Abstract: Multiwall carbon nanotubes are produced by decomposition of acetylene at 600 degreesC on metal catalysts supported on NaY zeolite. The support and the metal are eliminated by dissolving them in aqueous hydrofluoric acid (HF). Two methods were used to eliminate the pyrolitic carbon: oxidation in air at 500 degreesC and oxidation by potassium permanganate in acidic solution at 70 degreesC. The progress and efficacy of the purification methods are verified by TEM. The properties of the purified multiwalled carbon nanotubes are probed using C-13 and Xe-129 NMR spectroscopy under continuous-flow optical-pumping conditions. Xenon is shown to penetrate the interior of the nanotubes. A distribution of inner tube diameters gives rise to chemical shift dispersion. When the temperature is lowered, an increasing fraction of xenon resides inside the nanotubes and is not capable of exchanging with xenon in the interparticle space. In the case of the permanganate-oxidized sample, rapid xenon relaxation is attributed to interaction with residual MnO2 nanoparticles in the interior of the tubes.

Abstract: Not much about the effect of thiocyanate addition on the sulphur ripening is known, although it is used for many applications in photographic practice. Via a combination of tracer analysis and diffuse reflectance spectroscopy the effect of thiocyanate addition on the sulphur and sulphur-plus-gold ripening could be unveiled. When thiocyanate is added prior to the sulphur addition, it appears to rearrange the silver halide surface in such way that the sulphur deposition rate is enhanced, but the supply of interstitials is limited. Addition of thiocyanate after the sulphur reaction results in the formation of thiocyanate complexes with silver, from which a silver ion is more easily deposited in a surface cell of the silver sulphide clusters thus enhancing the sensitization rate. For sulphur-plus-gold sensitized emulsions it was observed that part of the gold ions could be removed out of the Ag2-xAuxS clusters by addition of thiocyanate ions and subsequent washing. Hence, it was concluded that two different types of gold ions are present in the silver sulphide clusters; 1. gold ions which are substitutional for silver (bound between sulphur and bromide ions) 2. gold ions which bridge two or three sulphur atoms. Incorporation of gold ions into silver sulphide clusters suppresses their optical absorption in diffuse reflectance spectroscopy. Since the optical absorption at 505 nm can completely be restored by addition of thiocyanate, it is assumed that the entity absorbing at this wavelength is a monomer of silver sulphide.

Abstract: Defects in AgG tabular crystals with {111} surfaces are characterised by transmission electron microscopy (TEM) and their influence on the growth process is discussed. In the tabular crystals, twins parallel to the tabular face as well as dislocations along different directions are observed. The twins induce the tabular growth, while the dislocations do not influence the morphology. In 10 to 30% of the crystals that have been characterised, thickness growth is observed and it is shown that in all cases twins on other planes than the tabular ones are present. Two configurations occur more frequently and are analysed in detail. For the first group, twins parallel to the tabular face as well as a microtwin along a non-parallel {111} plane and ending inside the crystal are present. In the crystals of the second group only one extra non-parallel twin occurs giving rise to a bicrystal built up by a tetrahedral shaped part and a flat triangular or trapezoidal part. More complex twin configurations give rise to various, less characteristic morphologies.