“Characterization of IASCC crack tips extracted from neutron-irradiated flux thimble tube specimens in view of a probabilistic fracture model”. Penders AG, Konstantinović, MJ, Van Renterghem W, Bosch R-W, Schryvers D, Somville F, Journal of nuclear materials 571, 154015 (2022). http://doi.org/10.1016/J.JNUCMAT.2022.154015
Abstract: This study reports the properties of irradiation assisted stress corrosion crack tips extracted by means of focused-ion beam from 60 to 80 dpa neutron-irradiated O-ring specimens tested under straining conditions under a pressurized-water reactor environment. Various crack tip morphologies and surrounding deformation features were analyzed as a function of applied stress, surface oxidation state and loading form – constant versus cyclic. All investigated cracks exhibit grain boundary oxidation in front of the crack tip, with the extent of oxidation being proportional to applied stress. These findings clearly demonstrate that, under the subcritical crack propagation regime, the grain boundary oxide grows faster than the crack. On the other hand, crack tips appertaining to specimens with removed oxide layer at the outer surface show comparatively less oxidation at the crack tip, which could indicate towards crack initiation from regions that exemplify lower stress, such as the O-ring inner surface. Cyclic loading is found to have a more pronounced effect on the crack tip microstructure, demonstrating increased deformation twinning and -martensitic transformation, which signifies towards an increased susceptibility to intergranular failure. Still, the extent of crack tip grain boundary oxidation in this case agrees well with expected values for maximum stress applied during cyclic loading. All results are interpreted based on the probabilistic subcritical crack propagation mechanism and provide strong support to a stress-driven internal oxidation model.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.1
DOI: 10.1016/J.JNUCMAT.2022.154015
|
“Discovery of core-shell quasicrystalline particles”. Yang T, Kong Y, Du Y, Li K, Schryvers D, Scripta materialia 222, 115040 (2023). http://doi.org/10.1016/J.SCRIPTAMAT.2022.115040
Abstract: Submicron-sized quasicrystalline particles were obtained in an Al-Zn-Mg-Cu alloy produced by traditional melting. These particles consist of an Al-Fe-Ni core and a Mg-Cu-Zn shell and were found to be stable and embedded randomly in the Al matrix. The diffraction patterns of these core-shell particles reveal a decagonal core and an icosahedral shell with, respectively, ten- and five-fold axes aligned. High resolution scanning transmission electron microscopy of the Mg-Cu-Zn shell confirms the five-fold symmetry atomic arrangement and the icosahedral structure. It can therefore be concluded that Fe and Ni impurities play an important role in mediating the formation of such an unusual ternary core-shell quasicrystalline particle. These findings provide some novel insights in the formation of quasicrystals in traditional industrial Al alloys.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6
DOI: 10.1016/J.SCRIPTAMAT.2022.115040
|
“On the formation mechanisms of intragranular shear bands in olivine by stress-induced amorphization”. Idrissi H, Béché, A, Gauquelin N, Ul-Haq I, Bollinger C, Demouchy S, Verbeeck J, Pardoen T, Schryvers D, Cordier P, Acta materialia 239, 118247 (2022). http://doi.org/10.1016/J.ACTAMAT.2022.118247
Abstract: Intragranular amorphization shear lamellae are found in deformed olivine aggregates. The detailed trans-mission electron microscopy analysis of intragranular lamella arrested in the core of a grain provides novel information on the amorphization mechanism. The deformation field is complex and heteroge-neous, corresponding to a shear crack type instability involving mode I, II and III loading components. The formation and propagation of the amorphous lamella is accompanied by the formation of crystal defects ahead of the tip. These defects are geometrically necessary [001] dislocations, characteristics of high-stress deformation in olivine, and rotational nanodomains which are tentatively interpreted as disclinations. We show that these defects play an important role in dictating the path followed by the amorphous lamella. Stress-induced amorphization in olivine would thus result from a direct crystal-to -amorphous transformation associated with a shear instability and not from a mechanical destabilization due to the accumulation of high number of defects from an intense preliminary deformation. The pref-erential alignment of some lamellae along (010) is a proof of the lower ultimate mechanical strength of these planes.(c) 2022 The Authors. Published by Elsevier Ltd on behalf of Acta Materialia Inc. This is an open access article under the CC BY license ( http://creativecommons.org/licenses/by/4.0/ )
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.4
Times cited: 5
DOI: 10.1016/J.ACTAMAT.2022.118247
|
“Enhancement of toughness of Al-to-steel Friction Melt Bonded welds via metallic interlayers”. Jimenez-Mena N, Jacques PJ, Ding L, Gauquelin N, Schryvers D, Idrissi H, Delannay F, Simar A, Materials science and engineering: part A: structural materials: properties, microstructure and processing 740-741, 274 (2019). http://doi.org/10.1016/j.msea.2018.10.101
Abstract: The toughness of Al-to-steel welds decreases with increasing thickness of the intermetallic (IM) layer formed at the interface. Co plating has been added as interlayer in Al-to-steel Friction Melt Bonded (FMB) welds to control the nature and thickness of the IM layer. In comparison to a weld without interlayer, Co plating brings about a reduction of the thickness of the IM layer by 70%. The critical energy release rate of the crack propagating in the weld is used as an indicator of toughness. It is evaluated via an adapted crack propagation test using an energy conservation criterion. For a weld without interlayer, critical energy release rate is found to increase when the thickness of the intermetallic layer decreases. When the intermetallic layer is thick, the crack propagates in a brittle manner through the intermetallic whereas, at low layer thickness, the crack deviates and partially propagates through the Al plate, which causes an increase of toughness. The use of a Co interlayer brings about an increase of toughness by causing full deviation of the crack towards the Al plate.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 4
DOI: 10.1016/j.msea.2018.10.101
|
“Characterization of (Ti,Mo,Cr)C nanoprecipitates in an austenitic stainless steel on the atomic scale”. Cautaerts N, Delville R, Stergar E, Schryvers D, Verwerft M, Acta materialia 164, 90 (2019). http://doi.org/10.1016/j.actamat.2018.10.018
Abstract: Nanometer sized (Ti,Mo,Cr)C (MX-type) precipitates that grew in a 24% cold worked Ti-stabilized austenitic stainless steel (grade DIN 1.4970, member of the 15-15Ti austenitic stainless steels) after heat treatment were fully characterized with transmission electron microscopy (TEM), probe corrected high angle annular dark field scanning transmission electron microscopy (HR-HAADF STEM), and atom probe tomography (APT). The precipitates shared the cube-on-cube orientation with the matrix and were facetted on {111} planes, yielding octahedral and elongated octahedral shapes. The misfit dislocations were believed to have Burgers vectors a/6<112> which was verified by geometrical phase analysis (GPA) strain mapping of a matrix-precipitate interface. The dislocations were spaced five to seven atomic
planes apart, on average slightly wider than expected for the lattice parameters of steel and TiC. Quantitative atom probe tomography analysis of the precipitates showed that precipitates were significantly enriched in Mo, Cr and V, and that they were hypostoichiometric with respect to C. These findings were consistent with a reduced lattice parameter. The precipitates were found primarily on Shockley
partial dislocations originating from the original perfect dislocation network. These novel findings could contribute to the understanding of how TiC nanoprecipitates interact with point defects and matrix dislocations. This is essential for the application of these Ti-stabilized steels in high temperature environments or fast spectrum nuclear fission reactors.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 2
DOI: 10.1016/j.actamat.2018.10.018
|
“Ni cluster formation in low temperature annealed Ni50.6Ti49.4”. Pourbabak S, Wang X, Van Dyck D, Verlinden B, Schryvers D, Functional materials letters 10, 1740005 (2017). http://doi.org/10.1142/S1793604717400057
Abstract: Various low temperature treatments of Ni50.6Ti49.4 have shown an unexpected effect on the martensitic start temperature. Periodic diffuse intensity distributions in reciprocal space indicate the formation of short pure Ni strings along the <111> directions in the B2 ordered lattice, precursing the formation of Ni4Ti3 precipitates formed at higher annealing temperatures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 1.234
Times cited: 4
DOI: 10.1142/S1793604717400057
|
“Reclaiming the image of daguerreotypes: Characterization of the corroded surface before and after atmospheric plasma treatment”. Grieten E, Schalm O, Tack P, Bauters S, Storme P, Gauquelin N, Caen J, Patelli A, Vincze L, Schryvers D, Journal of cultural heritage (2017). http://doi.org/10.1016/j.culher.2017.05.008
Abstract: Technological developments such as atmospheric plasma jets for industry can be adapted for the conservation of cultural heritage. This application might offer a potential method for the removal or transformation of the corrosion on historical photographs. We focus on daguerreotypes and present an in-depth study of the induced changes by a multi-analytical approach using optical microscopy, scanning electron microscopy, different types of transmission electron microscopy and X-ray absorption fine structure. The H2-He afterglow removes S from an Ag2S or Cu2S layer which results in a nano-layer of metallic Ag or Cu on top of the deteriorated microstructure. In case the corrosion layer is composed of Cu-Ag-S compounds, our proposed setup can be used to partially remove the corrosion. These alterations of the corrosion results in an improvement in the readability of the photographic image.
Keywords: A1 Journal article; Art; History; Electron microscopy for materials research (EMAT); Antwerp Cultural Heritage Sciences (ARCHES)
Impact Factor: 1.838
Times cited: 9
DOI: 10.1016/j.culher.2017.05.008
|
“Martensite crystallography and chemistry in dual phase and fully martensitic steels”. Du C, Hoefnagels JPM, Kolling S, Geers MGD, Sietsma J, Petrov R, Bliznuk V, Koenraad PM, Schryvers D, Amin-Ahmadi B, Materials characterization 139, 411 (2018). http://doi.org/10.1016/j.matchar.2018.03.011
Abstract: Lath martensite is important in industry because it is the key strengthening component in many advanced high strength steels. The study of crystallography and chemistry of lath martensite is extensive in the literature, however, mostly based on fully martensitic steels. In this work, lath martensite in dual phase steels is investigated with a focus on the substructure identification of the martensite islands and microstructural bands using electron backscattered diffraction, and on the influence of the accompanied tempering process during industrial coating process on the distribution of alloying elements using atom probe tomography. Unlike findings for the fully martensitic steels, no martensite islands with all 24 Kurdjumov-Sachs variants have been observed. Almost all martensite islands contain only one main packet with all six variants and minor variants from the remaining three packets of the same prior austenite grain. Similarly, the martensite bands are typically composed of connected domains originating from prior austenite grains, each containing one main packets (mostly with all variants) and few separate variants. The effect of tempering at similar to 450 degrees C (due to the industrial zinc coating process) has also been investigated. The results show a strong carbon partitioning to lath boundaries and Cottrell atmospheres at dislocation core regions due to the thermal process of coating. In contrast, auto-tempering contributes to the carbon redistribution only in a limited manner. The substitutional elements are all homogenously distributed. The phase transformation process has two effects on the material: mechanically, the earlier-formed laths are larger and softer and therefore more ductile (as revealed by nanoindentation); chemically, due to the higher dislocation density inside the later-formed laths, which are generally smaller, carbon Cottrell atmospheres are predominantly observed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
DOI: 10.1016/j.matchar.2018.03.011
|
“Tailoring the Ti-C nanoprecipitate population and microstructure of titanium stabilized austenitic steels”. Cautaerts N, Delville R, Stergar E, Schryvers D, Verwerft M, Journal of nuclear materials 507, 177 (2018). http://doi.org/10.1016/J.JNUCMAT.2018.04.041
Abstract: The present work reports on the microstructural evolution of a new heat of 24% cold worked austenitic DIN 1.4970 (15-15Ti) nuclear cladding steel subjected to ageing heat treatments of varying duration between 500 and 800 degrees C (by steps of 100 degrees C). The primary aim was studying the finely dispersed Ti-C nanoprecipitate population, which are thought to be beneficial for creep and swelling resistance during service. Their size distribution and number density were estimated through dark field imaging and bright field Moire imaging techniques in the transmission electron microscope. Nanoprecipitates formed at and above 600 degrees C, which is a lower temperature than previously reported. The observed nucleation, growth and coarsening behavior of the nanoprecipitates were consistent with simple diffusion arguments. The formation of nanoprecipitates coincided with significant dissociation of dislocations as evidenced by weak beam dark field imaging. Possible mechanisms, including Silcock's stacking fault growth model and Suzuki segregation, are discussed. Recrystallization observed after extended ageing at 800 degrees C caused the redissolution of nanoprecipitates. Large primary Ti(C,N) and (Ti,Mo)C precipitates that occur in the as-received material, and M23C6 precipitates that nucleate on grain boundaries at low temperatures were also characterized by a selective dissolution procedure involving filtration, X-ray diffraction and quantitative Rietveld refinement. The partitioning of key elements between the different phases was derived by combining these findings and was consistent with thermodynamic considerations and the processing history of the steel. (C) 2018 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.048
Times cited: 1
DOI: 10.1016/J.JNUCMAT.2018.04.041
|
“Dislocation driven nanosample plasticity: new insights from quantitative in-situ TEM tensile testing”. Samaee V, Gatti R, Devincre B, Pardoen T, Schryvers D, Idrissi H, Scientific Reports 8, 12012 (2018). http://doi.org/10.1038/s41598-018-30639-8
Abstract: Intrinsic dislocation mechanisms in the vicinity of free surfaces of an almost FIB damage-free single crystal Ni sample have been quantitatively investigated owing to a novel sample preparation method combining twin-jet electro-polishing, in-situ TEM heating and FIB. The results reveal that the small-scale plasticity is mainly controlled by the conversion of few tangled dislocations, still present after heating, into stable single arm sources (SASs) as well as by the successive operation of these sources. Strain hardening resulting from the operation of an individual SAS is reported and attributed to the decrease of the length of the source. Moreover, the impact of the shortening of the dislocation source on the intermittent plastic flow, characteristic of SASs, is discussed. These findings provide essential information for the understanding of the regime of ‘dislocation source’ controlled plasticity and the related mechanical size effect.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 4.259
Times cited: 9
DOI: 10.1038/s41598-018-30639-8
|
“Effect of hydriding induced defects on the small-scale plasticity mechanisms in nanocrystalline palladium thin films”. Lumbeeck G, Idrissi H, Amin-Ahmadi B, Favache A, Delmelle R, Samaee V, Proost J, Pardoen T, Schryvers D, Journal Of Applied Physics 124, 225105 (2018). http://doi.org/10.1063/1.5055274
Abstract: Nanoindentation tests performed on nanocrystalline palladium films subjected to hydriding/dehydriding cycles demonstrate a significant softening when compared to the as-received material. The origin of this softening is unraveled by combining in situ TEM nanomechanical testing with automated crystal orientation mapping in TEM and high resolution TEM. The softening is attributed to the presence of a high density of stacking faults and of Shockley partial dislocations after hydrogen loading. The hydrogen induced defects affect the elementary plasticity mechanisms and the mechanical response by acting as preferential sites for twinning/detwinning during deformation. These results are analyzed and compared to previous experimental and simulation works in the literature. This study provides new insights into the effect of hydrogen on the atomistic deformation and cracking mechanisms as well as on the mechanical properties of nanocrystalline thin films and membranes.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 2.068
Times cited: 2
DOI: 10.1063/1.5055274
|
“Study of the Q&prime, (Q)-phase precipitation in Al–Mg–Si–Cu alloys by quantification of atomic-resolution transmission electron microscopy images and atom probe tomography”. Ding L, Orekhov A, Weng Y, Jia Z, Idrissi H, Schryvers D, Muraishi S, Hao L, Liu Q, Journal of materials science 54, 7943 (2019). http://doi.org/10.1007/s10853-019-03427-6
Abstract: The precipitation mechanism of the Q phase in Al-Mg-Si-Cu alloys has long been the subject of ambiguity and debate since its metastable phase (Q 0) has the same crystal structure and similar lattice parameters as its equilibrium counterparts. In the present work, the evolution of the Q 0 (Q) phase during aging is studied by combination of quantitative atomic-resolution scanning transmission electron microscopy and atom probe tomography. It was found that the transformation from the Q 0 to the Q phase involves changes of the occupancy of Al atoms in atomic columns of the Q 0 (Q) phase. The Al atoms incorporated in the Cu, Si and Mg columns are gradually released into the Al matrix, while mixing between Cu and Si atoms occurs in the Si columns. This transformation process is mainly attributed to the low lattice misfit of the equilibrium Q phase. Besides, the formation of various compositions of the Q phase is due to the different occupancy in the atomic columns of the Q phase. The occupancy changes in the columns of the Q phase are kinetically controlled and are strongly influenced by the alloy composition and aging temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.599
Times cited: 1
DOI: 10.1007/s10853-019-03427-6
|
“ALPHABETA: a dedicated open-source tool for calculating TEM stage tilt angles”. Cautaerts N, Delville R, Schryvers D, Journal of microscopy 273, 189 (2019). http://doi.org/10.1111/jmi.12774
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.692
Times cited: 2
DOI: 10.1111/jmi.12774
|
“In-Situ TEM Stress Induced Martensitic Transformation in Ni50.8Ti49.2 Microwires”. Pourbabak S, Orekhov A, Samaee V, Verlinden B, Van Humbeeck J, Schryvers D, Shape memory and superelasticity 5, 154 (2019). http://doi.org/10.1007/s40830-019-00217-6
Abstract: In-situ transmission electron microscopy tensile straining is used to study the stress induced martensitic transformation in Ni50.8Ti49.2. Two microwire samples with different heat treatment are investigated from which one single crystal and three polycrystalline TEM specimens, the latter with micro- and nano-size grains, have been produced. The measured Young’s modulus for all TEM specimens is around 70 GPa, considerably higher than the averaged 55 GPa of the original microwire sample. The height of the superelastic stress plateau shows an inverse relationship with the specimen thickness for the polycrystalline specimens. Martensite starts nucleating within the elastic region of the stress–strain curve and on the edges of the specimens while also grain boundaries act as nucleation sites in the polycrystalline specimens. When a martensite plate reaches a grain boundary in the polycrystalline specimen, it initiates the transformation in the neighboring grain at the other side of the grain boundary. In later stages martensite plates coalesce at higher loads in the stress plateau. In highly strained specimens, residual martensite remains after release.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1007/s40830-019-00217-6
|
“Microscopic investigation of as built and hot isostatic pressed Hastelloy X processed by Selective Laser Melting”. Pourbabak S, Montero-Sistiaga ML, Schryvers D, Van Humbeeck J, Vanmeensel K, Materials characterization 153, 366 (2019). http://doi.org/10.1016/j.matchar.2019.05.024
Abstract: Microstructural characteristics of Hastelloy X produced by Selective Laser Melting have been investigated by various microscopic techniques in the as built (AB) condition and after hot isostatic pressing (HIP). At sub-grain level the AB material consists of columnar high density dislocation cells while the HIP sample consists of columnar sub-grains with lower dislocation density that originate from the original dislocation cells, contradicting existing models. The sub-grains contain nanoscale precipitates enriched in Al, Ti, Cr and O, located at sub-grain boundaries in the AB condition and within the grains after HIP. At some grain boundaries, micrometer sized chromium carbides are detected after HIP. Micro hardness within the grains was found to decrease after HIP, which was attributed to the decrease in dislocation density due to recovery annealing.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 2
DOI: 10.1016/j.matchar.2019.05.024
|
“Orientation relationship of the austenite-to-ferrite transformation in austenitic stainless steels due to dissolution corrosion in contact with liquid Pb-Bi eutectic”. Charalampopoulou E, Cautaerts N, Van der Donck T, Schryvers D, Lambrinou K, Delville R, Scripta materialia 167, 66 (2019). http://doi.org/10.1016/J.SCRIPTAMAT.2019.03.035
Abstract: The orientation relationship of an austenite-to-ferrite phase transformation in 316L stainless steels induced by the loss of austenite stabilizers resulting from the steel dissolution corrosion in liquid Pb-Bi eutectic was studied by means of electron backscatter diffraction. The misorientations at the austenite/ferrite interface were compared to the prevailing orientation relationship models in steels. The Pitsch orientation relationship model was found to be predominant, which is unusual for austenite-to-ferrite bulk transformations in steels. The nature of this particular transformation, which involves loss of steel alloying elements and the presence of an interfacial liquid metal layer, is discussed to explain this finding. (C) 2019 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 3
DOI: 10.1016/J.SCRIPTAMAT.2019.03.035
|
Cautaerts N, Lamm S, Stergar E, Pakarinen J, Yang Y, Hofer C, Schnitzer R, Felfer P, Verwerft M, Delville R, Schryvers D (2020) Atom probe tomography data collection from DIN 1.4970 (15-15Ti) austenitic stainless steel irradiated with Fe ions
Abstract: This dataset comprises a large collection of atom probe tomography datasets collected from DIN 1.4970 alloy that was irradiated with Fe ions at different conditions. The DIN 1.4970 alloy is an austenitic stainless steel with 15 wt% Cr, 15 wt% Ni, a small addition of Ti. The full composition and characterization of our material can be found published elsewhere [1,2]. Some of our material was subjected to ageing heat treatments at different temperatures for different times. Small samples of our original material and aged material was irradiated at the Michigan Ion Beam Laboratory in 2017 with 4.5 MeV Fe ions up to 40 dpa at an average dose rate of 2×10−4 dpa/s. This was done at three different temperatures: 300, 450, and 600 ºC. Atom probe samples were made of the irradiated layers (approximately 1.5 micron deep) with focused ion beam and mounted on Microtip coupons. APT measurements took place on three CAMECA LEAP-HR systems located at CAES in Idaho Falls, USA (files beginning with R33), at Montanuniversität Leoben in Leoben, Austria (R21) and at Friedrich–Alexander University in Erlangen, Germany (R56).
Keywords: Dataset; Electron microscopy for materials research (EMAT)
DOI: 10.5281/ZENODO.3407832
|
“Crack initiation in tapered high Si stainless steel specimens : stress threshold analyses”. Penders A, Konstantinovic MJ, Bosch RW, Schryvers D, Corrosion Engineering Science And Technology , 1 (2020). http://doi.org/10.1080/1478422X.2020.1785651
Abstract: Tapered specimens were used for an accelerated test technique to study the crack initiation of high Si stainless steel by means of constant elongation rate tensile testing in a simulated pressurised water reactor environment. Detailed crack density distributions were obtained by applying an advanced crack detection algorithm on iteratively displaced scanning electron microscopy pictures featuring stress corrosion cracks along the specimen's gauge length. By means of finite-element analysis, prominent peaks in the crack density graphs are demonstrated to be related to stress relief and stress build-up during the crack initiation phase. Intrinsic scatter related to the crack detection suggests that stress corrosion cracking is independent of the strain-rate for strain-rates lower than 10(-6 )s(-1). Based on the extrapolation to constant load conditions, the critical threshold value for the duplex high Si stainless steel is estimated to be around 580 MPa.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.8
Times cited: 1
DOI: 10.1080/1478422X.2020.1785651
|
“DSC cycling effects on phase transformation temperatures of micron and submicron grain Ni50.8Ti49.2 microwires”. Pourbabak S, Verlinden B, Van Humbeeck J, Schryvers D, Shape memory and superelasticity , 1 (2020). http://doi.org/10.1007/S40830-020-00278-Y
Abstract: The effect of thermal cycling parameters on the phase transformation temperatures of micron and submicron grain size recrystallized Ni-Ti microwires was investigated. The suppression of martensitic transformation by thermal cycling was found to enhance when combined with room temperature aging between the cycles and enhances even more when aged at elevated temperature of 100 degrees C. While aging at room temperature alone has no clear effect on the martensitic transformation, elevated temperature aging at 100 degrees C alone suppresses the martensitic transformation. All aforementioned effects were found to be stronger in large grain samples than in small grain samples. Martensitic transformation suppression in all cases was in line with the formation of Ni4Ti3 precursors in the form of < 111 & rang;(B2) Ni clusters as concluded from the observed diffuse intensity in the electron diffraction patterns revealing short-range ordering enhancement. Performing thermal cycling in some different temperature ranges to separate the effect of martensitic transformation and high temperature range of DSC cycling revealed that both high temperature- and martensitic transformation-included cycles enhance the short-range ordering.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1007/S40830-020-00278-Y
|
“TEM investigation of the role of the polycrystalline-silicon film/substrate interface in high quality radio frequency silicon substrates”. Ding L, Raskin J-P, Lumbeeck G, Schryvers D, Idrissi H, Materials Characterization 161, 110174 (2020). http://doi.org/10.1016/J.MATCHAR.2020.110174
Abstract: The microstructural characteristics of two polycrystalline silicon (poly-Si) films with different electrical properties produced by low-pressure chemical vapour deposition on top of high resistivity silicon substrates were investigated by advanced transmission electron microscopy (TEM), including high resolution aberration corrected TEM and automated crystallographic orientation mapping in TEM. The results reveal that the nature of the poly-Si film/Si substrate interface is the main factor controlling the electrical resistivity of the poly-Si films. The high resistivity and high electrical linearity of poly-Si films are strongly promoted by the Sigma 3 twin type character of the poly-Si/Si substrate interface, leading to the generation of a huge amount of extended defects including stacking faults, Sigma 3 twin boundaries as well as Sigma 9 grain boundaries at this interface. Furthermore, a high density of interfacial dislocations has been observed at numerous common and more exotic grain boundaries deviating from their standard crystallographic planes. In contrast, poly-Si film/Si substrate interfaces with random character do not favour the formation of such complex patterns of defects, leading to poor electrical resistivity of the poly-Si film. This finding opens windows for the development of high resistivity silicon substrates for Radio Frequency (RF) integrated circuits (ICs) applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.7
DOI: 10.1016/J.MATCHAR.2020.110174
|
“The role of Ti and TiC nanoprecipitates in radiation resistant austenitic steel: A nanoscale study”. Cautaerts N, Delville R, Stergar E, Pakarinen J, Verwerft M, Yang Y, Hofer C, Schnitzer R, Lamm S, Felfer P, Schryvers D, Acta Materialia 197, 184 (2020). http://doi.org/10.1016/J.ACTAMAT.2020.07.022
Abstract: This work encompasses an in-depth transmission electron microscopy and atom probe tomography study of Ti-stabilized austenitic steel irradiated with Fe-ions. The focus is on radiation induced segregation and precipitation, and in particular on how Ti and TiC affect these processes. A 15-15Ti steel (grade: DIN 1.4970) in two thermo-mechanical states (cold-worked and aged) was irradiated at different temperatures up to a dose of 40 dpa. At low irradiation temperatures, the cold-worked and aged materials evolved to a similar microstructure dominated by small Si and Ni clusters, corresponding to segregation to small point defect clusters. TiC precipitates, initially present in the aged material, were found to be unstable under these irradiation conditions. Elevated irradiation temperatures resulted in the nucleation of nanometer sized Cr enriched TiC precipitates surrounded by Si and Ni enriched shells. In addition, nanometer sized Ti- and Mn-enriched G-phase (M6Ni16Si7) precipitates formed, often attached to TiC precipitates. Post irradiation, larger number densities of TiC were observed in the cold-worked material compared to the aged material. This was correlated with a lower volume fraction of G-phase. The findings suggest that at elevated irradiation temperatures, the precipitate-matrix interface is an important point defect sink and contributes to the improved radiation resistance of this material. The study is a first of its kind on stabilized steel and demonstrates the significance of the small Ti addition to the evolution of the microstructure under irradiation. (C) 2020 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.4
DOI: 10.1016/J.ACTAMAT.2020.07.022
|
“Optical encoding of luminescent carbon nanodots in confined spaces”. Bartholomeeusen E, De Cremer G, Kennes K, Hammond C, Hermans I, Lu J-B, Schryvers D, Jacobs PA, Roeffaers MBJ, Hofkens J, Sels BF, Coutino-Gonzalez E, Chemical Communications 57, 11952 (2021). http://doi.org/10.1039/D1CC04777A
Abstract: Stable emissive carbon nanodots were generated in zeolite crystals using near infrared photon irradiation gradually converting the occluded organic template, originally used to synthesize the zeolite crystals, into discrete luminescent species consisting of nano-sized carbogenic fluorophores, as ascertained using Raman microscopy, and steady-state and time-resolved spectroscopic techniques. Photoactivation in a confocal laser fluorescence microscope allows 3D resolved writing of luminescent carbon nanodot patterns inside zeolites providing a cost-effective and non-toxic alternative to previously reported metal-based nanoclusters confined in zeolites, and opens up opportunities in bio-labelling and sensing applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
DOI: 10.1039/D1CC04777A
|
““Branched&rdquo, structural transformation of the L12-Al3Zr phase manipulated by Cu substitution/segregation in the Al-Cu-Zr alloy system”. Ding L, Zhao M, Ehlers FJH, Jia Z, Zhang Z, Weng Y, Schryvers D, Liu Q, Idrissi H, Journal of materials science &, technology 185, 186 (2024). http://doi.org/10.1016/j.jmst.2023.11.015
Abstract: The effect of Cu on the evolution of the Al3Zr phase in an Al-Cu-Zr cast alloy during solution treatment at 500 °C has been thoroughly studied by combining atomic resolution high-angle annular dark-field scanning transmission electron microscopy, energy-dispersive X-ray spectroscopy and first-principles cal- culations. The heat treatment initially produces a pure L12-Al3Zr microstructure, allowing for about 13 % Cu to be incorporated in the dispersoid. Cu incorporation increases the energy barrier for anti-phase boundary (APB) activation, thus stabilizing the L12 structure. Additional heating leads to a Cu-induced “branched”path for the L12 structural transformation, with the latter process accelerated once the first APB has been created. Cu atoms may either (i) be repelled by the APBs, promoting the transformation to a Cu-poor D023 phase, or (ii) they may segregate at one Al-Zr layer adjacent to the APB, promoting a transformation to a new thermodynamically favored phase, Al4CuZr, formed when these segregation layers are periodically arranged. Theoretical studies suggest that the branching of the L12 transformation path is linked to the speed at which an APB is created, with Cu attraction triggered by a comparatively slow process. This unexpected transformation behavior of the L12-Al3Zr phase opens a new path to understanding, and potentially regulating the Al3Zr dispersoid evolution for high temperature applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 10.9
DOI: 10.1016/j.jmst.2023.11.015
|
“Electronic and chemical properties of nickel oxide thin films and the intrinsic defects compensation mechanism”. Poulain R, Lumbeeck G, Hunka J, Proost J, Savolainen H, Idrissi H, Schryvers D, Gauquelin N, Klein A, ACS applied electronic materials 4, 2718 (2022). http://doi.org/10.1021/ACSAELM.2C00230
Abstract: Although largely studied, contradictory results on nickel oxide (NiO) properties can be found in the literature. We herein propose a comprehensive study that aims at leveling contradictions related to NiO materials with a focus on its conductivity, surface properties, and the intrinsic charge defects compensation mechanism with regards to the conditions preparation. The experiments were performed by in situ photo-electron spectroscopy, electron energy loss spectroscopy, and optical as well as electrical measurements on polycrystalline NiO thin films prepared under various preparation conditions by reactive sputtering. The results show that surface and bulk properties were strongly related to the deposition temperature with in particular the observation of Fermi level pinning, high work function, and unstable oxygen-rich grain boundaries for the thin films produced at room temperature but not at high temperature (>200 degrees C). Finally, this study provides substantial information about surface and bulk NiO properties enabling to unveil the origin of the high electrical conductivity of room temperature NiO thin films and also for supporting a general electronic charge compensation mechanism of intrinsic defects according to the deposition temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1021/ACSAELM.2C00230
|
“Quasicrystalline clusters transformed from C14-MgZn₂, nanoprecipitates in Al alloys”. Yang T, Kong Y, Li K, Lu Q, Wang Y, Du Y, Schryvers D, Materials characterization 199, 112772 (2023). http://doi.org/10.1016/J.MATCHAR.2023.112772
Abstract: Ultrafine faulty C14-MgZn2 Laves phase precipitates containing quasicrystalline clusters and demonstrating the formation of binary quasicrystalline precipitates with Penrose-like random-tiling were observed in the over-aged FCC matrix of a commercial 7N01 Al-Zn-Mg alloy, using high angle annular dark field scanning transmission electron microscopy. The evolution from C14-Laves phase to quasicrystalline clusters is illustrated, and five-fold symmetry can be found in both real and reciprocal spaces. Our findings reveal the possibility of quasicrystalline formation from Laves phase in a highly plastic metal matrix like Al and demonstrate the structural relationship between Laves phase and quasicrystals.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.7
DOI: 10.1016/J.MATCHAR.2023.112772
|
“Determination of the atomic width of an APB in ordered CoPt using quantified HAADF-STEM”. Akamine H, Van den Bos KHW, Gauquelin N, Farjami S, Van Aert S, Schryvers D, Nishida M, Journal of alloys and compounds 644, 570 (2015). http://doi.org/10.1016/j.jallcom.2015.04.205
Abstract: Anti-phase boundaries (APBs) in an ordered CoPt alloy are planar defects which disturb the ordered structure in their vicinity and decrease the magnetic properties. However, it has not yet been clarified to what extend the APBs disturb the ordering. In this study, high-resolution HAADF-STEM images are statistically analysed based on the image intensities estimated by the statistical parameter estimation theory. In the procedure, averaging intensities, fitting the intensity profiles to specific functions, and assessment based on a statistical test are performed. As a result, the APBs in the stable CoPt are found to be characterised by two atomic planes, and a contrast transition range as well as the centre of an inclined APB is determined. These results show that the APBs are quite sharp and therefore may have no notable effect on the net magnetic properties due to their small volume fraction. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 12
DOI: 10.1016/j.jallcom.2015.04.205
|
“Dynamic shear localization in Ti6Al4V”. Peirs J, Verleysen P, Tirry W, Rabet L, Schryvers D, Degrieck J, Procedia Engineering
T2 –, 11th International Conference on the Mechanical Behavior of Materials, (ICM), 2011, Como, ITALY (ICM11) , 1 (2011). http://doi.org/10.1016/j.proeng.2011.04.386
Abstract: The alloy Ti6Al4V is known to be prone to the formation of adiabatic shear bands when dynamically loaded in shear. This causes a catastrophic decrease of the load carrying capacity and is usually followed by fracture. Although, the main mechanism is recognized to be the competition between strain hardening and thermal softening, a detailed understanding of the role of microstructural plasticity mechanisms and macroscopic loading conditions does not exist yet. To study strain localization and shear fracture, different high strain rate shear tests have been carried out: compression of hat-shaped specimens, torsion of thin walled tubular specimens and in-plane shear tests. The value of the three techniques in studying shear localization is evaluated. Post-mortem analysis of the fracture surface and the materials' microstructure is performed with optical and electron microscopy. In all cases a ductile fracture is observed. SEM and TEM techniques are used to study the local microstructure and composition in the shear band and as such the driving mechanism for the ASB formation. (C) 2011 Published by Elsevier Ltd. Selection and/or peer-review under responsibility of ICM11
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 4
DOI: 10.1016/j.proeng.2011.04.386
|
“ELNES study of carbon K-edge spectra of plasma deposited carbon films”. Hamon A-L, Verbeeck J, Schryvers D, Benedikt J, van den Sanden RMCM, Journal of materials chemistry 14, 2030 (2004). http://doi.org/10.1039/b406468m
Abstract: Electron energy loss spectroscopy was used to investigate the bonding of plasma deposited carbon films. The experimental conditions include the use of a specific collection angle for which the shape of the spectra is free of the orientation dependency usually encountered in graphite due to its anisotropic structure. The first quantification process of the energy loss near-edge structure was performed by a standard fit of the collected spectrum, corrected for background and multiple scattering, with three Gaussian functions followed by a comparison with the graphite spectrum obtained under equivalent experimental conditions. In a second approach a fitting model directly incorporating the background subtraction and multiple scattering removal was applied. The final numerical results are interpreted in view of the deposition conditions of the films and the actual fitting procedure with the related choice of parameters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.626
Times cited: 61
DOI: 10.1039/b406468m
|
“Investigation of Ag, Ag2S and Ag(Br,I) small particles by HREM and AEM”. Oleshko V, Schryvers D, Gijbels R, Jacob W s.l., page 293 (1998).
Keywords: H3 Book chapter; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
|
“Structural and chemical effects on EELS L3,2 ionization edges in Ni-based intermetallic compounds”. Potapov PL, Kulkova SE, Schryvers D, Verbeeck J, Physical review : B : condensed matter and materials physics 64, 184110 (2001). http://doi.org/10.1103/PhysRevB.64.184110
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 44
DOI: 10.1103/PhysRevB.64.184110
|