Abstract: Pd particles supported on SnO2 and GeO2 have been structurally investigated by X-ray diffraction, (High-Resolution) transmission and scanning electron microscopy after different reductive treatments to monitor the eventual formation of bimetallic phases and catalytically tested in methanol dehydrogenation/ reforming. For both oxides this included a thin film sample with well-defined Pd particles and a powder catalyst prepared by incipient wetness impregnation. The hexagonal and the tetragonal polymorph were studied for powder GeO2. Pd2Ge formation was observed on all GeO2-supported catalysts, strongly depending on the specific sample used. Reduction of the thin film at 573K resulted in full transformation into the bimetallic state. The partial solubility of hexagonal GeO2 in water and its thermal structural instability yielded Pd2Ge formation at 473 K, at the cost of a structurally inhomogeneous support and Ge metal formation at higher reduction temperatures. Pd on tetragonal GeO2 entered a state of strong metalsupport interaction after reduction at 573673 K, resulting in coalescing Pd2Ge particles on a sintered and re-crystallized support, apparently partially covering the bimetallic particles and decreasing the catalytic activity. Pd2Ge on amorphous thin film and hexagonal GeO2 converted methanol primarily via dehydrogenation to CO and H2. At 573 K, formation of Pd2Sn and also PdSn occurred on the Pd/SnO2 thin film. Pd3Sn2 (and to some extent Pd2Sn) were predominantly obtained on the respective powder catalyst. Strong deactivation with increasing reduction temperature was observed, likely not based on the classical strong metalsupport interaction effect, but rather on a combination of missing active structural ensembles on Sn-enriched bimetallic phases and the formation of metallic -Sn. Correlations to Pd and its bimetallics supported on ZnO, Ga2O3 and In2O3 were also discussed.

Abstract: A thorough investigation was performed on the physical (mechanical, thermal, and hydrothermal stability) and chemical (ion exchange capacity and silanol number) characteristics of aluminosilicate FSMs, synthesized via a new successful short-time synthesis route using leached saponite and a low concentration of CTAB. Moreover, the influence of an additional Al incorporation, utilizing different aluminum sources, on the structure of the FSM derived from saponite is studied. A mesoporous aluminosilicate with a low Si/Al ratio of 12.8 is synthesized, and still has a very large surface area of 1130 m(2)/g and pore volume of 0.92 cm(3)/g. The aluminum-containing samples all have a high cation exchange capacity of around 1 mmol/9 while they still have a silanol number of about 0.9 OH/nm(2); both characteristics being interesting for high-yield postsynthesis modification reactions. Finally, a study is performed on the transformation of the aluminosilicates into their Bronsted acid form via the exchange with ammonium ions and a consecutive heat treatment.

Abstract: This report describes the effect of light irradiation on the synthesis of silver nanowires by the well-known polyol method. High quality nanowires are produced in high yields when the reaction suspension is irradiated with 400500 nm light during the nucleation stage. These studies suggest that light accelerates the formation of the nanoparticle seeds most appropriate for nanowire growth.

Abstract: Composite (La0.67Ca0.33MnO3)(1-x):(MgO)(x) films were prepared by metalorganic aerosol deposition on a (100)MgO substrate for different concentrations of the (MgO) phase (0less than or equal toxless than or equal to0.8). At xapproximate to0.3 a percolation threshold in conductivity is reached, at which an infinite insulating MgO cluster forms around the La0.67Ca0.33MnO3 grains. This yields a drastic increase of the electrical resistance for films with x>0.3. The film structure is characterized by x-ray diffraction and transmission electron microscopy. The local structure of the La0.67Ca0.33MnO3 within the film depends on the MgO concentration which grows epitaxially along the domain boundaries. A different structural phase transition from the orthorhombic Pnma structure to an unusual rhombohedral R (3) over barc structure at the percolation threshold xapproximate to0.3 is found for La0.67Ca0.33MnO3. A three-dimensional stress accommodation in thick films through a phase transition is suggested.

Abstract: Complex [(La0.7Sr0.3MnO3)(m)(SrTiO3)(n)] [(LSMO)(m)/(STO)(8)](15) superlattices with different layer thicknesses (m=5, 8, 12, 16, 32) have been prepared using pulsed liquid injection metalorganic chemical vapor deposition. Transmission electron microscopy and electron diffraction reveal a very clear and well-separated layer sequence. The remarkable microstructure, as well as the ferromagnetic transition temperature, depends on the LSMO layer thickness. Apart from a very clear layer sequence, electron microscopy shows evidence of a self-assembled nanostructure formation: SrMnO3 nanoinclusions and associated SrTiO3-SrMnO3 thin walls. A formation model and growth mechanism for the self-assembled structure is proposed, based on high resolution and energy filtered elemental imaging. (C) 2003 American Institute of Physics.

Abstract: The structure and defect structure of superconducting ferromagnetic bulk RuSr2GdCu2O8 has been investigated using high-resolution transmission electron microscopy and high-resolution scanning transmission microscopy. Two distinct, but closely related structures, due to ordering of rotated RuO6 octahedra and due to Cu substitution in the Ru-O layer, have been revealed. The structure of Ru1-xSr2GdCu2+xO8-delta can be described as a periodic alteration along the c axis of CuO4 planes and RuO6 octahedra. The unit-cell parameters of this phase are root 2a(p) x root 2a(p) x 2c. The possible influence of this phase and defect structure on the sensitivity of the superconductivity and magnetic properties is discussed. Local defects such as 90 S domain boundaries, (130) antiphase boundaries, and the associated dislocations are analyzed.

Abstract: La1-xCaxMnO3-delta (LCMO) thin films are grown by pulsed laser deposition on a (100) SrTiO3 substrate at temperatures between 530 degrees C and 890 degrees C. The magnetotransport properties show a high negative magnetoresistance and a shift of the maximum of the R(T) curve as function of temperature. The Curie temperature changes with deposition temperature and film quality in the range of 100-220K. The film quality is characterised by X-ray diffraction and transmission electron microscopy (TEM); film and target compositions were verified by atomic emission spectroscopy. The local structure of the film depends on the growth conditions and substrate temperature. TEM reveals a slight distortion of the film leading to a breakdown of the symmetry from orthorhombic to monoclinic. At the highest growth temperatures, a well defined interface is observed within the LCMO film, parallel to the substrate surface; this interface divides the film into two lamellae with a different microstructure. The lamella close to the substrate is perfectly coherent with the substrate, suggesting that it is strained as a result of the lattice parameter mismatch; the upper lamella shows a typical domain structure with unusual translation interfaces characterised by a displacement vector of the type 1/2[010](m) and 1/2[001](m) when referred ten the monoclinic lattice.