“Pr/ZrO2 prepared by atomic trapping : an efficient catalyst for the conversion of glycerol to lactic acid with concomitant transfer hydrogenation of cyclohexene”. Tang Z, Liu P, Cao H, Bals S, Heeres HJ, Pescarmona PP, ACS catalysis 9, 9953 (2019). http://doi.org/10.1021/ACSCATAL.9B02139
Abstract: A series of heterogeneous catalysts consisting of highly dispersed Pt nanoparticles supported on nanosized ZrO2 (20 to 60 nm) was synthesized and investigated for the one-pot transfer hydrogenation between glycerol and cyclohexene to produce lactic acid and cyclohexane, without any additional H-2. Different preparation methods were screened, by varying the calcination and reduction procedures with the purpose of optimizing the dispersion of Pt species (i.e., as single-atom sites or extra-fine Pt nanoparticles) on the ZrO2 support. The Pt/ZrO2 catalysts were characterized by means of transmission electron microscopy techniques (HAADF-STEM, TEM), elemental analysis (ICP-OES, EDX mapping), N-2-physisorption, H-2 temperature-programmed-reduction (H-2-TPR), X-ray photoelectron spectroscopy (XPS), and X-ray diffraction (XRD). Based on this combination of techniques it was possible to correlate the temperature of the calcination and reduction treatments with the nature of the Pt species. The best catalyst consisted of subnanometer Pt clusters (<1 nm) and atomically dispersed Pt (as Pt2+ and Pt4+) on the ZrO2 support, which were converted into extra-fine Pt nanoparticles (average size = 1.4 nm) upon reduction. These nanoparticles acted as catalytic species for the transfer hydrogenation of glycerol with cyclohexene, which gave an unsurpassed 95% yield of lactic acid salt at 96% glycerol conversion (aqueous glycerol solution, NaOH as promoter, 160 degrees C, 4.5 h, at 20 bar N-2). This is the highest yield and selectivity of lactic acid (salt) reported in the literature so far. Reusability experiments showed a partial and gradual loss of activity of the Pt/ZrO2 catalyst, which was attributed to the experimentally observed aggregation of Pt nanoparticles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 10.614
Times cited: 46
DOI: 10.1021/ACSCATAL.9B02139
|
|
|
“Firsto order phase transformation in the Ni-Al system”. Tanner LE, Shapiro SM, Krumhansl JA, Schryvers D, Noda Y, Yamada Y, Barsch GR, Gooding R, Moss SC, Metallurgy and Ceramics (1992)
Abstract: First-order displacive phase transformations in alloys and compounds are of high technological importance. We have studied this class of phase transformation in the high-temperature-stable Ni-Al f32(B2) phase as a function of composition, temperature, and stress using transmission electron microscopy and neutron scattering. The results show in detail the direct relationship between the unusually low energies of the transformation-related phonon modes and the development of pre-transformation microstructures (strain-embryos, etc.) via anharmonic coupling processes that ultimately lead to the nucleation and growth of the low-temperature martensitic phases. With these results, it is now possible to develop effective models for nonclassical heterogeneous nucleation of martensite transformations in bulk materials. This tills a critical gap and sets the stage for us to proceed in developing a more global understanding of condensed matter transformations including the coupling of displacive with replacive mechanisms.
Keywords: A3 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
|
|
|
“Review of phonon behaviour and microstructural development leading to martensitic transformations in NixAl100-x alloys”. Tanner LE, Shapiro SM, Schryvers D, Noda Y, Shape memory materials and phenomena: fundamental aspects and applications 246, 265 (1992)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 4
|
|
|
“Controllable synthesis of novel one-dimensional carbon nanomaterials on an alkali-element-modified Cu catalyst”. Tao XY, Zhang XB, Cheng J-P, Liu F, Li Y, Van Tendeloo G, Nanotechnology 17, 224 (2006). http://doi.org/10.1088/0957-4484/17/1/037
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 4
DOI: 10.1088/0957-4484/17/1/037
|
|
|
“Synthesis of multi-branched porous carbon nanofibers and their application in electrochemical double-layer capacitors”. Tao XY, Zhang XB, Zhang L, Cheng JP, Liu F, Luo JH, Luo ZQ, Geise HJ, Carbon 44, 1425 (2006). http://doi.org/10.1016/j.carbon.2005.11.024
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.337
Times cited: 77
DOI: 10.1016/j.carbon.2005.11.024
|
|
|
“Investigation of stacking disorder in Li2SnO3”. Tarakina NV, Denisova TA, Maksimova LG, Baklanova YV, Tyutyunnik AP, Berger IF, Zubkov VG, Van Tendeloo G, Zeitschrift für Kristallographie , 375 (2009). http://doi.org/10.1524/zksu.2009.0055
Abstract: A crystal structure investigation of the low temperature Li2SnO3 modification has been carried out. X-ray, neutron powder and electron diffraction data showed that this compound crystallizes in a monoclinic unit cell with parameters: a = 5.3033(2)Å, b = 9.1738(3)Å, c = 10.0195(2)Å, β ~ 100.042(2)º and has stacking disorder along the c-axis. Simulation of diffraction patterns with different stacking faults mainly reveal the presence of rotational stacking faults with a probability of about 40% .
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 16
DOI: 10.1524/zksu.2009.0055
|
|
|
“Crystal structure and magnetic properties of complex oxides Mg4-xNixO9, 0\leq x\leq4”. Tarakina NV, Nikulina EA, Hadermann J, Kellerman DG, Tyutunnik AP, Berger IF, Zubkov VG, Van Tendeloo G, Journal of solid state chemistry 180, 3180 (2007). http://doi.org/10.1016/j.jssc.2007.09.007
Abstract: In the Mg4−xNixNb2O9 (0x4) system two ranges of solid solution have been found. One of the solid solutions has a corundum-related structure type (space group ); the second one adopts the II-Ni4Nb2O9 structure type (space group Pbcn). The unit cell constants and atomic positions have been determined and refined using neutron powder diffraction data. Electron diffraction and high-resolution transmission electron microscopy (HRTEM) from MgNi3Nb2O9 crystals identify the presence of planar defects and the intergrowth of several (structurally related) phases. The magnetic susceptibility of Mg3NiNb2O9, measured in the temperature range T=2300 K, shows no indications of magnetic ordering at low temperatures, while for MgNi3Nb2O9 there is a magnetic ordering at temperatures below 45.5 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 3
DOI: 10.1016/j.jssc.2007.09.007
|
|
|
“Crystal structure of the group of optical materials Ln2MeGe4O12 (Me = Ca, Mn)”. Tarakina NV, Zubkov VG, Leonidov II, Tyutunnik AP, Surat LL, Hadermann J, Van Tendeloo G, Zeitschrift für Kristallographie , 401 (2009). http://doi.org/10.1524/zksu.2009.0059
Abstract: The crystal structure of the group of optical materials Ln2MeGe4O12, Ln = Eu, Gd, Dy-Lu, Y; Me = Ca, Mn and of the solid solution (Y1-xErx)2CaGe4O12 (x = 0 – 1), promising materials for photonics, has been studied in detail. The crystal structure of all compounds exhibit two alternating layers: one formed by Ln and Me atoms and another by cyclic [Ge4O12]8- anions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 7
DOI: 10.1524/zksu.2009.0059
|
|
|
“One-Step Microheterogeneous Formation of Rutile@Anatase Core–Shell Nanostructured Microspheres Discovered by Precise Phase Mapping”. Tarasov A, Hu Z-Y, Meledina M, Trusov G, Goodilin E, Van Tendeloo G, Dobrovolsky Y, The journal of physical chemistry: C : nanomaterials and interfaces 121, 4443 (2017). http://doi.org/10.1021/acs.jpcc.6b12991
Abstract: Nanostructured core−shell microspheres with a rough rutile core and a thin anatase shell are synthesized via a one-step heterogeneous templated hydrolysis process of TiCl4 vapor on the aerosol water−air interface. The rutile-in-anatase core−shell structure has been evidenced by different electron microscopy techniques, including electron energy-loss spectroscopy and 3D electron tomography. A new mechanism for the formation of a crystalline rutile core inside the anatase shell is proposed based on a statistical evaluation of a large number of electron microscopy data. We found that the control over the TiCl4 vapor pressure, the ratio between TiCl4 and H2O aerosol, and the reaction conditions plays a crucial role in the formation of the core−shell morphology and increases the yield of nanostructured microspheres.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 4
DOI: 10.1021/acs.jpcc.6b12991
|
|
|
Tavernier S, op de Beeck W, Ghekiere J-P, Van Tendeloo G (1996) Positively charged toner for use in electrostatography : US5532097 : 07/02/1996
Keywords: Patent; Electron microscopy for materials research (EMAT)
|
|
|
“In situ transmission electron microscopy study of Ni silicide phases formed on (001) Si active lines”. Teodorescu V, Nistor L, Bender H, Steegen A, Lauwers A, Maex K, van Landuyt J, Journal of applied physics 90, 167 (2001). http://doi.org/10.1063/1.1378812
Abstract: The formation of Ni silicides is studied by transmission electron microscopy during in situ heating experiments of 12 nm Ni layers on blanket silicon, or in patterned structures covered with a thin chemical oxide. It is shown that the first phase formed is the NiSi2 which grows epitaxially in pyramidal crystals. The formation of NiSi occurs quite abruptly around 400 degreesC when a monosilicide layer covers the disilicide grains and the silicon in between. The NiSi phase remains stable up to 800 degreesC, at which temperature the layer finally fully transforms to NiSi2. The monosilicide grains show different epitaxial relationships with the Si substrate. Ni2Si is never observed. (C) 2001 American Institute of Physics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 97
DOI: 10.1063/1.1378812
|
|
|
“Laser induced phase transition in iron thin films”. Teodorescu VS, Mihailescu IN, Dinescu M, Chitica N, Nistor LC, van Landuyt J, Barborica A, Journal de physique: 3: applied physics, materials science, fluids, plasma and instrumentation 4, 127 (1994). http://doi.org/10.1051/jp4:1994427
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1051/jp4:1994427
|
|
|
“The study of a crater forming on the surface of a Ti target submitted to multipulse excimer laser irradiation under low pressure N2”. Teodorescu VS, Mihailescu IN, Gyorgy E, Luches A, Martino M, Nistor LC, van Landuyt J, Hermann J, Journal of modern optics 43, 1773 (1996). http://doi.org/10.1080/095003496154815
Abstract: A Ti target was submitted to laser ablation in low ambient pressure N-2. Electron microscopy examination of the cross-section of the crater zone forming on the Ti target, and XPS analyses, indicate that there is a small effect on the nitridation processes taking place on and in the vicinity of the target. The studies show a zone influenced by the multipulse laser treatment extending beneath the crater down to a depth of the same order of magnitude as the crater depth (i.e. similar to 10 mu m). In this zone, TiN could be identified as being present only in traces, while the whole zone exhibited a layer structure with differences in morphology and mechanical wear.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.008
Times cited: 11
DOI: 10.1080/095003496154815
|
|
|
“High resolution TEM observation of in situ colloid formation in CaF2 crystals”. Teodorescu VS, Nistor LC, van Landuyt J, Materials science forum 239-241, 671 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 3
|
|
|
“TEM study of laser induced phase transition in iron thin films”. Teodorescu VS, Nistor LC, van Landuyt J, Dinescu M, Materials research bulletin 29, 63 (1994). http://doi.org/10.1016/0025-5408(94)90106-6
Abstract: Laser induced phase transition from b.c.c.(alpha) to f.c.c.(gamma) iron thin films is studied by high resolution TEM. The iron film has been covered on both sides with carbon layers to protect it against oxidation. Single pulse, tau FWHM = 20ns KrF (lambda = 248nm) excimer laser irradiation was performed in air with the film on the substrate. The laser pulse acts like a heat pulse followed by a rapid quenching revealing sequential aspects of the phase transition process. The presence of a fine mixture of the alpha + gamma phases between the alpha and gamma regions of the film has been interpreted as an incomplet transformation. The results are explained by assuming that the transformation took place via a phonon drag mechanism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.288
Times cited: 2
DOI: 10.1016/0025-5408(94)90106-6
|
|
|
“Interfacial oxidation and photoluminescence of InP-Based core/shell quantum dots”. Tessier MD, Baquero EA, Dupont D, Grigel V, Bladt E, Bals S, Coppel Y, Hens Z, Nayral C, Delpech F, Chemistry of materials 30, 6877 (2018). http://doi.org/10.1021/ACS.CHEMMATER.8B03117
Abstract: Indium phosphide colloidal quantum dots (QDs) are emerging as an efficient cadmium-free alternative for optoelectronic applications. Recently, syntheses based on easy-to-implement aminophosphine precursors have been developed. We show by solid-state nuclear magnetic resonance spectroscopy that this new approach allows oxide-free indium phosphide core or core/shell quantum dots to be made. Importantly, the oxide-free core/shell interface does not help in achieving higher luminescence efficiencies. We demonstrate that in the case of InP/ZnS and InP/ZnSe QDs, a more pronounced oxidation concurs with a higher photoluminescence efficiency. This study suggests that a II-VI shell on a III-V core generates an interface prone to defects. The most efficient InP/ZnS or InP/ZnSe QDs are therefore made with an oxide buffer layer between the core and the shell: it passivates these interface defects but also results in a somewhat broader emission line width.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 74
DOI: 10.1021/ACS.CHEMMATER.8B03117
|
|
|
“Additivity of Atomic Strain Fields as a Tool to Strain-Engineering Phase-Stabilized CsPbI3Perovskites”. Teunissen JL, Braeckevelt T, Skvortsova I, Guo J, Pradhan B, Debroye E, Roeffaers MBJ, Hofkens J, Van Aert S, Bals S, Rogge SMJ, Van Speybroeck V, The Journal of Physical Chemistry C 127, 23400 (2023). http://doi.org/10.1021/acs.jpcc.3c05770
Abstract: CsPbI3 is a promising perovskite material for photovoltaic applications in its photoactive perovskite or black phase. However, the material degrades to a photovoltaically inactive or yellow phase at room temperature. Various mitigation strategies are currently being developed to increase the lifetime of the black phase, many of which rely on inducing strains in the material that hinder the black-to-yellow phase transition. Physical insight into how these strategies exactly induce strain as well as knowledge of the spatial extent over which these strains impact the material is crucial to optimize these approaches but is still lacking. Herein, we combine machine learning potential-based molecular dynamics simulations with our in silico strain engineering approach to accurately quantify strained large-scale atomic structures on a nanosecond time scale. To this end, we first model the strain fields introduced by atomic substitutions as they form the most elementary strain sources. We demonstrate that the magnitude of the induced strain fields decays exponentially with the distance from the strain source, following a decay rate that is largely independent of the specific substitution. Second, we show that the total strain field induced by multiple strain sources can be predicted to an excellent approximation by summing the strain fields of each individual source. Finally, through a case study, we illustrate how this additive character allows us to explain how complex strain fields, induced by spatially extended strain sources, can be predicted by adequately combining the strain fields caused by local strain sources. Hence, the strain additivity proposed here can be adopted to further our insight into the complex strain behavior in perovskites and to design strain from the atomic level onward to enhance their sought-after phase stability.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 3.7
DOI: 10.1021/acs.jpcc.3c05770
|
|
|
“Fe-containing magnesium aluminate support for stability and carbon control during methane reforming”. Theofanidis SA, Galvita VV, Poelman H, Dharanipragada NVRA, Longo A, Meledina M, Van Tendeloo G, Detavernier C, Marin GB, ACS catalysis 8, 5983 (2018). http://doi.org/10.1021/ACSCATAL.8B01039
Abstract: We report a MgFexAl2-xO4 synthetic spinel, where x varies from 0 to 0.26, as support for Ni-based catalysts, offering stability and carbon control under various conditions of methane reforming. By incorporation of Fe into a magnesium aluminate spine!, a support is created with redox functionality and high thermal stability, as concluded from temporal analysis of products (TAP) experiments and redox cycling, respectively. A diffusion coefficient of 3 x 10(-17) m(2) s(-1) was estimated for lattice oxygen at 993 K from TAP experiments. X-ray diffraction (XRD) and extended X-ray absorption fine structure (EXAFS) modeling identified that the incorporation of iron occurs as Fe3+ in the octahedral sites of the spinel lattice, replacing aluminum. Simulation of the X-ray absorption near edge structure (XANES) spectrum of the reduced support showed that 60 +/- 10% of iron was reduced from 3+ to 2+ at 1073 K, while there was no formation of metallic iron. A series of Ni/MgFexAl2-xO4 catalysts, where x varies from 0 to 0.26, was synthesized and reduced, yielding a supported Ni-Fe alloy. The evolution of the catalyst structure during H-2 temperature-programmed reduction (TPR) and CO2 temperature-programmed oxidation (TPO) was examined using time-resolved in situ XRD and XANES. During reforming, iron in both the support and alloy keeps control of carbon accumulation, as confirmed by O-2-TPO on the spent catalysts. By fine tuning the amount of Fe in MgFexAl2-xO4, a supported alloy was obtained with a Ni/Fe molar ratio of similar to 10, which was active for reforming and stable. By comparison of the performance of Ni-based catalysts with Fe either incorporated into or deposited onto the support, the location of Fe within the support proved crucial for the stability and carbon mitigation under reforming conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 10.614
Times cited: 18
DOI: 10.1021/ACSCATAL.8B01039
|
|
|
“Formation of carbon nitride nanospheres by ion implantation”. Thomé, T, Colaux JL, Colomer J-F, Bertoni G, Terwagne G, Materials chemistry and physics 103, 290 (2007). http://doi.org/10.1016/j.matchemphys.2007.02.028
Abstract: Carbon nitride nanospheres have been synthesized into copper by simultaneous high fluence (10(18) at. cm(-2)) implantations of C-12 and N-15 ions. The composition of the implanted region has been measured using C-12(d,p(0))C-13 and N-15(d,alpha(0))C-13 nuclear reactions induced by a 1.05 MeV deuteron beam. The C-12 and N-15 depth profiles are very close and the retained doses into copper are relatively high, which indicates that carbon and nitrogen diffusion processes are likely limited during implantation. High resolution transmission electron microscopy (HRTEM) observations and electron diffraction (ED) analyses have been carried out to determine the structure of the nanospheres formed during implantation. Some consist in small hollow amorphous nanocapsules with sizes ranging from 30 to 100 nm. Large gas bubbles with diameters up to 300 mn have also been observed in the copper matrix. Electron energy-loss spectroscopy (EELS) measurements performed on the small nanocapsules indicate that their shells are composed of carbon and nitrogen. (c) 2007 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.084
Times cited: 1
DOI: 10.1016/j.matchemphys.2007.02.028
|
|
|
“Nanodiamonds do not provide unique evidence for a Younger Dryas impact”. Tian H, Schryvers D, Claeys P, Proceedings of the National Academy of Sciences of the United States of America 108, 40 (2011). http://doi.org/10.1073/pnas.1007695108
Abstract: Microstructural, δ13C isotope and C/N ratio investigations were conducted on excavated material from the black Younger Dryas boundary in Lommel, Belgium, aiming for a characterisation of the carbon content and structures. Cubic diamond nanoparticles are found in large numbers. The larger ones with diameters around or above 10 nm often exhibit single or multiple twins. The smaller ones around 5 nm in diameter are mostly defect-free. Also larger flake-like particles, around 100 nm in lateral dimension, with a cubic diamond structure are observed as well as large carbon onion structures. The combination of these characteristics does not yield unique evidence for an exogenic impact related to the investigated layer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.661
Times cited: 32
DOI: 10.1073/pnas.1007695108
|
|
|
“Stability of Ni in nitinol oxide surfaces”. Tian H, Schryvers D, Liu D, Jiang Q, van Humbeeck J, Acta biomaterialia 7, 892 (2011). http://doi.org/10.1016/j.actbio.2010.09.009
Abstract: The stability of Ni in titanium oxide surface layers on nitinol wires known to release certain amounts of Ni was investigated by first principles density functional theory and transmission electron microscopy. The oxides were identified as a combination of TiO and TiO2 depending on the thickness of the layer. The calculations indicate that free Ni atoms can exist in TiO at ambient temperature while Ni particles form in TiO2, which was confirmed by the transmission electron microscopy observations. The results are discussed with respect to surface stability and Ni release due to free Ni atoms and Ni particles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 39
DOI: 10.1016/j.actbio.2010.09.009
|
|
|
“Fabrication and characterization of functionally graded Ni-Ti multilayer thin films”. Tian H, Schryvers D, Mohanchandra KP, Carman GP, van Humbeeck J, Functional materials letters 2, 61 (2009). http://doi.org/10.1142/S1793604709000570
Abstract: A functionally graded multilayer NiTi thin film was deposited on a SiO2/Si substrate by d.c. sputtering using a ramped heated NiTi alloy target. The stand-alone films were crystallized at 500°C in vacuum better than 10-7 Torr. Transmission electron microscopy micrographs taken along the film cross section show two distinct regions, thin and thick, with weak R and B2 phases, respectively. The film compositions along the thickness were measured and quantified using the standard-less EELSMODEL method. The film deposited during the initial thermal ramp (thin regions) displays an average of 54 at.% Ni while the film deposited at a more elevated target temperature (thick regions) shows about 51 at.% Ni.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.234
Times cited: 9
DOI: 10.1142/S1793604709000570
|
|
|
“Microstructure of surface and subsurface layers of a Ni-Ti shape memory microwire”. Tian H, Schryvers D, Shabalovskaya S, van Humbeeck J, Microscopy and microanalysis 15, 62 (2009). http://doi.org/10.1017/S1431927609090059
Abstract: The microstructure of a 55 Êm diameter, cold-worked Ni-Ti microwire is investigated by different transmission electron microscopy techniques. The surface consists of a few hundred nanometer thick oxide layer composed of TiO and TiO2 with a small fraction of inhomogeneously distributed Ni. The interior of the wire has a core-shell structure with primarily B2 grains in the 1 Êm thick shell, and heavily twinned B19 martensite in the core. This core-shell structure can be explained by a concentration gradient of the alloying elements resulting in a structure separation due to the strong temperature dependence of the martensitic start temperature. Moreover, in between the B2 part of the metallic core-shell and the oxide layer, a Ni3Ti interfacial layer is detected.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 15
DOI: 10.1017/S1431927609090059
|
|
|
“TEM study of the mechanism of Ni ion release from Nitinol wires with original oxides”. Tian H, Schryvers D, Shabalovskaya S, van Humbeeck J, , 05027 (2009). http://doi.org/10.1051/esomat/200905027
Abstract: The surface of commercial Nitinol wires with original oxides and a thickness in the 30-190 nm range was investigated by different state of art TEM techniques. The oxide surface layer was identified as a combination of TiO and TiO2 depending on the processing of the wire. Between the core of the wires and the oxidized surface, an interfacial Ni3Ti nanolayer was observed while Ni nanoparticles are found inside the original oxide. The particle sizes, their distribution in the surface and the Ti-O stoichiometry were deduced from the analysis of the obtained data. Molecular dynamics calculations performed for evaluation of the stability of Ni particles relative to the atomic state revealed that a pure Ni particle has a lower energy than free Ni atoms inside the TiO2 lattice. The obtained results are discussed with respect to surface stability and Ni release in the human body.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1051/esomat/200905027
|
|
|
“Interface-induced modulation of charge and polarization in thin film Fe3O4”. Tian H, Verbeeck J, Brück S, Paul M, Kufer D, Sing M, Claessen R, Van Tendeloo G, Advanced materials 26, 461 (2014). http://doi.org/10.1002/adma.201303329
Abstract: Charge and polarization modulations in Fe3O4 are controlled by taking advantage of interfacial strain effects. The feasibility of oxidation state control by strain modification is demonstrated and it is shown that this approach offers a stable configuration at room temperature. Direct evidence of how a local strain field changes the atomic coordination and introduces atomic displacements leading to polarization of Fe ions is presented.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 15
DOI: 10.1002/adma.201303329
|
|
|
“The chemical vapor infiltration of exfoliated graphite to produce carbon/carbon composites”. Tikhomirov AS, Sorokina NE, Shornikova ON, Morozov VA, Van Tendeloo G, Avdeev VV, Carbon 49, 147 (2011). http://doi.org/10.1016/j.carbon.2010.08.054
Abstract: Chemical vapor infiltration was used for the production of carbon/carbon composites based on exfoliated graphite and pyrolytic carbon Two different exfoliated graphites compacted to densities of 0 05-0 4 g/cm(3) were used as a preform The influence of the synthesis conditions (temperature, pressure, time etc) on the degree of infiltration, the pyrolytic carbon morphology and the C/C composite characteristics was examined using Raman spectroscopy, scanning electron microscopy and low-temperature nitrogen adsorption (C) 2010 Elsevier Ltd All rights reserved
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.337
Times cited: 7
DOI: 10.1016/j.carbon.2010.08.054
|
|
|
“Preparation and luminescence of bulk oxyfluoride glasses doped with Ag nanoclusters”. Tikhomirov VK, Rodriguez VD, Kutznetsov D, Kirilenko D, Van Tendeloo G, Moshchalkov VV, Optics express 18, 22032 (2010). http://doi.org/10.1364/OE.18.022032
Abstract: Bulk oxyfluoride glasses doped with Ag nanoclusters have been prepared using the melt quenching technique. When pumped in the absorption band of Ag nanoclusters between 300 to 500 nm, these glasses emit a very broad luminescence band covering all the visible range with a weak tail extending into the near infrared. The maximum of the luminescence band and its color shifts to the blue with a shortening of the excitation wavelength and an increasing ratio of oxide to fluoride components, resulting in white color luminescence at a particular ratio of oxide to fluoride; with a quantum yield above 20%.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.307
Times cited: 74
DOI: 10.1364/OE.18.022032
|
|
|
“Optimizing Er/Yb ratio and content in Er-Yb co-doped glass-ceramics for enhancement of the up- and down-conversion luminescence”. Tikhomirov VK, Rodríguez VD, Méndez-Ramos J, del- Castillo J, Kirilenko D, Van Tendeloo G, Moshchalkov VV, Solar energy materials and solar cells 100, 209 (2012). http://doi.org/10.1016/j.solmat.2012.01.019
Abstract: Er3+Yb3+ co-doped transparent glass-ceramics with varying Er/Yb content and ratio have been prepared. High quantum yields for up- and down-conversion luminescence by energy transfer from Yb3+ to Er3+ and from Er3+ to Yb3+, respectively, have been detected and optimized with respect to the Er/Yb content and ratio, and proposed in particular for up- and down-conversion of solar spectrum for enhancement of the efficiency of solar cells. The rise and decay kinetics for the population of the excited levels of Er3+ and Yb3+ have been studied and fit. Based on these experimental data, the mechanisms for the energy transfers have been suggested with emphasis on the optimized Er/Yb content and ratio for enhancement of the efficiency of the Er3+↔Yb3+ energy transfers.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.784
Times cited: 66
DOI: 10.1016/j.solmat.2012.01.019
|
|
|
“Luminescence of oxyfluoride glasses co-doped with Ag nanoclusters and Yb3+ ions”. Tikhomirov VK, Vosch T, Fron E, Rodríguez VD, Velázquez JJ, Kirilenko D, Van Tendeloo G, Hofkens J, Van der Auweraer M, Moshchalkov VV, RSC advances 2, 1496 (2012). http://doi.org/10.1039/c1ra01026c
Abstract: Bulk oxyfluoride glasses co-doped with Ag nanoclusters and Yb3+ ions have been prepared by a melt quenching technique. When excited in the absorption band of the Ag nanoclusters between 300 to 500 nm, these glasses emit a broad band characteristic of the Ag nanoclusters between 400 to 750 nm as well as an emission band between 900 to 1100 nm, originating from Yb3+ ions. The intensity ratio of the Yb3+/Ag emission bands increases with the Ag doping level at a fixed concentration of Yb3+, indicating the presence of energy transfer mechanism from the Ag nanoclusters to the Yb3+ ions. Comparison of time-resolved decay kinetics of the luminescence in the respectively Ag nanocluster-Yb3+ co-doped and single Ag nanocluster doped glasses, hints towards an energy transfer from the red and infrared emitting Ag nanoclusters to the Yb3+ ions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 46
DOI: 10.1039/c1ra01026c
|
|
|
“Twinning in pure Ti subjected to monotonic simple shear deformation”. Tirry W, Bouvier S, Benmhenni N, Hammami W, Habraken AM, Coghe F, Schryvers D, Rabet L, Materials characterization 72, 24 (2012). http://doi.org/10.1016/j.matchar.2012.07.001
Abstract: The aim of this paper is to provide a thorough study on the occurrence and importance of deformation twinning in simple shear deformed pure α-Ti. A statistically relevant inspection of the morphology of the deformation twins in relation to the applied strain/deformation is performed. The investigated microstructural aspects are the twin volume fraction, the twin thickness distribution and the resolved shear stress distribution on the twin plane. All these aspects are examined as a function of the twin types and two initial textures. Monotonic simple shear experiments are carried out for three different loading directions with respect to a direction linked to the initial crystallographic texture. EBSD and TEM observations reveal the presence of View the MathML source and View the MathML source twins. The statistical analysis reveals that View the MathML source and View the MathML source twins have a similar average thickness around 1.9 nm, but the View the MathML source twins show a far larger spread on their thickness and can grow to almost the size of the original parent grain. Correlation of the twin fractions with the RSS analysis shows that RSS is an acceptable method explaining the difference in twin fractions for different textures and orientations. A detailed analysis shows that View the MathML source twins occur in average with a smaller volume fraction but with a higher RSS, indicating they are more difficult to nucleate or grow compared to View the MathML source twinning. In general a higher RSS value on the twin plane is not connected to a higher twin thickness; only in the case of View the MathML source twins the highest RSS values show clearly thicker twins.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 25
DOI: 10.1016/j.matchar.2012.07.001
|
|