“CO₂, electrochemical reduction with Zn-Al layered double hydroxide-loaded gas-diffusion electrode”. Nakazato R, Matsumoto K, Yamaguchi N, Cavallo M, Crocella V, Bonino F, Quintelier M, Hadermann J, Rosero-navarro NC, Miura A, Tadanaga K, Electrochemistry 91, 097003 (2023). http://doi.org/10.5796/ELECTROCHEMISTRY.23-00080
Abstract: Carbon dioxide electrochemical reduction (CO2ER) has attracted considerable attention as a technology to recycle CO2 into raw materials for chemicals using renewable energies. We recently found that Zn-Al layered double hydroxides (Zn-Al LDH) have the CO-forming CO2ER activity. However, the activity was only evaluated by using the liquid-phase CO2ER. In this study, Ni-Al and Ni-Fe LDHs as well as Zn-Al LDH were synthesized using a facile coprecipitation process and the gas-phase CO2ER with the LDH-loaded gas-diffusion electrode (GDE) was examined. The products were characterized by XRD, STEM-EDX, BF-TEM and ATR-IR spectroscopy. In the ATR-IR results, the interaction of CO2 with Zn-Al LDH showed a different carbonates evolution with respect to other LDHs, suggesting a different electrocatalytic activity. The LDH-loaded GDE was prepared by simple drop-casting of a catalyst ink onto carbon paper. For gas-phase CO2ER, only Zn-Al LDH exhibited the CO2ER activity for carbon monoxide (CO) formation. By using different potassium salt electrolytes affording neutral to strongly basic conditions, such as KCl, KHCO3 and KOH, the gas-phase CO2ER with Zn-Al LDH-loaded GDE showed 1.3 to 2.1 times higher partial current density for CO formation than the liquid-phase CO2ER.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.5796/ELECTROCHEMISTRY.23-00080
|
Nakazato R, Matsumoto K, Yamaguchi N, Cavallo M, Crocella V, Bonino F, Quintelier M, Hadermann J, Rosero-Navarro NC, Miura A, Tadanaga K (2023) CO2 Electrochemical Reduction with Zn-Al Layered Double Hydroxide-Loaded Gas-Diffusion Electrode (Supporting Information)
Abstract: Carbon dioxide electrochemical reduction (CO2ER) has attracted considerable attention as a technology to recycle CO2 into raw materials for chemicals using renewable energies. We recently found that Zn-Al layered double hydroxides (Zn-Al LDH) have the CO-forming CO2ER activity. However, the activity was only evaluated by using the liquid-phase CO2ER. In this study, Ni-Al and Ni-Fe LDHs as well as Zn-Al LDH were synthesized using a facile coprecipitation process and the gas-phase CO2ER with the LDH-loaded gas-diffusion electrode (GDE) was examined. The products were characterized by XRD, STEM-EDX, BF-TEM and ATR-IR spectroscopy. In the ATR-IR results, the interaction of CO2 with Zn-Al LDH showed a different carbonates evolution with respect to other LDHs, suggesting a different electrocatalytic activity. The LDH-loaded GDE was prepared by simple drop-casting of a catalyst ink onto carbon paper. For gas-phase CO2ER, only Zn-Al LDH exhibited the CO2ER activity for carbon monoxide (CO) formation. By using different potassium salt electrolytes affording neutral to strongly basic conditions, such as KCl, KHCO3 and KOH, the gas-phase CO2ER with Zn-Al LDH-loaded GDE showed 1.3 to 2.1 times higher partial current density for CO formation than the liquid-phase CO2ER.
Keywords: Dataset; Electron microscopy for materials research (EMAT)
DOI: 10.50892/DATA.ELECTROCHEMISTRY.24069993
|
“Insight on Zn-Al LDH as electrocatalyst for CO2 reduction reaction: An in-situ ATR-IR study”. Cavallo M, Dosa M, Nakazato R, Porcaro NG, Signorile M, Quintelier M, Hadermann J, Bordiga S, Rosero-Navarro NC, Tadanaga K, Crocellà, V, Bonino F, Journal of CO2 Utilization 83, 102804 (2024). http://doi.org/10.1016/j.jcou.2024.102804
Abstract: Electrochemical reduction of CO2 (CO2RR) is expected to play a key role among the various strategies being explored to limit global warming. In this scenario, Layered Double Hydroxides (LDHs) are emerging as a promising class of electrocatalysts to replace the most used noble metals. In this work three Zn-Al LDH with different Zn2+/Al3+ ratio were synthesized and characterized by means of XRD, STEM-EDX and HR-TEM. Their suitability for CO2RR to CO was assessed by means of a custom-made three-compartment cell, showing an increase in CO selectivity by decreasing the Zn2+/Al3+ ratio. The CO2 interaction with the samples was firstly
characterized by means of volumetric adsorption measurements, exhibiting an increase in capture capacity by decreasing the Zn2+/Al3+ ratio. The evolution of the samples in interaction with a CO2-saturated liquid flow was then deeply investigated by means of in-situ ATR-IR spectroscopy. The samples displayed a different evolution in the vibrational region of the carbonate-like species (1800–1200 cm???? 1). To better discriminate the different carbonate cyclohexane was also employed. A definitive assignment of the main IR bands of the carbonate was
carried out by studying the spectral behavior of the different bands observed in the ATR-IR experiments and by comparing these results with the existing literature. Interestingly, Zn-Al 1:2 LDH, the most efficient electrocatalyst for CO2RR, is also the sole sample exhibiting a higher monodentate to total bidentate carbonates ratio, suggesting that the existence of a higher content of low coordination oxygen anions with stronger basic character can influence the final catalytic activity.
Keywords: A1 Journal Article; In-situ ATR-IR spectroscopy; Layered Double Hydroxide; CO2 reduction reaction; Electrocatalysis; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 7.7
DOI: 10.1016/j.jcou.2024.102804
|