“Ferrimagnetism as a consequence of cation ordering in the perovskite LaSr2Cr2SbO9”. Hunter EC, Battle PD, Sena RP, Hadermann J, Journal of solid state chemistry 248, 96 (2017). http://doi.org/10.1016/J.JSSC.2017.01.024
Abstract: A polycrystalline sample of LaSr2Cr2SbO9 has been synthesised using a standard ceramic method and characterized by x-ray and neutron diffraction, magnetometry and electron microscopy. The perovskite-related compound crystallises in the triclinic space group I1 with unit cell parameters of a=5.5344(6) angstrom, b=5.5562(5) angstrom, c=7.8292(7) angstrom, a=89.986(12)degrees, beta=90.350(5)degrees and gamma=89.926(9)degrees at room temperature. The two crystallographically-distinct, six-coordinate cation sites are occupied by Cr3+ and Sb5+ in ratios of 0.868(2):0.132(2) and 0.462(2):0.538(2). Ac and de magnetometry revealed that LaSr2Cr2SbO9 is ferrimagnetic below 150 K with a magnetisation of similar to 1.25 mu(B) per formula unit in 50 kOe at 5 K. Neutron diffraction showed that the cations on the two sites order in a G-type arrangement with a mean Cr3+ moment of 2.17(1) mu(B) at 5 K, consistent with a magnetisation of 1.32 mu(B) per formula unit.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 14
DOI: 10.1016/J.JSSC.2017.01.024
|
“Synthesis and characterization of mercury based “1222&rdquo, cuprates (Hg1-xMx)(Sr,Ba)2Pr2Cu2O9-\delta (M = Pr, Pb, Bi, Tl)”. Hervieu M, Van Tendeloo G, Michel C, Martin C, Maignan A, Raveau B, Journal of solid state chemistry 115, 525 (1995). http://doi.org/10.1006/jssc.1995.1169
Abstract: Five new layered cuprates, with a 1222-type structure, have been synthesized according to the formula (Hg(1-x)M(x))(Sr,Ba)(2) Pr2Cu2O9-delta with M = Pr, Pb, Pi, and Tl. They crystallize in a tetragonal cell with a approximate to a(p) and c approximate to 29.5 Angstrom; their structure consists in a triple intergrowth of oxygen-deficient perovskite, rock-salt-and fluorite-type layers. They are characterized by a mixed [Hg(1-x)M(x)O(1-delta)] layer in the rock-sail-type slice. The ED and HREM studies show that Tl, Bi, and Pb are statistically distributed in the mixed [Hg(1-x)M(x)O(1-delta)] layer, contrary to Pr which involves an ordering phenomenon along a. Different stacking defects are observed and discussed as well as the cleavage mode of the crystals. (C) 1995 Academic Press, Inc.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 5
DOI: 10.1006/jssc.1995.1169
|
“Structural characteristics of the 40K superconductor Bi2Sr5Cu3(CO3)2O10: a HREM study”. Hervieu M, Pelloquin D, Michel C, Van Tendeloo G, Raveau B, Journal of solid state chemistry 112, 139 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 5
|
“Structural and magnetic properties of the perovskites A₂LaFe₂SbO₉, (A = Ca, Sr, Ba)”. Hendrickx M, Tang Y, Hunter EC, Battle PD, Hadermann J, Journal Of Solid State Chemistry 295, 121914 (2021). http://doi.org/10.1016/J.JSSC.2020.121914
Abstract: Polycrystalline samples of A(2)LaFe(2)SbO(9) (A = Ca, Sr, Ba) perovskites appeared monophasic to X-ray or neutron powder diffraction but a single-crystal study utilising transmission electron microscopy revealed a greater level of complexity. Although local charge balance is maintained, compositional and structural variations are present among and within the submicron-sized crystals. Despite the inhomogeneity, A = Ca is monophasic with a partially-ordered distribution of Fe3+ and Sb5+ cations across two crystallographically-distinct octahedral sites, i.e. Ca2La(Fe1.25Sb0.25)(2d) (Fe0.75Sb0.75)(2c)O-9. For A = Sr or Ba, the inhomogeneities result in differences in the filling patterns of the octahedra and the ordering of the B cations. Particles of A = Sr contain a phase (Fe:Sb similar to 2:1) without B cation ordering and one (Fe:Sb similar to 1:1) with B cation ordering. Monophasic A = Ba lacks long-range cation order although ordered nanodomains are present within the disordered phase. The temperature dependence of the magnetic properties of each sample is discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
DOI: 10.1016/J.JSSC.2020.121914
|
“CaLa2FeCoSbO9 and ALa2FeNiSbO9 (A = Ca, Sr, Ba): cation-ordered, inhomogeneous, ferrimagnetic perovskites”. Hendrickx M, Tang Y, Hunter EC, Battle PD, Cadogan Jm, Hadermann J, Journal Of Solid State Chemistry 285, 121226 (2020). http://doi.org/10.1016/j.jssc.2020.121226
Abstract: Polycrystalline samples of CaLa2FeCoSbO9 and ALa2FeNiSbO9 (A=Ca, Sr, Ba) have been prepared in solid-state reactions and studied by a combination of transmission electron microscopy, magnetometry, X-ray diffraction, neutron diffraction and Mössbauer spectroscopy. Diffraction and TEM showed that each shows 1:1 B-site ordering in which Co2+/Ni2+ and Sb5+ tend to occupy two distinct crystallographic sites while Fe3+ is distributed over both sites. While X-ray and neutron diffraction agreed that all four compositions are monophasic with space group P21/n, TEM revealed different levels of compositional inhomogeneity at the subcrystal scale, which, in the case of BaLa2FeNiSbO9, leads to the occurrence of both a P21/n and an I2/m phase. Magnetometry and neutron diffraction show that these perovskites are ferrimagnets with a G-type magnetic structure. Their relatively low magnetisation can be attributed to their inhomogeneity. This work demonstrates the importance of studying the microstructure of complex compositions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.3
DOI: 10.1016/j.jssc.2020.121226
|
“90°, Rotation of orbital stripes in bilayer manganite PrCa2Mn2O7 studied by in situ transmission electron microscopy”. He ZB, Deng G, Tian H, Xu Q, Van Tendeloo G, Journal of solid state chemistry 200, 287 (2013). http://doi.org/10.1016/j.jssc.2013.01.051
Abstract: We present an in situ transmission electron microscopy study on the half-doped bilayer manganite PrCa2Mn2O7 to reveal the rotation process of the orbital stripes. Between the reported initial and final ordering phases, we identified an intermediate state with two sets of satellite spots to bridge the 90° rotation of the orbital stripes. Furthermore, we determined that the rotation of the orbital stripes does not always occur. Some restricted conditions for the orbital rotation to occur were found and reasons are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/j.jssc.2013.01.051
|
“HREM study of fluorinated Nd2CuO4”. Hadermann J, Van Tendeloo G, Abakumov AM, Rozova MG, Antipov EV, Journal of solid state chemistry 157, 56 (2001). http://doi.org/10.1006/jssc.2000.9038
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 7
DOI: 10.1006/jssc.2000.9038
|
“Suppression of modulations in fluorinated Bi-2201 phases”. Hadermann J, Khasanova NR, Van Tendeloo G, Abakumov AM, Rozova MG, Alekseeva AM, Antipov EV, Journal of solid state chemistry 156, 445 (2001). http://doi.org/10.1006/jssc.2000.9020
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1006/jssc.2000.9020
|
“New perovskite-based manganite Pb2Mn2O5”. Hadermann J, Abakumov AM, Perkisas T, d' Hondt H, Tan H, Verbeeck J, Filonenko VP, Antipov EV, Van Tendeloo G, Journal of solid state chemistry 183, 2190 (2010). http://doi.org/10.1016/j.jssc.2010.07.032
Abstract: A new perovskite based compound Pb2Mn2O5 has been synthesized using a high pressure high temperature technique. The structure model of Pb2Mn2O5 is proposed based on electron diffraction, high angle annular dark field scanning transmission electron microscopy and high resolution transmission electron microscopy. The compound crystallizes in an orthorhombic unit cell with parameters a=5.736(1)Å≈√2a p p p (a p the parameter of the perovskite subcell) and space group Pnma. The Pb2Mn2O5 structure consists of quasi two-dimensional perovskite blocks separated by 1/2[110] p (1̄01) p crystallographic shear planes. The blocks are connected to each other by chains of edge-sharing MnO5 distorted tetragonal pyramids. The chains of MnO5 pyramids and the MnO6 octahedra of the perovskite blocks delimit six-sided tunnels accommodating double chains of Pb atoms. The tunnels and pyramidal chains adopt two mirror-related configurations (left L and right R) and layers consisting of chains and tunnels of the same configuration alternate in the structure according to an -LRLR-sequence. The sequence is sometimes locally violated by the appearance of -LL- or -RR-fragments. A scheme is proposed with a JahnTeller distortion of the MnO6 octahedra with two long and two short bonds lying in the ac plane, along two perpendicular orientations within this plane, forming a d-type pattern.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1016/j.jssc.2010.07.032
|
“Structural transformations in the fluorinated T* phase”. Hadermann J, Abakumov AM, Lebedev OI, Van Tendeloo G, Rozova MG, Shpanchenko RV, Pavljuk BP, Kopnin EM, Antipov EV, Journal of solid state chemistry 147, 647 (1999). http://doi.org/10.1006/jssc.1999.8438
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1006/jssc.1999.8438
|
“Effect of cobalt content on the properties of quintuple perovskites Sm₂Ba₃Fe₅-xCoxO₁₅-δ”. Golovachev IB, Mychinko MY, Volkova NE, Gavrilova LY, Raveau B, Maignan A, Cherepanov VA, Journal Of Solid State Chemistry 301, 122324 (2021). http://doi.org/10.1016/J.JSSC.2021.122324
Abstract: Quintuple perovskites Sm2Ba3Fe5-xCoxO15-delta = 0.5, 1.0 and 1.5) have been prepared by glycerin-nitrate tech- nique in air. The phase purity was confirmed by XRD. Partial substitution of Co for Fe decreases the oxygen content and thus the mean oxidation state of 3d-metals. It also slightly decreases the thermal expansion coefficient of oxides. Positive value of the Seebeck coefficient confirmed p-type conductivity, though the thermopower decreases as the Co content increases. The temperature dependence of electrical conductivity reveals a maximum at 550-750 degrees C.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
DOI: 10.1016/J.JSSC.2021.122324
|
“Synthesis and characterization of the reduced double-layer manganite Sr3Mn2O6+x”. Gillie LJ, Wright AJ, Hadermann J, Van Tendeloo G, Greaves C, Journal of solid state chemistry 175, 188 (2003). http://doi.org/10.1016/S0022-4596(03)00245-7
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 18
DOI: 10.1016/S0022-4596(03)00245-7
|
“Synthesis and characterization of the reduced single-layer manganite Sr2MnO3.5+x”. Gillie LJ, Wright AJ, Hadermann J, Van Tendeloo G, Greaves C, Journal of solid state chemistry 167, 145 (2002). http://doi.org/10.1006/jssc.2002.9636
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 25
DOI: 10.1006/jssc.2002.9636
|
“SrMn3O6: an incommensurate modulated tunnel structure”. Gillie LJ, Hadermann J, Pérez O, Martin C, Hervieu M, Suard E, Journal of solid state chemistry 177, 3383 (2004). http://doi.org/10.1016/j.jssc.2004.05.057
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 19
DOI: 10.1016/j.jssc.2004.05.057
|
“Oxygen exchange on nanocrystalline tin dioxide modified by palladium”. Frolov DD, Kotovshchikov YN, Morozov IV, Boltalin AI, Fedorova AA, Marikutsa AV, Rumyantseva MN, Gaskov AM, Sadovskaya EM, Abakumov AM, Journal of solid state chemistry 186, 1 (2012). http://doi.org/10.1016/j.jssc.2011.11.028
Abstract: Temperature-programmed oxygen isotopic exchange study was performed on nanocrystalline tin dioxide-based materials synthesized via sol-gel route and modified by palladium. Such materials are widely used as resistive gas sensors. The experiments were carried out in a flow-reactor up to complete isotopic substitution of oxygen. Substantial rates of isotopic exchange for SnO2 were observed from about 700 K. The distribution of isotopic molecules O-16(2). (OO)-O-16-O-18 and O-18(2) corresponds to simple dioxygen heteroexchange mechanism with single lattice oxygen atom. The modification of SnO2 by Pd introduced multiple heteroexchange mechanism with preliminary O-2 dissociation on the clusters surface. Spill-over of atomic oxygen from Pd to the surface of SnO2 and fast exchange with lattice oxygen result in more than 100% increase of apparent heteroexchange rate. The exchange on SnO2/Pd was shown to be a complex process involving partial deactivation of the catalytic centers at temperature higher than 750 K. (C) 2011 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 34
DOI: 10.1016/j.jssc.2011.11.028
|
“Structural and microstructural aspects of Six(Ta, Nb)Te2”. Frangis N, Van Tendeloo G, Manolikas C, Amelinckx S, Journal of solid state chemistry 139, 105 (1998). http://doi.org/10.1006/jssc.1998.7815
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 2
DOI: 10.1006/jssc.1998.7815
|
“Synthesis, structure and electrochemical properties of LiNaCo0.5Fe0.5PO4F fluoride-phosphate”. Fedotov SS, Kuzovchikov SM, Khasanova NR, Drozhzhin OA, Filimonov DS, Karakulina OM, Hadermann J, Abakumov AM, Antipov EV, Journal of solid state chemistry 242, 70 (2016). http://doi.org/10.1016/j.jssc.2016.02.042
Abstract: LiNaCo 0.5 Fe 0.5 PO 4 F fluoride-phosphate was synthesized via conventional solid-state and novel freeze-drying routes. The crystal structure was refined based on neutron powder diffraction (NPD) data and validated by electron diffraction (ED) and high-resolution transmission electron microscopy (HRTEM). The alkali ions are ordered in LiNaCo 0.5 Fe 0.5 PO 4 F and the transition metals jointly occupy the same crystallographic sites. The oxidation state and oxygen coordination environment of the Fe atoms were verified by 57 Fe Mössbauer spectroscopy. Electrochemical tests of the LiNaCo 0.5 Fe 0.5 PO 4 F cathode material demonstrated a reversible activity of the Fe 3+ /Fe 2+ redox couple at the electrode potential near 3.4 V and minor activity of the Co 3+ /Co 2+ redox couple over 5 V vs Li/Li + . The material exhibits a good capacity retention in the 2.4÷4.6 V vs Li/Li + potential range with the delivered discharge capacity of more than 82% (theo.) regarding Fe 3+ /Fe 2+ .
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 1
DOI: 10.1016/j.jssc.2016.02.042
|
“Synthesis and characterization of La1+xSr2-xCoMnO7-\delta (x=0,0.2, \delta=0,1)”. El Shinawi H, Bertha A, Hadermann J, Herranz T, Santos B, Marco JF, Berry FJ, Greaves C, Journal of solid state chemistry 183, 1347 (2010). http://doi.org/10.1016/j.jssc.2010.04.018
Abstract: The n=2 Ruddlesden-Popper phases LaSr(2)CoMnO(7) and La(1 2)Sr(1 8)CoMnO(7) have been synthesized by a sol-gel method The O6-type phases LaSr(2)CoMnO(6) and La(1 2)Sr(1 8)CoMnO(6) were produced by reduction of the 07 phases under a hydrogen atmosphere The materials crystallize in the tetragonal I4/mmm space group with no evidence of long-range cation order in the neutron and electron diffraction data Oxygen vacancies in the reduced materials are located primarily at the common apex of the double perovskite layers giving rise to square pyramidal coordination around cobalt and manganese ions. The oxidation states Co(3+)/Mn(4+) and Co(2+)/Mn(3+) predominate in the as-prepared and reduced materials, respectively The materials are spin glasses at low temperature and the dominant magnetic interactions change from ferro- to antiferromagnetic following reduction (C) 2010 Elsevier Inc All rights reserved
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/j.jssc.2010.04.018
|
“The structural investigation of Ba4Bi3F17”. Dombrovski EN, Serov TV, Abakumov AM, Ardashnikova EI, Dolgikh VA, Van Tendeloo G, Journal of solid state chemistry 177, 312 (2004). http://doi.org/10.1016/j.jssc.2003.08.022
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 9
DOI: 10.1016/j.jssc.2003.08.022
|
“The synthesis and complex anion-vacancy ordered structure of La0.33Sr0.67MnO2.42”. Dixon E, Hadermann J, Hayward MA, Journal of solid state chemistry 184, 1791 (2011). http://doi.org/10.1016/j.jssc.2011.05.026
Abstract: The low-temperature topotactic reduction of La0.33Sr0.67MnO3 with NaH results in the formation of La0.33Sr0.67MnO2.42. A combination of neutron powder and electron diffraction data show that La0.33Sr0.67MnO2.42 adopts a novel anion-vacancy ordered structure with a 6-layer OOTOOT' stacking sequence of the octahedral and tetrahedral layers (Pcmb, a=5.5804(1) Å, b=23.4104(7) Å, c=11.2441(3) Å). A significant concentration of anion vacancies at the anion site, which links neighbouring octahedral layers means that only 25% of the octahedral manganese coordination sites actually have 6-fold MnO6 coordination, the remainder being MnO5 square-based pyramidal sites. The chains of cooperatively twisted apex-linked MnO4 tetrahedra adopt an ordered -LRLR- arrangement within each tetrahedral layer. This is the first published example of a fully refined structure of this type which exhibits such intralayer ordering of the twisted tetrahedral chains. The rationale behind the contrasting structures of La0.33Sr0.67MnO2.42 and other previously reported reduced La1−xSrxMnO3−y phases is discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1016/j.jssc.2011.05.026
|
“Synthesis, crystal structure and magnetic properties of the Sr2Al0.78Mn1.22O5.2 anion-deficient layered perovskite”. d' Hondt H, Hadermann J, Abakumov AM, Kalyuzhnaya AS, Rozova MG, Tsirlin AA, Tan H, Verbeeck J, Antipov EV, Van Tendeloo G, Journal of solid state chemistry 182, 356 (2009). http://doi.org/10.1016/j.jssc.2008.11.002
Abstract: A new layered perovskite Sr2Al0.78Mn1.22O5.2 has been synthesized by solid state reaction in a sealed evacuated silica tube. The crystal structure has been determined using electron diffraction, high-resolution electron microscopy, and high-angle annular dark field imaging and refined from X-ray powder diffraction data (space group P4/mmm, a=3.89023(5) Å, c=7.8034(1) Å, RI=0.023, RP=0.015). The structure is characterized by an alternation of MnO2 and (Al0.78Mn0.22)O1.2 layers. Oxygen atoms and vacancies, as well as the Al and Mn atoms in the (Al0.78Mn0.22)O1.2 layers are disordered. The local atomic arrangement in these layers is suggested to consist of short fragments of brownmillerite-type tetrahedral chains of corner-sharing AlO4 tetrahedra interrupted by MnO6 octahedra, at which the chain fragments rotate over 90°. This results in an averaged tetragonal symmetry. This is confirmed by the valence state of Mn measured by EELS. The relationship between the Sr2Al0.78Mn1.22O5.2 tetragonal perovskite and the parent Sr2Al1.07Mn0.93O5 brownmillerite is discussed. Magnetic susceptibility measurements indicate spin glass behavior of Sr2Al0.78Mn1.22O5.2. The lack of long-range magnetic ordering contrasts with Mn-containing brownmillerites and is likely caused by the frustration of interlayer interactions due to presence of the Mn atoms in the (Al0.78Mn0.22)O1.2 layers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 12
DOI: 10.1016/j.jssc.2008.11.002
|
“Magnetic properties of La3Ni2Sb Ta Nb1––O9, from relaxor to spin glass”. Chin C–M, Battle PD, Hunter EC, Avdeev M, Hendrickx M, Hadermann J, Journal of solid state chemistry (Print) 273, 175 (2019). http://doi.org/10.1016/j.jssc.2019.02.044
Abstract: Neutron diffraction experiments conducted at 5 K in a magnetic field 0 < H/kOe < 50 have shown that the monoclinic perovskite La3Ni2TaO9 behaves as a relaxor ferromagnet. Compositions in the series La3Ni2SbxTayNb1–x–yO9 have been synthesized in polycrystalline form. Electron microscopy, X–ray diffraction and neutron diffraction have shown that the solid solutions are largely homogeneous and monophasic. Magnetometry and neutron diffraction have shown that the relaxor magnetisation persists in low fields when x + y = 1 but is rapidly diminished by the introduction of niobium. This change in magnetic behaviour is ascribed to the differences in the d–orbital energies of Sb5+, Nb5+ and Ta5+.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1016/j.jssc.2019.02.044
|
“Interplay of structural chemistry and magnetism in perovskites : a study of CaLn2Ni2WO9: Ln=La, Pr, Nd”. Chin C-M, Sena RP, Hunter EC, Hadermann J, Battle PD, Journal of solid state chemistry 251, 224 (2017). http://doi.org/10.1016/J.JSSC.2017.04.023
Abstract: Polycrystalline samples of CaLn(2)Ni(2)WO(9) (Ln=La, Pr, Nd) have been synthesized and characterised by a combination of X-ray and neutron diffraction, electron microscopy and magnetometry. Each composition adopts a perovskite-like structure with a similar to 5.50, b similar to 5.56, c similar to 7.78 angstrom beta similar to 90.1 degrees in space group P2(1)/n. Of the two crystallographically distinct six-coordinate sites, one is occupied entirely (Ln=Pr) or predominantly (Ln=La, Nd) by Ni2+ and the other by Ni2+ and W6+ in a ratio of approximately 1:2. None of the compounds shows long-range magnetic order at 5 K. The magnetometry data show that the magnetic moments of the Ni2+ cations form a spin glass below 30 K in each case. The Pr3+ moments in CaPr2Ni2WO9 also freeze but the Nd3+ moments in CaNd2Ni2WO9 do not. This behaviour is contrasted with that observed in other (A,A')B2B'O-9 perovskites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/J.JSSC.2017.04.023
|
“Stabilisation of magnetic ordering in La3Ni2-xCuxB'O9(B'=Sb,Ta,Nb) by the introduction of Cu2+”. Chin C-M, Battle PD, Hunter EC, Avdeev M, Hendrickx M, Hadermann J, Journal of solid state chemistry 276, 164 (2019). http://doi.org/10.1016/J.JSSC.2019.05.006
Abstract: La3Ni2-xCuxB'O-9 (x = 0.25; B' = Sb, Ta, Nb: x = 0.5; B' = Nb) have been synthesized and characterised by transmission electron microscopy, neutron diffraction and magnetometry. Each adopts a perovskite-like structure (space group P2(1)/n) with two crystallographically-distinct six-coordinate sites, one occupied by a disordered arrangement of Ni2+ and Cu2+ and the other by a disordered similar to 1:2 distribution of Ni2+ and B'(5+), although some Cu2+ is found on the latter site when x = 0.5. Each composition undergoes a magnetic transition in the range 90 <= T/K <= 130 and shows a spontaneous magnetisation at 5 K; the transition temperature always exceeds that of the x = 0 composition by >= 30 K. A long-range ordered G-type ferrimagnetic structure is present in each composition, but small relaxor domains are also present. This contrasts with the pure relaxor and spin-glass behaviour of x = 0, B' = Ta, Nb, respectively.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 2
DOI: 10.1016/J.JSSC.2019.05.006
|
“Comparative study of the magnetic properties of La3Ni2B'O9 for B' = Nb, Ta or Sb”. Chin C-M, Battle PD, Blundell SJ, Hunter E, Lang F, Hendrickx M, Sena RP, Hadermann J, Journal of solid state chemistry 258, 825 (2018). http://doi.org/10.1016/J.JSSC.2017.12.018
Abstract: Polycrystalline samples of La3Ni2NbO9 and La3Ni2TaO9 have been characterised by X-ray and neutron diffraction, electron microscopy, magnetometry and muon spin relaxation (mu SR); the latter technique was also applied to La3Ni2SbO9. On the length scale of a neutron diffraction experiment, the six-coordinate sites of the monoclinic perovskite structure are occupied in a 1:1 ordered manner by Ni and a random 1/3Ni/2/3B' mixture. Electron microscopy demonstrated that this 1:1 ordering is maintained over microscopic distances, although diffuse scattering indicative of short-range ordering on the mixed site was observed. No magnetic Bragg scattering was observed in neutron diffraction patterns collected from La3Ni2B'O-9 (B' = Nb or Ta) at 5 K although in each case mu SR identified the presence of static spins below 30 K. Magnetometry showed that La3Ni2NbO9 behaves as a spin glass below 29 K but significant short-range interactions are present in La3Ni2NbO9 below 85 K. The contrasting properties of these compounds are discussed in terms of their microstructure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 6
DOI: 10.1016/J.JSSC.2017.12.018
|
“Crystal structure and properties of the new vanadyl(IV)phosphates Na2MVO(PO4)2 M=Ca and Sr”. Chernaya VV, Tsirlin AA, Shpanchenko RV, Antipov EV, Gippius AA, Morozova EN, Dyakov V, Hadermann J, Kaul EE, Geibel C, Journal of solid state chemistry 177, 2875 (2004). http://doi.org/10.1016/j.jssc.2004.04.035
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 6
DOI: 10.1016/j.jssc.2004.04.035
|
“Synthesis and magnetic properties of rare earth ruthenates, Ln5Ru2O12 (Ln=Pr, Nd, SmTb)”. Bharathy M, Gemmill WR, Fox AH, Darriet J, Smith MD, Hadermann J, Remy MS, zur Loye H-C, Journal of solid state chemistry 182, 1164 (2009). http://doi.org/10.1016/j.jssc.2009.02.013
Abstract: Single crystals of Ln5Ru2O12 (Ln=Pr, Nd, SmTb) were grown out of either NaOH or KOH fluxes in sealed silver tubes. The crystals of all the phases were observed to be twinned as confirmed by TEM studies. The series crystallize in the C2/m monoclinic system with lattice parameters, a=12.4049(4)12.7621(6) Å, b=5.8414(2)5.9488(3) Å, c=7.3489(2)7.6424(4) Å, β=107.425(3)107.432(2)° and Z=2. The crystal structure is isotypic with the defect/disorder model of Ln5Re2O12 (Ln = Y, Gd) and consists of one dimensional edge shared RuO6 octahedral chains separated by a two dimensional LnOx polyhedral framework. Magnetic measurements indicate paramagnetic and antiferromagnetic behavior for Ln=Nd, SmGd and Ln=Tb, respectively.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 4
DOI: 10.1016/j.jssc.2009.02.013
|
“The local structure and composition of Ba4Nb2O9-based oxycarbonates”. Bezjak J, Abakumov AM, Recnik A, Krzmanc MM, Jancar B, Suvorov D, Journal of solid state chemistry 183, 1823 (2010). http://doi.org/10.1016/j.jssc.2010.06.003
Abstract: X-ray powder-diffraction(XRD),high-resolutiontransmissionelectronmicroscopy(HRTEM),electron diffraction(ED),infraredspectroscopy(IR),thermogravimetry(TG)andmassspectroscopy(MS)were performedtoinvestigatethecompositionandthecrystalstructureoftetra-bariumdi-niobate(V) Ba4Nb2O9. TheTG,MSandIRstudiesrevealedthatthecompoundisahydratedoxycarbonate.Assuming that thecarbonatestoichiometricallyreplacesoxygen,thecompositionofthelow-temperature a-modification,obtainedbyslowcoolingfrom1100 1C, correspondstoBa4Nb2O8.8(CO3)0.2 0.1H2O, while thequenchedhigh-temperature g-modificationhastheBa4Nb2O8.42(CO3)0.58 0.38H2O composi- tion. The a-phase hasacompositeincommensuratelymodulatedstructureconsistingoftwomutually interacting[Ba]N and the[(Nb,)O3]N subsystems.Thecompositemodulatedcrystalstructureofthe a-phase canbedescribedwiththelatticeparameters a¼10.2688(1) A˚ , c¼2.82426(8) A˚ , q¼0.66774(2)c* and asuperspacegroup R3m(00g)0s. TheHRTEManalysisdemonstratesthenanoscale twinningofthetrigonaldomainsparalleltothe{100}crystallographicplanes.Thetwinningintroduces a one-dimensionaldisorderintothe[(Nb,)O3]N subsystem,whichresultsinanaverage P62c crystal structureofthe a-phase. Possibleplacesforthecarbonategroupinthestructurearediscussedusinga comparisonwithotherhexagonalperovskite-basedoxycarbonates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 10
DOI: 10.1016/j.jssc.2010.06.003
|
“Crystal structure study of manganese and titanium substituted BaLaFe2O6-δ”. Ben Hafsia A, Hendrickx M, Batuk M, Khitouni M, Hadermann J, Greneche J-M, Rammeh N, Journal of solid state chemistry 251, 186 (2017). http://doi.org/10.1016/j.jssc.2017.04.019
Abstract: Barium lanthanum ferrite and four Mn/Ti substituted materials were synthesized by the sol-gel method. The crystal structure of the materials was studied by a combination of X-ray powder diffraction, electron diffraction, scanning transmission electron microscopy and 57Fe Mössbauer spectrometry. BaLaFe2O6-δ has a cubic perovskite structure and Ba0.7La1.3FeMnO6-δ is distorted perovskite with the R-3c symmetry, both from electron diffraction and X-ray powder diffraction. However, according to transmission electron microscopy, the crystals of BaLaFeTiO6-δ, BaLaFeTi0.5Mn0.5O6-δ, and BaLaFe0.5Ti0.5MnO6-δ consist of nanodomains with different symmetries (Pm3m next to R-3c due to octahedral tilts), whereas the bulk X-ray powder diffraction patterns for these compounds correspond to the simple cubic structure. 57Fe Mössbauer spectrometry confirms that all materials contain high spin state Fe3+ ions which are strongly influenced by the chemical disorder
resulting from various cationic environments.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
DOI: 10.1016/j.jssc.2017.04.019
|
“Pb5Fe3TiO11Cl : a rare example of Ti(IV) in a square pyramidal oxygen coordination”. Batuk M, Batuk D, Abakumov AM, Hadermann J, Journal of solid state chemistry 215, 245 (2014). http://doi.org/10.1016/j.jssc.2014.04.002
Abstract: A new oxychloride Pb5Fe3TiO11Cl has been synthesized using the solid state method. Its crystal and magnetic structure was investigated in the 1.5550 K temperature range using electron diffraction, high angle annular dark field scanning transmission electron microscopy, atomic resolution energy dispersive X-ray spectroscopy, neutron and X-ray powder diffraction. At room temperature Pb5Fe3TiO11Cl crystallizes in the P4/mmm space group with the unit cell parameters a=3.91803(3) Å and c=19.3345(2) Å. Pb5Fe3TiO11Cl is a new n=4 member of the oxychloride perovskite-based homologous series An+1BnO3n−1Cl. The structure is built of truncated Pb3Fe3TiO11 quadruple perovskite blocks separated by CsCl-type Pb2Cl slabs. The perovskite blocks consist of two layers of (Fe,Ti)O6 octahedra sandwiched between two layers of (Fe,Ti)O5 square pyramids. The Ti4+ cations are preferentially located in the octahedral layers, however, the presence of a noticeable amount of Ti4+ in a five-fold coordination environment has been undoubtedly proven using neutron powder diffraction and atomic resolution compositional mapping. Pb5Fe3TiO11Cl is antiferromagnetically ordered below 450(10) K. The ordered Fe magnetic moments at 1.5 K are 4.06(4) μB and 3.86(5) μB on the octahedral and square-pyramidal sites, respectively.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 4
DOI: 10.1016/j.jssc.2014.04.002
|