Abstract: The structure of Fe/GaN/Fe ferromagnetic electrodes is studied by high resolution transmission electron microscopy. The layers grow epitaxially on the GaAs substrate with the top Fe layer 90degrees rotated compared to the bottom one. The interfaces are quite rough. There is an indication of the possible occurrence of Fe3GaAs formation on the GaAs interface.

Abstract: Flexible graphite foil produced by rolling expanded graphite impregnated with boron oxide was analyzed by laser mass spectroscopy, X-ray photoelectron spectroscopy, scanning electron microscopy and thermogravimetry. It was shown that the modification of the graphite foil by boron oxide increases the onset temperature of oxidation by ∼ 150 °C. Impregnation of less than 2 mass% boron oxide also increased the tensile strength of the materials. The observed improvement was attributed to the blocking of active sites by boron oxide, which is probably chemically bonded to the edges of graphene sheets in expanded graphite particles.

Abstract: It is known that the neutral image tone of a developed photographic film becomes brownish when the thickness of the original silver halide tabular crystals is reduced. We investigate by electron microscopy to what extent the silver filament structure has changed and how it induces the shift in image tone. Therefore, two samples of AgBr {111} tabular crystals with average thicknesses of 160 nm and 90 nm respectively, are compared. It is shown that the dimensions and defect structure of the filaments are comparable, but that the 90 nm crystals result in a more widely spaced structure, which explains the shift in image tone on a qualitative level. The influence of the addition of an image toner, i.e., phenylmercaptotetrazole, on the filament structure is also investigated. An even more open filament structure of longer, but smaller filaments was observed.

Abstract: The melting transition of the five different lattices of a bilayer crystal is studied using the Monte-Carlo (MC) technique. We found the surprising result that the square lattice has a substantial larger melting temperature as compared to the other lattice structures, which is a consequence of the specific topology of the temperature induced defects. A new melting criterion is formulated which we show to be universal for bilayers as well as for single layer crystals.

Abstract: A crystal structure investigation of the low temperature Li2SnO3 modification has been carried out. X-ray, neutron powder and electron diffraction data showed that this compound crystallizes in a monoclinic unit cell with parameters: a = 5.3033(2)Å, b = 9.1738(3)Å, c = 10.0195(2)Å, β ~ 100.042(2)º and has stacking disorder along the c-axis. Simulation of diffraction patterns with different stacking faults mainly reveal the presence of rotational stacking faults with a probability of about 40% .

Abstract: We report a microstructural and compositional study of a 90% Pb(Mg1/3Nb2/3)O-3 – 10% PbTiO3 ceramic sample. High resolution transmission electron microscopy (HRTEM) revealed the presence of compositional ordered nano-domains (1 – 4 mn), observable in two specific orientations, [0 (1) over bar 1] and [1 1 (2) over bar]. However, the visibility and the ordering degree of the nano-domains on the HRTEM images are not at all obvious. Fourier filtering of the images clearly revealed the ordered domains. Antiphase boundaries lying in the (111) planes separate them, while (100) and (111) facets separate the ordered domains from the disordered matrix. Their shape is plate-like, not uniformly spread in the disordered matrix. Their average size varies in different regions of the sample, most probably due to a non-uniform distribution of Ti, as observed by energy dispersive X-ray spectroscopy. (c) 2007 WILEY-VCH Verlag GmbH Co. KGaA, Weinheim.

Abstract: The microstructure and phase transitions in the perovskite-based ferroelectric lead scandium tantalate, Pb(Sc0.5Ta0.5)O-3 have been investigated by transmission electron microscopy. The effects of ordering of Sc and Ta cations are apparent in reciprocal space as well as in direct space images. High-resolution observations allow direct structure imaging of the domain structure. The structure of the low temperature ferroelectric phase is studied by selected area electron diffraction (SAED) and electron microdiffraction. The relaxer behaviour of this paraelectric-ferroelectric transition is displayed by diffuse intensities in the SAED patterns at temperatures around the Curie point.

Abstract: Microstructural investigations with transmission electron microscopy were carried out on quenched Ni-Ti alloys with 52 and 54.5 at% Ni. For the Ni52Ti48 specimen long time exposed diffraction patterns of a single grain show besides the expected reflections of the B2-phase, two sets of extra reflections in different zones. The first type of spots is explained by lattice displacement waves, which are regarded as precursors of the martensitic Ni-Ti phases, B 19' and R-phase, respectively. The second set of reflection with more diffuse intensity than the other reflections is related to Ni4Ti3 precipitates in an early state of formation. For the Ni-richer Ni54.5Ti45.5 alloy only Ni4Ti3 precipitates in an early state of formation are found but no precursors of the B 19'- and R-phase.