“New insights in the formation of combined zeolitic/mesoporous materials by using a one-pot templating synthesis”. Vernimmen J, Meynen V, Herregods SJF, Mertens M, Lebedev OI, Van Tendeloo G, Cool P, European journal of inorganic chemistry , 4234 (2011). http://doi.org/10.1002/ejic.201100268
Abstract: Zeolitic growth is often absent or occurs in separate phases when synthetic strategies based on the combination of zeolite templates and mesopore templating agents are applied. In this work, zeolitic growth and mesopore formation have been investigated at different temperatures by applying a one-pot templating approach, based on a TS-1 zeolite synthesis whereby part of the microtemplate (tetrapropylammonium hydroxide, TPAOH) is replaced by a mesotemplate (hexadecyltrimethylammonium bromide, CTMABr). Moreover, the synthesis duration and the molar ratio of the microtemplate/mesotemplate have also been studied. The different syntheses clearly show the inherent competitive mechanism between zeolitic growth and mesopore formation. These insights have led to the conclusion that by following a one-pot templating strategy with standard, nonexotic commercial templates, i.e. CTMABr and TPAOH, it is not possible to develop a true hierarchical mesoporous zeolite, meaning a mesoporous siliceous material with highly crystalline zeolitic walls. The resultant materials are instead combined zeolitic/mesoporous composite structures with, however, highly tuneable and controllable porosity characteristics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.444
Times cited: 7
DOI: 10.1002/ejic.201100268
|
“Formation of a Ti-siliceous trimodal material with macroholes, mesopores and zeolitic features via a one-pot templating synthesis”. Vernimmen J, Meynen V, Mertens M, Lebedev OI, Van Tendeloo G, Cool P, Journal of porous materials 19, 153 (2012). http://doi.org/10.1007/s10934-011-9470-0
Abstract: Based on a facile one-pot templating synthesis, using a TS-1 zeolite recipe whereby part of the zeolite structure directing agent is replaced by a mesopore templating agent, a trimodal material is formed. The resulting meso-TSM material combines mesoporosity (Ti-MCM-41) with zeolitic features (TS-1) and a unique sheet-like morphology with uniform macroporous voids (macroholes). Moreover, the macrohole formation, mesoporosity and zeolitic properties of the meso-TSM material can be controlled in a straightforward way by adjusting the length of the hydrothermal treatment. This newly developed material may imply great potential for catalytic redox applications and diffusion limitated processes because of its highly tunable character in all three dimensions (micro-, meso- and macroporous scale).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 1.624
Times cited: 2
DOI: 10.1007/s10934-011-9470-0
|
“Nanodiamond photoemitters based on strong narrow-band luminescence from silicon-vacancy defects”. Vlasov II, Barnard AS, Ralchenko VG, Lebedev OI, Kanzyuba MV, Saveliev AV, Konov VI, Goovaerts E, Advanced materials 21, 808 (2009). http://doi.org/10.1002/adma.200802160
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Nanostructured and organic optical and electronic materials (NANOrOPT)
Impact Factor: 19.791
Times cited: 98
DOI: 10.1002/adma.200802160
|
“Nitrogen and luminescent nitrogen-vacancy defects in detonation nanodiamond”. Vlasov II, Shenderova O, Turner S, Lebedev OI, Basov AA, Sildos I, Rähn M, Shiryaev AA, Van Tendeloo G, Small 6, 687 (2010). http://doi.org/10.1002/smll.200901587
Abstract: An efficient method to investigate the microstructure and spatial distribution of nitrogen and nitrogen-vacancy (N-V) defects in detonation nanodiamond (DND) with primary particle sizes ranging from approximately 3 to 50 nm is presented. Detailed analysis reveals atomic nitrogen concentrations as high as 3 at% in 50% of diamond primary particles with sizes smaller than 6 nm. A non-uniform distribution of nitrogen within larger primary DND particles is also presented, indicating a preference for location within the defective central part or at twin boundaries. A photoluminescence (PL) spectrum with well-pronounced zero-phonon lines related to the N-V centers is demonstrated for the first time for electron-irradiated and annealed DND particles at continuous laser excitation. Combined Raman and PL analysis of DND crystallites dispersed on a Si substrate leads to the conclusion that the observed N-V luminescence originates from primary particles with sizes exceeding 30 nm. These findings demonstrate that by manipulation of the size/nitrogen content in DND there are prospects for mass production of nanodiamond photoemitters based on bright and stable luminescence from nitrogen-related defects.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 84
DOI: 10.1002/smll.200901587
|
“Hybrid diamond-graphite nanowires produced by microwave plasma chemical vapor deposition”. Vlasov IL, Lebedev OI, Ralchenko VG, Goovaerts E, Bertoni G, Van Tendeloo G, Konov VI, Advanced materials 19, 4058 (2007). http://doi.org/10.1002/adma.200700442
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Nanostructured and organic optical and electronic materials (NANOrOPT)
Impact Factor: 19.791
Times cited: 75
DOI: 10.1002/adma.200700442
|
“Nanoscale ordering in oxygen deficient quintuple perovskite Sm2-\epsilonBa3+\epsilonFe5O15-\delta : implication for magnetism and oxygen stoichiometry”. Volkova NE, Lebedev OI, Gavrilova LY, Turner S, Gauquelin N, Seikh MM, Caignaert V, Cherepanov VA, Raveau B, Van Tendeloo G, Chemistry of materials 26, 6303 (2014). http://doi.org/10.1021/cm503276p
Abstract: The investigation of the system SmBaFe-O in air has allowed an oxygen deficient perovskite Sm2-epsilon Ba3+epsilon Fe5O15-delta (delta = 0.75, epsilon = 0.125) to be synthesized. In contrast to the XRPD pattern which gives a cubic symmetry (a(p) = 3.934 angstrom), the combined HREM/EELS study shows that this phase is nanoscale ordered with a quintuple tetragonal cell, a(p) X a(p) X 5(ap). The nanodomains exhibit a unique stacking sequence of the A-site cationic layers along the crystallographic c-axis, namely SmBaBa/SmBa/SmBaSm, and are chemically twinned in the three crystallographic directions. The nanoscale ordering of this perovskite explains its peculiar magnetic properties on the basis of antiferromagnetic interactions with spin blockade at the boundary between the nanodomains. The variation of electrical conductivity and oxygen content of this oxide versus temperature suggest potential SOFC applications. They may be related to the particular distribution of oxygen vacancies in the lattice and to the 3d(5)(L) under bar configuration of iron.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 16
DOI: 10.1021/cm503276p
|
“Phase transition and magnetic anisotropy of (La,Sr)MnO3 thin films”. Wang Z-H, Kronmüller H, Lebedev OI, Gross GM, Razavi FS, Habermeier HU, Shen BG, Physical review : B : condensed matter and materials physics 65, 054411 (2002). http://doi.org/10.1103/PhysRevB.65.054411
Abstract: The magnetic proper-ties and their correlation with the microstructure and electrical transport are investigated in La0.88Sr0.1MnO3 films grown on (100)SrTiO3 Single crystal substrates with thickness ranging from 100 to 2500 Angstrom. The ultrathin film (t = 100 Angstrom) has a single ferromagnetic transition (FMT) at T-c of 250 K, whereas the thicker films exhibit two FMTs, with the main one at a lowered T-c of 200 K while the minor one around 300 K. Furthermore, a thickness dependent magnetic anisotropy has been found, strongly indicating the existence of strain effect, which is also revealed by the transmission electron microscopy study. The suppressed Jahn-Teller distortion (JTD) by the epitaxial strain, and the recovered JTD due to the strain relexation are suggested to explain the metallic behavior in thin films and the insulating behavior in the thick film (t = 2500 Angstrom), repectively.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 23
DOI: 10.1103/PhysRevB.65.054411
|
“Crosshatching on La0.5Ca0.5MnO3 ultrathin films epitaxially grown on SrTiO3(100)”. Wang Z-H, Lebedev OI, Van Tendeloo G, Cristiani G, Habermeier H-U, Physical review : B : condensed matter and materials physics 77, 1 (2008). http://doi.org/10.1103/PhysRevB.77.115330
Abstract: The morphological evolution in La(0.5)Ca(0.5)MnO(3)/SrTiO(3)(100) ultrathin films has been revealed by atomic force microscopy. It was found that ordered linear defects, which are in 1-2 unit cells high and oriented along the cubic [110] and [100] directions, first appear on the smooth surface of films with a thickness of 10 nm. As the epitaxial growth proceeds, these lines on surface develop into a crosshatch pattern for films with a thickness of 25 nm. Using the results of transmission electron microscopy and electrical measurements, we discuss the interplay between the surface pattern formation, the internal dislocation structure, and the variations in the electrical properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 8
DOI: 10.1103/PhysRevB.77.115330
|
“Preparing polymer films doped with magnetic nanoparticles by spin-coating and melt-processing can induce an in-plane magnetic anisotropy”. Wouters J, Lebedev OI, Van Tendeloo G, Yamada H, Sato N, Vanacken J, Moshchalkov VV, Verbiest T, Valev VK, Journal of applied physics 109, 076105 (2011). http://doi.org/10.1063/1.3572048
Abstract: Faraday rotation has been used to investigate a series of polymer films doped with magnetic iron oxide nanoparticles. The films have been prepared by spin-coating and melt-processing. In each case, upon varying the angle of optical incidence on the films, an in-plane magnetic anisotropy is observed. The effect of such an anisotropy on the Faraday rotation as a function of the angle of optical incidence is verified by comparison with magnetically poled films. These results demonstrate that care should be taken upon analyzing the magnetic behavior of such films on account of the sample preparation techniques themselves being able to affect the magnetization.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 10
DOI: 10.1063/1.3572048
|
“Faceted sidewalls of silicon nanowires: Au-induced structural reconstructions and electronic properties”. Xu T, Nys J-P, Addad A, Lebedev OI, Urbieta A, Salhi B, Berthe M, Grandidier B, Stievenard D, Physical review : B : condensed matter and materials physics 81, 115403 (2010). http://doi.org/10.1103/PhysRevB.81.115403
Abstract: Si nanowires with a ⟨111⟩ orientation, synthesized by vapor-liquid-solid process with low silane partial pressure reactant and gold as the catalyst, are known to exhibit sawtooth facets containing gold adsorbates. We report herein the study of the nanowire morphology by means of transmission electron microscopy and scanning tunneling microscopy. The nanowires consist of faceted sidewalls. The number of the sidewalls changes from 12 to 6 along the growth axis, giving rise to nanowires with an irregular hexagonal cross section at their base. The sidewalls are covered with Au-rich clusters. Their facets also exhibit atomic structures that reveal the presence of gold, resulting from the diffusion of gold during the growth. Based on these observations, the tapering of the nanowire is found to be related to two contributions: the reduction in the catalyst particle size during the growth and lateral overgrowth from the direct incorporation of Si species onto the nanowire sidewalls. Because the rearrangement of atoms at surfaces and interfaces might affect the growth kinetics, the trigonal symmetry as well as the higher lateral growth rate on the widest sidewalls are explained from the existence of an interfacial atomic structure with two inequivalent parts in the unit cell. Finally, spectroscopic measurements were performed on the major facets and revealed a metallic behavior at 77 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 42
DOI: 10.1103/PhysRevB.81.115403
|
“Highly disordered crystal structure and thermoelectric properties of Sn3P4”. Zaikina JV, Kovnir KA, Sobolev AN, Presniakov IA, Kytin VG, Kulbachinskii VA, Olenev AV, Lebedev OI, Van Tendeloo G, Dikarev EV, Shevelkov AV, Chemistry of materials 20, 2476 (2008). http://doi.org/10.1021/cm702655g
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 33
DOI: 10.1021/cm702655g
|
“Sn20.5-3.5As22I8: a largely disordered cationic clathrate with a new type of superstructure and abnormally low thermal conductivity”. Zaikina JV, Kovnir KA, Sobolev AV, Presniakov IA, Prots Y, Baitinger M, Schnelle W, Olenev AV, Lebedev OI, Van Tendeloo G, Grin Y, Shevelkov AV, Chemistry: a European journal 13, 5090 (2007). http://doi.org/10.1002/chem.200601772
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 44
DOI: 10.1002/chem.200601772
|
“Catalytic characterization of pure SnO2 and GeO2 in methanol steam reforming”. Zhao Q, Lorenz H, Turner S, Lebedev OI, Van Tendeloo G, Rameshan C, Klötzer B, Konzett J, Penner S, Applied catalysis : A : general 375, 188 (2010). http://doi.org/10.1016/j.apcata.2009.12.027
Abstract: Structural changes of a variety of different SnO, SnO2 and GeO2 catalysts upon reduction in hydrogen were correlated with associated catalytic changes in methanol steam reforming. Studied systems include SnO, SnO2 and GeO2 thin film model catalysts prepared by vapour phase deposition and growth on polycrystalline NaCl surfaces and, for comparison, the corresponding pure oxide powder catalysts. Reduction of both the SnO2 thin film and powder at around 673 K in 1 bar hydrogen leads to a substantial reduction of the bulk structure and yields a mixture of SnO2 and metallic β-Sn. On the powder catalyst this transformation is fully reversible upon oxidation in 1 bar O2 at 673 K. Strongly reduced thin films, however, can only be re-transformed to SnO2 if the reduction temperature did not exceed 573 K. For GeO2, the situation is more complex due to its polymorphism. Whereas the tetragonal phase is structurally stable during reduction, oxidation or catalytic reaction, a small part of the hexagonal phase is always transformed into the tetragonal at 673 K independent of the gas phase used. SnO2 is highly active and CO2 selective in methanol steam reforming, but the initial high activity drops considerably upon reduction between 373 and 573 K and almost complete catalyst deactivation is observed after reduction at 673 K, which is associated with the parallel formation of β-Sn. In close correlation to the structural results, the catalytic activity and selectivity can be restored upon an oxidative catalyst regeneration at 673 K. Tetragonal GeO2 exhibits only a small activity and no pronounced selectivity to either CO or CO2, at least after reduction. In its fully oxidized state release of surface/lattice oxygen results in a non-catalytic formation of CO2 by oxidation of CO originating from catalytic dehydrogenation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 20
DOI: 10.1016/j.apcata.2009.12.027
|
“Crystallization of PZT in porous alumina membrane channels”. Zhigalina OM, Mishina ED, Sherstyuk NE, Vorotilov KA, Vasiljev VA, Sigov AS, Lebedev OI, Grigoriev YV, de Santo MP, Barberi R, Rasing T, Ferroelectrics 336, 247 (2006). http://doi.org/10.1080/00150190600697756
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.551
Times cited: 10
DOI: 10.1080/00150190600697756
|