“The superstructure and superconductivity of Ru1222 based RuSr2Gd2-x-yYyCexCu2O10-\delta compounds”. Tan H, Lebedev OI, McLaughlin AC, Van Tendeloo G, Superconductor science and technology 23, 115013 (2010). http://doi.org/10.1088/0953-2048/23/11/115013
Abstract: For the first time, the local structure and physical properties of Ru1222 based compounds (RuSr(2)Gd(1.4)Ce(0.6)Cu(2)O(10-delta) and RuSr(2)Gd(1.8-x)Y(0.2)CexCu(2)O(10) (x = 0.90-0.55)) have been investigated and analyzed together on the very same compounds. The Ru1222 superstructure was confirmed by TEM at a local scale and was suggested to have an orthorhombic symmetry with space group Aba2 and lattice parameters a(s) similar or equal to root 2a, b(s) similar or equal to root 2a and c(s) = c. This new Ru1222 superstructure distortion from tetragonal symmetry is proposed to have a positive correlation with the superconductivity variation of these compounds. The more the distortion towards orthorhombic symmetry, the higher the critical superconducting temperature these compounds can achieve. The T(c)(0) of RuSr(2)Gd(1.8-x)Y(0.2)Ce(x)Cu(2)O(10-delta) (x = 0.85-0.55) increases monotonically from 4 to 16 K when x decreases from 0.85 to 0.70, then RuSr(2)Gd(2)Cu(2)O(8) defects emerge and the T(c) decreases with decreasing x. Ru1212 defects are observed to intergrow epitaxially with the Ru1222 structure as lamellas along the c-axis in RuSr(2)Gd(1.4)Ce(0.6)Cu(2)O(10-delta). Although Ru1212 is a superconductor, the intergrowth severely restrains its superconductivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 1
DOI: 10.1088/0953-2048/23/11/115013
|
“Anion ordering and defect structure in Ruddlesden-Popper strontium niobium oxynitrides”. Tobías G, Beltrán-Porter D, Lebedev OI, Van Tendeloo G, Rodríguez-Carvajal J, Fuertes A, Inorganic chemistry 43, 8010 (2004). http://doi.org/10.1021/ic049236k
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 31
DOI: 10.1021/ic049236k
|
“The determination of the interface structure between ionocovalent compounds: the general case study of the Al2O3/ZrO2 large mis-fit system”. Trolliard G, Benmechta R, Mercurio D, Lebedev OI, Journal of materials chemistry 16, 3640 (2006). http://doi.org/10.1039/b604232e
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 6
DOI: 10.1039/b604232e
|
“Direct imaging of loaded metal-organic framework materials (metal@MOF-5)”. Turner S, Lebedev OI, Schroeder F, Fischer RA, Van Tendeloo G, Chemistry of materials 20, 5622 (2008). http://doi.org/10.1021/cm801165s
Abstract: We illustrate the potential of advanced transmission electron microscopy for the characterization of a new class of soft porous materials: metal@Zn4O(bdc)3 (metal@MOF-5; bdc = 1,4-benzenedicarboxylate). By combining several electron microscopy techniques (transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), electron diffraction (ED), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), and electron tomography) and by carefully reducing the electron dose to avoid beam damage, it is possible to simultaneously characterize the MOF-5 framework material and the loaded metal nanoparticles. We also demonstrate that electron tomography can be used to accurately determine the position and distribution of the particles within the MOF-5 framework. To demonstrate the implementation of these microscopy techniques and what kind of results can be expected, measurements on gas-phase-loaded metal−organic framework materials Ru@MOF-5 and Pd@MOF-5 are presented.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 112
DOI: 10.1021/cm801165s
|
“Determination of size, morphology, and nitrogen impurity location in treated detonation nanodiamond by transmission electron microscopy”. Turner S, Lebedev OI, Shenderova O, Vlasov II, Verbeeck J, Van Tendeloo G, Advanced functional materials 19, 2116 (2009). http://doi.org/10.1002/adfm.200801872
Abstract: Size, morphology, and nitrogen impurity location, all of which are all thought to be related to the luminescent properties of detonation nanodiamonds, are determined in several detonation nanodiamond samples using a combination of transmission electron microscopy techniques. Results obtained from annealed and cleaned detonation nanodiamond samples are compared to results from conventionally purified detonation nanodiamond. Detailed electron energy loss spectroscopy combined with model-based quantification provides direct evidence for the sp3 like embedding of nitrogen impurities into the diamond cores of all the studied nanodiamond samples. Simultaneously, the structure and morphology of the cleaned detonation nanodiamond particles are studied using high resolution transmission electron microscopy. The results show that the size and morphology of detonation nanodiamonds can be modified by temperature treatment and that by applying a special cleaning procedure after temperature treatment, nanodiamond particles with clean facets almost free from sp2 carbon can be prepared. These clean facets are clear evidence that nanodiamond cores are not necessarily in coexistence with a graphitic shell of non-diamond carbon.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 100
DOI: 10.1002/adfm.200801872
|
“Structural phase transition and spontaneous interface reconstruction in La2/3Ca1/3MnO3/BaTiO3 superlattices”. Turner S, Lebedev OI, Verbeeck J, Gehrke K, Moshnyaga V, Van Tendeloo G, Physical review : B : condensed matter and materials physics 87, 035418 (2013). http://doi.org/10.1103/PhysRevB.87.035418
Abstract: (La2/3Ca1/3MnO3)n/(BaTiO3)m (LCMOn/BTOm) superlattices on MgO and SrTiO3 substrates with different layer thicknesses (n = 10, 38, 40 and m = 5, 18, 20) have been grown by metal organic aerosol deposition (MAD) and have been fully characterized down to the atomic scale to study the interface characteristics. Scanning transmission electron microscopy combined with spatially resolved electron energy-loss spectroscopy provides clear evidence for the existence of atomically sharp interfaces in MAD grown films, which exhibit epitaxial growth conditions, a uniform normal strain, and a fully oxidized state. Below a critical layer thickness the LCMO structure is found to change from the bulk Pnma symmetry to a pseudocubic R3̅ c symmetry. An atomically flat interface reconstruction consisting of a single Ca-rich atomic layer is observed on the compressively strained BTO on LCMO interface, which is thought to partially neutralize the total charge from the alternating polar atomic layers in LCMO as well as relieving strain at the interface. No interface reconstruction is observed at the tensile strained LCMO on BTO interface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 12
DOI: 10.1103/PhysRevB.87.035418
|
“Formation of a combined micro- and mesoporous material using zeolite Beta nanoparticles”. van Oers CJ, Stevens WJJ, Bruijn E, Mertens M, Lebedev OI, Van Tendeloo G, Meynen V, Cool P, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 120, 29 (2009). http://doi.org/10.1016/j.micromeso.2008.08.056
Abstract: Composite micro- and mesoporous materials are synthesized using zeolite Beta nanoparticles without the need for a structure directing agent to form the mesopores. This leads to important ecological and economical advantages. The influence of the way of cooling the aged nanoparticles solution on the formation of the composite materials has been studied. The materials have been characterized towards porosity by N2-sorption, towards zeolitic properties by TGA, DRIFT, XRD and TEM, towards aluminium content by EPMA. All prepared structures possess zeolitic properties. However, the method of cooling down of the aged seeds leads to differences in the porosity and intensity of the zeolitic characteristics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 42
DOI: 10.1016/j.micromeso.2008.08.056
|
“Atomic and microstructure of CMR materials”. Van Tendeloo G, Lebedev OI, Amelinckx S, Journal of magnetism and magnetic materials 211, 73 (2000). http://doi.org/10.1016/S0304-8853(99)00716-7
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.63
Times cited: 48
DOI: 10.1016/S0304-8853(99)00716-7
|
“Structure of nanoscale mesoporous silica spheres?”.Van Tendeloo G, Lebedev OI, Collart O, Cool P, Vansant EF, Journal of physics : condensed matter 15, S3037 (2003)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.649
|
“Structure and microstructure of colossal magnetoresistant materials”. Van Tendeloo G, Lebedev OI, Hervieu M, Raveau B, Reports on progress in physics 67, 1315 (2004). http://doi.org/10.1088/0034-4885/67/8/R01
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 14.311
Times cited: 79
DOI: 10.1088/0034-4885/67/8/R01
|
“Structure determination of YBCO fluorinated phases by HREM”. Van Tendeloo G, Lebedev OI, Shpanchenko RV, Antipov EV, Journal of electron microscopy 1, 23 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.9
|
“The local structure of YBCO based materials by TEM”. Van Tendeloo G, Lebedev OI, Verbist K, Abakumov AM, Shpanchenko RV, Antipov EV, Blank DHA Kluwer Academic, Dordrecht, page 11 (1999).
Keywords: H1 Book chapter; Electron microscopy for materials research (EMAT)
|
“Fe and Co nanowires and nanotubes synthesized by template electrodeposition: a HRTEM and EELS study”. Verbeeck J, Lebedev OI, Van Tendeloo G, Cagnon L, Bougerol C, Tourillon T, Journal of the electrochemical society 150, E468 (2003). http://doi.org/10.1149/1.1601230
Abstract: Co and Fe nanowires and/or nanotubes are electrochemically synthesized through nanoporous membranes. By combining high-resolution transmission electron microscopy (HRTEM), electron energy loss spectroscopy (EELS), and energy filtered TEM techniques, their structural and crystallographic characteristics are precisely determined. The synthesis was shown to produce cigar-shaped single monocrystalline Co and Fe nanowires with a diameter of about 60 nm. All wires were surrounded by an epitaxial oxide layer (Co3O4 or Fe3O4) of roughly 10 nm. The Fe nanotubes were built up of Fe3O4 nanocrystals. Electron diffraction showed that all nanocrystals had a common crystallographic axis, creating a pseudomonocrystalline wall in the nanotubes. (C) 2003 The Electrochemical Society.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.259
Times cited: 41
DOI: 10.1149/1.1601230
|
“SrTiO3(100)/(LaMnO3)m(SrMnO3)n layered heterostructures: a combined EELS and TEM study”. Verbeeck J, Lebedev OI, Van Tendeloo G, Mercey B, Physical review : B : condensed matter and materials physics 66, 184426 (2002). http://doi.org/10.1103/PhysRevB.66.184426
Abstract: Epitaxially grown heterostructures consisting of alternating layers of LaMnO(3) (LMO, 9 or 15 unit cells) and SrMnO(3) (SMO, 4 or 6 unit cells) on a SrTiO(3)(100) (STO(100)) substrate have been studied by a combination of high resolution transmission electron microscopy (HRTEM), electron diffraction, quantitative electron energy loss spectroscopy (EELS) with model fitting, energy filtered TEM (EFTEM) and imaging spectroscopy on an atomic scale. The combination of these techniques is necessary for the structural, chemical, and electronic characterization of these heterostructures. A model is proposed containing chemically and structurally sharp interfaces. The SrMnO(3) layers are stabilized in a Pm3m structure between two LMO layers. Tensile stress causes oxygen deficiency in the SMO layers increasing the number of 3d electrons on the Mn sites to resemble the Mn(3+) sites in LMO. The energy loss near edge structure (ELNES) of O and Mn is compared for both LMO and SMO layers and shows that the Mn-O bonds have a partially covalent character. The absence of a strong valency effect in the Mn ELNES is due to the oxygen vacancies in SMO.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 32
DOI: 10.1103/PhysRevB.66.184426
|
“Electron energy-loss spectroscopy study of a (LaMnO3)8(SrMnO3)4 heterostructure”. Verbeeck J, Lebedev OI, Van Tendeloo G, Silcox J, Mercey B, Hervieu M, Haghiri-Gosnet AM, Applied physics letters 79, 2037 (2001). http://doi.org/10.1063/1.1403316
Abstract: An epitaxially grown heterostructure consisting of alternating layers of LaMnO3 (8 unit cells) and SrMnO3 (4 unit cells) on a SrTiO3 substrate has been studied by a combination of electron energy-loss spectroscopy (EELS) and high-resolution transmission electron microscopy (HRTEM) on an atomic scale. Excitation edges of all elements are captured with subnanometer spatial accuracy, and parametrized to obtain chemical profiles. The fine-edge structure of O K and Mn L-2,L-3 edges are interpreted as signatures of the local electronic structure and show a spatial modulation of the concentration of holes with O 2p character. The chemical concentration is found to be different for the bottom and top interface of a SrMnO3 layer. HRTEM complements the EELS results and confirms the asymmetry of the interfaces. (C) 2001 American Institute of Physics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 19
DOI: 10.1063/1.1403316
|
“A potential method to correlate electrical properties and microstructure of a unique high-Tc superconducting Josephson junction”. Verbist K, Lebedev OI, Van Tendeloo G, Tafuri F, Granozio FM, Di Chiara A, Bender H, Applied physics letters 74, 1024 (1999). http://doi.org/10.1063/1.123443
Abstract: A method to correlate microstructure from cross-section transmission electron microscopy (TEM) investigations and transport properties of a single well characterized high-T-c artificial grain boundary junction is reported. A YBa2Cu3O7-delta 45 degrees twist junction exhibiting the typical phenomenology of high T-c Josephson weak links was employed. The TEM sample preparation is based on focused ion beam etching and allows to easily localize the electron transparent area on a microbridge. The reported technique opens clear perspectives in the determination of the microstructural origin of variations in Josephson junction properties, such as the spread in I-c and IcRN values and the presence of different transport regimes in nominally identical junctions. (C) 1999 American Institute of Physics. [S0003-6951(99)03404-X].
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 5
DOI: 10.1063/1.123443
|
“Low- or high-angle Ar ion-beam etching to create ramp-type Josephson junctions”. Verbist K, Lebedev OI, Van Tendeloo G, Verhoeven MAJ, Rijnders AJHM, Blank DHA, Superconductor science and technology 9, 978 (1996). http://doi.org/10.1088/0953-2048/9/11/009
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.325
Times cited: 10
DOI: 10.1088/0953-2048/9/11/009
|
“Study of ramp-type Josephson junctions by HREM”. Verbist K, Lebedev OI, Van Tendeloo G, Verhoeven MAJ, Rijnders AJHM, Blank DHA, Electronic Applications, Vol 2: Large Scale And Power Applications , 49 (1997)
Abstract: Structural aspects of ramp-type Josephson junctions based on REBa2Cu3O7-delta high-T-c superconductors, are investigated by cross-section transmission electron microscopy and results related to fabrication process or physical properties. The barrier layer material is PrBa2Cu3-xGaxO7-delta. The ramp-geometry depends on the etching conditions. High levels of Ga doping (x>0.7) influence the microstructure of the barrier layer thereby changing the junctions properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
“Ga segregation in DyBa2Cu3O7-\delta/PrBa2Cu3-xGaxO7-\delta/DyBa2Cu3O7-\delta ramp-type Josephson junctions”. Verbist K, Lebedev OI, Van Tendeloo G, Verhoeven MAJ, Rijnders AJHM, Blank DHA, Rogalia H, Applied physics letters 70, 1167 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 8
|
“Microstructure of YBa2Cu3O7-\delta Josephson junctions in relation to their properties”. Verbist K, Lebedev OI, Verhoeven MAJ, Winchern R, Rijnders AJHM, Blank DHA, Tafuri F, Bender H, Van Tendeloo G, Superconductor science and technology 11, 13 (1998). http://doi.org/10.1088/0953-2048/11/1/004
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
DOI: 10.1088/0953-2048/11/1/004
|
“Synthesis of highly stable pure-silica thin-walled hexagonally ordered mesoporous material”. Verlooy P, Aerts A, Lebedev OI, Van Tendeloo G, Kirschhock C, Martens JA, Chemical communications , 4287 (2009). http://doi.org/10.1039/b901796h
Abstract: Hexagonally ordered mesoporous silica with a very narrow mesopore size distribution and exceptionally high stability paired with unusually thin pore walls was prepared using piperidine and cetyltrimethylammonium bromide.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 17
DOI: 10.1039/b901796h
|
“Synthesis and characterization of the new cyclosilicate hydrate (hexamethyleneimine)4.[Si8O16(OH)4].12H2O”. Verlooy PLH, Robeyns K, van Meervelt L, Lebedev OI, Van Tendeloo G, Martens JA, Kirschhock CEA, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 130, 14 (2010). http://doi.org/10.1016/j.micromeso.2009.10.006
Abstract: A new cyclosilicate hydrate with composition (C6H14N)4·[Si8O16(OH)4]·12H2O was crystallized and the structure determined by single-crystal X-ray diffraction. The structure, described by the tetragonal space group I41/a, with unit cell dimensions of a = 39.2150(2) Å and c = 14.1553(2) Å, contains columns of hydrogen-bonded cubic octamer silicate anions. The space between silicate columns holds hydrogen-bonded water and protonated hexamethyleneimine molecules compensating the negative charge of the silicate. The crystal water can be removed resulting in a rearrangement of the columns into orthorhombic symmetry. Removal of the organic moiety causes amorphisation. Flash evacuation results in a new microporous material with pore volumes typical of a zeolite.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 5
DOI: 10.1016/j.micromeso.2009.10.006
|
“Immersion calorimetry as a tool to evaluate the catalytic performance of titanosilicate materials in the epoxidation of cyclohexene”. Vernimmen J, Guidotti M, Silvestre-Albero J, Jardim EO, Mertens M, Lebedev OI, Van Tendeloo G, Psaro R, Rodríguez-Reinoso F, Meynen V, Cool P, Langmuir: the ACS journal of surfaces and colloids 27, 3618 (2011). http://doi.org/10.1021/la104808v
Abstract: Different types of titanosilicates are synthesized, structurally characterized, and subsequently catalytically tested in the liquid-phase epoxidation of cyclohexene. The performance of three types of combined zeolitic/mesoporous materials is compared with that of widely studied Ti-grafted-MCM-41 molecular sieve and the TS-1 microporous titanosilicate. The catalytic test results are correlated with the structural characteristics of the different catalysts. Moreover, for the first time, immersion calorimetry with the same substrate molecule as in the catalytic test reaction is applied as an extra means to interpret the catalytic results. A good correlation between catalytic performance and immersion calorimetry results is found. This work points out that the combination of catalytic testing and immersion calorimetry can lead to important insights into the influence of the materials structural characteristics on catalysis. Moreover, the potential of using immersion calorimetry as a screening tool for catalysts in epoxidation reactions is shown.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.833
Times cited: 19
DOI: 10.1021/la104808v
|
“New insights in the formation of combined zeolitic/mesoporous materials by using a one-pot templating synthesis”. Vernimmen J, Meynen V, Herregods SJF, Mertens M, Lebedev OI, Van Tendeloo G, Cool P, European journal of inorganic chemistry , 4234 (2011). http://doi.org/10.1002/ejic.201100268
Abstract: Zeolitic growth is often absent or occurs in separate phases when synthetic strategies based on the combination of zeolite templates and mesopore templating agents are applied. In this work, zeolitic growth and mesopore formation have been investigated at different temperatures by applying a one-pot templating approach, based on a TS-1 zeolite synthesis whereby part of the microtemplate (tetrapropylammonium hydroxide, TPAOH) is replaced by a mesotemplate (hexadecyltrimethylammonium bromide, CTMABr). Moreover, the synthesis duration and the molar ratio of the microtemplate/mesotemplate have also been studied. The different syntheses clearly show the inherent competitive mechanism between zeolitic growth and mesopore formation. These insights have led to the conclusion that by following a one-pot templating strategy with standard, nonexotic commercial templates, i.e. CTMABr and TPAOH, it is not possible to develop a true hierarchical mesoporous zeolite, meaning a mesoporous siliceous material with highly crystalline zeolitic walls. The resultant materials are instead combined zeolitic/mesoporous composite structures with, however, highly tuneable and controllable porosity characteristics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.444
Times cited: 7
DOI: 10.1002/ejic.201100268
|
“Formation of a Ti-siliceous trimodal material with macroholes, mesopores and zeolitic features via a one-pot templating synthesis”. Vernimmen J, Meynen V, Mertens M, Lebedev OI, Van Tendeloo G, Cool P, Journal of porous materials 19, 153 (2012). http://doi.org/10.1007/s10934-011-9470-0
Abstract: Based on a facile one-pot templating synthesis, using a TS-1 zeolite recipe whereby part of the zeolite structure directing agent is replaced by a mesopore templating agent, a trimodal material is formed. The resulting meso-TSM material combines mesoporosity (Ti-MCM-41) with zeolitic features (TS-1) and a unique sheet-like morphology with uniform macroporous voids (macroholes). Moreover, the macrohole formation, mesoporosity and zeolitic properties of the meso-TSM material can be controlled in a straightforward way by adjusting the length of the hydrothermal treatment. This newly developed material may imply great potential for catalytic redox applications and diffusion limitated processes because of its highly tunable character in all three dimensions (micro-, meso- and macroporous scale).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 1.624
Times cited: 2
DOI: 10.1007/s10934-011-9470-0
|
“Nanodiamond photoemitters based on strong narrow-band luminescence from silicon-vacancy defects”. Vlasov II, Barnard AS, Ralchenko VG, Lebedev OI, Kanzyuba MV, Saveliev AV, Konov VI, Goovaerts E, Advanced materials 21, 808 (2009). http://doi.org/10.1002/adma.200802160
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Nanostructured and organic optical and electronic materials (NANOrOPT)
Impact Factor: 19.791
Times cited: 98
DOI: 10.1002/adma.200802160
|
“Nitrogen and luminescent nitrogen-vacancy defects in detonation nanodiamond”. Vlasov II, Shenderova O, Turner S, Lebedev OI, Basov AA, Sildos I, Rähn M, Shiryaev AA, Van Tendeloo G, Small 6, 687 (2010). http://doi.org/10.1002/smll.200901587
Abstract: An efficient method to investigate the microstructure and spatial distribution of nitrogen and nitrogen-vacancy (N-V) defects in detonation nanodiamond (DND) with primary particle sizes ranging from approximately 3 to 50 nm is presented. Detailed analysis reveals atomic nitrogen concentrations as high as 3 at% in 50% of diamond primary particles with sizes smaller than 6 nm. A non-uniform distribution of nitrogen within larger primary DND particles is also presented, indicating a preference for location within the defective central part or at twin boundaries. A photoluminescence (PL) spectrum with well-pronounced zero-phonon lines related to the N-V centers is demonstrated for the first time for electron-irradiated and annealed DND particles at continuous laser excitation. Combined Raman and PL analysis of DND crystallites dispersed on a Si substrate leads to the conclusion that the observed N-V luminescence originates from primary particles with sizes exceeding 30 nm. These findings demonstrate that by manipulation of the size/nitrogen content in DND there are prospects for mass production of nanodiamond photoemitters based on bright and stable luminescence from nitrogen-related defects.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 84
DOI: 10.1002/smll.200901587
|
“Hybrid diamond-graphite nanowires produced by microwave plasma chemical vapor deposition”. Vlasov IL, Lebedev OI, Ralchenko VG, Goovaerts E, Bertoni G, Van Tendeloo G, Konov VI, Advanced materials 19, 4058 (2007). http://doi.org/10.1002/adma.200700442
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Nanostructured and organic optical and electronic materials (NANOrOPT)
Impact Factor: 19.791
Times cited: 75
DOI: 10.1002/adma.200700442
|
“Nanoscale ordering in oxygen deficient quintuple perovskite Sm2-\epsilonBa3+\epsilonFe5O15-\delta : implication for magnetism and oxygen stoichiometry”. Volkova NE, Lebedev OI, Gavrilova LY, Turner S, Gauquelin N, Seikh MM, Caignaert V, Cherepanov VA, Raveau B, Van Tendeloo G, Chemistry of materials 26, 6303 (2014). http://doi.org/10.1021/cm503276p
Abstract: The investigation of the system SmBaFe-O in air has allowed an oxygen deficient perovskite Sm2-epsilon Ba3+epsilon Fe5O15-delta (delta = 0.75, epsilon = 0.125) to be synthesized. In contrast to the XRPD pattern which gives a cubic symmetry (a(p) = 3.934 angstrom), the combined HREM/EELS study shows that this phase is nanoscale ordered with a quintuple tetragonal cell, a(p) X a(p) X 5(ap). The nanodomains exhibit a unique stacking sequence of the A-site cationic layers along the crystallographic c-axis, namely SmBaBa/SmBa/SmBaSm, and are chemically twinned in the three crystallographic directions. The nanoscale ordering of this perovskite explains its peculiar magnetic properties on the basis of antiferromagnetic interactions with spin blockade at the boundary between the nanodomains. The variation of electrical conductivity and oxygen content of this oxide versus temperature suggest potential SOFC applications. They may be related to the particular distribution of oxygen vacancies in the lattice and to the 3d(5)(L) under bar configuration of iron.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 16
DOI: 10.1021/cm503276p
|
“Phase transition and magnetic anisotropy of (La,Sr)MnO3 thin films”. Wang Z-H, Kronmüller H, Lebedev OI, Gross GM, Razavi FS, Habermeier HU, Shen BG, Physical review : B : condensed matter and materials physics 65, 054411 (2002). http://doi.org/10.1103/PhysRevB.65.054411
Abstract: The magnetic proper-ties and their correlation with the microstructure and electrical transport are investigated in La0.88Sr0.1MnO3 films grown on (100)SrTiO3 Single crystal substrates with thickness ranging from 100 to 2500 Angstrom. The ultrathin film (t = 100 Angstrom) has a single ferromagnetic transition (FMT) at T-c of 250 K, whereas the thicker films exhibit two FMTs, with the main one at a lowered T-c of 200 K while the minor one around 300 K. Furthermore, a thickness dependent magnetic anisotropy has been found, strongly indicating the existence of strain effect, which is also revealed by the transmission electron microscopy study. The suppressed Jahn-Teller distortion (JTD) by the epitaxial strain, and the recovered JTD due to the strain relexation are suggested to explain the metallic behavior in thin films and the insulating behavior in the thick film (t = 2500 Angstrom), repectively.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 23
DOI: 10.1103/PhysRevB.65.054411
|