Abstract: The rational synthesis, comprehensive characterization, and mechanical and micromechanical properties of a calcium phosphate cement are presented. Hydroxyapatite cement biomaterial was synthesized from reactive sub-micrometer-sized dicalcium phosphate dihydrate and tetracalcium phosphate via a dissolution-precipitation reaction using water as the liquid phase. As a result nanostructured, Ca-deficient and carbonated B-type hydroxyapatite is formed. The cement shows good processibility, sets in 22 ± 2 min and entirely transforms to the end product after 6 h of setting reaction, one of the highest conversion rates among previously reported for calcium phosphate cements based on dicalcium and tetracalcium phosphates. The combination of all elucidated physical-chemical traits leads to an essential bioactivity and biocompatibility of the cement, as revealed by in vitro acellular simulated body fluid and cell culture studies. The compressive strength of the produced cement biomaterial was established to be 25 ± 3 MPa. Furthermore, nanoindentation tests were performed directly on the cement to probe its local elasticity and plasticity at sub-micrometer/micrometer level. The measured elastic modulus and hardness were established to be Es = 23 ± 3.5 and H = 0.7 ± 0.2 GPa, respectively. These values are in close agreement with those reported in literature for trabecular and cortical bones, reflecting good elastic and plastic coherence between synthesized cement biomaterial and human bones.

Abstract: The Zn-carboxylate-based porous coordination polymer MOF-5 [Zn4O(bdc)3] and the metal oxide loaded materials ZnO@MOF-5 and TiO2@MOF-5 were loaded in a second step with the precursor [ClAuCO] to yield intermediate materials denoted as [ClAuCO]@MOF-5, [ClAuCO]/ZnO@MOF-5 and [ClAuCO]/TiO2@MOF-5. These composites were decomposed to Au@MOF-5, Au/ZnO@MOF-5 and Au/TiO2@MOF-5 under hydrogen at 100 °C. The nanoparticle-loaded hybrid materials were characterised by powder X-ray diffraction (PXRD), IR spectroscopy, X-ray photoelectron spectroscopy (XPS) and N2 sorption measurements, which reveal an intact MOF-5 structure that maintains a high specific surface area. For Au@MOF-5, crystalline Au nanoparticles were distributed over the MOF matrix in a homogeneous fashion with a size of ca. 13 nm, evidenced by high resolution transmission electron microscopy. In the case of Au/ZnO@MOF-5, the Au and metal oxide particles of a few nm in size were coexistent in a given volume of the MOF-5 matrix and were not separated in different crystalline MOF particles. For the TiO2 loaded materials the oxide is preferentially located near the outer surface of the MOF particles, leading to an increase of larger exterior Au particles in comparison to very small interior Au particles as observed for the other materials. Au@MOF-5, Au/ZnO@MOF-5 and Au/TiO2@MOF-5 were tested in liquid-phase oxidation of alcohols. Preliminary results show a high activity for the Au loaded materials in this reaction. This observation is attributed to the microstructure of the composites with very small Au particles distributed homogeneously over the MOF matrix.

Abstract: 'Colossal magnetoresistance' in perovskite manganites such as La0.7Ca0.3MnO3 (LCMO), is caused by the interplay of ferro-paramagnetic, metal-insulator and structural phase transitions. Moreover, different electronic phases can coexist on a very fine scale resulting in percolative electron transport. Here we report on (LCMO)(1-x):(MgO)(x) (0 < x less than or equal to 0.8) epitaxial nano-composite films in which the structure and magnetotransport properties of the manganite nanoclusters can be tuned by the tensile stress originating from the MgO second phase. With increasing x, the lattice of LCMO was found to expand, yielding a bulk tensile strain. The largest colossal magnetoresistance of 10(5)% was observed at the percolation threshold in the conductivity at x(c) approximate to 0.3, which is coupled to a structural phase transition from orthorhombic (0 < x less than or equal to 0.1) to rhombohedral R (3) over barc structure (0.33 less than or equal to x less than or equal to 0.8). An increase of the Curie temperature for the R (3) over barc phase was observed. These results may provide a general method for controlling the magnetotransport properties of manganite-based composite films by appropriate choice of the second phase.

Abstract: Scheelite related compounds (A',A '')(n)[(B',B '')O-4](m) with B', B '' = W and/or Mo are promising new materials for red phosphors in pc-WLEDs (phosphor-converted white-light-emitting-diode) and solid-state lasers. Cation substitution in CaMoO4 of Ca2+ by the combination of Na+ and Eu3+, with the creation of A cation vacancies, has been investigated as a factor for controlling the scheelite-type structure and the luminescent properties. Na5Eu(MoO4)(4) and NaxEu(2-x)/33+square(2-x)/3MoO4 (0.138 <= x <= 0.5) phases with a scheelite-type structure were synthesized by the solid state method; their structural characteristics were investigated using transmission electron microscopy. Contrary to powder synchrotron X-ray diffraction before, the study by electron diffraction and high resolution transmission electron microscopy in this paper revealed that Na0.286Eu0.571MoO4 has a (3 + 2)D incommensurately modulated structure and that (3 + 2)D incommensurately modulated domains are present in Na0.200Eu0.600MoO4. It also confirmed the (3 + 1)D incommensurately modulated character of Na(0.138)Eu(0.621)Mo04. The luminescent properties of all phases under near-ultraviolet (n-UV) light have been investigated. The excitation spectra of these phosphors show the strongest absorption at about 395 nm, which matches well with the commercially available n-UV-emitting GaN-based LED chip. The emission spectra indicate an intense red emission due to the D-5(0) -> F-7(2) transition of Eu3+, with local minima in the intensity at Na0.286Eu0.571MoO4 and Na0.200Eu0.600MoO4 for similar to 613 nm and similar to 616 nm bands. The phosphor Na5Eu(MoO4)(4) shows the brightest red light emission among the phosphors in the Na2MoO4-Eu2/3MoO4 system and the maximum luminescence intensity of Na5Eu(MoO4)(4) (lambda(ex) = 395 nm) in the D-5(0) -> F-7(2) transition region is close to that of the commercially used red phosphor YVO4:Eu3+ (lambda(ex) = 326 nm). Electron energy loss spectroscopy measurements revealed the influence of the structure and Na/Eu cation distribution on the number and positions of bands in the UV-optical-infrared regions of the EELS spectrum.

Abstract: The double phosphate Ca9In(PO4)(7) was obtained by solid-state reaction and was studied by room and high-temperature Xray powder diffraction, electron diffraction, high-resolution electron microscopy, second-harmonic generation (SHG) technique, differential scanning calorimetry, dielectric and conductivity measurements. The beta-Ca9In(PO4)(7) room-temperature phase is related to the mineral whitlockite and is similar to beta-Ca-3(PO4)(2). It has space group R (3) over barc, with unit cell parameters: a = 10.4008(1) Angstrom, c = 37.272(1) Angstrom, Z = 6. The structure was refined by the Rietveld method (R-wp = 4.69, R-I = 1.81). A reversible first-order beta <----> beta' phase transition of the ferroelectric type with T-c = 902 K is revealed by SHG, differential scanning calorimetry and dielectric measurements. The centrosymmetric beta'-Ca9In(PO4)(7) (973 K) has space group R (3) over barc, a = 10.4611(2) Angstrom, c = 37.874 (1) Angstrom (R-wp = 4.27, R-I = 4.11). Compared to the low-temperature beta-Ca9In(PO4)(7) structure, beta'-Ca9In(PO4)(7) can be described as an orientational disordering of the P1O(4) tetrahedra together with a calcium disordering on the M3 site. (C) 2002 Elsevier Science (USA).

Abstract: Scheelite-type compounds with the general formula (A1,A2)n[(B1,B2)O4]m (2/3 ≤ n/m ≤ 3/2) are the subject of large interest owing to their stability, relatively simple preparation, and optical properties. The creation of cation vacancies (□) in the scheelite-type framework and the ordering of A cations and vacancies can be a new factor in controlling the scheelite-type structure and properties. For a long time, cation-deficient Nd3+:M2/7Gd4/7□1/7MoO4 (M = Li, Na) compounds were considered as potential lasers with diode pumping. They have a defect scheelite-type 3D structure (space group I41/a) with a random distribution of Li+(Na+), Gd3+, and vacancies in the crystal. A Na2/7Gd4/7MoO4 single crystal with scheelite-type structure has been grown by the Czochralski method. Transmission electron microscopy revealed that Na2/7Gd4/7MoO4 has a (3 + 2)D incommensurately modulated structure. The (3 + 2)D incommensurately modulated scheelite-type cation-deficient structure of Na2/7Gd4/7MoO4 [super space group I4̅ (αβ0,βα0)00] has been solved from single-crystal diffraction data. The solution of the (3 + 2)D incommensurately modulated structure revealed the partially disordered distribution of vacancies and Na and Gd cations. High-temperature conductivity measurements performed along the [100] and [001] orientation of the single crystal revealed that the conductivity of Na2/7Gd4/7MoO4 at T = 973 K equals σ = 1.13 × 105 Ω1 cm1.

Abstract: An Er3Fe5O12 ceramic has been sintered in oxygen atmosphere at 1400 °C for dielectric measurements. Its structural quality at room temperature has been checked by combining transmission electron microscopy and X-ray diffraction. It crystallizes in the cubic space group Ia3d with a = 12.3488(1). The dielectric permittivity ([variantgreekepsilon]′) and losses (tan δ) measurements as a function of temperature reveal the existence of two anomalies, a broad one between 110 K and 80 K, attributed to the Er3+ spin reorientation, and a second sharper feature at about 45 K associated to the appearance of irreversibility on the magnetic susceptibility curves. In contrast to the lack of magnetic field impact on [variantgreekepsilon]′ for the former anomaly, a complex magnetic field effect has been evidenced below 45 K. The isothermal [variantgreekepsilon]′(H) curves show the existence of positive magnetodielectric effect, reaching a maximum of 0.14% at 3 T and 10 K. Its magnitude decreases as H is further increased. Interestingly, for the lowest H values, a linear regime in the [variantgreekepsilon]′(H) curve is observed. From this experimental study, it is concluded that the [variantgreekepsilon]′ anomaly, starting above the compensation temperature Tc (75 K) and driven by the internal magnetic field, is not sensitive to an applied external magnetic field. Thus, below 45 K, it is the magnetic structure which is responsible for the coupling between spin and charge in this iron garnet.

Abstract: The transport and magnetic measurements of polycrystalline Pb1.6V8O16 hollandite reveal a concomitant metal to insulator and antiferromagnetic transition at TMI≈140 K. A clear localization is found below TMI, evidenced by a rapid increase in the absolute value of the negative Seebeck coefficient. The structural study by x-ray and transmission electron microscopy confirms the hollandite structure and shows that no structural transition occurs at TMI, ruling out a possible charge orbital ordering. The negative Seebeck coefficient observed from 50 K up to 900 K, with values reaching S=−38 μV K−1 at 900 K, is explained by the electron doping of ∼1.4e− in the V empty t2g orbitals responsible for the bad metal resistivity (ρ900 K∼2 mΩ cm). As this S value is close to that obtained by considering only the spin and orbital degeneracies, it is expected that |S| for such vanadates will not be sensitive at high temperature to the t2g band filling

Abstract: Ag/ZnO and Au/CuxO (x = 1, 2) nanocomposites supported on Si(100) and polycrystalline Al2O3 were synthesised by hybrid approaches, combining chemical vapor deposition (either thermal or plasma-assisted) of host oxide matrices and subsequent radio frequency-sputtering of guest metal particles. The influence of the adopted synthetic parameters on the nanocomposite morphological and compositional features was investigated by field emission-scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy and X-ray photoelectron spectroscopy. Results confirm the synthesis of ZnO and CuxO nanoarchitectures, characterized by a tailored morphology and an intimate metal/oxide contact. A careful control of the processing conditions enabled a fine tuning of the mutual constituent distribution, opening thus attractive perspectives for the engineering of advanced nanomaterials.

Abstract: Structure, morphology and composition of different tin oxide and germanium oxide thin film catalysts for the methanol steam reforming (MSR) reaction have been studied by a combination of (high-resolution) transmission electron microscopy, selected area electron diffraction, dark-field imaging and electron energy-loss spectroscopy. Deposition of the thin films on NaCl(0 0 1) cleavage faces has been carried out by thermal evaporation of the respective SnO2 and GeO2 powders in varying oxygen partial pressures and at different substrate temperatures. Preparation of tin oxide films in high oxygen pressures (10−1 Pa) exclusively resulted in SnO phases, at and above 473 K substrate temperature epitaxial growth of SnO on NaCl(0 0 1) leads to well-ordered films. For lower oxygen partial pressures (10−3 to 10−2 Pa), mixtures of SnO and β-Sn are obtained. Well-ordered SnO2 films, as verified by electron diffraction patterns and energy-loss spectra, are only obtained after post-oxidation of SnO films at temperatures T ≥ 673 K in 105 Pa O2. Preparation of GeOx films inevitably results in amorphous films with a composition close to GeO2, which cannot be crystallized by annealing treatments in oxygen or hydrogen at temperatures comparable to SnO/SnO2. Similarities and differences to neighbouring oxides relevant for selective MSR in the third group of the periodic system (In2O3 and Ga2O3) are also discussed with the aim of cross-correlation in formation of nanomaterials, and ultimately, also catalytic properties.