge transfer were probed by high energy resolution monochromated electron energy-loss spectroscopy. This technique made it possible to distinguish superconducting from non-superconducting areas in nanocomposite samples with atomic resolution in real space, allowing the identification of local pinning sites on the order of the coherence length of YBCO (~1.5 nm) and the determination of 0.25 nm dislocation cores.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 4
DOI: 10.1088/0953-2048/28/11/115009
|
|
|
“Nanoscale mapping of plasmon and exciton in ZnO tetrapods coupled with Au nanoparticles”. Bertoni G, Fabbri F, Villani M, Lazzarini L, Turner S, Van Tendeloo G, Calestani D, Gradečak S, Zappettini A, Salviati G, Scientific reports 6, 19168 (2016). http://doi.org/10.1038/srep19168
Abstract: Metallic nanoparticles can be used to enhance optical absorption or emission in semiconductors, thanks to a strong interaction of collective excitations of free charges (plasmons) with electromagnetic fields. Herein we present the direct imaging at the nanoscale of plasmon-exciton coupling in Au/ZnO nanostructures by combining scanning transmission electron energy loss and cathodoluminescence spectroscopy and mapping. The Au nanoparticles (~30 nm in diameter) are grown in-situ on ZnO nanotetrapods by means of a photochemical process without the need of binding agents or capping molecules. This results in clean interfaces, enabling to prove the occurrence of the plasmon-exciton coupling and the straightforward mapping of its spatial localization. Interestingly, the Au plasmon resonance is localized at the Au/vacuum interface, rather than presenting an isotropic distribution around the nanoparticle. On the contrary, a strong localization of the ZnO excitons, has been observed inside the Au nanoparticle, revealing the existence of the plasmon-exciton coupling, as also confirmed by numerical simulations.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.259
Times cited: 15
DOI: 10.1038/srep19168
|
|
|
“The role of hydrogen during Pt-Ga nanocatalyst formation”. Filez M, Redekop EA, Galvita VV, Poelman H, Meledina M, Turner S, Van Tendeloo G, Bell AT, Marin GB, Physical chemistry, chemical physics 18, 3234 (2016). http://doi.org/10.1039/c5cp07344h
Abstract: Hydrogen plays an essential role during the in situ assembly of tailored catalytic materials, and serves as key ingredient in multifarious chemical reactions promoted by these catalysts. Despite intensive debate for several decades, the existence and nature of hydrogen-involved mechanisms – such as hydrogen-spillover, surface migration – have not been unambiguously proven and elucidated up to date. Here, Pt-Ga alloy formation is used as a probe reaction to study the behavior and atomic transport of H and Ga, starting from Pt nanoparticles on hydrotalcite-derived Mg(Ga)(Al)Ox supports. In situ XANES spectroscopy, time-resolved TAP kinetic experiments, HAADF-STEM imaging and EDX mapping are combined to probe Pt, Ga and H in a series of H2 reduction experiments up to 650 degrees C. Mg(Ga)(Al)Ox by itself dissociates hydrogen, but these dissociated hydrogen species do not induce significant reduction of Ga3+ cations in the support. Only in the presence of Pt, partial reduction of Ga3+ into Gadelta+ is observed, suggesting that different reaction mechanisms dominate for Pt- and Mg(Ga)(Al)Ox-dissociated hydrogen species. This partial reduction of Ga3+ is made possible by Pt-dissociated H species which spillover onto non-reducible Mg(Al)Ox or partially reducible Mg(Ga)(Al)Ox and undergo long-range transport over the support surface. Moderately mobile Gadelta+Ox migrates towards Pt clusters, where Gadelta+ is only fully reduced to Ga0 on condition of immediate stabilization inside Pt-Ga alloyed nanoparticles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.123
Times cited: 10
DOI: 10.1039/c5cp07344h
|
|
|
“Atomic Layer Deposition of Pt Nanoparticles within the Cages of MIL-101: A Mild and Recyclable Hydrogenation Catalyst”. Leus K, Dendooven J, Tahir N, Ramachandran R, Meledina M, Turner S, Van Tendeloo G, Goeman J, Van der Eycken J, Detavernier C, Van Der Voort P, Nanomaterials 6, 45 (2016). http://doi.org/10.3390/nano6030045
Abstract: We present the in situ synthesis of Pt nanoparticles within MIL-101-Cr (MIL = Materials Institute Lavoisier) by means of atomic layer deposition (ALD). The obtained Pt@MIL-101 materials were characterized by means of N2 adsorption and X-ray powder diffraction (XRPD) measurements, showing that the structure of the metal organic framework was well preserved during the ALD deposition. X-ray fluorescence (XRF) and transmission electron microscopy (TEM) analysis confirmed the deposition of highly dispersed Pt nanoparticles with sizes determined by the MIL-101-Cr pore sizes and with an increased Pt loading for an increasing number of ALD cycles. The Pt@MIL-101 material was examined as catalyst in the hydrogenation of different linear and cyclic olefins at room temperature, showing full conversion for each substrate. Moreover, even under solvent free conditions, full conversion of the substrate was observed. A high concentration test has been performed showing that the Pt@MIL-101 is stable for a long reaction time without loss of activity, crystallinity and with very low Pt leaching.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.553
Times cited: 19
DOI: 10.3390/nano6030045
|
|
|
“Direct Imaging of ALD Deposited Pt Nanoclusters inside the Giant Pores of MIL-101”. Meledina M, Turner S, Filippousi M, Leus K, Lobato I, Ramachandran RK, Dendooven J, Detavernier C, Van Der Voort P, Van Tendeloo G, Particle and particle systems characterization 33, 382 (2016). http://doi.org/10.1002/ppsc.201500252
Abstract: MIL-101 giant-pore metal-organic framework (MOF) materials have been loaded with Pt nanoparticles using atomic layer deposition. The final structure has been investigated by aberration-corrected annular dark-field scanning transmission electron microscopy under strictly controlled low dose conditions. By combining the acquired experimental data with image simulations, the position of the small clusters within the individual pores of a metal-organic framework has been determined. The embedding of the Pt nanoparticles is confirmed by electron tomography, which shows a distinct ordering of the highly uniform Pt nanoparticles. The results show that atomic layer deposition is particularly well-suited for the deposition of individual nanoparticles inside MOF framework pores and that, upon proper regulation of the incident electron dose, annular dark-field scanning transmission electron microscopy is a powerful tool for the characterization of this type of materials at a local scale.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.474
Times cited: 11
DOI: 10.1002/ppsc.201500252
|
|
|
“Dislocation/hydrogen interaction mechanisms in hydrided nanocrystalline palladium films”. Amin-Ahmadi B, Connétable D, Fivel M, Tanguy D, Delmelle R, Turner S, Malet L, Godet S, Pardoen T, Proost J, Schryvers D, Idrissi H, Acta materialia 111, 253 (2016). http://doi.org/10.1016/j.actamat.2016.03.054
Abstract: The nanoscale plasticity mechanisms activated during hydriding cycles in sputtered nanocrystalline Pd films have been investigated ex-situ using advanced transmission electron microscopy techniques. The internal stress developing within the films during hydriding has been monitored in-situ. Results showed that in Pd films hydrided to β-phase, local plasticity was mainly controlled by dislocation activity in spite of the small grain size. Changes of the grain size distribution and the crystallographic texture have not been observed. In contrast, significant microstructural changes were not observed in Pd films hydrided to α-phase. Moreover, the effect of hydrogen loading on the nature and density of dislocations has been investigated using aberration-corrected TEM. Surprisingly, a high density of shear type stacking faults has been observed after dehydriding, indicating a significant effect of hydrogen on the nucleation energy barriers of Shockley partial dislocations. Ab-initio calculations of the effect of hydrogen on the intrinsic stable and unstable stacking fault energies of palladium confirm the experimental observations.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 14
DOI: 10.1016/j.actamat.2016.03.054
|
|
|
“One-pot synthesis of Pt catalysts based on layered double hydroxides: an application in propane dehydrogenation”. Filez M, Redekop EA, Poelman H, Galvita VV, Meledina M, Turner S, Van Tendeloo G, Detavernier C, Marin GB, Catalysis science &, technology 6, 1863 (2016). http://doi.org/10.1039/C5CY01274K
Abstract: Simple methods for producing noble metal catalysts with well-defined active sites and improved performance are highly desired in the chemical industry. However, the development of such methods still presents a formidable synthetic challenge. Here, we demonstrate a one-pot synthesis route for the controlled production of bimetallic Pt–In catalysts based on the single-step formation of Mg,Al,Pt,In-containing layered double hydroxides (LDHs). Besides their simple synthesis, these Pt–In catalysts exhibit superior propane dehydrogenation activity compared to their multi-step synthesized analogs. The presented material serves as a showcase for the one-pot synthesis of a broader class of LDH-derived mono- and multimetallic Pt catalysts. The compositional flexibility provided by LDH materials can pave the way towards highperforming Pt-based catalysts with tunable physicochemical properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.773
Times cited: 12
DOI: 10.1039/C5CY01274K
|
|
|
“Fabrication and Characterization of Fe2O3-Based Nanostructures Functionalized with Metal Particles and Oxide Overlayers”. Barreca D, Carraro G, Gasparotto A, Maccato C, Warwick MEA, Turner S, Van Tendeloo G, Journal of advanced microscopy research 10, 239 (2015). http://doi.org/10.1166/jamr.2015.1270
Abstract: We report on the design of nanosystems based on functionalized -Fe 2 O 3 nanostructures supported on fluorine-doped tin oxide (FTO) substrates. The target materials were developed by means of hybrid vapor phase approaches, combining plasma assisted-chemical vapor deposition (PA-CVD) for the production of iron(III) oxide systems and the subsequent radio frequency (RF)-sputtering or atomic layer deposition (ALD) for the functionalization with Au nanoparticles or TiO 2 overlayers, respectively. The interplay between material characteristics and the adopted processing parameters was investigated by complementary analytical techniques, encompassing X-ray photoelectron spectroscopy (XPS), field emission-scanning electron microscopy (FE-SEM), high angle annular dark field-scanning transmission electron microscopy (HAADF-STEM), and energy dispersive X-ray spectroscopy (EDXS). The obtained results highlight the possibility of fabricating Au/ -Fe 2 O 3 nanocomposites, with a controlled dispersion and distribution of metal particles, and TiO 2 / -Fe 2 O 3 heterostructures, characterized by an intimate coupling between the constituent oxides.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1166/jamr.2015.1270
|
|
|
“Anatase TiO2nanoparticle coating on porous COK-12 platelets as highly active and reusable photocatalysts”. Wee LH, Meledina M, Turner S, Custers K, Kerkhofs S, Sree SP, Gobechiya E, Kirschhock CEA, Van Tendeloo G, Martens JA, RSC advances 6, 46678 (2016). http://doi.org/10.1039/C6RA06141A
Abstract: Nanoscale TiO2 photocatalysts are widely used for biomedical applications, self-cleaning processes and wastewater treatments. The impregnation/deposition of TiO2 nanoparticles is indispensable for facile handling and separation as well as the improvement of their photocatalytic performance. In the present study, ordered mesoporous COK-12 silica thin platelets with a high-aspect-ratio and rough surfaces are demonstrated as a potential nanoporous support for homogeneous TiO2 nanoparticle coatings with high loading up to 16.7 wt%. The photocatalytic composite of COK-12 platelets and TiO2 nanoparticles is characterized in detail by HRSEM, SAXS, XRD, N2 physisorption analysis, solid-state UV-vis spectroscopy, HAADF-STEM, EDX analysis, and electron tomography. HAADF-STEM-EDX and electron tomography studies reveal a homogeneous dispersion of nanosized TiO2 nanoparticles over COK-12 platelets. The final composite material with anatase TiO2 nanoparticles that demonstrate a blueshifted semiconductor band gap energy of 3.2 eV coated on a highly porous COK-12 support shows exceptional photocatalytic catalytic activity for photodegradation of organic dyes (rhodamine 6G and methylene blue) and an organic pollutant (1-adamantanol) under UV light radiation, outperforming the commercial P25 TiO2 (Degussa) catalyst.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 6
DOI: 10.1039/C6RA06141A
|
|
|
“Biocompatible Zr-based nanoscale MOFs coated with modified poly(epsilon-caprolactone) as anticancer drug carriers”. Filippousi M, Turner S, Leus K, Siafaka PI, Tseligka ED, Vandichel M, Nanaki SG, Vizirianakis IS, Bikiaris DN, Van Der Voort P, Van Tendeloo G, International journal of pharmaceutics 509, 208 (2016). http://doi.org/10.1016/j.ijpharm.2016.05.048
Abstract: Nanoscale Zr-based metal organic frameworks (MOFs) UiO-66 and UiO-67 were studied as potential anticancer drug delivery vehicles. Two model drugs were used, hydrophobic paclitaxel and hydrophilic cisplatin, and were adsorbed onto/into the nano MOFs (NMOFs). The drug loaded MOFs were further encapsulated inside a modified poly(epsilon-caprolactone) with d-alpha-tocopheryl polyethylene glycol succinate polymeric matrix, in the form of microparticles, in order to prepare sustained release formulations and to reduce the drug toxicity. The drugs physical state and release rate was studied at 37 degrees C using Simulated Body Fluid. It was found that the drug release depends on the interaction between the MOFs and the drugs while the controlled release rates can be attributed to the microencapsulated formulations. The in vitro antitumor activity was assessed using HSC-3 (human oral squamous carcinoma; head and neck) and U-87 MG (human glioblastoma grade IV; astrocytoma) cancer cells. Cytotoxicity studies for both cell lines showed that the polymer coated, drug loaded MOFs exhibited better anticancer activity compared to free paclitaxel and cisplatin solutions at different concentrations.
Keywords: A1 Journal article; Pharmacology. Therapy; Electron microscopy for materials research (EMAT)
Impact Factor: 3.649
Times cited: 37
DOI: 10.1016/j.ijpharm.2016.05.048
|
|
|
“CVD diamond growth from nanodiamond seeds buried under a thin chromium layer”. Degutis G, Pobedinskas P, Turner S, Lu Y-G, Al Riyami S, Ruttens B, Yoshitake T, D'Haen J, Haenen K, Verbeeck J, Hardy A, Van Bael MK, Diamond and related materials 64, 163 (2016). http://doi.org/10.1016/j.diamond.2016.02.013
Abstract: This work presents a morphological and structural analysis of CVD diamond growth on silicon from nanodiamond seeds covered by a 50 nm thick chromium layer. The role of carbon diffusion as well as chromium and carbon silicide formation is analyzed. The local diamond environment is investigated by scanning transmission electron microscopy in combination with electron energy-loss spectroscopy. The evolution of the diamond phase composition (sp3/sp2) is evaluated by micro-Raman spectroscopy. Raman and X-ray diffraction analysis are used to identify the interfacial phases formed during CVD growth. Based upon the observed morphological and structural evolution, a diamond growth model from nanodiamond seeds buried beneath a thin Cr layer is proposed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 11
DOI: 10.1016/j.diamond.2016.02.013
|
|
|
“Strongly Exchange Coupled Core|Shell Nanoparticles with High Magnetic Anisotropy: A Strategy toward Rare-Earth-Free Permanent Magnets”. Lottini E, López-Ortega A, Bertoni G, Turner S, Meledina M, Van Tendeloo G, de Julián Fernández C, Sangregorio C, Chemistry of materials 28, 4214 (2016). http://doi.org/10.1021/acs.chemmater.6b00623
Abstract: Antiferromagnetic(AFM)|ferrimagnetic(FiM) core|shell (CS) nanoparticles (NPs) of formula Co0.3Fe0.7O|Co0.6Fe2.4O4 with mean diameter from 6 to 18 nm have been synthesized through a one-pot thermal decomposition process. The CS structure has been generated by topotaxial oxidation of the core region, leading to the formation of a highly monodisperse single inverted AFM|FiM CS system with variable AFM-core diameter and constant FiM-shell thickness (~2 nm). The sharp interface, the high structural matching between both phases and the good crystallinity of the AFM material have been structurally demonstrated and are corroborated by the robust exchange-coupling between AFM and FiM phases, which gives rise to one among the largest exchange bias (HE) values ever reported for CS NPs (8.6 kOe) and to a strongly enhanced coercive field (HC). In addition, the investigation of the magnetic properties as a function of the AFM-core size (dAFM), revealed a non-monotonous trend of both HC and HE, which display a maximum value for dAFM = 5 nm (19.3 and 8.6 kOe, respectively). These properties induce a huge improvement of the capability of storing energy of the material, a result which suggests that the combination of highly anisotropic AFM|FiM materials can be an efficient strategy towards the realization of novel Rare Earth-free permanent magnets.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 48
DOI: 10.1021/acs.chemmater.6b00623
|
|
|
“Enhanced optoelectronic performances of vertically aligned hexagonal boron nitride nanowalls-nanocrystalline diamond heterostructures”. Sankaran KJ, Hoang DQ, Kunuku S, Korneychuk S, Turner S, Pobedinskas P, Drijkoningen S, Van Bael MK, D' Haen J, Verbeeck J, Leou K-C, Lin I-N, Haenen K, Scientific reports 6, 29444 (2016). http://doi.org/10.1038/srep29444
Abstract: Field electron emission (FEE) properties of vertically aligned hexagonal boron nitride nanowalls (hBNNWs) grown on Si have been markedly enhanced through the use of nitrogen doped nanocrystalline diamond (nNCD) films as an interlayer. The FEE properties of hBNNWs-nNCD heterostructures show a low turn-on field of 15.2 V/mum, a high FEE current density of 1.48 mA/cm(2) and life-time up to a period of 248 min. These values are far superior to those for hBNNWs grown on Si substrates without the nNCD interlayer, which have a turn-on field of 46.6 V/mum with 0.21 mA/cm(2) FEE current density and life-time of 27 min. Cross-sectional TEM investigation reveals that the utilization of the diamond interlayer circumvented the formation of amorphous boron nitride prior to the growth of hexagonal boron nitride. Moreover, incorporation of carbon in hBNNWs improves the conductivity of hBNNWs. Such a unique combination of materials results in efficient electron transport crossing nNCD-to-hBNNWs interface and inside the hBNNWs that results in enhanced field emission of electrons. The prospective application of these materials is manifested by plasma illumination measurements with lower threshold voltage (370 V) and longer life-time, authorizing the role of hBNNWs-nNCD heterostructures in the enhancement of electron emission.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.259
Times cited: 15
DOI: 10.1038/srep29444
|
|
|
“The effect of molecular structure of organic compound on the direct high-pressure synthesis of boron-doped nanodiamond: Effect of organic compound on synthesis of boron-doped nanodiamond”. Ekimov EA, Kudryavtsev OS, Turner S, Korneychuk S, Sirotinkin VP, Dolenko TA, Vervald AM, Vlasov II, Physica status solidi : A : applications and materials science 213, 2582 (2016). http://doi.org/10.1002/pssa.201600181
Abstract: Evolution of crystalline phases with temperature has been studied in materials produced by high-pressure high-temperature treatment of 9-borabicyclo[3.3.1]nonane dimer (9BBN), triphenylborane and trimesitylborane. The boron-doped diamond nanoparticles with a size below 10 nm were obtained at 8–9 GPa and temperatures 970–1250 °C from 9BBN only. Bridged structure and the presence of boron atom in the carbon cycle of 9BBN were revealed to be a key point for the direct synthesis of doped diamond nanocrystals. The diffusional transformation of the disordered carbon phase is suggested to be the main mechanism of the nanodiamond formation from 9BBN in the temperature range of 970–1400 °C. Aqueous suspensions of primary boron-doped diamond nanocrystals were prepared upon removal of non-diamond phases that opens wide opportunities for application of this new nanomaterial in electronics and biotechnologies.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.775
Times cited: 8
DOI: 10.1002/pssa.201600181
|
|
|
“Direct imaging of boron segregation at dislocations in B:diamond heteroepitaxial films”. Turner S, Idrissi H, Sartori AF, Korneychuck S, Lu Y-G, Verbeeck J, Schreck M, Van Tendeloo G, Nanoscale 8, 2212 (2016). http://doi.org/10.1039/c5nr07535a
Abstract: A thin film of heavily B-doped diamond has been grown epitaxially by microwave plasma chemical vapor deposition on an undoped diamond layer, on top of a Ir/YSZ/Si(001) substrate stack, to study the boron segregation and boron environment at the dislocations present in the film. The density and nature of the dislocations were investigated by conventional and weak-beam dark-field transmission electron microscopy techniques, revealing the presence of two types of dislocations: edge and mixed-type 45 degrees dislocations. The presence and distribution of B in the sample was studied using annular dark-field scanning transmission electron microscopy and spatially resolved electron energy-loss spectroscopy. Using these techniques, a segregation of B at the dislocations in the film is evidenced, which is shown to be intermittent along the dislocation. A single edge-type dislocation was selected to study the distribution of the boron surrounding the dislocation core. By imaging this defect at atomic resolution, the boron is revealed to segregate towards the tensile strain field surrounding the edge-type dislocations. An investigation of the fine structure of the B-K edge at the dislocation core shows that the boron is partially substitutionally incorporated into the diamond lattice and partially present in a lower coordination (sp(2)-like hybridization).
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 15
DOI: 10.1039/c5nr07535a
|
|
|
“Influence of defect distribution on the reducibility of CeO2-x nanoparticles”. Spadaro MC, Luches P, Bertoni G, Grillo V, Turner S, Van Tendeloo G, Valeri S, D'Addato S, Nanotechnology 27, 425705 (2016). http://doi.org/10.1088/0957-4484/27/42/425705
Abstract: Ceria nanoparticles (NPs) are fundamental in heterogeneous catalysis because of their ability to store or release oxygen depending on the ambient conditions. Their oxygen storage capacity is strictly related to the exposed planes, crystallinity, density and distribution of defects. In this work a study of ceria NPs produced with a ligand-free, physical synthesis method is presented. The NP films were grown by a magnetron sputtering based gas aggregation source and studied by high resolution- and scanning-transmission electron microscopy and x-ray photoelectron spectroscopy. In particular, the influence of the oxidation procedure on the NP reducibility has been investigated. The different reducibility has been correlated to the exposed planes, crystallinity and density and distribution of structural defects. The results obtained in this work represent a basis to obtain cerium oxide NP with desired oxygen transport properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 11
DOI: 10.1088/0957-4484/27/42/425705
|
|
|
“Unique nanostructural features in Fe, Mn-doped YBCO thin films”. Meledin A, Turner S, Cayado P, Mundet B, Solano E, Ricart S, Ros J, Puig T, Obradors X, Van Tendeloo G, Superconductor science and technology 29, 125009 (2016). http://doi.org/10.1088/0953-2048/29/12/125009
Abstract: An attempt to grow a thin epitaxial composite film of YBa2Cu3O7−δ (YBCO) with spinel MnFe2O4 (MFO) nanoparticles on a LAO substrate using the CSD approach resulted in a decomposition of the spinel and various doping modes of YBCO with the Fe and Mn cations. These nanostructural effects lead to a lowering of T c and a slight J c increase in field. Using a combination of advanced transmission electron microscopy (TEM) techniques such as atomic resolution high-angle annular dark field scanning TEM, energy dispersive x-ray spectroscopy and electron energy-loss spectroscopy we have been able to decipher and characterize the effects of the Fe and Mn doping on the film architecture. The YBaCuFeO5 anion-deficient double perovskite phase was detected in the form of 3D inclusions as well as epitaxially grown lamellas within the YBCO matrix. These nano-inclusions play a positive role as pinning centers responsible for the J c/J sf (H) dependency smoothening at high magnetic fields in the YBCO-MFO films with respect to the pristine YBCO films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 6
DOI: 10.1088/0953-2048/29/12/125009
|
|
|
“Thick homoepitaxial (110)-oriented phosphorus-doped n-type diamond”. Balasubramaniam Y, Pobedinskas P, Janssens SD, Sakr G, Jomard F, Turner S, Lu YG, Dexters W, Soltani A, Verbeeck J, Barjon J, Nesládek M, Haenen K;, Applied physics letters 109, 062105 (2016). http://doi.org/10.1063/1.4960970
Abstract: The fabrication of n-type diamond is essential for the realization of electronic components for extreme environments. We report on the growth of a 66 mu m thick homoepitaxial phosphorus-doped diamond on a (110)-oriented diamond substrate, grown at a very high deposition rate of 33 mu m h(-1). A pristine diamond lattice is observed by high resolution transmission electron microscopy, which indicates the growth of high quality diamond. About 2.9 x 10(16) cm(-3) phosphorus atoms are electrically active as substitutional donors, which is 60% of all incorporated dopant atoms. These results indicate that P-doped (110)-oriented diamond films deposited at high growth rates are promising candidates for future use in high-power electronic applications. Published by AIP Publishing.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 20
DOI: 10.1063/1.4960970
|
|
|
“Atomic-scale viscoplasticity mechanisms revealed in high ductility metallic glass films”. Idrissi H, Ghidelli M, Béché, A, Turner S, Gravier S, Blandin J-J, Raskin J-P, Schryvers D, Pardoen T, Scientific reports 9, 13426 (2019). http://doi.org/10.1038/s41598-019-49910-7
Abstract: The fundamental plasticity mechanisms in thin freestanding Zr65Ni35 metallic glass films are investigated in order to unravel the origin of an outstanding strength/ductility balance. The deformation process is homogenous until fracture with no evidence of catastrophic shear banding. The creep/relaxation behaviour of the films was characterized by on-chip tensile testing, revealing an activation volume in the range 100–200 Å3. Advanced high-resolution transmission electron microscopy imaging and spectroscopy exhibit a very fine glassy nanostructure with well-defined dense Ni-rich clusters embedded in Zr-rich clusters of lower atomic density and a ~2–3 nm characteristic length scale. Nanobeam electron diffraction analysis reveals that the accumulation of plastic deformation at roomtemperature
correlates with monotonously increasing disruption of the local atomic order. These results provide experimental evidences of the dynamics of shear transformation zones activation in metallic glasses. The impact of the nanoscale structural heterogeneities on the mechanical properties including the rate dependent behaviour is discussed, shedding new light on the governing plasticity mechanisms in metallic glasses with initially heterogeneous atomic arrangement.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.259
DOI: 10.1038/s41598-019-49910-7
|
|
|
“2D atomic mapping of oxidation states in transition metal oxides by scanning transmission electron microscopy and electron energy-loss spectroscopy : reply”. Tan H, Turner S, Yucelen E, Verbeeck J, Van Tendeloo G, Physical review letters 108, 259702 (2012). http://doi.org/10.1103/PHYSREVLETT.108.259702
Keywords: Editorial; Electron microscopy for materials research (EMAT)
Impact Factor: 8.462
DOI: 10.1103/PHYSREVLETT.108.259702
|
|
|
“2D atomic mapping of oxidation states in transition metal oxides by scanning transmission electron microscopy and electron energy-loss spectroscopy”. Tan H, Turner S, Yücelen E, Verbeeck J, Van Tendeloo G, Physical review letters 107, 107602 (2011). http://doi.org/10.1103/PhysRevLett.107.107602
Abstract: Using a combination of high-angle annular dark-field scanning transmission electron microscopy and atomically resolved electron energy-loss spectroscopy in an aberration-corrected transmission electron microscope we demonstrate the possibility of 2D atom by atom valence mapping in the mixed valence compound Mn3O4. The Mn L2,3 energy-loss near-edge structures from Mn2+ and Mn3+ cation sites are similar to those of MnO and Mn2O3 references. Comparison with simulations shows that even though a local interpretation is valid here, intermixing of the inelastic signal plays a significant role. This type of experiment should be applicable to challenging topics in materials science, such as the investigation of charge ordering or single atom column oxidation states in, e.g., dislocations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.462
Times cited: 115
DOI: 10.1103/PhysRevLett.107.107602
|
|
|
“Aberration-corrected microscopy and spectroscopy analysis of pristine, nitrogen containing detonation nanodiamond”. Turner S, Shenderova O, da Pieve F, Lu Y-G, Yücelen E, Verbeeck J, Lamoen D, Van Tendeloo G, Physica status solidi : A : applications and materials science 210, 1976 (2013). http://doi.org/10.1002/pssa.201300315
Abstract: Aberration-corrected transmission electron microscopy, electron energy-loss spectroscopy, and density functional theory (DFT) calculations are used to solve several key questions about the surface structure, the particle morphology, and the distribution and nature of nitrogen impurities in detonation nanodiamond (DND) cleaned by a recently developed ozone treatment. All microscopy and spectroscopy measurements are performed at a lowered acceleration voltage (80/120kV), allowing prolonged and detailed experiments to be carried out while minimizing the risk of knock-on damage or surface graphitization of the nanodiamond. High-resolution TEM (HRTEM) demonstrates the stability of even the smallest nanodiamonds under electron illumination at low voltage and is used to image the surface structure of pristine DND. High resolution electron energy-loss spectroscopy (EELS) measurements on the fine structure of the carbon K-edge of nanodiamond demonstrate that the typical * pre-peak in fact consists of three sub-peaks that arise from the presence of, amongst others, minimal fullerene-like reconstructions at the nanoparticle surfaces and deviations from perfect sp(3) coordination at defects in the nanodiamonds. Spatially resolved EELS experiments evidence the presence of nitrogen within the core of DND particles. The nitrogen is present throughout the whole diamond core, and can be enriched at defect regions. By comparing the fine structure of the experimental nitrogen K-edge with calculated energy-loss near-edge structure (ELNES) spectra from DFT, the embedded nitrogen is most likely related to small amounts of single substitutional and/or A-center nitrogen, combined with larger nitrogen clusters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.775
Times cited: 37
DOI: 10.1002/pssa.201300315
|
|
|
“Advanced TEM investigation of the plasticity mechanisms in nanocrystalline freestanding palladium films with nanoscale twins”. Wang B, Idrissi H, Galceran M, Colla MS, Turner S, Hui S, Raskin JP, Pardoen T, Godet S, Schryvers D, International journal of plasticity 37, 140 (2012). http://doi.org/10.1016/j.ijplas.2012.04.003
Abstract: Nanocrystalline palladium thin films deposited by electron-beam evaporation and deformed by on-chip tensile testing reveal a surprisingly large strain hardening capacity when considering the small similar to 25 nm grain size. The as-grown films contain several coherent single and multifold twin boundaries. The coherency of the twin boundaries considerably decreases with deformation due to dislocation/twin boundary interactions. These reactions are described based on a detailed analysis of the number and the type of dislocations located at the twin boundaries using high-resolution TEM, including aberration corrected microscopy. Sessile Frank dislocations were observed at the twin/matrix interfaces, explaining the loss of the TB coherency due to the Burgers vector pointing out of the twinning plane. Grain boundary mediated processes were excluded as a mechanism dominating the plastic deformation based on the investigation of the grain size distribution as well as the crystallographic texture using Automated Crystallographic Orientation Indexation TEM. Other factors influencing the plastic deformation such as impurities and the presence of a native passivation oxide layer at the surface of the films were investigated using analytical TEM. The twin boundaries observed in the present work partly explain the high strain hardening capacity by providing both increasing resistance to dislocation motion with deformation and a source for dislocation multiplication. (C) 2012 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.702
Times cited: 44
DOI: 10.1016/j.ijplas.2012.04.003
|
|
|
“Ag nanoparticles on mixed Al2O3-Ga2O3 supports as catalysts for the N-alkylation of amines with alcohols”. Geukens I, Vermoortele F, Meledina M, Turner S, Van Tendeloo G, De Vos DE, Applied catalysis : A : general 469, 373 (2014). http://doi.org/10.1016/j.apcata.2013.09.044
Abstract: The combination of AgNO3 with NaH results in Ag nanoparticles that can selectively perform alcohol aminations under mild reaction conditions (110 °C). NaH not only serves as a reducing agent for the Ag salt, but also activates the alcohol for dehydrogenation to the corresponding ketone/aldehyde. The stability of the particles can be improved by immobilizing them onto mixed Al2O3Ga2O3 supports; the combination of Ga and Al provides materials with stronger Lewis acidic sites compared to pure alumina or gallium oxide supports. This leads to catalysts with enhanced activities, without the necessity of adding external Lewis acids. Detailed TEM characterization also reveals a close interaction between the Ag NPs and the gallium oxide phase. The obtained catalysts are recyclable and show activity for the alcohol amination using a variety of aliphatic and aromatic amines under mild conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 24
DOI: 10.1016/j.apcata.2013.09.044
|
|
|
“Analytical TEM study of CVD diamond growth on TiO2 sol-gel layers”. Lu Y-G, Verbeeck J, Turner S, Hardy A, Janssens SD, De Dobbelaere C, Wagner P, Van Bael MK, Van Tendeloo G, Diamond and related materials 23, 93 (2012). http://doi.org/10.1016/j.diamond.2012.01.022
Abstract: The early growth stages of chemical vapor deposition (CVD) diamond on a solgel TiO2 film with buried ultra dispersed diamond seeds (UDD) have been studied. In order to investigate the diamond growth mechanism and understand the role of the TiO2 layer in the growth process, high resolution transmission electron microscopy (HRTEM), energy-filtered TEM and electron energy loss spectroscopy (EELS) techniques were applied to cross sectional diamond film samples. We find evidence for the formation of TiC crystallites inside the TiO2 layer at different diamond growth stages. However, there is no evidence that diamond nucleation starts from these crystallites. Carbon diffusion into the TiO2 layer and the chemical bonding state of carbon (sp2/sp3) were both extensively investigated. We provide evidence that carbon diffuses through the TiO2 layer and that the diamond seeds partially convert to amorphous carbon during growth. This carbon diffusion and diamond to amorphous carbon conversion make the seed areas below the TiO2 layer grow and bend the TiO2 layer upwards to form the nucleation center of the diamond film. In some of the protuberances a core of diamond seed remains, covered by amorphous carbon. It is however unlikely that the remaining seeds are still active during the growth process.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 16
DOI: 10.1016/j.diamond.2012.01.022
|
|
|
“Assisted spray pyrolysis production and characterisation of ZnO nanoparticles with narrow size distribution”. Turner S, Tavernier SMF, Huyberechts G, Bals S, Batenburg KJ, Van Tendeloo G, Journal of nanoparticle research 12, 615 (2010). http://doi.org/10.1007/s11051-009-9630-1
Abstract: Nano-sized ZnO particles with a narrow size distribution and high crystallinity were prepared from aqueous solutions with high concentrations of Zn2+ containing salts and citric acid in a conventional spray pyrolysis setup. Structure, morphology and size of the produced material were compared to ZnO material produced by simple spray pyrolysis of zinc nitrates in the same experimental setup. Using transmission electron microscopy and electron tomography it has been shown that citric acid-assisted spray pyrolysed material is made up of micron sized secondary particles comprising a shell of lightly agglomerated, monocrystalline primary ZnO nanoparticles with sizes in the 2030 nm range, separable by a simple ultrasonic treatment step.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.02
Times cited: 27
DOI: 10.1007/s11051-009-9630-1
|
|
|
“Atomic structure of defects in anion-deficient perovskite-based ferrites with a crystallographic shear structure”. Batuk M, Turner S, Abakumov AM, Batuk D, Hadermann J, Van Tendeloo G, Inorganic chemistry 53, 2171 (2014). http://doi.org/10.1021/ic4028404
Abstract: Crystallographic shear (CS) planes provide a new structure-generation mechanism in the anion-deficient perovskites containing lone-pair cations. Pb2Sr2Bi2Fe6O16, a new n = 6 representative of the AnBnO3n2 homologous series of the perovskite-based ferrites with the CS structure, has been synthesized using the solid-state technique. The structure is built of perovskite blocks with a thickness of four FeO6 octahedra spaced by double columns of FeO5 edge-sharing distorted tetragonal pyramids, forming 1/2[110](101)p CS planes (space group Pnma, a = 5.6690(2) Å, b = 3.9108(1) Å, c = 32.643(1) Å). Pb2Sr2Bi2Fe6O16 features a wealth of microstructural phenomena caused by the flexibility of the CS planes due to the variable ratio and length of the constituting fragments with {101}p and {001}p orientation. This leads to the formation of waves, hairpins, Γ-shaped defects, and inclusions of the hitherto unknown layered anion-deficient perovskites Bi2(Sr,Pb)Fe3O8.5 and Bi3(Sr,Pb)Fe4O11.5. Using a combination of diffraction, imaging, and spectroscopic transmission electron microscopy techniques this complex microstructure was fully characterized, including direct determination of positions, chemical composition, and coordination number of individual atomic species. The complex defect structure makes these perovskites particularly similar to the CS structures in ReO3-type oxides. The flexibility of the CS planes appears to be a specific feature of the Sr-based system, related to the geometric match between the SrO perovskite layers and the {100}p segments of the CS planes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 6
DOI: 10.1021/ic4028404
|
|
|
“Atomic structure of quantum gold nanowires : quantification of the lattice strain”. Kundu P, Turner S, Van Aert S, Ravishankar N, Van Tendeloo G, ACS nano 8, 599 (2014). http://doi.org/10.1021/nn4052315
Abstract: Theoretical studies exist to compute the atomic arrangement in gold nanowires and the influence on their electronic behavior with decreasing diameter. Experimental studies, e.g., by transmission electron microscopy, on chemically synthesized ultrafine wires are however lacking owing to the unavailability of suitable protocols for sample preparation and the stability of the wires under electron beam irradiation. In this work, we present an atomic scale structural investigation on quantum single crystalline gold nanowires of 2 nm diameter, chemically prepared on a carbon film grid. Using low dose aberration-corrected high resolution (S)TEM, we observe an inhomogeneous strain distribution in the crystal, largely concentrated at the twin boundaries and the surface along with the presence of facets and surface steps leading to a noncircular cross section of the wires. These structural aspects are critical inputs needed to determine their unique electronic character and their potential as a suitable catalyst material. Furthermore, electron-beam-induced structural changes at the atomic scale, having implications on their mechanical behavior and their suitability as interconnects, are discussed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 20
DOI: 10.1021/nn4052315
|
|
|
“Au@MOF-5 and Au/Mox@MOF-5 (M = Zn, Ti, x = 1, 2) : preparation and microstructural characterisation”. Müller M, Turner S, Lebedev OI, Wang Y, Van Tendeloo G, Fischer RA, European journal of inorganic chemistry , 1876 (2011). http://doi.org/10.1002/ejic.201001297
Abstract: The Zn-carboxylate-based porous coordination polymer MOF-5 [Zn4O(bdc)3] and the metal oxide loaded materials ZnO@MOF-5 and TiO2@MOF-5 were loaded in a second step with the precursor [ClAuCO] to yield intermediate materials denoted as [ClAuCO]@MOF-5, [ClAuCO]/ZnO@MOF-5 and [ClAuCO]/TiO2@MOF-5. These composites were decomposed to Au@MOF-5, Au/ZnO@MOF-5 and Au/TiO2@MOF-5 under hydrogen at 100 °C. The nanoparticle-loaded hybrid materials were characterised by powder X-ray diffraction (PXRD), IR spectroscopy, X-ray photoelectron spectroscopy (XPS) and N2 sorption measurements, which reveal an intact MOF-5 structure that maintains a high specific surface area. For Au@MOF-5, crystalline Au nanoparticles were distributed over the MOF matrix in a homogeneous fashion with a size of ca. 13 nm, evidenced by high resolution transmission electron microscopy. In the case of Au/ZnO@MOF-5, the Au and metal oxide particles of a few nm in size were coexistent in a given volume of the MOF-5 matrix and were not separated in different crystalline MOF particles. For the TiO2 loaded materials the oxide is preferentially located near the outer surface of the MOF particles, leading to an increase of larger exterior Au particles in comparison to very small interior Au particles as observed for the other materials. Au@MOF-5, Au/ZnO@MOF-5 and Au/TiO2@MOF-5 were tested in liquid-phase oxidation of alcohols. Preliminary results show a high activity for the Au loaded materials in this reaction. This observation is attributed to the microstructure of the composites with very small Au particles distributed homogeneously over the MOF matrix.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
Times cited: 75
DOI: 10.1002/ejic.201001297
|
|
|
“Au@UiO-66 : a base free oxidation catalyst”. Leus K, Concepcion P, Vandichel M, Meledina M, Grirrane A, Esquivel D, Turner S, Poelman D, Waroquier M, Van Speybroeck V, Van Tendeloo G, García H, Van Der Voort P;, RSC advances 5, 22334 (2015). http://doi.org/10.1039/c4ra16800c
Abstract: We present the in situ synthesis of Au nanoparticles within the Zr based Metal Organic Framework, UiO-66. The resulting Au@UiO-66 materials were characterized by means of N-2 sorption, XRPD, UV-Vis, XRF, XPS and TEM analysis. The Au nanoparticles (NP) are homogeneously distributed along the UiO-66 host matrix when using NaBH4 or H-2 as reducing agents. The Au@UiO-66 materials were evaluated as catalysts in the oxidation of benzyl alcohol and benzyl amine employing O-2 as oxidant. The Au@MOF materials exhibit a very high selectivity towards the ketone (up to 100%). Regenerability and stability tests demonstrate that the Au@UiO-66 catalyst can be recycled with a negligible loss of Au species and no loss of crystallinity. In situ IR measurements of UiO-66 and Au@UiO-66-NaBH4, before and after treatment with alcohol, showed an increase in IR bands that can be assigned to a combination of physisorbed and chemisorbed alcohol species. This was confirmed by velocity power spectra obtained from the molecular dynamics simulations. Active peroxo and oxo species on Au could be visualized with Raman analysis.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 38
DOI: 10.1039/c4ra16800c
|
|