“High magnetic ordering temperature in the perovskites Sr4-xLaxFe3ReO12 (x=0.0, 1.0, 2.0)”. Retuerto M, Li MR, Go YB, Ignatov A, Croft M, Ramanujachary KV, Herber RH, Nowik I, Hodges JP, Dachraoui W, Hadermann J, Greenblatt M;, Journal of solid state chemistry 194, 48 (2012). http://doi.org/10.1016/j.jssc.2012.06.031
Abstract: A series of perovskites Sr4−xLaxFe3ReO12 (x=0.0, 1.0, 2.0) has been prepared by wet chemistry methods. The structure analyses by powder X-ray and neutron diffraction and electron microscopy show that these compounds adopt simple perovskite structures without cation ordering over the B sites: tetragonal (I4/mcm) for x=0.0 and 1.0 and orthorhombic (Pbmn) for x=2.0. The oxidation states of the cations in the compound with x=0.0 appear to be Fe3+/4+ and Re7+ and decrease for both with La substitution as evidenced by X-ray absorption spectroscopy. All the compounds are antiferromagnetically ordered above room temperature, as demonstrated by Mössbauer spectroscopy and the magnetic structures, which were determined by powder neutron diffraction. The substitution of Sr by La strongly affects the magnetic properties with an increase of TN up to ∼750 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 9
DOI: 10.1016/j.jssc.2012.06.031
|
|
|
“From spin induced ferroelectricity to dipolar glasses : spinel chromites and mixed delafossites”. Maignan A, Martin C, Singh K, Simon C, Lebedev OI, Turner S, Journal of solid state chemistry 195, 41 (2012). http://doi.org/10.1016/j.jssc.2012.01.063
Abstract: Magnetoelectric multiferroics showing coupling between polarization and magnetic order are attracting much attention. For instance, they could be used in memory devices. Metal-transition oxides are provided several examples of inorganic magnetoelectric multiferroics. In the present short review, spinel and delafossite chromites are described. For the former, an electric polarization is evidenced in the ferrimagnetic state for ACr2O4 polycrystalline samples (A=Ni, Fe, Co). The presence of a JahnTeller cation such as Ni2+ at the A site is shown to yield larger polarization values. In the delafossites, substitution by V3+ at the Cr or Fe site in CuCrO2 (CuFeO2) suppresses the complex antiferromagnetic structure at the benefit of a spin glass state. The presence of cation disorder, probed by transmission electron microscopy, favors relaxor-like ferroelectricity. The results on the ferroelectricity of ferrimagnets and insulating spin glasses demonstrate that, in this research field, transition-metal oxides are worth to be studied.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 27
DOI: 10.1016/j.jssc.2012.01.063
|
|
|
“Structure and high-temperature properties of the (Sr,Ca,Y)(Co,Mn)O3-y perovskites –, perspective cathode materials for IT-SOFC”. Napolsky PS, Drozhzhin OA, Istomin SY, Kazakov SM, Antipov EV, Galeeva AV, Gippius AA, Svensson G, Abakumov AM, Van Tendeloo G, Journal of solid state chemistry 192, 186 (2012). http://doi.org/10.1016/j.jssc.2012.03.056
Abstract: Oxygen deficient perovskites Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75, were prepared by using the citrate route at 1373-1573 K for 48 h. The cubic Pm-3m perovskite structure for x=0.5 was confirmed by electron diffraction study and refined using neutron powder diffraction (NPD) data. For x=0.75, the superstructure corresponding to a=root 2 x a(per), b=2 x a(per), c=root 2 x a(per) (a(0)b(-)b(-) tilt system, space group Imma) was revealed by electron diffraction. The solid solution Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= x <= 0.6 and compound Ca0.75Y0.25Mn0.85Co0.15O2.92 were prepared in air at 1573 K for 48 h. The crystal structure of Ca0.75Y0.25Mn0.85Co0.15O2.92 was refined using NPD data (S.G. Pnma, a=5.36595(4), b=7.5091(6), c=5.2992(4) angstrom, R-p=0.057, R-wp=0.056, chi(2)=4.26). High-temperature thermal expansion properties of the prepared compounds were studied in air using both dilatometry and high-temperature X-ray powder diffraction data (HTXRPD). They expanding non-linearly at 298-1073 K due to the loss of oxygen at high temperatures. Calculated average thermal expansion coefficients (TECs) for Sr0.75Y0.25Co1-xMnxO3-y, x=0.5, 0.75 and Ca0.75Y0.25Mn0.85Co0.15O2.92(1) are 15.5, 15.1, and 13.8 ppm K-1, respectively. Anisotropy of the thermal expansion along different unit cell axes was observed for Sr0.15Ca0.6Y0.25Co0.25Mn0.75O3-y, and Ca0.75Y0.25Mn0.85Co0.15O2.92. Conductivity of Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75 increases with the temperature reaching 110 S/cm for x=0.5 and 44 S/cm for x=0.75 at 1173 K. Samples of Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= y <= 0.6 were found to be n-type conductors at room temperature with the similar temperature dependence of the conductivity and demonstrated the increase of the sigma value from similar to 1 to similar to 50 S/cm as the temperature increases from 300 to 1173 K. Their conductivity is described in terms of the small polaron charge transport with the activation energy (E-p) increasing from 340 to 430 meV with an increase of the calcium content from x=0 to x=0.6. (C) 2012 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/j.jssc.2012.03.056
|
|
|
“Structural aspects and antiferromagnetic ordering in the “123&rdquo, derivative LnSr2Cu2Ga1-xFexO7-\delta (Ln = Y, Ho)”. Rykov A, Caignaert V, Van Tendeloo G, Greneche JM, Studer F, Nguyen N, Ducouret A, Bonville P, Raveau B, Journal of solid state chemistry 113, 94 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 9
|
|
|
“High resolution electron microscopic study of Ba7Sc6Al2O19 and related phases”. Shpanchenko RV, Nistor L, Van Tendeloo G, Amelinckx S, Antipov EV, Kovba LM, Journal of solid state chemistry 113, 193 (1994). http://doi.org/10.1006/jssc.1994.1359
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 3
DOI: 10.1006/jssc.1994.1359
|
|
|
“Structural characteristics of the 40K superconductor Bi2Sr5Cu3(CO3)2O10: a HREM study”. Hervieu M, Pelloquin D, Michel C, Van Tendeloo G, Raveau B, Journal of solid state chemistry 112, 139 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 5
|
|
|
“Structural aspects of Li-doped tubular bismuth cuprates (Bi2Sr3Cu2-xLixOy): an electron microscopy study”. Van Tendeloo G, Domengès B, Caldes MT, Hervieu M, Raveau B, Journal of solid state chemistry 112, 161 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
|
|
|
“Defects and phase transformation in monclinic natural hollandite: BaxMn8O16”. Nistor LC, Van Tendeloo G, Amelinckx S, Journal of solid state chemistry 109, 152 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 13
|
|
|
“Structural considerations and HREM on LanTin-\deltaO3n (n≥4δ)”. Van Tendeloo G, Amelinckx S, Darriet B, Bontchev R, Darriet J, Weill F, Journal of solid state chemistry 108, 314 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 29
|
|
|
“Effect of cobalt content on the properties of quintuple perovskites Sm₂Ba₃Fe₅-xCoxO₁₅-δ”. Golovachev IB, Mychinko MY, Volkova NE, Gavrilova LY, Raveau B, Maignan A, Cherepanov VA, Journal Of Solid State Chemistry 301, 122324 (2021). http://doi.org/10.1016/J.JSSC.2021.122324
Abstract: Quintuple perovskites Sm2Ba3Fe5-xCoxO15-delta = 0.5, 1.0 and 1.5) have been prepared by glycerin-nitrate tech- nique in air. The phase purity was confirmed by XRD. Partial substitution of Co for Fe decreases the oxygen content and thus the mean oxidation state of 3d-metals. It also slightly decreases the thermal expansion coefficient of oxides. Positive value of the Seebeck coefficient confirmed p-type conductivity, though the thermopower decreases as the Co content increases. The temperature dependence of electrical conductivity reveals a maximum at 550-750 degrees C.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
DOI: 10.1016/J.JSSC.2021.122324
|
|
|
“Structural and magnetic properties of the perovskites A₂LaFe₂SbO₉, (A = Ca, Sr, Ba)”. Hendrickx M, Tang Y, Hunter EC, Battle PD, Hadermann J, Journal Of Solid State Chemistry 295, 121914 (2021). http://doi.org/10.1016/J.JSSC.2020.121914
Abstract: Polycrystalline samples of A(2)LaFe(2)SbO(9) (A = Ca, Sr, Ba) perovskites appeared monophasic to X-ray or neutron powder diffraction but a single-crystal study utilising transmission electron microscopy revealed a greater level of complexity. Although local charge balance is maintained, compositional and structural variations are present among and within the submicron-sized crystals. Despite the inhomogeneity, A = Ca is monophasic with a partially-ordered distribution of Fe3+ and Sb5+ cations across two crystallographically-distinct octahedral sites, i.e. Ca2La(Fe1.25Sb0.25)(2d) (Fe0.75Sb0.75)(2c)O-9. For A = Sr or Ba, the inhomogeneities result in differences in the filling patterns of the octahedra and the ordering of the B cations. Particles of A = Sr contain a phase (Fe:Sb similar to 2:1) without B cation ordering and one (Fe:Sb similar to 1:1) with B cation ordering. Monophasic A = Ba lacks long-range cation order although ordered nanodomains are present within the disordered phase. The temperature dependence of the magnetic properties of each sample is discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
DOI: 10.1016/J.JSSC.2020.121914
|
|
|
“Preparation of the noncentrosymmetric ferrimagnetic phase La0.9Ba0.1Mn0.96O2.43 by topochemical reduction”. Parsons TG, Hadermann J, Halasyamani PS, Hayward MA, Journal Of Solid State Chemistry 287, 121356 (2020). http://doi.org/10.1016/J.JSSC.2020.121356
Abstract: Topochemical reduction of La0.9Ba0.1MnO3 with NaH at 225 degrees C yields the brownmillerite phase La0.9Ba0.1MnO2.5. However, reduction with CaH2 at 435 degrees C results in the formation of La0.9Ba0.1Mn0.96O2.43 via the deintercalation of both oxide anions and manganese cations from the parent perovskite phase. Electron and neutron diffraction data reveal La0.9Ba0.1Mn0.96O2.43 adopts a complex noncentrosymmetric structure, described in space group I23, confirmed by SHG measurements. Low-temperature neutron diffraction data reveal La0.9Ba0.1Mn0.96O2.43 adopts an ordered magnetic structure in which all the nearest neighbor interactions are antiferromagnetic. However, the presence of ordered manganese cation-vacancies results in a net ferrimagnetic structure with net saturated moment of 0.157(2) mu B per manganese center.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.3
DOI: 10.1016/J.JSSC.2020.121356
|
|
|
“Toward unlocking the Mn3+/Mn2+ redox pair in alluaudite-type Na2+2zMn2-z(SO4)3-x(SeO4)x cathodes for sodium-ion batteries”. Kirsanova MA, De Sloovere D, Karakulina OM, Hadermann J, Van Bael MK, Hardy A, Abakumov AM, Journal of solid state chemistry 277, 804 (2019). http://doi.org/10.1016/J.JSSC.2019.07.032
Abstract: In polyanion cathodes, the inductive effect alters the potential of a M(n+1)+/Mn+ redox couple (M – transition metal) according to the electronegativity of the X cation in the polyanion groups (XO4m+). To manipulate the operating potential, we synthesized a series of mixed sulfate-selenate alluaudites, with structure formulas Na2+2zMn2-z(SO4)(3-x)(SeO4)(x) and Na2.81Ni1.60(SO4)(1.43)(SeO4)(1.57). Their crystal structure was determined from powder X-ray diffraction data, revealing that the Mn-based alluaudites form solid solutions with the same crystal structure for x = 0.75; 1.125 and 1.5. Na2.81Ni1.60(SO4)(1.43)(SeO4)(1.57) is isostructural to the Mn-based alluaudites. Although the Na2+2zMn2-z(SO4)(3-x)(SeO4)(x) compound with the highest selenium content demonstrates a reversible discharge capacity of 60 mAh g(-1), only a small part of this electrochemical activity can be ascribed to the Mn3+/Mn2+ redox couple. The redox potential of the Mn3+/Mn2+ pair in Na2+2zMn2-z(SO4)(3-)x(SeO4)(x) decreases with increasing values of x, in agreement with the lower electronegativity of Se compared to that of S.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
DOI: 10.1016/J.JSSC.2019.07.032
|
|
|
“Stabilisation of magnetic ordering in La3Ni2-xCuxB'O9(B'=Sb,Ta,Nb) by the introduction of Cu2+”. Chin C-M, Battle PD, Hunter EC, Avdeev M, Hendrickx M, Hadermann J, Journal of solid state chemistry 276, 164 (2019). http://doi.org/10.1016/J.JSSC.2019.05.006
Abstract: La3Ni2-xCuxB'O-9 (x = 0.25; B' = Sb, Ta, Nb: x = 0.5; B' = Nb) have been synthesized and characterised by transmission electron microscopy, neutron diffraction and magnetometry. Each adopts a perovskite-like structure (space group P2(1)/n) with two crystallographically-distinct six-coordinate sites, one occupied by a disordered arrangement of Ni2+ and Cu2+ and the other by a disordered similar to 1:2 distribution of Ni2+ and B'(5+), although some Cu2+ is found on the latter site when x = 0.5. Each composition undergoes a magnetic transition in the range 90 <= T/K <= 130 and shows a spontaneous magnetisation at 5 K; the transition temperature always exceeds that of the x = 0 composition by >= 30 K. A long-range ordered G-type ferrimagnetic structure is present in each composition, but small relaxor domains are also present. This contrasts with the pure relaxor and spin-glass behaviour of x = 0, B' = Ta, Nb, respectively.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 2
DOI: 10.1016/J.JSSC.2019.05.006
|
|
|
“CaLa2FeCoSbO9 and ALa2FeNiSbO9 (A = Ca, Sr, Ba): cation-ordered, inhomogeneous, ferrimagnetic perovskites”. Hendrickx M, Tang Y, Hunter EC, Battle PD, Cadogan Jm, Hadermann J, Journal Of Solid State Chemistry 285, 121226 (2020). http://doi.org/10.1016/j.jssc.2020.121226
Abstract: Polycrystalline samples of CaLa2FeCoSbO9 and ALa2FeNiSbO9 (A=Ca, Sr, Ba) have been prepared in solid-state reactions and studied by a combination of transmission electron microscopy, magnetometry, X-ray diffraction, neutron diffraction and Mössbauer spectroscopy. Diffraction and TEM showed that each shows 1:1 B-site ordering in which Co2+/Ni2+ and Sb5+ tend to occupy two distinct crystallographic sites while Fe3+ is distributed over both sites. While X-ray and neutron diffraction agreed that all four compositions are monophasic with space group P21/n, TEM revealed different levels of compositional inhomogeneity at the subcrystal scale, which, in the case of BaLa2FeNiSbO9, leads to the occurrence of both a P21/n and an I2/m phase. Magnetometry and neutron diffraction show that these perovskites are ferrimagnets with a G-type magnetic structure. Their relatively low magnetisation can be attributed to their inhomogeneity. This work demonstrates the importance of studying the microstructure of complex compositions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.3
DOI: 10.1016/j.jssc.2020.121226
|
|
|
“Crystal structure study of manganese and titanium substituted BaLaFe2O6-δ”. Ben Hafsia A, Hendrickx M, Batuk M, Khitouni M, Hadermann J, Greneche J-M, Rammeh N, Journal of solid state chemistry 251, 186 (2017). http://doi.org/10.1016/j.jssc.2017.04.019
Abstract: Barium lanthanum ferrite and four Mn/Ti substituted materials were synthesized by the sol-gel method. The crystal structure of the materials was studied by a combination of X-ray powder diffraction, electron diffraction, scanning transmission electron microscopy and 57Fe Mössbauer spectrometry. BaLaFe2O6-δ has a cubic perovskite structure and Ba0.7La1.3FeMnO6-δ is distorted perovskite with the R-3c symmetry, both from electron diffraction and X-ray powder diffraction. However, according to transmission electron microscopy, the crystals of BaLaFeTiO6-δ, BaLaFeTi0.5Mn0.5O6-δ, and BaLaFe0.5Ti0.5MnO6-δ consist of nanodomains with different symmetries (Pm3m next to R-3c due to octahedral tilts), whereas the bulk X-ray powder diffraction patterns for these compounds correspond to the simple cubic structure. 57Fe Mössbauer spectrometry confirms that all materials contain high spin state Fe3+ ions which are strongly influenced by the chemical disorder
resulting from various cationic environments.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
DOI: 10.1016/j.jssc.2017.04.019
|
|
|
“Synthesis, structure and electrochemical properties of LiNaCo0.5Fe0.5PO4F fluoride-phosphate”. Fedotov SS, Kuzovchikov SM, Khasanova NR, Drozhzhin OA, Filimonov DS, Karakulina OM, Hadermann J, Abakumov AM, Antipov EV, Journal of solid state chemistry 242, 70 (2016). http://doi.org/10.1016/j.jssc.2016.02.042
Abstract: LiNaCo 0.5 Fe 0.5 PO 4 F fluoride-phosphate was synthesized via conventional solid-state and novel freeze-drying routes. The crystal structure was refined based on neutron powder diffraction (NPD) data and validated by electron diffraction (ED) and high-resolution transmission electron microscopy (HRTEM). The alkali ions are ordered in LiNaCo 0.5 Fe 0.5 PO 4 F and the transition metals jointly occupy the same crystallographic sites. The oxidation state and oxygen coordination environment of the Fe atoms were verified by 57 Fe Mössbauer spectroscopy. Electrochemical tests of the LiNaCo 0.5 Fe 0.5 PO 4 F cathode material demonstrated a reversible activity of the Fe 3+ /Fe 2+ redox couple at the electrode potential near 3.4 V and minor activity of the Co 3+ /Co 2+ redox couple over 5 V vs Li/Li + . The material exhibits a good capacity retention in the 2.4÷4.6 V vs Li/Li + potential range with the delivered discharge capacity of more than 82% (theo.) regarding Fe 3+ /Fe 2+ .
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 1
DOI: 10.1016/j.jssc.2016.02.042
|
|