“Soft chemical control of the crystal and magnetic structure of a layered mixed valent manganite oxide sulfide”. Blandy JN, Abakumov AM, Christensen KE, Hadermann J, Adamson P, Cassidy SJ, Ramos S, Free DG, Cohen H, Woodruff DN, Thompson AL, Clarke SJ;, APL materials 3, 041520 (2015). http://doi.org/10.1063/1.4918973
Abstract: Oxidative deintercalation of copper ions from the sulfide layers of the layered mixed-valent manganite oxide sulfide Sr2MnO2Cu1.5S2 results in control of the copper-vacancy modulated superstructure and the ordered arrangement of magnetic moments carried by the manganese ions. This soft chemistry enables control of the structures and properties of these complex materials which complement mixed-valent perovskite and perovskite-related transition metal oxides. (C) 2015 Author(s).
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.335
Times cited: 5
DOI: 10.1063/1.4918973
|
“A pseudo-tetragonal tungsten bronze superstructure: a combined solution of the crystal structure of K6.4(Nb,Ta)36.3O94 with advanced transmission electron microscopy and neutron diffraction”. Paria Sena R, Babaryk AA, Khainakov S, Garcia-Granda S, Slobodyanik NS, Van Tendeloo G, Abakumov AM, Hadermann J, Journal of the Chemical Society : Dalton transactions 45, 973 (2016). http://doi.org/10.1039/c5dt03479e
Abstract: The crystal structure of the K6.4Nb28.2Ta8.1O94 pseudo-tetragonal tungsten bronze-type oxide was determined using a combination of X-ray powder diffraction, neutron diffraction and transmission electron microscopy techniques, including electron diffraction, high angle annular dark field scanning transmission electron microscopy (HAADF-STEM), annular bright field STEM (ABF-STEM) and energy-dispersive X-ray compositional mapping (STEM-EDX). The compound crystallizes in the space group Pbam with unit cell parameters a = 37.468(9) A, b = 12.493(3) A, c = 3.95333(15) A. The structure consists of corner sharing (Nb,Ta)O6 octahedra forming trigonal, tetragonal and pentagonal tunnels. All tetragonal tunnels are occupied by K(+) ions, while 1/3 of the pentagonal tunnels are preferentially occupied by Nb(5+)/Ta(5+) and 2/3 are occupied by K(+) in a regular pattern. A fractional substitution of K(+) in the pentagonal tunnels by Nb(5+)/Ta(5+) is suggested by the analysis of the HAADF-STEM images. In contrast to similar structures, such as K2Nb8O21, also parts of the trigonal tunnels are fractionally occupied by K(+) cations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
Times cited: 6
DOI: 10.1039/c5dt03479e
|
“AVPO4F (A = Li, K): A 4 V Cathode Material for High-Power Rechargeable Batteries”. Fedotov SS, Khasanova NR, Samarin AS, Drozhzhin OA, Batuk D, Karakulina OM, Hadermann J, Abakumov AM, Antipov EV, Chemistry of materials 28, 411 (2016). http://doi.org/10.1021/acs.chemmater.5b04065
Abstract: A novel potassium-based fluoride-phosphate, KVPO4F, with a KTiOPO4 (KTP) type structure is synthesized and characterized. About 85% of potassium has been electrochemically extracted on oxidation producing a cathode material with attractive performance for Li-ion batteries. The material operates at the electrode potential near 4V vs Li/Li+ exhibiting a sloping voltage profile, extremely low polarization, small volume change of about 2% and excellent rate capability, maintaining more than 75% of the initial capacity at 40C discharge rate without significant fading.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 46
DOI: 10.1021/acs.chemmater.5b04065
|
“Visualization of O-O peroxo-like dimers in high-capacity layered oxides for Li-ion batteries”. McCalla E, Abakumov AM, Saubanere M, Foix D, Berg EJ, Rousse G, Doublet M-L, Gonbeau D, Novak P, Van Tendeloo G, Dominko R, Tarascon J-M, Science 350, 1516 (2015). http://doi.org/10.1126/science.aac8260
Abstract: Lithium-ion (Li-ion) batteries that rely on cationic redox reactions are the primary energy source for portable electronics. One pathway toward greater energy density is through the use of Li-rich layered oxides. The capacity of this class of materials (>270 milliampere hours per gram) has been shown to be nested in anionic redox reactions, which are thought to form peroxo-like species. However, the oxygen-oxygen (O-O) bonding pattern has not been observed in previous studies, nor has there been a satisfactory explanation for the irreversible changes that occur during first delithiation. By using Li2IrO3 as a model compound, we visualize the O-O dimers via transmission electron microscopy and neutron diffraction. Our findings establish the fundamental relation between the anionic redox process and the evolution of the O-O bonding in layered oxides.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 37.205
Times cited: 281
DOI: 10.1126/science.aac8260
|
“Switching between solid solution and two-phase regimes in the Li1-xFe1-yMnyPO4 cathode materials during lithium (de)insertion: combined PITT, in situ XRPD and electron diffraction tomography study”. Drozhzhin OA, Sumanov VD, Karakulina OM, Abakumov AM, Hadermann J, Baranov AN, Stevenson KJ, Antipov EV, Electrochimica acta 191, 149 (2016). http://doi.org/10.1016/j.electacta.2016.01.018
Abstract: The electrochemical properties and phase transformations during (de)insertion of Li+ in LiFePO4, LiFe0.9Mn0.1PO4 and LiFe0.5Mn0.5PO4 are studied by means of galvanostatic cycling, potential intermittent titration technique (PITT) and in situ X-ray powder diffraction. Different modes of switching between the solid solution and two-phase regimes are revealed which are influenced by the Mn content in Li1-xFe1-yMnyPO4. Additionally, an increase in electrochemical capacity with the Mn content is observed at high rates of galvanostatic cycling (10C, 20C), which is in good agreement with the numerically estimated contribution of the solid solution mechanism determined from PITT data. The observed asymmetric behavior of the phase transformations in Li1-xFe0.5Mn0.5PO4 during charge and discharge is discussed. For the first time, the crystal structures of electrochemically deintercalated Li1-xFe0.5Mn0.5PO4 with different Li content – LiFe0.5Mn0.5PO4, Li0.5Fe0.5Mn0.5PO4 and Li0.1Fe0.5Mn0.5PO4 – are refined, including the occupancy factors of the Li position. This refinement is done using electron diffraction tomography data. The crystallographic analyses of Li1-xFe0.5Mn0.5PO4 reveal that at x = 0.5 and 0.9 the structure retains the Pnma symmetry and the main motif of the pristine x = 0 structure without noticeable short range order effects.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.798
Times cited: 27
DOI: 10.1016/j.electacta.2016.01.018
|
“Charge-ordering transition in iron oxide Fe4O5 involving competing dimer and trimer formation”. Ovsyannikov SV, Bykov M, Bykova E, Kozlenko DP, Tsirlin AA, Karkin AE, Shchennikov VV, Kichanov SE, Gou H, Abakumov AM, Egoavil R, Verbeeck J, McCammon C, Dyadkin V, Chernyshov D, van Smaalen S, Dubrovinsky LS, Nature chemistry 8, 501 (2016). http://doi.org/10.1038/nchem.2478
Abstract: Phase transitions that occur in materials, driven, for instance, by changes in temperature or pressure, can dramatically change the materials' properties. Discovering new types of transitions and understanding their mechanisms is important not only from a fundamental perspective, but also for practical applications. Here we investigate a recently discovered Fe4O5 that adopts an orthorhombic CaFe3O5-type crystal structure that features linear chains of Fe ions. On cooling below approximately 150 K, Fe4O5 undergoes an unusual charge-ordering transition that involves competing dimeric and trimeric ordering within the chains of Fe ions. This transition is concurrent with a significant increase in electrical resistivity. Magnetic-susceptibility measurements and neutron diffraction establish the formation of a collinear antiferromagnetic order above room temperature and a spin canting at 85 K that gives rise to spontaneous magnetization. We discuss possible mechanisms of this transition and compare it with the trimeronic charge ordering observed in magnetite below the Verwey transition temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 25.87
Times cited: 51
DOI: 10.1038/nchem.2478
|
“Bi(3n+1)Ti7Fe(3n-3)O(9n+11) Homologous Series: Slicing Perovskite Structure with Planar Interfaces Containing Anatase-like Chains”. Batuk D, Tsirlin AA, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev A, Hadermann J, Abakumov AM, Inorganic chemistry 55, 1245 (2016). http://doi.org/10.1021/acs.inorgchem.5b02465
Abstract: The n = 3-6 members of a new perovskite-based homologous series Bi(3n+1)Ti7Fe(3n-3)O(9n+11) are reported. The crystal structure of the n = 3 Bi10Ti7Fe6O38 member is refined using a combination of X-ray and neutron powder diffraction data (a = 11.8511(2) A, b = 3.85076(4) A, c = 33.0722(6) A, S.G. Immm), unveiling the partially ordered distribution of Ti(4+) and Fe(3+) cations and indicating the presence of static random displacements of the Bi and O atoms. All Bi(3n+1)Ti7Fe(3n-3)O(9n+11) structures are composed of perovskite blocks separated by translational interfaces parallel to the (001)p perovskite planes. The thickness of the perovskite blocks increases with n, while the atomic arrangement at the interfaces remains the same. The interfaces comprise chains of double edge-sharing (Fe,Ti)O6 octahedra connected to the octahedra of the perovskite blocks by sharing edges and corners. This configuration shifts the adjacent perovskite blocks relative to each other over a vector (1/2)[110]p and creates S-shaped tunnels along the [010] direction. The tunnels accommodate double columns of the Bi(3+) cations, which stabilize the interfaces owing to the stereochemical activity of their lone electron pairs. The Bi(3n+1)Ti7Fe(3n-3)O(9n+11) structures can be formally considered either as intergrowths of perovskite modules and polysynthetically twinned modules of the Bi2Ti4O11 structure or as intergrowths of the 2D perovskite and 1D anatase fragments. Transmission electron microscopy (TEM) on Bi10Ti7Fe6O38 reveals that static atomic displacements of Bi and O inside the perovskite blocks are not completely random; they are cooperative, yet only short-range ordered. According to TEM, the interfaces can be laterally shifted with respect to each other over +/-1/3a, introducing an additional degree of disorder. Bi10Ti7Fe6O38 is paramagnetic in the 1.5-1000 K temperature range due to dilution of the magnetic Fe(3+) cations with nonmagnetic Ti(4+). The n = 3, 4 compounds demonstrate a high dielectric constant of 70-165 at room temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 3
DOI: 10.1021/acs.inorgchem.5b02465
|
“Synthesis, structure and electrochemical properties of LiNaCo0.5Fe0.5PO4F fluoride-phosphate”. Fedotov SS, Kuzovchikov SM, Khasanova NR, Drozhzhin OA, Filimonov DS, Karakulina OM, Hadermann J, Abakumov AM, Antipov EV, Journal of solid state chemistry 242, 70 (2016). http://doi.org/10.1016/j.jssc.2016.02.042
Abstract: LiNaCo 0.5 Fe 0.5 PO 4 F fluoride-phosphate was synthesized via conventional solid-state and novel freeze-drying routes. The crystal structure was refined based on neutron powder diffraction (NPD) data and validated by electron diffraction (ED) and high-resolution transmission electron microscopy (HRTEM). The alkali ions are ordered in LiNaCo 0.5 Fe 0.5 PO 4 F and the transition metals jointly occupy the same crystallographic sites. The oxidation state and oxygen coordination environment of the Fe atoms were verified by 57 Fe Mössbauer spectroscopy. Electrochemical tests of the LiNaCo 0.5 Fe 0.5 PO 4 F cathode material demonstrated a reversible activity of the Fe 3+ /Fe 2+ redox couple at the electrode potential near 3.4 V and minor activity of the Co 3+ /Co 2+ redox couple over 5 V vs Li/Li + . The material exhibits a good capacity retention in the 2.4÷4.6 V vs Li/Li + potential range with the delivered discharge capacity of more than 82% (theo.) regarding Fe 3+ /Fe 2+ .
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 1
DOI: 10.1016/j.jssc.2016.02.042
|
“Trapping of Oxygen Vacancies at Crystallographic Shear Planes in Acceptor-Doped Pb-Based Ferroelectrics”. Batuk D, Batuk M, Tsirlin AA, Hadermann J, Abakumov AM, Angewandte Chemie: international edition in English 54, 14787 (2015). http://doi.org/10.1002/anie.201507729
Abstract: The defect chemistry of the ferroelectric material PbTiO3 after doping with Fe(III) acceptor ions is reported. Using advanced transmission electron microscopy and powder X-ray and neutron diffraction, we demonstrate that even at concentrations as low as circa 1.7% (material composition approximately ABO2.95), the oxygen vacancies are trapped into extended planar defects, specifically crystallographic shear planes. We investigate the evolution of these defects upon doping and unravel their detailed atomic structure using the formalism of superspace crystallography, thus unveiling their role in nonstoichiometry in the Pb-based perovskites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 3
DOI: 10.1002/anie.201507729
|
“Direct Observation of Ferroelectric Domain Walls in LiNbO3: Wall-Meanders, Kinks, and Local Electric Charges”. Gonnissen J, Batuk D, Nataf GF, Jones L, Abakumov AM, Van Aert S, Schryvers D, Salje EKH, Advanced functional materials 26, 7599 (2016). http://doi.org/10.1002/adfm.201603489
Abstract: Direct observations of the ferroelectric domain boundaries in LiNbO3 are performed using high-resolution high-angle annular dark field scanning transmission electron microscopy imaging, revealing a very narrow width of the domain wall between the 180° domains. The domain walls demonstrate local side-way meandering, which results in inclinations even when the overall wall orientation follows the ferroelectric polarization. These local meanders contain kinks with “head-to-head” and “tail-to-tail” dipolar configurations and are therefore locally charged. The charged meanders are confined to a few cation layers along the polarization direction and are separated by longer stretches of straight domain walls.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 23
DOI: 10.1002/adfm.201603489
|
“Structural, electrochemical and magnetic properties of a novel KFeSO4F polymorph”. Lander L, Rousse G, Abakumov AM, Sougrati M, Van Tendeloo G, Tarascon J-M, Journal of materials chemistry A : materials for energy and sustainability 3, 19754 (2015). http://doi.org/10.1039/c5ta05548b
Abstract: In the quest for sustainable and low-cost positive electrode materials for Li-ion batteries, we discovered, as reported herein, a new low temperature polymorph of KFeSO4F. Contrary to the high temperature phase crystallizing in a KTiOPO4-like structure, this new phase adopts a complex layer-like structure built on FeO4F2 octahedra and SO4 tetrahedra, with potassium cations located in between the layers, as solved using neutron and synchrotron diffraction experiments coupled with electron diffraction. The detailed analysis of the structure reveals an alternation of edge-and corner-shared FeO4F2 octahedra leading to a large monoclinic cell of 1771.774(7) angstrom(3). The potassium atoms are mobile within the structure as deduced by ionic conductivity measurements and confirmed by the bond valence energy landscape approach thus enabling a partial electrochemical removal of K+ and uptake of Li+ at an average potential of 3.7 V vs. Li+/Li-0. Finally, neutron diffraction experiments coupled with SQUID measurements reveal a long range antiferromagnetic ordering of the Fe2+ magnetic moments below 22 K with a possible magnetoelectric behavior.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 11
DOI: 10.1039/c5ta05548b
|
“Water electrolysis on La1-xSrxCoO3-\delta perovskite electrocatalysts”. Mefford JT, Rong X, Abakumov AM, Hardin WG, Dai S, Kolpak AM, Johnston KP, Stevenson KJ, Nature communications 7, 11053 (2016). http://doi.org/10.1038/ncomms11053
Abstract: Perovskite oxides are attractive candidates as catalysts for the electrolysis of water in alkaline energy storage and conversion systems. However, the rational design of active catalysts has been hampered by the lack of understanding of the mechanism of water electrolysis on perovskite surfaces. Key parameters that have been overlooked include the role of oxygen vacancies, B-O bond covalency, and redox activity of lattice oxygen species. Here we present a series of cobaltite perovskites where the covalency of the Co-O bond and the concentration of oxygen vacancies are controlled through Sr2+ substitution into La1 – xSrxCoO3 – delta. We attempt to rationalize the high activities of La1 – xSrxCoO3 – delta through the electronic structure and participation of lattice oxygen in the mechanism of water electrolysis as revealed through ab initio modelling. Using this approach, we report a material, SrCoO2.7, with a high, room temperature-specific activity and mass activity towards alkaline water electrolysis.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 278
DOI: 10.1038/ncomms11053
|
“Strong oxygen participation in the redox governing the structural and electrochemical properties of Na-rich layered oxide Na2IrO3”. Perez AJ, Batuk D, Saubanère M, Rousse G, Foix D, Mc Calla E, J Berg E, Dugas R, van den Bos K H W, Doublet M-L, Gonbeau D, Abakumov AM, Van Tendeloo G, Tarascon J-M, Chemistry of materials 28, 8278 (2016). http://doi.org/10.1021/acs.chemmater.6b03338
Abstract: The recent revival of the Na-ion battery concept has prompted intense activities in the search for new Na-based layered oxide positive electrodes. The largest capacity to date was obtained for a Na-deficient layered oxide that relies on cationic redox processes only. To go beyond this limit, we decided to chemically manipulate these Na-based layered compounds in a way to trigger the participation of the anionic network. We herein report the electrochemical properties of a Na-rich phase Na2IrO3, which can reversibly cycle 1.5 Na+ per formula unit while not suffering from oxygen release nor cationic migrations. Such large capacities, as deduced by complementary XPS, X-ray/neutron diffraction and transmission electron microscopy measurements, arise from cumulative cationic and anionic redox processes occurring simultaneously at potentials as low as 3.0 V. The inability to remove more than 1.5 Na+ is rooted in the formation of an O1-type phase having highly stabilized Na sites as confirmed by DFT calculations, which could rationalize as well the competing metal/oxygen redox processes in Na2IrO3. This work will help to define the most fertile directions in the search for novel high energy Na-rich materials based on more sustainable elements than Ir.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 45
DOI: 10.1021/acs.chemmater.6b03338
|
“Evaluation of Ce-doped Pr2CuO4for potential application as a cathode material for solid oxide fuel cells”. Kolchina L M, Lyskov NV, Kuznetsov AN, Kazakov SM, Galin MZ, Meledin A, Abakumov AM, Bredikhin SI, Mazo GN, Antipov EV, RSC advances 6, 101029 (2016). http://doi.org/10.1039/C6RA21970E
Abstract: Pr2−xCexCuO4 (x = 0.05; 0.1; 0.15) samples were synthesized and systematically characterized towards application as a cathode material for solid oxide fuel cells (SOFCs). High-temperature electrical conductivity, thermal expansion, and electrocatalytic activity in the oxygen reduction reaction (ORR) were examined. The electrical conductivity of Pr2−xCexCuO4 oxides demonstrates semiconducting behavior up to 900 °C. Small Ce-doping (2.5 at%) allows an increase in electrical conductivity from 100 to 130 S cm−1 in air at 500–800 °C. DFT calculations revealed that the density of states directly below the Fermi level, comprised mainly of Cu 3d and O 2p states, is significantly affected by atoms in rare earth positions, which might give an indication of a correlation between calculated electronic structures and measured conducting properties. Ce-doping in Pr2−xCexCuO4 slightly increases TEC from 11.9 × 10−6 K−1 for x = 0 to 14.2 × 10−6 K−1 for x = 0.15. Substitution of 2.5% of Pr atoms in Pr2CuO4 by Ce is effective to enhance the electrochemical performance of the material as a SOFC cathode in the ORR (ASR of Pr1.95Ce0.05CuO4 electrode applied on Ce0.9Gd0.1O1.95 electrolyte is 0.39 Ω cm2 at 750 °C in air). The peak power density achieved for the electrolyte-supported fuel cell with the Pr1.95Ce0.05CuO4 cathode is 150 mW cm−2 at 800 °C
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 7
DOI: 10.1039/C6RA21970E
|
“Layered-to-Tunnel Structure Transformation and Oxygen Redox Chemistry in LiRhO2upon Li Extraction and Insertion”. Mikhailova D, Karakulina OM, Batuk D, Hadermann J, Abakumov AM, Herklotz M, Tsirlin AA, Oswald S, Giebeler L, Schmidt M, Eckert J, Knapp M, Ehrenberg H, Inorganic chemistry 55, 7079 (2016). http://doi.org/10.1021/acs.inorgchem.6b01008
Abstract: Layered Li(M,Li)O2 (where M is a transition metal) ordered rock-salt-type structures are used in advanced metal-ion batteries as one of the best hosts for the reversible intercalation of Li ions. Besides the conventional redox reaction involving oxidation/reduction of the M cation upon Li extraction/insertion, creating oxygen-located holes because of the partial oxygen oxidation increases capacity while maintaining the oxidized oxygen species in the lattice through high covalency of the M–O bonding. Typical degradation mechanism of the Li(M,Li)O2 electrodes involves partially irreversible M cation migration toward the Li positions, resulting in gradual capacity/voltage fade. Here, using LiRhO2 as a model system (isostructural and isoelectronic to LiCoO2), for the first time, we demonstrate an intimate coupling between the oxygen redox and M cation migration. A formation of the oxidized oxygen species upon electrochemical Li extraction coincides with transformation of the layered Li1–xRhO2 structure into the γ-MnO2-type rutile–ramsdellite intergrowth LiyRh3O6 structure with rutile-like [1 × 1] channels along with bigger ramsdellite-like [2 × 1] tunnels through massive and concerted Rh migration toward the empty positions in the Li layers. The oxidized oxygen dimers with the O–O distances as short as 2.26 Å are stabilized in this structure via the local Rh–O configuration reminiscent to that in the μ-peroxo-μ-hydroxo Rh complexes. The LiyRh3O6 structure is remarkably stable upon electrochemical cycling illustrating that proper structural implementation of the oxidized oxygen species can open a pathway toward deliberate employment of the anion redox chemistry in high-capacity/high-voltage positive electrodes for metal-ion batteries. Upon chemical or electrochemical oxidation, layered LiRhO2 shows a unique structural transformation that involves both cation migration and oxidation of oxygen resulting in a stable tunnel-like rutile−ramsdellite intergrowth LiyRh3O6 structure. This structure demonstrates excellent performance with the steady and reversible capacity of ∼200 mAh/g. The stability of LiyRh3O6 is rooted in the accommodation of partially oxidized oxygen species through the formation of short O−O distances that are compatible with the connectivity of RhO6 octahedra.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 12
DOI: 10.1021/acs.inorgchem.6b01008
|
“Antisite Disorder and Bond Valence Compensation in Li2FePO4F Cathode for Li-Ion Batteries”. Karakulina OM, Khasanova NR, Drozhzhin OA, Tsirlin AA, Hadermann J, Antipov EV, Abakumov AM, Chemistry Of Materials 28, 7578 (2016). http://doi.org/10.1021/acs.chemmater.6b03746
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 10
DOI: 10.1021/acs.chemmater.6b03746
|
“Visible light activation of room temperature NO2 gas sensors based on ZnO, SnO2 and In2O3 sensitized with CdSe quantum dots”. Chizhov AS, Rumyantseva MN, Vasiliev RB, Filatova DG, Drozdov KA, Krylov IV, Marchevsky AV, Karakulina OM, Abakumov AM, Gaskov AM, Thin solid films : an international journal on the science and technology of thin and thick films 618, 253 (2016). http://doi.org/10.1016/j.tsf.2016.09.029
Abstract: This work reports the analysis of visible light activation of room temperature NO2 gas sensitivity of metal oxide semiconductors (MOS): blank and CdSe quantum dots (QDs) sensitized nanocrystallinematrixes ZnO, SnO2 and In2O3. Nanocrystalline metal oxides (MOx) ZnO, SnO2, In2O3 were synthesized by the precipitation method. Colloidal CdSe QDs were obtained by high temperature colloidal synthesis. Sensitization was effectuated by direct adsorption of CdSe QDs stabilized with oleic acid on MOx surface. The role of illumination consists in generation of electrons, which can be transferred into MOx conduction band, and holes that can recombine with the electrons previously trapped by the chemisorbed acceptor species and thus activate desorption of analyte molecules. Under green light illumination for blank SnO2 and In2O3 matrixes the indirect consequential mechanism for the generation of holes is proposed. Anothermechanismis realized in the presence of CdSe QDs. In this case the electron-hole pair is generated in the CdSe quantum dot. Sensor measurements demonstrated that synthesizedmaterials can be used for NO2 detection under visible (green) light illumination at room temperature without any thermal heating.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.879
Times cited: 19
DOI: 10.1016/j.tsf.2016.09.029
|
“{110}-Layered B-cation ordering in the anion-deficient perovskite Pb2.4Ba2.6Fe2Sc2TiO13 with the crystallographic shear structure”. Tyablikov OA, Batuk D, Tsirlin AA, Batuk M, Verchenko VY, Filimonov DS, Pokholok KV, Sheptyakov DV, Rozova MG, Hadermann J, Antipov EV, Abakumov AM;, Journal of the Chemical Society : Dalton transactions 44, 10753 (2015). http://doi.org/10.1039/c4dt03867c
Abstract: A novel anion-deficient perovskite-based compound, Pb2.4Ba2.6Fe2Sc2TiO13, was synthesized via the citrate-based route. This compound is an n = 5 member of the A(n)B(n)O(3n-2) homologous series with unit-cell parameters related to the perovskite subcell a(p) approximate to 4.0 angstrom as a(p)root 2 x a(p) x 5a(p)root 2. The crystal structure of Pb2.4Ba2.6Fe2Sc2TiO13 consists of quasi-2D perovskite blocks with a thickness of three octahedral layers separated by the 1/2[110]((1) over bar 01)(p) crystallographic shear (CS) planes, which are parallel to the {110} plane of the perovskite subcell. The CS planes transform the corner-sharing octahedra into chains of edge-sharing distorted tetragonal pyramids. Using a combination of neutron powder diffraction, Fe-57 Mossbauer spectroscopy and atomic resolution electron energy-loss spectroscopy we demonstrate that the B-cations in Pb2.4Ba2.6Fe2Sc2TiO13 are ordered along the {110} perovskite layers with Fe3+ in distorted tetragonal pyramids along the CS planes, Ti4+ preferentially in the central octahedra of the perovskite blocks and Sc3+ in the outer octahedra of the perovskite blocks. Magnetic susceptibility and Mossbauer spectroscopy indicate a broadened magnetic transition around T-N similar to 45 K and the onset of local magnetic fields at low temperatures. The magnetic order is probably reminiscent of that in other A(n)B(n)O(3n-2) homologues, where G-type AFM order within the perovskite blocks has been observed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
Times cited: 1
DOI: 10.1039/c4dt03867c
|
“Advanced electron microscopy and its possibilities to solve complex structures: application to transition metal oxides”. Van Tendeloo G, Hadermann J, Abakumov AM, Antipov EV, Journal of materials chemistry 19, 2660 (2009). http://doi.org/10.1039/b817914j
Abstract: Design and optimization of materials properties can only be performed through a thorough knowledge of the structure of the compound. In this feature article we illustrate the possibilities of advanced electron microscopy in materials science and solid state chemistry. The different techniques are briefly discussed and several examples are given where the structures of complex oxides, often with a modulated structure, have been solved using electron microscopy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 9
DOI: 10.1039/b817914j
|
“An oxysulfate Fe2O(SO4)2 electrode for sustainable Li-based batteries”. Sun M, Rousse G, Abakumov AM, Van Tendeloo G, Sougrati M-T, Courty M, Doublet M-L, Tarascon J-M, Journal of the American Chemical Society 136, 12658 (2014). http://doi.org/10.1021/ja505268y
Abstract: High-performing Fe-based electrodes for Li-based batteries are eagerly pursued because of the abundance and environmental benignity of iron, with especially great interest in polyanionic compounds because of their flexibility in tuning the Fe3+/Fe2+ redox potential. We report herein the synthesis and structure of a new Fe-based oxysulfate phase, Fe2O(SO4)(2), made at low temperature from abundant elements, which electrochemically reacts with nearly 1.6 Li atoms at an average voltage of 3.0 V versus Li+/Li, leading to a sustained reversible capacity of similar to 125 mAh/g. The Li insertiondeinsertion process, the first ever reported in any oxysulfate, entails complex phase transformations associated with the position of iron within the FeO6 octahedra. This finding opens a new path worth exploring in the quest for new positive electrode materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 11
DOI: 10.1021/ja505268y
|
“Anion ordering in fluorinated La2CuO4”. Abakumov AM, Hadermann J, Van Tendeloo G, Shpanchenko RV, Oleinikov PN, Antipov EV, Journal of solid state chemistry 142, 311 (1999). http://doi.org/10.1006/jssc.1998.8064
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 20
DOI: 10.1006/jssc.1998.8064
|
“Anion ordering in fluorinated La2CuO4”. Hadermann J, Abakumov AM, Van Tendeloo G, Shpanchenko RV, Oleinikov PN, Antipov EV s.l., page 133 (1999).
Keywords: H1 Book chapter; Electron microscopy for materials research (EMAT)
|
“Anion rearrangements in fluorinated Nd2CuO3.5”. Corbel G, Attfield JP, Hadermann J, Abakumov AM, Alekseeva AM, Rozova MG, Antipov EV, Chemistry of materials 15, 189 (2003). http://doi.org/10.1021/cm021102m
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 9
DOI: 10.1021/cm021102m
|
“Antiferroelectric (Pb,Bi)1-xFe1+xO3-y perovskites modulated by crystallographic shear planes”. Abakumov AM, Batuk D, Hadermann J, Rozova MG, Sheptyakov DV, Tsirlin AA, Niermann D, Waschowski F, Hemberger J, Van Tendeloo G, Antipov EV, Chemistry of materials 23, 255 (2011). http://doi.org/10.1021/cm102907h
Abstract: We demonstrate for the first time a possibility to vary the anion content in perovskites over a wide range through a long-range-ordered arrangement of crystallographic shear (CS) planes. Anion-deficient perovskites (Pb,Bi)1−xFe1+xO3−y with incommensurately modulated structures were prepared as single phases in the compositional range from Pb0.857Bi0.094Fe1.049O2.572 to Pb0.409Bi0.567Fe1.025O2.796. Using a combination of electron diffraction and high-resolution scanning transmission electron microscopy, we constructed a superspace model describing a periodic arrangement of the CS planes. The model was verified by refinement of the Pb0.64Bi0.32Fe1.04O2.675 crystal structure from neutron powder diffraction data ((3 + 1)D S.G. X2/m(α0γ), X = [1/2,1/2,1/2,1/2], a = 3.9082(1) Å, b = 3.90333(8) Å, c = 4.0900(1) Å, β = 91.936(2)°, q = 0.05013(4)a* + 0.09170(3)c* at T = 700 K, RP = 0.036, RwP = 0.048). The (Pb,Bi)1−xFe1+xO3−y structures consist of perovskite blocks separated by CS planes confined to nearly the (509)p perovskite plane. Along the CS planes, the perovskite blocks are shifted with respect to each other over the 1/2[110]p vector that transforms the corner-sharing connectivity of the FeO6 octahedra in the perovskite framework to an edge-sharing connectivity of the FeO5 pyramids at the CS plane, thus reducing the oxygen content. Variation of the chemical composition in the (Pb,Bi)1−xFe1+xO3−y series occurs mainly because of a changing thickness of the perovskite block between the interfaces, that can be expressed through the components of the q vector as Pb6γ+2αBi1−7γ−αFe1+γ−αO3−3γ−α. The Pb, Bi, and Fe atoms are subjected to strong displacements occurring in antiparallel directions on both sides of the perovskite blocks, resulting in an antiferroelectric-type structure. This is corroborated by the temperature-, frequency-, and field-dependent complex permittivity measurements. Pb0.64Bi0.32Fe1.04O2.675 demonstrates a remarkably high resistivity >0.1 T Ω cm at room temperature and orders antiferromagnetically below TN = 608(10) K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 29
DOI: 10.1021/cm102907h
|
“Article Structure and magnetic properties of BiFe0.75Mn0.25O3 perovskite prepared at ambient and high pressure”. Belik AA, Abakumov AM, Tsirlin AA, Hadermann J, Kim J, Van Tendeloo G, Takayama-Muromachi E, Chemistry of materials 23, 4505 (2011). http://doi.org/10.1021/cm201774y
Abstract: Solid solutions of BiFe1xMnxO3 (0.0 ≤ x ≤ 0.4) were prepared at ambient pressure and at 6 GPa. The ambient-pressure (AP) phases crystallize in space group R3c similarly to BiFeO3. The high-pressure (HP) phases crystallize in space group R3c for x = 0.05 and in space group Pnma for 0.15 ≤ x ≤ 0.4. The structure of HP-BiFe0.75Mn0.25O3 was investigated using synchrotron X-ray powder diffraction, electron diffraction, and transmission electron microscopy. HP-BiFe0.75Mn0.25O3 has a PbZrO3-related √2ap × 4ap × 2√2ap (ap is the parameter of the cubic perovskite subcell) superstructure with a = 5.60125(9) Å, b = 15.6610(2) Å, and c = 11.2515(2) Å similar to that of Bi0.82La0.18FeO3. A remarkable feature of this structure is the unconventional octahedral tilt system, with the primary ab0a tilt superimposed on pairwise clockwise and counterclockwise rotations around the b-axis according to the oioi sequence (o stands for out-of-phase tilt, and i stands for in-phase tilt). The (FeMn)O6 octahedra are distorted, with one longer metaloxygen bond (2.222.23 Å) that can be attributed to a compensation for covalent BiO bonding. Such bonding results in the localization of the lone electron pair on Bi3+ cations, as confirmed by electron localization function analysis. The relationship between HP-BiFe0.75Mn0.25O3 and antiferroelectric structures of PbZrO3 and NaNbO3 is discussed. On heating in air, HP-BiFe0.75Mn0.25O3 irreversibly transforms to AP-BiFe0.75Mn0.25O3 starting from about 600 K. Both AP and HP phases undergo an antiferromagnetic ordering at TN ≈ 485 and 520 K, respectively, and develop a weak net magnetic moment at low temperatures. Additionally, ceramic samples of AP-BiFe0.75Mn0.25O3 show a peculiar phenomenon of magnetization reversal.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 57
DOI: 10.1021/cm201774y
|
“Atomic structure of defects in anion-deficient perovskite-based ferrites with a crystallographic shear structure”. Batuk M, Turner S, Abakumov AM, Batuk D, Hadermann J, Van Tendeloo G, Inorganic chemistry 53, 2171 (2014). http://doi.org/10.1021/ic4028404
Abstract: Crystallographic shear (CS) planes provide a new structure-generation mechanism in the anion-deficient perovskites containing lone-pair cations. Pb2Sr2Bi2Fe6O16, a new n = 6 representative of the AnBnO3n2 homologous series of the perovskite-based ferrites with the CS structure, has been synthesized using the solid-state technique. The structure is built of perovskite blocks with a thickness of four FeO6 octahedra spaced by double columns of FeO5 edge-sharing distorted tetragonal pyramids, forming 1/2[110](101)p CS planes (space group Pnma, a = 5.6690(2) Å, b = 3.9108(1) Å, c = 32.643(1) Å). Pb2Sr2Bi2Fe6O16 features a wealth of microstructural phenomena caused by the flexibility of the CS planes due to the variable ratio and length of the constituting fragments with {101}p and {001}p orientation. This leads to the formation of waves, hairpins, Γ-shaped defects, and inclusions of the hitherto unknown layered anion-deficient perovskites Bi2(Sr,Pb)Fe3O8.5 and Bi3(Sr,Pb)Fe4O11.5. Using a combination of diffraction, imaging, and spectroscopic transmission electron microscopy techniques this complex microstructure was fully characterized, including direct determination of positions, chemical composition, and coordination number of individual atomic species. The complex defect structure makes these perovskites particularly similar to the CS structures in ReO3-type oxides. The flexibility of the CS planes appears to be a specific feature of the Sr-based system, related to the geometric match between the SrO perovskite layers and the {100}p segments of the CS planes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 6
DOI: 10.1021/ic4028404
|
“Cation ordering and flexibility of the BO42- tetrahedra in incommensurately modulated CaEu2(BO4)4 (B = Mo, W) scheelites”. Abakumov AM, Morozov VA, Tsirlin AA, Verbeeck J, Hadermann J, Inorganic chemistry 53, 9407 (2014). http://doi.org/10.1021/ic5015412
Abstract: The factors mediating cation ordering in the scheelite-based molybdates and tungstates are discussed on the basis of the incommensurately modulated crystal structures of the CaEu2(BO4)(4) (B = Mo, W) red phosphors solved from high-resolution synchrotron powder X-ray diffraction data. Monoclinic CaEu2(WO4)(4) adopts a (3 + 1)-dimensionally modulated structure [superspace group I2/b(alpha beta 0)00, a = 5.238 73(1)A, b = 5.266 35(1) A, c = 11.463 19(9) A, gamma = 91.1511(2)degrees, q = 0.56153(6)a* + 0.7708(9)b*, R-F = 0.050, R-p = 0.069], whereas tetragonal CaEu2(MoO4)(4) is (3 + 2)-dimensionally modulated [superspace group I4(1)/ a(alpha beta 0)00(-beta alpha 0)00, a = 5.238 672(7) A, c = 11.548 43(2) A, q(1) = 035331(8)a* + 0.82068(9)b*, q(2) = -0.82068(9)a* + 0.55331(8)b*, R-F = 0.061, R-p = 0.082]. In both cases the modulation arises from the ordering of the Ca/Eu cations and the cation vacancies at the A-sublattice of the parent scheelite ABO(4) structure. The cation ordering is incomplete and better described with harmonic rather than with steplike occupational modulation functions. The structures respond to the variation of the effective charge and cation size at the A-position through the flexible geometry of the MoO42- and WO42- tetrahedra demonstrating an alternation of stretching the B-O bond lengths and bending the O-B-O bond angles. The tendency towards A-site cation ordering in scheelites is rationalized using the difference in ionic radii and concentration of the A-site vacancies as parameters and presented in the form of a structure map.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 48
DOI: 10.1021/ic5015412
|
“Cationic clathrate of type-III Ge172-xPxTey (y\approx21,5, x\approx2y) : synthesis, crystal structure and thermoelectric properties”. Kirsanova MA, Mori T, Maruyama S, Abakumov AM, Van Tendeloo G, Olenev A, Shevelkov AV, Inorganic chemistry 52, 8272 (2013). http://doi.org/10.1021/ic401203r
Abstract: A first germanium-based cationic clathrate of type-III, Ge129.3P42.7Te21.53, was synthesized and structurally characterized (space group P42/mnm, a = 19.948(3) Å, c = 10.440(2) Å, Z = 1). In its crystal structure, germanium and phosphorus atoms form three types of polyhedral cages centered with Te atoms. The polyhedra share pentagonal and hexagonal faces to form a 3D framework. Despite the complexity of the crystal structure, the Ge129.3P42.7Te21.53 composition corresponds to the Zintl counting scheme with a good accuracy. Ge129.3P42.7Te21.53 demonstrates semiconducting/insulating behavior of electric resistivity, high positive Seebeck coefficient (500 μV K1 at 300 K), and low thermal conductivity (<0.92 W m1 K1) within the measured temperature range.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 3
DOI: 10.1021/ic401203r
|
“Chemistry and structure of anion-deficient perovskites with translational interfaces”. Abakumov AM, Hadermann J, Van Tendeloo G, Antipov EV, Journal of the American Ceramic Society 91, 1807 (2008). http://doi.org/10.1111/j.1551-2916.2008.02351.x
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.841
Times cited: 39
DOI: 10.1111/j.1551-2916.2008.02351.x
|
“Comment on ALaMn2O6-y (A = K, Rb): novel ferromagnetic manganites exhibiting negative giant magnetoresistance”. Hadermann J, Abakumov AM, Van Rompaey S, Mankevich AS, Korsakov IE, Chemistry of materials 21, 2000 (2009). http://doi.org/10.1021/cm900298a
Keywords: Editorial; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 4
DOI: 10.1021/cm900298a
|