“Aberration-corrected microscopy and spectroscopy analysis of pristine, nitrogen containing detonation nanodiamond”. Turner S, Shenderova O, da Pieve F, Lu Y-G, Yücelen E, Verbeeck J, Lamoen D, Van Tendeloo G, Physica status solidi : A : applications and materials science 210, 1976 (2013). http://doi.org/10.1002/pssa.201300315
Abstract: Aberration-corrected transmission electron microscopy, electron energy-loss spectroscopy, and density functional theory (DFT) calculations are used to solve several key questions about the surface structure, the particle morphology, and the distribution and nature of nitrogen impurities in detonation nanodiamond (DND) cleaned by a recently developed ozone treatment. All microscopy and spectroscopy measurements are performed at a lowered acceleration voltage (80/120kV), allowing prolonged and detailed experiments to be carried out while minimizing the risk of knock-on damage or surface graphitization of the nanodiamond. High-resolution TEM (HRTEM) demonstrates the stability of even the smallest nanodiamonds under electron illumination at low voltage and is used to image the surface structure of pristine DND. High resolution electron energy-loss spectroscopy (EELS) measurements on the fine structure of the carbon K-edge of nanodiamond demonstrate that the typical * pre-peak in fact consists of three sub-peaks that arise from the presence of, amongst others, minimal fullerene-like reconstructions at the nanoparticle surfaces and deviations from perfect sp(3) coordination at defects in the nanodiamonds. Spatially resolved EELS experiments evidence the presence of nitrogen within the core of DND particles. The nitrogen is present throughout the whole diamond core, and can be enriched at defect regions. By comparing the fine structure of the experimental nitrogen K-edge with calculated energy-loss near-edge structure (ELNES) spectra from DFT, the embedded nitrogen is most likely related to small amounts of single substitutional and/or A-center nitrogen, combined with larger nitrogen clusters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.775
Times cited: 37
DOI: 10.1002/pssa.201300315
|
|
|
“Carbon-dot-decorated nanodiamonds”. Shenderova O, Hens S, Vlasov I, Turner S, Lu Y-G, Van Tendeloo G, Schrand A, Burikov SA, Dolenko TA, Particle and particle systems characterization 31, 580 (2014). http://doi.org/10.1002/ppsc.201300251
Abstract: The synthesis of a new class of fluorescent carbon nanomaterials, carbon-dot-decorated nanodiamonds (CDD-ND), is reported. These CDD-NDs are produced by specific acid treatment of detonation soot, forming tiny rounded sp2 carbon species (carbon dots), 12 atomic layers thick and 12 nm in size, covalently attached to the surface of the detonation diamond nanoparticles. A combination of nanodiamonds bonded with a graphitic phase as a starting material and the application of graphite intercalated acids for oxidation of the graphitic carbon is necessary for the successful production of CDD-ND. The CDD-ND photoluminescence (PL) is stable, 20 times more intense than the intrinsic PL of well-purified NDs and can be tailored by changing the oxidation process parameters. Carbon-dot-decorated DNDs are shown to be excellent probes for bioimaging applications and inexpensive additives for PL nanocomposites.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.474
Times cited: 30
DOI: 10.1002/ppsc.201300251
|
|
|
“Nanodiamond-based nanolubricants : investigation of friction surfaces”. Shenderova O, Vargas A, Turner S, Ivanov DM, Ivanov MG, Tribology transactions 57, 1051 (2014). http://doi.org/10.1080/10402004.2014.933933
Abstract: Synergistic compositions of detonation nanodiamond (DND) particles with polytetrafluoroethylene and molybdenum dialkyldithiophosphate were used in ring-on-ring, four-ball, and block-on-ring tests as an additive to polyalphaolefins and engine oils. Modest to significant reductions in the friction coefficients, wear, or both were observed. In the wear scars produced in the block-on-ring tests, the friction surfaces were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and profilometry. Significant polishing effects of the friction surfaces in lubricants containing DND were revealed in SEM observations and roughness measurements. The roughness of the scar surfaces produced in the presence of DND additives was about 35% lower than the roughness of the scars observed in pure oil experiments.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.685
Times cited: 23
DOI: 10.1080/10402004.2014.933933
|
|
|
“Determination of size, morphology, and nitrogen impurity location in treated detonation nanodiamond by transmission electron microscopy”. Turner S, Lebedev OI, Shenderova O, Vlasov II, Verbeeck J, Van Tendeloo G, Advanced functional materials 19, 2116 (2009). http://doi.org/10.1002/adfm.200801872
Abstract: Size, morphology, and nitrogen impurity location, all of which are all thought to be related to the luminescent properties of detonation nanodiamonds, are determined in several detonation nanodiamond samples using a combination of transmission electron microscopy techniques. Results obtained from annealed and cleaned detonation nanodiamond samples are compared to results from conventionally purified detonation nanodiamond. Detailed electron energy loss spectroscopy combined with model-based quantification provides direct evidence for the sp3 like embedding of nitrogen impurities into the diamond cores of all the studied nanodiamond samples. Simultaneously, the structure and morphology of the cleaned detonation nanodiamond particles are studied using high resolution transmission electron microscopy. The results show that the size and morphology of detonation nanodiamonds can be modified by temperature treatment and that by applying a special cleaning procedure after temperature treatment, nanodiamond particles with clean facets almost free from sp2 carbon can be prepared. These clean facets are clear evidence that nanodiamond cores are not necessarily in coexistence with a graphitic shell of non-diamond carbon.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 100
DOI: 10.1002/adfm.200801872
|
|
|
“Nitrogen and luminescent nitrogen-vacancy defects in detonation nanodiamond”. Vlasov II, Shenderova O, Turner S, Lebedev OI, Basov AA, Sildos I, Rähn M, Shiryaev AA, Van Tendeloo G, Small 6, 687 (2010). http://doi.org/10.1002/smll.200901587
Abstract: An efficient method to investigate the microstructure and spatial distribution of nitrogen and nitrogen-vacancy (N-V) defects in detonation nanodiamond (DND) with primary particle sizes ranging from approximately 3 to 50 nm is presented. Detailed analysis reveals atomic nitrogen concentrations as high as 3 at% in 50% of diamond primary particles with sizes smaller than 6 nm. A non-uniform distribution of nitrogen within larger primary DND particles is also presented, indicating a preference for location within the defective central part or at twin boundaries. A photoluminescence (PL) spectrum with well-pronounced zero-phonon lines related to the N-V centers is demonstrated for the first time for electron-irradiated and annealed DND particles at continuous laser excitation. Combined Raman and PL analysis of DND crystallites dispersed on a Si substrate leads to the conclusion that the observed N-V luminescence originates from primary particles with sizes exceeding 30 nm. These findings demonstrate that by manipulation of the size/nitrogen content in DND there are prospects for mass production of nanodiamond photoemitters based on bright and stable luminescence from nitrogen-related defects.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 84
DOI: 10.1002/smll.200901587
|
|
|
“Surface chemistry and properties of ozone-purified detonation nanodiamonds”. Shenderova O, Koscheev A, Zaripov N, Petrov I, Skryabin Y, Detkov P, Turner S, Van Tendeloo G, The journal of physical chemistry: C : nanomaterials and interfaces 115, 9827 (2011). http://doi.org/10.1021/jp1102466
Abstract: Nanodiamond from ozone purification (NDO) demonstrates very distinctive properties within the class of detonation nanodiamonds, namely very high acidity and high colloidal stability in a broad pH range. To understand the origin of these unusual properties of NDO, the nature of the surface functional groups formed during detonation soot oxidation by ozone needs to be revealed. In this work, thermal desorption mass spectrometry (TDMS) and IR spectroscopy were used for the identification of surface groups and it was concluded that carboxylic anhydride groups prevail on the NDO surface. On the basis of the temperature profiles of the desorbed volatile products and their mass balance, it is hypothesized that decomposition of carboxylic anhydride groups from NDO during heating proceeds by two different mechanisms. Other distinctive features of NDO in comparison with air-treated nanodiamond are also reported.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 105
DOI: 10.1021/jp1102466
|
|
|
“Nitrogen control in nanodiamond produced by detonation shock-wave-assisted synthesis”. Shenderova OA, Vlasov II, Turner S, Van Tendeloo G, Orlinskii SB, Shiryaev AA, Khomich AA, Sulyanov SN, Jelezko F, Wrachtrup J, The journal of physical chemistry: C : nanomaterials and interfaces 115, 14014 (2011). http://doi.org/10.1021/jp202057q
Abstract: Development of efficient production methods of nanodiamond (ND) particles containing substitutional nitrogen and nitrogen-vacancy (NV) complexes remains an important goal in the nanodiamond community. ND synthesized from explosives is generally not among the preferred candidates for imaging applications owing to lack of optically active particles containing NV centers. In this paper, we have systematically studied representative classes of NDs produced by detonation shock wave conversion of different carbon precursor materials, namely, graphite and a graphite/hexogen mixture into ND, as well as ND produced from different combinations of explosives using different cooling methods (wet or dry cooling). We demonstrate that (i) the N content in nanodiamond particles can be controlled through a correct selection of the carbon precursor material (addition of graphite, explosives composition); (ii) particles larger than approximately 20 nm may contain in situ produced optically active NV centers, and (iii) in ND produced from explosives, NV centers are detected only in ND produced by wet synthesis. ND synthesized from a mixture of graphite/explosive contains the largest amount of NV centers formed during synthesis and thus deserves special attention.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 54
DOI: 10.1021/jp202057q
|
|
|
“Identification of substitutional nitrogen and surface paramagnetic centers in nanodiamond of dynamic synthesis by electron paramagnetic resonance”. Orlinskii SB, Bogomolov RS, Kiyamova AM, Yavkin BV, Mamin GM, Turner S, Van Tendeloo G, Shiryaev AA, Vlasov II, Shenderova O, Nanoscience and nanotechnology letters 3, 63 (2011). http://doi.org/10.1166/nnl.2011.1121
Abstract: Production of nanodiamond particles containing substitutional nitrogen is important for a wide variety of advanced applications. In the current work nanodiamond particles synthesized from a mixture of graphite and hexogen were analyzed to determine the presence of substitutional nitrogen using pulsed electron paramagnetic resonance (EPR) spectroscopy. Nitrogen paramagnetic centers in the amount of 1.2 ppm have been identified. The spin relaxation characteristics for both nitrogen and surface defects are also reported. A new approach for efficient depletion of the strong non-nitrogen EPR signal in nanodiamond material by immersing nanodiamond particles into ice matrix is suggested. This approach allows an essential decrease of the spin relaxation time of the dominant non-nitrogen defects, while preserving the substitutional nitrogen spin relaxation time.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.889
Times cited: 14
DOI: 10.1166/nnl.2011.1121
|
|
|
“Producing photoluminescent species from Sp2 carbons”. Hens SC, Shenderova O, Turner S, Fullerenes, nanotubes, and carbon nanostructures 20, 502 (2012). http://doi.org/10.1080/1536383X.2012.655667
Abstract: The treatment of sp2 carbon materials, including micrographite, nanographite, HOPG, onion-like-carbon, and single-walled carbon nanotubes, in a 3:1 sulfuric to nitric acid mixture produced photoluminescent reaction solutions. These colloidal, aqueous solutions appeared photoluminescently stable under a UV lamp and ranged in color from red to blue. The photoluminescent wavelength shifted to shorter wavelength with increasing reaction time or increasing reaction temperature. Raman spectroscopy showed evidence of defect structures in graphitic residue, and transmission electron microscopy showed unusual structures present in the supernatant including graphitic balls.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.35
Times cited: 4
DOI: 10.1080/1536383X.2012.655667
|
|