“The corrosion process of sterling silver exposed to a Na2S solution: monitoring and characterizing the complex surface evolution using a multi-analytical approach”. Schalm O, Crabbé, A, Storme P, Wiesinger R, Gambirasi A, Grieten E, Tack P, Bauters S, Kleber C, Favaro M, Schryvers D, Vincze L, Terryn H, Patelli A, Applied Physics A-Materials Science &, Processing 122, 903 (2016). http://doi.org/10.1007/s00339-016-0436-6
Abstract: Many historical ‘silver’ objects are composed of sterling silver, a silver alloy containing small amounts of copper. Besides the dramatic impact of copper on the corrosion process, the chemical composition of the corrosion layer evolves continuously. The evolution of the surface during the exposure to a Na2S solution was monitored by means of visual observation at macroscopic level, chemical analysis at microscopic level and analysis at the nanoscopic level. The corrosion process starts with the preferential oxidation of copper, forming mixtures of oxides and sulphides while voids are being created beneath the corrosion layer. Only at a later stage, the silver below the corrosion layer is consumed. This results in the formation of jalpaite and at a later stage of acanthite. The acanthite is found inside the corrosion layer at the boundaries of jalpaite grains and as individual grains between the jalpaite grains but also as a thin film on top of the corrosion layer. The corrosion process could be described as a sequence of 5 subsequent surface states with transitions between these states.
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 1.455
Times cited: 9
DOI: 10.1007/s00339-016-0436-6
|
“Melamine–Formaldehyde Microcapsules: Micro- and Nanostructural Characterization with Electron Microscopy”. Heidari H, Rivero G, Idrissi H, Ramachandran D, Cakir S, Egoavil R, Kurttepeli M, Crabbé, AC, Hauffman T, Terryn H, Du Prez F, Schryvers D, Microscopy and microanalysis 22, 1222 (2016). http://doi.org/10.1017/S1431927616012484
Abstract: A systematic study has been carried out to compare the surface morphology, shell thickness, mechanical properties, and binding behavior of melamine–formaldehyde microcapsules of 5–30 μm diameter size with various amounts of core content by using scanning and transmission electron microscopy including electron tomography, in situ nanomechanical tensile testing, and electron energy-loss spectroscopy. It is found that porosities are present on the outside surface of the capsule shell, but not on the inner surface of the shell. Nanomechanical tensile tests on the capsule shells reveal that Young’s modulus of the shell material is higher than that of bulk melamine–formaldehyde and that the shells exhibit a larger fracture strain compared with the bulk. Core-loss elemental analysis of microcapsules embedded in epoxy indicates that during the curing process, the microcapsule-matrix interface remains uniform and the epoxy matrix penetrates into the surface micro-porosities of the capsule shells.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 2
DOI: 10.1017/S1431927616012484
|
“Quantitative measurement for the microstructural parameters of nano-precipitates in Al-Mg-Si-Cu alloys”. Li K, Idrissi H, Sha G, Song M, Lu J, Shi H, Wang W, Ringer SP, Du Y, Schryvers D, Materials characterization 118, 352 (2016). http://doi.org/10.1016/j.matchar.2016.06.007
Abstract: Size, number density and volume fraction of nano-precipitates are important microstructural parameters controlling the strengthening of materials. In this work a widely accessible, convenient, moderately time efficient method with acceptable accuracy and precision has been provided for measurement of volume fraction of nano-precipitates in crystalline materials. The method is based on the traditional but highly accurate technique of measuring foil thickness via convergent beam electron diffraction. A new equation is proposed and verified with the aid of 3-dimensional atom probe (3DAP) analysis, to compensate for the additional error resulted from the hardly distinguishable contrast of too short incomplete precipitates cut by the foil surface. The method can be performed on a regular foil specimen with a modem LaB6 or field-emission-gun transmission electron microscope. Precisions around +/- 16% have been obtained for precipitate volume fractions of needle-like beta ''/C and Q precipitates in an aged Al-Mg-Si-Cu alloy. The measured number density is dose to that directly obtained using 3DAP analysis by a misfit of 45%, and the estimated precision for number density measurement is about +/- 11%. The limitations of the method are also discussed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 9
DOI: 10.1016/j.matchar.2016.06.007
|
“Towards biolubricant compatible vegetable oils by pore mouth hydrogenation with shape-selective Pt/ZSM-5 catalysts”. Van Aelst J, Philippaerts A, Bartholomeeusen E, Fayad E, Thibault-Starzyk F, Lu J, Schryvers D, Ooms R, Verboekend D, Jacobs P, Sels B, Catalysis science &, technology 6, 2820 (2016). http://doi.org/10.1039/C6CY00498A
Abstract: Pt/ZSM-5 catalysts with various crystal sizes were prepared via competitive ion-exchange, followed by a slow activation procedure. Even when using very large ZSM-5 crystals, highly dispersed Pt nano-clusters were contained within the zeolite crystal's voids, as ascertained by 2D pressure-jump IR spectroscopy of adsorbed CO and focussed ion-beam transmission electron microscopy. The shape-selective properties of the Pt/ZSM-5 catalysts were evaluated in the partial hydrogenation of soybean oil. Unique hydrogenation selectivities were observed, as the fatty acids located at the central position of the triacylglycerol (TAG) molecules were preferentially hydrogenated. The resulting oil has therefore high levels of intermediately melting TAGs, which are compatible with biolubricants due to their improved oxidative stability and still appropriate low-temperature fluidity. The TAG distribution in the partially hydrogenated soybean oil samples was independent from the zeolite crystal size, while the hydrogenation activity linearly increases with the crystal's external surface area. This trend was confirmed with a Pt loaded mesoporous ZSM-5 zeolite, obtained via a mild alkaline treatment. These observations imply and confirm a genuine pore mouth catalysis mechanism, in which only one fatty acid chain of the TAG is able to enter the micropores of ZSM-5, where the double bonds are hydrogenated by the crystal encapsulated Pt-clusters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.773
Times cited: 5
DOI: 10.1039/C6CY00498A
|
“Electronically decoupled stacking fault tetrahedra embedded in Au(111) films”. Schouteden K, Amin-Ahmadi B, Li Z, Muzychenko D, Schryvers D, Van Haesendonck C, Nature communications 7, 14001 (2016). http://doi.org/10.1038/ncomms14001
Abstract: Stacking faults are known as defective structures in crystalline materials that typically lower the structural quality of the material. Here, we show that a particular type of defects, i.e., stacking fault tetrahedra (SFTs), exhibits quantized, particle-in-a-box electronic behaviour, revealing a potential synthetic route to decoupled nanoparticles in metal films. We report on the electronic properties of SFTs that exist in Au(111) films, as evidenced by scanning tunnelling microscopy and confirmed by transmission electron microscopy. We find that the SFTs reveal a remarkable decoupling from their metal surroundings, leading to pronounced energy level quantization effects within the SFTs. The electronic behaviour of the SFTs can be described well by the particle-in-a-box model. Our findings demonstrate that controlled preparation of SFTs may offer an alternative way to achieve well decoupled nanoparticles of high crystalline quality in metal thin films without the need of thin insulating layers.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 7
DOI: 10.1038/ncomms14001
|
“Electron microscopy study of twinning in the Ni5Al3 bainitic phase”. Schryvers D, Ma Y, Toth L, Tanner L, TMS (1994)
Abstract: This contribution describes conventional and high resolution electron microscopy results on the different twinning arrangements in NisAl3 precipitates grown inside the B2 austenite phase. Short annealings introduce self-accommodating three-pointed star shaped precipitates consisting of twin related parts of different variants of the NisAl3 structure. Longer annealings result in plates growing separately from these wings and developing microtwinning in order to accommodate stress built-up at the interfaces with the surrounding matrix.
Keywords: A3 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
|
“Electron microscopy study of twin sequences and branching in NissAl34 3R martensite”. Schryvers D, Van Landuyt J, ICOMAT (1992)
Abstract: Microtwin sequences in Ni66Al34 martensite plates of different size were investigated by electron microscopy. Although mostly irregular sequences were observed an average twin width w can be determined which increases with twin length L following the expected relation w ~ sqrt(L). High resolution electron microscopy was used to study the twin branching close to the plate boundaries and an atomic model for the branching of a microtwin and the changes in twin thickness is suggested
Keywords: A3 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
|
“Firsto order phase transformation in the Ni-Al system”. Tanner LE, Shapiro SM, Krumhansl JA, Schryvers D, Noda Y, Yamada Y, Barsch GR, Gooding R, Moss SC, Metallurgy and Ceramics (1992)
Abstract: First-order displacive phase transformations in alloys and compounds are of high technological importance. We have studied this class of phase transformation in the high-temperature-stable Ni-Al f32(B2) phase as a function of composition, temperature, and stress using transmission electron microscopy and neutron scattering. The results show in detail the direct relationship between the unusually low energies of the transformation-related phonon modes and the development of pre-transformation microstructures (strain-embryos, etc.) via anharmonic coupling processes that ultimately lead to the nucleation and growth of the low-temperature martensitic phases. With these results, it is now possible to develop effective models for nonclassical heterogeneous nucleation of martensite transformations in bulk materials. This tills a critical gap and sets the stage for us to proceed in developing a more global understanding of condensed matter transformations including the coupling of displacive with replacive mechanisms.
Keywords: A3 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
|
“On the phase-like nature of the 7M structure in Ni-Al”. Schryvers D, Tanner LE, Ecomaterials , 849 (1994). http://doi.org/10.1016/B978-1-4832-8381-4.50198-0
Abstract: The existence of the (52) stacking of the 7M martensite structure in Ni-Al is discussed in view of different experimental observations relating this structure to the premartensitic anomalies. It is concluded that the extreme fineness of the twinning is inherited from the wavelength of the premartensitic anomalies, while, given this dimension, the actual stacking tries to comply with stress free habit plane conditions by choosing the specific (52) stacking.
Keywords: A3 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
DOI: 10.1016/B978-1-4832-8381-4.50198-0
|
“Atomic-scale viscoplasticity mechanisms revealed in high ductility metallic glass films”. Idrissi H, Ghidelli M, Béché, A, Turner S, Gravier S, Blandin J-J, Raskin J-P, Schryvers D, Pardoen T, Scientific reports 9, 13426 (2019). http://doi.org/10.1038/s41598-019-49910-7
Abstract: The fundamental plasticity mechanisms in thin freestanding Zr65Ni35 metallic glass films are investigated in order to unravel the origin of an outstanding strength/ductility balance. The deformation process is homogenous until fracture with no evidence of catastrophic shear banding. The creep/relaxation behaviour of the films was characterized by on-chip tensile testing, revealing an activation volume in the range 100–200 Å3. Advanced high-resolution transmission electron microscopy imaging and spectroscopy exhibit a very fine glassy nanostructure with well-defined dense Ni-rich clusters embedded in Zr-rich clusters of lower atomic density and a ~2–3 nm characteristic length scale. Nanobeam electron diffraction analysis reveals that the accumulation of plastic deformation at roomtemperature
correlates with monotonously increasing disruption of the local atomic order. These results provide experimental evidences of the dynamics of shear transformation zones activation in metallic glasses. The impact of the nanoscale structural heterogeneities on the mechanical properties including the rate dependent behaviour is discussed, shedding new light on the governing plasticity mechanisms in metallic glasses with initially heterogeneous atomic arrangement.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.259
DOI: 10.1038/s41598-019-49910-7
|
“Interfacial characteristics and cohesion mechanisms of linear friction welded dissimilar titanium alloys: Ti–5Al–2Sn–2Zr–4Mo–4Cr (Ti17) and Ti–6Al–2Sn–4Zr–2Mo (Ti6242)”. Boyat X, Ballat-Durand D, Marteau J, Bouvier S, Favergeon J, Orekhov A, Schryvers D, Materials characterization 158, 109942 (2019). http://doi.org/10.1016/j.matchar.2019.109942
Abstract: A detailed microstructural examination endeavoring to understand the interfacial phenomena yielding to cohesion
in solid-state assembling processes was performed. This study focuses on the transition zone of a dissimilar
titanium alloy joint obtained by Linear Friction Welding (LFW) the β-metastable Ti17 to the near-α
Ti6242. The transition zone delimitating both alloys is characterized by a sharp microstructure change from
acicular HCP (Hexagonal Close-Packed) α′ martensitic laths in the Ti6242 to equiaxed BCC β (Body-Centered
Cubic) subgrains in the Ti17; these α′ plates were shown to precipitate within prior-β subgrains remarkably more
rotated than the ones formed in the Ti17. Both α′ and β microstructures were found to be intermingled within
transitional subgrains demarcating a limited gradient from one chemical composition to the other. These peculiar
interfacial grains revealed that the cohesive mechanisms between the rubbing surfaces occurred in the
single-phase β domain under severe strain and high-temperature conditions. During the hot deformation process,
the mutual migration of the crystalline interfaces from one material to another assisted by a continuous dynamic
recrystallization process was identified as the main adhesive mechanism at the junction zone. The latter led to
successful cohesion between the rubbing surfaces. Once the reciprocating motion stopped, fast cooling caused
both materials to experience either a βlean→α′ or βlean→βmetastable transformation in the interfacial zone depending
on their local chemical composition. The limited process time and the subsequent hindered chemical
homogenization at the transition zone led to retaining the so-called intermingled α’/βm subgrains constituting
the border between both Ti-alloys.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
DOI: 10.1016/j.matchar.2019.109942
|
“Ni cluster formation in low temperature annealed Ni50.6Ti49.4”. Pourbabak S, Wang X, Van Dyck D, Verlinden B, Schryvers D, Functional materials letters 10, 1740005 (2017). http://doi.org/10.1142/S1793604717400057
Abstract: Various low temperature treatments of Ni50.6Ti49.4 have shown an unexpected effect on the martensitic start temperature. Periodic diffuse intensity distributions in reciprocal space indicate the formation of short pure Ni strings along the <111> directions in the B2 ordered lattice, precursing the formation of Ni4Ti3 precipitates formed at higher annealing temperatures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 1.234
Times cited: 4
DOI: 10.1142/S1793604717400057
|
“Reclaiming the image of daguerreotypes: Characterization of the corroded surface before and after atmospheric plasma treatment”. Grieten E, Schalm O, Tack P, Bauters S, Storme P, Gauquelin N, Caen J, Patelli A, Vincze L, Schryvers D, Journal of cultural heritage (2017). http://doi.org/10.1016/j.culher.2017.05.008
Abstract: Technological developments such as atmospheric plasma jets for industry can be adapted for the conservation of cultural heritage. This application might offer a potential method for the removal or transformation of the corrosion on historical photographs. We focus on daguerreotypes and present an in-depth study of the induced changes by a multi-analytical approach using optical microscopy, scanning electron microscopy, different types of transmission electron microscopy and X-ray absorption fine structure. The H2-He afterglow removes S from an Ag2S or Cu2S layer which results in a nano-layer of metallic Ag or Cu on top of the deteriorated microstructure. In case the corrosion layer is composed of Cu-Ag-S compounds, our proposed setup can be used to partially remove the corrosion. These alterations of the corrosion results in an improvement in the readability of the photographic image.
Keywords: A1 Journal article; Art; History; Electron microscopy for materials research (EMAT); Antwerp Cultural Heritage Sciences (ARCHES)
Impact Factor: 1.838
Times cited: 9
DOI: 10.1016/j.culher.2017.05.008
|
“Martensite crystallography and chemistry in dual phase and fully martensitic steels”. Du C, Hoefnagels JPM, Kolling S, Geers MGD, Sietsma J, Petrov R, Bliznuk V, Koenraad PM, Schryvers D, Amin-Ahmadi B, Materials characterization 139, 411 (2018). http://doi.org/10.1016/j.matchar.2018.03.011
Abstract: Lath martensite is important in industry because it is the key strengthening component in many advanced high strength steels. The study of crystallography and chemistry of lath martensite is extensive in the literature, however, mostly based on fully martensitic steels. In this work, lath martensite in dual phase steels is investigated with a focus on the substructure identification of the martensite islands and microstructural bands using electron backscattered diffraction, and on the influence of the accompanied tempering process during industrial coating process on the distribution of alloying elements using atom probe tomography. Unlike findings for the fully martensitic steels, no martensite islands with all 24 Kurdjumov-Sachs variants have been observed. Almost all martensite islands contain only one main packet with all six variants and minor variants from the remaining three packets of the same prior austenite grain. Similarly, the martensite bands are typically composed of connected domains originating from prior austenite grains, each containing one main packets (mostly with all variants) and few separate variants. The effect of tempering at similar to 450 degrees C (due to the industrial zinc coating process) has also been investigated. The results show a strong carbon partitioning to lath boundaries and Cottrell atmospheres at dislocation core regions due to the thermal process of coating. In contrast, auto-tempering contributes to the carbon redistribution only in a limited manner. The substitutional elements are all homogenously distributed. The phase transformation process has two effects on the material: mechanically, the earlier-formed laths are larger and softer and therefore more ductile (as revealed by nanoindentation); chemically, due to the higher dislocation density inside the later-formed laths, which are generally smaller, carbon Cottrell atmospheres are predominantly observed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
DOI: 10.1016/j.matchar.2018.03.011
|
“Tailoring the Ti-C nanoprecipitate population and microstructure of titanium stabilized austenitic steels”. Cautaerts N, Delville R, Stergar E, Schryvers D, Verwerft M, Journal of nuclear materials 507, 177 (2018). http://doi.org/10.1016/J.JNUCMAT.2018.04.041
Abstract: The present work reports on the microstructural evolution of a new heat of 24% cold worked austenitic DIN 1.4970 (15-15Ti) nuclear cladding steel subjected to ageing heat treatments of varying duration between 500 and 800 degrees C (by steps of 100 degrees C). The primary aim was studying the finely dispersed Ti-C nanoprecipitate population, which are thought to be beneficial for creep and swelling resistance during service. Their size distribution and number density were estimated through dark field imaging and bright field Moire imaging techniques in the transmission electron microscope. Nanoprecipitates formed at and above 600 degrees C, which is a lower temperature than previously reported. The observed nucleation, growth and coarsening behavior of the nanoprecipitates were consistent with simple diffusion arguments. The formation of nanoprecipitates coincided with significant dissociation of dislocations as evidenced by weak beam dark field imaging. Possible mechanisms, including Silcock's stacking fault growth model and Suzuki segregation, are discussed. Recrystallization observed after extended ageing at 800 degrees C caused the redissolution of nanoprecipitates. Large primary Ti(C,N) and (Ti,Mo)C precipitates that occur in the as-received material, and M23C6 precipitates that nucleate on grain boundaries at low temperatures were also characterized by a selective dissolution procedure involving filtration, X-ray diffraction and quantitative Rietveld refinement. The partitioning of key elements between the different phases was derived by combining these findings and was consistent with thermodynamic considerations and the processing history of the steel. (C) 2018 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.048
Times cited: 1
DOI: 10.1016/J.JNUCMAT.2018.04.041
|
“Dislocation driven nanosample plasticity: new insights from quantitative in-situ TEM tensile testing”. Samaee V, Gatti R, Devincre B, Pardoen T, Schryvers D, Idrissi H, Scientific Reports 8, 12012 (2018). http://doi.org/10.1038/s41598-018-30639-8
Abstract: Intrinsic dislocation mechanisms in the vicinity of free surfaces of an almost FIB damage-free single crystal Ni sample have been quantitatively investigated owing to a novel sample preparation method combining twin-jet electro-polishing, in-situ TEM heating and FIB. The results reveal that the small-scale plasticity is mainly controlled by the conversion of few tangled dislocations, still present after heating, into stable single arm sources (SASs) as well as by the successive operation of these sources. Strain hardening resulting from the operation of an individual SAS is reported and attributed to the decrease of the length of the source. Moreover, the impact of the shortening of the dislocation source on the intermittent plastic flow, characteristic of SASs, is discussed. These findings provide essential information for the understanding of the regime of ‘dislocation source’ controlled plasticity and the related mechanical size effect.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 4.259
Times cited: 9
DOI: 10.1038/s41598-018-30639-8
|
“Effect of hydriding induced defects on the small-scale plasticity mechanisms in nanocrystalline palladium thin films”. Lumbeeck G, Idrissi H, Amin-Ahmadi B, Favache A, Delmelle R, Samaee V, Proost J, Pardoen T, Schryvers D, Journal Of Applied Physics 124, 225105 (2018). http://doi.org/10.1063/1.5055274
Abstract: Nanoindentation tests performed on nanocrystalline palladium films subjected to hydriding/dehydriding cycles demonstrate a significant softening when compared to the as-received material. The origin of this softening is unraveled by combining in situ TEM nanomechanical testing with automated crystal orientation mapping in TEM and high resolution TEM. The softening is attributed to the presence of a high density of stacking faults and of Shockley partial dislocations after hydrogen loading. The hydrogen induced defects affect the elementary plasticity mechanisms and the mechanical response by acting as preferential sites for twinning/detwinning during deformation. These results are analyzed and compared to previous experimental and simulation works in the literature. This study provides new insights into the effect of hydrogen on the atomistic deformation and cracking mechanisms as well as on the mechanical properties of nanocrystalline thin films and membranes.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 2.068
Times cited: 2
DOI: 10.1063/1.5055274
|
“Study of the Q&prime, (Q)-phase precipitation in Al–Mg–Si–Cu alloys by quantification of atomic-resolution transmission electron microscopy images and atom probe tomography”. Ding L, Orekhov A, Weng Y, Jia Z, Idrissi H, Schryvers D, Muraishi S, Hao L, Liu Q, Journal of materials science 54, 7943 (2019). http://doi.org/10.1007/s10853-019-03427-6
Abstract: The precipitation mechanism of the Q phase in Al-Mg-Si-Cu alloys has long been the subject of ambiguity and debate since its metastable phase (Q 0) has the same crystal structure and similar lattice parameters as its equilibrium counterparts. In the present work, the evolution of the Q 0 (Q) phase during aging is studied by combination of quantitative atomic-resolution scanning transmission electron microscopy and atom probe tomography. It was found that the transformation from the Q 0 to the Q phase involves changes of the occupancy of Al atoms in atomic columns of the Q 0 (Q) phase. The Al atoms incorporated in the Cu, Si and Mg columns are gradually released into the Al matrix, while mixing between Cu and Si atoms occurs in the Si columns. This transformation process is mainly attributed to the low lattice misfit of the equilibrium Q phase. Besides, the formation of various compositions of the Q phase is due to the different occupancy in the atomic columns of the Q phase. The occupancy changes in the columns of the Q phase are kinetically controlled and are strongly influenced by the alloy composition and aging temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.599
Times cited: 1
DOI: 10.1007/s10853-019-03427-6
|
“ALPHABETA: a dedicated open-source tool for calculating TEM stage tilt angles”. Cautaerts N, Delville R, Schryvers D, Journal of microscopy 273, 189 (2019). http://doi.org/10.1111/jmi.12774
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.692
Times cited: 2
DOI: 10.1111/jmi.12774
|
“In-Situ TEM Stress Induced Martensitic Transformation in Ni50.8Ti49.2 Microwires”. Pourbabak S, Orekhov A, Samaee V, Verlinden B, Van Humbeeck J, Schryvers D, Shape memory and superelasticity 5, 154 (2019). http://doi.org/10.1007/s40830-019-00217-6
Abstract: In-situ transmission electron microscopy tensile straining is used to study the stress induced martensitic transformation in Ni50.8Ti49.2. Two microwire samples with different heat treatment are investigated from which one single crystal and three polycrystalline TEM specimens, the latter with micro- and nano-size grains, have been produced. The measured Young’s modulus for all TEM specimens is around 70 GPa, considerably higher than the averaged 55 GPa of the original microwire sample. The height of the superelastic stress plateau shows an inverse relationship with the specimen thickness for the polycrystalline specimens. Martensite starts nucleating within the elastic region of the stress–strain curve and on the edges of the specimens while also grain boundaries act as nucleation sites in the polycrystalline specimens. When a martensite plate reaches a grain boundary in the polycrystalline specimen, it initiates the transformation in the neighboring grain at the other side of the grain boundary. In later stages martensite plates coalesce at higher loads in the stress plateau. In highly strained specimens, residual martensite remains after release.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1007/s40830-019-00217-6
|
“Microscopic investigation of as built and hot isostatic pressed Hastelloy X processed by Selective Laser Melting”. Pourbabak S, Montero-Sistiaga ML, Schryvers D, Van Humbeeck J, Vanmeensel K, Materials characterization 153, 366 (2019). http://doi.org/10.1016/j.matchar.2019.05.024
Abstract: Microstructural characteristics of Hastelloy X produced by Selective Laser Melting have been investigated by various microscopic techniques in the as built (AB) condition and after hot isostatic pressing (HIP). At sub-grain level the AB material consists of columnar high density dislocation cells while the HIP sample consists of columnar sub-grains with lower dislocation density that originate from the original dislocation cells, contradicting existing models. The sub-grains contain nanoscale precipitates enriched in Al, Ti, Cr and O, located at sub-grain boundaries in the AB condition and within the grains after HIP. At some grain boundaries, micrometer sized chromium carbides are detected after HIP. Micro hardness within the grains was found to decrease after HIP, which was attributed to the decrease in dislocation density due to recovery annealing.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 2
DOI: 10.1016/j.matchar.2019.05.024
|
“Orientation relationship of the austenite-to-ferrite transformation in austenitic stainless steels due to dissolution corrosion in contact with liquid Pb-Bi eutectic”. Charalampopoulou E, Cautaerts N, Van der Donck T, Schryvers D, Lambrinou K, Delville R, Scripta materialia 167, 66 (2019). http://doi.org/10.1016/J.SCRIPTAMAT.2019.03.035
Abstract: The orientation relationship of an austenite-to-ferrite phase transformation in 316L stainless steels induced by the loss of austenite stabilizers resulting from the steel dissolution corrosion in liquid Pb-Bi eutectic was studied by means of electron backscatter diffraction. The misorientations at the austenite/ferrite interface were compared to the prevailing orientation relationship models in steels. The Pitsch orientation relationship model was found to be predominant, which is unusual for austenite-to-ferrite bulk transformations in steels. The nature of this particular transformation, which involves loss of steel alloying elements and the presence of an interfacial liquid metal layer, is discussed to explain this finding. (C) 2019 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 3
DOI: 10.1016/J.SCRIPTAMAT.2019.03.035
|
Cautaerts N, Lamm S, Stergar E, Pakarinen J, Yang Y, Hofer C, Schnitzer R, Felfer P, Verwerft M, Delville R, Schryvers D (2020) Atom probe tomography data collection from DIN 1.4970 (15-15Ti) austenitic stainless steel irradiated with Fe ions
Abstract: This dataset comprises a large collection of atom probe tomography datasets collected from DIN 1.4970 alloy that was irradiated with Fe ions at different conditions. The DIN 1.4970 alloy is an austenitic stainless steel with 15 wt% Cr, 15 wt% Ni, a small addition of Ti. The full composition and characterization of our material can be found published elsewhere [1,2]. Some of our material was subjected to ageing heat treatments at different temperatures for different times. Small samples of our original material and aged material was irradiated at the Michigan Ion Beam Laboratory in 2017 with 4.5 MeV Fe ions up to 40 dpa at an average dose rate of 2×10−4 dpa/s. This was done at three different temperatures: 300, 450, and 600 ºC. Atom probe samples were made of the irradiated layers (approximately 1.5 micron deep) with focused ion beam and mounted on Microtip coupons. APT measurements took place on three CAMECA LEAP-HR systems located at CAES in Idaho Falls, USA (files beginning with R33), at Montanuniversität Leoben in Leoben, Austria (R21) and at Friedrich–Alexander University in Erlangen, Germany (R56).
Keywords: Dataset; Electron microscopy for materials research (EMAT)
DOI: 10.5281/ZENODO.3407832
|
“Crack initiation in tapered high Si stainless steel specimens : stress threshold analyses”. Penders A, Konstantinovic MJ, Bosch RW, Schryvers D, Corrosion Engineering Science And Technology , 1 (2020). http://doi.org/10.1080/1478422X.2020.1785651
Abstract: Tapered specimens were used for an accelerated test technique to study the crack initiation of high Si stainless steel by means of constant elongation rate tensile testing in a simulated pressurised water reactor environment. Detailed crack density distributions were obtained by applying an advanced crack detection algorithm on iteratively displaced scanning electron microscopy pictures featuring stress corrosion cracks along the specimen's gauge length. By means of finite-element analysis, prominent peaks in the crack density graphs are demonstrated to be related to stress relief and stress build-up during the crack initiation phase. Intrinsic scatter related to the crack detection suggests that stress corrosion cracking is independent of the strain-rate for strain-rates lower than 10(-6 )s(-1). Based on the extrapolation to constant load conditions, the critical threshold value for the duplex high Si stainless steel is estimated to be around 580 MPa.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.8
Times cited: 1
DOI: 10.1080/1478422X.2020.1785651
|
“DSC cycling effects on phase transformation temperatures of micron and submicron grain Ni50.8Ti49.2 microwires”. Pourbabak S, Verlinden B, Van Humbeeck J, Schryvers D, Shape memory and superelasticity , 1 (2020). http://doi.org/10.1007/S40830-020-00278-Y
Abstract: The effect of thermal cycling parameters on the phase transformation temperatures of micron and submicron grain size recrystallized Ni-Ti microwires was investigated. The suppression of martensitic transformation by thermal cycling was found to enhance when combined with room temperature aging between the cycles and enhances even more when aged at elevated temperature of 100 degrees C. While aging at room temperature alone has no clear effect on the martensitic transformation, elevated temperature aging at 100 degrees C alone suppresses the martensitic transformation. All aforementioned effects were found to be stronger in large grain samples than in small grain samples. Martensitic transformation suppression in all cases was in line with the formation of Ni4Ti3 precursors in the form of < 111 & rang;(B2) Ni clusters as concluded from the observed diffuse intensity in the electron diffraction patterns revealing short-range ordering enhancement. Performing thermal cycling in some different temperature ranges to separate the effect of martensitic transformation and high temperature range of DSC cycling revealed that both high temperature- and martensitic transformation-included cycles enhance the short-range ordering.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1007/S40830-020-00278-Y
|
“TEM investigation of the role of the polycrystalline-silicon film/substrate interface in high quality radio frequency silicon substrates”. Ding L, Raskin J-P, Lumbeeck G, Schryvers D, Idrissi H, Materials Characterization 161, 110174 (2020). http://doi.org/10.1016/J.MATCHAR.2020.110174
Abstract: The microstructural characteristics of two polycrystalline silicon (poly-Si) films with different electrical properties produced by low-pressure chemical vapour deposition on top of high resistivity silicon substrates were investigated by advanced transmission electron microscopy (TEM), including high resolution aberration corrected TEM and automated crystallographic orientation mapping in TEM. The results reveal that the nature of the poly-Si film/Si substrate interface is the main factor controlling the electrical resistivity of the poly-Si films. The high resistivity and high electrical linearity of poly-Si films are strongly promoted by the Sigma 3 twin type character of the poly-Si/Si substrate interface, leading to the generation of a huge amount of extended defects including stacking faults, Sigma 3 twin boundaries as well as Sigma 9 grain boundaries at this interface. Furthermore, a high density of interfacial dislocations has been observed at numerous common and more exotic grain boundaries deviating from their standard crystallographic planes. In contrast, poly-Si film/Si substrate interfaces with random character do not favour the formation of such complex patterns of defects, leading to poor electrical resistivity of the poly-Si film. This finding opens windows for the development of high resistivity silicon substrates for Radio Frequency (RF) integrated circuits (ICs) applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.7
DOI: 10.1016/J.MATCHAR.2020.110174
|
“The role of Ti and TiC nanoprecipitates in radiation resistant austenitic steel: A nanoscale study”. Cautaerts N, Delville R, Stergar E, Pakarinen J, Verwerft M, Yang Y, Hofer C, Schnitzer R, Lamm S, Felfer P, Schryvers D, Acta Materialia 197, 184 (2020). http://doi.org/10.1016/J.ACTAMAT.2020.07.022
Abstract: This work encompasses an in-depth transmission electron microscopy and atom probe tomography study of Ti-stabilized austenitic steel irradiated with Fe-ions. The focus is on radiation induced segregation and precipitation, and in particular on how Ti and TiC affect these processes. A 15-15Ti steel (grade: DIN 1.4970) in two thermo-mechanical states (cold-worked and aged) was irradiated at different temperatures up to a dose of 40 dpa. At low irradiation temperatures, the cold-worked and aged materials evolved to a similar microstructure dominated by small Si and Ni clusters, corresponding to segregation to small point defect clusters. TiC precipitates, initially present in the aged material, were found to be unstable under these irradiation conditions. Elevated irradiation temperatures resulted in the nucleation of nanometer sized Cr enriched TiC precipitates surrounded by Si and Ni enriched shells. In addition, nanometer sized Ti- and Mn-enriched G-phase (M6Ni16Si7) precipitates formed, often attached to TiC precipitates. Post irradiation, larger number densities of TiC were observed in the cold-worked material compared to the aged material. This was correlated with a lower volume fraction of G-phase. The findings suggest that at elevated irradiation temperatures, the precipitate-matrix interface is an important point defect sink and contributes to the improved radiation resistance of this material. The study is a first of its kind on stabilized steel and demonstrates the significance of the small Ti addition to the evolution of the microstructure under irradiation. (C) 2020 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.4
DOI: 10.1016/J.ACTAMAT.2020.07.022
|
“Optical encoding of luminescent carbon nanodots in confined spaces”. Bartholomeeusen E, De Cremer G, Kennes K, Hammond C, Hermans I, Lu J-B, Schryvers D, Jacobs PA, Roeffaers MBJ, Hofkens J, Sels BF, Coutino-Gonzalez E, Chemical Communications 57, 11952 (2021). http://doi.org/10.1039/D1CC04777A
Abstract: Stable emissive carbon nanodots were generated in zeolite crystals using near infrared photon irradiation gradually converting the occluded organic template, originally used to synthesize the zeolite crystals, into discrete luminescent species consisting of nano-sized carbogenic fluorophores, as ascertained using Raman microscopy, and steady-state and time-resolved spectroscopic techniques. Photoactivation in a confocal laser fluorescence microscope allows 3D resolved writing of luminescent carbon nanodot patterns inside zeolites providing a cost-effective and non-toxic alternative to previously reported metal-based nanoclusters confined in zeolites, and opens up opportunities in bio-labelling and sensing applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
DOI: 10.1039/D1CC04777A
|
““Branched&rdquo, structural transformation of the L12-Al3Zr phase manipulated by Cu substitution/segregation in the Al-Cu-Zr alloy system”. Ding L, Zhao M, Ehlers FJH, Jia Z, Zhang Z, Weng Y, Schryvers D, Liu Q, Idrissi H, Journal of materials science &, technology 185, 186 (2024). http://doi.org/10.1016/j.jmst.2023.11.015
Abstract: The effect of Cu on the evolution of the Al3Zr phase in an Al-Cu-Zr cast alloy during solution treatment at 500 °C has been thoroughly studied by combining atomic resolution high-angle annular dark-field scanning transmission electron microscopy, energy-dispersive X-ray spectroscopy and first-principles cal- culations. The heat treatment initially produces a pure L12-Al3Zr microstructure, allowing for about 13 % Cu to be incorporated in the dispersoid. Cu incorporation increases the energy barrier for anti-phase boundary (APB) activation, thus stabilizing the L12 structure. Additional heating leads to a Cu-induced “branched”path for the L12 structural transformation, with the latter process accelerated once the first APB has been created. Cu atoms may either (i) be repelled by the APBs, promoting the transformation to a Cu-poor D023 phase, or (ii) they may segregate at one Al-Zr layer adjacent to the APB, promoting a transformation to a new thermodynamically favored phase, Al4CuZr, formed when these segregation layers are periodically arranged. Theoretical studies suggest that the branching of the L12 transformation path is linked to the speed at which an APB is created, with Cu attraction triggered by a comparatively slow process. This unexpected transformation behavior of the L12-Al3Zr phase opens a new path to understanding, and potentially regulating the Al3Zr dispersoid evolution for high temperature applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 10.9
DOI: 10.1016/j.jmst.2023.11.015
|
“Electronic and chemical properties of nickel oxide thin films and the intrinsic defects compensation mechanism”. Poulain R, Lumbeeck G, Hunka J, Proost J, Savolainen H, Idrissi H, Schryvers D, Gauquelin N, Klein A, ACS applied electronic materials 4, 2718 (2022). http://doi.org/10.1021/ACSAELM.2C00230
Abstract: Although largely studied, contradictory results on nickel oxide (NiO) properties can be found in the literature. We herein propose a comprehensive study that aims at leveling contradictions related to NiO materials with a focus on its conductivity, surface properties, and the intrinsic charge defects compensation mechanism with regards to the conditions preparation. The experiments were performed by in situ photo-electron spectroscopy, electron energy loss spectroscopy, and optical as well as electrical measurements on polycrystalline NiO thin films prepared under various preparation conditions by reactive sputtering. The results show that surface and bulk properties were strongly related to the deposition temperature with in particular the observation of Fermi level pinning, high work function, and unstable oxygen-rich grain boundaries for the thin films produced at room temperature but not at high temperature (>200 degrees C). Finally, this study provides substantial information about surface and bulk NiO properties enabling to unveil the origin of the high electrical conductivity of room temperature NiO thin films and also for supporting a general electronic charge compensation mechanism of intrinsic defects according to the deposition temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1021/ACSAELM.2C00230
|