Abstract: Responses of mesoscopic superconducting rings and disks to perpendicular magnetic fields are studied by using the multiple-small-tunnel-junction method, in which transport properties of several small tunnel junctions attached to the sample are measured simultaneously. This allows us for a direct experimental observation of the paramagnetic supercurrent, which is closely related to the paramagnetic Meissner effect. The results are compared with numerical results based on the nonlinear Ginzburg-Landau theory.

Abstract: For many years magnesium oxide (MgO) has been a topic of research as buffer layer for high-temperature superconducting copper oxides and as protective layer in plasma display panels. Since epitaxial growth of MgO is expensive, time consuming and size restricted, other techniques have been developed to grow highly oriented MgO layers for industrial processes. MgO thin films were deposited on a tilted polycrystalline substrate by reactive sputtering using an unbalanced magnetron. By varying different deposition parameters, it is possible to grow biaxially aligned MgO layers, i.e. layers with both out-of-plane and in-plane alignment. XRD measurements were performed to examine the crystallographic structure of the thin film. The preferential out-of-plane orientation is analysed by angular scans using the peak intensity of different reflections while the in-plane orientation is determined by (002) pole figures. Fully [111] out-of-plane oriented layers were grown with a strong in-plane alignment. SEM and TEM measurements were performed to reveal the topographical and cross-sectional microstructure and to investigate the texture evolution of the MgO layers. Evolutionary columnar growth and a roof-tile surface have been observed.

Abstract: Single-crystalline MnOOH and Mn3O4 nanowires have been prepared by hydrothermal treatment of commercial bulky manganese oxide particles. beta-MnO2 and alpha-Mn2O3 nanowires were prepared by calcination of MnOOH nanowires. Transmission electron microscopy analysis demonstrates that MnOOH nanowires grow directly from MnO2 raw particles. The diameter of the nanowires is 20-70 nm, while the length can reach several micrometers. MnOOH nanowires grow preferentially along the [010] direction and Mn3O4 nanowires prefer to grow along the [001] direction; the long dimension of both beta-MnO2 and alpha-Mn2O3 nanowires is along [001]. Electron energy-loss spectroscopy analysis shows that the position of the prepeak of the oxygen K edge shifts to higher energy and the energy separation between the two main peaks of the oxygen K edge decreases with decreasing manganese oxidation state. The manganese-white-line ratios (L-3/L-2) were calculated. (C) 2005 American Institute of Physics.