Abstract: The synthesis, electron diffraction (ED), synchrotron X-ray and neutron structure, X-ray absorption spectroscopy (XAS) and magnetic property studies of La2MnVO6 double perovskite are described. Analysis of the synchrotron powder X-ray diffraction data for La2MnVO6 indicates a disordered arrangement of Mn and V at the B-site of the perovskite structure. Absence of super-lattice reflections in the ED patterns for La2MnVO6 supports the disordered cation arrangement. Room temperature time-of-flight (TOF) neutron powder diffraction (NPD) data show no evidence of cation ordering, in corroboration with the ED and synchrotron studies (orthorhombic Pnma, a = 5.6097(3), b = 7.8837(5) and c = 5.5668(3) ; 295 K, NPD). A comparison of XAS analyses of La2TVO6 with T = Ni and Co shows T2+ formal oxidation state while the T = Mn material evidences a Mn3+ admixture into a dominantly Mn2+ ground state. V-K edge measurements manifest a mirror image behavior with a V4+ state for T = Ni and Co with a V3+ admixture arising in the T = Mn material. The magnetic susceptibility data for La2MnVO6 show ferromagnetic correlations; the observed effective moment, µeff (5.72 µB) is much smaller than the calculated moment (6.16 µB) based on the spin-only formula for Mn2+ (d5, HS) /V4+ (d1), supportive of the partly oxidized Mn and reduced V scenario (Mn3+/V3+).

Abstract: The cyclotron resonance (CR) absorption spectrum is calculated for a II-VI parabolic quantum dot (QD) containing few electrons and a single magnetic dopant (Mn(2+)). We find that Kohn's theorem no longer holds for this system and that the CR spectrum depends on the number of electrons inside the QD. The electron-Mn-ion interaction strength can be tuned for example by the magnetic field and by moving the Mn-ion to different positions inside the QD. We demonstrate that due to the presence of the Mn-ion the relative motion of the electrons couple with their center-of-mass motion through the electron-Mn-ion spin-spin exchange term resulting in an electron-electron interaction dependence of the magneto-optical absorption spectrum. At the ferromagnetic-antiferromagnetic transition we observe significant discontinuities in the CR lines.

Abstract: Transmission electron microscopy is used to evaluate different deposition techniques, which optimize the microstructure and physical properties of superconducting thin films. High-resolution electron microscopy proves that the use of an YBa2Cu2Ox buffer layer can avoid a variable interface configuration in YBa2Cu3O7-delta thin films grown on SrTiO3. The growth can also be controlled at an atomic level by, using sub-unit cell layer epitaxy, which results in films with high quality and few structural defects. Epitaxial strain in Sr0.85La0.15CuO2 infinite layer thin films influences the critical temperature of these films, as well as the microstructure. Compressive stress is released by a modulated or a twinned microstructure, which eliminates superconductivity. On the other hand, also tensile strain seems to lower the critical temperature of the infinite layer.

Abstract: We studied the optical Aharonov-Bohm effect for an exciton in a semiconductor quantum ring. A perpendicular electric field applied to a quantum ring with large height, is able to tune the exciton ground state energy such that it exhibits a weak observable Aharonov-Bohm oscillations. This Aharonov-Bohm effect is tunable in strength and period.

Abstract: Experimentally, multivortex states and giant vortex states in mesoscopic superconductors can be distinguished directly by using the multiple-small-tunnel-junctions, and indirectly by studying the temperature dependence of the expulsion fields. These experimental results are compared with the theoretical prediction from the nonlinear Ginzburg- Landau theory.

Abstract: We have used high resolution Hall probe microscopy to image vortex-antivortex (V-AV) 'molecules' induced in superconducting Pb films by the stray fields from square arrays of ferromagnetic Co/Pt dots. We have directly observed spontaneous V-AV pairs and studied how they interact with added 'free' (anti)fluxons in an applied magnetic field. We observe a rich variety of subtle phenomena arising from competing symmetries in our system which can either drive added antivortices to join AV shells around nanomagnets or stabilise the translationally symmetric AV lattice between the dots. Added vortices annihilate AV shells, leading eventually to a stable 'nulling' state with no free fluxons, which should exhibit a strongly (field-)enhanced critical current. At higher densities we actually observe vortex shells around the magnets, stabilised by the asymmetric anti-pinning potential. Our experimental findings are in good agreement with Ginzburg-Landau calculations.

Abstract: The magnetic properties of a superconducting disk change dramatically when its dimensions become mesoscopic. Unlike large disks, where the screening currents induced by an applied magnetic field are strong enough to force vortices to accumulate in a 'puddle' at the centre, in a mesoscopic disk the interaction between one of these vortices and the edge currents can be comparable to the intervortex repulsion, resulting in a destruction of the ordered triangular vortex lattice structure at the centre. Vortices instead form clusters which adopt polygonal and shell-like structures which exhibit magic number states similar to those of charged particles in a confining potential, and electrons in artificial atoms. We have fabricated mesoscopic high temperature superconducting Bi2Sr2CaCu2O8+δ disks and investigated their magnetic properties using magneto-optical imaging (MOI) and high resolution scanning Hall probe microscopy (SHPM). The temperature dependence of the vortex penetration field measured using MOI is in excellent agreement with models of the thermal excitation of pancake vortices over edge barriers. The growth of the central vortex puddle has been directly imaged using SHPM and magic vortex numbers showing higher stability have been correlated with abrupt jumps in the measured local magnetisation curves.

Abstract: The interest in 2-dimensional systems with a honeycomb lattice and related Dirac-­type electronic bands has exceeded the prototype graphene1. Currently, 2-­dimensional atomic2,3 and nanoscale4-­8 systems are extensively investigated in the search for materials with novel electronic properties that can be tailored by geometry. The immediate question that arises is how to fabricate 2-­D semiconductors that have a honeycomb nanogeometry, and as a consequence of that, display a Dirac-­type band structure? Here, we show that atomically coherent honeycomb superlattices of rocksalt (PbSe, PbTe) and zincblende (CdSe, CdTe) semiconductors can be obtained by nanocrystal self-­assembly and facet-­to-­facet atomic bonding, and subsequent cation exchange. We present a extended structural analysis of atomically coherent 2-­D honeycomb structures that were recently obtained with self-assembly and facet-­to-­facet bonding9. We show that this process may in principle lead to three different types of honeycomb structures, one with a graphene type-­, and two others with a silicene-­type structure. Using TEM, electron diffraction, STM and GISAXS it is convincingly shown that the structures are from the silicene-­type. In the second part of this work, we describe the electronic structure of graphene-­type and silicene type honeycomb semiconductors. We present the results of advanced electronic structure calculations using the sp3d5s* atomistic tight-­binding method10. For simplicity, we focus on semiconductors with a simple and single conduction band for the native bulk semiconductor. When the 3-­D geometry is changed into 2-­D honeycomb, a conduction band structure transformation to two types of Dirac cones, one for S-­ and one for P-­orbitals, is observed. The width of the bands depends on the honeycomb period and the coupling between the nanocrystals. Furthermore, there is a dispersionless P-­orbital band, which also forms a landmark of the honeycomb structure. The effects of considerable intrinsic spin-­orbit coupling are briefly considered. For heavy-­element compounds such as CdTe, strong intrinsic spin-­‐orbit coupling opens a non-­trivial gap at the P-­orbital Dirac point, leading to a quantum Spin Hall effect10-­12. Our work shows that well known semiconductor crystals, known for centuries, can lead to systems with entirely new electronic properties, by the simple action of nanogeometry. It can be foreseen that such structures will play a key role in future opto-­electronic applications, provided that they can be fabricated in a straightforward way.

Abstract: Pure and 6 mol% BaHfO3 (BHO) doped YBa2Cu3O7-δ (YBCO) films were prepared on CeO2-buffered ABAD-YSZ templates by pulsed laser deposition. The self-field Jc at 77 K reaches 1.1 MA/cm² in the doped sample compared to 2.5 MA/cm² in pure YBCO, at a film thickness of around 1 μm. Above a magnetic field of 2.2 T along B||c, Jc of the BHO-doped sample exceeds the Jc of the undoped film. The maximum pinning force density (FP,max) reaches a value of around 3 GN/cm² for both samples, but B(FP,max) increases from 1.4 T (pure) to a value of 2.9 T (BHO:YBCO). The Jc anisotropy curves of the doped sample show a large and broad peak at B||c and a strongly reduced anisotropy at all temperatures and fields compared to the pure sample. A complex defect structure with YBa2Cu4O8 intergrowths, Y2O3 precipitates and BHO nanocolumns with a fanshaped structure is observed by TEM investigations, which can explain the measured Jc(B,θ) behavior.

Abstract: Although high temperature superconductors are promising for power applications, the production of low-cost coated conductors with high current densities—at high magnetic fields—remains challenging. A superior superconducting YBa2Cu3O7–δ nanocomposite is fabricated via chemical solution deposition (CSD) using preformed nanocrystals (NCs). Preformed, colloidally stable ZrO2 NCs are added to the trifluoroacetic acid based precursor solution and the NCs' stability is confirmed up to 50 mol% for at least 2.5 months. These NCs tend to disrupt the epitaxial growth of YBa2Cu3O7–δ, unless a thin seed layer is applied. A 10 mol% ZrO2 NC addition proved to be optimal, yielding a critical current density JC of 5 MA cm−2 at 77 K in self-field. Importantly, this new approach results in a smaller magnetic field decay of JC(H//c) for the nanocomposite compared to a pristine film. Furthermore, microstructural analysis of the YBa2Cu3O7–δ nanocomposite films reveals that different strain generation mechanisms may occur compared to the spontaneous segregation approach. Yet, the generated nanostrain in the YBa2Cu3O7–δ nanocomposite results in an improvement of the superconducting properties similar to the spontaneous segregation approach. This new approach, using preformed NCs in CSD coatings, can be of great potential for high magnetic field applications.

Abstract: The tunneling current between two crossed graphene ribbons is described invoking the empirical pseudopotential approximation and the Bardeen transfer Hamiltonian method. Results indicate that the density of states is the most important factor determining the tunneling current between small (similar to nm) ribbons. The quasi-one dimensional nature of graphene nanoribbons is shown to result in resonant tunneling.