“Ultrasonication induces oxygenated species and defects onto exfoliated graphene”. Skaltsas T, Ke X, Bittencourt C, Tagmatarchis N, The journal of physical chemistry: C : nanomaterials and interfaces 117, 23272 (2013). http://doi.org/10.1021/jp4057048
Abstract: The effect of ultrasonication parameters, such as time and power applied, to exfoliate graphite in o-dichlorobenzene (o-DCB) and N-methyl-1,2-pyrrolidone (NMP) was examined. It was found that the concentration of graphene was higher in o-DCB, while its dispersibility was increased when sonication was applied for a longer period and/or at higher power. However, spectroscopic examination by X-ray photoelectron spectroscopy (XPS) revealed that ultrasonication causes defects and induces oxygen functional groups in the form of carboxylic acids and ethers/epoxides onto the graphene lattice. Additional proof for the latter arose from Raman, IR, and thermogravimetry studies. The carboxylic acids and ethers/epoxides onto exfoliated graphene were derived from air during ultrasonication and found independent of the solvent used for the exfoliation and the power and/or time ultrasonication applied. Quantitative evaluation of the amount of oxygenated species present on exfoliated graphene as performed by high-resolution XPS revealed that the relative oxygen percentage was higher when exfoliation was performed in NMP. Finally, the sonication time and/or power affected the oxygen content on exfoliated graphene, since extended ultrasonication resulted in a decrease in the oxygen content on exfoliated graphene, with a simultaneous increase of defected sp(3) carbon atoms.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 65
DOI: 10.1021/jp4057048
|
“Selective decoration of isolated carbon nanotubes by potassium evaporation : scanning photoemission microscopy and density functional theory”. Struzzi C, Erbahar D, Scardamaglia M, Amati M, Gregoratti L, Lagos, Van Tendeloo G, Snyders R, Ewels C, Bittencourt C, Journal of materials chemistry C : materials for optical and electronic devices 3, 2518 (2015). http://doi.org/10.1039/c4tc02478h
Abstract: Site selective doping of aligned carbon nanostructures represents a promising approach for their implementation in actual devices. In the present work we report on alkali metals decoration on low density vertically aligned carbon nanotubes, disclosing the possibility of engineering site selective depositions of potassium atoms on the carbon systems. Photoemission measurements were combined with microscopy demonstrating the effective spatial control of alkali deposition. The changes of electronic structures of locally doped carbon regions were studied by exploiting the ability of the scanning photoemission microscopy technique. From the analysis of experimental data supported by theoretical calculations, we show the tuning of the charge transfer from potassium to carbon atoms belonging to neighboring nanotubes or along the same tube structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.256
Times cited: 6
DOI: 10.1039/c4tc02478h
|
“Probing the interaction between gold nanoparticles and oxygen functionalized carbon nanotubes”. Suarez-Martinez I, Bittencourt C, Ke X, Felten A, Pireaux JJ, Ghijsen J, Drube W, Van Tendeloo G, Ewels CP, Carbon 47, 1549 (2009). http://doi.org/10.1016/j.carbon.2009.02.002
Abstract: The interaction between evaporated gold and pristine or oxygen plasma treated multi-walled carbon nanotubes (MWCNTs) is investigated. Experimental and theoretical results indicate that gold nucleation occurs at defect sites, whether initially present or introduced by oxygen plasma treatment. Uniform gold cluster dispersion is observed on plasma treated carbon nanotubes (CNTs) and associated with the presence of uniformly dispersed oxidized vacancy centres on the CNT surface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.337
Times cited: 38
DOI: 10.1016/j.carbon.2009.02.002
|
“Study of the interface between rhodium and carbon nanotubes”. Suarez-Martinez I, Ewels CP, Ke X, Van Tendeloo G, Thiess S, Drube W, Felten A, Pireaux J-J, Ghijsen J, Bittencourt C, ACS nano 4, 1680 (2010). http://doi.org/10.1021/nn9015955
Abstract: X-ray photoelectron spectroscopy at 3.5 keV photon energy, in combination with high-resolution transmission electron microscopy, is used to follow the formation of the interface between rhodium and carbon nanotubes. Rh nucleates at defect sites, whether initially present or induced by oxygen-plasma treatment. More uniform Rh cluster dispersion is observed on plasma-treated CNTs. Experimental results are compared to DFT calculations of small Rh clusters on pristine and defective graphene. While Rh interacts as strongly with the carbon as Ti, it is less sensitive to the presence of oxygen, suggesting it as a good candidate for nanotube contacts.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 26
DOI: 10.1021/nn9015955
|