“Wafer-level electrical evaluation of vertical carbon nanotube bundles as a function of growth temperature”. Vereecke B, van der Veen MH, Sugiura M, Kashiwagi Y, Ke X, Cott DJ, Hantschel T, Huyghebaert C, Tökei Z, Japanese journal of applied physics 52, 04cn02 (2013). http://doi.org/10.7567/JJAP.52.04CN02
Abstract: We have evaluated the resistance of carbon nanotubes (CNTs) grown at a CMOS-compatible temperature using a realistic integration scheme. The structural analysis of the CNTs by transmission electron microscopy (TEM) showed that the degree of graphitization decreased significantly when the growth temperature was decreased from 540 to 400 °C. The CNTs were integrated to form 150-nm-diameter vertical interconnects between a TiN layer and Cu metal trenches on 200 mm full wafers. Wafers with CNTs grown at low temperature were found to have a lower single-contact resistance than those produced at high temperatures. Thickness measurements showed that the low contact resistance is a result of small contact height. This height dependence is masking the impact of CNT graphitization quality on resistance. When benchmarking our results with data from the literature, a relationship between resistivity and growth temperature cannot be found for CNT-based vertical interconnects.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.384
Times cited: 5
DOI: 10.7567/JJAP.52.04CN02
|
“Synthesis of highly luminescent silica-coated CdSe/CdS nanorods”. Pietra F, van Dijk-Moes RJA, Ke X, Bals S, Van Tendeloo G, de Mello Donega C, Vanmaekelbergh D, Chemistry of materials 25, 3427 (2013). http://doi.org/10.1021/cm401169t
Abstract: CdSe(core)/CdS(shell) nanorods (NRs) have been extensively investigated for their unique optical properties, such as high photoluminescence (PL) quantum efficiency (QE) and polarized light emission. The incorporation of these NRs in silica (SiO2) is of high interest, since this renders them processable in polar solvents while increasing their photochemical stability, which would be beneficial for their application in LEDs and as biolabels. We report the synthesis of highly luminescent silica-coated CdSe/CdS NRs, by using the reverse micelle method. The mechanism for the encapsulation of the NRs in silica is unravelled and shown to be strongly influenced by the NR shape and its asymmetry. This is attributed to both the different morphology and the different crystallographic nature of the facets terminating the opposite tips of the NRs. These results lead to the formation of a novel class of NR architectures, whose symmetry can be controlled by tuning the degree of coverage of the silica shell. Interestingly, the encapsulation of the NRs in silica leads to a remarkable increase in their photostability, while preserving their optical properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 46
DOI: 10.1021/cm401169t
|
“Tailoring ZnSe-CdSe colloidal quantum dots via cation exchange : from core/shell to alloy nanocrystals”. Groeneveld E, Witteman L, Lefferts M, Ke X, Bals S, Van Tendeloo G, de Mello Donega C, ACS nano 7, 7913 (2013). http://doi.org/10.1021/nn402931y
Abstract: We report a study of Zn2+ by Cd2+ cation exchange (CE) in colloidal ZnSe nanocrystals (NCs). Our results reveal that CE in ZnSe NCs is a thermally activated isotropic process. The CE efficiency (i.e., fraction of Cd2+ ions originally in solution, Cdsol, that is incorporated in the ZnSe NC) increases with temperature and depends also on the Cdsol/ZnSe ratio. Interestingly, the reaction temperature can be used as a sensitive parameter to tailor both the composition and the elemental distribution profile of the product (Zn,Cd)Se NCs. At 150 °C ZnSe/CdSe core/shell hetero-NCs (HNCs) are obtained, while higher temperatures (200 and 220 °C) produce (Zn1xCdx)Se gradient alloy NCs, with increasingly smoother gradients as the temperature increases, until homogeneous alloy NCs are obtained at T ≥ 240 °C. Remarkably, sequential heating (150 °C followed by 220 °C) leads to ZnSe/CdSe core/shell HNCs with thicker shells, rather than (Zn1xCdx)Se gradient alloy NCs. Thermal treatment at 250 °C converts the ZnSe/CdSe core/shell HNCs into (Zn1xCdx)Se homogeneous alloy NCs, while preserving the NC shape. A mechanism for the cation exchange in ZnSe NCs is proposed, in which fast CE takes place at the NC surface, and is followed by relatively slower thermally activated solid-state cation diffusion, which is mediated by Frenkel defects. The findings presented here demonstrate that cation exchange in colloidal ZnSe NCs provides a very sensitive tool to tailor the nature and localization regime of the electron and hole wave functions and the optoelectronic properties of colloidal ZnSeCdSe NCs.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 153
DOI: 10.1021/nn402931y
|
“A nanoscale shape memory oxide”. Zhang J, Ke X, Gou G, Seidel J, Xiang B, Yu P, Liang WI, Minor AM, Chu Yh, Van Tendeloo G, Ren X, Ramesh R;, Nature communications 4, 2768 (2013). http://doi.org/10.1038/ncomms3768
Abstract: Stimulus-responsive shape-memory materials have attracted tremendous research interests recently, with much effort focused on improving their mechanical actuation. Driven by the needs of nanoelectromechanical devices, materials with large mechanical strain, particularly at nanoscale level, are therefore desired. Here we report on the discovery of a large shape-memory effect in bismuth ferrite at the nanoscale. A maximum strain of up to ~14% and a large volumetric work density of ~600±90 J cm−3 can be achieved in association with a martensitic-like phase transformation. With a single step, control of the phase transformation by thermal activation or electric field has been reversibly achieved without the assistance of external recovery stress. Although aspects such as hysteresis, microcracking and so on have to be taken into consideration for real devices, the large shape-memory effect in this oxide surpasses most alloys and, therefore, demonstrates itself as an extraordinary material for potential use in state-of-art nanosystems.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 67
DOI: 10.1038/ncomms3768
|
“Magnetically decorated multiwalled carbon nanotubes as dual MRI and SPECT contrast agents”. Wang JTW, Cabana L, Bourgognon M, Kafa H, Protti A, Venner K, Shah AM, Sosabowski JK, Mather SJ, Roig A, Ke X, Van Tendeloo G, de Rosales RTM, Tobias G, Al-Jamal KT, Advanced functional materials 24, 1880 (2014). http://doi.org/10.1002/adfm.201302892
Abstract: Carbon nanotubes (CNTs) are one of the most promising nanomaterials to be used in biomedicine for drug/gene delivery as well as biomedical imaging. This study develops radio-labeled, iron oxide-decorated multiwalled CNTs (MWNTs) as dual magnetic resonance (MR) and single photon emission computed tomography (SPECT) contrast agents. Hybrids containing different amounts of iron oxide are synthesized by in situ generation. Physicochemical characterisations reveal the presence of superparamagnetic iron oxide nanoparticles (SPION) granted the magnetic properties of the hybrids. Further comprehensive examinations including high resolution transmission electron microscopy (HRTEM), fast Fourier transform simulations, X-ray diffraction, and X-ray photoelectron spectroscopy assure the conformation of prepared SPION as γ-Fe2O3. High r2 relaxivities are obtained in both phantom and in vivo MRI compared to the clinically approved SPION Endorem. The hybrids are successfully radio labeled with technetium-99m through a functionalized bisphosphonate and enable SPECT/CT imaging and γ-scintigraphy to quantitatively analyze the biodistribution in mice. No abnormality is found by histological examination and the presence of SPION and MWNT are identified by Perls stain and Neutral Red stain, respectively. TEM images of liver and spleen tissues show the co-localization of SPION and MWNTs within the same intracellular vesicles, indicating the in vivo stability of the hybrids after intravenous injection. The results demonstrate the capability of the present SPIONMWNT hybrids as dual MRI and SPECT contrast agents for in vivo use.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 50
DOI: 10.1002/adfm.201302892
|
“NEXAFS spectromicroscopy of suspended carbon nanohorns”. Bittencourt C, Ke X, Van Tendeloo G, Tagmatarchis N, Guttmann P, Chemical physics letters 587, 85 (2013). http://doi.org/10.1016/j.cplett.2013.09.034
Abstract: We demonstrate that near-edge X-ray-absorption fine-structure spectroscopy combined with full-field transmission X-ray microscopy can be used to study the electronic structure of suspended carbon nanohorns. Based on reports of electronic structure calculations additional spectral features observed in the π region of the NEXAFS spectrum recorded on the carbon nanohorns were associated to the presence of the pentagonal rings and the folding of the graphene sheet.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 4
DOI: 10.1016/j.cplett.2013.09.034
|
“Ultrasonication induces oxygenated species and defects onto exfoliated graphene”. Skaltsas T, Ke X, Bittencourt C, Tagmatarchis N, The journal of physical chemistry: C : nanomaterials and interfaces 117, 23272 (2013). http://doi.org/10.1021/jp4057048
Abstract: The effect of ultrasonication parameters, such as time and power applied, to exfoliate graphite in o-dichlorobenzene (o-DCB) and N-methyl-1,2-pyrrolidone (NMP) was examined. It was found that the concentration of graphene was higher in o-DCB, while its dispersibility was increased when sonication was applied for a longer period and/or at higher power. However, spectroscopic examination by X-ray photoelectron spectroscopy (XPS) revealed that ultrasonication causes defects and induces oxygen functional groups in the form of carboxylic acids and ethers/epoxides onto the graphene lattice. Additional proof for the latter arose from Raman, IR, and thermogravimetry studies. The carboxylic acids and ethers/epoxides onto exfoliated graphene were derived from air during ultrasonication and found independent of the solvent used for the exfoliation and the power and/or time ultrasonication applied. Quantitative evaluation of the amount of oxygenated species present on exfoliated graphene as performed by high-resolution XPS revealed that the relative oxygen percentage was higher when exfoliation was performed in NMP. Finally, the sonication time and/or power affected the oxygen content on exfoliated graphene, since extended ultrasonication resulted in a decrease in the oxygen content on exfoliated graphene, with a simultaneous increase of defected sp(3) carbon atoms.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 65
DOI: 10.1021/jp4057048
|
“TXM-NEXAFS of TiO2-based nanostructures”. Guttmann P, Bittencourt C, Ke X, Van Tendeloo G, Umek P, Arcon D, Ewels CP, Rehbein S, Heim S, Schneider G, AIP conference proceedings 1365, 437 (2011). http://doi.org/10.1063/1.3625396
Abstract: In this work, electronic properties of individual TiOx-pristine nanoribbons (NR) prepared by hydrothermal treatment of anatase TiO(2) micro-particles were studied using the HZB transmission x-ray microscope (TXM) at the BESSY II undulator beamline U41-FSGM. NEXAFS is ideally suited to study TiO(2)-based materials because both the O K-edge and Ti L-edge features are very sensitive to the local bonding environment, providing diagnostic information about the crystal structures and oxidation states of various forms of titanium oxides and sub-oxides. TXM-NEXAFS combines full-field x-ray microscopy with spectroscopy, allowing the study of the electronic structure of individual nanostructures with spatial resolution better than 25 nm and a spectral resolution of up to E/Delta E = 10000. The typical image field in TXM-NEXAFS measurements is about 10 mu m. 10 mu m, which is large compared to the individual nanoparticle. Therefore, one image stack already contains statistically significant data. In addition, the directional electric field vector ((E) over bar) of the x-rays can be used as a “search tool” for the direction of chemical bonds of the atom selected by its absorption edge.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1063/1.3625396
|
“Positive graphene by chemical design : tuning supramolecular strategies for functional surfaces”. Hadad C, Ke X, Carraro M, Sartorel A, Bittencourt C, Van Tendeloo G, Bonchio M, Quintana M, Prato M, Chemical communications 50, 885 (2014). http://doi.org/10.1039/c3cc47056c
Abstract: A diazonium based-arylation reaction was efficiently used for the covalent addition of 4-amino-N,N,N-trimethylbenzene ammonium to stable dispersions of few layer graphene (FLG) yielding an innovative FLG platform with positive charges to immobilize inorganic polyanions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 19
DOI: 10.1039/c3cc47056c
|
“Homopolymers as nanocarriers for the loading of block copolymer micelles with metal salts : a facile way to large-scale ordered arrays of transition-metal nanoparticles”. Shan L, Punniyakoti S, Van Bael MJ, Temst K, Van Bael MK, Ke X, Bals S, Van Tendeloo G, D'Olieslaeger M, Wagner P, Haenen K, Boyen HG;, Journal of materials chemistry C : materials for optical and electronic devices 2, 701 (2014). http://doi.org/10.1039/c3tc31333f
Abstract: A new and facile approach is presented for generating quasi-regular patterns of transition metal-based nanoparticles on flat substrates exploiting polystyrene-block-poly2vinyl pyridine (PS-b-P2VP) micelles as intermediate templates. Direct loading of such micellar nanoreactors by polar transition metal salts in solution usually results in nanoparticle ensembles exhibiting only short range order accompanied by broad distributions of particle size and inter-particle distance. Here, we demonstrate that the use of P2VP homopolymers of appropriate length as molecular carriers to transport precursor salts into the micellar cores can significantly increase the degree of lateral order within the final nanoparticle arrays combined with a decrease in spreading in particle size. Thus, a significantly extended range of materials is now available which can be exploited to study fundamental properties at the transition from clusters to solids by means of well-organized, well-separated, size-selected metal and metal oxide nanostructures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.256
Times cited: 5
DOI: 10.1039/c3tc31333f
|
“High-mobility Bi2Se3 nanoplates manifesting quantum oscillations of surface states in the sidewalls”. Yan Y, Wang L-X, Ke X, Van Tendeloo G, Wu X-S, Yu D-P, Liao Z-M, Scientific reports 4, 3817 (2014). http://doi.org/10.1038/srep03817
Abstract: Magnetotransport measurements of topological insulators are very important to reveal the exotic topological surface states for spintronic applications. However, the novel properties related to the surface Dirac fermions are usually accompanied by a large linear magnetoresistance under perpendicular magnetic field, which makes the identification of the surface states obscure. Here, we report prominent Shubnikov-de Haas (SdH) oscillations under an in-plane magnetic field, which are identified to originate from the surface states in the sidewalls of topological insulator Bi2Se3 nanoplates. Importantly, the SdH oscillations appear with a dramatically weakened magnetoresistance background, offering an easy path to probe the surface states directly when the coexistence of surface states and bulk conduction is inevitable. Moreover, under a perpendicular magnetic field, the oscillations in Hall conductivity have peak-to-valley amplitudes of 2 e(2)/h, giving confidence to achieve a quantum Hall effect in this system. A cross-section view of the nanoplate shows that the sidewall is (015) facet dominant and therefore forms a 586 angle with regard to the top/ bottom surface instead of being perpendicular; this gives credit to the surface states' behavior as two-dimensional transport.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.259
Times cited: 31
DOI: 10.1038/srep03817
|
“Dynamic motion of Ru-polyoxometalate ions (POMs) on functionalized few-layer graphene”. Ke X, Turner S, Quintana M, Hadad C, Montellano-López A, Carraro M, Sartorel A, Bonchio M, Prato M, Bittencourt C, Van Tendeloo G;, Small 9, 3922 (2013). http://doi.org/10.1002/smll.201300378
Abstract: The interaction and stability of Ru4POM on few layer graphene via functional groups is investigated by time-dependent imaging using aberration-corrected transmission electron microscopy. The Ru4POM demonstrates dynamic motion on the graphene surface with its frequency and amplitude of rotation related to the nature of the functional group used. The stability of the Ru4POMgraphene hybrid corroborates its long-term robustness when applied to multielectronic catalytic processes.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 16
DOI: 10.1002/smll.201300378
|
“Topological surface state enhanced photothermoelectric effect in Bi2Se3 nanoribbons”. Yan Y, Liao ZM, Ke X, Van Tendeloo G, Wang Q, Sun D, Yao W, Zhou S, Zhang L, Wu HC, Yu DP;, Nano letters 14, 4389 (2014). http://doi.org/10.1021/nl501276e
Abstract: The photothermoelectric effect in topological insulator Bi2Se3 nanoribbons is studied. The topological surface states are excited to be spin-polarized by circularly polarized light. Because the direction of the electron spin is locked to its momentum for the spin-helical surface states, the photothermoelectric effect is significantly enhanced as the oriented motions of the polarized spins are accelerated by the temperature gradient. The results are explained based on the microscopic mechanisms of a photon induced spin transition from the surface Dirac cone to the bulk conduction band. The as-reported enhanced photothermoelectric effect is expected to have potential applications in a spin-polarized power source.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 51
DOI: 10.1021/nl501276e
|
“One particle@one cell : highly monodispersed PtPd bimetallic nanoparticles for enhanced oxygen reduction reaction”. Ying J, Yang X-Y, Hu Z-Y, Mu S-C, Janiak C, Geng W, Pan M, Ke X, Van Tendeloo G, Su B-L, Nano energy 8, 214 (2014). http://doi.org/10.1016/j.nanoen.2014.06.010
Abstract: Highly monodispersed platinum-based nanoalloys are the best-known catalysts for the oxygen reduction reaction. Although certainly promising, the durability and stability are among the main requirements for commercializing fuel cell electrocatalysts in practical applications. Herein, we synthesize highly stable, durable and catalytic active monodispersed PtPd nano-particles encapsulated in a unique one particle@one cell structure by adjusting the viscosity of solvents using mesocellular foam. PtPd nanoparticles in mesocellular carbon foam exhibit an excellent electrocatalytic activity (over 4 times mass and specific activities than the commercial Pt/C catalyst). Most importantly, this nanocatalyst shows no obvious change of structure and only a 29.5% loss in electrochemically active surface area after 5000 potential sweeps between 0.6 and 1.1 V versus reversible hydrogen electrode cycles. (C) 2014 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.343
Times cited: 40
DOI: 10.1016/j.nanoen.2014.06.010
|
“Towards Novel Multifunctional Pillared Nanostructures: Effective Intercalation of Adamantylamine in Graphene Oxide and Smectite Clays”. Spyrou K, Potsi G, Diamanti EK, Ke X, Serestatidou E, Verginadis II, Velalopoulou AP, Evangelou AM, Deligiannakis Y, Van Tendeloo G, Gournis D, Rudolf P;, Advanced functional materials 24, 5841 (2014). http://doi.org/10.1002/adfm.201400975
Abstract: Multifunctional pillared materials are synthesized by the intercalation of cage-shaped adamantylamine (ADMA) molecules into the interlayer space of graphite oxide (GO) and aluminosilicate clays. The physicochemical and structural properties of these hybrids, determined by X-ray diffraction (XRD), Fourier transform infrared (FTIR), Raman and X-ray photoemission (XPS) spectroscopies and transmission electron microscopy (TEM) show that they can serve as tunable hydrophobic/hydrophilic and stereospecific nanotemplates. Thus, in ADMA-pillared clay hybrids, the phyllomorphous clay provides a hydrophilic nanoenvironment where the local hydrophobicity is modulated by the presence of ADMA moieties. On the other hand, in the ADMA-GO hybrid, both the aromatic rings of GO sheets and the ADMA molecules define a hydrophobic nanoenvironment where sp(3)-oxo moieties (epoxy, hydroxyl and carboxyl groups), present on GO, modulate hydrophilicity. As test applications, these pillared nanostructures are capable of selective/stereospecific trapping of small chlorophenols or can act as cytotoxic agents.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 19
DOI: 10.1002/adfm.201400975
|
“An eco-friendly soft template synthesis of mesostructured silica-carbon nanocomposites for acid catalysis”. Zhong R, Peng L, de Clippel F, Gommes C, Goderis B, Ke X, Van Tendeloo G, Jacobs PA, Sels BF, ChemCatChem 7, 3047 (2015). http://doi.org/10.1002/cctc.201500728
Abstract: The synthesis of ordered mesoporous silica-carbon composites was explored by employing TEOS and sucrose as the silica and carbon precursor respectively, and the triblock copolymer F127 as a structure-directing agent via an evaporation-induced self-assembly (EISA) process. It is demonstrated that the synthesis procedures allow for control of the textural properties and final composition of these silica-carbon nanocomposites via adjustment of the effective SiO2/C weight ratio. Characterization by SAXS, N-2 physisorption, HRTEM, TGA, and C-13 and Si-29 solid-state MAS NMR show a 2D hexagonal mesostructure with uniform large pore size ranging from 5.2 to 7.6nm, comprising of separate carbon phases in a continuous silica phase. Ordered mesoporous silica and non-ordered porous carbon can be obtained by combustion of the pyrolyzed nanocomposites in air or etching with HF solution, respectively. Sulfonic acid groups can be readily introduced to such kind of silica-carbon nanocomposites by a standard sulfonation procedure with concentrated sulfuric acid. Excellent acid-catalytic activities and selectivities for the dimerization of styrene to produce 1,3-diphenyl-1-butene and dimerization of -methylstyrene to unsaturated dimers were demonstrated with the sulfonated materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.803
Times cited: 13
DOI: 10.1002/cctc.201500728
|
“Development of photocatalytic efficient Ti-based nanotubes and nanoribbons by conventional and microwave assisted synthesis strategies”. Ribbens S, Meynen V, Van Tendeloo G, Ke X, Mertens M, Maes BUW, Cool P, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 114, 401 (2008). http://doi.org/10.1016/j.micromeso.2008.01.028
Abstract: Titanate nanotubes were prepared via a hydrothermal treatment of TiO2 powders (Riedel De Haen) in a basic solution. Morphology and structure of the prepared samples were characterized by high resolution transmission electron microscopy (HRTEM), selected area electron diffraction (SAED), XRD, FT-Raman spectroscopy, nitrogen sorption and DSC. The photocatalytic activity was evaluated by photocatalytic oxidation of rhodamine 6G. Trititanate nanotubes (TTNT) with inner pore diameters between 4 and 4.2 nm and surface areas up till 360 m(2)/g could be synthesized. The synthesis route was modified by introduction of a calcination step, by applying a lower hydrothermal temperature and microwave irradiation in order to increase the photocatalytic activity of the porous photoactive nanotubular materials. Calcination and a softer hydrothermal treatment led to the formation of anatase without affecting the surface area and nanotubular shape of the samples. In this way, the photocatalytic activity of the original trititanate nanotubes could be significantly increased. By making use of microwave assisted synthesis, the photocatalytic activity call also be increased due to the presence of anatase. However, by applying microwave synthesis, a different structure was obtained, nanoribbons (NR) instead of nanotubcs, resulting in a decrease in surface area and porosity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY)
Impact Factor: 3.615
Times cited: 47
DOI: 10.1016/j.micromeso.2008.01.028
|
“Platinumcarbon nanotube interaction”. Bittencourt C, Hecq M, Felten A, Pireaux JJ, Ghijsen J, Felicissimo MP, Rudolf P, Drube W, Ke X, Van Tendeloo G, Chemical physics letters 462, 260 (2008). http://doi.org/10.1016/j.cplett.2008.07.082
Abstract: The interaction between evaporated Pt and pristine or oxygen-plasma-treated multiwall carbon nanotubes (CNTs) is investigated. Pt is found to nucleate at defect sites, whether initially present or introduced by oxygen plasma treatment. The plasma treatment induces a uniform dispersion of Pt nanoparticles at the CNT surface. The absence of additional features in the C 1s core level spectrum indicates that no mixed PtC phase is formed. The formation of COPt bonds at the cluster-CNT interface is suggested to reduce the electronic interaction between Pt nanoparticles and the CNT surface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 62
DOI: 10.1016/j.cplett.2008.07.082
|
“Probing the interaction between gold nanoparticles and oxygen functionalized carbon nanotubes”. Suarez-Martinez I, Bittencourt C, Ke X, Felten A, Pireaux JJ, Ghijsen J, Drube W, Van Tendeloo G, Ewels CP, Carbon 47, 1549 (2009). http://doi.org/10.1016/j.carbon.2009.02.002
Abstract: The interaction between evaporated gold and pristine or oxygen plasma treated multi-walled carbon nanotubes (MWCNTs) is investigated. Experimental and theoretical results indicate that gold nucleation occurs at defect sites, whether initially present or introduced by oxygen plasma treatment. Uniform gold cluster dispersion is observed on plasma treated carbon nanotubes (CNTs) and associated with the presence of uniformly dispersed oxidized vacancy centres on the CNT surface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.337
Times cited: 38
DOI: 10.1016/j.carbon.2009.02.002
|
“Spectroscopy and defect identification for fluorinated carbon nanotubes”. Bittencourt C, van Lier G, Ke X, Suarez-Martinez I, Felten A, Ghijsen J, Van Tendeloo G, Ewels CO, ChemPhysChem : a European journal of chemical physics and physical chemistry 10, 920 (2009). http://doi.org/10.1002/cphc.200800851
Abstract: Multi-wall carbon nanotubes (MWCNTs) were exposed to a CF4 radio-frequency (rf) plasma. High-resolution photoelectron spectroscopy shows that the treatment effectively grafts fluorine atoms onto the MWCNTs, altering the valence electronic states. Fluorine surface concentration can be tuned by varying the exposure time. Evaporation of gold onto MWCNTs is used to mark active site formation. High-resolution transmission electron microscopy coupled with density functional theory (DFT) modelling is used to characterise the surface defects formed, indicating that the plasma treatment does not etch the tube surface. We suggest that this combination of theory and microscopy of thermally evaporated gold atoms onto the CNT surface may be a powerful approach to characterise both surface defect density as well as defect type.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 14
DOI: 10.1002/cphc.200800851
|
“The role of oxygen at the interface between titanium and carbon nanotubes”. Felten A, Suarez-Martinez I, Ke X, Van Tendeloo G, Ghijsen J, Pireaux J-J, Drube W, Bittencourt C, Ewels CP, ChemPhysChem : a European journal of chemical physics and physical chemistry 10, 1799 (2009). http://doi.org/10.1002/cphc.200900193
Abstract: We study the interface between carbon nanotubes (CNTs) and surface-deposited titanium using electron microscopy and photoemission spectroscopy, supported by density functional calculations. Charge transfer from the Ti atoms to the nanotube and carbide formation is observed at the interface which indicates strong interaction. Nevertheless, the presence of oxygen between the Ti and the CNTs significantly weakens the Ti-CNT interaction. Ti atoms at the surface will preferentially bond to oxygenated sites. Potential sources of oxygen impurities are examined, namely oxygen from any residual atmosphere and pre-existing oxygen impurities on the nanotube surface, which we enhance through oxygen plasma surface pre-treatment. Variation in literature data concerning Ohmic contacts between Ti and carbon nanotubes is explained via sample pre-treatment and differing vacuum levels, and we suggest improved treatment routes for reliable Schottky barrier-free Ti-nanotube contact formation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 38
DOI: 10.1002/cphc.200900193
|
“TEM sample preparation by FIB for carbon nanotube interconnects”. Ke X, Bals S, Romo Negreira A, Hantschel T, Bender H, Van Tendeloo G, Ultramicroscopy 109, 1353 (2009). http://doi.org/10.1016/j.ultramic.2009.06.011
Abstract: A powerful method to study carbon nanotubes (CNTs) grown in patterned substrates for potential interconnects applications is transmission electron microscopy (TEM). However, high-quality TEM samples are necessary for such a study. Here, TEM specimen preparation by focused ion beam (FIB) has been used to obtain lamellae of patterned samples containing CNTs grown inside contact holes. A dual-cap Pt protection layer and an extensive 5 kV cleaning procedure are applied in order to preserve the CNTs and avoid deterioration during milling. TEM results show that the inner shell structure of the carbon nanotubes has been preserved, which proves that focused ion beam is a useful technique to prepare TEM samples of CNT interconnects.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 21
DOI: 10.1016/j.ultramic.2009.06.011
|
“Molecular sieve properties of mesoporous silica with intraporous nanocarbon”. de Clippel F, Harkiolakis A, Ke X, Vosch T, Van Tendeloo G, Baron GV, Jacobs PA, Denayer JFM, Sels BF, Chemical communications 46, 928 (2010). http://doi.org/10.1039/b918864a
Abstract: Biporous carbonsilica materials (CSM) with molecular sieve properties and high sorption capacity were developed by synthesizing nano-sized carbon crystallites in the mesopores of Al-MCM-41.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 21
DOI: 10.1039/b918864a
|
“Preparation of sulfonated ordered mesoporous carbon and its use for the esterification of fatty acids”. Peng L, Philippaerts A, Ke X, van Noyen J, de Cleppel F, Van Tendeloo G, Jacobs PA, Sels BF, Catalysis today 150, 140 (2010). http://doi.org/10.1016/j.cattod.2009.07.066
Abstract: Mesoporous carbon, which can be replicated from mesoporous silica and whose surface is hydrophobic, can be an ideal catalyst for the esterification of fatty acids. Here we report an easy and low cost way to prepare sulfonic acid group-functionalized mesoporous carbon. A sample of calcined mesoporous silica SBA-15 was added to an aqueous sucrose solution followed by drying and calcination at different temperatures. In contrast to existing procedures, the obtained hybrid Si/C material was then first sulfonated in H2SO4, before the final removal of the silica template in order to stabilize the porous structure towards the liquid phase sulfonation treatment. Thus the silicacarbon composites, instead of the mesoporous carbon, were successfully sulfonated to introduce SO3H groups, while keeping the ordered mesoporous structure intact. The influence of carbonization temperature was investigated, suggesting an optimum temperature of 873 K. The SO3H group-functionalized mesoporous carbon, denoted as CMK-3-873-SO3H, was characterized by means of XRD, N2 physisorption, SEM, FT-IR, elemental analysis and TEM. It followed that a uniform mesoporous carbon was obtained with an average pore size of 3.89 nm, a specific surface of 807 m2/g and a SO3H group loading of 0.39 meq/g of dry material. Compared with other solid acid catalysts, the resulting material shows enhanced activity in the acid-catalyzed esterification of oleic acid with methanol, and can be used repeatedly. The increased catalytic performance is attributed to the hydrophobic surface and larger pore size of the new catalyst. It can effectively accommodate long chain fatty acids and reject formed water, making the active sites easily accessible.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.636
Times cited: 132
DOI: 10.1016/j.cattod.2009.07.066
|
“Three-dimensional analysis of carbon nanotube networks in interconnects by electron tomography without missing wedge artifacts”. Ke X, Bals S, Cott D, Hantschel T, Bender H, Van Tendeloo G, Microscopy and microanalysis 16, 210 (2010). http://doi.org/10.1017/S1431927609991371
Abstract: The three-dimensional (3D) distribution of carbon nanotubes (CNTs) grown inside semiconductor contact holes is studied by electron tomography. The use of a specialized tomography holder results in an angular tilt range of ±90°, which means that the so-called missing wedge is absent. The transmission electron microscopy (TEM) sample for this purpose consists of a micropillar that is prepared by a dedicated procedure using the focused ion beam (FIB) but keeping the CNTs intact. The 3D results are combined with energy dispersive X-ray spectroscopy (EDS) to study the relation between the CNTs and the catalyst particles used during their growth. The reconstruction, based on the full range of tilt angles, is compared with a reconstruction where a missing wedge is present. This clearly illustates that the missing wedge will lead to an unreliable interpretation and will limit quantitative studies
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 42
DOI: 10.1017/S1431927609991371
|
“Study of the interface between rhodium and carbon nanotubes”. Suarez-Martinez I, Ewels CP, Ke X, Van Tendeloo G, Thiess S, Drube W, Felten A, Pireaux J-J, Ghijsen J, Bittencourt C, ACS nano 4, 1680 (2010). http://doi.org/10.1021/nn9015955
Abstract: X-ray photoelectron spectroscopy at 3.5 keV photon energy, in combination with high-resolution transmission electron microscopy, is used to follow the formation of the interface between rhodium and carbon nanotubes. Rh nucleates at defect sites, whether initially present or induced by oxygen-plasma treatment. More uniform Rh cluster dispersion is observed on plasma-treated CNTs. Experimental results are compared to DFT calculations of small Rh clusters on pristine and defective graphene. While Rh interacts as strongly with the carbon as Ti, it is less sensitive to the presence of oxygen, suggesting it as a good candidate for nanotube contacts.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 26
DOI: 10.1021/nn9015955
|
“Measuring point defect density in individual carbon nanotubes using polarization-dependent X-ray microscopy”. Felten A, Gillon X, Gulas M, Pireaux J-J, Ke X, Van Tendeloo G, Bittencourt C, Najafi E, Hitchcock AP, ACS nano 4, 4431 (2010). http://doi.org/10.1021/nn1002248
Abstract: The presence of defects in carbon nanotubes strongly modifies their electrical, mechanical, and chemical properties. It was long thought undesirable, but recent experiments have shown that introduction of structural defects using ion or electron irradiation can lead to novel nanodevices. We demonstrate a method for detecting and quantifying point defect density in individual carbon nanotubes (CNTs) based on measuring the polarization dependence (linear dichroism) of the C 1s → π* transition at specific locations along individual CNTs with a scanning transmission X-ray microscope (STXM). We show that STXM can be used to probe defect density in individual CNTs with high spatial resolution. The quantitative relationship between ion dose, nanotube diameter, and defect density was explored by purposely irradiating selected sections of nanotubes with kiloelectronvolt (keV) Ga+ ions. Our results establish polarization-dependent X-ray microscopy as a new and very powerful characterization technique for carbon nanotubes and other anisotropic nanostructures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 26
DOI: 10.1021/nn1002248
|
“From polyester grafting onto POSS nanocage by ring-opening polymerization to high performance polyester/POSS nanocomposites”. Goffin A-L, Duquesne E, Raquez J-M, Miltner HE, Ke X, Alexandre M, Van Tendeloo G, van Mele B, Dubois P, Journal of materials chemistry 20, 9415 (2010). http://doi.org/10.1039/c0jm00283f
Abstract: Polyester-grafted polyhedral oligomeric silsesquioxane (POSS) nanohybrids selectively produced by ring-opening polymerization of ε-caprolactone and L,L-lactide (A.-L. Goffin, E. Duquesne, S. Moins, M. Alexandre, Ph. Dubois, Eur. Polym. Journal, 2007, 43, 4103) were studied as masterbatches by melt-blending within their corresponding commercial polymeric matrices, i.e., poly(ε-caprolactone) (PCL) and poly(L,L-lactide) (PLA). For the sake of comparison, neat POSS nanoparticles were also dispersed in PCL and PLA. The objective was to prepare aliphatic polyester-based nanocomposites with enhanced crystallization behavior, and therefore, enhanced thermo-mechanical properties. Wide-angle X-ray scattering and transmission electron microscopy attested for the dispersion of individualized POSS nanoparticles in the resulting nanocomposite materials only when the polyester-grafted POSS nanohybrid was used as a masterbatch. The large impact of such finely dispersed (grafted) nanoparticles on the crystallization behavior for the corresponding polyester matrices was noticed, as evidenced by differential scanning calorimetry analysis. Indeed, well-dispersed POSS nanoparticles acted as efficient nucleating sites, significantly increasing the crystallinity degree of both PCL and PLA matrices. As a result, a positive impact on thermo-mechanical properties was highlighted by dynamic mechanical thermal analysis.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 42
DOI: 10.1039/c0jm00283f
|
Ke X (2010) From top-down to bottom-up : from carbon nanotubes to nanodevices. Antwerpen
Keywords: Doctoral thesis; Electron microscopy for materials research (EMAT)
|
“A cyclic catalyst pretreatment in CO2 for high yield production of Carbon nanofibers with narrow diameter distribution”. Corthals S, van Noyen J, Liang D, Ke X, Van Tendeloo G, Jacobs P, Sels B, Catalysis letters 141, 1621 (2011). http://doi.org/10.1007/s10562-011-0690-3
Abstract: This paper presents a cyclic catalyst pretreatment process to improve the CNF yield with narrow size distribution by sequentially feeding the CVD reactor with CH4/CO2 mixtures (carbon deposition) and CO2 (carbon removal) prior to the actual growth process. A mechanism based on a break-up of large Ni particles tentatively explains the beneficial effect of the cyclic carbon deposition/removal CVD procedure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.799
Times cited: 1
DOI: 10.1007/s10562-011-0690-3
|