“Physical and electrical characterization of high-performance Cu2ZnSnSe4 based thin film solar cells”. Oueslati S, Brammertz G, Buffiere M, ElAnzeery H, Touayar O, Koeble C, Bekaert J, Meuris M, Poortmans J, Thin solid films : an international journal on the science and technology of thin and thick films 582, 224 (2015). http://doi.org/10.1016/j.tsf.2014.10.052
Abstract: We report on the electrical, optical and physical properties of Cu2ZnSnSe4 solar cells using an absorber layer fabricated by selenization of sputtered Cu, Zn and Cu10Sn90 multilayers. A maximum active-area conversion efficiency of 10.4% under AM1.5G was measured with a maximum short circuit current density of 39.7 mA/cm(2), an open circuit voltage of 394 mV and a fill factor of 66.4%. We perform electrical and optical characterization using photoluminescence spectroscopy, external quantum efficiency, current-voltage and admittance versus temperature measurements in order to derive information about possible causes for the low open circuit voltage values observed. The main defects derived from these measurements are strong potential fluctuations in the absorber layer as well as a potential barrier of the order of 133 meV at the back side contact. (C) 2014 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 1.879
Times cited: 49
DOI: 10.1016/j.tsf.2014.10.052
|
“Titania-functionalized diatom frustules as photocatalyst for indoor air purification”. Ouwehand J, Van Eynde E, De Canck E, Lenaerts S, Verberckmoes A, Van der Voort P, Applied catalysis : B : environmental 226, 303 (2018). http://doi.org/10.1016/J.APCATB.2017.12.063
Abstract: Diatom frustules were extracted from the species Thalassiosira pseudonana and functionalized with titania to be used as photocatalysts in the abatement of acetaldehyde. The synthetic procedure is water-based and environmentally friendly. The synthesis parameters were optimized to give the highest possible photocatalytic activity. The optimized material, visualized with TEM and STEM-EDX, shows the TiO2 nanoparticles grafted inside the frustule pores, as well as on the silica surface. The titania particles, stabilized by the frustules, are 2.5 times more active than the P25 benchmark material. The photocatalyst is then tested in conditions of elevated relative humidity, to simulate indoor air. The catalytic activity only shows a minor decrease at 50% relative humidity, which is a better result than for the P25 benchmark. When tested over an extended period of time, the photocatalyst only shows a minor decrease in activity.
Keywords: A1 Journal article; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 9.446
Times cited: 4
DOI: 10.1016/J.APCATB.2017.12.063
|
“Perovskite-like Mn2O3 : a path to new manganites”. Ovsyannikov SV, Abakumov AM, Tsirlin AA, Schnelle W, Egoavil R, Verbeeck J, Van Tendeloo G, Glazyrin KV, Hanfland M, Dubrovinsky L, Angewandte Chemie 52, 1494 (2013). http://doi.org/10.1002/anie.201208553
Abstract: Korund-artiges ε-Mn2O3 und Perowskit-artiges ζ-Mn2O3, zwei neue Phasen von Mn2O3, wurden unter hohen Drücken bei hohen Temperaturen synthetisiert. Die Manganatome können vollständig die A- und B-Positionen der Perowskitstruktur besetzen. ζ-Mn2O3 (siehe Bild, A-Positionsordnung) enthält Mn in den drei Oxidationsstufen +II, +III und +IV.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 84
DOI: 10.1002/anie.201208553
|
“Charge-ordering transition in iron oxide Fe4O5 involving competing dimer and trimer formation”. Ovsyannikov SV, Bykov M, Bykova E, Kozlenko DP, Tsirlin AA, Karkin AE, Shchennikov VV, Kichanov SE, Gou H, Abakumov AM, Egoavil R, Verbeeck J, McCammon C, Dyadkin V, Chernyshov D, van Smaalen S, Dubrovinsky LS, Nature chemistry 8, 501 (2016). http://doi.org/10.1038/nchem.2478
Abstract: Phase transitions that occur in materials, driven, for instance, by changes in temperature or pressure, can dramatically change the materials' properties. Discovering new types of transitions and understanding their mechanisms is important not only from a fundamental perspective, but also for practical applications. Here we investigate a recently discovered Fe4O5 that adopts an orthorhombic CaFe3O5-type crystal structure that features linear chains of Fe ions. On cooling below approximately 150 K, Fe4O5 undergoes an unusual charge-ordering transition that involves competing dimeric and trimeric ordering within the chains of Fe ions. This transition is concurrent with a significant increase in electrical resistivity. Magnetic-susceptibility measurements and neutron diffraction establish the formation of a collinear antiferromagnetic order above room temperature and a spin canting at 85 K that gives rise to spontaneous magnetization. We discuss possible mechanisms of this transition and compare it with the trimeronic charge ordering observed in magnetite below the Verwey transition temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 25.87
Times cited: 51
DOI: 10.1038/nchem.2478
|
“A hard oxide semiconductor with a direct and narrow bandgap and switchable pn electrical conduction”. Ovsyannikov SV, Karkin AE, Morozova NV, Shchennikov VV, Bykova E, Abakumov AM, Tsirlin AA, Glazyrin KV, Dubrovinsky L, Advanced materials 26, 8185 (2014). http://doi.org/10.1002/adma.201403304
Abstract: An oxide semiconductor (perovskite-type Mn2O3) is reported which has a narrow and direct bandgap of 0.45 eV and a high Vickers hardness of 15 GPa. All the known materials with similar electronic band structures (e.g., InSb, PbTe, PbSe, PbS, and InAs) play crucial roles in the semiconductor industry. The perovskite-type Mn2O3 described is much stronger than the above semiconductors and may find useful applications in different semiconductor devices, e.g., in IR detectors.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 27
DOI: 10.1002/adma.201403304
|
“Electronic and magnetic properties of 1T-TiSe2 nanoribbons”. Ozaydin HD, Sahin H, Kang J, Peeters FM, Senger RT, 2D materials 2, 044002 (2015). http://doi.org/10.1088/2053-1583/2/4/044002
Abstract: Motivated by the recent synthesis of single layer TiSe2, we used state-of-the-art density functional theory calculations, to investigate the structural and electronic properties of zigzag and armchair-edged nanoribbons (NRs) of this material. Our analysis reveals that, differing from ribbons of other ultra-thin materials such as graphene, TiSe2 NRs have some distinctive properties. The electronic band gap of the NRs decreases exponentially with the width and vanishes for ribbons wider than 20 angstrom. For ultranarrow zigzag-edged NRs we find odd-even oscillations in the band gap width, although their band structures show similar features. Moreover, our detailed magnetic-ground-state analysis reveals that zigzag and armchair edged ribbons have non-magnetic ground states. Passivating the dangling bonds with hydrogen at the edges of the structures influences the band dispersion. Our results shed light on the characteristic properties of T phase NRs of similar crystal structures.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 6.937
Times cited: 20
DOI: 10.1088/2053-1583/2/4/044002
|
“Formation and diffusion characteristics of Pt clusters on Graphene, 1H-MoS2 and 1T-TaS2”. Ozaydin HD, Sahin H, Senger RT, Peeters FM, Annalen der Physik 526, 423 (2014). http://doi.org/10.1002/andp.201400079
Abstract: Many experiments have revealed that the surfaces of graphene and graphene-like structures can play an active role as a host surface for clusterization of transition metal atoms. Motivated by these observations, we investigate theoretically the adsorption, diffusion and magnetic properties of Pt clusters on three different two-dimensional atomic crystals using first principles density functional theory. We found that monolayers of graphene, molybdenum disulfide (1H-MoS2) and tantalum disulfide (1T-TaS2) provide different nucleation characteristics for Pt cluster formation. At low temperatures, while the bridge site is the most favorable site where the growth of a Pt cluster starts on graphene, top-Mo and top-Ta sites are preferred on 1H-MoS2 and 1T-TaS2, respectively. Ground state structures and magnetic properties of Pt-n clusters (n= 2,3,4) on three different monolayer crystal structures are obtained. We found that the formation of Pt-2 dimer and a triangle-shaped Pt-3 cluster perpendicular to the surface are favored over the three different surfaces. While bent rhombus shaped Pt-4 is formed on graphene, the formation of tetrahedral shaped clusters are more favorable on 1H-MoS2 and 1T-TaS2. Our study of the formation of Pt-n clusters on three different monolayers provides a gateway for further exploration of nanocluster formations on various surfaces.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.039
Times cited: 10
DOI: 10.1002/andp.201400079
|
“Ballistic thermoelectric properties of monolayer semiconducting transition metal dichalcogenides and oxides”. Ozbal G, Senger RT, Sevik C, Sevincli H, Physical review B 100, 085415 (2019). http://doi.org/10.1103/PHYSREVB.100.085415
Abstract: Combining first-principles calculations with Landauer-Mittiker formalism, ballistic thermoelectric transport properties of semiconducting two-dimensional transition metal dichalcogenides (TMDs) and oxides (TMOs) (namely MX2 with M = Cr, Mo, W, Ti, Zr, Hf; X = O, S, Se, Te) are investigated in their 2H and 1T phases. Having computed structural, as well as ballistic electronic and phononic transport properties for all structures, we report the thermoelectric properties of the semiconducting ones. We find that 2H phases of four of the studied structures have very promising thermoelectric properties, unlike their 1T phases. The maximum room temperature p-type thermoelectric figure of merit (ZT) of 1.57 is obtained for 2H-HfSe2, which can be as high as 3.30 at T = 800 K. Additionally, 2H-ZrSe2, 2H-ZrTe2, and 2H-HfS2 have considerable ZT values (both nand p-type), that are above 1 at room temperature. The 1T phases of Zr and Hf-based oxides possess relatively high power factors, however their high lattice thermal conductance values limit their ZT values to below 1 at room temperature.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
DOI: 10.1103/PHYSREVB.100.085415
|
“Structural, electronic and vibrational properties of ultra-thin octahedrally coordinated structure of EuO2”. Ozcan M, Ozen S, Yagmurcukardes M, Sahin H, Journal Of Magnetism And Magnetic Materials 493, 165668 (2020). http://doi.org/10.1016/J.JMMM.2019.165668
Abstract: Novel stable ultra-thin phases of europium oxide are investigated by means of state-of-the-art first principles calculations. Total energy calculations show that single layers of EuO2 and Eu(OH)(2) can be stabilized in an octahedrally coordinated (1T) atomic structure. However, phonon calculations reveal that although both structures are energetically feasible, only the 1T-EuO2 phase has dynamical stability. The phonon spectrum of 1T-EuO2 displays three Raman active modes; a non-degenerate out-of-plane A(1g) mode at 353.5 cm(-1) and two doubly-degenerate in-plane E-g modes at 304.3 cm(-1). Furthermore, magnetic ground state and electronic band dispersion calculations show that the single layer EuO2 is a metal with net magnetic moment of 5(mu B) per unitcell resulting in a half-metallic ferrimagnetic behavior. Moreover, robustness of the half-metallic ferrimagnetic characteristics of EuO2 is confirmed by the application of electric field and charging. Single layer 1T-EuO2, with its stable ultra-thin structure and half-metallic ferrimagnetic feature, is a promising novel material for nanoscale electronic and spintronic applications.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.7
Times cited: 1
DOI: 10.1016/J.JMMM.2019.165668
|
“Exploring the adsorption mechanisms of neurotransmitter and amino acid on Ti3C2-MXene monolayer : insights from DFT calculations”. Ozdemir I, Arkin H, Milošević, MV, V Barth J, Aktuerk E, Surfaces and interfaces 46, 104169 (2024). http://doi.org/10.1016/J.SURFIN.2024.104169
Abstract: In this study, we conducted a systematic density functional theory (DFT) investigation of the interaction between Ti3C2-MXene monolayer and biological molecules dopamine (DA) and serine (Ser) as neurotransmitter and amino acid, respectively. Our calculations show good agreement with previous literature findings for the optimized Ti3C2 monolayer. We found that DA and Ser molecules bind to the Ti3C2 surface with adsorption energies of -2.244 eV and -3.960 eV, respectively. The adsorption of Ser resulted in the dissociation of one H atom. Electronic density of states analyses revealed little changes in the electronic properties of the Ti3C2-MXene monolayer upon adsorption of the biomolecules. We further investigated the interaction of DA and Ser with Ti3C2 monolayers featuring surface -termination with OH functional group, and Ti -vacancy. Our calculations indicate that the adsorption energies significantly decrease in the presence of surface termination, with adsorption energies of -0.097 eV and -0.330 eV for DA and Ser, respectively. Adsorption energies on the Ti -vacancy surface, on the other hand, are calculated to be -3.584 eV and -3.856 eV for DA and Ser, respectively. Our results provide insights into the adsorption behavior of biological molecules on Ti3C2-MXene, demonstrating the potential of this material for biosensing and other biomedical applications. These findings highlight the importance of surface modifications in the development of functional materials and devices based on Ti3C2-MXene, and pave the way for future investigations into the use of 2D materials for biomedical applications.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 6.2
DOI: 10.1016/J.SURFIN.2024.104169
|
“CVD growth of monolayer MoS2: Role of growth zone configuration and precursors ratio”. Ozden A, Ay F, Sevik C, Perkgoz NK, Japanese journal of applied physics 56, 06gg05 (2017). http://doi.org/10.7567/JJAP.56.06GG05
Abstract: Single-layer, large-scale two-dimensional material growth is still a challenge for their wide-range usage. Therefore, we carried out a comprehensive study of monolayer MoS2 growth by CVD investigating the influence of growth zone configuration and precursors ratio. We first compared the two commonly used approaches regarding the relative substrate and precursor positions, namely, horizontal and face-down configurations where facedown approach is found to be more favorable to obtain larger flakes under identical growth conditions. Secondly, we used different types of substrate holders to investigate the influence of the Mo and S vapor confinement on the resulting diffusion environment. We suggest that local changes of the S to Mo vapor ratio in the growth zone is a key factor for the change of shape, size and uniformity of the resulting MoS2 formations, which is also confirmed by performing depositions under different precursor ratios. Therefore, to obtain continuous monolayer films, the S to Mo vapor ratio is needed to be kept within a certain range throughout the substrate. As a conclusion, we obtained monolayer triangles with a side length of 90 mu m and circles with a diameter of 500 mu m and continuous films with an area of 85 0 mu m x 1 cm when the S-to-Mo vapor ratio is optimized. (C) 2017 The Japan Society of Applied Physics
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
DOI: 10.7567/JJAP.56.06GG05
|
“Hydrothermal synthesis of carbonate-free submicron-sized barium titanate from an amorphous precursor : synthesis and characterization”. Özen M, Mertens M, Luyten J, Snijkers F, d' Hondt H, Cool P, Ceramics international 38, 619 (2012). http://doi.org/10.1016/j.ceramint.2011.07.051
Abstract: In this paper, the amorphous barium titanate precursor was prepared by the peroxo-hydroxide method and post-treated by various drying procedures, such as: room temperature drying, room temperature vacuum drying and vacuum drying at 50 degrees C. The objective in the latter two treatments was to increase the Ti-O-Ba bonds of the precursor. The post-treated precursors were compared with the untreated (i.e., 'wet') precursor. Also, a barium titanate precursor was prepared by an alkoxide route. Afterwards, the precursors were hydrothermally treated at 200 degrees C in a 10 M NaOH solution. Vacuum drying of the precursor seemingly promoted the formation of Ti-O-Ti bonds in the hydrothermal end-product. The low Ba:Ti ratio (0.66) of the alkoxide-route prepared precursor lead to a multi-phase hydrothermal product with BaTiO(3) as the main phase. In contrast, phase pure BaTiO(3), i.e. without BaCO(3) contamination, was obtained for the precursor which was dried at room temperature. Cube-shaped and highly crystalline BaTiO(3) particles were observed by electron microscopy for the hydrothermally treated peroxo-hydroxide-route prepared precursor. (C) 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.986
Times cited: 14
DOI: 10.1016/j.ceramint.2011.07.051
|
“Texturing of hydrothermally synthesized BaTiO3 in a strong magnetic field by slip casting”. Özen M, Mertens M, Snijkers F, Van Tendeloo G, Cool P, Ceramics international 42, 5382 (2016). http://doi.org/10.1016/j.ceramint.2015.12.073
Abstract: Barium titanate powder was processed by slip casting in a rotating strong magnetic field of 9.4 T. The orientation factor of the sintered compact was analyzed by the X-ray diffraction technique and the microstructure (grain-size) was analyzed by scanning electron microscope. The hydrothermally prepared barium titanate was used as matrix material and the molten-salt synthesized barium titanate, with a larger particle-size, was used as template for the templated grain-growth process. Addition of large template particles was observed to increase the orientation factor of the sintered cast (5 vol% loading). Template particles acted as starting grains for the abnormal grain-growth process and the average grain-size was increased after sintering. Increasing the solid loading (15 vol%) resulted in a similar orientation factor with a decrease of the average grain size by more than half. However, addition of templates to the 15 vol% cast had a negative effect on the orientation factor. The impingement of growing particles was stated as the primary cause of particle misorientation resulting in a low orientation factor after sintering. Different heating conditions were tested and it was determined that a slow heating rate gave the highest orientation factor, the smallest average grain-size and the highest relative density. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.986
Times cited: 11
DOI: 10.1016/j.ceramint.2015.12.073
|
“Investigation of heavy metal distributions along 15m soil profiles using EDXRF, XRD, SEM-EDX, and ICP-MS techniques”. Ozen SA, Ozkalayci F, Cevik U, Van Grieken R, X-ray spectrometry 47, 231 (2018). http://doi.org/10.1002/XRS.2832
Abstract: The research of soil contamination by heavy metal is an important field due to its environmental and health implications. The goal was to study the elemental mobility as a function of depth. For this reason, the distribution of heavy metals (V, Cr, Co, Ni, Cu, Zn, As, Sn, and Pb) was investigated along soil profiles up to a depth of 15m at 9 sampling sites in the Nilufer industrial district (Bursa, Turkey). Elemental analyses were done with the Epsilon 5 energy dispersive X-ray fluorescence and inductively coupled plasma mass spectrometry equipment. Particle analysis was performed with a JEOL scanning electron microscope equipped with a Si(Li) X-ray detector. The crystallographic compositions of oxide compounds in soil samples were identified by a Rigaku X-ray diffraction instrument. Different parameters such as the soil's chemical (mineralogical structure, pH, and electrical conductivity) and physical properties (the number of blows, the stiffness index, the liquidity index, the plasticity index, and the water content) were analyzed. To assess the mobility of the heavy metals, diffusion (D) and convection coefficients (?) were calculated with the finite difference method. Convection was determined to dominate the studied region. In addition, the mobility coefficient was determined for each metal. High mobilities were determined for Zn and V, moderate mobilities for Cr, Ni, Cu, and As, and low mobilities were determined for Co and Pb. The results revealed that elements had reached depths of up to 15m, causing irreversible soil contamination that may lead to environmental health issues.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1002/XRS.2832
|
“Routes to increase the conversion and the energy efficiency in the splitting of CO2by a dielectric barrier discharge”. Ozkan A, Bogaerts A, Reniers F, Journal of physics: D: applied physics 50, 084004 (2017). http://doi.org/10.1088/1361-6463/aa562c
Abstract: Here, we present routes to increase CO2 conversion into CO using an atmospheric pressure dielectric-barrier discharge. The change in conversion as a function of simple plasma parameters, such as power, flow rate, but also frequency, on-and-off power pulse, thickness and the chemical nature of the dielectric, wall and gas temperature, are described. By means of an in-depth electrical characterization of the discharge (effective plasma voltage, dielectric voltage, plasma current, number and lifetime of the microdischarges), combined with infrared analysis of the walls of the reactor, optical emission spectroscopy for the gas temperature, and mass spectrometry for the CO2 conversion, we propose a global interpretation of the effect of all the experimental parameters on the conversion and efficiency of the reaction.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.588
Times cited: 28
DOI: 10.1088/1361-6463/aa562c
|
“CO2-CH4 conversion and syngas formation at atmospheric pressure using a multi-electrode dielectric barrier discharge”. Ozkan A, Dufour T, Arnoult G, De Keyzer P, Bogaerts A, Reniers F, Journal of CO2 utilization 9, 74 (2015). http://doi.org/10.1016/j.jcou.2015.01.002
Abstract: The conversion of CO2 and CH4 into value-added chemicals is studied in a new geometry of a dielectric barrier discharge (DBD) with multi-electrodes, dedicated to the treatment of high gas flow rates. Gas chromatography is used to define the CO2 and CH4 conversion as well as the yields of the products of decomposition (CO, O2 and H2) and of recombination (C2H4, C2H6 and CH2O). The influence of three parameters is investigated on the conversion: the CO2 and CH4 flow rates, the plasma power and the nature of the carrier gas (argon or helium). The energy efficiency of the CO2 conversion is estimated and compared with those of similar atmospheric plasma sources. Our DBD reactor shows a good compromise between a good energy efficiency and the treatment of a large CO2 flow rate.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 4.292
Times cited: 57
DOI: 10.1016/j.jcou.2015.01.002
|
“How do the barrier thickness and dielectric material influence the filamentary mode and CO2conversion in a flowing DBD?”.Ozkan A, Dufour T, Bogaerts A, Reniers F, Plasma sources science and technology 25, 045016 (2016). http://doi.org/10.1088/0963-0252/25/4/045016
Abstract: Dielectric barrier discharges (DBDs) are commonly used to generate cold plasmas at
atmospheric pressure. Whatever their configuration (tubular or planar), the presence of a dielectric barrier is mandatory to prevent too much charge build up in the plasma and the formation of a thermal arc. In this article, the role of the barrier thickness (2.0, 2.4 and 2.8 mm) and of the kind of dielectric material (alumina, mullite, pyrex, quartz) is investigated on the filamentary behavior in the plasma and on the CO2 conversion in a tubular flowing DBD, by means of mass spectrometry measurements correlated with electrical characterization and IR imaging. Increasing the barrier thickness decreases the capacitance, while preserving the electrical charge. As a result, the voltage over the dielectric increases and a larger number of microdischarges is generated, which enhances the CO2 conversion. Furthermore, changing the dielectric material of the barrier, while keeping the same geometry and dimensions, also affects the CO2 conversion. The highest CO2 conversion and energy efficiency are obtained for quartz and alumina, thus not following the trend of the relative permittivity. From the
electrical characterization, we clearly demonstrate that the most important parameters are the somewhat higher effective plasma voltage (yielding a somewhat higher electric field and electron energy in the plasma) for quartz, as well as the higher plasma current (and thus larger electron density) and the larger number of microdischarge filaments (mainly for alumina, but also for quartz). The latter could be correlated to the higher surface roughness for alumina and to the higher voltage over the dielectric for quartz.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 3.302
Times cited: 24
DOI: 10.1088/0963-0252/25/4/045016
|
“The influence of power and frequency on the filamentary behavior of a flowing DBD—application to the splitting of CO2”. Ozkan A, Dufour T, Silva T, Britun N, Snyders R, Bogaerts A, Reniers F, Plasma sources science and technology 25, 025013 (2016). http://doi.org/10.1088/0963-0252/25/2/025013
Abstract: In this experimental study, a flowing dielectric barrier discharge operating at atmospheric pressure is used for the splitting of CO2 into O2 and CO. The influence of the applied frequency and plasma power on the microdischarge properties is investigated to understand their role on the CO2 conversion. Electrical measurements are carried out to explain the conversion trends and to characterize the microdischarges through their number, their lifetime,
their intensity and the induced electrical charge. Their influence on the gas and electrode temperatures is also evidenced through optical emission spectroscopy and infrared imaging. It is shown that, in our configuration, the conversion depends mostly on the charge delivered in the plasma and not on the effective plasma voltage when the applied power is modified. Similarly, at constant total current, a better conversion is observed at low frequencies, where a less filamentary discharge regime with a higher effective plasma voltage than that at a higher
frequency is obtained.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 3.302
Times cited: 40
DOI: 10.1088/0963-0252/25/2/025013
|
“DBD in burst mode: solution for more efficient CO2conversion?”.Ozkan A, Dufour T, Silva T, Britun N, Snyders R, Reniers F, Bogaerts A, Plasma sources science and technology 25, 055005 (2016). http://doi.org/10.1088/0963-0252/25/5/055005
Abstract: CO2 conversion into value-added products has gained significant interest over the few last years, as the greenhouse gas concentrations constantly increase due to anthropogenic activities. Here we report on experiments for CO2 conversion by means of a cold atmospheric plasma using a cylindrical flowing dielectric barrier discharge (DBD) reactor. A detailed comparison of this DBD ignited in a so-called burst mode (i.e. where an AC voltage is applied during a limited amount of time) and pure AC mode is carried out to evaluate their effect on the conversion of CO2 as well as on the energy efficiency. Decreasing the duty cycle in the burst mode from 100% (i.e. corresponding to pure AC mode) to 40% leads to a rise in the
conversion from 16–26% and to a rise in the energy efficiency from 15 to 23%. Based on a detailed electrical analysis, we show that the conversion correlates with the features of the microfilaments. Moreover, the root-mean-square voltage in the burst mode remains constant as a function of the process time for the duty cycles <70%, while a higher duty cycle or the usual pure AC mode leads to a clear voltage decay by more than 500 V, over approximately 90 s, before reaching a steady state regime. The higher plasma voltage in the burst mode yields a higher electric field. This causes the increasing the electron energy, and therefore their
involvement in the CO2 dissociation process, which is an additional explanation for the higher CO2 conversion and energy efficiency in the burst mode.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 3.302
Times cited: 17
DOI: 10.1088/0963-0252/25/5/055005
|
“Bi0.75Sr0.25FeO3-\delta : revealing order/disorder phenomena by combining diffraction techniques”. Pachoud E, Bréard Y, Martin C, Maignan A, Abakumov AM, Suard E, Smith RI, Suchomel MR, Solid state communications 152, 331 (2012). http://doi.org/10.1016/j.ssc.2011.12.023
Abstract: The local and long range structure of polycrystalline samples of Bi0.75Sr0.25FeO3-delta has been probed by neutron and synchrotron X-ray diffraction coupled with transmission electron microscopy. It is found that the long range structure on average can be described by the cubic space group Pm-3m (a(p) congruent to 3.951 angstrom). However, the refinements revealed large atomic displacements for the (Bi, Sr) cations and the oxygen atoms from their ideal positions. The electron microscopy study indicates the existence of local phenomena like local ordering of oxygen vacancies, which are segregated at the randomly spaced parallel (FeO2-delta) planes, or the existence of region of different symmetry, probably R3c. At room temperature, the compound exhibits G-type antiferromagnetism (T-N congruent to 650 K) with a magnetic moment of congruent to 3.7 mu(B). (C) 2012 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.554
Times cited: 6
DOI: 10.1016/j.ssc.2011.12.023
|
“Increasing the cost-effectiveness of EU agri-environment policy measures through evaluation of farm and field-level environmental and economic performance”. Pacini GC, Merante P, Lazzerini G, Van Passel S, Agricultural Systems 136, 70 (2015). http://doi.org/10.1016/J.AGSY.2015.02.004
Abstract: A lot of attention in the debate on the 2014-2020 programming period of the EU CAP and rural development policy revolves around the policy's contribution to enhancing resource use efficiency, decreasing environmental impact, restoring ecosystems and how to ensure more efficient and effective agrienvironmental measures (AEMs). Nevertheless, studies that simultaneously address multiple measures with multiple environmental objectives and targets are underrepresented in the scientific literature. The objectives of the present article are (i) to present an integrated tool-kit for AEM design resulting from the combination of farm modelling with the Sustainable Value Approach (SVA), and (ii) to evaluate the potential of the tool-kit to support AEM design through an application to estimate cost-effective organic agriculture payments for the dairy sector in Mugello, northern Tuscany. Sustainability assessment of organic and conventional farming systems (OFS and CFS, respectively.) under the 2007-2013 EU CAP support schemes and a no EU support scenario show better OFS performances regarding nitrogen leaching (-52% and -47% under the current CAP and the no EU support scenarios, respectively), soil erosion (-24% and -34%), potential pesticide risks (-100%), biodiversity (+13% and +30%). Income foregone for the production of environmental benefits from organic agriculture under a no EU support scenario is equal to 210 Euro/ha. Sustainable value calculations combined with modelling results indicate soil erosion and nitrogen leaching as the environmental processes to be addressed with specific policy measures to further increase the efficiency of organic farming. A new organic agriculture support scheme designed based on such indications further increases the OFS SV and almost closes the GAP with a benchmark farm of the area, featured with ideal performances in terms of environmental and economic indicators. The payment scheme we designed with the support of the integrated tool-kit shows to be more cost-effective and efficient of current AEMs. (C) 2015 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Economics; Engineering Management (ENM)
Impact Factor: 2.571
Times cited: 12
DOI: 10.1016/J.AGSY.2015.02.004
|
“Size-controlled electrodeposition of Cu nanoparticles on gas diffusion electrodes in methanesulfonic acid solution”. Pacquets L, Irtem E, Neukermans S, Daems N, Bals S, Breugelmans T, Journal Of Applied Electrochemistry 51 (2020). http://doi.org/10.1007/S10800-020-01474-5
Abstract: In this paper electrodeposition is used to obtain Cu nanoparticles, as it allows good control over particle size and distribution. These Cu particles were deposited onto a gas diffusion electrode which increased the resulting surface area. Prior to deposition, the surface was pre-treated with NaOH, HNO3, MQ and TX100 to investigate the influence on the electrodeposition of Cu on the gas diffusion electrode (GDE). When using HNO3, the smallest particles with the most homogeneous distribution and high particle roughness were obtained. Once the optimal substrate was determined, we further demonstrated that by altering the electrodeposition parameters, the particle size and density could be tuned. On the one hand, increasing the nucleation potential led to a higher particle density resulting in smaller particles because of an increased competition between particles. Finally, the Cu particle size increased when applying a greater growth charge and growth potential. This fundamental study thus opens up a path towards the synthesis of supported Cu materials with increased surface areas, which is interesting from a catalytic point of view. Larger surface areas are generally correlated with a better catalyst performance and thus higher product yields. This research can contributed in obtaining new insides into the deposition of metallic nanoparticles on rough surfaces. [GRAPHICS] .
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 2.9
Times cited: 3
DOI: 10.1007/S10800-020-01474-5
|
“Use of nanoscale carbon layers on Ag-based gas diffusion electrodes to promote CO production”. Pacquets L, Van den Hoek J, Arenas Esteban D, Ciocarlan R-G, Cool P, Baert K, Hauffman T, Daems N, Bals S, Breugelmans T, ACS applied nano materials 5, 7723 (2022). http://doi.org/10.1021/ACSANM.2C00473
Abstract: A promising strategy for the inhibition of the hydrogen evolution reaction along with the stabilization of the electrocatalyst in electrochemical CO2 reduction cells involves the application of a nanoscale amorphous carbon layer on top of the active catalyst layer in a gas diffusion electrode. Without modifying the chemical nature of the electrocatalyst itself, these amorphous carbon layers lead to the stabilization of the electrocatalyst, and a significant improvement with respect to the inhibition of the hydrogen evolution reaction was also obtained. The faradaic efficiencies of hydrogen could be reduced from 31.4 to 2.1% after 1 h of electrolysis with a 5 nm thick carbon layer. Furthermore, the impact of the carbon layer thickness (5–30 nm) on this inhibiting effect was investigated. We determined an optimal thickness of 15 nm where the hydrogen evolution reaction was inhibited and a decent stability was obtained. Next, a thickness of 15 nm was selected for durability measurements. Interestingly, these durability measurements revealed the beneficial impact of the carbon layer already after 6 h by suppressing the hydrogen evolution such that an increase of only 37.9% exists compared to 56.9% without the use of an additional carbon layer, which is an improvement of 150%. Since carbon is only applied afterward, it reveals its great potential in terms of electrocatalysis in general.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 5.9
Times cited: 3
DOI: 10.1021/ACSANM.2C00473
|
“Microanalytical characterization of surface decoration in Majolica pottery”. Padilla R, Schalm O, Janssens K, Arrazcaeta R, van Espen P, Analytica chimica acta 535, 201 (2005). http://doi.org/10.1016/J.ACA.2004.11.082
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Chemometrics (Mitac 3)
Impact Factor: 4.95
Times cited: 20
DOI: 10.1016/J.ACA.2004.11.082
|
“Semiempirical approach for standardless calibration in µ-XRF spectrometry using capillary lenses”. Padilla R, van Espen P, Abrahantes A, Janssens K, X-ray spectrometry 34, 19 (2005). http://doi.org/10.1002/XRS.781
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Chemometrics (Mitac 3)
Impact Factor: 1.298
Times cited: 23
DOI: 10.1002/XRS.781
|
“Reduced Anisotropy and Enhanced In-Field Performance of Thick BaHfO3-Doped Films on ABAD-YSZ Templates”. Pahlke P, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Hanisch J, Sieger M, Usoskin A, Stromer J, Holzapfel B, Schultz L, Huhne R, IEEE transactions on applied superconductivity 26, 1 (2016). http://doi.org/10.1109/TASC.2016.2541998
Abstract: Pure and 6 mol% BaHfO3 (BHO) doped YBa2Cu3O7-δ (YBCO) films were prepared on CeO2-buffered ABAD-YSZ templates by pulsed laser deposition. The self-field Jc at 77 K reaches 1.1 MA/cm² in the doped sample compared to 2.5 MA/cm² in pure YBCO, at a film thickness of around 1 μm. Above a magnetic field of 2.2 T along B||c, Jc of the BHO-doped sample exceeds the Jc of the undoped film. The maximum pinning force density (FP,max) reaches a value of around 3 GN/cm² for both samples, but B(FP,max) increases from 1.4 T (pure) to a value of 2.9 T (BHO:YBCO). The Jc anisotropy curves of the doped sample show a large and broad peak at B||c and a strongly reduced anisotropy at all temperatures and fields compared to the pure sample. A complex defect structure with YBa2Cu4O8 intergrowths, Y2O3 precipitates and BHO nanocolumns with a fanshaped structure is observed by TEM investigations, which can explain the measured Jc(B,θ) behavior.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 14
DOI: 10.1109/TASC.2016.2541998
|
“Influence of artificial pinning centers on structural and superconducting properties of thick YBCO films on ABAD-YSZ templates”. Pahlke P, Sieger M, Ottolinger R, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Haenisch J, Holzapfel B, Schultz L, Nielsch K, Huehne R, Superconductor science and technology 31, 044007 (2018). http://doi.org/10.1088/1361-6668/AAAFBE
Abstract: Recent efforts in the development of YBa2Cu3O7-x (YBCO) coated conductors are devoted to the increase of the critical current I-c in magnetic fields. This is typically realized by growing thicker YBCO layers as well as by the incorporation of artificial pinning centers. We studied the growth of doped YBCO layers with a thickness of up to 7 mu m using pulsed laser deposition with a growth rate of about 1.2 nm s(-1). Industrially fabricated ion-beam textured YSZ templates based on metal tapes were used as substrates for this study. The incorporation of BaHfO3 (BHO) or Ba2Y(Nb0.5Ta0.5)O-6 (BYNTO) secondary phase additions leads to a denser microstructure compared to undoped films. A purely c-axis-oriented YBCO growth is preserved up to a thickness of about 4 mu m, whereas misoriented texture components were observed in thicker films. The critical temperature is slightly reduced compared to undoped films and independent of film thickness. The critical current density J(c) of the BHO- and BYNTO-doped YBCO layers is lower at 77 K and self-field compared to pure YBCO layers; however, I-c increases up to a thickness of 5 mu m. A comparison between films with a thickness of 1.3 mu m revealed that the anisotropy of the critical current density J(c)(theta) strongly depends on the incorporated pinning centers. Whereas BHO nanorods lead to a strong B vertical bar vertical bar c-axis peak, the overall anisotropy is significantly reduced by the incorporation of BYNTO forming a mixture of short c-axis-oriented nanorods and small (a-b)-oriented platelets. As a result, the J(c) values of the doped films outperform the undoped samples at higher fields and lower temperatures for most magnetic field directions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 9
DOI: 10.1088/1361-6668/AAAFBE
|
“An effective lowest Landau level treatment of demagnetization in superconducting mesoscopic disks”. Palacios JJ, Peeters FM, Baelus BJ, Physical review : B : condensed matter and materials physics 64, 134514 (2001). http://doi.org/10.1103/PhysRevB.64.134514
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 4
DOI: 10.1103/PhysRevB.64.134514
|
“Characterization of black volcanites from the Limay river basin, Patagonia, Argentina, using energy dispersive X-ray fluorescence spectrometry : an aid to infer human group mobility”. Palacios OM, van Meel K, Van Grieken R, Marcó, P L-M, Vázquez C, Journal of radioanalytical and nuclear chemistry 298, 1245 (2013). http://doi.org/10.1007/S10967-013-2600-1
Abstract: The investigation of hunter-gatherers archaeological sites in the Limay river basin, Patagonia, Argentina, raised questions concerning the lithic technology. The chemical characterization of artifacts, rocks and possible sources of provenances could help to elucidate the hunter-gatherer mobility. In three archaeological sitesRincón Chico 2 (RCh2/87; 14C 710 ± 60 BP), Cueva Traful I (CTI; 14C 9430 ± 230 BP) and Casa de Piedra de Ortega (CPO; 14C 2840 ± 80 BP), tools and debitage or discarded flakes made in black volcanic rock have been found. Nearby an extensive rock outcrop of black volcanite, Paso Limay quarry (CPL), with similar characteristics was located. Samples coming from these four sites were analyzed by energy dispersive X-ray fluorescence spectrometry. This characterization allowed the geochemical classification of the lithic material and to correlate the samples with the suspected source after a previous statistical analysis. The majority of the samples were classified as dacites and rhyolites. Only samples coming from CPO site, the closest place to CPL were made exclusively with the quarry rocks. A set of five samples from RCh2/87 and two samples from CTI appear to have same chemical composition as CPL in spite of this site is placed in the opposite bank of the Limay river suggesting that hunter-gatherers could accede to the quarry, eventually. Finally, only a set of five samples coming from RCh2/87 and CTI do not group with the quarry. This fact evidences the existence of secondary sources of supply. The information of this research allowed inferring ancient human mobility patterns in the region.
Keywords: A1 Journal article; Engineering sciences. Technology; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1007/S10967-013-2600-1
|
“Flexoelectricity and transport properties of phosphorene nanoribbons under mechanical bending”. Pandey T, Covaci L, Milošević, MV, Peeters FM, Physical Review B 103, 235406 (2021). http://doi.org/10.1103/PHYSREVB.103.235406
Abstract: We examine from first principles the flexoelectric properties of phosphorene nanoribbons under mechanical bending along armchair and zigzag directions. In both cases we find that the radial polarization depends linearly on the strain gradient. The flexoelectricity along the armchair direction is over 40% larger than along the zigzag direction. The obtained flexoelectric coefficients of phosphorene are four orders of magnitude larger than those of graphene and comparable to transition metal dichalcogenides. Analysis of charge density shows that the flexoelectricity mainly arises from the pz orbitals of phosphorus atoms. The electron mobilities in bent phosphorene can be enhanced by over 60% along the armchair direction, which is significantly higher than previous reports of mobility tuned by uniaxial strain. Our results indicate phosphorene is a candidate for a two-dimensional material applicable in flexible-electronic devices.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 12
DOI: 10.1103/PHYSREVB.103.235406
|