“Structural aspects of Bi2-xPbxSr3.5Cu2(CO3)O8-\delta for 0\leq x\leq0.75 : an electron-microscopy study”. Zhang XF, Van Tendeloo G, Amelinckx S, Pelloquin D, Michel C, Hervieu M, Raveau B, Journal of solid state chemistry 113, 327 (1994). http://doi.org/10.1006/jssc.1994.1378
Abstract: The structure and defect structure of Bi2-xPbxSr3.5Cu2 (CO3)O8-delta compounds with 0 less-than-or-equal-to x less-than-or-equal-to 0.75 are carefully investigated by electron diffraction and high-resolution electron microscopy. All compounds have an orthorhombic structure with a almost-equal-to b almost-equal-to 5.4 angstrom and c almost-equal-to 39.5 angstrom. The length of the b-axis decreases monotonically with increasing x. The space group for the basic structure is Abm2. The structure can be considered as an intergrowth of Bi2Sr2CuO6 lamellae with Sr2CuO2 (CO3) lamellae along the c-axis. CO3 groups behave as bridges connecting the CuO6 octahedra. In the x = 0 compound the carbon atoms are shifted away from their symmetry positions; the orientational ordering of the CO3 groups (or the carbon shift) in successive CO planes alternates along +b and -b. Typical Bi-type and Pb-type modulations are found along the b-axis up to a Pb content x = 0.5. Electron beam irradiation destroys the ordering of the CO3 groups and alters the modulated structure. (C) 1994 Academic press, inc.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 8
DOI: 10.1006/jssc.1994.1378
|
“B-site ordered perovskite LaSrMnNbO6 : synthesis, structure and antiferromagnetism”. Yang T, Perkisas T, Hadermann J, Croft M, Ignatov A, Greenblatt M, Journal of solid state chemistry 183, 2689 (2010). http://doi.org/10.1016/j.jssc.2010.08.041
Abstract: LaSrMnNbO6 has been synthesized by high temperature solid state reaction under 1% H2/Ar dynamic flow. The structure is determined by Rietveld refinement of the powder X-ray diffraction data. It crystallizes in the monoclinic space group P21/n with the unit cell parameters: a=5.69187(12), b=5.74732(10), c=8.07018(15) Å and β=90.0504(29)°, which were also confirmed by electron diffraction. The Mn2+ and Nb5+ ions, whose valence states are confirmed by X-ray absorption near-edge spectroscopy, are almost completely ordered over the B-site (<1% inversion) of the perovskite structure due to the large differences of both cationic size (0.19 Å) and charge. The octahedral framework displays significant tilting distortion according to Glazers tilt system a−b−c+. Upon heating, LaSrMnNbO6 decomposes at 690 °C under O2 flow or at 775 °C in air. The magnetic susceptibility data indicate the presence of long-range antiferromagnetic ordering at TN=8 K; the experimentally observed effective paramagnetic moment, μeff=5.76 μB for high spin Mn2+ (3d5, S=5/2) is in good agreement with the calculated value (μcalcd=5.92 μB).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 13
DOI: 10.1016/j.jssc.2010.08.041
|
“HREM image analysis up to structure determination of SbCrSe3: a new 1D ferromagnet”. Volkov VV, Van Tendeloo G, van Landuyt J, Amelinckx S, Busheva EE, Shabunina GG, Aminov TG, Novotortsev VM, Journal of solid state chemistry 132, 257 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 1
|
“Electron microscopic and X-ray structural analysis of the layered crystals TaReSe4: structure, defect structure, and microstructure, including rotation twins”. Volkov VV, van Landuyt J, Amelinckx S, Pervov VS, Makhonina EV, Journal of solid state chemistry 135, 235 (1998). http://doi.org/10.1006/jssc.1997.7621
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 3
DOI: 10.1006/jssc.1997.7621
|
“Ordering principles and defect structure of “1201”, “1212”, and “1222&rdquo, type (Hg,Pr)-Sr-(Sr,Ca,Pr)-Cu-O superconductors”. Van Tendeloo G, Hervieu M, Zhang XF, Raveau B, Journal of solid state chemistry 114, 369 (1995). http://doi.org/10.1006/jssc.1995.1057
Abstract: The new families of superconducting compounds ''1201'' (Hg0.4Pr0.6Sr2CuO4+delta), ''1212'' (Hg0.4Pr0.6Sr2(Ca1-x-ySrxPry) Cu2O6+delta), and ''1222'' (Hg0.4Pr0.6Sr2(Pr1.7Sr0.3)(2)Cu2O8+delta) all show ordering between praseodymium and mercury in the (Hg,Pr)O-delta plane, reducing the symmetry from tetragonal to orthorhombic or even to monoclinic. In the 1201 compound the ordered superstructure can be described as O-I (a(I) approximate to 2a(p), b(I), approximate to a(p), c(I) approximate to c(1201)). In the 1212 compound two distinct superstructures are identified, O-I (a(I) approximate to 2a(p), b(II) approximate to a(p), c(I) approximate to c(1212)) and O-II (a(II) approximate to 2a(p), b(II) approximate to a(p), c(II) approximate to 2c(1212)). In some compounds, such as Hg0.4Pr0.6Sr2(Ca0.4Sr0.4Pr0.2) Cu2O6+delta, the Hg-Pr ordering is only present in microdomains, but due to an ordering between Sr layers and Ca layers, the c-axis doubles and one obtains a tetragonal superstructure T-III (a(III) approximate to a(p), c(III) approximate to 2c(1212)). In the 1222 compound, ordering in the (Pr,Hg)O-delta plane is very defective; a large number of translation defects actually reduce the symmetry to triclinic. (C) 1995 Academic Press, Inc.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 11
DOI: 10.1006/jssc.1995.1057
|
“The fine structure of YCuO2+x delafossite determined by synchrotron powder diffraction and electron microscopy”. Van Tendeloo G, Garlea O, Darie C, Bougerol-Chaillout C, Bordet P, Journal of solid state chemistry 156, 428 (2001). http://doi.org/10.1006/jssc.2000.9018
Abstract: YCuO2 delafossite crystallizes into two stacking variants; hexagonal 2H or rhombohedral 3R, depending on the preparation conditions. The structure of the fully oxygenated material YCuO2.50 has been determined as orthorhombic (a(O) = 6.1961 Angstrom; b(O) = 11.2158 Angstrom; c(O) = 7.1505 Angstrom; space group Pnma). The structure is based on the hexagonal 2H structure (a(O) = a(H)root3; b(O) = c(H); c(O) = 2a(H)). Upon incomplete oxidation, a different YCuOZ phase with ideal composition YCuO2.33 and lattice parameters a(H root)3, a(H)root3, c(H) is also formed. Diffraction patterns are often very complex because of the presence of planar defects and intergrowth of both phases. Under electron beam irradiation, oxygen is released from the structure and one phase gradually transforms into the other. (C) 2001 Academic Press.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 33
DOI: 10.1006/jssc.2000.9018
|
“Structural aspects of Li-doped tubular bismuth cuprates (Bi2Sr3Cu2-xLixOy): an electron microscopy study”. Van Tendeloo G, Domengès B, Caldes MT, Hervieu M, Raveau B, Journal of solid state chemistry 112, 161 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
|
“Cation ordering in [(Tl, M)O] layers of “1202”-based cuprates : similarity to ordering in fcc-based alloys”. Van Tendeloo G, De Meulenaere P, Letouzé, F, Martin C, Hervieu M, Raveau B, Journal of solid state chemistry 132, 113 (1997). http://doi.org/10.1006/jssc.1997.7418
Abstract: ''1201'' Tl-based substituted cuprates of the type (Tl1-xMx) Sr2CuO5 have been synthesized for M = Nb, Ta, or W. These materials do not superconduct due to a statistical distribution of some of the M for Cu. The remarkable feature of these materials is the ordering observed between Tl and M in the (Tl1-xMx-epsilon)O plane. The type of ordering depends on the composition and shows remarkable similarities with the ordering in Ni-Mo or other so-called 1 1/2 0 type fcc-based alloys or with the ordering in rocksalt oxides TiOx. The short-range order, for M = W, can be readily interpreted in terms of a mixing of nano-clusters with two different compositions. These observations of two-dimensional ordering confirm recent ideas about ordering in three-dimensional fcc-based alloys.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 2
DOI: 10.1006/jssc.1997.7418
|
“Structural considerations and high-resolution electron-microscopy observations on LanTin-\deltaO3n(n\geq4\delta)”. Van Tendeloo G, Amelinckx S, Darriet B, Bontchev R, Darriet J, Weill F, Journal of solid state chemistry 108, 314 (1994). http://doi.org/10.1006/jssc.1994.1048
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 29
DOI: 10.1006/jssc.1994.1048
|
“Structural considerations and HREM on LanTin-\deltaO3n (n≥4δ)”. Van Tendeloo G, Amelinckx S, Darriet B, Bontchev R, Darriet J, Weill F, Journal of solid state chemistry 108, 314 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 29
|
“Crystal structure and magnetic properties of complex oxides Mg4-xNixO9, 0\leq x\leq4”. Tarakina NV, Nikulina EA, Hadermann J, Kellerman DG, Tyutunnik AP, Berger IF, Zubkov VG, Van Tendeloo G, Journal of solid state chemistry 180, 3180 (2007). http://doi.org/10.1016/j.jssc.2007.09.007
Abstract: In the Mg4−xNixNb2O9 (0x4) system two ranges of solid solution have been found. One of the solid solutions has a corundum-related structure type (space group ); the second one adopts the II-Ni4Nb2O9 structure type (space group Pbcn). The unit cell constants and atomic positions have been determined and refined using neutron powder diffraction data. Electron diffraction and high-resolution transmission electron microscopy (HRTEM) from MgNi3Nb2O9 crystals identify the presence of planar defects and the intergrowth of several (structurally related) phases. The magnetic susceptibility of Mg3NiNb2O9, measured in the temperature range T=2300 K, shows no indications of magnetic ordering at low temperatures, while for MgNi3Nb2O9 there is a magnetic ordering at temperatures below 45.5 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 3
DOI: 10.1016/j.jssc.2007.09.007
|
“Magnetic properties of the 6H perovskite Ba3Fe2TeO9”. Tang Y, Sena RP, Aydeev M, Battle PD, Cadogan JM, Hadermann J, Hunter EC, Journal of solid state chemistry 253, 347 (2017). http://doi.org/10.1016/J.JSSC.2017.06.019
Abstract: A polycrystalline sample of Ba3Fe2TeO9 having the 6H perovskite structure has been prepared in a solid-state reaction and studied by a combination of electron microscopy, Mossbauer spectroscopy, magnetometry, X-ray diffraction and neutron diffraction. Partial ordering of Fe3+ and Te6+ cations occurs over the six-coordinate sites; the corner-sharing octahedra are predominantly occupied by the former and the face-sharing octahedra by a 1:1 mixture of the two. On cooling through the temperature range 18 < T/K < 295 an increasing number of spins join an antiferromagnetic backbone running through the structure while the remainder show complex relaxation effects. At 3 K an antiferromagnetic phase and a spin glass coexist.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 6
DOI: 10.1016/J.JSSC.2017.06.019
|
“Structural chemistry and magnetic properties of the perovskite Sr3Fe2TeO9”. Tang Y, Hunter EC, Battle PD, Sena RP, Hadermann J, Avdeev M, Cadogan JM, Journal of solid state chemistry 242, 86 (2016). http://doi.org/10.1016/j.jssc.2016.06.024
Abstract: A polycrystalline sample of perovskite-like Sr3Fe2TeO9 has been prepared in a solid-state reaction and studied by a combination of electron microscopy, Mossbauer spectroscopy, magnetometry, X-ray diffraction and neutron diffraction. The majority of the reaction product is shown to be a trigonal phase with a 2:1 ordered arrangement of Fe3+ and Te6+ cations. However, the sample is prone to nano twinning and tetragonal domains with a different pattern of cation ordering exist within many crystallites. Antiferromagnetic ordering exists in the trigonal phase at 300 K and Sr3Fe2TeO9 is thus the first example of a perovskite with 2:1 trigonal cation ordering to show long-range magnetic order. At 300 K the antiferromagnetic phase coexists with two paramagnetic phases which show spin -glass behaviour below similar to 80 K. (C) 2016 The Authors. Published by Elsevier Inc.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 12
DOI: 10.1016/j.jssc.2016.06.024
|
“Crystallographic and magnetic characterisation of the brownmillerite Sr2Co2O5”. Sullivan E, Hadermann J, Greaves C, Journal of solid state chemistry 184, 649 (2011). http://doi.org/10.1016/j.jssc.2011.01.026
Abstract: Sr2Co2O5 with the perovskite-related brownmillerite structure has been synthesised via quenching, with the orthorhombic unit cell parameters a=5.4639(3) Å, b=15.6486(8) Å and c=5.5667(3) Å based on refinement of neutron powder diffraction data collected at 4 K. Electron microscopy revealed LRLR-intralayer ordering of chain orientations, which require a doubling of the unit cell along the c-parameter, consistent with the assignment of the space group Pcmb. However, on the length scale pertinent to NPD, no long-range order is observed and the disordered space group Imma appears more appropriate. The magnetic structure corresponds to G-type order with a moment of 3.00(4) μB directed along [1 0 0].
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 19
DOI: 10.1016/j.jssc.2011.01.026
|
“Local structure and oxidation state of uranium in some ternary oxides: X-ray absorption analysis”. Soldatov AV, Lamoen D, Konstantinović, MJ, van den Berghe S, Scheinost AC, Verwerft M, Journal Of Solid State Chemistry 180, 54 (2007). http://doi.org/10.1016/j.jssc.2006.08.038
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 2.299
Times cited: 60
DOI: 10.1016/j.jssc.2006.08.038
|
“New germanates RCrGeO5 (R=NdEr, Y): synthesis, structure, and properties”. Shpanchenko RV, Tsirlin AA, Kondakova ES, Antipov EV, Bougerol C, Hadermann J, Van Tendeloo G, Sakurai H, Takayama-Muromachi E, Journal of solid state chemistry 181, 2433 (2008). http://doi.org/10.1016/j.jssc.2008.05.043
Abstract: The new complex germanates RCrGeO5 (R=NdEr, Y) have been synthesized and investigated by means of X-ray powder diffraction, electron microscopy, magnetic susceptibility and specific heat measurements. All the compounds are isostructural and crystallize in the orthorhombic symmetry, space group Pbam, and Z=4. The crystal structure of RCrGeO5, as refined using X-ray powder diffraction data, includes infinite chains built by edge-sharing Cr+3O6 octahedra with two alternating Cr−Cr distances. The chains are combined into a three-dimensional framework by Ge2O8 groups consisting of two edge-linked square pyramids oriented in opposite directions. The resulting framework contains pentagonal channels where rare-earth elements are located. Thus, RCrGeO5 germanates present new examples of RMn2O5-type compounds and show ordering of Cr+3 and Ge+4 cations. Electron diffraction as well as high-resolution electron microscopy confirm the structure solution. Magnetic susceptibility data for R=Nd, Sm, and Eu are qualitatively consistent with the presence of isolated 3d (antiferromagnetically coupled Cr+3 cations) and 4f (R+3) spin subsystems in the RCrGeO5 compounds. NdCrGeO5 undergoes long-range magnetic ordering at 2.6 K, while SmCrGeO5 and EuCrGeO5 do not show any phase transitions down to 2 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 6
DOI: 10.1016/j.jssc.2008.05.043
|
“Synthesis and structure investigation of the Pb3V(PO4)3 eulytite”. Shpanchenko RV, Panin RV, Hadermann J, Bougerol C, Takayama-Muromachi E, Antipov EV, Journal of solid state chemistry 178, 3715 (2005). http://doi.org/10.1016/j.jssc.2005.09.045
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 17
DOI: 10.1016/j.jssc.2005.09.045
|
“Structural studies on new ternary oxides Ba8Ta4Ti3O24 and Ba10Ta7.04Ti1.2O30”. Shpanchenko RV, Nistor L, Van Tendeloo G, van Landuyt J, Amelinckx S, Journal of solid state chemistry 114, 560 (1995). http://doi.org/10.1006/jssc.1995.1086
Abstract: The ternary oxides Ba8Ta4Ti3O24 and Ba10Ta7.04Ti1.2O30 were synthesized and their crystal structures and defects were studied by means of X-ray powder diffraction, electron diffraction, and high resolution electron microscopy. The crystal structure of Ba8Ta4Ti3O24 is based on the 8H (cchc)(2) close-packed stacking (a 10.0314 Angstrom, c = 18.869 Angstrom, SG P6(3)/mcm, Z = 3) and that of Ba10Ta7.04Ti1.2O30 and on the 10H (cchcc)(2) close-packed stacking (a = 5.7981 Angstrom, c = 23.755 Angstrom, SG P6(3)/mmc, Z = 1) of BaO3 layers. The structural refinements gave the following values for the R factors for Ba8Ta4Ti3O24 (Ba10Ta7.04Ti1.2O30) R(I) = 0.041 (0.039), R(P) = 0.108 (0.118), and R(wP) = 0.094 (0.099). The main feature of both structures is the presence of two types of face-sharing octahedra (FSO) with different occupancies by Ta atoms, Ti atoms, and vacancies, which results in the formation of a superstructure. It was shown that in the Ba8Ta4Ti3O24 structure these pairs of FSO occur in an ordered fashion and in the Ba10Ta7.04Ti1.2O30 structure in a disordered fashion. The existence of the wide range of solid solutions was shown to be also a consequence of the presence of one of the two types of face-sharing octahedra. (C) 1995 Academic Press, Inc,
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 23
DOI: 10.1006/jssc.1995.1086
|
“High resolution electron microscopic study of Ba7Sc6Al2O19 and related phases”. Shpanchenko RV, Nistor L, Van Tendeloo G, Amelinckx S, Antipov EV, Kovba LM, Journal of solid state chemistry 113, 193 (1994). http://doi.org/10.1006/jssc.1994.1359
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 3
DOI: 10.1006/jssc.1994.1359
|
“Synthesis, structure and magnetic properties of the new mixed-valence vanadate Na2SrV3O9”. Shpanchenko RV, Chernaya VV, Antipov EV, Hadermann J, Kaul EE, Geibel C, Journal of solid state chemistry 173, 244 (2003). http://doi.org/10.1016/S0022-4596(03)00039-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/S0022-4596(03)00039-2
|
“Structural study of the new complex oxides Ba5-ySryR2-xAl2Zr1+xO13+x/2 (R=Gd-Lu, Y, Sc)”. Shpanchenko RV, Abakumov AM, Antipov EV, Nistor L, Van Tendeloo G, Amelinckx S, Journal of solid state chemistry 118, 180 (1995). http://doi.org/10.1006/jssc.1995.1329
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 8
DOI: 10.1006/jssc.1995.1329
|
“Structural chemistry and magnetic properties of the perovskite SrLa2Ni2TeO9”. Sena RP, Hadermann J, Chin C-M, Hunter EC, Battle PD, Journal of solid state chemistry 243, 304 (2016). http://doi.org/10.1016/J.JSSC.2016.09.004
Abstract: A polycrystalline sample of SrLa2Ni2TeO9 has been synthesized using a standard ceramic method and characterized by neutron diffraction, magnetometry and electron microscopy. The compound adopts a monoclinic, perovskite-like structure with space group P2(1)/n in and unit cell parameters a=5.6008(1), b = 5.5872(1), c=7.9018(2) angstrom, p=90.021(6)degrees at room temperature. The two crystallographically-distinct B sites are occupied by Ni2+ and Te6+ in ratios of 83:17 and 50:50. Both ac and dc magnetometry suggest that the compound is a spin glass below 35 K but the neutron diffraction data show that some regions of the sample are antiferromagnetic. Electron microscopy revealed twinning on a nanoscale and local variations in composition. These defects are thought to be responsible for the presence of two distinct types of antiferromagnetic ordering. (C) 2016 The Authors. Published by Elsevier Inc.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 6
DOI: 10.1016/J.JSSC.2016.09.004
|
“Structural determination of the charge ordering process in Nd0.5Ca0.5Mn1-xCrxO3 manganites”. Schuddinck W, Van Tendeloo G, Barnabé, A, Hervieu M, Raveau B, Journal of solid state chemistry 148, 333 (1999). http://doi.org/10.1006/jssc.1999.8457
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 12
DOI: 10.1006/jssc.1999.8457
|
“Structural aspects and antiferromagnetic ordering in the “123&rdquo, derivative LnSr2Cu2Ga1-xFexO7-\delta (Ln = Y, Ho)”. Rykov A, Caignaert V, Van Tendeloo G, Greneche JM, Studer F, Nguyen N, Ducouret A, Bonville P, Raveau B, Journal of solid state chemistry 113, 94 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 9
|
“Evolution of crystallographic phases in (Sr1-xCax)TiO3 with composition (x)”. Ranjan R, Pandey D, Schuddinck W, Richard O, De Meulenaere P, van Landuyt J, Van Tendeloo G, Journal of solid state chemistry 162, 20 (2001). http://doi.org/10.1006/jssc.2001.9336
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 45
DOI: 10.1006/jssc.2001.9336
|
“Synthesis and characterization of new phases: Sr3.75K1.75Bi3O12 and Sr3.1Na2.9Bi3O12”. Pshirkov JS, Kazakov SM, Abakumov AM, Putilin SN, Antipov EV, Bougerol-Chaillout C, Lebedev OI, Van Tendeloo G, Journal of solid state chemistry 152, 492 (2000). http://doi.org/10.1006/jssc.2000.8718
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 2
DOI: 10.1006/jssc.2000.8718
|
“Preparation of the noncentrosymmetric ferrimagnetic phase La0.9Ba0.1Mn0.96O2.43 by topochemical reduction”. Parsons TG, Hadermann J, Halasyamani PS, Hayward MA, Journal Of Solid State Chemistry 287, 121356 (2020). http://doi.org/10.1016/J.JSSC.2020.121356
Abstract: Topochemical reduction of La0.9Ba0.1MnO3 with NaH at 225 degrees C yields the brownmillerite phase La0.9Ba0.1MnO2.5. However, reduction with CaH2 at 435 degrees C results in the formation of La0.9Ba0.1Mn0.96O2.43 via the deintercalation of both oxide anions and manganese cations from the parent perovskite phase. Electron and neutron diffraction data reveal La0.9Ba0.1Mn0.96O2.43 adopts a complex noncentrosymmetric structure, described in space group I23, confirmed by SHG measurements. Low-temperature neutron diffraction data reveal La0.9Ba0.1Mn0.96O2.43 adopts an ordered magnetic structure in which all the nearest neighbor interactions are antiferromagnetic. However, the presence of ordered manganese cation-vacancies results in a net ferrimagnetic structure with net saturated moment of 0.157(2) mu B per manganese center.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.3
DOI: 10.1016/J.JSSC.2020.121356
|
“Synthesis and crystal structure of the palladium oxides NaPd3O4, Na2PdO3 and K3Pd2O4”. Panin RV, Khasanova NR, Abakumov AM, Antipov EV, Van Tendeloo G, Schnelle W, Journal of solid state chemistry 180, 1566 (2007). http://doi.org/10.1016/j.jssc.2007.03.005
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 24
DOI: 10.1016/j.jssc.2007.03.005
|
“Synthesis, crystal structure and physico-chemical properties of the new quaternary oxide Sr5BiNi2O9.6”. Novitskaya M, Makhnach L, Ivashkevich L, Pankov V, Klein H, Regeau A, David J, Gemmi M, Hadermann J, Strobel P, Journal of solid state chemistry 184, 3262 (2011). http://doi.org/10.1016/j.jssc.2011.10.020
Abstract: A new black quaternary oxide Sr5BiNi2O9.6 was synthesized by solid state reaction at 1200 °C. Its structure was solved by electron crystallography and X-ray powder refinement, yielding a tetragonal structure with space group I4/mmm, a=5.3637 (2) Å, c=17.5541(5) Å, Z=4. The structure can be described as a stacking of (Bi,Sr)O rocksalt slabs and SrNiO3−δ perovskite slabs. The initial nickel valence is close to +3.1. Thermogravimetry and high-temperature oxygen coulometry showed that this compound has variable oxygen content as a function of temperature and oxygen pressure, and ultimately decomposes when heated in low oxygen pressure above 800 °C. It is a metallic conductor with n-type conduction. Its thermoelectric power was determined and found to be −20 and −38 μV/K at 300 and 650 °C, respectively. Magnetic measurements confirm the nickel valence close to +3 and show evidence of magnetic ordering at 20 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 4
DOI: 10.1016/j.jssc.2011.10.020
|
“The real (incommensurate interface modulated) structure of Ni6\pm xSe5”. Norén L, Van Tendeloo G, Withers RL, Journal of solid state chemistry 162, 122 (2001). http://doi.org/10.1006/jssc.2001.9365
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 4
DOI: 10.1006/jssc.2001.9365
|