Abstract: The optical properties of PbSe/CdSe core/shell quantum dots with core sizes smaller than 4 nm in the 5300 K range are reported. The photoluminescence spectra show two peaks, which become increasingly separated in energy as the core diameter is reduced below 4 nm. It is shown that these peaks are due to intrinsic exciton transitions in each quantum dot, rather than emission from different quantum dot sub-ensembles. Most likely, the energy separation between the peaks is due to inter-valley coupling between the L-points of PbSe. The temperature dependence of the relative intensities of the peaks implies that the two emitting states are not in thermal equilibrium and that dark exciton states must play an important role.

Abstract: The main purpose of this research is to manage simultaneous measurement of velocity and concentration in large cross-sections by recording and processing images of cloud structures to provide more detailed information for e.g. validation of CFD simulations. Dispersion from an isolated stack in an Atmospheric Boundary Layer (ABL) was chosen as the test case and investigated both experimentally and numerically in a wind tunnel. Large Scale-Particle Image Velocimetry (LS-PIV), which records cloud structures instead of individual particles, was used to obtain the velocity field in a vertical plane. The concentration field was determined by two methods: Aspiration Probe (AP) measurements and Light Scattering Technique (LST). In the latter approach, the same set of images used in the LS-PIV was employed. The test case was also simulated using the CFD solver FLUENT 6.3. Comparison between AP measurements and CFD revealed that there is good agreement when using a turbulent Schmidt number of 0.4. For the LST measurements, a non-linear relation between concentration and light intensity was observed and a hyperbolic-based function is proposed as correction function. After applying this correction function, a close agreement between CFD and LST measurements is obtained. (C) 2009 Elsevier Ltd. All rights reserved.

Abstract: The effect of the oxygen plasma treatment on the electronic states of multi-wall carbon nanotubes (MWCNTs) is analyzed by X-ray photoemission measurements (XPS) and UPS, both using synchrotron radiation. It is found that the plasma treatment effectively grafts oxygen at the CNT-surface. Thereafter, the interaction between evaporated Pd and pristine or oxygen plasma-treated MWCNTs is investigated. Pd is found to nucleate at defective sites, whether initially present or introduced by oxygen plasma treatment. The plasma treatment induced a uniform dispersion of Pd clusters at the CNT-surface. The absence of additional features in the Pd 3d and C I s core levels spectra testifies that no Pd-C bond is formed. The shift of the Pd 3d core level towards high-binding energy for the smallest clusters is attributed to the Coulomb energy of the charged final state. (C) 2008 Elsevier Ltd. All rights reserved.

Abstract: Dislocation microstructures have been characterized by transmission electron microscopy in polycrystalline coesite deformed experimentally at 4 GPa, 1200 degrees C. Burgers vectors have been determined by large-angle convergent-beam electron diffraction. Sample orientation was assisted by precession electron diffraction to overcome difficulties arising from pseudo-hexagonal symmetry. The results are explained by using a pseudo-hexagonal setting. We found that most dislocations observed are of the 1/3 < 2 (1) over bar(1) over bar0 > type. No clear glide plane was identified, suggesting that climb is activated under these conditions. This conclusion is supported by the observation of numerous subgrain boundaries. We have also observed some [00011 dislocations. Finally, the C12/cl space group to which coesite belongs being centred, an additional slip system is observed: 1/6[(1) over bar2 (1) over bar3](01 (1) over bar1) (1/2[(1) over bar 10](110) in the monoclinic setting).

Abstract: We report a microstructural and compositional study of a 90% Pb(Mg1/3Nb2/3)O-3 – 10% PbTiO3 ceramic sample. High resolution transmission electron microscopy (HRTEM) revealed the presence of compositional ordered nano-domains (1 – 4 mn), observable in two specific orientations, [0 (1) over bar 1] and [1 1 (2) over bar]. However, the visibility and the ordering degree of the nano-domains on the HRTEM images are not at all obvious. Fourier filtering of the images clearly revealed the ordered domains. Antiphase boundaries lying in the (111) planes separate them, while (100) and (111) facets separate the ordered domains from the disordered matrix. Their shape is plate-like, not uniformly spread in the disordered matrix. Their average size varies in different regions of the sample, most probably due to a non-uniform distribution of Ti, as observed by energy dispersive X-ray spectroscopy. (c) 2007 WILEY-VCH Verlag GmbH Co. KGaA, Weinheim.

Abstract: Samples of transparent glass-ceramics in the ternary system Li2O-Al2O3-SiO2 (LAS), with Er2O3 as a luminescent dopant, are investigated. The initial glass is obtained by the classical melting technique. In order to induce ceramization of the glass, TiO2 and ZrO2 are added in small amount as nucleating agents. The thermal treatments at 730 and 770 degrees C are carried out to promote formation of titanium zirconate solid solution precipitates. The spatial distribution of the precipitates in the material, their morphology, and their composition are investigated with TEM, HRTEM, HAADF-STEM, EELS and EFTEM. The results demonstrate that with the glass-melting preparation technique it is possible to achieve small nanoparticles with uniform distribution and higher number density than with the sol-gel glass preparation.

Abstract: Transmission electron microscopy has been applied to study Ti and Al/Ti contacts on GaN and AlGaN/GaN as a function of annealing temperature. This has lead to a profound understanding of the role of Al, both in the contact formation on n-GaN and on AlGaN/GaN. Al in the AlGaN decreases the N-extraction by Ti out of the nitride, because of the strong Al-N bond. Al in the metal bilayer also reduces the N-extraction by Ti due to a preferential alloy mixing.

Abstract: Tetrahedral chain ordering in the Sr2MnGaO5 structure is studied using electron diffraction (ED) and high-resolution electron microscopy. The ED patterns show the presence of satellite reflections, which indicate a commensurately modulated structure with a = 5.4056(8) Angstrom b 16.171(3) Angstrom, c = 5.5592(7) Angstrom, q – 1/2c*, superspace group Immma(00gamma,)s00. The Superstructure arises due to ordering of the two types of symmetry related tetrahedral chains (L and R) according to a ... LRLR ... sequence, where L and R chains alternate along the c-axis within the same (GaO) layer. Numerous defects at different structural levels were observed, comprising interleaving L and R chains, violation of the ... LRLR ... chain sequence within one layer, different stacking modes of the ... LRLR ... ordered layers with subsequent alternation of blocks of different width along the h-axis of the brownmillerite subcell and island fragmentation of the modulated superstructure. By in situ heating ED experiments it is found that the long-range ordering of the tetrahedral chains is stable tip to 665degreesC and is completely suppressed at 905degreesC. (C) 2003 Elsevier Inc. All rights reserved.

Abstract: High-resolution transmission electron microscopy was performed on compacted Ni(3)Al nanostructured material prepared by the inert gas condensation technique. From electron diffraction data an incomplete L1(2) ordering of the crystallites is observed in the free particles as well as in the room temperature compacted samples. However, a completely ordered L1(2) structure with much bigger and well-defined crystallites exhibiting several defects is observed in material compacted and annealed at 773 K. Sharp crystallite boundaries as well as amorphous material and voids are observed in between crystallites in all samples, the former being dominant in the annealed material, the latter in the as-prepared one.

Abstract: Nickel foams were used as catalysts to dissociate acetylene and deposit carbon atoms. Graphite nanofibers with distinct structures were developed at 550degreesC with nickel foams pretreated with hydrogen. HREM observations showed that the graphite layers of the nanofibers were aligned at a certain angle to the fiber axis. It is suggested that hydrogen treatment and metal catalysts have a tremendous impact on the yields and microstructures of the graphite nanofibers. The growth mechanism of these fish-bone graphite nanofibers is also discussed.

Abstract: The use of an energy-filtering held emission gun transmission electron microscope (CM30 FEG Ultratwin) allows, apart from imaging morphologies down to nanometer scale, the fast acquisition of high-resolution element distributions. Electrons that have lost energy corresponding to characteristic inner-shell loss edges are used to form the element maps. The production of Ultra Large-Scale Integration (ULSI) devices with dimensions below 0.25 mum requires among others the formation of a multilayer metallization scheme by means of repeatedly applying the deposition and etching of dielectrics and metals. In this work the evolution of the surface chemical species on etched Al lines in a post-etch cleaning process has been investigated by energy filtering transmission electron microscopy, with the aim to understand the role of each process step on the removal of the etching residues. (C) 2001 Elsevier Science Ltd. All rights reserved.

Abstract: The early growth stages of chemical vapor deposition (CVD) diamond on a solgel TiO2 film with buried ultra dispersed diamond seeds (UDD) have been studied. In order to investigate the diamond growth mechanism and understand the role of the TiO2 layer in the growth process, high resolution transmission electron microscopy (HRTEM), energy-filtered TEM and electron energy loss spectroscopy (EELS) techniques were applied to cross sectional diamond film samples. We find evidence for the formation of TiC crystallites inside the TiO2 layer at different diamond growth stages. However, there is no evidence that diamond nucleation starts from these crystallites. Carbon diffusion into the TiO2 layer and the chemical bonding state of carbon (sp2/sp3) were both extensively investigated. We provide evidence that carbon diffuses through the TiO2 layer and that the diamond seeds partially convert to amorphous carbon during growth. This carbon diffusion and diamond to amorphous carbon conversion make the seed areas below the TiO2 layer grow and bend the TiO2 layer upwards to form the nucleation center of the diamond film. In some of the protuberances a core of diamond seed remains, covered by amorphous carbon. It is however unlikely that the remaining seeds are still active during the growth process.

Abstract: The local and average crystal structures and magnetic properties of the oxygen-deficient perovskite Sr2Fe1.5Cr0.5O5+y were studied using powder X-ray and neutron diffraction, neutron-pair distribution function analysis, and electron energy-loss spectroscopy. This material crystallizes in the cubic Pm3̅m space group, with a = 3.94491(14) Å. The oxygen vacancies are distributed randomly throughout the perovskite-type structure, and the average coordination number of the Fe(Cr) sites is 5. Refinement of the neutron diffraction data indicates y 0.05. This is in discordance with an earlier report on a material with the same nominal composition and cell constant. Electron energy-loss Cr L2,3-edge spectroscopy shows that Cr3+ is present, which is also contrary to previous speculation. Neutron-pair distribution function studies show that a brownmillerite-like model involving ordered vacancies and alternating octahedral and tetrahedral coordination at the metal sites, gives a better description of the local structure out to 5 Å. A remarkable phenomenon determined by neutron diffraction in Sr2Fe1.5Cr0.5O5 is the occurrence of a long-range G-type antiferromagnetic ordering with Tc ≈ 565 K because cubic oxygen-deficient perovskites with B-site disorder usually do not undergo transitions to magnetically ordered states. The observation of long-range antiferromagnetic order and the Tc value are in accordance with previous Mössbauer spectroscopic studies.

Abstract: We have investigated the magnetic depth profile of an epitaxial Fe3O4 thin film grown directly on a semiconducting ZnO substrate by soft x-ray resonant magnetic reflectometry (XRMR) and electron energy loss spectroscopy (EELS). Consistent chemical profiles at the interface between ZnO and Fe3O4 are found from both methods. Valence selective EELS and XRMR reveal independently that the first monolayer of Fe at the interface between ZnO and Fe3O4 contains only Fe3+ ions. Besides this narrow 2.5 Å interface layer, Fe3O4 shows magnetic bulk properties throughout the whole film making highly efficient spin injection in this system feasible.