“Structure and high-temperature properties of the (Sr,Ca,Y)(Co,Mn)O3-y perovskites –, perspective cathode materials for IT-SOFC”. Napolsky PS, Drozhzhin OA, Istomin SY, Kazakov SM, Antipov EV, Galeeva AV, Gippius AA, Svensson G, Abakumov AM, Van Tendeloo G, Journal of solid state chemistry 192, 186 (2012). http://doi.org/10.1016/j.jssc.2012.03.056
Abstract: Oxygen deficient perovskites Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75, were prepared by using the citrate route at 1373-1573 K for 48 h. The cubic Pm-3m perovskite structure for x=0.5 was confirmed by electron diffraction study and refined using neutron powder diffraction (NPD) data. For x=0.75, the superstructure corresponding to a=root 2 x a(per), b=2 x a(per), c=root 2 x a(per) (a(0)b(-)b(-) tilt system, space group Imma) was revealed by electron diffraction. The solid solution Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= x <= 0.6 and compound Ca0.75Y0.25Mn0.85Co0.15O2.92 were prepared in air at 1573 K for 48 h. The crystal structure of Ca0.75Y0.25Mn0.85Co0.15O2.92 was refined using NPD data (S.G. Pnma, a=5.36595(4), b=7.5091(6), c=5.2992(4) angstrom, R-p=0.057, R-wp=0.056, chi(2)=4.26). High-temperature thermal expansion properties of the prepared compounds were studied in air using both dilatometry and high-temperature X-ray powder diffraction data (HTXRPD). They expanding non-linearly at 298-1073 K due to the loss of oxygen at high temperatures. Calculated average thermal expansion coefficients (TECs) for Sr0.75Y0.25Co1-xMnxO3-y, x=0.5, 0.75 and Ca0.75Y0.25Mn0.85Co0.15O2.92(1) are 15.5, 15.1, and 13.8 ppm K-1, respectively. Anisotropy of the thermal expansion along different unit cell axes was observed for Sr0.15Ca0.6Y0.25Co0.25Mn0.75O3-y, and Ca0.75Y0.25Mn0.85Co0.15O2.92. Conductivity of Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75 increases with the temperature reaching 110 S/cm for x=0.5 and 44 S/cm for x=0.75 at 1173 K. Samples of Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= y <= 0.6 were found to be n-type conductors at room temperature with the similar temperature dependence of the conductivity and demonstrated the increase of the sigma value from similar to 1 to similar to 50 S/cm as the temperature increases from 300 to 1173 K. Their conductivity is described in terms of the small polaron charge transport with the activation energy (E-p) increasing from 340 to 430 meV with an increase of the calcium content from x=0 to x=0.6. (C) 2012 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/j.jssc.2012.03.056
|
|
|
“90°, Rotation of orbital stripes in bilayer manganite PrCa2Mn2O7 studied by in situ transmission electron microscopy”. He ZB, Deng G, Tian H, Xu Q, Van Tendeloo G, Journal of solid state chemistry 200, 287 (2013). http://doi.org/10.1016/j.jssc.2013.01.051
Abstract: We present an in situ transmission electron microscopy study on the half-doped bilayer manganite PrCa2Mn2O7 to reveal the rotation process of the orbital stripes. Between the reported initial and final ordering phases, we identified an intermediate state with two sets of satellite spots to bridge the 90° rotation of the orbital stripes. Furthermore, we determined that the rotation of the orbital stripes does not always occur. Some restricted conditions for the orbital rotation to occur were found and reasons are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/j.jssc.2013.01.051
|
|
|
“Synthesis, crystal structure, and properties of KSbO3-type Bi3Mn1.9Te1.1O11”. Li MR, Retuerto M, Bok Go Y, Emge TJ, Croft M, Ignatov A, Ramanujachary KV, Dachraoui W, Hadermann J, Tang MB, Zhao JT, Greenblatt M;, Journal of solid state chemistry 197, 543 (2013). http://doi.org/10.1016/j.jssc.2012.07.038
Abstract: Single crystals of Bi3Mn1.9Te1.1O11 were prepared from NaCl+KCl flux. This compound adopts KSbO3-type crystal structure as evidenced by electron and single crystal X-ray diffraction analysis. The three-dimensional channel structure is formed by corner-sharing octahedral (Mn0.63Te0.37)2O10 dimers and two identical (Bi1)4(Bi2)2 interpenetrating lattices. The intra-dimer Mn/TeMn/Te distances in Bi3Mn1.9Te1.1O11 are short and are consistent with weak metalmetal interactions. The mixed oxidation state of manganese and the edge-sharing octahedral features are confirmed by X-ray near edge absorption spectroscopy measurements, which indicate Bi3(MnIII1.1MnIV0.8)TeVI1.1O11 with 57.7% Mn3+ and 42.3% Mn4+. The partial substitution of Te for Mn perturbs long-range magnetic interactions, thereby destroying the ferromagnetic ordering found in Bi3Mn3O11 (TC=150 K).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 13
DOI: 10.1016/j.jssc.2012.07.038
|
|
|
“Pb5Fe3TiO11Cl : a rare example of Ti(IV) in a square pyramidal oxygen coordination”. Batuk M, Batuk D, Abakumov AM, Hadermann J, Journal of solid state chemistry 215, 245 (2014). http://doi.org/10.1016/j.jssc.2014.04.002
Abstract: A new oxychloride Pb5Fe3TiO11Cl has been synthesized using the solid state method. Its crystal and magnetic structure was investigated in the 1.5550 K temperature range using electron diffraction, high angle annular dark field scanning transmission electron microscopy, atomic resolution energy dispersive X-ray spectroscopy, neutron and X-ray powder diffraction. At room temperature Pb5Fe3TiO11Cl crystallizes in the P4/mmm space group with the unit cell parameters a=3.91803(3) Å and c=19.3345(2) Å. Pb5Fe3TiO11Cl is a new n=4 member of the oxychloride perovskite-based homologous series An+1BnO3n−1Cl. The structure is built of truncated Pb3Fe3TiO11 quadruple perovskite blocks separated by CsCl-type Pb2Cl slabs. The perovskite blocks consist of two layers of (Fe,Ti)O6 octahedra sandwiched between two layers of (Fe,Ti)O5 square pyramids. The Ti4+ cations are preferentially located in the octahedral layers, however, the presence of a noticeable amount of Ti4+ in a five-fold coordination environment has been undoubtedly proven using neutron powder diffraction and atomic resolution compositional mapping. Pb5Fe3TiO11Cl is antiferromagnetically ordered below 450(10) K. The ordered Fe magnetic moments at 1.5 K are 4.06(4) μB and 3.86(5) μB on the octahedral and square-pyramidal sites, respectively.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 4
DOI: 10.1016/j.jssc.2014.04.002
|
|
|
“The interplay of microstructure and magnetism in La3Ni2SbO9”. Battle PD, Avdeev M, Hadermann J, Journal of solid state chemistry 220, 163 (2014). http://doi.org/10.1016/j.jssc.2014.08.024
Abstract: La3Ni2SbO9 adopts a perovskite-related structure in which the six-coordinate cation sites are occupied alternately by Ni2+ and a disordered arrangement of Ni2+/Sb5+. A polycrystalline sample has been studied by neutron diffraction in applied magnetic fields of 0 <= H/kOe <= 50 at 5 K. In 0 kOe, weak magnetic Bragg scattering consistent with the adoption of a G-type ferrimagnetic structure is observed; the ordered component of the magnetic moment was found to be 0.89(7) mu(B) per Ni2+ cation. This increased to 1.60(3) mu(B) in a field of 50 kOe. Transmission electron microscopy revealed variations in the Ni:Sb ratio across crystallites of the sample. It is proposed that these composition variations disrupt the magnetic superexchange interactions within the compound, leading to domain formation and a reduced average moment. The application of a magnetic field aligns the magnetisation vectors across the crystal and the average moment measured by neutron diffraction increases accordingly. The role played by variations in the local chemical composition in determining the magnetic properties invites comparison with the behaviour of relaxor ferroelectrics. (C) 2014 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 13
DOI: 10.1016/j.jssc.2014.08.024
|
|
|
“CaLa2FeCoSbO9 and ALa2FeNiSbO9 (A = Ca, Sr, Ba): cation-ordered, inhomogeneous, ferrimagnetic perovskites”. Hendrickx M, Tang Y, Hunter EC, Battle PD, Cadogan Jm, Hadermann J, Journal Of Solid State Chemistry 285, 121226 (2020). http://doi.org/10.1016/j.jssc.2020.121226
Abstract: Polycrystalline samples of CaLa2FeCoSbO9 and ALa2FeNiSbO9 (A=Ca, Sr, Ba) have been prepared in solid-state reactions and studied by a combination of transmission electron microscopy, magnetometry, X-ray diffraction, neutron diffraction and Mössbauer spectroscopy. Diffraction and TEM showed that each shows 1:1 B-site ordering in which Co2+/Ni2+ and Sb5+ tend to occupy two distinct crystallographic sites while Fe3+ is distributed over both sites. While X-ray and neutron diffraction agreed that all four compositions are monophasic with space group P21/n, TEM revealed different levels of compositional inhomogeneity at the subcrystal scale, which, in the case of BaLa2FeNiSbO9, leads to the occurrence of both a P21/n and an I2/m phase. Magnetometry and neutron diffraction show that these perovskites are ferrimagnets with a G-type magnetic structure. Their relatively low magnetisation can be attributed to their inhomogeneity. This work demonstrates the importance of studying the microstructure of complex compositions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.3
DOI: 10.1016/j.jssc.2020.121226
|
|
|
“Preparation of the noncentrosymmetric ferrimagnetic phase La0.9Ba0.1Mn0.96O2.43 by topochemical reduction”. Parsons TG, Hadermann J, Halasyamani PS, Hayward MA, Journal Of Solid State Chemistry 287, 121356 (2020). http://doi.org/10.1016/J.JSSC.2020.121356
Abstract: Topochemical reduction of La0.9Ba0.1MnO3 with NaH at 225 degrees C yields the brownmillerite phase La0.9Ba0.1MnO2.5. However, reduction with CaH2 at 435 degrees C results in the formation of La0.9Ba0.1Mn0.96O2.43 via the deintercalation of both oxide anions and manganese cations from the parent perovskite phase. Electron and neutron diffraction data reveal La0.9Ba0.1Mn0.96O2.43 adopts a complex noncentrosymmetric structure, described in space group I23, confirmed by SHG measurements. Low-temperature neutron diffraction data reveal La0.9Ba0.1Mn0.96O2.43 adopts an ordered magnetic structure in which all the nearest neighbor interactions are antiferromagnetic. However, the presence of ordered manganese cation-vacancies results in a net ferrimagnetic structure with net saturated moment of 0.157(2) mu B per manganese center.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.3
DOI: 10.1016/J.JSSC.2020.121356
|
|
|
“The crystal structure of Ba8Ta6NiO24: cation ordering in hexagonal perovskites”. Abakumov AM, Van Tendeloo G, Scheglov AA, Shpanchenko RV, Antipov EV, Journal of solid state chemistry 125, 102 (1996). http://doi.org/10.1006/jssc.1996.0270
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 38
DOI: 10.1006/jssc.1996.0270
|
|
|
“Defects and phase transformation in monclinic natural hollandite: BaxMn8O16”. Nistor LC, Van Tendeloo G, Amelinckx S, Journal of solid state chemistry 109, 152 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 13
|
|
|
“Defects and phase transition in monoclinic natural hollandite : BaxMn8O16”. Nistor LC, Van Tendeloo G, Amelinckx S, Journal of solid state chemistry 109, 152 (1994). http://doi.org/10.1006/jssc.1994.1085
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 13
DOI: 10.1006/jssc.1994.1085
|
|
|
“High resolution electron microscopic study of Ba7Sc6Al2O19 and related phases”. Shpanchenko RV, Nistor L, Van Tendeloo G, Amelinckx S, Antipov EV, Kovba LM, Journal of solid state chemistry 113, 193 (1994). http://doi.org/10.1006/jssc.1994.1359
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 3
DOI: 10.1006/jssc.1994.1359
|
|
|
“In situ study of the phase transition in Bi2Ti4O11”. Nistor L, Van Tendeloo G, Amelinckx S, Kahlenberg V, Böhm H, Journal of solid state chemistry 119, 281 (1995). http://doi.org/10.1016/0022-4596(95)80042-N
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 10
DOI: 10.1016/0022-4596(95)80042-N
|
|
|
“The modulated structure of Ca.85CuO2 as studied by means of electron diffraction”. Milat O, Van Tendeloo G, Amelinckx S, Babu TGN, Greaves C, Journal of solid state chemistry 97, 405 (1992)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 15
|
|
|
“Order and disorder in (Nd,Ce)nO2nSr2GaCu2O5 and YSr2CoCu2O7”. Krekels T, Milat O, Van Tendeloo G, Amelinckx S, Babu TGN, Wright AJ, Greaves C, Journal of solid state chemistry 105, 313 (1993). http://doi.org/10.1006/jssc.1993.1222
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 50
DOI: 10.1006/jssc.1993.1222
|
|
|
“Ordering principles and defect structure of “1201”, “1212”, and “1222&rdquo, type (Hg,Pr)-Sr-(Sr,Ca,Pr)-Cu-O superconductors”. Van Tendeloo G, Hervieu M, Zhang XF, Raveau B, Journal of solid state chemistry 114, 369 (1995). http://doi.org/10.1006/jssc.1995.1057
Abstract: The new families of superconducting compounds ''1201'' (Hg0.4Pr0.6Sr2CuO4+delta), ''1212'' (Hg0.4Pr0.6Sr2(Ca1-x-ySrxPry) Cu2O6+delta), and ''1222'' (Hg0.4Pr0.6Sr2(Pr1.7Sr0.3)(2)Cu2O8+delta) all show ordering between praseodymium and mercury in the (Hg,Pr)O-delta plane, reducing the symmetry from tetragonal to orthorhombic or even to monoclinic. In the 1201 compound the ordered superstructure can be described as O-I (a(I) approximate to 2a(p), b(I), approximate to a(p), c(I) approximate to c(1201)). In the 1212 compound two distinct superstructures are identified, O-I (a(I) approximate to 2a(p), b(II) approximate to a(p), c(I) approximate to c(1212)) and O-II (a(II) approximate to 2a(p), b(II) approximate to a(p), c(II) approximate to 2c(1212)). In some compounds, such as Hg0.4Pr0.6Sr2(Ca0.4Sr0.4Pr0.2) Cu2O6+delta, the Hg-Pr ordering is only present in microdomains, but due to an ordering between Sr layers and Ca layers, the c-axis doubles and one obtains a tetragonal superstructure T-III (a(III) approximate to a(p), c(III) approximate to 2c(1212)). In the 1222 compound, ordering in the (Pr,Hg)O-delta plane is very defective; a large number of translation defects actually reduce the symmetry to triclinic. (C) 1995 Academic Press, Inc.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 11
DOI: 10.1006/jssc.1995.1057
|
|
|
“A new cuprate with mercury bilayers : the “2222&rdquo, oxide Hg2-xMxBa2Pr2Cu2O10-\delta (M= Cu,Pr)”. Huve M, Martin C, Maignan A, Michel C, Van Tendeloo G, Hervieu M, Raveau B, Journal of solid state chemistry 114, 230 (1995). http://doi.org/10.1006/jssc.1995.1033
Abstract: A ''2222'' cuprate with mercury bilayers (Hg1.5Cu0.2Pr0.3)Ba2Pr2Cu2O10-delta, has been synthesized for the first time. It crystallizes in the P4/nmm space group with a = 3.9072(1) Angstrom and c = 17.219(1) Angstrom. The powder XRD and HREM studies of this new cuprate show that its structure consists of an intergrowth of double pyramidal (oxygen-deficient perovskite) copper layers, with double fluorite-type layers and distorted triple rock salt layers (mercury bilayers). The structure of this phase can be deduced from that of the ''2212'' mercury cuprate (Hg1.5Cu0.2Pr0.3)Ba2PrCu2O8-delta by the introduction of one additional [PrO2]infinity fluorite layer. The regular stacking of the metallic layer and the uniform cationic distribution in the mercury bilayers are remarkable features of this cuprate. The stabilization of the mercury bilayers by praseodymium and the absence of superconductivity are discussed. (C) 1995 Academic Press, Inc.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 6
DOI: 10.1006/jssc.1995.1033
|
|
|
“Superstructure and structural variants in Sr2CuO2(CO3)”. Milat O, Van Tendeloo G, Amelinckx S, Babu TGN, Greaves C, Journal of solid state chemistry 109, 5 (1994). http://doi.org/10.1006/jssc.1994.1063
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 11
DOI: 10.1006/jssc.1994.1063
|
|
|
“The modulated structure of Ca.85CuO2 as studied by means of electron diffraction and microscopy”. Milat O, Van Tendeloo G, Amelinckx S, Babu TGN, Greaves C, Journal of solid state chemistry 97, 405 (1992). http://doi.org/10.1016/0022-4596(92)90050-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 15
DOI: 10.1016/0022-4596(92)90050-6
|
|